ES2088274T3 - Metodo para la produccion de polvo de nitruro de aluminio resistente a la humedad y polvo asi producido. - Google Patents

Metodo para la produccion de polvo de nitruro de aluminio resistente a la humedad y polvo asi producido.

Info

Publication number
ES2088274T3
ES2088274T3 ES93904878T ES93904878T ES2088274T3 ES 2088274 T3 ES2088274 T3 ES 2088274T3 ES 93904878 T ES93904878 T ES 93904878T ES 93904878 T ES93904878 T ES 93904878T ES 2088274 T3 ES2088274 T3 ES 2088274T3
Authority
ES
Spain
Prior art keywords
aluminum nitride
powder
moisture resistant
resistant aluminum
produced
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES93904878T
Other languages
English (en)
Inventor
Kevin E Howard
Daniel F Carroll
Scott J Biskupski
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Chemical Co
Original Assignee
Dow Chemical Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Chemical Co filed Critical Dow Chemical Co
Application granted granted Critical
Publication of ES2088274T3 publication Critical patent/ES2088274T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

UN METODO PARA FABRICAR UN POLVO QUE CONTIENE NITRURO DE ALUMINIO RESISTENTE DE HUMEDAD QUE INCLUYE (A) CUBRIR UNA CAPA DE SILICATO EN EL POLVO QUE CONTIENE NITRURO DE ALUMINIO QUE TIENE NITRURO DE ALUMINIO EN AL MENOS UNA PARTE DE SU SUPERFICIE Y (B) TRATAR CON CALOR EL POLVO QUE CONTIENE EL NITRURO DE ALUMINIO CUBIERTO A UNA TEMPERATURA DE 350 A 1000 C POR UN PERIODO DE TIEMPO SUFICIENTE PARA OBLIGAR AL SILICATO A REACCIONAR CON EL NITRURO DE ALUMINIO DE SUPERFICIE POR LO CUAL FORMAR UNA CAPA DE SI-AL-O-N UNIDA AL NITRURO DE ALUMINIO DE SUPERFICIE. EL SILICATO TIENE UNIDOS RADICALES ALQUILO O ALCOXIALQUILO. EL METODO PRODUCE UN POLVO QUE CONTIENE NITRURO DE ALUMINIO RESISTENTE DE HUMEDAD TENIENDO UNA CAPA DE SI-AL-O-N UNIDO DE REACCION AL NITRURO DE ALUMINIO DE SUPERFICIE.
ES93904878T 1992-06-08 1993-01-28 Metodo para la produccion de polvo de nitruro de aluminio resistente a la humedad y polvo asi producido. Expired - Lifetime ES2088274T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US07/895,496 US5234712A (en) 1992-06-08 1992-06-08 Method of making moisture resistant aluminum nitride powder and powder produced thereby

Publications (1)

Publication Number Publication Date
ES2088274T3 true ES2088274T3 (es) 1996-08-01

Family

ID=25404587

Family Applications (1)

Application Number Title Priority Date Filing Date
ES93904878T Expired - Lifetime ES2088274T3 (es) 1992-06-08 1993-01-28 Metodo para la produccion de polvo de nitruro de aluminio resistente a la humedad y polvo asi producido.

Country Status (9)

Country Link
US (2) US5234712A (es)
EP (1) EP0644863B1 (es)
JP (1) JP3446053B2 (es)
KR (1) KR100249750B1 (es)
AU (1) AU669509B2 (es)
CA (1) CA2137251C (es)
DE (1) DE69302907T2 (es)
ES (1) ES2088274T3 (es)
WO (1) WO1993025496A1 (es)

Families Citing this family (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5627107A (en) * 1992-06-08 1997-05-06 The Dow Chemical Company Semiconductor devices encapsulated with aluminum nitride-filled resins and process for preparing same
US5234712A (en) * 1992-06-08 1993-08-10 The Dow Chemical Company Method of making moisture resistant aluminum nitride powder and powder produced thereby
US5525320A (en) * 1994-07-11 1996-06-11 University Of Cincinnati Process for aluminum nitride powder production
US5494703A (en) * 1994-11-29 1996-02-27 University Of Kentucky Research Foundation Oxidation proof silicate surface coating on iron sulfides
US5601874A (en) * 1994-12-08 1997-02-11 The Dow Chemical Company Method of making moisture resistant aluminum nitride powder and powder produced thereby
US5863970A (en) * 1995-12-06 1999-01-26 Polyset Company, Inc. Epoxy resin composition with cycloaliphatic epoxy-functional siloxane
US6832735B2 (en) * 2002-01-03 2004-12-21 Nanoproducts Corporation Post-processed nanoscale powders and method for such post-processing
SI9700229A (sl) * 1997-09-05 1999-04-30 Inštitut "Jožef Stefan" Postopek zaščite prahu AlN pred hidrolizo
AU9481798A (en) * 1997-09-15 1999-04-05 Advanced Refractory Technologies, Inc. Silica-coated aluminum nitride powders with improved properties and methos for their preparation
US6168859B1 (en) 1998-01-29 2001-01-02 The Dow Chemical Company Filler powder comprising a partially coated alumina powder and process to make the filler powder
DE10085011T1 (de) * 1999-09-21 2003-01-16 Saint Gobain Ceramics Wärmeleitfähige Materialien in einer hydrophoben Verbindung für die Handhabung von Wärme
US6660241B2 (en) 2000-05-01 2003-12-09 Saint-Gobain Ceramics & Plastics, Inc. Highly delaminated hexagonal boron nitride powders, process for making, and uses thereof
US6794435B2 (en) 2000-05-18 2004-09-21 Saint Gobain Ceramics & Plastics, Inc. Agglomerated hexagonal boron nitride powders, method of making, and uses thereof
US6764975B1 (en) 2000-11-28 2004-07-20 Saint-Gobain Ceramics & Plastics, Inc. Method for making high thermal diffusivity boron nitride powders
CA2445555C (en) * 2001-04-30 2010-11-23 Saint-Gobain Ceramics & Plastics, Inc. Polymer processing aid and method for processing polymers
US6645612B2 (en) 2001-08-07 2003-11-11 Saint-Gobain Ceramics & Plastics, Inc. High solids hBN slurry, hBN paste, spherical hBN powder, and methods of making and using them
US7494635B2 (en) * 2003-08-21 2009-02-24 Saint-Gobain Ceramics & Plastics, Inc. Boron nitride agglomerated powder
SG141222A1 (en) * 2003-12-04 2008-04-28 Sumitomo Bakelite Singapore Pt Semiconductor devices containing epoxy moulding compositions and the compositions per se
US8679624B2 (en) * 2009-06-05 2014-03-25 Xerox Corporation Passivated aluminum nitride for enhanced thermal conductivity materials for fuser belts
JPWO2018139632A1 (ja) * 2017-01-30 2019-11-21 日本山村硝子株式会社 シリコーン系ハイブリッドポリマー被覆ＡｌＮフィラー
CN111479773B (zh) * 2017-12-21 2022-04-29 昭和电工株式会社 玻璃被覆氮化铝粒子、其制造方法和含有它的放热性树脂组合物
EP3805152B1 (en) * 2018-06-06 2023-09-06 Resonac Corporation Method for producing glass-coated aluminum nitride particles, and method for producing heat-dissipating resin composition containing said glass-coated aluminum nitride particles
EP4253483A3 (en) * 2018-08-24 2024-03-27 Resonac Corporation Silicon-containing oxide-coated aluminum nitride particles
JP7395111B2 (ja) * 2019-08-01 2023-12-11 株式会社レゾナック 無機粒子分散樹脂組成物及び無機粒子分散樹脂組成物の製造方法
JP7434818B2 (ja) * 2019-11-12 2024-02-21 株式会社レゾナック 珪素含有酸化物被覆窒化アルミニウム粒子の製造方法および放熱性樹脂組成物の製造方法
CN112250047A (zh) * 2020-10-28 2021-01-22 苏州巨峰电气绝缘***股份有限公司 一种氮化铝粉体的抗水解改性方法
CN114560705B (zh) * 2022-01-19 2023-01-24 福建华清电子材料科技有限公司 一种不研磨氮化铝陶瓷基板的制备方法
WO2024127697A1 (ja) * 2022-12-16 2024-06-20 株式会社レゾナック 珪素含有酸化物被覆窒化アルミニウム粒子の製造方法

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59203715A (ja) * 1983-04-30 1984-11-17 Toshiba Corp 複合セラミックス粉末の製造方法
US5234712A (en) * 1992-06-08 1993-08-10 The Dow Chemical Company Method of making moisture resistant aluminum nitride powder and powder produced thereby

Also Published As

Publication number Publication date
KR100249750B1 (ko) 2000-03-15
AU669509B2 (en) 1996-06-13
JP3446053B2 (ja) 2003-09-16
EP0644863B1 (en) 1996-05-29
CA2137251A1 (en) 1993-12-23
DE69302907D1 (de) 1996-07-04
US5234712A (en) 1993-08-10
US5508110A (en) 1996-04-16
WO1993025496A1 (en) 1993-12-23
CA2137251C (en) 2004-04-20
DE69302907T2 (de) 1996-09-26
EP0644863A1 (en) 1995-03-29
JPH07507760A (ja) 1995-08-31
KR950701892A (ko) 1995-05-17
AU3608893A (en) 1994-01-04

Similar Documents

Publication Publication Date Title
ES2088274T3 (es) Metodo para la produccion de polvo de nitruro de aluminio resistente a la humedad y polvo asi producido.
BR8606145A (pt) Processos de formacao de um revestimento de difusao de silicio sobre a superficie de um metal,para protecao de um metal pela formacao desse revestimento e para protecao de um artigo metalico
EP1185145A4 (en) CERAMIC HEATER.
BR9804242A (pt) Processo para produzir refratário a base de sílica, e, artigo de refratário a base de sílica.
AU2957889A (en) Aluminum products having improved corrosion resistance
ATE68019T1 (de) Schutzschicht.
BR9205896A (pt) Composição de revestimento, artigo de metal, processo para aperfeiçoar a proteção de uma superfície de metal e processo aperfeiçoado para formação de um revestimento resistente a corrosão
SE8501204L (sv) Metod for framstellning av en termisk barrierbeleggning och de derigenom framstellda beleggningarna
ES2055133T5 (es) Procedimiento para revestir sustratos metalicos con la ayuda de un producto primario en polvo y de un revestimiento superficial aplicado por inmersion, y materiales compuestos obtenidos.
MX170165B (es) Metodo para revestir ceramica sobre metales
CH653205GA3 (es)
ES515798A0 (es) Procedimiento para fabricar un articulo metalico que tiene un recubrimiento por conversion quimica sobre superficies de hierro y-o de zinc del mismo.
ES2128872T3 (es) Modulo de chip.
ES2112505T5 (es) Capa de oxido esmaltable.
JPS56129044A (en) Thermal shock resistant ceramic honeycomb structure
JPS572368A (en) Material for coating hot steel surface
IT1152138B (it) Procedimento e apparecchiatura per l'applicazione di strati di rivestimento a corpi di forma e dimensioni diverse, come pillole, articoli di confetteria e/o simili
NO880097D0 (no) Anordning for framstilling av keramiske komposittgjenstander.
FR2640658B1 (fr) Revetement organique pour proteger les constructions, notamment contre le feu et la chaleur
JPS5448877A (en) Rireproof panel
GR3003755T3 (es)
FR2358964A1 (fr) Procede pour fabriquer des objets resistant aux fortes temperatures a partir de materiaux ligneux, et objets obtenus par ce procede
EP0072643A3 (en) Cordierite powders and protective coatings formed therefrom
ES2161475T3 (es) Procedimiento para el tratamiento termico de chapa fina recubierta con znal por galvanizacion por inmersion en caliente.
HUT41356A (en) Heat-insulating preparation

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 644863

Country of ref document: ES