ES2781148A1 - DIGITAL INK FOR SELECTIVE ABSORPTION OF IR RADIATION (Machine-translation by Google Translate, not legally binding) - Google Patents

DIGITAL INK FOR SELECTIVE ABSORPTION OF IR RADIATION (Machine-translation by Google Translate, not legally binding) Download PDF

Info

Publication number
ES2781148A1
ES2781148A1 ES201930178A ES201930178A ES2781148A1 ES 2781148 A1 ES2781148 A1 ES 2781148A1 ES 201930178 A ES201930178 A ES 201930178A ES 201930178 A ES201930178 A ES 201930178A ES 2781148 A1 ES2781148 A1 ES 2781148A1
Authority
ES
Spain
Prior art keywords
ink
radiation
composition according
ink composition
absorption
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
ES201930178A
Other languages
Spanish (es)
Inventor
Ripoll Juan Vicente Corts
Vega Oscar Ruiz
Roche Francisco Sanmiguel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Torrecid SA
Original Assignee
Torrecid SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Torrecid SA filed Critical Torrecid SA
Priority to ES201930178A priority Critical patent/ES2781148A1/en
Publication of ES2781148A1 publication Critical patent/ES2781148A1/en
Withdrawn legal-status Critical Current

Abstract

An ink composition for ultraviolet curing applicable by means of drop-on-demand technology (DoD-drop-on-demand) of inkjet for applications in selective absorption of IR radiation of substrates such as glass, plastic or fired tile, where the resulting layer of the ink printing shows, after UV curing, an absorption greater than or equal to 90% of the radiation at 1000 nm, an absorption less than or equal to 4.5% at 615 nm, an absorption greater than or equal to 80% of IR radiation in the range 820 nm to 1020 nm, an absorption less than or equal to 12% of the radiation in the range 500 nm to 700 nm and an absorption less than or equal to 15% in the range of radiation photosynthetically active between 380 nm and 700 nm. (Machine-translation by Google Translate, not legally binding)

Description

DESCRIPCIÓNDESCRIPTION

TINTA DIGITAL PARA ABSORCIÓN SELECTIVA DE RADIACIÓN IRDIGITAL INK FOR SELECTIVE ABSORPTION OF IR RADIATION

La presente invención, tinta digital para absorción selectiva de radiación IR (Infra-Roja), se enmarca en el campo de las tintas para inyección de tinta por curado UV (Ultra­ Violeta) que, una vez impresas, permiten la absorción selectiva de radiación IR en soportes como vidrio, plástico o azulejos cerámicos cocidos.The present invention, digital ink for selective absorption of IR radiation (Infra-Red), is part of the field of inkjet inks for UV curing (Ultra Violet) that, once printed, allow the selective absorption of IR radiation. on supports such as glass, plastic or fired ceramic tiles.

ESTADO DE LA TÉCNICASTATE OF THE ART

En el estado de la técnica existen ejemplos de composiciones destinadas a la absorción selectiva de la radiación IR. Así la solicitud de patente US2008/02411492A1 divulga una pasta para impresión por gravado en acero que comprende un ligante orgánico polimérico y una material absorbedor de IR. El material absorbedor de IR es un elemento de transición que puede ser Ti, V, Cr, Mn, Fe, Co, Ni y Cu. Dichos elementos de transición pueden estar en forma de iones o formando un vidrio de fosfato o fluoruro. Esta pasta, según la citada solicitud US2008/02411492A1, está destinada a aplicaciones en documentos de seguridad como pasaporte y sellos, entre otros. Sin embargo, la mencionada solicitud de patente US2008/02411492A1 presenta la limitación de ser opaca por lo que no se puede destinar a aplicaciones como el vidrio, el plástico, superficies metálicas, vajilla o el azulejo cerámico cocido donde interesa que la capa resultante de la impresión mantenga la transparencia en el caso del vidrio o plástico o permita ver la decoración en el caso de la superficie metálica, vajilla o el azulejo cerámico cocido. Una segunda limitación de la solicitud de patente US2008/02411492A1 es que está destinada a aplicaciones de impresión por grabado en acero con valores de viscosidad a 40°C de al menos 3 Pa.s (3000 cP). Cabe indicar que en el campo de las tintas para inyección de tinta es habitual el uso de la unidad cegesimal centipoise (cP) donde 1 cP equivale a 0,001 Pas en el Sistema Internacional de Unidades. Por lo tanto los valores de viscosidad son inviables para aplicaciones de inyección de tinta donde la viscosidad es del orden de 10 cP (0,010 Pa.s) a 25 cP (0,025 Pa.s).In the state of the art there are examples of compositions intended for the selective absorption of IR radiation. Thus, patent application US2008 / 02411492A1 discloses a paste for etching printing on steel comprising a polymeric organic binder and an IR absorbing material. The IR absorbing material is a transition element that can be Ti, V, Cr, Mn, Fe, Co, Ni and Cu. Said transition elements can be in the form of ions or forming a phosphate or fluoride glass. This paste, according to the aforementioned application US2008 / 02411492A1, is intended for applications in security documents such as passport and stamps, among others. However, the aforementioned patent application US2008 / 02411492A1 has the limitation of being opaque so it cannot be used for applications such as glass, plastic, metal surfaces, tableware or fired ceramic tiles where it is of interest that the layer resulting from the Print maintain transparency in the case of glass or plastic or allow to see the decoration in the case of metal surface, crockery or fired ceramic tile. A second limitation of patent application US2008 / 02411492A1 is that it is intended for etch printing applications on steel with viscosity values at 40 ° C of at least 3 Pa.s (3000 cP). It should be noted that in the field of inkjet inks it is common to use the cegesimal centipoise (cP) unit where 1 cP is equivalent to 0.001 Pas in the International System of Units. Therefore the viscosity values are unfeasible for inkjet applications where the viscosity is on the order of 10 cP (0.010 Pa.s) to 25 cP (0.025 Pa.s).

Por su parte, la patente US4244741 protege una tinta para flexografía, plásticos, soluciones acuosas y pinturas basada en heteropoliácidos de fósforo-molibdeno, fósforowolframio, silicio-molibdeno y silicio-wolframio. Su aplicación está especialmente destinada a códigos de barras y lectores ópticos. Sin embargo la mencionada patente US4244741 también presenta la limitación de que es opaca y por lo tanto no se puede utilizar para sustratos donde se quiera preservar la transparencia o el diseño del propio sustrato.For its part, patent US4244741 protects an ink for flexography, plastics, aqueous solutions and paints based on phosphorous-molybdenum heteropolyacids, tungsten phosphorus, silicon-molybdenum and silicon-tungsten. Its application is specially designed for barcodes and optical readers. However, the aforementioned patent US4244741 It also has the limitation that it is opaque and therefore cannot be used for substrates where the transparency or design of the substrate itself is to be preserved.

EXPLICACIÓN DE LA INVENCIÓNEXPLANATION OF THE INVENTION

A lo largo de la invención y las reivindicaciones la palabra "comprende” y sus variantes no pretenden excluir otras características técnicas, aditivos, componentes o pasos. Además, la palabra "comprende” incluye el caso "consiste en”. Para los expertos en la materia, otros objetos, ventajas y características de la invención se desprenderán en parte de la descripción y en parte de la práctica de la invención.Throughout the invention and the claims the word "comprises" and its variants are not intended to exclude other technical characteristics, additives, components or steps. Furthermore, the word "comprises" includes the case "consists of". For those skilled in the art subject matter, other objects, advantages and characteristics of the invention will emerge in part from the description and in part from the practice of the invention.

La presente invención una composición de tinta para curado ultravioleta aplicable mediante tecnología por gota bajo demanda (DoD-dmp-on-demand) de inyección de tinta para aplicaciones en absorción selectiva de radiación IR que comprende:The present invention is an ink composition for ultraviolet curing applicable by drop -on-demand technology ( DoD-dmp-on-demand) of inkjet for applications in selective absorption of IR radiation comprising:

a. Un compuesto de la familia de las cianinas que contiene al menos un grupo indol, soluble en el medio líquido de la tinta y en un porcentaje en peso de la tinta de 0,2%. b. Al menos un monómero en un porcentaje en peso de la tinta comprendido entre 35% y 45%.to. A compound of the cyanine family that contains at least one indole group, soluble in the liquid medium of the ink and in a percentage by weight of the ink of 0.2%. b. At least one monomer in a percentage by weight of the ink comprised between 35% and 45%.

c. Al menos un oligómero en un porcentaje en peso de la tinta comprendido entre 15% y 30%.c. At least one oligomer in a percentage by weight of the ink comprised between 15% and 30%.

d. Al menos un fotoiniciador en un porcentaje en peso de la tinta comprendido entre 10% y 20%.d. At least one photoinitiator in a percentage by weight of the ink comprised between 10% and 20%.

e. Al menos un disolvente en un porcentaje en peso de la tinta comprendido entre 10% y 25% y que se selecciona del grupo que comprende ciclohexanona y 2-metil-3-pentanona.and. At least one solvent in a percentage by weight of the ink comprised between 10% and 25% and which is selected from the group comprising cyclohexanone and 2-methyl-3-pentanone.

f. Al menos un humectante en un porcentaje en peso de la tinta comprendido 0,5% y 3%. g. Al menos un antiespumante en un porcentaje en peso de la tinta comprendido entre 1% y 5%.F. At least one humectant in a percentage by weight of the ink comprised between 0.5% and 3%. g. At least one defoamer in a percentage by weight of the ink comprised between 1% and 5%.

h. Presentando la capa resultante de la impresión de la tinta después del curado UV una absorción mayor o igual a 90% de la radiación a 1000 nm y una absorción menor o igual a 4,5% de la radiación a 615 nm.h. The layer resulting from ink printing after UV curing has an absorption greater than or equal to 90% of the radiation at 1000 nm and an absorption less than or equal to 4.5% of the radiation at 615 nm.

La medida de la absorción de las capas resultantes de aplicar la tinta objeto de invención se ha realizado con un espectrofotómetro marca PERKIN ELMER LAMBDA 950.The measurement of the absorption of the layers resulting from applying the ink object of the invention has been carried out with a PERKIN ELMER LAMBDA 950 spectrophotometer.

En la formulación de tintas para tecnología de inyección de tinta es fundamental definir una serie de propiedades que aseguren su correcto comportamiento. En este sentido cabe destacar el valor de la viscosidad en función de la velocidad de cizalladura o derivada de la deformación transversal respecto del tiempo, tanto cuando la tinta está prácticamente en reposo (velocidad de cizalladura a 10 s-1) como cuando se encuentra en movimiento en el circuito del equipo impresión (velocidad de cizalladura comprendido entre 100 s-1 y 1000 s-1). La medida de la velocidad de cizalladura se ha realizado con un reómetro de tipo cono-plato Anton Paar modelo MCR102. El procedimiento de medida consiste en colocar la tinta en una placa horizontal calefactable. Posteriormente el cono baja y comienza a girar midiéndose el par de torsión. A partir del valor de par de torsión se calcula el valor de viscosidad a una determinada temperatura y velocidad de cizalladura. En este sentido la tinta base agua objeto de la presente invención presenta los siguientes valores de viscosidad a 25°C en función de la velocidad de cizalladura:In the formulation of inks for inkjet technology it is essential to define a series of properties that ensure their correct behavior. In this sense, it is worth highlighting the value of the viscosity as a function of the shear rate or derived from the transverse deformation with respect to time, both when the ink is practically at rest (shear speed at 10 s-1) and when it is in motion in the circuit of the printing equipment (shear speed between 100 s-1 and 1000 s-1). The shear rate was measured with a Anton Paar MCR102 cone-plate rheometer. The measurement procedure consists of placing the ink on a heated horizontal plate. Subsequently the cone lowers and begins to rotate, measuring the torque. From the torque value, the viscosity value is calculated at a given temperature and shear rate. In this sense, the water-based ink object of the present invention has the following viscosity values at 25 ° C as a function of the shear rate:

• Entre 10 cP y 25 cP a 10 s-1 de velocidad de cizalladura.• Between 10 cP and 25 cP at 10 s-1 shear rate.

• Entre 10 cP y 18 cP a 100 s-1 de velocidad de cizalladura.• Between 10 cP and 18 cP at 100 s-1 shear rate.

• Entre 10 cP y 18 cP a 1000 s-1 de velocidad de cizalladura.• Between 10 cP and 18 cP at 1000 s-1 shear rate.

Cabe destacar que la capa resultante de la impresión de la tinta objeto de invención se caracteriza por tener una absorción mayor o igual a 80% de la radiación IR en el intervalo comprendido entre 820nm y 1020nm después del curado UV. Adicionalmente dicha capa, después del curado UV, se caracteriza por tener una absorción menor o igual a 12% el intervalo de la radiación UV-Visible comprendido entre 500nm y 700nm y una absorción menor o igual a 15% en el intervalo de la radiación fotosintéticamente activa o RFA (también conocida por sus siglas en inglés PAR) comprendido entre 380nm y 700nm. Todo ello permite su aplicación en plásticos y vidrios destinados a invernaderos para el cultivo de frutas, verduras y flores.It should be noted that the layer resulting from the printing of the ink object of the invention is characterized by having an absorption greater than or equal to 80% of the IR radiation in the range between 820nm and 1020nm after UV curing. Additionally, said layer, after UV curing, is characterized by having an absorption less than or equal to 12% in the range of UV-Visible radiation comprised between 500nm and 700nm and an absorption less than or equal to 15% in the range of photosynthetically radiation. active or RFA (also known by its acronym in English PAR) between 380nm and 700nm. All this allows its application in plastics and glass intended for greenhouses for the cultivation of fruits, vegetables and flowers.

En la tinta objeto de la invención el monómero se selecciona preferiblemente del grupo que comprende acrilato alquídico, acrilato cíclico y acrilato fenoxialquídico. Por su parte el oligómero se selecciona del grupo que comprende acrilatos de poliéter, acrilatos uretánicos, acrilatos de poliéster y acrilatos epoxi. Adicionalmente el fotoiniciador sensible a la luz ultravioleta se selecciona del grupo que comprende alfa-aminocetonas, alfahidroxicetonas, metilcetenas, fenilglioxilatos, fosifinas, alquilbenzoatos y benzofenonas.In the ink object of the invention, the monomer is preferably selected from the group comprising alkyd acrylate, cyclic acrylate and phenoxyalkyd acrylate. For its part, the oligomer is selected from the group comprising polyether acrylates, urethane acrylates, polyester acrylates and epoxy acrylates. Additionally, the ultraviolet light sensitive photoinitiator is selected from the group comprising alpha-aminoketones, alpha-hydroxyketones, methyl ketones, phenylglyoxylates, phosphines, alkylbenzoates and benzophenones.

Otra característica de la presente invención es que la tinta contiene al menos un humectante que preferiblemente se selecciona del grupo que comprende mezcla de éteres con glicol de polietileno-polipropileno con éter monobencílico y alcoholes C8-C10, copolímero de poliéter polisiloxano, surfactantes no iónicos, polidimetilsiloxano modificado con poliéter, derivados fluorados, alcoholes alcoxilados, copolímeros de óxido de etileno y polietileno y polidimetilsiloxanos modificados con poliéster. Another characteristic of the present invention is that the ink contains at least one humectant which is preferably selected from the group comprising mixture of ethers with polyethylene-polypropylene glycol with monobenzyl ether and C8-C10 alcohols, polyether polysiloxane copolymer, non-ionic surfactants, polyether modified polydimethylsiloxane, fluorinated derivatives, alkoxylated alcohols, copolymers of ethylene oxide and polyethylene and polyester modified polydimethylsiloxanes.

Cabe también destacar que la presencia de espuma o burbujas es un gran problema cuando se imprime mediante tecnología de inyección de tinta puesto que el cabezal de inyección inyecta aire en vez de tinta, lo que provoca un defecto en la aplicación final. Por ello, la presente invención comprende también al menos un antiespumante que preferiblemente se selecciona del grupo que comprende polisiloxanos, polisiloxanos modificados con polieter, siliconas modificadas, polidimetilsiloxanos, derivados de aceite mineral y derivados de ácidos grasos.It should also be noted that the presence of foam or bubbles is a big problem when printing using inkjet technology since the inkjet head injects air instead of ink, which causes a defect in the final application. Therefore, the present invention also comprises at least one defoamer that is preferably selected from the group comprising polysiloxanes, polyether-modified polysiloxanes, modified silicones, polydimethylsiloxanes, mineral oil derivatives and fatty acid derivatives.

FORMAS PREFERENTES DE REALIZACIÓNPREFERRED FORMS OF REALIZATION

Los siguientes ejemplos se proporcionan a título ilustrativo, y no se pretende que sean limitativos de la presente invención. Además, la presente invención cubre todas las posibles combinaciones de realizaciones particulares y preferidas aquí indicadas.The following examples are provided for illustrative purposes, and are not intended to be limiting of the present invention. Furthermore, the present invention covers all the possible combinations of particular and preferred embodiments indicated herein.

Ejemplo 1. Example 1 .

Se preparó una composición de tinta según la presente invención. En la Tabla 1 se indica la composición expresada en porcentajes en peso de cada uno de los componentes.An ink composition was prepared according to the present invention. Table 1 indicates the composition expressed in percentages by weight of each of the components.

Tabla 1Table 1

Figure imgf000005_0001
Figure imgf000005_0001

A continuación se indica los valores de viscosidad de la tinta:The following are the viscosity values of the ink:

Tabla 2Table 2

Figure imgf000005_0002
Figure imgf000005_0002

La tinta se aplicó mediante la tecnología de inyección de tinta sobre un sustrato de vidrio. Seguidamente el sustrato de vidrio impreso se sometió a un curado con una lámpara ultravioleta. Finalmente la capa obtenida se caracterizó mediante espectrocopía UV-Vis-IR con un espectrofotómetro. En la siguiente tabla se indican los valores promedio de absorción expresados en % de diferentes intervalos de longitud de onda, expresada en nanómetros.The ink was applied using inkjet technology on a glass substrate. The printed glass substrate was then cured with an ultraviolet lamp. Finally, the layer obtained was characterized by UV-Vis-IR spectrocopy with a spectrophotometer. The following table indicates the average absorption values expressed in% of different wavelength ranges, expressed in nanometers.

Tabla 3Table 3

Figure imgf000006_0001
Figure imgf000006_0001

Ejemplo 2. Example 2 .

Se preparó una composición de tinta según la presente invención. En la Tabla 4 se indica la composición expresada en porcentajes en peso de cada uno de los componentes.An ink composition was prepared according to the present invention. Table 4 indicates the composition expressed in percentages by weight of each of the components.

Tabla 4Table 4

Figure imgf000006_0002
Figure imgf000006_0002

A continuación se indica los valores de viscosidad de la tinta: The following are the viscosity values of the ink:

Tabla 5Table 5

Figure imgf000007_0003
Figure imgf000007_0003

La tinta se aplicó mediante la tecnología de inyección de tinta sobre un sustrato de plástico de policarbonato. Seguidamente el sustrato de policarbonato impreso se sometió a un curado con una lámpara ultravioleta. Finalmente la capa obtenida se caracterizó mediante espectrocopía UV-Vis-IR con un espectrofotómetro. En la siguiente tabla se indican los valores promedio de absorción expresados en % de diferentes intervalos de longitud de onda, expresada en nanómetros.The ink was applied by inkjet technology on a polycarbonate plastic substrate. The printed polycarbonate substrate was then cured with an ultraviolet lamp. Finally, the layer obtained was characterized by UV-Vis-IR spectrocopy with a spectrophotometer. The following table indicates the average absorption values expressed in% of different wavelength ranges, expressed in nanometers.

Tabla 6Table 6

Figure imgf000007_0001
Figure imgf000007_0001

Ejemplo 3.Example 3.

Se preparó una composición de tinta según la presente invención. En la Tabla 7 se indica la composición expresada en porcentajes en peso de cada uno de los componentes.An ink composition was prepared according to the present invention. Table 7 indicates the composition expressed in percentages by weight of each of the components.

Tabla 7Table 7

Figure imgf000007_0002
Figure imgf000007_0002

Figure imgf000008_0002
Figure imgf000008_0002

A continuación se indica los valores de viscosidad de la tinta:The following are the viscosity values of the ink:

Tabla 8Table 8

Figure imgf000008_0003
Figure imgf000008_0003

La tinta se aplicó mediante la tecnología de inyección de tinta sobre un sustrato de plástico de policarbonato. Seguidamente el sustrato de policarbonato impreso se sometió a un curado con una lámpara ultravioleta. Finalmente la capa obtenida se caracterizó mediante espectrocopía UV-Vis-IR con un espectrofotómetro. En la siguiente tabla se indican los valores promedio de absorción expresados en % de diferentes intervalos de longitud de onda, expresada en nanómetros.The ink was applied by inkjet technology on a polycarbonate plastic substrate. The printed polycarbonate substrate was then cured with an ultraviolet lamp. Finally, the layer obtained was characterized by UV-Vis-IR spectrocopy with a spectrophotometer. The following table indicates the average absorption values expressed in% of different wavelength ranges, expressed in nanometers.

Tabla 9Table 9

Figure imgf000008_0001
Figure imgf000008_0001

Claims (10)

REIVINDICACIONES 1. Una composición de tinta para curado ultravioleta aplicable mediante tecnología por gota bajo demanda (DoD-dmp-on-demand) de inyección de tinta para aplicaciones en absorción selectiva de radiación IR que comprende:1. An ink composition for ultraviolet curing applicable by drop -on-demand technology ( DoD-dmp-on-demand) of inkjet for applications in selective absorption of IR radiation comprising: a. Un compuesto de la familia de las cianinas que contiene al menos un grupo indol, soluble en el medio líquido de la tinta y en un porcentaje en peso de la tinta de 0,2%.to. A compound of the cyanine family that contains at least one indole group, soluble in the liquid medium of the ink and in a percentage by weight of the ink of 0.2%. b. Al menos un monómero en un porcentaje en peso de la tinta comprendido entre 35% y 45%.b. At least one monomer in a percentage by weight of the ink comprised between 35% and 45%. c. Al menos un oligómero en un porcentaje en peso de la tinta comprendido entre 15% y 30%.c. At least one oligomer in a percentage by weight of the ink comprised between 15% and 30%. d. Al menos un fotoiniciador en un porcentaje en peso de la tinta comprendido entre 10% y 20%.d. At least one photoinitiator in a percentage by weight of the ink comprised between 10% and 20%. e. Al menos un disolvente en un porcentaje en peso de la tinta comprendido entre 10% y 25% y que se selecciona del grupo que comprende ciclohexanona y 2-metil-3-pentanona.and. At least one solvent in a percentage by weight of the ink comprised between 10% and 25% and which is selected from the group comprising cyclohexanone and 2-methyl-3-pentanone. f. Al menos un humectante en un porcentaje en peso de la tinta comprendido 0,5% y 3%.F. At least one humectant in a percentage by weight of the ink comprised between 0.5% and 3%. g. Al menos un antiespumante en un porcentaje en peso de la tinta comprendido entre 1% y 5%.g. At least one defoamer in a percentage by weight of the ink comprised between 1% and 5%. h. Presentando la capa resultante de la impresión de la tinta después del curado UV una absorción mayor o igual a 90% de la radiación a 1000 nm y una absorción menor o igual a 4,5% de la radiación a 615 nm.h. The layer resulting from ink printing after UV curing has an absorption greater than or equal to 90% of the radiation at 1000 nm and an absorption less than or equal to 4.5% of the radiation at 615 nm. 2. La composición de tinta según la reivindicación 1 donde los valores de viscosidad a 25 °C en función de la velocidad de cizalladura son:2. The ink composition according to claim 1 wherein the viscosity values at 25 ° C as a function of the shear rate are: a. Entre 10cP y 25 cP a 10 s"1 de velocidad de cizalladura.to. Between 10cP and 25 cP at 10 s "1 shear rate. b. Entre 10 cP y 18cP a 100 s"1 de velocidad de cizalladura.b. Between 10 cP and 18cP at 100 s "1 shear rate. c. Entre 10 cP y 18 cP a 1000 s"1 de velocidad de cizalladura.c. Between 10 cP and 18 cP at 1000 s "1 shear rate. 3. La composición de tinta según cualquiera de las reivindicaciones anteriores donde la capa resultante de la impresión de la tinta presenta, después del curado UV, una absorción mayor o igual a 80% de la radiación IR en el intervalo comprendido entre 820nm y 1020nm.3. The ink composition according to any of the preceding claims, wherein the layer resulting from the printing of the ink has, after UV curing, an absorption greater than or equal to 80% of the IR radiation in the range between 820nm and 1020nm. 4. La composición de tinta según cualquier de las reivindicaciones anteriores donde la capa resultante de la impresión de la tinta presenta, después del curado UV, una absorción menor o igual a 12% de la radiación en el intervalo comprendido entre 500nm y 700nm.The ink composition according to any of the preceding claims, wherein the layer resulting from the printing of the ink has, after UV curing, a absorption less than or equal to 12% of radiation in the range between 500nm and 700nm. 5. La composición de tinta según cualquier de las reivindicaciones anteriores donde la capa resultante de la impresión de la tinta presenta, después del curado UV, una absorción menor o igual a 15% en el intervalo de la radiación fotosintéticamente activa comprendido entre 380nm y 700nm.5. The ink composition according to any of the preceding claims, wherein the layer resulting from the printing of the ink exhibits, after UV curing, an absorption less than or equal to 15% in the range of photosynthetically active radiation comprised between 380nm and 700nm . 6. La composición de tinta según cualquiera de las reivindicaciones anteriores donde el monómero se selecciona del grupo que comprende acrilato alquídico, acrilato cíclico y acrilato fenoxialquídico.6. The ink composition according to any of the preceding claims wherein the monomer is selected from the group comprising alkyd acrylate, cyclic acrylate and phenoxyalkid acrylate. 7. La composición de tinta según cualquiera de las reivindicaciones anteriores donde el oligómero se selecciona del grupo que comprende acrilatos de poliéter, acrilatos uretánicos, acrilatos de poliéster y acrilatos epoxi.7. The ink composition according to any one of the preceding claims wherein the oligomer is selected from the group comprising polyether acrylates, urethane acrylates, polyester acrylates, and epoxy acrylates. 8. La composición de tinta según cualquiera de las reivindicaciones anteriores donde el fotoiniciador sensible a la luz ultravioleta se selecciona del grupo que comprende alfa-aminocetonas, alfa-hidroxicetonas, metilcetenas, fenilglioxilatos, fosifinas, alquilbenzoatos y benzofenonas.8. The ink composition according to any of the preceding claims wherein the ultraviolet light sensitive photoinitiator is selected from the group comprising alpha-aminoketones, alpha-hydroxyketones, methyl ketones, phenylglyoxylates, phosphines, alkylbenzoates and benzophenones. 9. La composición de tinta según la reivindicación 1 donde el humectante se seleccionan del grupo que comprende mezcla de éteres con glicol de polietilenopolipropileno con éter monobencílico y alcoholes C8-C10, copolímero de poliéter polisiloxano, surfactantes no iónicos, polidimetilsiloxano modificado con poliéter, derivados fluorados, alcoholes alcoxilados, copolímeros de óxido de etileno y polietileno y polidimetilsiloxanos modificados con poliéster.9. The ink composition according to claim 1 wherein the humectant is selected from the group comprising mixing ethers with polyethylene polypropylene glycol with monobenzyl ether and C8-C10 alcohols, polyether polysiloxane copolymer, nonionic surfactants, polyether modified polydimethylsiloxane, derivatives fluorides, alkoxylated alcohols, copolymers of ethylene oxide and polyethylene, and polyester-modified polydimethylsiloxanes. 10. La composición de tinta según la reivindicación 1 donde el antiespumante se selecciona del grupo que comprende polisiloxanos, polisiloxanos modificados con polieter, siliconas modificadas, polidimetilsiloxanos, derivados de aceite mineral y derivados de ácidos grasos. 10. The ink composition according to claim 1 wherein the defoamer is selected from the group comprising polysiloxanes, polyether modified polysiloxanes, modified silicones, polydimethylsiloxanes, mineral oil derivatives and fatty acid derivatives.
ES201930178A 2019-02-27 2019-02-27 DIGITAL INK FOR SELECTIVE ABSORPTION OF IR RADIATION (Machine-translation by Google Translate, not legally binding) Withdrawn ES2781148A1 (en)