DE861748C - Method and device for regenerating rubber - Google Patents
Method and device for regenerating rubberInfo
- Publication number
- DE861748C DE861748C DEK3305D DEK0003305D DE861748C DE 861748 C DE861748 C DE 861748C DE K3305 D DEK3305 D DE K3305D DE K0003305 D DEK0003305 D DE K0003305D DE 861748 C DE861748 C DE 861748C
- Authority
- DE
- Germany
- Prior art keywords
- screw
- alkali
- troughs
- superheated steam
- lye
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren und Vorrichtung zum Regenerieren von Kautschuk Es ist zum Regenerieren von Kautschukwaren das Kochen des vorzerkleinerten Altmaterials in Alkalilauge bekannt, das ein sehr gutes Regenerat ergibt, weil von der Lauge das unter Umständen in den Kautschukwaren befindliche Gewebe zerstört und ein Teil des Schwefels ausgewaschen bzw. gebunden wird.Method and device for regenerating rubber It is for Regeneration of rubber products involves cooking the pre-shredded waste material in Alkali lye known, which results in a very good regenerated material, because of the lye the any tissue in the rubber goods is destroyed and part of the Sulfur is washed out or bound.
Dies Verfahren wird allgemein angewendet, obgleich es sehr teuer ist, denn es braucht zu seiner Durchführung viel Zeit. Das Altmaterial muß z. B. IO bis I5 Stunden in der Lauge gekocht werden. Auch ist der Alkaliverbrauch sehr hoch, weil die dem Gut anhaftende Lauge beim Waschen mit dem Waschwasser bei diesem bekannten Verfahren verlorengeht. Hinzu kommt das Trocknen des Gutes als ebenfalls sehr teurer Arbeitsgang.This method is widely used, although it is very expensive to because it takes a lot of time to carry it out. The old material must z. B. IO to Can be boiled in the lye for 15 hours. The alkali consumption is also very high, because the lye adhering to the good is known when washing with the washing water Procedure is lost. In addition, the drying of the goods is also very expensive Operation.
Erheblich einfacher und billiger ist das sogenannte Heißdampfverfahren, das in verhältnismäßig kurzer Zeit und ohne Aufwand teurer chemischer Mittel durchführbar ist. Bei diesem Verfahren wird das Altmaterial in geschlossenen Kesseln unter Druck mit überhitztem Dampf einige Stunden behandelt. Hierbei sollen die Gewebeteile in dem durch die hohe Temperatur erweichten Material verbrannt werden. The so-called superheated steam process is considerably simpler and cheaper, this can be carried out in a relatively short time and without the use of expensive chemical agents is. In this process, the waste material is put under pressure in closed tanks treated with superheated steam for a few hours. Here, the tissue parts should be in the material softened by the high temperature are burned.
Dies ist bei kurzer Behandlungsdauer und nicht zu hohen Temperaturen nicht mit Sicherheit zu erreichen.This is done with a short treatment time and not too high temperatures cannot be reached with certainty.
Bei längerer Behandlungsdauer und höheren Temperaturen werden zwar die Gewebeteilchen verbrannt, zugleich aber wird die Güte des Regenerats gemindert.With a longer treatment time and higher temperatures the tissue particles are burned, but at the same time the quality of the regenerate is reduced.
Beide Verfahren haben mit allen anderen bekannten Regenerierverfahren den großen Nachteil, daß sie nicht kontinuierlich arbeiten und infolgedessen sehr hohe BedienungskoSten erfordern. Durch das zeitraubende Entleeren und Füllen der Kesselanlagen ist der Wirkungsgrad dieser Verfahren schlecht. Both processes have with all other known regeneration processes the big disadvantage that they do not work continuously and as a result require very high operating costs. Due to the time-consuming emptying and filling of the boiler systems, the efficiency of these processes is poor.
Erfindungsgemäß soll durch das den Gegenstand der Erfindung bildende Verfahren und eine Vorrichtung zu dessen Durchführung diesen bestehenden Mängeln abgeholfen werden. Dies geschieht dadurch, daß das vorzerkleinerte Altmaterial in ununterbrochenem Fluß durch an sich bekannte mit Förder- und Rührmitteln versehene Behälter, wie z. B. Schneckentröge od; dgl., geschickt wird, die von dem Regeneriermittel durchströmt werden. Hierbei lassen sich die Vorteile des Alkalikochverfahrens und des Heißdampfverfahrens nutzbar machen unter Ausschaltung der den einzelnen Verfahren anhaftenden Nachteile. According to the invention by the forming the subject matter of the invention A method and a device for its implementation address these existing shortcomings be remedied. This happens because the pre-shredded waste material in uninterrupted flow through known per se provided with conveying and stirring means Containers, such as B. screw troughs od; Like., Is sent by the regenerant are flowed through. The advantages of the alkali cooking method and Make the superheated steam process usable by eliminating the individual processes inherent disadvantages.
Die erfindungsgemäße Vorrichtung wird hierunter an Hand der schematisch in. der Zeichnung dargestellten Anlage beschrieben. The device according to the invention is shown schematically below with reference to FIG Described in. Plant shown in the drawing.
Fig. I zeigt die Vorrichtung im senkrechten Schnitt, Fig. 2 einen durch verschiedene Ebenen geführten Querschnitt des oberen Teiles der Vorrichtung. Fig. I shows the device in vertical section, Fig. 2 shows a Cross-section of the upper part of the device through different levels.
Die Vorrichtung arbeitet in mehreren Stufen. Zum Kochen in Alkalilauge wird das genügend zerkleinerte Material bei A an dem einen Ende des Troges einer Förder- und Rührschnecke T1, die durch- entsprechende Ausbildung gleichzeitig für eine gute Umwälzung und Durchmischung des Materials mit der Lauge sorgt, aufgegeben und langsam nach der am anderen Ende vorgesehenen Auspreßvorrichtung pl, z. B. einer Schneckenpresse, transportiert. The device works in several stages. For cooking in alkaline lye the sufficiently shredded material becomes one at A at one end of the trough Conveyor and agitator worm T1, which by-appropriate training at the same time for ensures good circulation and mixing of the material with the lye, abandoned and slowly after the extrusion device provided at the other end pl, z. B. one Screw press, transported.
Kurz vor dem Eintritt in die Auspreßvorrichtung zu wird bei F hochkonzentrierte -Frischlauge in den Schneckentrog T1 eingeführt, so daß dasjenige Material, dessen Gewebe schon am weitesten zerstört ist, zuerst mit der frischen Lauge in Berührung kommt, wodurch die restlqse Zerstörung des - Gewebes sichergestellt und beschleunigt und der Kochprozeß in Alkalilauge wesentlich abgekürzt wird. Außerdem ist der Schneckentrog T1 geheizt (Heizmantel H),- so daß ständig Flüssigkeit verdampft und damit die Laugenkonzentration auf hoher und möglichst gleichbleibender Dichte gehalten wird. Man hat es ohne weiteres in der Hand, die Verhältnisse so zu wählen, daß ständig eine der kontinuierlich zugeführten Menge Frischlauge entsprechende Menge Flüssigkeit im Schneckentrog T1 verdampft und abgeführt wird. Es besteht auch die Möglichkeit, mit der Lauge Lösungsmittel, wie Xylol, oder einen Zusatz von Erweichern zuzuführen. In diesem Fall wird der aus dem Schneckentrog T1 bei B1 entweichende Dampf in einem Kondensator niedergeschlagen und das Lösungsmittel zurückgewonnen, um erneut wieder zugeführt zu werden. Shortly before entering the extrusion device, F becomes highly concentrated -Fresh liquor introduced into the screw trough T1 so that the material whose Tissue is already most destroyed, first in contact with the fresh lye comes, whereby the remaining destruction of the - tissue is ensured and accelerated and the cooking process in alkali is significantly shortened. In addition, there is the snail trough T1 heated (heating jacket H), - so that liquid constantly evaporates and with it the alkali concentration is kept at a high and as constant as possible density. One has it without further ado in hand to choose the proportions so that one of the continuous The amount of fresh liquor supplied corresponds to the amount of liquid in the screw trough T1 is evaporated and discharged. There is also the option of using the caustic solution to such as xylene, or an addition of softeners. In this case the Steam escaping from the screw trough T1 at B1 is deposited in a condenser and recovering the solvent to be recycled.
Aus der als Schneckenpresse arbeitenden Auspreßvorrichtung Pl tritt das ausgepreßte Material bei C in -einen zweiten Schneckentrog mit Förderschnecke T2 ein, in welchem das Waschen des Materials dadurch erfolgt, daß es langsam unter ständigem guten Umrühren nach der am anderen Ende vorgesehenen Auspreßvorrichtung p2 durch den Trog gefördert wird. From the extrusion device Pl, which works as a screw press, occurs the pressed material at C in -a second screw trough with a screw conveyor T2 a, in which the washing of the material takes place by slowly taking it under constant good stirring after the extrusion device provided at the other end p2 is promoted through the trough.
-Kurz vor dem Eintritt in die Auspreßvorrichtung p2 wird zum Auswaschen der noch anhaftenden Lauge tei G--warmes Wasser zugeführt. Das Wasser läuft im Gegenstrom zum Material, wodurch das reinste Wasser mit dem schon am weitesten ausgewaschenen Material in Berührung gelangt, so daß bei geringstem Wasserverbrauch ein sehr hoher Auswaschgrad erreicht wird.-Shortly before entering the extrusion device p2 is used to wash out the still adhering lye tei G - supplied with warm water. The water runs in countercurrent to the material, whereby the purest water with the most washed out Material comes into contact, so that with the lowest water consumption a very high Degree of washing is reached.
Das Waschwasser verläßt am Materialeintritt C durch den Überlauf 0 den Trog mit einer hohen Laugenkonzentration: Infolgedessen kann es nach Klärung von mitgeführten Schlammteilchen und nach Zusatz von Alkali wieder als Frischlauge dem Schneckentrog T1 zugeführt werden.The washing water leaves at material inlet C through overflow 0 As a result, it can after clarification: the trough with a high concentration of lye of entrained sludge particles and, after the addition of alkali, again as fresh liquor fed to the screw trough T1.
Es besteht auch die Möglichkeit, den Waschprozeß in zwei Schneckentrögen, die hintereinandergeschaltet sind, durchzuführen, um durch nochmaliges Nachwaschen mit reichlichem Reinwasserüberschuß einen besonders hohen Auswaschgrad zu erreichen. Mit der restlosen Wiederverwendung der Lauge ist auch das bisher viele Sorgen machende Problem der Abführung der laugenhaltigen Abwässer aus den Regenerierwerken gelöst, da keine Lauge mehr abgeführt zu werden braucht. There is also the option of carrying out the washing process in two screw troughs, that are connected in series, to be carried out by rewashing to achieve a particularly high degree of washing with a copious excess of pure water. With the complete reuse of the lye, that is also what has been worrying so far Problem of the removal of the alkaline wastewater from the regeneration plants solved, since no more lye needs to be discharged.
Aus der Auspreßvorrichtung p2 des Waschtroges tritt das ausgepreßte Material bei D in den Trog der Förder- und Rührschnecke zum Regenerieren in Heißdampf ein. Diese Verfahrensstufe kann, weil sie mehr Zeit benötigt, auf mehrere Schneckentröge verteilt sein. The squeezed out comes out of the squeezing device p2 of the washing tub Material at D in the trough of the conveyor and stirring screw for regeneration in superheated steam a. Because it takes more time, this process stage can be carried out on several screw troughs be distributed.
Am Materialeintritt D der Schnecke T8 kann entsprechend dem zu regenerierenden Material Weichmacheröl oder ein anderes Weichmachungsmittel und nötigenfalls, wie z. B. bei Kautschukwaren aus künstlichem Kautschuk, Luft in einer dem Materialdurchlauf entsprechenden Dosierung zugesetzt werden. Die Tröge dieser Schnecken T8 sind geheizt, so daß der aus dem dem Material noch anhaftenden Wasser sich bildende Dampf an den Gehäusewandungen überhitzt und als Heißdampf zum Regenerieren benutzt wird. At the material inlet D of the screw T8 can be regenerated according to the Material softening oil or another softening agent and, if necessary, how z. B. in rubber goods made of artificial rubber, air in one of the material flow appropriate dosage can be added. The troughs of these T8 snails are heated, so that the steam forming from the water still adhering to the material is sent to the Housing walls overheated and used as superheated steam for regeneration.
Durch die Schnecken T3 wird wiederum das Material unter ständigem Umrühren dem Austritt bei E zugeführt, wo es fertig regeneriert ankommt und sofort den Refinierwerken zugeführt werden kann, so daß vom Zerkleinern des Materials bis einschließlich zum Refinern in kontinuierlichem Fluß ohne jeden Handtransport oder manuelle Betätigung gearbeitet werden kann.By the screw T3 the material is in turn under constant Stirring is fed to the outlet at E, where it arrives fully regenerated and immediately can be fed to the refining units, so that from crushing the material up to including for refining in continuous flow without any manual transport or manual operation can be worked.
Der aus den Schneckentrögen der Schnecken T1 und T3 entweichende Dampf findet zum Vorwärmen des Waschwassers Verwendung. The one escaping from the troughs of the screws T1 and T3 Steam is used to preheat the wash water.
Durch diese erfindungsgemäße, kombinierte und kontinuierlich arbeitende Vorrichtung werden bei wesentlich geringerem Alkali-, Dampf-, Waschwasser und Zeitverbrauch in z. B. 4 Stunden für den Materialdurchlauf für das Kochen in Alkali, Waschen und Regenerieren in Heißdampf gegenüber Io bis 15 Stunden Verfahrensdauer beim Regenerieren in Alkali ohne Waschen und Trocknen die gleichen Gütewerte erreicht wie beim reinen Alkaliverfahren. Durch das kontinuierliche Arbeiten fällt jeder Arbeitszeitaufwand für Füllen und Entleeren der Kessel oder fürMaterialtransport fort. By this invention, combined and continuously working Device are with significantly lower alkali, steam, washing water and time consumption in z. B. 4 hours for the material flow for cooking in alkali, washing and Regeneration in superheated steam compared to Io up to 15 hours process duration during regeneration reached the same quality values in alkali without washing and drying as with pure Alkali process. Due to the continuous work, there is no need for any working time for filling and emptying the boiler or for transporting material.
Claims (5)