FR2723389A1 - WALL COATING BASE - Google Patents
WALL COATING BASE Download PDFInfo
- Publication number
- FR2723389A1 FR2723389A1 FR9509538A FR9509538A FR2723389A1 FR 2723389 A1 FR2723389 A1 FR 2723389A1 FR 9509538 A FR9509538 A FR 9509538A FR 9509538 A FR9509538 A FR 9509538A FR 2723389 A1 FR2723389 A1 FR 2723389A1
- Authority
- FR
- France
- Prior art keywords
- weight
- parts
- base
- pigment
- wall covering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
On décrit une base de revêtement mural, exempte de couche de chlorure de vinyle, dans laquelle une unique couche d'enduction ignifuge, comprenant 100 parties en poids d'un pigment et plus de 70 parties en poids mais moins de 100 parties en poids d'une résine synthétique, avec 30 parties en poids, ou davantage, du pigment pour 100 parties en poids de la résine synthétique qui sont constituées par de l'hydroxyde d'aluminium, est appliquée en revêtement en une quantité de plus de 10 g/m**2 à moins de 30 g/m**2 sur la surface d'une matière de papier de base qui a été soumise à un traitement d'ignifugation, ce par quoi l'on empêche l'évaporation de l'humidité à partir de ladite base de revêtement mural, en même temps qu'on lui confère une aptitude à l'impression, sans provoquer de détérioration de son ignifugation. Il est ainsi proposé de façon économique une base de revêtement mural, exempte de couche de chlorure de vinyle, qui présente un temps ouvert suffisamment long pour l'opération de collage, qui est attrayante une fois imprimée, et qui présente un caractère ignifuge.Disclosed is a wallcovering base, free from a vinyl chloride layer, wherein a single flame retardant coating layer comprising 100 parts by weight of a pigment and more than 70 parts by weight but less than 100 parts by weight of a pigment. a synthetic resin, with 30 parts by weight, or more, of the pigment per 100 parts by weight of the synthetic resin which consists of aluminum hydroxide, is coated in an amount of more than 10 g / m ** 2 to less than 30 g / m ** 2 on the surface of a base paper material which has been subjected to a fireproofing treatment, whereby evaporation of moisture is prevented from said wall covering base, at the same time as imparting printability to it, without causing deterioration of its flame retardancy. There is thus economically provided a wallcovering base, free of vinyl chloride layer, which has a sufficiently long open time for the gluing operation, which is attractive when printed, and which exhibits flame retardancy.
Description
BASE DE REV TEMENT MURALBASE OF WALL COVER
La présente invention porte, d'une manière générale, sur une base de revêtement mural, et, plus spécifiquement, sur une base de revêtement mural pour la production d'un revêtement mural qui peut être laissé plus longtemps après l'application d'une pate aqueuse sur lui, qui présente un caractère ignifuge, et qui peut ajouter un The present invention generally relates to a wall covering base, and, more specifically, to a wall covering base for the production of a wall covering that can be left longer after the application of a wall covering. aqueous paste on it, which has a flame-retardant character, and which can add a
fini décoratif au mur.decorative finish on the wall.
Comme revêtement mural, on utilise généralement un revêtement mural vinylique, comprenant une couche enduite de As a wall covering, a vinyl wall covering is generally used, comprising a layer coated with
chlorure de vinyle sur une base de revêtement mural. vinyl chloride on a wall covering basis.
Cependant, le revêtement mural vinylique pose un problème de mise au rebut. Comme autre possibilité, on a proposé un revêtement mural ne présentant pas de couche de chlorure de vinyle. Cependant, un problème qui se pose avec cet autre type de revêtement mural est qu'étant donné qu'il est impossible d'empêcher l'évaporation de l'humidité à partir de la surface, par suite de l'absence de la couche de chlorure de vinyle servant de couche barrière, le temps qui s'écoule entre l'application d'une pate aqueuse sur le revêtement mural et le collage du revêtement mural sur le mur (généralement appelé le "temps ouvert") est très court, et également le revêtement mural devient peu attrayant une fois qu'il a été imprimé. Ces problèmes peuvent, à première vue, être résolus par une matière de revêtement mural décrite dans la publication du brevet Japonais nô 5(1993)-59 700, qui est caractérisée par la disposition, sur la surface arrière, d'une couche de revêtement de pigment et, sur la surface avant, d'une couche barrière ne laissant pas passer l'eau et d'un plastifiant, et d'une couche conférant l'aptitude à l'impression. Cependant, ce revêtement mural coûte cher et est, de ce fait, peu économique, en raison du fait que, pour obtenir des avantages suffisants, la base de However, vinyl wallcovering poses a disposal problem. As another possibility, a wall covering having no vinyl chloride layer has been proposed. However, a problem that arises with this other type of wallcovering is that since it is impossible to prevent the evaporation of moisture from the surface, due to the absence of the a barrier layer of vinyl chloride, the time elapsing between the application of an aqueous paste on the wall covering and the bonding of the wall covering to the wall (generally called "open time") is very short, and also the wallcovering becomes unattractive once it has been printed. These problems may, at first sight, be solved by a wall covering material described in Japanese Patent Publication No. 5 (1993) -59,700, which is characterized by the provision on the back surface of a coating layer. of pigment and, on the front surface, a barrier layer that does not allow water to pass and a plasticizer, and a layer that imparts printability. However, this wall covering is expensive and therefore uneconomical because of the fact that, in order to obtain sufficient benefits, the
revêtement mural doit être enduite trois fois. wallcovering should be coated three times.
La publication du brevet Japonais nô 56(1981)- Japanese Patent Publication No. 56 (1981) -
144 298 décrit une invention caractérisée par la disposition, sur la surface arrière d'un papier, d'une couche d'enduction de résine ayant une bonne résistance à la pénétration de l'humidité, et la publication du modèle d'utilité japonais n 61(1986)-23040 décrit une structure multicouche, caractérisée par le fait qu'elle comprend un couche de papier, une couche de résine synthétique, et une No. 144,298 discloses an invention characterized by disposing, on the back surface of a paper, a resin coating layer having good resistance to moisture penetration, and the publication of the Japanese utility model 61 (1986) -23040 discloses a multilayer structure, characterized in that it comprises a paper layer, a synthetic resin layer, and a
couche de renfort.reinforcement layer.
Cependant, comme indiqué dans la publication du brevet japonais ne 559700, le revêtement mural décrit dans la publication du brevet japonais ne 56-144 298 pose le problème qu'une adhérence de contact entre feuilles (blocking) se produit facilement. Un autre problème est qu'une difficulté se présente lorsque l'on confère à ce revêtement mural un degré de perméabilité à l'humidité suffisamment bon pour empêcher le glissement vers le bas du revêtement mural pendant l'opération de collage. La structure multicouche décrite dans la publication du modèle d'utilité japonais n0 61-23 040 est non seulement However, as disclosed in Japanese Patent Publication No. 559700, the wallcovering disclosed in Japanese Patent Publication No. 56-144298 raises the problem that blocking contact between sheets occurs easily. Another problem is that a difficulty arises in giving this wallcovering a degree of moisture permeability sufficiently good to prevent downward sliding of the wallcovering during the bonding operation. The multilayer structure described in Japanese Utility Model Publication No. 61-23,040 is not only
compliquée, mais encore coûte cher, comme mentionné ci- complicated, but still expensive, as mentioned above.
dessus.above.
La publication du brevet Japonais n 5(1993)- Japanese Patent Publication No. 5 (1993) -
247 898 décrit une invention caractérisée par l'application en revêtement, sur une base de revêtement mural, d'un agent d'enduction comprenant 100 parties en poids d'un pigment insoluble dans l'eau et 30 à 70 parties en poids d'un liant de type latex. Conformément à cette invention, il est possible d'améliorer l'aptitude à l'impression du revêtement mural, mais le temps ouvert est estimé être court parce que l'inhibition de l'évaporation de l'humidité à travers la 247,898 discloses an invention characterized by coating, on a wall-coating basis, a coating agent comprising 100 parts by weight of a water-insoluble pigment and 30 to 70 parts by weight of a binder of the latex type. In accordance with this invention, it is possible to improve the printability of the wallcovering, but the open time is believed to be short because the inhibition of moisture evaporation through the
base de revêtement mural n'est pas prise en considération. wall covering base is not taken into consideration.
Jamais jusqu'à maintenant l'on a trouvé de compromis satisfaisant entre l'aptitude à la mise en oeuvre Never until now has there been a satisfactory compromise between the suitability for implementation
et l'économie de la production.and the economy of production.
Un but de la présente invention est de proposer une base de revêtement mural, exempte de couche de chlorure de vinyle, qui présente un long temps ouvert alloué pour l'opération de collage, et qui possède une aptitude à It is an object of the present invention to provide a vinyl chloride-free wallcovering base which has a long open time allocated for the bonding operation, and which has the ability to
l'impression et un caractère ignifuge (retard de flamme). printing and flame retardancy (flame retardancy).
Conformément à la présente invention, le but ci- In accordance with the present invention, the purpose of
dessus est atteint par la réalisation d'une base de revêtement mural caractérisée en ce qu'elle comprend une seule couche d'enduction sur la surface de la matière de papier de base, ce par quoi l'évaporation de l'humidité à partir de celle-ci est inhibée avec une amélioration de l'aptitude à l'impression et néanmoins sans provoquer de détérioration de l'ignifugation de la matière de papier de base. En particulier, la couche unique d'enduction décrite ci-dessus, disposée sur le côté de la surface, combine une fonction de barrière avec une fonction conférant l'aptitude à l'impression sans être séparée en deux couches, à savoir une barrière et une couche conférant l'aptitude à l'impression, comme présenté dans l'invention décrite dans the above is achieved by producing a wall covering base characterized in that it comprises a single coating layer on the surface of the base paper material, whereby the evaporation of moisture from this is inhibited with an improvement in printability and yet without causing deterioration of flame retardancy of the base paper material. In particular, the single coating layer described above, disposed on the side of the surface, combines a barrier function with a printability-imparting function without being separated into two layers, namely a barrier and a printability conferring layer as presented in the invention described in
la publication du brevet japonais ne 5-59 700. Japanese Patent Publication No. 5-59,700.
De façon plus spécifique, conformément à la présente invention, il est proposé une base de revêtement mural, exempte de couche de chlorure de vinyle, caractérisée en ce qu'une couche unique d'enduction ignifuge, comprenant 100 parties en poids d'un pigment et plus de 70 parties en poids mais moins de 100 parties en poids d'une résine synthétique avec 30 parties en poids, ou davantage, du pigment pour 100 parties en poids de la résine synthétique qui sont constituées par de l'hydroxyde d'aluminium, est appliquée en revêtement en une quantité de plus de 10 g/m2 à moins de 30 g/m2 sur la surface d'une matière de papier de More specifically, according to the present invention, there is provided a wall covering base, free of vinyl chloride layer, characterized in that a single layer of flame retardant coating comprising 100 parts by weight of a pigment and more than 70 parts by weight but less than 100 parts by weight of a synthetic resin with 30 parts by weight or more of the pigment per 100 parts by weight of the synthetic resin which consist of aluminum hydroxide , is coated in an amount of more than 10 g / m 2 to less than 30 g / m 2 on the surface of a paper
base soumise à un traitement d'ignifugation. base subjected to fireproofing treatment.
La matière de papier de base utilisée présentement n'est pas critique, et, ainsi, les matières de type papier de renfort ordinaire pour revêtement mural, les matières de type papier ordinaire pour revêtement mural, et les matières de type papier inorganique peuvent être utilisées à la The base paper material currently being used is not critical, and thus ordinary wall-coat type paper materials, plain wall paper type materials, and inorganic paper type materials can be used. to the
condition qu'une ignifugation leur ait été conférée. provided that fireproofing has been conferred upon them.
La manière dont on confère l'ignifugation à ces matières de papier de base n'est pas critique, et, ainsi, l'ignifugation peut être obtenue par l'imprégnation de la matière de papier avec des agents retardateurs de flamme, à l'aide d'une pression appliquée au moyen d'une presse encolleuse ou de l'incorporation de charges minérales, telles que l'hydroxyde d'aluminium, dans la matière de papier. Le pigment utilisé présentement n'est pas non plus critique. Par exemple, utilisation peut être faite d'argile, de carbonate de calcium, d'oxyde de titane, de silice et d'hydroxyde d'aluminium, toutes ces matières étant à The manner in which flame retardancy is imparted to these base paper materials is not critical, and thus flame retardancy can be obtained by impregnating the paper material with flame retardants at the same time. using a pressure applied by means of a gluing press or the incorporation of mineral fillers, such as aluminum hydroxide, into the paper material. The pigment currently used is not critical either. For example, use may be made of clay, calcium carbonate, titanium oxide, silica and aluminum hydroxide, all these materials being
disposition pour l'enduction de papier ordinaire. provision for coating ordinary paper.
Cependant, il existe l'exigence que 30 parties en poids, ou davantage, d'hydroxyde d'aluminium soient utilisées pour parties en poids de résine synthétique. A moins de parties en poids, on ne peut pas obtenir une ignifugation suffisante. La résine synthétique utilisée présentement doit satisfaire deux fonctions en même temps, l'une étant d'inhiber l'évaporation de l'humidité et, par là, d'augmenter le temps ouvert, et l'autre, de servir comme However, there is a requirement that 30 parts by weight or more of aluminum hydroxide be used for parts by weight of synthetic resin. At least parts by weight, sufficient flame retardancy can not be achieved. The synthetic resin currently used must satisfy two functions at the same time, one of which is to inhibit the evaporation of moisture and thereby increase the open time, and the other to serve as
liant pour lier le pigment à la matière de papier de base. binder for binding the pigment to the base paper material.
N'importe quelle résine synthétique peut être utilisée si elle satisfait ces deux exigences. Par exemple, les résines acryliques, le poly(acétate de vinyle) et les résines de type alcool polyvinylique peuvent être utilisées individuellement ou en mélange de deux d'entre elles ou davantage. Cependant, le caoutchouc styrène-butadiène n'est pas désiré parce qu'il vire au Jaune ou au brun lors de l'exposition aux rayons du soleil en raison de sa médiocre Any synthetic resin can be used if it meets both requirements. For example, acrylic resins, polyvinyl acetate and polyvinyl alcohol resins can be used individually or as a mixture of two or more of them. However, styrene-butadiene rubber is not desired because it turns yellow or brown when exposed to sunlight because of its poor
résistance à la lumière.resistance to light.
Une quantité de plus de 70 parties en poids à moins de 100 parties en poids de la résine synthétique est utilisée pour 100 parties en poids du pigment. A 70 parties en poids, ou au-dessous, il est difficile d'obtenir une inhibition suffisante de l'évaporation de l'humidité et, par là, d'augmenter le temps ouvert, alors qu'à 100 parties en poids, ou davantage, il est difficile de conférer une An amount of greater than 70 parts by weight to less than 100 parts by weight of the synthetic resin is used per 100 parts by weight of the pigment. At 70 parts by weight, or below, it is difficult to obtain a sufficient inhibition of the evaporation of moisture and thereby increase the open time, while at 100 parts by weight, or more, it is difficult to confer a
aptitude à l'impression à la matière de papier de base. ability to print basic paper material.
Comme mentionné, aucune limitation n'est placée sur le type de pigment utilisé. Cependant, pour obtenir un revêtement mural ignifuge, 30 parties en poids, ou davantage, d'hydroxyde d'aluminium doivent être utilisées pour 100 parties en poids de la résine synthétique. Si nécessaire, mais non exclusivement, divers adjuvants, tels que des agents de rétention d'eau, par exemple l'amidon, des lubrifiants, des agents améliorant la fluidité, des dispersants, des régulateurs de pH, des agents As mentioned, no limitation is placed on the type of pigment used. However, to obtain a flame retardant wallcovering, 30 parts by weight or more of aluminum hydroxide should be used per 100 parts by weight of the synthetic resin. If necessary, but not exclusively, various adjuvants, such as water retention agents, for example starch, lubricants, flow improvers, dispersants, pH regulators, agents
anti-mousse et des conservateurs, peuvent être utilisés. antifoam and preservatives, can be used.
La manière dont est effectuée l'enduction n'est pas critique et la couche d'enduction peut être appliquée par les techniques d'enduction de papier habituellement utilisées, telles que l'enduction à l'aide d'une enduiseuse à barre, le couchage par lame d'acier, le couchage à la lame The manner in which the coating is performed is not critical and the coating layer can be applied by the commonly used paper coating techniques, such as coating with a bar coater, sleeping by steel blade, the coating to the blade
ou le couchage par rouleau.or the coating by roll.
La couche d'enduction peut être appliquée en une quantité de 10 g/m2 ou davantage à moins de 30 g/m2. A moins de 10 g/m2, on n'obtient pas suffisamment d'inhibition de l'évaporation de l'humidité, et ceci amène la pâte à se dessécher immédiatement, conduisant à une diminution du temps ouvert. Par ailleurs, à 30 g/m2 ou davantage, un problème se pose en rapport avec l'économie de la production. La présente invention va maintenant être expliquée plus spécifiquement mais non exclusivement, en référence à The coating layer may be applied in an amount of 10 g / m 2 or more to less than 30 g / m 2. At less than 10 g / m 2, insufficient inhibition of moisture evaporation is obtained, and this causes the dough to dry out immediately, leading to a decrease in open time. In addition, at 30 g / m2 or more, a problem arises with respect to the economy of production. The present invention will now be explained more specifically but not exclusively, with reference to
certains exemples.some examples.
Excepté dans le cas de l'eau ammoniacale, les parties en poids utilisées présentement sont entendues comme Except in the case of ammonia water, the parts by weight currently used are understood as
étant calculées en tant que solide. being calculated as a solid.
Exemple 1Example 1
Une solution d'enduction, consistant en parties en poids d'hydroxyde d'aluminium (marque de fabrique HIGILITE H-42, fabriqué par Showa Denko K.K.), 90 parties en poids d'une émulsion de résine acrylique (marque de fabrique: AE-322, fabriquée par Japan Synthetic Rubber Co., Ltd.), 0,5 partie en poids d'un dispersant, et des régulateurs de pH, à savoir 0,05 partie en poids d'hydroxyde de sodium et 2 parties en poids d'une eau ammoniacale à 29%, a été appliquée en revêtement en une quantité de 25 g/m2 sur la surface d'un papier de base (marque de fabrique: 140 AF-P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 140 g/m2 et ayant été soumis à un traitement d'ignifugation par enduction à l'aide d'une enduiseuse à barre, permettant ainsi d'obtenir A coating solution, consisting of parts by weight of aluminum hydroxide (trade name HIGILITE H-42, manufactured by Showa Denko KK), 90 parts by weight of an acrylic resin emulsion (trade name: AE -322, manufactured by Japan Synthetic Rubber Co., Ltd.), 0.5 parts by weight of a dispersant, and pH regulators, namely 0.05 parts by weight of sodium hydroxide and 2 parts by weight 29% ammonia water was coated in an amount of 25 g / m2 on the surface of a base paper (trade name: 140 AF-P (D), manufactured by Nippon Paper Industries Co ., Ltd.) having a basis weight of 140 g / m 2 and having been subjected to flame retardant treatment by coating with a bar coater, thereby obtaining
une base de revêtement mural.a wall covering base.
Exemple 2Example 2
Une solution d'enduction, consistant en 30 parties en poids d'hydroxyde d'aluminium (marque de fabrique: HIGILITE H-42, fabriqué par Showa Denko K.K.), 70 parties en poids de carbonate de calcium (marque de fabrique: ESCALON #2000, fabriqué par Sankyo Seifun Co., Ltd.), 80 parties en poids d'une émulsion de résine acrylique (marque de fabrique: AE-322, fabriquée par Japan Synthetic Rubber Co., Ltd.), 0,5 partie en poids d'un dispersant, et des régulateurs de pH, à savoir 0,05 partie en poids d'hydroxyde de sodium et 2 parties en poids d'une eau ammoniacale à 29%, a été appliquée en revêtement en une quantité de 28 g/m2 sur A coating solution, consisting of 30 parts by weight of aluminum hydroxide (trade name: HIGILITE H-42, manufactured by Showa Denko KK), 70 parts by weight of calcium carbonate (trade name: ESCALON # 2000, manufactured by Sankyo Seifun Co., Ltd.), 80 parts by weight of an acrylic resin emulsion (trade name: AE-322, manufactured by Japan Synthetic Rubber Co., Ltd.), 0.5 parts by weight. The weight of a dispersant, and pH regulators, namely 0.05 parts by weight of sodium hydroxide and 2 parts by weight of a 29% ammonia water, was coated in an amount of 28 grams. / m2 on
la surface d'un papier de base (marque de fabrique 80AF- the surface of a base paper (trade name 80AF-
P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 80 g/m2 et ayant été soumis à un traitement d'ignifugation par enduction à l'aide d'une enduiseuse à barre, permettant ainsi d'obtenir une base de revêtement mural. P (D), manufactured by Nippon Paper Industries Co., Ltd.) having a basis weight of 80 g / m 2 and having been subjected to flame retardant treatment by coating with a bar coater, thus allowing to obtain a wall covering base.
Exemple 3Example 3
Une solution d'enduction, consistant en 40 parties en poids d'hydroxyde d'aluminium (marque de fabrique: HIGILITE H-42, fabriqué par Showa Denko K.K.), 50 parties en poids de kaolin (marque de fabrique: AMAZON-88, fabriqué par Caulim du Amazonia S.A.), 10 parties en poids de silice (marque de fabrique: FINESIL X-37, fabriquée par Tokuyama Co., Ltd.), 80 parties en poids d'une émulsion de résine acrylique (marque de fabrique: AE-322, fabriquée par Japan Synthetic Rubber Co., Ltd.), 0,5 partie en poids d'un dispersant, et des régulateurs de pH, à savoir 0,05 partie en poids d'hydroxyde de sodium et 2 parties en poids d'une eau ammoniacale à 29%, a été appliquée en revêtement en une quantité de 20 g/m2 sur la surface d'un papier de base (marque de fabrique: 160AF- P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 160 g/m2 et ayant été soumis à un traitement d'ignifugation par enduction à l'aide d'une enduiseuse à barre, permettant ainsi d'obtenir A coating solution, consisting of 40 parts by weight of aluminum hydroxide (trade name: HIGILITE H-42, manufactured by Showa Denko KK), 50 parts by weight of kaolin (trade name: AMAZON-88, manufactured by Caulim of Amazonia SA), 10 parts by weight of silica (trade name: FINESIL X-37, manufactured by Tokuyama Co., Ltd.), 80 parts by weight of an acrylic resin emulsion (trade name: AE-322, manufactured by Japan Synthetic Rubber Co., Ltd.), 0.5 parts by weight of a dispersant, and pH regulators, namely 0.05 parts by weight of sodium hydroxide and 2 parts by weight of weight of a 29% ammonia water, was applied as a coating in an amount of 20 g / m2 on the surface of a base paper (trade name: 160AF-P (D), manufactured by Nippon Paper Industries Co ., Ltd.) having a basis weight of 160 g / m 2 and having been subjected to a flame retardant treatment by coating with a bar coater, thereby obtaining ir
une base de revêtement mural.a wall covering base.
ExemDle Comparatif 1 On a utilisé un papier de base de revêtement mural, disponible dans le commerce (marque de fabrique: AF-P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 140 g/m2 et ayant été soumis à un EXAMPLE 1 A commercially available wallcovering base paper (trade name: AF-P (D), manufactured by Nippon Paper Industries Co., Ltd.) having a basis weight of 140 g / m 2 was used. having been subjected to
traitement d'ignifugation.fireproofing treatment.
Exemple Comparatif 2 Une émulsion de résine acrylique (marque de fabrique: AE-322, fabriquée par Japan Synthetic Rubber Co., Ltd.) a été appliquée en revêtement en une quantité de 20 g/m2 sur la surface d'un papier de base (marque de fabrique: 80AF-P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 80 g/m2 et ayant été soumis à un traitement d'ignifugation par enduction à l'aide d'une enduiseuse à barre, permettant ainsi d'obtenir une base de Comparative Example 2 An acrylic resin emulsion (trade name: AE-322, manufactured by Japan Synthetic Rubber Co., Ltd.) was coated in an amount of 20 g / m 2 on the surface of a base paper (Trade name: 80AF-P (D), manufactured by Nippon Paper Industries Co., Ltd.) having a basis weight of 80 g / m 2 and having been subjected to a flame retardant treatment by coating with a bar coater, thus providing a basis for
revêtement mural.Wall cover.
Exemple Comparatif 3 Une solution d'enduction, consistant en 30 parties en poids d'hydroxyde d'aluminium (marque de fabrique: HIGILITE H-42, fabriqué par Showa Denko K.K.), 70 parties en poids de carbonate de calcium (marque de fabrique: ESCALON #2000, fabriqué par Sankyo Seifun Co., Ltd.), 80 parties en poids d'une émulsion de résine acrylique (marque de fabrique: AE-322, fabriquée par Japan Synthetic Rubber Co., Ltd.), 0,5 partie en poids d'un dispersant, et des régulateurs de pH, à savoir 0,05 partie en poids d'hydroxyde de sodium et 2 parties en poids d'une eau ammoniacale à 29%, a été appliquée en revêtement en une quantité de 5 g/m2 sur Comparative Example 3 A coating solution, consisting of 30 parts by weight of aluminum hydroxide (trade name: HIGILITE H-42, manufactured by Showa Denko KK), 70 parts by weight of calcium carbonate (trade mark : ESCALON # 2000, manufactured by Sankyo Seifun Co., Ltd.), 80 parts by weight of an acrylic resin emulsion (trade name: AE-322, manufactured by Japan Synthetic Rubber Co., Ltd.), 0, 5 parts by weight of a dispersant, and pH regulators, namely 0.05 parts by weight of sodium hydroxide and 2 parts by weight of 29% ammonia water, were coated in a quantity of 5 g / m2 on
la surface d'un papier de base (marque de fabrique: 80AF- the surface of a base paper (trade name: 80AF-
P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 80 g/m2 et ayant été soumis à un traitement d'ignifugation par enduction à l'aide d'une enduiseuse à barre, permettant ainsi d'obtenir une base de revêtement mural. Exemple Comparatif 4 Une solution d'enduction, consistant en 50 parties en poids d'hydroxyde d'aluminium (marque de fabrique: HIGILITE H-42, fabriqué par Showa Denko K.K.), 50 parties en poids de carbonate de calcium (marque de fabrique: ESCALON #2000, fabriqué par Sankyo Seifun Co., Ltd.), 60 parties en poids d'une émulsion de résine acrylique (marque de fabrique: AE-322, fabriquée par Japan Synthetic Rubber Co., Ltd.), 0,5 partie en poids d'un dispersant, et des régulateurs de pH, à savoir 0,05 partie en poids d'hydroxyde de sodium et 2 parties en poids d'une eau ammoniacale à 29%, a été appliquée en revêtement en une quantité de 25 g/m2 sur la surface d'un papier de base (marque de fabrique: 80AF-P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 80 g/m2 et ayant été soumis à un traitement d'ignifugation par enduction à l'aide d'une enduiseuse à barre, permettant ainsi d'obtenir P (D), manufactured by Nippon Paper Industries Co., Ltd.) having a basis weight of 80 g / m 2 and having been subjected to flame retardant treatment by coating with a bar coater, thus allowing to obtain a wall covering base. Comparative Example 4 A coating solution, consisting of 50 parts by weight of aluminum hydroxide (trade name: HIGILITE H-42, manufactured by Showa Denko KK), 50 parts by weight of calcium carbonate (trade name : ESCALON # 2000, manufactured by Sankyo Seifun Co., Ltd.), 60 parts by weight of an acrylic resin emulsion (trade name: AE-322, manufactured by Japan Synthetic Rubber Co., Ltd.), 0, 5 parts by weight of a dispersant, and pH regulators, namely 0.05 parts by weight of sodium hydroxide and 2 parts by weight of 29% ammonia water, were coated in a quantity of 25 g / m 2 on the surface of a base paper (trade name: 80AF-P (D), manufactured by Nippon Paper Industries Co., Ltd.) having a basis weight of 80 g / m 2 and having been subjected to flame retardant treatment by means of a bar coater, thus making it possible to obtain
une base de revêtement mural.a wall covering base.
Exemple Comparatif 5 Une solution d'enduction, consistant en 15 parties en poids d'hydroxyde d'aluminium (marque de fabrique: HIGILITE H-42, fabriqué par Showa Denko K.K.), 85 parties en poids de carbonate de calcium (marque de fabrique: ESCALON #2000, fabriqué par Sankyo Seifun Co., Ltd.), parties en poids d'une émulsion de résine acrylique (marque de fabrique: AE-322, fabriquée par Japan Synthetic Rubber Co., Ltd.), 0,5 partie en poids d'un dispersant, et des régulateurs de pH, à savoir 0,05 partie en poids d'hydroxyde de sodium et 2 parties en poids d'une eau ammoniacale à 29%, a été appliquée en revêtement en une quantité de 28 g/m2 sur la surface d'un papier de base (marque de fabrique: 80AF-P(D), fabriqué par Nippon Paper Industries Co., Ltd.) ayant un grammage de 80 g/m2 et ayant été soumis à un traitement d'ignifugation par enduction à l'aide d'une enduiseuse à barre, permettant ainsi d'obtenir Comparative Example 5 A coating solution, consisting of 15 parts by weight of aluminum hydroxide (trade name: HIGILITE H-42, manufactured by Showa Denko KK), 85 parts by weight of calcium carbonate (trade name : ESCALAT # 2000, manufactured by Sankyo Seifun Co., Ltd.), parts by weight of an acrylic resin emulsion (trade name: AE-322, manufactured by Japan Synthetic Rubber Co., Ltd.), 0.5 part by weight of a dispersant, and pH regulators, namely 0.05 part by weight of sodium hydroxide and 2 parts by weight of a 29% ammonia water, was coated in an amount of 28 g / m.sup.2 on the surface of a base paper (trade name: 80AF-P (D), manufactured by Nippon Paper Industries Co., Ltd.) having a basis weight of 80 g / m 2 and having been subjected to flame retardant treatment by coating with a bar coater, thus obtaining
une base de revêtement mural.a wall covering base.
Les trois estimations suivantes ont été faites des bases de revêtement mural obtenues dans les Exemples et The following three estimates were made of the wall cladding bases obtained in the Examples and
Exemples Comparatifs.Comparative Examples.
1. Effet sur l'inhibition de l'évaporation de l'inhibition Une pâte d'amidon à 10% en poids (sous la forme d'une solution aqueuse) a été appliquée sur la surface arrière de chaque base de revêtement mural, que l'on a repliée sur elle-même avec les surfaces arrière en contact entre elles, puis qu'on a laissé reposer seule à 20 C et sous une humidité de 65% pendant 2 heures, pour estimer si elle était ou non apte à être collée sur un mur. Dans le Tableau 1, les bases de revêtement mural acceptables sont marquées par des cercles, et celles qui ne le sont pas, par 1. Effect on Inhibition of Evaporation of Inhibition A 10% by weight starch paste (in the form of an aqueous solution) was applied to the back surface of each wall covering base, which it was folded back on itself with the rear surfaces in contact with each other, then allowed to stand alone at 20 C and under a humidity of 65% for 2 hours, to estimate whether or not it was fit to be stuck on a wall. In Table 1, acceptable wall cladding bases are marked with circles, and those that are not, by
des croix.crosses.
2. Aptitude à l'imDression A l'aide d'une machine d'essai d'aptitude à l'impression en creux, fabriquée par Kumagai Riki Kogyo Co., Ltd., chaque base de revêtement mural a été soumise à une impression en creux pour effectuer une estimation visuelle de l'état dans lequel elle était imprimée. Dans le Tableau 1, les bases de revêtement mural bien imprimés sont marquées par des cercles, celles imprimées normalement par des 2. PRoJeCtIty With the aid of an intaglio printability testing machine, manufactured by Kumagai Riki Kogyo Co., Ltd., each wall covering base was printed. intaglio to make a visual estimate of the state in which it was printed. In Table 1, well-printed wallcovering bases are marked with circles, those normally printed by
triangles, et celles mal imprimées, par des croix. triangles, and those poorly printed, by crosses.
3. Iqnifugation L'ignifugation a été estimée conformément à JIS A1322. Dans le Tableau 1, les bases de revêtement mural d'ignifugation de seconde classe sont marquées par des 3. Fireproofing Fireproofing has been estimated in accordance with JIS A1322. In Table 1, second-class flame retardant wallcovering bases are marked by
cercles, et celles non acceptables, par des croix. circles, and those not acceptable, by crosses.
Tableau 1Table 1
Effet sur Aptitude à Ignifugation l'inhibition l'impression de l'évaporation Exemple 1 O O O Exemple 2 O O O Exemple 3 O O O Exemple x x O Comparatif 1 Exemple O x Comparatif 2 Exemple x O O Comparatif 3 Exemple x O O Comparatif 4 Exemple O O x Comparatif 5 Le Tableau i montre que les bases de revêtement mural conformes à la présente invention ont un caractère ignifuge et une aptitude à l'impression, et présentent un temps ouvert long par suite de l'inhibition de l'évaporation de l'humidité. Par ailleurs, aucune des bases de revêtement Effect on Ignition Ability Inhibition Printing of Evaporation Example 1 OOO Example 2 OOO Example 3 OOO Example xx O Comparative 1 Example O x Comparative 2 Example x OO Comparative 3 Example x OO Comparative 4 Example OO x Comparative 5 Table 1 shows that the wall-covering bases according to the present invention have a flame retardancy and printability, and have a long open time as a result of inhibition of moisture evaporation. Moreover, none of the coating bases
mural comparatives ne satisfait toutes les exigences. Wall-mounted comparatives do not meet all the requirements.
Conformément à la présente invention, il est possible de proposer de façon économique une base de revêtement mural, exempte de couche de chlorure de vinyle, qui présente un temps ouvert suffisamment long pour l'opération de collage, qui est attrayante une fois In accordance with the present invention, it is possible to economically provide a wallcovering base, free of vinyl chloride layer, which has an open time long enough for the bonding operation, which is attractive once.
imprimée, et qui présente un caractère ignifuge. printed, and which has a fireproof character.
Claims (1)