EA201071211A1 - Сэндвичевый материал для пайки с высокой прочностью при высокой температуре - Google Patents
Сэндвичевый материал для пайки с высокой прочностью при высокой температуреInfo
- Publication number
- EA201071211A1 EA201071211A1 EA201071211A EA201071211A EA201071211A1 EA 201071211 A1 EA201071211 A1 EA 201071211A1 EA 201071211 A EA201071211 A EA 201071211A EA 201071211 A EA201071211 A EA 201071211A EA 201071211 A1 EA201071211 A1 EA 201071211A1
- Authority
- EA
- Eurasian Patent Office
- Prior art keywords
- sandwich material
- high temperature
- soldering
- strength soldering
- relates
- Prior art date
Abstract
Изобретение относится к сэндвичевому материалу для пайки, включающему сердцевинный слой из первого алюминиевого сплава и барьерный слой из второго алюминиевого сплава, отличающийся тем, что первый сплав, составляющий сердцевинный слой, содержит (в вес.%): 0,8-2% Mn, ≤1,0% Mg, 0,3-1,5% Si, ≤0,3% Ti, ≤0,3% Cr, ≤0,3% Zr, ≤1,3% Cu, ≤0,5% Zn, ≤0,2% In, ≤0,1% Sn и ≤0,7% (Fe+Ni), причем остальное количество составляет Al и ≤0,05% каждой из неизбежных загрязняющих примесей, и что второй сплав, составляющий барьерный слой, содержит (в вес.%): ≤0,2% Mn+Cr, ≤1,0% Mg, ≤1,5% Si, ≤0,3% Ti, ≤0,2% Zr, ≤0,3% Cu, ≤0,5% Zn, ≤0,2% In, ≤0,1% Sn и ≤1,5% (Fe+Ni), причем остальное количество составляет Al и ≤0,05% каждой из неизбежных загрязняющих примесей. Изобретение также относится к способу получения сэндвичевого материала, спаянному продукту, такому как теплообменник, включающий сэндвичевый материал, и применению спаянного продукта при высоких и низких температурах.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SE0800898A SE533287C2 (sv) | 2008-04-18 | 2008-04-18 | Sandwichmaterial för lödning med hög hållfasthet vid hög temperatur |
PCT/SE2009/050139 WO2009128766A1 (en) | 2008-04-18 | 2009-02-10 | Sandwich material for brazing with high strength at high temperature |
Publications (2)
Publication Number | Publication Date |
---|---|
EA201071211A1 true EA201071211A1 (ru) | 2011-04-29 |
EA025938B1 EA025938B1 (ru) | 2017-02-28 |
Family
ID=41199327
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
EA201071211A EA025938B1 (ru) | 2008-04-18 | 2009-02-10 | Сэндвичевый материал для пайки |
Country Status (13)
Country | Link |
---|---|
US (1) | US8574723B2 (ru) |
EP (1) | EP2271489B1 (ru) |
JP (2) | JP2011520032A (ru) |
KR (1) | KR101557903B1 (ru) |
CN (1) | CN102083620B (ru) |
BR (1) | BRPI0910597A2 (ru) |
CA (1) | CA2721747C (ru) |
EA (1) | EA025938B1 (ru) |
MX (1) | MX2010011443A (ru) |
PL (1) | PL2271489T3 (ru) |
SE (1) | SE533287C2 (ru) |
WO (1) | WO2009128766A1 (ru) |
ZA (1) | ZA201008031B (ru) |
Families Citing this family (24)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SE0950756A1 (sv) | 2009-10-13 | 2011-04-14 | Sapa Heat Transfer Ab | Sandwichmaterial med hög hållfasthet vid hög temperatur för tunna band i värmeväxlare |
FR2967765B1 (fr) * | 2010-11-19 | 2015-03-06 | Valeo Systemes Thermiques | Composant brasable et echangeur de chaleur le comportant |
CN102296217A (zh) * | 2011-08-24 | 2011-12-28 | 吴江市精工铝字制造厂 | 高强度耐热铝合金 |
KR102045789B1 (ko) | 2012-05-23 | 2019-11-18 | 그랑게스 스웨덴 아베 | 아주 고 강도의 초고 새깅 및 용융 내성 핀 재료 |
WO2014017976A1 (en) | 2012-07-27 | 2014-01-30 | Gränges Sweden Ab | Strip material with excellent corrosion resistance after brazing |
JP6182876B2 (ja) * | 2013-01-25 | 2017-08-23 | 株式会社デンソー | 熱交換器用チューブおよび熱交換器の製造方法 |
FR3018213B1 (fr) | 2014-03-06 | 2016-10-21 | Constellium France | Tole de brasage a placages multiples |
US20170113305A1 (en) * | 2014-03-19 | 2017-04-27 | Uacj Corporation | Cladded aluminium-alloy material and production method therefor, and heat exchanger using said cladded aluminium-alloy material and production method therefor |
CN106061666B (zh) * | 2014-03-31 | 2018-10-02 | 株式会社Uacj | 铝包层构件的制造方法 |
CN104384871B (zh) * | 2014-12-15 | 2016-08-24 | 西南铝业(集团)有限责任公司 | 一种铝合金钎焊板的生产工艺 |
CN104526280A (zh) * | 2014-12-15 | 2015-04-22 | 西南铝业(集团)有限责任公司 | 一种铝合金钎焊板的制备方法 |
WO2016138223A1 (en) * | 2015-02-26 | 2016-09-01 | Alcoa Inc. | Multilayer brazing sheet for vacuum braze applications |
KR20180043371A (ko) * | 2015-10-05 | 2018-04-27 | 하이드로 알루미늄 롤드 프로덕츠 게엠베하 | 써멀 플럭스-프리 접합 방법에 사용하기 위한 알루미늄 복합 재료 및 그러한 알루미늄 복합 재료를 제조하는 방법 |
CN106427129A (zh) * | 2016-11-24 | 2017-02-22 | 苏州华意铭铄激光科技有限公司 | 一种耐热稳定性好的复合金属制品 |
JP6487974B2 (ja) | 2017-08-17 | 2019-03-20 | 株式会社Uacj | 熱交換器用アルミニウム合金ブレージングシート及び熱交換器用アルミニウム合金ブレージングシートの製造方法 |
CN107755427B (zh) * | 2017-09-30 | 2019-07-23 | 银邦金属复合材料股份有限公司 | 一种铝合金复合箔及其制备方法 |
FR3080058B1 (fr) | 2018-04-16 | 2023-05-12 | Constellium Neuf Brisach | Tole de brasage multicouche |
US20210310754A1 (en) * | 2018-09-24 | 2021-10-07 | Aleris Rolled Products Germany Gmbh | Aluminium alloy fin stock material |
CN109402460B (zh) * | 2018-12-25 | 2023-06-23 | 江苏中基新能源科技集团有限公司 | 合金化高剥离强度高热封强度sp药包用双零铝箔 |
US11320206B2 (en) | 2019-10-04 | 2022-05-03 | Hamilton Sundstrand Corporation | Pressure vessel with barrier layer |
EP4267376A1 (en) | 2020-12-28 | 2023-11-01 | Alloy Enterprises, Inc. | Homogenizing heterogeneous foils for light alloy metal parts |
US11566589B2 (en) * | 2021-01-20 | 2023-01-31 | International Engine Intellectual Property Company, Llc | Exhaust gas recirculation cooler barrier layer |
CN114261156B (zh) * | 2021-12-28 | 2024-05-03 | 郑州机械研究所有限公司 | 一种钛合金钎焊用多层夹芯钎料箔及其制备方法 |
CN114752829B (zh) * | 2022-05-05 | 2022-10-04 | 银邦金属复合材料股份有限公司 | 新能源动力电池液冷板用复合铝合金板及其制备方法 |
Family Cites Families (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3168381A (en) * | 1960-09-01 | 1965-02-02 | Kaiser Aluminium Chem Corp | Aluminum alloy and article |
US3261724A (en) * | 1965-06-28 | 1966-07-19 | Composite Metal Products Inc | Stainless steel clad aluminum and methods of making same |
US3917151A (en) * | 1973-02-08 | 1975-11-04 | Kaiser Aluminium Chem Corp | Vacuum brazing process |
US4246045A (en) * | 1979-04-24 | 1981-01-20 | Clad Metals, Inc. | Multiple member clad metal products and methods of making the same |
JP2842665B2 (ja) * | 1990-06-01 | 1999-01-06 | 住友軽金属工業株式会社 | アルミニウム製熱交換器 |
JPH06228695A (ja) * | 1993-02-04 | 1994-08-16 | Furukawa Alum Co Ltd | 熱交換器用高強度高耐食性アルミニウム合金複合材 |
TW315338B (ru) * | 1996-02-08 | 1997-09-11 | Showa Aluminiun Co Ltd | |
JP3734302B2 (ja) * | 1996-04-02 | 2006-01-11 | 神鋼アルコア輸送機材株式会社 | ろう付熱交換器用アルミニウム合金製ブレージングシート |
SE9604458L (sv) * | 1996-12-03 | 1998-06-04 | Graenges Ab | Sandwichmaterial med hög hållfasthet efter lödning |
US6251527B1 (en) * | 1998-04-20 | 2001-06-26 | Alcoa Inc. | Alclad inset into grooved ingot |
JP3494591B2 (ja) | 1999-06-23 | 2004-02-09 | 株式会社デンソー | 耐食性が良好な真空ろう付け用アルミニウム合金ブレージングシート及びこれを使用した熱交換器 |
JP2001225187A (ja) * | 2000-02-15 | 2001-08-21 | Sumitomo Light Metal Ind Ltd | 耐食性に優れた熱交換器用アルミニウム合金クラッド材 |
JP2001269794A (ja) * | 2000-03-24 | 2001-10-02 | Kobe Steel Ltd | 熱交換器用アルミニウム合金クラッド材 |
JP2001340989A (ja) * | 2000-05-31 | 2001-12-11 | Kobe Steel Ltd | 成形性が優れたアルミニウム合金製ブレージングシート及びその製造方法 |
JP2002001574A (ja) * | 2000-06-20 | 2002-01-08 | Kobe Steel Ltd | アルミニウム合金製ブレージングシート及びその製造方法 |
US7255932B1 (en) * | 2002-04-18 | 2007-08-14 | Alcoa Inc. | Ultra-longlife, high formability brazing sheet |
JP2004017116A (ja) * | 2002-06-18 | 2004-01-22 | Mitsubishi Alum Co Ltd | ろう付造管チューブ用アルミニウム合金ブレージングシートおよびその製造方法 |
US20040137260A1 (en) * | 2002-11-19 | 2004-07-15 | Clad Metals Llc | Copper clad aluminum core composite material suitable for making a cellular telephone transmission tower antenna |
JP4352454B2 (ja) * | 2003-12-05 | 2009-10-28 | 三菱アルミニウム株式会社 | 強度および耐ろう侵食性に優れた熱交換器用ブレージングシートの製造方法 |
JP4352455B2 (ja) * | 2003-12-22 | 2009-10-28 | 三菱アルミニウム株式会社 | 強度および耐ろう侵食性に優れたブレージングシートの製造方法 |
JP4352456B2 (ja) * | 2003-12-22 | 2009-10-28 | 三菱アルミニウム株式会社 | 強度および耐ろう侵食性に優れたブレージングシートの製造方法 |
JP4401186B2 (ja) * | 2004-02-16 | 2010-01-20 | 株式会社神戸製鋼所 | アルミニウム合金ろう付け部材 |
US7374827B2 (en) | 2004-10-13 | 2008-05-20 | Alcoa Inc. | Recovered high strength multi-layer aluminum brazing sheet products |
JP5414991B2 (ja) * | 2004-10-19 | 2014-02-12 | アレリス、アルミナム、コブレンツ、ゲゼルシャフト、ミット、ベシュレンクテル、ハフツング | アルミニウム合金ろう付けシートおよび軽量のろう付けした熱交換機組立品の製造方法 |
JP4448758B2 (ja) * | 2004-11-02 | 2010-04-14 | 株式会社デンソー | ろう付け性、耐食性および熱間圧延性に優れた熱交換器用アルミニウム合金クラッド材 |
JP4263160B2 (ja) * | 2004-11-16 | 2009-05-13 | 古河スカイ株式会社 | アルミニウム合金クラッド材並びにそれを用いた熱交換器用チューブ及び熱交換器 |
JP4266919B2 (ja) * | 2004-11-30 | 2009-05-27 | 株式会社デンソー | 耐エロージョン・コロージョン性と一般耐食性に優れた熱交換器用アルミニウム合金クラッド材 |
JP5030487B2 (ja) | 2005-08-31 | 2012-09-19 | 昭和電工株式会社 | クラッド材およびその製造方法 |
WO2007042206A1 (en) * | 2005-10-13 | 2007-04-19 | Aleris Aluminum Koblenz Gmbh | Multi-layered brazing sheet |
SE0950756A1 (sv) * | 2009-10-13 | 2011-04-14 | Sapa Heat Transfer Ab | Sandwichmaterial med hög hållfasthet vid hög temperatur för tunna band i värmeväxlare |
-
2008
- 2008-04-18 SE SE0800898A patent/SE533287C2/sv unknown
-
2009
- 2009-02-10 WO PCT/SE2009/050139 patent/WO2009128766A1/en active Application Filing
- 2009-02-10 EA EA201071211A patent/EA025938B1/ru not_active IP Right Cessation
- 2009-02-10 MX MX2010011443A patent/MX2010011443A/es active IP Right Grant
- 2009-02-10 BR BRPI0910597A patent/BRPI0910597A2/pt not_active Application Discontinuation
- 2009-02-10 JP JP2011504958A patent/JP2011520032A/ja active Pending
- 2009-02-10 EP EP09732199.6A patent/EP2271489B1/en active Active
- 2009-02-10 CA CA2721747A patent/CA2721747C/en not_active Expired - Fee Related
- 2009-02-10 PL PL09732199T patent/PL2271489T3/pl unknown
- 2009-02-10 KR KR1020107025692A patent/KR101557903B1/ko active IP Right Grant
- 2009-02-10 US US12/937,914 patent/US8574723B2/en active Active
- 2009-02-10 CN CN200980122186.5A patent/CN102083620B/zh active Active
-
2010
- 2010-11-09 ZA ZA2010/08031A patent/ZA201008031B/en unknown
-
2014
- 2014-04-24 JP JP2014090043A patent/JP5960748B2/ja not_active Expired - Fee Related
Also Published As
Publication number | Publication date |
---|---|
US20110042053A1 (en) | 2011-02-24 |
SE533287C2 (sv) | 2010-08-10 |
US8574723B2 (en) | 2013-11-05 |
EP2271489A1 (en) | 2011-01-12 |
EP2271489B1 (en) | 2019-12-25 |
KR20100136548A (ko) | 2010-12-28 |
CN102083620A (zh) | 2011-06-01 |
WO2009128766A1 (en) | 2009-10-22 |
JP5960748B2 (ja) | 2016-08-02 |
CA2721747C (en) | 2016-01-26 |
SE0800898L (sv) | 2009-10-19 |
EP2271489A4 (en) | 2017-05-03 |
CN102083620B (zh) | 2014-06-18 |
EA025938B1 (ru) | 2017-02-28 |
BRPI0910597A2 (pt) | 2016-08-16 |
MX2010011443A (es) | 2010-12-21 |
CA2721747A1 (en) | 2009-10-22 |
PL2271489T3 (pl) | 2020-05-18 |
KR101557903B1 (ko) | 2015-10-06 |
ZA201008031B (en) | 2011-08-31 |
JP2011520032A (ja) | 2011-07-14 |
JP2014177706A (ja) | 2014-09-25 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EA201071211A1 (ru) | Сэндвичевый материал для пайки с высокой прочностью при высокой температуре | |
IN2012DN02225A (ru) | ||
MX2012003974A (es) | Material de emparedado con alta resistencia a alta temperatura para tiras delgadas en intercambiadores de calor. | |
IN2014MN01665A (ru) | ||
CA2711415A1 (en) | Carburization resistant metal material | |
CN101423906B (zh) | 高弹性高导电无铍铜合金材料及加工工艺 | |
JP2016035112A5 (ru) | ||
MX2018005945A (es) | Hoja de soldadura fuerte y método de producción. | |
MX359572B (es) | Aleacion de aluminio para aleta y método para producir la misma. | |
GB2500825A8 (en) | Alloy and method of production thereof | |
WO2015011346A8 (fr) | Elément de structure extrados en alliage aluminium cuivre lithium | |
WO2017182145A8 (de) | Aluminiumverbundwerkstoff mit korrosionsschutzschicht | |
CN102776409A (zh) | 一种耐蚀铜合金的制备工艺 | |
DE502005007283D1 (de) | Korrosionsbeständige kupferlegierung mit magnesium und deren verwendung | |
MX2020001837A (es) | Lamina de aleacion de aluminio para intercambiador de calor. | |
CN103924174A (zh) | 一种可用于加工耐高温钎焊的铝/钢复合带的热处理工艺 | |
WO2009041194A1 (ja) | 熱間加工性に優れた高強度高導電性銅合金 | |
CN103031472B (zh) | 一种空分设备用钎焊板及其制备方法 | |
RU2011147703A (ru) | Алюминиевая лента с высоким содержанием марганца и магния | |
RU2013125561A (ru) | Титановый сплав с превосходными ингибированием отложения накипи и формуемостью и способы его получения, а также теплообменник или испаритель морской воды | |
CN103173695A (zh) | 含有稀土元素Ce和La的形状记忆不锈钢 | |
RU2011147705A (ru) | Алюминиевая лента с высоким содержанием марганца и очень высоким содержанием магния | |
JP5825218B2 (ja) | ダイクエンチ用ステンレス鋼板およびそれを用いたダイクエンチ部材 | |
JPH044391B2 (ru) | ||
WO2022234207A3 (fr) | Bande ou tôle en alliage d'aluminium pour la fabrication d'échangeurs de chaleur brasés |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
MM4A | Lapse of a eurasian patent due to non-payment of renewal fees within the time limit in the following designated state(s) |
Designated state(s): AM AZ BY KZ KG MD TJ TM RU |