ES2614806T9 - Método para la fabricación de lámina de acero de alta resistencia que tiene una excelente capacidad de conformación - Google Patents

Método para la fabricación de lámina de acero de alta resistencia que tiene una excelente capacidad de conformación Download PDF

Info

Publication number
ES2614806T9
ES2614806T9 ES11732927.6T ES11732927T ES2614806T9 ES 2614806 T9 ES2614806 T9 ES 2614806T9 ES 11732927 T ES11732927 T ES 11732927T ES 2614806 T9 ES2614806 T9 ES 2614806T9
Authority
ES
Spain
Prior art keywords
steel sheet
high strength
strength steel
manufacturing high
excellent conformability
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
ES11732927.6T
Other languages
English (en)
Other versions
ES2614806T3 (es
Inventor
Toshiki Nonaka
Naoki Matsutani
Toshio Ogawa
Nobuhiro Fujita
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel and Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel and Sumitomo Metal Corp filed Critical Nippon Steel and Sumitomo Metal Corp
Application granted granted Critical
Publication of ES2614806T3 publication Critical patent/ES2614806T3/es
Publication of ES2614806T9 publication Critical patent/ES2614806T9/es
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

Yprom
ES11732927.6T 2010-01-13 2011-01-13 Método para la fabricación de lámina de acero de alta resistencia que tiene una excelente capacidad de conformación Active ES2614806T3 (es)