ES2140252A1 - Un procedimiento para la obtencion de fibras cortas y largas y sus telas de entrecruzamiento quimico por centrifugacion, estirado o extrusion de soles obtenidos mediante hidrolisis controlada de disoluciones de alcoxidos metalicos. - Google Patents
Un procedimiento para la obtencion de fibras cortas y largas y sus telas de entrecruzamiento quimico por centrifugacion, estirado o extrusion de soles obtenidos mediante hidrolisis controlada de disoluciones de alcoxidos metalicos.Info
- Publication number
- ES2140252A1 ES2140252A1 ES009500039A ES9500039A ES2140252A1 ES 2140252 A1 ES2140252 A1 ES 2140252A1 ES 009500039 A ES009500039 A ES 009500039A ES 9500039 A ES9500039 A ES 9500039A ES 2140252 A1 ES2140252 A1 ES 2140252A1
- Authority
- ES
- Spain
- Prior art keywords
- sols
- chemically cross
- extrusion
- centrifugation
- controlled hydrolysis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Un procedimiento para la obtención de fibras cortas y largas y sus telas de entrecruzamiento químico por centrifugación, estirado o extrusión de soles obtenidos mediante hidrólisis controlada de disoluciones de alcóxidos metálicos. Procedimiento para la obtención de fibras cortas y largas y sus telas de entrecruzamiento químicas de fórmula general xSiO{sub,2 -(100-x) M{sub,y O{sub,y+1 donde O<x<100, 1{< y{< 2 y M = Zr, Ti y Al; conformadas por centrifugación, rodillos, estirado, extrusión o cualquier otro procedimiento, de "soles'' muy homogéneos. Los soles conformables se obtienen por la hidrólisis controlada de mezclas de cualquier alcóxido de Si, Zr, Ti y Al en solución alcohólica, por burbujeo controlado a través de la disolución de cualquier gas saturado con vapor de agua.Tras el conformado, los "soles'' gelifican, dando lugar a productos que, por secado y consolidación mediante adecuado tratamiento térmica conducen a los citados materiales fibrosos con muchas aplicaciones y, particularmente, como reforzantes de matrices poliméricas, cerámicas vítreas, metálicas o cementíceas. Las fibras y telas de entrecruzamiento químico obtenidas, debido a su composición, homogeneidad, propiedades mecánicas y características energéticas superficiales, presentan indudablemente ventajas para su aplicación tecnológica en el campo de los materiales compuestos.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
ES9500039A ES2140252B1 (es) | 1995-01-11 | 1995-01-11 | Un procedimiento para la obtencion de fibras cortas y largas y sus telas de entrecruzamiento quimico por centrifugacion, estirado o extrusion de soles obtenidos mediante hidrolisis controlada de disoluciones de alcoxidos metalicos. |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
ES9500039A ES2140252B1 (es) | 1995-01-11 | 1995-01-11 | Un procedimiento para la obtencion de fibras cortas y largas y sus telas de entrecruzamiento quimico por centrifugacion, estirado o extrusion de soles obtenidos mediante hidrolisis controlada de disoluciones de alcoxidos metalicos. |
Publications (2)
Publication Number | Publication Date |
---|---|
ES2140252A1 true ES2140252A1 (es) | 2000-02-16 |
ES2140252B1 ES2140252B1 (es) | 2001-02-01 |
Family
ID=8289120
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ES9500039A Expired - Lifetime ES2140252B1 (es) | 1995-01-11 | 1995-01-11 | Un procedimiento para la obtencion de fibras cortas y largas y sus telas de entrecruzamiento quimico por centrifugacion, estirado o extrusion de soles obtenidos mediante hidrolisis controlada de disoluciones de alcoxidos metalicos. |
Country Status (1)
Country | Link |
---|---|
ES (1) | ES2140252B1 (es) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1122090A (en) * | 1965-09-07 | 1968-07-31 | Shell Int Research | Oxidation of paraffins to secondary aliphatic alcohols |
EP0297176A1 (en) * | 1987-07-03 | 1989-01-04 | Asahi Glass Company Ltd. | Process for producing silica glass fibers |
US5089188A (en) * | 1989-01-04 | 1992-02-18 | Ppg Industries, Inc. | Spinning of sol gel siliceous-containing fibers with wet coagulation |
EP0510653A1 (en) * | 1991-04-24 | 1992-10-28 | Asahi Glass Company Ltd. | Highly heat resistant glass fiber and process for its production |
EP0582879A1 (de) * | 1992-08-06 | 1994-02-16 | Degussa Ag | Geformte Organosiloxan-Polykondensate, Verfahren zu ihrer Herstellung und Verwendung |
-
1995
- 1995-01-11 ES ES9500039A patent/ES2140252B1/es not_active Expired - Lifetime
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1122090A (en) * | 1965-09-07 | 1968-07-31 | Shell Int Research | Oxidation of paraffins to secondary aliphatic alcohols |
EP0297176A1 (en) * | 1987-07-03 | 1989-01-04 | Asahi Glass Company Ltd. | Process for producing silica glass fibers |
US5089188A (en) * | 1989-01-04 | 1992-02-18 | Ppg Industries, Inc. | Spinning of sol gel siliceous-containing fibers with wet coagulation |
EP0510653A1 (en) * | 1991-04-24 | 1992-10-28 | Asahi Glass Company Ltd. | Highly heat resistant glass fiber and process for its production |
EP0582879A1 (de) * | 1992-08-06 | 1994-02-16 | Degussa Ag | Geformte Organosiloxan-Polykondensate, Verfahren zu ihrer Herstellung und Verwendung |
Also Published As
Publication number | Publication date |
---|---|
ES2140252B1 (es) | 2001-02-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US5290350A (en) | Insulating shaped articles comprising inorganic fibrous matrices and xanthan gum/cationic starch binders | |
Zhang et al. | Poly (methyl methacrylate)–titania hybrid materials by sol–gel processing | |
CA2404200A1 (en) | System for preparing glass fiber pellets having low discoloration | |
ZA824440B (en) | A process of making foamed articles | |
NZ336921A (en) | Method for making compressed articles of ceramic fibers and compressed articles obtained thereby | |
KR20010009582A (ko) | 저밀도 고강도의 단열재 및 그 제조방법 | |
CA2056789A1 (en) | A process for the manufacture of a fibrous preform formed of refractory fibers for producing a composite material article | |
DE69617820T2 (de) | Steinwolle mit hohem Widerstand und Verfahren zu seiner Herstellung | |
WO2003053875A3 (en) | System for preparing glass fiber pellets having low discoloration | |
CN106987924A (zh) | 聚碳硅烷不熔化纤维的制备方法 | |
ES2140252A1 (es) | Un procedimiento para la obtencion de fibras cortas y largas y sus telas de entrecruzamiento quimico por centrifugacion, estirado o extrusion de soles obtenidos mediante hidrolisis controlada de disoluciones de alcoxidos metalicos. | |
RU94046448A (ru) | Формованные изделия из политетрафторэтилена и способ их получения | |
CA2035685A1 (en) | Process for the manufacture of a carbon fiber reinforced composite material having a ceramic matrix | |
EP0374657A3 (de) | Neue thermotrope Polyester, Verfahren zu ihrer Herstellung sowie ihre Verwendung zur Herstellung von Formkörpern, Filamenten, Fasern und Folien | |
Abe et al. | Preparation and properties of silicon-containing hybrid gels from vinyltrimethoxysilane | |
Wojcik et al. | Organic-inorganic gels based on silica and multifunctional acrylates: Code: B8 | |
US2981980A (en) | Production of light polarizing elements | |
CA2043757A1 (en) | Glass-ceramic li-al-si-o composition and process for its production | |
Nielsen | The mechanical and other physical properties of polyelectrolyte salts in the solid state | |
US5492661A (en) | Process for producing a casting ceramic | |
Nazeri et al. | Ceramic Composites by the Sol‐Gel Method: A Review | |
Gao et al. | Preparation of styrene–maleic anhydride copolymer/Si O network nanocomposites by the sol–gel process | |
CN1597618A (zh) | 陶瓷纤维模具板 | |
KR940002183A (ko) | 알루미나세라믹 섬유제조용 슬러리의 제조방법 | |
JPH0534308B2 (es) |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
EC2A | Search report published |
Date of ref document: 20000216 Kind code of ref document: A1 Effective date: 20000216 |