DE9321379U1 - Variable molded part, especially from renewable raw materials - Google Patents

Variable molded part, especially from renewable raw materials

Info

Publication number
DE9321379U1
DE9321379U1 DE9321379U DE9321379U DE9321379U1 DE 9321379 U1 DE9321379 U1 DE 9321379U1 DE 9321379 U DE9321379 U DE 9321379U DE 9321379 U DE9321379 U DE 9321379U DE 9321379 U1 DE9321379 U1 DE 9321379U1
Authority
DE
Germany
Prior art keywords
filling
molded
part according
foam
moulded part
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE9321379U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BioTec Biologische Naturverpackungen GmbH and Co KG
Original Assignee
BioTec Biologische Naturverpackungen GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BioTec Biologische Naturverpackungen GmbH and Co KG filed Critical BioTec Biologische Naturverpackungen GmbH and Co KG
Priority to DE9321379U priority Critical patent/DE9321379U1/en
Priority claimed from DE19934317693 external-priority patent/DE4317693C2/en
Publication of DE9321379U1 publication Critical patent/DE9321379U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

BIOTEC Biologische Naturverpackungen GmbH & Co.
Produktions- und Marketing KG
D-4240 EmmerichBIOTEC Biological Natural Packaging GmbH & Co.
Production and Marketing KG
D-4240 Emmerich

Variables Formteil insbesondere aus nachwachsendenVariable molded part especially from renewable RohstoffenRaw materials

Die Erfindung betrifft ein variables Formteil, insbesondere auf Stärkebasis, das besonders bei Transporten für die Stoßabsorption empfindlicher Güter mit unterschiedlichster Form und Masse sowie für die Wärmedämmung verwendet wird.The invention relates to a variable molded part, in particular based on starch, which is used particularly in the transport of shock-absorbing sensitive goods of various shapes and masses, as well as for thermal insulation.

Formschäume aus Kunststoff (z.B. EPS) und/oder Formteile aus Karton, Wellpappe und Faserguß schützen empfindliche Produkte wie Glaswaren, Porzellan, Erzeugnisse der Elektro-, Haushalts-, Maschinenbau-, Automobil-, Elektronik-, Lebensmittel- und Spielwarenindustrie etc. beim Transport. Formteile müssen für jedes zu schützende Produkt paßgenau hergestellt werden. Daraus ergibt sich eine ebenso große Vielzahl an Verpackungsformteilen wie an zu schützenden Erzeugnissen, mit der Konsequenz von hohen Kosten für die Schutzverpackung, insbesondere bei kleinen Stückzahlen. Neuere Aktivitäten umweltfreundliche Schutzverpackungsmaterialien zu entwickeln, führen zunehmend zu Faserguß- und PuIp-ProduktenMolded foams made of plastic (e.g. EPS) and/or molded parts made of cardboard, corrugated cardboard and fiber-molded cardboard protect sensitive products such as glassware, porcelain, products from the electrical, household, mechanical engineering, automotive, electronics, food and toy industries, etc. during transport. Molded parts must be manufactured to fit each product to be protected. This results in an equally large number of molded packaging parts as there are products to be protected, with the consequence of high costs for protective packaging, especially for small quantities. Newer activities to develop environmentally friendly protective packaging materials are increasingly leading to fiber-molded and pulp products.

auf Basis von Recycling-Papier/-Karton und/oder Cellulose und/oder anderen Naturfasern. Diese Produkte haben aber eine im Vergleich zum EPS weniger gute Schockabsorption und ein viel höheres Gewicht.based on recycled paper/cardboard and/or cellulose and/or other natural fibers. However, these products have less good shock absorption than EPS and are much heavier.

Aus der DE 38 39 225 Al ist es bekannt, Strohfasern in kissenförmige Hüllen zu füllen und als stoßdämpfendes Material in Verpackungsbehältern zu verwenden. Für diesen Zweck ist es ebenso bekannt, zu Kugeln gepreßtes, fein zerkleinertes Stroh als Kissenfüllung zu verwenden. (DE 40 25 257 C2).From DE 38 39 225 A1 it is known to fill straw fibers into pillow-shaped casings and use them as shock-absorbing material in packaging containers. For this purpose it is also known to use finely chopped straw pressed into balls as pillow filling. (DE 40 25 257 C2).

Stroh als Dämpfungsmaterial hat jedoch ebenfalls die Nachteile eines hohen Gewichtes und einer im Verhältnis dazu zu geringen Elastizität, so daß dessen Verwendungsmöglichkeiten stark eingeschränkt sind. Die gegen Stöße schützende. Dämpfungswirkung dieser Strohkugeln gestaltet sich bei größeren auf das Transportgut wirkenden Kräften oder einem hohen Gewicht des Transportgutes nicht zufriedenstellend. Darüber hinaus zerfallen Strohfasern bei zu hoher Beanspruchung und verursachen Staub.However, straw as a damping material also has the disadvantages of being heavy and relatively low in elasticity, so that its possible uses are severely limited. The shock-absorbing effect of these straw balls is not satisfactory when there are large forces acting on the transported goods or when the transported goods are heavy. In addition, straw fibers disintegrate when subjected to excessive stress and cause dust.

Aufgabe der Erfindung ist es, ein variables Formteil zur Verwendung als Transportschutz zu schaffen, das unterschiedlichste Belastungsarten dämpfen kann, mehrfach verwendet werden kann, den Verpackungsaufwand minimiert und vollständig biologisch abbaubar ist. Ferner soll ein Baudämmstoff geschaffen werden.The object of the invention is to create a variable molded part for use as transport protection, which can absorb a wide variety of stresses, can be used multiple times, minimizes packaging costs and is completely biodegradable. Furthermore, a building insulation material is to be created.

Diese Aufgabe wird mit den Merkmalen der Schutzansprüche gelöst. This task is solved with the features of the protection claims.

Bei der Lösung geht die Erfindung von dem Grundgedanken aus, elastische Formteile, aus Stärkeschaum zu fertigen und in eine Hülle aus ebenfalls biologisch abbaubarem Material zu füllen. Der Stärkeschaum ist in variabler Form, Größe und Dichte ausgeführt und besitzt daher auch eine variableThe solution is based on the basic idea of producing elastic molded parts from starch foam and filling them in a shell made of biodegradable material. The starch foam is made in variable shape, size and density and therefore also has a variable

Elastizität. Der Volumenanteil der Füllung wird an den Verwendungszweck z.B. die Transportanforderungen bei der Verwendung als Transportschutz und das Gewicht des Packgutes angepaßt. Die Verwendung der variablen Formteile erfolgt auch als Füllmaterial für Baudämmstoffsysteme.Elasticity. The volume proportion of the filling is adapted to the intended use e.g. the transport requirements when used as transport protection and the weight of the packaged goods. The variable molded parts are also used as filling material for building insulation systems.

Das variable Formteil besitzt folgende Vorteile:The variable molded part has the following advantages:

- Mit wenigen unterschiedlichen Kissenvolumen können ver-1^ schieden große Erzeugnisse auf dem Transport vor Beschädigung durch Schockbelastung wirkungsvoll geschützt werden.- With just a few different cushion volumes, products of different sizes can be effectively protected against damage caused by shock during transport.

- Durch die Variation der Kissenfüllung aus expandierter Stärke sowie durch das Schüttgewicht und die Formgestal-- By varying the cushion filling made of expanded starch as well as the bulk density and the shape design

!5 tung (Kugeln, Zylinder bzw. Hohlzylinder) wird das Schutzpolster auf leichte oder schwere Erzeugnisse angepaßt.!5 tion (balls, cylinders or hollow cylinders) the protective pad is adapted to light or heavy products.

- Die Formteile sind sehr leicht (5 bis 50 kg/m3) , sie können mehrfach verwendet werden, sind antistatisch, vollständig biologisch abbaubar und kompostierbar.- The molded parts are very light (5 to 50 kg/m 3 ), they can be used multiple times, are antistatic, completely biodegradable and compostable.

- Die Herstellung der Formteile direkt beim Anwender, führt zu erheblicher Reduzierung der Maschinen-, Personal- und Raumkosten und vereinfacht den Transport, da im Vergleich zu fertig geschäumten Chips das Transportvolumen erheblich geringer ist.- The production of the molded parts directly at the user's site leads to a significant reduction in machine, personnel and space costs and simplifies transport, as the transport volume is considerably lower compared to ready-foamed chips.

- Bei der Verwendung für Baudämmstoffsysteme läßt sich Stärkeschaum gegenüber bisher gebräuchlichen Mineralfasern sehr einfkach verarbeiten, da sowohl der übliche Juckreiz durch Faserstaub als auch die Gefahr der Gesundheitsschädigung aufgrund der krebserregenden Wirkung entfällt.- When used for building insulation systems, starch foam is much easier to process than the mineral fibers that have been used up to now, as it eliminates the usual itching caused by fiber dust and the risk of damage to health due to its carcinogenic effect.

Im folgenden wird die Erfindung anhand der Zeichnungen näher erläutert. Es zeigen:The invention is explained in more detail below with reference to the drawings. They show:

Fig. la - Ig erfindungsgemäße Ausführungsformen der Stärkeschaumkörper ,Fig. la - ig embodiments of the starch foam bodies according to the invention ,

Fig. 2 das Verfahrensprinzip zur Herstellung erfindungsgemäßer Baudämmstoffsysteme,Fig. 2 the process principle for producing building insulation systems according to the invention,

Fig. 3 eine Ansicht des Baudämmstoffes mit aneinandergereihten Baudämmstoffbeuteln von oben und
Fig. 4 einen Schnitt durch die Figur 3.Fig. 3 a view of the building insulation material with building insulation bags lined up from above and
Fig. 4 is a section through Figure 3.

Nach einem Ausführungsbeispiel der Erfindung zur Ausbildung 1^ eines Transportschutzes wird ein Kissenpolster aus einem Hüllenmaterial, bestehend aus Papier, insbesondere Filterpapier, Teebeutelpapier, Cellulosefaservlies und/oder Textilmaterial gefertigt und mit einer Polsterfüllung aus einem elastischen, flexiblen Stärkeschaum mit kugeliger und/oder !5 zylindrischer Gestalt auf Basis natürlicher Pflanzenstärke versehen (Figuren la bis Ig) . Das Volumen des Hüllenmaterials ist teilweise 50 bis 90 % mit Stärkeschaumkugeln gefüllt, so daß das Schutzpolster sich der Form des zu schützenden Erzeugnisses und der Form des Verpackungsmittels (Umkarton, Kiste, Dose) selbständig anpaßt.According to an embodiment of the invention for forming a transport protection , a cushion pad is made from a cover material consisting of paper, in particular filter paper, tea bag paper, cellulose fiber fleece and/or textile material and provided with a cushion filling made of an elastic, flexible starch foam with a spherical and/or cylindrical shape based on natural plant starch (Figures la to ig). The volume of the cover material is partially filled 50 to 90% with starch foam balls, so that the protective pad automatically adapts to the shape of the product to be protected and the shape of the packaging material (outer carton, box, can).

Durch die allseitige Umhüllung des stoßempfindlichen Erzeugnisses mit den elastischen, aufgeblähten, eingehüllten Stärkekugeln wird das Erzeugnis hervorragend gegen Transportbe-Schädigungen geschützt. Die Stärkeschaumfüllung kann durch Einstellung des Schüttgewichtes zwischen 5 und 50 kg/m3 je nach Anforderungen für leichte oder schwere zu schützende Gegenstände variieren. Ebenso kann die Kissenform auf die geforderte Verpackungsgröße mit einer großen Variationsbreite eingestellt werden.By covering the shock-sensitive product on all sides with the elastic, inflated, wrapped starch balls, the product is excellently protected against damage during transport. The starch foam filling can be varied by adjusting the bulk density between 5 and 50 kg/m 3 depending on the requirements for light or heavy objects to be protected. The cushion shape can also be adjusted to the required packaging size with a wide range of variations.

Für die bedarfsgerechte Verwendung der Formteile ist es möglich, direkt beim Anwender in einem geeigneten kleineren Heißluft- oder Mikrowellengerät geschnittene Hohlstränge oder Granulate zu Stärkeschaumchips aufzublähen.To use the molded parts as required, it is possible to expand hollow strands or granules cut directly by the user in a suitable small hot air or microwave device to form starch foam chips.

Somit kann die Form, Größe, Elastizität und benötigte Menge der Formteile vom Anwender selbst am Einsatzort bestimmt werden.This means that the shape, size, elasticity and required quantity of the molded parts can be determined by the user at the site.

Im Rahmen der Erfindung werden auch solche Formteile beansprucht, die geformte Schaumteile aus Kunststoffschaum, z.B. Polystyrol enthalten und deren Hülle aus Naturprodukten oder auch aus Kunststoffen besteht.The invention also relates to molded parts which contain molded foam parts made of plastic foam, e.g. polystyrene, and whose shell consists of natural products or plastics.

1^ Nach der Erfindung wird der geformte Stärkeschaum auch als Füllmaterial für Baudämmstoffsysteme verwendet. Dazu wird schüttfähiger Stärkeschaum in eine Hülle, insbesondere in Papierschläuche gefüllt, die Baudämmstoffbeutel bilden. Diese werden quer abgesteppt, so daß der Stärkeschaum in seinem jeweiligen Volumenabschnitt des Beutels verbleibt. 1 ^ According to the invention, the shaped starch foam is also used as a filling material for building insulation systems. For this purpose, pourable starch foam is filled into a casing, in particular into paper tubes, which form building insulation bags. These are stitched crosswise so that the starch foam remains in its respective volume section of the bag.

Die Volumenabschnitte des Beutels können unterschiedlich gefüllt oder der abgesteppte Beutel aufgerollt oder gefaltet werden. Die Beutel sind in variablen Abmessungen herstellbar und mit seitlich angeordneten Befestigungslaschen versehen.The volume sections of the bag can be filled differently or the quilted bag can be rolled up or folded. The bags can be produced in variable dimensions and are provided with fastening tabs on the sides.

Über · die Schüttdichte des Stärkeschaumes und den Grad der Beutelfüllung sind die Baudämmstoffbeutel auf einen gewünschten Wärmedämmwert einstellbar.
25The building insulation bags can be adjusted to a desired thermal insulation value using the bulk density of the starch foam and the degree of bag filling.
25

Für die Herstellung der Baudämmstoffbeutel wird als Hülle vorzugsweise Papier, beschichtetes Papier, ein Papier-Aluminiumverbund und/oder Kunststoffolie verwendet.For the production of the building insulation bags, paper, coated paper, a paper-aluminium composite and/or plastic film are preferably used as the casing.

Nach einem anhand der Figuren 2 bis 4 erläutertem weiteren Ausführungsbeispiel werden zwei Bänder 1 des Hüllmaterials kontinuierlich von ihren Rollen 2 abgerollt, über Umlenkrollen 3 gespannt und horizontal übereinander verlaufend bis zu einem bestimmten Abstand zusammengeführt. Eine Uralenkrolle 4According to a further embodiment explained with reference to Figures 2 to 4, two bands 1 of the wrapping material are continuously unrolled from their rolls 2, stretched over deflection rollers 3 and brought together horizontally one above the other up to a certain distance. A Ural guide roller 4

3S besitzt abgesenkte Außenränder, so daß eines der Bänder 1 entlang seiner äußeren Längsseiten mit geringem Abstand von der Außenkante gefalzt wird und so der für die Füllung vor- 3 S has lowered outer edges so that one of the bands 1 is folded along its outer long sides with a small distance from the outer edge and thus the

gesehene Raum vorgeformt wird. Fig. 4 verdeutlicht diese Ausbildung des oberen Bandes 1. In den Zwischenraum zwischen die Bänder 1 wird geformter Stärkeschaum 5, aus dem die Füllung besteht, von einer Füllstoffaufgäbe 6 eingebracht und die Bänder 1 gleichzeitig entlang ihrer äußeren Längsseiten zur Ausbildung eines Schlauches 7 miteinander verschweißt oder in einer anderen geeigneten Weise dicht zusammengefügt. Die Schweißnaht verläuft, wie Figur 3 zeigt, in geringem Abstand vom Rand der Bänder 1 und die äußeren Längsseiten des 1^ Schlauches 7 bilden somit Befestigungslaschen 8, die später das Anbringen der fertigen Baudämmstoffbeutel 9 bei deren bestimmungsgemäßem Gebrauch erleichtert.seen space is preformed. Fig. 4 illustrates this formation of the upper band 1. In the space between the bands 1, shaped starch foam 5, of which the filling consists, is introduced from a filler feeder 6 and the bands 1 are simultaneously welded together along their outer long sides to form a tube 7 or joined tightly together in another suitable manner. The weld seam runs, as Fig. 3 shows, at a short distance from the edge of the bands 1 and the outer long sides of the tube 7 thus form fastening tabs 8, which later facilitate the attachment of the finished building insulation bags 9 when they are used as intended.

Nach einer weiteren Ausführung kann die Hülle ebenso als fertiger Schlauch mit angeformten Befestigungslaschen -9 vorliegen und mit dem Stärkeschaum 5 befüllt werden.According to a further embodiment, the casing can also be available as a finished tube with molded fastening tabs -9 and filled with the starch foam 5.

Gleichzeitig mit dem Einbringen des Stärkeschaumes 5 in die Hülle wird dieser auch in seiner Hülle verdichtet. Durch unterschiedliche Befüllung und Dicke der Baudämmstoffbeutel 9 sind diese auf den gewünschten Wärmedämmwert einstellbar.At the same time as the starch foam 5 is introduced into the casing, it is also compressed in its casing. By varying the filling and thickness of the building insulation bags 9, they can be adjusted to the desired thermal insulation value.

Die Breite der Baudämmstoffbeutel 9 ist entsprechend dem jeweiligen Einsatzgebiet, beispielsweise bei Verwendung für Dachisolationen auf die Sparren- bzw. Balkenabstände abgestimmt und kann 40, 60 oder 80 cm betragen. Die Länge der Baudämmstoffbeutel 9 ist mittels einer Steppeinrichtung 10 einstellbar und richtet sich ebenfalls nach den Einsatzbedingungen. Der fertige Schlauch 7 mit den aneinandergereihten Baudämmstoffbeuteln 9 ist endlos lang ausgebildet und wird auf eine Rolle 11 aufgerollt. Bei der späteren Verarbeitung ist er zweckmäßigerweise an den Steppnähten trennbar. The width of the construction insulation bags 9 is adjusted to the respective area of application, for example when used for roof insulation, to the rafter or beam spacing, and can be 40, 60 or 80 cm. The length of the construction insulation bags 9 can be adjusted using a stitching device 10 and also depends on the conditions of use. The finished tube 7 with the construction insulation bags 9 lined up next to one another is endlessly long and is rolled up onto a roll 11. During later processing, it can be conveniently separated at the stitching seams.

Claims (10)

SchutzansprücheProtection claims 1. Variables Formteil aus nachwachsenden Rohstoffen, insbesondere zur Verwendung als Transportschutz oder als Baudämmstoff, mit einer Hülle und einer Füllung, dadurch gekennzeichnet, daß die Füllung aus geformtem Schaumstoff, insbesondere geformtem Stärkeschaum besteht.1. Variable molded part made of renewable raw materials, in particular for use as transport protection or as building insulation material, with a shell and a filling, characterized in that the filling consists of molded foam, in particular molded starch foam. 2. Variables Formteil aus nachwachsenden Rohstoffen, insbesondere zur Verwendung als Transportschutz oder als Baudämmstoff, mit einer Hülle und einer Füllung, dadurch gekennzeichnet, daß die Füllung aus einer Vielzahl von geformtem, biologisch abbaubaren Stärkeschaumformkörpern besteht.2. Variable molded part made of renewable raw materials, in particular for use as transport protection or as building insulation material, with a shell and a filling, characterized in that the filling consists of a plurality of molded, biodegradable starch foam moldings. 3. Formteil nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Hülle und die Füllung an das Verpackungsgut und/oder die Umverpackung angepaßt ist.3. Moulded part according to claim 1 or 2, characterized in that the casing and the filling are adapted to the packaged goods and/or the outer packaging. 4. Formteil nach Anspruch 1, 2 oder 3, dadurch gekennzeichnet, daß das Material der Hülle aus Papier, Faservlies, Textilmaterial oder einer perforierten Folie aus Kunststoffmaterial besteht.4. Moulded part according to claim 1, 2 or 3, characterized in that the material of the cover consists of paper, nonwoven fabric, textile material or a perforated film made of plastic material. 5. Formteil nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß der Schaumstoff aufgebläht ist.5. Moulded part according to one of claims 1 to 4, characterized in that the foam is inflated. 6. Formteil nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß der Schaumstoff zu kugelförmigen, zylinderförmigen, ringförmigen, S-förmigen, halbringförmigen, kreuzförmigen, Y-förmigen und/oder hohlen Formkörpern oder daraus zusammengesetzten Formkörpern aufgebläht ist.6. Molded part according to one of claims 1 to 5, characterized in that the foam is inflated to form spherical, cylindrical, annular, S-shaped, semi-annular, cross-shaped, Y-shaped and/or hollow molded bodies or molded bodies composed thereof. ■ · ·{■ ·· im· «&igr; (tt, &ngr;"-;-·..'&ogr; S PAn(WcR GSR■ · ·{■ ·· im· «&igr; (tt , &ngr; "-;-·..'&ogr; S PAn(WcR GSR ft M &Lgr;, &Lgr; * » ■ J Ij ·- ..-.._ 1 ~. '■&bull;-&Oacgr;* \ ft M &Lgr;, &Lgr; * » ■ J Ij ·- ..-.._ 1 ~. '■&bull;-&Oacgr;* \ Bi.ot.ec... · :j : ; : &Zgr;9. J3j|i:/go? ^.^tanwältp Bi.ot.ec... · :j : ; : &Zgr;9. J3j|i:/go? ^.^tanlawyersp u.Z.: E 401 GM-DE/D .· *&Iacgr; m I I I <&trade;; T' eurc?ea;i fvTO;: uZ: E 401 GM-DE/D .· *&Iacgr; m II I <&trade;; T' eurc?ea;i fvTO;: ^ * ** · ·*" ·" Siebertsir. 4 - 3&iacgr;·375 MQnCh2n ^ * ** · ·*"·" Siebertsir. 4 - 3&iacgr;·375 MQnCh 2n 7. Formteil nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß der aufgeblähte Schaumstoff ein Schüttgewicht von 2 bis 200 kg/cm3, vorzugsweise 5 bis 50 kg/m3 besitzt.7. Moulding according to one of claims 1 to 6, characterised in that the expanded foam has a bulk density of 2 to 200 kg/cm 3 , preferably 5 to 50 kg/m 3 . 8. Formteil nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß der Stärkeschaum elastisch verformbar ist.8. Moulded part according to one of claims 1 to 7, characterized in that the starch foam is elastically deformable. 9. Formteil nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, daß die Füllung 10 bis 100 Vol.-%, vor-. zugsweise 50 bis 90 Vol.-%, insbesondere 60 bis 80 VoI.-9. Moulded part according to one of claims 1 to 8, characterized in that the filling contains 10 to 100 vol.%, preferably 50 to 90 vol.%, in particular 60 to 80 vol.%. % der Hülle beträgt.% of the shell. 10. Formteil nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, daß die Hülle quer geschlossen bzw. zu Volumenabschnitten abgesteppt ist, in denen die Füllung verbleibt.10. Moulded part according to one of claims 1 to 9, characterized in that the casing is closed transversely or is quilted to form volume sections in which the filling remains. ii. Formteil nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, daß die Füllung flammhemmend, antibakteriell und/oder hydrophob modifiziert ist.ii. Moulded part according to one of claims 1 to 10, characterized in that the filling is flame-retardant, antibacterial and/or hydrophobically modified. 3030 3535
DE9321379U 1993-05-27 1993-05-27 Variable molded part, especially from renewable raw materials Expired - Lifetime DE9321379U1 (en)