GB1268845A - Improvements in or relating to the manufacture of crystallized glass - Google Patents
Improvements in or relating to the manufacture of crystallized glassInfo
- Publication number
- GB1268845A GB1268845A GB3465369A GB3465369A GB1268845A GB 1268845 A GB1268845 A GB 1268845A GB 3465369 A GB3465369 A GB 3465369A GB 3465369 A GB3465369 A GB 3465369A GB 1268845 A GB1268845 A GB 1268845A
- Authority
- GB
- United Kingdom
- Prior art keywords
- glass
- crystallized glass
- july
- hours
- carrying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,268,845. Crystallized glass. NIPPON ELECTRIC GLASS CO. Ltd. 9 July, 1969 [29 July, 1968], No. 34653/69. Heading C1M. Crystallized glass is made from a glass comprising (in weight per cent) to an extent of at least 90%; SiO 2 55-73; Al 2 O 3 15-35; Li 2 O 2-6; ZrO 2 1-4; TiO 2 0À5-3; F 0.01-4; by carrying out a primary heat treatment for 0À5-20 hours between the transformation and softening temperatures of the glass, and then carrying out a secondary treatment by heating up to 850-1200‹ C. #-Encryptite is converted to #-Spodumene in the interior of the glass while remaining unchanged on the surface. The primary heat treatment may be at 700-770‹ C. The glass may be maintained at 850-1200‹ C. for 0-8 hours. The linear expansion coefficient of the crystallized glass is 7-30 x 10<SP>-7</SP>/‹ C., while the maximum bending strength is 1500- 6000 kg./cm.<SP>2</SP>. The surface compressive #- Eucryptite layer may be 50-100 Á thick.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP5302768 | 1968-07-29 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1268845A true GB1268845A (en) | 1972-03-29 |
Family
ID=12931392
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB3465369A Expired GB1268845A (en) | 1968-07-29 | 1969-07-09 | Improvements in or relating to the manufacture of crystallized glass |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB1268845A (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102016101066B3 (en) * | 2016-01-21 | 2017-02-23 | Schott Ag | Process for the preparation of a preferably non-colored glass-ceramic material with low scattered light content and glass-ceramic material produced according to the process and its use |
DE102016211065A1 (en) | 2016-06-21 | 2017-12-21 | Schott Ag | Transparent, preferably colored glass ceramic article with low scattered light content and high strength, as well as processes for its preparation and its use |
-
1969
- 1969-07-09 GB GB3465369A patent/GB1268845A/en not_active Expired
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102016101066B3 (en) * | 2016-01-21 | 2017-02-23 | Schott Ag | Process for the preparation of a preferably non-colored glass-ceramic material with low scattered light content and glass-ceramic material produced according to the process and its use |
EP3196174A1 (en) | 2016-01-21 | 2017-07-26 | Schott AG | Method for the manufacture of a preferably not coloured glass-ceramic material with a reduced diffused light and a glass ceramic material produced according to said method and its use |
DE102017101114A1 (en) | 2016-01-21 | 2017-07-27 | Schott Ag | Process for the preparation of a preferably non-colored glass-ceramic material with low scattered light content and glass-ceramic material produced according to the process and its use |
DE102017101114B4 (en) | 2016-01-21 | 2019-06-13 | Schott Ag | Process for the preparation of a preferably non-colored glass-ceramic material with low scattered light content and glass-ceramic material produced according to the process and its use |
DE102016211065A1 (en) | 2016-06-21 | 2017-12-21 | Schott Ag | Transparent, preferably colored glass ceramic article with low scattered light content and high strength, as well as processes for its preparation and its use |
DE102016211065B4 (en) | 2016-06-21 | 2019-09-05 | Schott Ag | Transparent, preferably colored glass ceramic article with low scattered light content and high strength, as well as processes for its preparation and its use |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB857367A (en) | Low expansion glass-ceramic and method of making it | |
NO921849L (en) | SILICO SOLAR, PROCEDURE FOR MANUFACTURING SILICO SOLAR AND USE OF IT | |
AU572467B2 (en) | Process for manufacturing crystalline alumina | |
GB1212123A (en) | Method for strengthening glass articles | |
GB885618A (en) | Glass body having a semi-crystalline surface layer and method of making the same | |
AU579349B2 (en) | Lithium alumino-silicate glass ceramics | |
GB1398908A (en) | Method of producing a compressive stress layer in the surface of a glass-ceamic body | |
GB1132885A (en) | Copper glass compositions, products and methods | |
EP0399786A3 (en) | Refractory linings capable of resisting sodium and sodium salts | |
ES469931A1 (en) | Heat radiation reflecive glass | |
GB1287970A (en) | ||
GB1286893A (en) | Coated metal article and method of making the same | |
GB1457627A (en) | Glass soldering mixture | |
GB1268845A (en) | Improvements in or relating to the manufacture of crystallized glass | |
GB1315009A (en) | Sealing composite bodies | |
AU4995379A (en) | Thermal toughening of glass | |
ES8607892A1 (en) | Method of manufacturing refractory bodies or compositions | |
GB1019821A (en) | Improvements in methods of bonding refractory bodies | |
ES8505319A1 (en) | Method of fire-polishing the surfaces of glass objects. | |
AU576940B2 (en) | Multi-layer refractory structure | |
ES379634A1 (en) | Glass-ceramic products | |
AU3552884A (en) | Process for the reversible transfer of thermal energy and heat transfer system useful therein | |
GB1331357A (en) | Method of producing top plates for use in ranges | |
AU605352B2 (en) | Process for preparing di-n-propylacetonitrile | |
ES8706586A1 (en) | Process for the production of a high tensile strength mortar for the walls of coking furnaces |