FR2464318A3 - TISSUE FABRIC WITH TEXTURE A MULTICOMPONENT - Google Patents

TISSUE FABRIC WITH TEXTURE A MULTICOMPONENT Download PDF

Info

Publication number
FR2464318A3
FR2464318A3 FR8018720A FR8018720A FR2464318A3 FR 2464318 A3 FR2464318 A3 FR 2464318A3 FR 8018720 A FR8018720 A FR 8018720A FR 8018720 A FR8018720 A FR 8018720A FR 2464318 A3 FR2464318 A3 FR 2464318A3
Authority
FR
France
Prior art keywords
filaments
matrix
yarns
individual
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR8018720A
Other languages
French (fr)
Other versions
FR2464318B3 (en
Inventor
Eberhard Kratzsch
Reiner Modtler
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Akzo NV
Original Assignee
Akzo NV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Akzo NV filed Critical Akzo NV
Publication of FR2464318A3 publication Critical patent/FR2464318A3/en
Application granted granted Critical
Publication of FR2464318B3 publication Critical patent/FR2464318B3/fr
Granted legal-status Critical Current

Abstract

BANDE DE TISSU EN FILE TEXTURE A MULTICOMPOSANTS. TISSU TEXTILE, COMPOSE EN CHAINE ET EN TRAME DE FIL A MULTIFILAMENTS TEXTURE, SE COMPOSANT POUR LEUR PART DE FILAMENTS DU TYPE A MATRICE ET A SEGMENTS. LES FILAMENTS SONT SUBDIVISES, DANS LE TISSU, EN LEURS COMPOSANTS MATRICE ET SEGMENTS, LES FILS A MULTIFILAMENTS PRESENTANT A DES INTERVALLES IRREGULIERS DES NOEUDS DE SOUDAGE ENGLOBANT LA TOTALITE OU UNE PARTIE SEULEMENT DE LA SECTION DES DIFFERENTS FILS.MULTI-COMPONENT TEXTURED MESH FABRIC STRIP. TEXTILE FABRIC, COMPOSED OF A CHAIN AND A WEFT WITH A MULTIFILAMENT TEXTURE, CONSISTING FOR THEIR PART OF FILAMENTS OF THE MATRIX AND SEGMENT TYPE. THE FILAMENTS ARE SUBDIVIDED IN THE FABRIC INTO THEIR MATRIX AND SEGMENT COMPONENTS, THE MULTIFILAMENT WIRES SHOWING IRREGULAR INTERVALS OF WELDING KNOTS INVOLVING ALL OR ONLY PART OF THE SECTION OF THE VARIOUS WIRES.

Description

Bande de tissu en filé texturé à multicomposants.Multicomponent textured yarn fabric web.

L'invention concerne une bande de tissu composée de fils à multifilaments, qui, pour leur part, se composent de fibres à multicomposants, essentiellement subdivisées, du type à matrice et à segments qui présentent, à des intervalles irréguliers, des points de soudure agissant sur la totalité ou une partie de la section transversale de chacun des fils  The present invention relates to a fabric web of multifilament yarns, which in turn consist of essentially subdivided, matrix-type and segmented multicomponent fibers having weld points at irregular intervals. on all or part of the cross-section of each wire

individuels à multifilaments.individual multifilaments.

On connaît déjà des fils constitués de filaments individuels du type à multicomposants à matrice et à segments, grâce aux brevets allemands n' 28 03 136 et 28 09 346. Ces fils se composent d'au moins deux polymères différents, qui présentent des comportements très différents l'un de l'autre pour ce qui est du rétrécissement (contraction, retrait). Le déclenchement du rétrécissement (différent pour les deux  Yarns consisting of individual multicomponent matrix and segment type filaments are already known from German Pat. Nos. 28 03 136 and 28 09 346. These yarns consist of at least two different polymers, which exhibit very different behaviors. different from each other with respect to narrowing (contraction, withdrawal). Shrink initiation (different for both

polymères) permet d'atteindre une séparation totale ou partiel-  polymers) makes it possible to achieve total or partial separation

le des composants.the components.

L'on a constaté que, dans certaines conditions, la textu-  It has been found that, under certain conditions, textual

ration par fausse torsion de fils du type décrit ci-dessus permettait d'obtenir des effets surprenants, grâce au choix  false twist of yarns of the type described above made it possible to obtain surprising effects, thanks to the choice

convenable des polymères utilisés et des conditions de textu-  suitable polymers and textual conditions.

ration. Les fils traités pai texturation par fausse torsion et appartenant au type décrit ci-dessus sont, à titre d'exemple, particulièrement adaptés pour être utilisés dans des matériaux textiles en nappe. En particulier leur utilisation pour des tissus conduits à des effets nouveaux et exceptionnels pour ce qui concerne l'aspect, le toucher et le comportement au  ration. The false twist textured yarns of the type described above are, by way of example, particularly suitable for use in web textile materials. In particular their use for tissues led to new and exceptional effects with regard to appearance, touch and

porter.carry.

L'invention a pour but de créer une bande de tissu en  The object of the invention is to create a web of fabric

fils texturés par fausse torsion et composés de filaments indi-  false-twist textured yarns and filament

viduels du type à multicomposants à matrice et à segments, permettant d'obtenir, à l'état prêt à l'emploi, un toucher  Multicomponent matrix and segment type videcs to achieve a ready-to-use touch

exceptionnel et nouveau, un bon aspect et d'excellentes pro-  exceptional and new, a good appearance and excellent

priétés au porter.worn to wear.

L'invention concerne à cet effet une bande de tissu, composée de fils à multifilaments, qui, pour leur part, se  The invention relates, for this purpose, to a web of fabric composed of multifilament yarns which, for their part, is

composent de fibres à multicomposants essentiellement subdi-  composed of multicomponent fibers essentially subdivided

visées, du type à matrice et à segments, et présentant à des intervalles irréguliers des points de soudure concernant la totalité ou une partie seulement de la section transversale de chaque fil individuel à multifilaments, cette bande de tissu étant caractérisée en ce que la chaîne et la trame sont  of the matrix and segment type, and having at irregular intervals weld points for all or only part of the cross-section of each individual multifilament yarn, said web being characterized in that the warp and the frame are

composées de fils d'aspect essentiellement indentique, pré-  composed of threads of essentially identical appearance,

sentant chacun un titre d'environ 35 à 120 dtex, et des filaments individuels de la partie segments de respectivement quatre à huit fois 0, 2 dtex à 1,2 dtex,les fils individuels à multifilaments présentant environ 3 à 80 noeuds ou points de soudure par mètre, concernant la totalité ou une partie seulement de la section transversale de chaque fil individuel  each having a title of about 35 to 120 dtex, and individual filaments of the segment portion of four to eight times respectively 0.2 dtex to 1.2 dtex, the individual multifilament yarns having about 3 to 80 knots or dots. solder per meter, in respect of all or only part of the cross section of each individual wire

à multifilaments.multifilament.

D'une manière avantageuse, les fils individuels à multi-  Advantageously, the individual son with multiple

filaments utilisés pour la chaîne et la trame présentent un titre d'environ 40 à 80 dtex, les filaments individuels étant des filaments du type à matrice et à segments, essentiellement subdivisés en leurs composants matrice et segments, ces filaments présentent, avant leur subdivision, six segments séparés les uns des autres par une matrice en forme d'étoile, le rapport des sections de la matrice et des segments dans la section non subdivisée du filament individuel étant comprise entre environ 15: 85 et 45: 55, et le titre individuel des différents segments se trouvant entre les noeuds de soudure étant compris entre environ 0,35 et 1,1 dtex. D'une manière avantageuse, le nombre de noeuds de soudage présentés par les différents fils à multifilaments est compris, sur le tissu fini, entre environ 10 et 75 par mètre. Le tissu peut être  filaments used for the warp and weft have a title of about 40 to 80 dtex, the individual filaments being matrix and segment type filaments, essentially subdivided into their matrix and segment components, these filaments have, before their subdivision, six segments separated from one another by a star-shaped matrix, the ratio of the sections of the matrix and segments in the undivided section of the individual filament being between about 15:85 and 45:55, and the individual title different segments lying between the solder nodes being between about 0.35 and 1.1 dtex. Advantageously, the number of welding knots presented by the various multifilament yarns is comprised, on the finished fabric, of between approximately 10 and 75 per meter. The fabric can be

réalisé en armure, toile ou sergé.  made of weave, canvas or twill.

Une réalisation particulièrement intéressante de l'invention consiste en une bande de tissu textile du type décrit ci-dessus, dans laquelle les fils utilisés pour la chaine et la trame se coirposent de filaments individuels du type à matrice et à segments qui contiennent en tant que matrice 20% de polyamide 6, et, en tant que segments chacun au total 80% de téréphtalate de polyéthylène, subdivisés en six segments individuels séparés les uns des autres par une matrice en forme d'étoile à six branches, le titre individuel des fils à multifilaments étant de 50 dtex pour 15 filaments, et la chaîne présente 30 à 68 fils par cm, et la trame 30 à 44 fils par cm, la densité des noeuds de soudage, dans le tissu fini, étant d'environ 5 à 75 noeuds par mètre, tant sur les fils de chaîne que sur les fils de trame. De préférence, le tissu textile a une armure toile. Le compte des fils peut alors être d'environ 30 à 48 fils par cm dans la chaîne et d'environ 28 à  A particularly advantageous embodiment of the invention consists of a textile fabric strip of the type described above, in which the warp and weft yarns are made of individual matrix and segment type filaments which contain as matrix 20% polyamide 6, and, as segments each in total 80% polyethylene terephthalate, subdivided into six individual segments separated from each other by a star-shaped six-branched matrix, the individual threads with multifilaments being 50 dtex for 15 filaments, and the warp has 30 to 68 yarns per cm, and weft 30 to 44 yarns per cm, the density of the knots in the finished fabric being about 5 to 75 knots per meter, both on warp and weft threads. Preferably, the textile fabric has plain weave. The thread count can then be about 30 to 48 threads per cm in the warp and about 28 to

46 fils dans la trame.46 sons in the frame.

Une autre réalisation avantageuse de la bande de tissu selon l'invention présente en chaîne et en trame des fils individuels à multifilaments, du type à matrice et à segments, le titre de chaque fil à multifilaments étant de 76 dtex pour à 24 filaments individuels du type à matrice et à segments, le compte des fils dans le tissu étant d'environ 28 à 50 fils par cm pour la chaîne et d'environ 25 à 40-fils par cm pour la trame. Dans une autre réalisation préférée, l'on utilise pour la chaîne des fils du type décrit ci-dessus et présentant un titre de 50 dtex pour 15 filaments, la trame utilisant des fils de 76 dtex pour 20 à 24 filaments; il s'est avéré que le compte préféré des fils était d'environ 30 à 68 fils par cm  Another advantageous embodiment of the fabric strip according to the invention has, in warp and weft, individual multifilament yarns, of the matrix and segment type, the title of each multifilament yarn being 76 dtex for 24 individual filaments of matrix and segment type, the count of yarns in the fabric being about 28 to 50 threads per cm for the warp and about 25 to 40 threads per cm for the weft. In another preferred embodiment, yarns of the type described above having a titer of 50 dtex for 15 filaments are used for the warp, the weft using yarns of 76 dtex for 20 to 24 filaments; it turned out that the preferred count of the threads was about 30 to 68 threads per cm

dans la chaîne et d'environ 25 à 40 fils par cm dans la trame.  in the warp and about 25 to 40 threads per cm in the weft.

Dans use autre réalisation de l'invention, la chaîne est formée de fils formés de filaments du type à matrice et à segments  In another embodiment of the invention, the chain is formed of threads formed of matrix and segment type filaments.

avec un titre de 76 dtex pour 20 à 24 filaments. La trame pos-  with a titre of 76 dtex for 20 to 24 filaments. The plot

sédant-des fils d'environ 100 à 110 dtex, pour un compte d'environ 28 à 50 fils par cm pourla chaîne et d'environ 22 à fils par cm pour la trame. Dans ce cas, les fils de titre dtex peuvent aussi être formés non pas de 15 filaments du type à matrice et à segments, mais par exemple de 12 à 20  sedant-threads of about 100 to 110 dtex, for an count of about 28 to 50 threads per cm for the warp and about 22 to threads per cm for the weft. In this case, the dtex title yarns may also be formed not of matrix and segment type filaments, but for example from 12 to 20

filaments du type à matrice et à segments.  filaments of the matrix and segment type.

Il s'est avéré que les propriétés de la bande de tissu selon l'invention, prête à l'emploi, dépendent essentiellement du titre individuel des différents segments des filaments, ainsi que de la densité, de la répartition et de la nature des noeuds de soudage, qui relient les filaments du type à matrice et à segments, subdivisés en leurs composants, sur la totalité ou une partie seulement de la section des fils; de cette manière, la structure individuelle des fils se maintient  It has been found that the properties of the fabric strip according to the invention, ready for use, depend essentially on the individual title of the different segments of the filaments, as well as the density, distribution and nature of the knots. welding machines, which connect the matrix and segment type filaments, subdivided into their components, over all or only part of the section of the wires; in this way, the individual structure of the wires is maintained

24643 1824643 18

dans le tissu fini, bien que cela ne soit pas visible d'après l'aspect. Lé toucher du tissu fini peut varier entre de larges limites grâce au choix du nombre de noeuds de soudage, et il  in the finished fabric, although this is not visible from the appearance. The touch of the finished fabric can vary between wide limits thanks to the choice of the number of knots of welding, and it

s'est avéré que les bandes de tissu selon l'invention présen-.  It has been found that the fabric strips according to the invention are present.

taient un toucher très proche de la soie, en particulier sous  were a touch very close to the silk, especially under

la forme décrite ci-dessus comme étant particulièrement intéres-  the form described above as being particularly interesting

sante. Le nombre des noeuds de soudage créés lors du traitement  health. The number of welding nodes created during processing

de texturation et restant dans le tissu fini dépend non seu-  texturing and remaining in the finished fabric depends not only on

lement de la structure du matériau utilisé pour la constitu-  the structure of the material used for

tion des filaments du type à matrice et à segments, mais surtout, et dans une grande mesure, de la température de fixation utilisée lors du processus de texturation et du temps de séjour dans le dispositif de fixation. Il s'est avéré que des températures comprises entre environ 212 et 2250C, lors de l'utilisation du polyamide 6 en tant que matériau pour la matrice et de téréphtalate de polyéthylène en tant que matériau pour lessegments, étaient particulièrement avantageuses, des températures de fixation comprises entre environ 214 et environ 2250C étant importantes, en particulier pour les traitements  the matrix and segment type filaments, but especially, and to a large extent, the fixing temperature used during the texturing process and the residence time in the fastener. It has been found that temperatures between about 212 ° C and 22 ° C, when using polyamide 6 as a matrix material and polyethylene terephthalate as the material for the segments, were particularly advantageous, fixing temperatures. from about 214 to about 2250C being important, particularly for

sur des matériels de tissage travaillant à grande vitesse.  on weaving equipment working at high speed.

De plus, un traitement de la bande textile à l'aide d'un solvant abaissant la température de rétrécissement nul du ou des polymères utilisés pour les segments d'au moins 1000C, ce traitement étant exécuté après la fabrication de là bande textile, joue un rôle particulièrement important; ce solvant est de préférence le chlorure de méthylène. Dans ce type de traitement, le processus de subdivision des filaments du type à matrice et à segments, déjà amorcé lors de la texturation des fils individuels, est conduit à son terme. Par-ailleurs, on assiste à une ouverture d'une partie des noeuds existant lors du traitement, qui facilitent la transformation et le traitement et qui rendent inutile l'encollage ou tout autre traitement destiné à obtenir un fil "fermé", permettant ainsi d'obtenir un toucher agréable et les caractéristiques préférées  In addition, treatment of the textile strip with a solvent lowering the zero shrinkage temperature of the polymer or polymers used for segments of at least 1000C, this treatment being performed after the manufacture of the textile strip, plays a particularly important role; this solvent is preferably methylene chloride. In this type of treatment, the process of subdivision of the matrix and segment type filaments, already initiated during the texturing of the individual threads, is completed. Moreover, there is an opening of a portion of the existing nodes during processing, which facilitate processing and processing and that make it unnecessary sizing or other treatment to obtain a "closed" wire, thus allowing 'get a nice touch and favorite features

d'aspect et de comportement au porter.  appearance and wearing behavior.

L'invention sera mieux comprise en regard des micro-  The invention will be better understood with regard to micro-

graphies annexées, qui représentent un exemple de réalisation  appended graphs, which represent an example of

de l'invention.of the invention.

Les micrographies ont été obtenues au microscope électro-  The micrographs were obtained by electron microscopy

nique à balayage, et présentent un exemple du tissu selon l'invention avant et après le traitement avec le solvant, par exemple le chlorure de méthylène.  and an example of the fabric according to the invention before and after the treatment with the solvent, for example methylene chloride.

Les figures 1 et 2 représentent un tissu selon l'inven-  Figures 1 and 2 show a fabric according to the invention

tion, respectivement à l'échelle 50: 1 et 100:1, avant le  at 50: 1 and 100: 1, respectively, before

traitement au solvant.solvent treatment.

Les figures 3 et 4 présentent le même tissu, respecti-  Figures 3 and 4 show the same fabric, respectively

vement à l'échelle 50: 1 et 100: 1, mais après le traitement  50: 1 and 100: 1, but after treatment

au solvant.to the solvent.

Bien entendu, l'invention n'est pas limitée aux exemples de réalisation ci-dessus décrits et représentés, à partir desquels on pourra prévoir d'autres modes et d'autres formes  Of course, the invention is not limited to the embodiments described above and shown, from which we can provide other modes and other forms.

de réalisation, sans pour cela sortir du cadre de l'invention.  embodiment, without departing from the scope of the invention.

Claims (12)

REVENDICATIONS 1. Bande de tissu formée de fils à multifilaments qui, pour leur part, se composent de fibres à multicomposants, essentiellement subdivisées du type à matrice -et. segments, et présentant à des intervalles irréguliers des points de soudage portant sur la totalité ou une partie seulement de  1. Fabric strip formed of multifilament yarns, which, for their part, consist of multicomponent fibers, essentially subdivided matrix type -and. segments, and having at irregular intervals weld points for all or part of la section de chacun des fils à multifilaments, bande carac-  the section of each of the multifilament yarns, which is térisée en ce que la chaîne et la trame du tissu sont composées de fils ayant essentiellement le même aspect présentant chacun un titre d'environ 35 à 120 dtex et des filaments individuels de la partie segments de respectivement quatre à huit fois 0,2 à 1,2 dtex, les différents fils à multifilaments possédant entre environ 3 et 80 noeuds de soudage par mètre englobant la totalité ou une partie seulement de la section de chaque fil.  characterized in that the warp and weft of the fabric are composed of yarns having substantially the same appearance each having a title of about 35 to 120 dtex and individual filaments of the segment portion of respectively four to eight times 0.2 to 1 , 2 dtex, the various multifilament yarns having between about 3 and 80 knots of welding per meter including all or only part of the section of each wire. 2. Bande de tissu selon la revendication 1, caractérisée en ce que les fils individuels à multifilaments contenus à la fois dans la chatne et dans la trame présentent un titre d'environ 40 à 80 dtex, les filaments individuels étant des filaments essentiellement subdivisés en leurs composants2. Fabric web according to claim 1, characterized in that the individual multifilament yarns contained in both the chat and the weft have a titer of about 40 to 80 dtex, the individual filaments being filaments substantially subdivided into their components matrice et segments, ces filaments présentant, avant la sub-  matrix and segments, these filaments having, before the sub- division, six- segments séparés les uns des autres par une matrice en forme d'étoile, le rapport des sections de la matrice et des segments dans la section non-subdivisée du filament étant d'environ 15: 85 à 45, et le titre individuel des segments se trouvant sous la forme de fibres individuelles entre les noeuds de soudage étant compris entre environ 0, 35 et  division, six-segments separated from each other by a star-shaped matrix, the ratio of the sections of the matrix and segments in the undivided section of the filament being from about 15: 85 to 45, and the title individual segments in the form of individual fibers between the welding knots being between about 0.35 and 1,1 dtex.1.1 dtex. 3. Bande de tissu selon la revendication 1 ou 2, carac-  3. Fabric web according to claim 1 or 2, characterized térisée en ce que le nombre des noeuds de soudage dans les * fils à multifilaments est en moyenne compris entre environ 10  characterized in that the number of welding knots in the multifilament yarns is on average between about 10 et 75 par mètre.and 75 per meter. 4. Bande de tissu selon l'une quelconque des revendica-  4. Fabric strip according to any one of the claims tions 1 ou 2, caractérisée en ce que le nombre des noeuds de soudage dans les fils à multifilaments est compris entre  1 or 2, characterized in that the number of welding knots in the multifilament yarns is between environ 5 et 65 par mètre.about 5 and 65 per meter. 5. Bande de tissu selon l'une quelconque des revendi-  5. Fabric web according to any of the claims cations 1 à 4, caractérisée en ce qu'elle est réalisée avec une armure toile.  cations 1 to 4, characterized in that it is carried out with a plain weave. 6. Bande de tissu selon l'une quelconque des revendi-  6. Fabric web according to any of the claims cations 1 à 4, caractérisée en ce qu'elle est réalisée en  cations 1 to 4, characterized in that it is carried out in armure sergé.twill weave. 7. Bande de tissu selon l'une quelconque des revendi-  7. Fabric web according to any of the claims cations 1 à 6, caractérisée en ce que le compte de fils dans la chaîne est compris entre environ 30 et environ 80 fils par  1 to 6, characterized in that the yarn count in the warp is from about 30 to about 80 threads per cm, ce compte étant d'environ 26 à 56 fils par cm dans la trame.  cm, this count being about 26 to 56 threads per cm in the weft. 8. Bande de tissu selon l'une quelconque des revendica-  8. Fabric strip according to any one of the claims tions 1 à 7, caractérisée en ce que les fils utilisés pour la chaîne et la trame sont formés de filaments individuels du type à matrice et à segments, qui contiennent environ 20% de polyamide 6 en tant que matrice et au total environ 80% de téréphtalate de polyéthylène en tant que segments subdivisés en six segments individuels séparés les uns des autres par la matrice centrale en forme d'étoile à six branches, que le titre individuel desdits fils à multifilaments est d'environ dtex pour 15 filaments, la chaîne possédant 30 à 68 fils par cm et la trame 30 à 44 fils par cm, et la densité des noeuds de soudage dans le tissu fini étant d'environ 10 à 75 noeuds par mètre de longueur de fil, tant dans les fils à  1 to 7, characterized in that the warp and weft yarns are formed from individual matrix and segment type filaments which contain about 20% polyamide 6 as a matrix and in total about 80% of polyethylene terephthalate as segments subdivided into six individual segments separated from each other by the six-pointed star-shaped central matrix, that the individual titer of said multifilament yarns is about dtex for 15 filaments, the chain possessing 30 to 68 yarns per cm and the weft 30 to 44 yarns per cm, and the density of the knots of welding in the finished fabric being about 10 to 75 knots per meter of yarn length, both in yarns to multifilaments de chaîne que de trame.  multifilament warp only weft. 9. Bande de tissu selon la revendication 8, caractérisée en ce que le titre individuel des fils est d'environ 76 dtex pour 20 à 24 filaments du type à matrice et à segments, le compte des fils dans le tissu étant d'environ 28 à 50 fils par cm pour la chaîne et d'environ 25 à 40 fils par cm pour la trame.  Fabric web according to claim 8, characterized in that the individual thread count is about 76 dtex for 20 to 24 matrix and segment type filaments, the count of yarns in the fabric being about 28 at 50 threads per cm for the warp and about 25 to 40 threads per cm for the weft. 10. Bande de tissu selon l'une quelconque des revendica-  10. Fabric strip according to any one of the claims tions 1 à 6, caractérisée en ce que les fils individuels à filaments du type à matrice et à segments présentent pour la chaîne un titre d'environ 50 dtex pour 15 filaments et pour la trame un titre d'environ 76 dtex pour 20 à 24 filaments, le compte des fils dans la chaîne étant d'environ 30 à 68  1 to 6, characterized in that the individual filament yarns of the matrix and segment type have a title of about 50 dtex for 15 filaments for the warp and for the weft a title of about 76 dtex for 20 to 24 filaments, the count of threads in the warp being from about 30 to 68 fils par cm, et d'environ 25 à 40 fils par cm pour la trame.  son per cm, and about 25 to 40 threads per cm for the weft. 11. Bande de tissu selon l'une quelconque des revendi-  11. A web of fabric according to any of the claims cations 1 à 6, caractérisée en ce que les fils individuels à filaments du type à matrice et à segments présentent pour la chaîne un titre de 76 dtex pour 20 à 24 filaments et pour la trame un titre d'environ 100 à 110 dtex pour 25 à 40 filaments, le compte de fils dans la chaîne étant d'environ 28 à 50 fils par cm, et d'environ 22 à 35 fils par cm dans  1 to 6, characterized in that the individual matrix and segment type filament yarns have a title of 76 dtex for 20 to 24 filaments for the warp and for the weft a title of about 100 to 110 dtex for 25 at 40 filaments, the yarn count in the warp being about 28 to 50 threads per cm, and about 22 to 35 threads per cm in la trame.the frame. 12. Bande de tissu selon la revendication 8 ou 10, caractérisée en ce que les fils individuels à multifilaments de titre 50 dtex, sont composés de 12 à 20 filaments du type  Fabric web according to claim 8 or 10, characterized in that the individual multifilament threads of the title 50 dtex are composed of 12 to 20 filaments of the type à matrice et à segments.with matrix and segments.
FR8018720A 1979-08-30 1980-08-28 TISSUE FABRIC WITH TEXTURE A MULTICOMPONENT Granted FR2464318A3 (en)