FR2649933A3 - Composite decoration and coating material - Google Patents
Composite decoration and coating material Download PDFInfo
- Publication number
- FR2649933A3 FR2649933A3 FR9009158A FR9009158A FR2649933A3 FR 2649933 A3 FR2649933 A3 FR 2649933A3 FR 9009158 A FR9009158 A FR 9009158A FR 9009158 A FR9009158 A FR 9009158A FR 2649933 A3 FR2649933 A3 FR 2649933A3
- Authority
- FR
- France
- Prior art keywords
- fabric
- article according
- microfibrous
- woven
- expanded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
MATERIAU COMPOSITE DE DECORATION ET DE REVETEMENTDECORATIVE AND COATING COMPOSITE MATERIAL
La présente invention concerne un article composite The present invention relates to a composite article
comprenant une couche d'un matériau microfibreux, non- comprising a layer of a microfibrous material, non-
tissé, utilisé avantageusement dans le domaine de la décoration intérieure et du revêtement. Les matériaux microfibreux, non-tissés, constitués par des microfibres de polyester ou de polyamide, par exemple des microfibres de Nylon-6, dans une matrice de polyuréthane, sont connus dans la technique. Parmi ces woven, advantageously used in the field of interior decoration and coating. Microfibrous, nonwoven materials consisting of polyester or polyamide microfibers, for example Nylon-6 microfibers, in a polyurethane matrix are known in the art. Among these
matériaux, ceux formés par des microfibres de poly- materials, those formed by poly-
(téréphtalate d'éthylène) dans une matrice de poly- (ethylene terephthalate) in a poly-
uréthane, constituent un produit valable, largement uti- urethane, constitute a valuable product, widely used
lisé, en particulier dans l'industrie de l'habillement, read, especially in the clothing industry,
grâce à ses caractéristiques excellentes en ce qui con- thanks to its excellent characteristics in terms of
cerne son aspect, sa "main" agréable, sa légèreté de poids, son velouté et à sa stabilité en présence de la outlines its appearance, its pleasant "hand", its light weight, its smoothness and its stability in the presence of
lumière et des oxydes d'azote présents dans l'atmos- light and nitrogen oxides present in the atmosphere
phère.phere.
Conformément à la présente invention, de tels maté- In accordance with the present invention, such materials
riaux microfibreux, non-tissés, sont accouplés à une couche d'une matière plastique expansée afin de donner des matériaux composites nouveaux dans lesquels un aspect esthétique extrêmement favorable se combine avec microfibrous, non-woven rials are coupled to a layer of an expanded plastic material in order to give new composite materials in which an extremely favorable aesthetic appearance is combined with
des caractéristiques qui rendent ces matériaux composi- characteristics that make these materials composi-
tes aptes à être utilisés dans le domaine de la décora- your suitable for use in the field of decoration
tion intérieure et dans le domaine du revêtement. interior and in the field of coating.
Conformément à ce qui précède, la présente inven- In accordance with the foregoing, the present invention
tion concerne un article composite particulièrement utile pour la décoration de murs et pour le revêtement de l'intérieur de moyens de transport, tels que des tion relates to a composite article particularly useful for decorating walls and for lining the interior of means of transport, such as
véhicules et des navires, cet article composite compre- vehicles and ships, this composite article comprises
nant une couche extérieure d'un tissu microfibreux, non- ning an outer layer of a microfibrous, non-
tissé, et une couche intérieure d'une matière plastique expansée. Dans la présente invention, on entend par le terme "microfibres" les fibres dont le titre est compris entre 0,01 denier et 0,40 denier, et de préférence de l'ordre woven, and an inner layer of foamed plastic. In the present invention, the term “microfibers” is understood to mean fibers whose titer is between 0.01 denier and 0.40 denier, and preferably of the order
de 0,08 à 0,15 denier.from 0.08 to 0.15 denier.
On peut obtenir le matériau microfibreux, non- We can get the microfibrous material, non-
tissé, formé par des microfibres de poly(téréphtalate d'éthylène) dans du polyuréthane au moyen d'un procédé comprenant d'une façon générale les étapes suivantes: - on imprègne un tissu non-tissé formé de microfibres de poly(téréphtalate d'éthylène) avec un élastomère polyuréthane; - on fait coaguler ledit élastomère polyuréthane afin de former une feuille composite microfibreuse; - on broie ladite feuille composite microfibreuse pour former un tissu brut microfibreux, non-tissé et - on teint ledit tissu brut microfibreux, non-tissé, woven, formed by microfibers of poly (ethylene terephthalate) in polyurethane by means of a process comprising generally the following steps: - impregnating a non-woven fabric formed of microfibers of poly (terephthalate of) ethylene) with a polyurethane elastomer; - Said polyurethane elastomer is coagulated in order to form a microfibrous composite sheet; - said microfibrous composite sheet is ground to form a raw microfibrous, non-woven fabric and - said raw microfibrous, non-woven fabric is dyed,
afin d'obtenir un produit final teint. in order to obtain a final dyed product.
On peut obtenir le tissu non-tissé en microfibres de poly(téréphtalate d'éthylène) à son tour à partir d'un feutre brut de fibres coupées, constitué par des microfibres de poly(téréphtalate d'éthylène) dans une matrice de polystyrène, ledit feutre brut étant soumis à un aiguilletage afin d'obtenir un feutre aiguilleté, ledit feutre aiguilleté étant traité tout d'abord avec une solution aqueuse de poly (alcool vinylique)piis avec du perchloroéthylène de manière à dissoudre la matrice de The nonwoven fabric of poly (ethylene terephthalate) microfibers can in turn be obtained from a raw felt of chopped fibers, consisting of poly (ethylene terephthalate) microfibers in a polystyrene matrix, said raw felt being subjected to needling in order to obtain a needled felt, said needled felt being treated first of all with an aqueous solution of poly (vinyl alcohol) then with perchlorethylene so as to dissolve the matrix of
polystyrène et à récupérer le tissu non-tissé en micro- polystyrene and to recover the non-woven fabric in micro-
fibres de poly(téréphtalate d'éthylène). poly (ethylene terephthalate) fibers.
Le matériau microfibreux, non-tissé, obtenu de cette façon, présente d'excellentes caractéristiques en ce qui concerne son aspect, son toucher, sa légèreté de poids, son velouté, sa stabilité en présence de la The microfibrous, non-woven material obtained in this way has excellent characteristics with regard to its appearance, its feel, its lightness of weight, its velvety, its stability in the presence of the
lumière et des oxydes d'azote présents dans l'atmos- light and nitrogen oxides present in the atmosphere
phère.phere.
En particulier, un tel matériau non-tissé, micro- In particular, such a nonwoven, micro-
fibreux, présente des caractéristiques tombant, d'une façon générale, dans la plage suivante de valeurs: - épaisseur (ASTM D-1910) de 0,6 à 0,9 mm poids par unité de surface de 170 à 250 g/m' - ténacité (ASTM D-1682) longitudinale de 5,0 à 9,0 kg/cm transversale de 3,0 à 6,0 kg/cm allongement jusqu'à rupture (ASTM D-1682) longitudinal de 65 à 80 % transversal de 110 à 130 % - résistance à la déchirure selon Elmendorf longitudinale de 2,3 à 1,5 kg transversale de 1,3 à 0,7 kg - stabilité en présence de la lumière (80 SHF; échelle des gris; AATCC 16A 1964) de 6 à 7 - stabilité en présence des oxydes d'azote atmosphériques (1 cycle; AATCC 23 1975) de 3 à 5 fibrous, has characteristics generally falling within the following range of values: - thickness (ASTM D-1910) 0.6 to 0.9 mm weight per unit area from 170 to 250 g / m ' - tenacity (ASTM D-1682) longitudinal from 5.0 to 9.0 kg / cm transverse from 3.0 to 6.0 kg / cm elongation until break (ASTM D-1682) longitudinal from 65 to 80% transverse from 110 to 130% - tear resistance according to Elmendorf longitudinal from 2.3 to 1.5 kg transverse from 1.3 to 0.7 kg - stability in the presence of light (80 SHF; gray scale; AATCC 16A 1964 ) from 6 to 7 - stability in the presence of atmospheric nitrogen oxides (1 cycle; AATCC 23 1975) from 3 to 5
Selon la présente invention, un tel matériau micro- According to the present invention, such a micro-material
fibreux, non-tissé, ou des matériaux microfibreux, non- fibrous, nonwoven, or microfibrous, non-
tissés, similaires, est(sont) accouplé(s) à une couche d'une matière plastique expansée afin de former des matériaux nouveaux, utilisés avantageusement dans les woven fabrics, similar, is (are) coupled to a layer of an expanded plastic material in order to form new materials, advantageously used in
domaines mentionnés ci-dessus.areas mentioned above.
Plus particulièrement, dans un mode de réalisation More particularly, in one embodiment
pratique de la présente invention, le matériau micro- practice of the present invention, the micro-material
fibreux, non-tissé, est accouplé à une matière plastique expansée au moyen d'un traitement à la flamme ou au fibrous, nonwoven, is coupled to a foamed plastic material by means of flame or flame treatment.
moyen de l'interposition d'un agent adhésif. by means of the interposition of an adhesive agent.
Les matières plastiques expansées avantageuses dans le but envisagé peuvent être sélectionnées parmi une large catégorie de matières, telles que, par exemple, les polyuréthanes, les polyéthers, les polyoléfines et le polystyrène. En règle générale, l'épaisseur de la couche de la matière expansée peut être comprise entre 2 et 10 mm, et la matière expansée peut être dotée de caractéristiques ignifuges, peut être soudée à chaud, ou peut ou non ne pas être pourvue d'une couche adhésive selon ce que l'on désire ou ce qui est nécessaire, en fonction de l'utilisation particulière envisagée. Les articles composites ainsi obtenus conviennent pour la décoration de murs, ou pour le revêtement de l'intérieur de moyens de transport, par exemple pour revêtir les surfaces intérieures des cabines de véhicules, et les The foamed plastics preferred for the intended purpose can be selected from a wide category of materials, such as, for example, polyurethanes, polyethers, polyolefins and polystyrene. Generally, the layer thickness of the foamed material may be between 2 and 10 mm, and the foamed material may be provided with flame retardant characteristics, may be heat-welded, or may or may not not be provided with. an adhesive layer according to what is desired or what is necessary, depending on the particular use envisaged. The composite articles thus obtained are suitable for decorating walls, or for coating the interior of means of transport, for example for coating the interior surfaces of vehicle cabins, and
surfaces de l'intérieur d'un navire. Dans ces applica- surfaces of the interior of a ship. In these applications
tions, les articles selon la présente invention présen- tions, the articles according to the present invention present
tent de très bonnes propriétés d'amortissement et have very good damping properties and
d'insonorisation ainsi que des caractéristiques de con- soundproofing as well as con
tact et de toucher agréables.pleasant tact and touch.
Selon un autre mode de réalisation pratique de la présente invention, on étale sur la face arrière du According to another practical embodiment of the present invention, it is spread over the rear face of the
matériau microfibreux, non-tissé, une émulsion de poly- microfibrous material, non-woven, an emulsion of poly-
uréthane au moyen d'une lame docteur afin de fabriquer urethane using a doctor blade to make
des articles composites rigides. Selon une autre techni- rigid composite articles. According to another technique
que, on accouple & la flamme une mousse de polyuréthane avec une couche d'un matériau microfibreux, non-tissé, et avec un film imperméable à l'eau afin d'obtenir des articles composites souples, dans lesquels l'épaisseur that a polyurethane foam is coupled to the flame with a layer of a microfibrous, non-woven material and with a waterproof film in order to obtain flexible composite articles, in which the thickness
de la couche de polyuréthane est de l'ordre de 2 & 8 mm. of the polyurethane layer is of the order of 2 & 8 mm.
De toute façon, les articles obtenus conviennent pour revêtir les parois intérieures des parties internes des véhicules, telles que les cabines, les portes et les In any case, the articles obtained are suitable for coating the interior walls of the internal parts of vehicles, such as cabins, doors and windows.
tableaux de bord.Dashboards.
Selon encore un autre mode de réalisation pratique, on accouple le matériau microfibreux, non-tissé, avec un tissu au moyen de la technique "multipoints" et on accouple à la flamme le produit ainsi obtenu avec une mousse de polyuréthane d'une épaisseur comprise entre 2 et 10 mm puis avec un tissu tricoté léger. Dans ce cas According to yet another practical embodiment, the microfibrous, non-woven material is coupled with a fabric by means of the "multipoint" technique and the product thus obtained is coupled to the flame with a polyurethane foam of a thickness included. between 2 and 10 mm then with a light knitted fabric. In that case
également, on obtient des articles composites qui con- also, composite articles are obtained which con-
viennent avantageusement pour les revêtements internes come advantageously for internal coatings
de véhicules.vehicles.
D'autres exemples encore d'articles composites Still other examples of composite articles
selon la présente invention sont constitués par les com- according to the present invention are constituted by the components
binaisons suivantes:following pairings:
- matériau microfibreux, non-tissé / matière plasti- - microfibrous material, non-woven / plastic material -
que expansée / tissu;as expanded / fabric;
- matériau microfibreux, non-tissé / matière plasti- - microfibrous material, non-woven / plastic material -
que expansée / tissu tricoté léger; - matériau microfibreux, non-tissé / tissu tricoté léger / matière.plastique expansée / tissu tricoté léger; et - matériau microfibreux, non-tissé / tissu / matière as foamed / lightweight knitted fabric; - microfibrous material, non-woven / light knitted fabric / expanded plastic material / light knitted fabric; and - microfibrous material, non-woven / fabric / material
plastique expansée / tissu.expanded plastic / fabric.
Les tissus peuvent être en coton, en polyester, en Fabrics can be cotton, polyester,
Nylon en fibres ou en fibres mélangées, et un ou plu- Nylon of fibers or mixed fibers, and one or more
sieurs composants du matériau composite peuvent être its components of the composite material can be
dotés de caractéristiques ignifuges. En outre, le maté- with flame retardant characteristics. In addition, the material
riau microfibreux, non-tissé, peut être perforé, cousu, microfibrous, non-woven, can be perforated, sewn,
tondu, imprimé ou gaufré.cropped, printed or embossed.
Dans les exemples expérimentaux ci-après, comme matériau microfibreux, non-tissé, on utilise le produit In the experimental examples below, as the microfibrous, non-woven material, the product is used
vendu sur le marché sous la marque déposée de MASTER- sold in the market under the registered trademark of MASTER-
COVER par la compagnie ALCANTARA, et présente les carac- COVER by the company ALCANTARA, and presents the charac-
téristiques suivantes: - épaisseur de 0,6 à 0,9 mm - poids par unité de surface de 170 à 230 g/m2 - ténacité longitudinale de 5,0 à 9,0 kg/cm transversale de 3,0 à 6,0 kg/cm - allongement longitudinal de 65 à 80 % transversal de 110 à 130 % - stabilité en présence de la lumière de 6 à 7 - stabilité en présence des oxydes d'azote de 3 à 5 En outre, un tel produit synthétique microfibreux a un aspect plaisant, un velouté épais et naturel et une following characteristics: - thickness from 0.6 to 0.9 mm - weight per unit area from 170 to 230 g / m2 - longitudinal tenacity from 5.0 to 9.0 kg / cm transverse from 3.0 to 6.0 kg / cm - longitudinal elongation from 65 to 80% transverse from 110 to 130% - stability in the presence of light from 6 to 7 - stability in the presence of nitrogen oxides from 3 to 5 In addition, such a microfibrous synthetic product has a pleasant appearance, a thick and natural velvety texture and a
aptitude à la teinture exempte de défauts. dyeability free from defects.
Exemple 1Example 1
Au cours d'un premier essai, on a accouplé à la flamme le matériau microfibreux, non-tissé, présentant les caractéristiques mentionnées dans le présent exposé avec une couche de polyuréthane expansé d'une épaisseur de 3 à 6 mm. Au cours d'un second essai, on a étalé au moyen d'une lame docteur un agent adhésif sur la face During a first test, the microfibrous, non-woven material having the characteristics mentioned in the present description was coupled to the flame with a layer of foamed polyurethane with a thickness of 3 to 6 mm. In a second test, an adhesive agent was spread over the face with a doctor blade.
arrière du matériau microfibreux, non-tissé, on a accou- back of the microfibrous, non-woven material, we delivered
plé ce matériau avec une couche de polyuréthane expansé du type décrit en détail ci-dessus et on a fait passer pleated this material with a layer of expanded polyurethane of the type described in detail above and passed
le matériau composite ainsi obtenu à travers un disposi- the composite material thus obtained through a device
tif de calandrage puis on l'a fait sécher dans un four à air. Dans les deux cas, on a obtenu un article composite ayant un aspect agréable, possédant des propriétés d'amortissement et d'insonorisation ainsi qu'un toucher et une "main" agréables. Il convient particulièrement pour décorer des murs et pour revêtir l'intérieur de calender and then dried in an air oven. In both cases, there was obtained a composite article having a pleasant appearance, possessing damping and soundproofing properties as well as a pleasant feel and "hand". It is particularly suitable for decorating walls and for lining the interior of
moyens de transport, en particulier de navires. means of transport, in particular ships.
Exemple 2Example 2
Au cours d'un premier essai, on a étalé sur la face During a first test, we spread on the face
arrière du matériau microfibreux, non-tissé, une émul- back of the microfibrous, non-woven material, an emul-
sion de polyuréthane au moyen d'une machine d'étalement à trois têtes afin de former un film d'un poids de 30 à polyurethane sizing by means of a three-head spreading machine to form a film with a weight of 30 to
g/m2. Au cours d'un second essai une mousse de poly- g / m2. During a second test, a poly-
uréthane de 3 à 6 mm et d'une densité de 28-50 kg/m3 a été accouplée, sur une de ses faces, avec le matériau microfibreux, non-tissé, et sur son autre face, avec un film de polyuréthane imperméable à l'eau. De cette façon, on a obtenu des articles composites avantageux urethane of 3 to 6 mm and a density of 28-50 kg / m3 has been coupled, on one side, with the microfibrous material, non-woven, and on its other side, with a polyurethane film impermeable to the water. In this way, advantageous composite articles were obtained.
pour la production de composants rigides et souples res- for the production of rigid and flexible components res-
pectifs qui conviennent pour revêtir l'intérieur des pectives suitable for coating the interior of
véhicules.vehicles.
Exemple 3Example 3
On accouple le matériau microfibreux, non-tissé, au moyen du système "multipoints" avec un tissu mixte coton-polyester. On traite ensuite le matériau composite sur une machine d'accouplement à la flamme à double tête. Pendant le passage de la première tête, ledit matériau est accouplé à une mousse de polyuréthane ayant une épaisseur de 3-6 mm et une densité de 24-50 kg/m3 et lors du passage de la seconde tête, le matériau est accouplé à la flamme avec un tissu tricoté léger en The microfibrous, non-woven material is coupled by means of the "multipoint" system with a mixed cotton-polyester fabric. The composite material is then processed on a double head flame coupling machine. During the passage of the first head, said material is coupled to a polyurethane foam having a thickness of 3-6 mm and a density of 24-50 kg / m3 and during the passage of the second head, the material is coupled to the flame with a lightweight knitted fabric
poly(téréphtalate d'éthylène) doté de propriétés élasti- poly (ethylene terephthalate) with elastic properties
ques aussi bien dans le sens longitudinal que dans le as well in the longitudinal direction as in the
sens transversal (c'est-à-dire un tissu tricoté bi- transverse direction (that is, a two-way knitted fabric
élastique). Le matériau composite peut être utilisé pour elastic). Composite material can be used for
des applications similaires à celles de l'Exemple 2. applications similar to those of Example 2.
Claims (12)