DE3636644A1 - Use of a concrete mixture as filler for strong-room walls - Google Patents
Use of a concrete mixture as filler for strong-room wallsInfo
- Publication number
- DE3636644A1 DE3636644A1 DE19863636644 DE3636644A DE3636644A1 DE 3636644 A1 DE3636644 A1 DE 3636644A1 DE 19863636644 DE19863636644 DE 19863636644 DE 3636644 A DE3636644 A DE 3636644A DE 3636644 A1 DE3636644 A1 DE 3636644A1
- Authority
- DE
- Germany
- Prior art keywords
- use according
- mixture
- proportion
- wetting agent
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die Erfindung betrifft die Verwendung einer Betonmischung als Füllschicht zwischen zwei Stahlplatten, die Wände, Wand- oder Verstärkungselemente von Tresoren oder Tresorräumen bilden.The invention relates to the use of a concrete mix as Filling layer between two steel plates, the walls, wall or Form reinforcement elements of safes or vaults.
Tresore und Tresorräume weisen üblicherweise Wandelemente auf, die aus zwei äußeren Stahlplatten bestehen, die zwischen sich eine Füllschicht aus einem Spezialbeton einfassen. Diese Wand elemente können als Module hergestellt werden, die die Wandele mente der Tresore oder Tresorräume bilden. Die Wandelemente kön nen auch nachträglich beispielsweise in Tresorräume eingebaut werden, um diesen einen höheren Sicherheitsfaktor zu verleihen. Die Wandelemente können 4 cm bis vorzugsweise 8 cm, 10 cm oder 50 cm dick sein. Zwischen ihren äußeren Deckschichten aus Stahl blech oder Stahlplatten weisen die Wandelemente üblicherweise Einbauten aus Profilstahl oder Stahlträgern auf, die dadurch eine erhöhte Sicherheit gegen Bohren gewährleisten, daß sie die Bohrer ablenken und/oder verklemmen. Zwischen die die Deckschich ten bildenden Stahlplatten wird ein Spezialbeton eingefüllt, so daß diese eine hohe Sicherheit gegen mechanische Beanspruchung, wie Zerstörung durch Bohren, Preßlufthämmer, Meißeln o. dgl., gewährleisten. Derartige Wandelemente weisen auch eine besondere Widerstandsfähigkeit gegen Sprengungen und thermische Behandlun gen, beispielsweise Aufschweißen, auf.Safes and vaults usually have wall elements, which consist of two outer steel plates that are between them enclose a filling layer made of a special concrete. This wall elements can be manufactured as modules that change form elements of the vaults or vaults. The wall elements can can also be retrofitted in vaults, for example to give them a higher safety factor. The wall elements can be 4 cm to preferably 8 cm, 10 cm or 50 cm thick. Between their outer steel layers The wall elements usually have sheet metal or steel plates Internals made of section steel or steel girders, which thereby increased security against drilling ensure that they the Deflect and / or jam the drill. Between the top layers A special concrete is poured into the forming steel plates, so that this provides a high level of security against mechanical stress, such as destruction by drilling, pneumatic hammers, chisels or the like, guarantee. Such wall elements also have a special one Resistance to blasting and thermal treatment conditions, for example welding.
Ein unter dem Markennamen "Densit" bekanntes Füllmaterial weist durch die Zumischung von Siliziumkarbid eine hohe Festigkeit auf. Dieses Füllmaterial ist jedoch sehr teuer und besitzt nicht die optimale Zähigkeit und Biege-Zugfestigkeit.A filling material known under the brand name "Densit" has high strength due to the addition of silicon carbide on. However, this filler is very expensive and does not have the optimal toughness and bending tensile strength.
Aufgabe der Erfindung ist es daher, für die eingangs angegebene Verwendung eine Betonmischung vorzuschlagen, die bei hoher Druck festigkeit und hoher Biege-Zugfestigkeit einen großen Widerstand gegen mechanische Zerstörung bietet.The object of the invention is therefore for the specified Use a concrete mix to suggest that at high pressure strength and high bending tensile strength a great resistance against mechanical destruction.
Erfindungsgemäß wird diese Aufgabe bei einer Verwendung der gat tungsgemäßen Art dadurch gelöst, daß die Betonmischung aus Sili katpulver in einem Anteil von 10 bis 20% des Zementgewichts und einem Benetzungsmittel auf Naphthalain-Sulfonatbasis in einem Anteil von 6 bis 10% des Zementgewichts, Rest Zement, Zuschlag stoffe und Wasser, besteht. Die in der erfindungsgemäßen Verwen dung eingesetzte Betonmischung zeichnet sich insbesondere durch einen geringen Wasser-Zement-Faktor aus, und führt zu einem Beton von hoher Druckfestigkeit und hoher Biege-Zugfestigkeit.According to the invention, this object is achieved when using the gat Appropriate type solved in that the concrete mixture of Sili cat powder in a proportion of 10 to 20% of the cement weight and a naphthalene sulfonate based wetting agent in one Share of 6 to 10% of the cement weight, rest of cement, surcharge substances and water. The use in the invention concrete mix is particularly characterized by a low water-cement factor, and leads to one Concrete with high compressive strength and high bending tensile strength.
Vorzugsweise enthält die Mischung Silikatpulver in einem Anteil von etwa 15% des Zementgewichts. Dieses sogenannte Mikrosilat in Form von SiO₂-Pulver gewährleistet eine beondere Dichtigkeit des erzielten Betons. Das Mikrosilat hat die Wirkung, daß fein ste Hohlräume ausgefüllt werden und der Zement zusätzlich akti viert wird. Der Beton wird daher in seiner Struktur fester und aufgrund weitgehender Porenfreiheit dichter.The mixture preferably contains silicate powder in one proportion about 15% of the cement weight. This so-called microsilate in the form of SiO₂ powder ensures a special tightness of the concrete achieved. The microsilate has the effect of being fine voids are filled in and the cement is additionally activated fourth. The structure of the concrete is therefore stronger and denser due to the absence of pores.
Zweiter wichtiger Bestandteil der erfindungsgemäß verwendeten Betonmischung ist das Benetzungsmittel. Die Mischung enthält vorzugsweise Benetzungsmittel in einem Anteil von etwa 8% des Zementgewichts. Dabei kann das Benetzungsmittel einen Feststoff gehalt von etwa 50% aufweisen. Ein erfindungsgemäß verwendbares Benetzungsmittel ist unter der Bezeichnung Sikament VP 316 im Handel und wird von der Firma Sika GmbH in Hamburg hergestellt. Vorzugsweise weist das Benetzungsmittel einen Feststoffbestand teil an Naphthalainsulfonat von etwa 4% des eingesetzten Zement gewichts auf, wobei der Feststoffgehalt an dem Gesamtbenetzungs mittel etwa 47% beträgt. Neben dem Hauptbestandteil Naphthalain sulfonat kann das Benetzungsmittel noch Stabilisierungsmittel aufweisen. Die erfindungsgemäße Verwendung des Benetzungsmittels ermöglicht einen geringen Wasserzementfaktor, der bei der erfin dungsgemäßen Mischung etwa bei 0,23 liegt.Second important component of those used according to the invention Concrete mix is the wetting agent. The mixture contains preferably wetting agent in a proportion of about 8% of the Cement weight. The wetting agent can be a solid have a content of about 50%. A usable according to the invention Wetting agent is under the name Sikament VP 316 in Trade and is manufactured by Sika GmbH in Hamburg. The wetting agent preferably has a solid inventory Part of naphthalene sulfonate of about 4% of the cement used weight, the solids content of the total wetting average is about 47%. In addition to the main ingredient naphthalene sulfonate, the wetting agent can also be a stabilizing agent exhibit. The use of the wetting agent according to the invention enables a low water cement factor, which is invented mixture according to the invention is approximately 0.23.
Die Zuschläge der erfindungsgemäß verwendeten Mischung können 1 bis 4 Vol.% und vorzugsweise etwa 2 Vol.-% Stahlfasern enthal ten. Die aus kurzen Stiften bestehenden Stahlfasern weisen vor zugsweise an ihren Enden bügelförmige Abkröpfungen auf.The additions of the mixture used according to the invention can 1 to 4% by volume and preferably about 2% by volume of steel fibers The steel fibers consisting of short pins show off preferably bow-shaped bends at their ends.
Die erfindungsgemäß verwendete Mischung kann Zuschläge aus Sand 0/2 mm bis 60%, Rest Basaltedelsplitt 2/5 mm und/oder oberreini sches Material 2/8 mm, also überwiegend quarzitisches Material, enthalten.The mixture used according to the invention can be sand aggregates 0/2 mm to 60%, the rest of basalt chippings 2/5 mm and / or top clean material 2/8 mm, mainly quartzite material, contain.
Zusätzlich kann der Mischung ein Kunststoffbinder oder auch Korundpulver zugesetzt werden. In addition, the mixture can be a plastic binder or Corundum powder can be added.
Die erfindungsgemäß verwendete Mischung hat in frischem Zustand einen Ausbreitwert von ca. 60 cm ohne Schock (nach DIN 1045).The mixture used according to the invention is fresh a spread value of approx. 60 cm without shock (according to DIN 1045).
Aus der erfindungsgemäß verwendeten Betonmischung hergestellte Betonplatten wurden Tests unterworfen und bewiesen dabei eine sehr viel höhere Widerstandsfähigkeit als bekannte bisher ver wendete Betone.Made from the concrete mix used in the invention Concrete slabs were subjected to tests and proved one much higher resistance than known ver applied concrete.
Das der erfindungsgemäß verwendeten Mischung zugesetzte Mikro silat kann Pulver- oder Granulatform aufweisen oder aber auch flüssig sein. Das Silikatpulver hat vorzugsweise eine Feinheit von etwa 20000 Blaine. In Flüssigform liegt das Mikrosilat als Emulsion vor.The micro added to the mixture used according to the invention silate can be in powder or granule form or else be fluid. The silicate powder preferably has a fineness of about 20,000 Blaine. The microsilate is in liquid form as Emulsion before.
Neben den vorstehend genannten Bestandteilen können der Mischung noch die Zähigkeit erhöhende Materialien, wie beispielsweise Karbide, zugesetzt werden. Die erfindungsgemäß verwendete Mischung soll keine oxidierend wirkenden Bestandteile enthalten, die den Stahl angreifen können. Insbesondere sind daher Chloride zu vermeiden.In addition to the above ingredients, the mixture materials which increase toughness, for example Carbides. The used according to the invention Mixture should not contain any oxidizing components that can attack the steel. Chlorides in particular are therefore to avoid.
Schließlich können auch Betonverzögerer zugesetzt werden, die zu einem besseren Aufschlag der Zementkörner führen.Finally, concrete retarders can also be added lead to a better impact of the cement granules.
Claims (10)