DE3325664A1 - Enamel badge with reflecting surfaces - Google Patents

Enamel badge with reflecting surfaces

Info

Publication number
DE3325664A1
DE3325664A1 DE19833325664 DE3325664A DE3325664A1 DE 3325664 A1 DE3325664 A1 DE 3325664A1 DE 19833325664 DE19833325664 DE 19833325664 DE 3325664 A DE3325664 A DE 3325664A DE 3325664 A1 DE3325664 A1 DE 3325664A1
Authority
DE
Germany
Prior art keywords
screen printing
enamel
layer
glass beads
printing ink
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE19833325664
Other languages
German (de)
Inventor
Peter Dipl.-Ing. Huber (FH), 8032 Gräfelfing
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUBER PETER DIPL ING FH
Original Assignee
HUBER PETER DIPL ING FH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUBER PETER DIPL ING FH filed Critical HUBER PETER DIPL ING FH
Priority to DE19833325664 priority Critical patent/DE3325664A1/en
Publication of DE3325664A1 publication Critical patent/DE3325664A1/en
Ceased legal-status Critical Current

Abstract

The invention relates to badges with reflecting surfaces, consisting of a substrate which bears an enamel coating and an illustration, applied to this enamel coating, consisting of stoved ceramic screen printing inks or a stoved ceramic transfer, and is characterised in that the layer of screen printing inks or transfer layer bears glass beads on its surface. The reflective surfaces forming the illustration possess high adhesive strength and very good reflective properties and durability.

Description

Beschreibung description

Die Erfindung betrifft Emailschilder mit reflektierenden Oberflächen.The invention relates to enamel signs with reflective surfaces.

Emaillierte bedruckte Schilder finden in vielen Gebieten der Technik, in der Werbung, im Straßen- und Schienenverkehrswesen und im täglichen Leben in zunehmendem Maße Verwendung. Als Warn- und Signaleinrichtungen verwendete Schilder sollen dabei möglichst weit und auch unter schlechten Sichtbedingungen wahrnehmbar und insbesondere auch von anderen optischen Eindrücken des modernen Lebens auffallend und leicht unterscheidbar sein. Für eine besonders gute und sichere Unterscheidbarkeit ist es jedoch wünschenswert, die mit Emailschildern hervorgerufenen Effekte noch zu verstärken oder auch abzuwandeln.Enamelled printed signs are used in many areas of technology, in advertising, road and rail transport, and everyday life in increasing use. Signs used as warning and signaling devices should be perceptible as far as possible and even under poor visibility conditions and especially striking from other visual impressions of modern life and be easily distinguishable. For a particularly good and reliable differentiation however, it is desirable to still have the effects created with enamel signs to strengthen or to modify.

Aufgabe der vorliegenden Erfindung ist deshalb die Bereitstellung von Emailschildern, die die zur Verwendung für Warn- und Signaleinrichtungen erforderlichen Eigenschaften besitzen und insbesondere sehr gut wahrnehmbar und unterscheidbar sind.The object of the present invention is therefore to provide of enamel signs, which are necessary for use for warning and signaling devices Have properties and, in particular, are very easily perceptible and distinguishable are.

Diese Aufgabe wird erfindungsgemäß gelöst durch ein Emailschild mit reflektierenden Oberflächen, bestehend aus einer Unterlage, die eine Emailbeschichtung trägt, und einer auf dieser Emailbeschichtung aufgebrachten Zeichnung aus Siebdruckfarben, das dadurch gekennzeichnet ist, daß die Siebdruckfarbenschicht an ihrer Oberfläche Glaskügelchen trägt.According to the invention, this object is achieved by an enamel sign reflective surfaces consisting of a backing that has an enamel coating and a drawing made of screen printing inks applied to this enamel coating, which is characterized in that the screen printing ink layer on its surface Bears glass beads.

Das erfindungsgemäße Emailschild wird durch die beigefügte Schnittzeichnung erläutert. In dieser bezeichnet 1 die Unterlage, 2 die Emailbeschichtung aus 2a Grundemail und 2b Deckemail, 3 die eingebrannte keramische Siebdruckfarbenschicht und 4 Glaskügelchen.The enamel sign according to the invention is illustrated by the attached sectional drawing explained. In this, 1 designates the base, 2 the enamel coating from FIG. 2a Base enamel and 2b cover enamel, 3 the burned-in ceramic screen printing paint layer and 4 glass beads.

Als Unterlage für die Emailbeschichtung kann jede für eine solche Beschichtung geeignete und unter Emaillierbedingungen beständige Unterlage verwendet werden. Üblicherweise werden Unterlagen aus Metall verwendet, wie z. B. Eisenblech, Stahlblech, Gußeisen, Leichtmetalle oder Leuchtmetallegierungen, wie zum Beispiel Aluminium, usw.As a base for the enamel coating, any Coating suitable and under enamelling conditions resistant underlay used will. Usually, metal bases are used, such as B. iron sheet, Sheet steel, cast iron, light metals or luminous metal alloys, such as Aluminum, etc.

Die Art und Zusammensetzung der verwendeten Emailbeschichtung ist insbesondere von der Art der Unterlage und vom Verwendungszweck abhängig; im allgemeinen lassen sich alle üblichen Emailbeschichtungen, die für Schilder geeignet sind, anwenden, wie Grundemail- und Deckemailarten, Aluminiumemail, Hochtemperaturemail, Keramikemail usw. Geeignet sind sowohl Opak-, Halbopak-, Transparentemails und Glasuren. Abhängig vom speziellen Verwendungszweck können Weißemailschichten oder auch matte oder farbige Emaillierungen verwendet werden. Bevorzugt sind im allgemeinen Weißemails auf Titandioxid-Basis, wie z. B. Bortitanweißemail sowie Zirkon- und Antimongetrübte Emails. Wenn erforderlich, kann die Emailbeschichtung auch aus zwei oder mehreren Emaillierungen bestehen, z. B. aus einer Grund- und mehreren Deckemailschichten.The type and composition of the enamel coating used is in particular depending on the type of document and the intended use; in general all common enamel coatings that are suitable for signs can be used, such as base enamel and top enamel types, aluminum enamel, high temperature enamel, ceramic enamel etc. Both opaque, semi-opaque, transparent enamels and glazes are suitable. Addicted White enamel layers or matt or colored enamel layers can be used for special purposes Enamels are used. In general, white enamels based on titanium dioxide are preferred, such as B. boron titanium white enamel as well as zirconium and antimony opaque enamels. If necessary, the enamel coating can also consist of two or more enamels, z. B. from a base and several top enamel layers.

Die Zeichnung der Schilder (Beschriftung, Symbole, Muster, bildhafte Darstellungen usw.) wird erfindungsgemäß durch eine Siebdruckfarbenschicht gebildet. Als Siebdruckfarben werden vorzugsweise übliche einbrennbare keramische Emailsiebdruckfarben verwendet. Art, Farbe und Zusammensetzung richten sich dabei insbesondere nach dem Verwendungszweck. Die handelsüblichen Emailsiebdruckfarben sind im wesentlichen ganz ähnlich zusammengesetzt wie die Emails selbst, sind jedoch feiner vermahlen und enthalten zusätzlich noch beim Einbrennen verschwindende Bindemittel. Geeignete Siebdruckfarben sind z. B. unter den Warenzeichen Vitromail (Bayer AG) und Sicopal (BASF) sowie von den Firmen Ferro und Degussa erhältlich. Zur Erzielung mehrfarbiger Zeichnungen können dabei auch zwei oder mehrere verschieden gefärbte Siebdruckfarben verwendet werden. Die Dicke der Siebdruckfarbschichten beträgt vorzugsweise 30 bis 60 Am, und insbesondere 40 bis 50 #m.The drawing of the signs (lettering, symbols, patterns, pictorial Representations, etc.) is formed according to the invention by a screen printing ink layer. As screen printing inks are preferably conventional ceramic ceramic Enamel screen printing inks used. The type, color and composition depend on it especially according to the intended use. The commercially available enamel screen printing inks are essentially composed very similarly to the emails themselves, but they are finely ground and also contain binding agents that disappear during stoving. Suitable screen printing inks are e.g. B. under the trademark Vitromail (Bayer AG) and Sicopal (BASF) and from Ferro and Degussa. To achieve Multicolored drawings can also be two or more differently colored Screen printing inks can be used. The thickness of the screen printing ink layers is preferably 30 to 60 µm, and especially 40 to 50 #m.

Erfindungsgemäß trägt die Siebdruckfarbschicht an ihrer Oberfläche Glaskügelchen. Die Glaskügelchen können dabei über eine Haftschicht mit dieser verbunden sein, ober liegen vorzugsweise direkt auf der Siebdruckfarbenschicht auf. Als Haftschichtbildner kann z. B. eine Paste dienen, die geeignete Bindemittel, wie z. B.According to the invention, the screen printing ink layer carries on its surface Glass beads. The glass beads can be connected to the latter via an adhesive layer be, upper are preferably directly on the screen printing ink layer. As an adhesive layer former can e.g. B. serve a paste, the suitable binder, such as. B.

Kolophoniumester, glasbildende Bestandteile, wie z. B.Rosin esters, glass-forming ingredients, such as. B.

Silikate, und/oder Metalloxide, wie z. B. Titandioxid, oder auch sogenannte Haftoxide, wie z. B. Kobaltoxid und/oder Nickeloxid, in einem Lösungsmittel wie z. B.Silicates, and / or metal oxides, such as. B. titanium dioxide, or so-called Adhesive oxides, such as. B. cobalt oxide and / or nickel oxide, in a solvent such as z. B.

Terpentinöl, Ester usw. enthalten. Die mengenmäßige Zusammensetzung kann in weiten Grenzen variieren; die Haftschichten können z. B. eine den Deckemails oder den Emailsiebdruckfarben entsprechende oder ähnliche Zusammensetzung haben. Die Farbe der Haftschicht kann von der der Siebdruckschicht abweichen; vorzugsweise ist die Haftschicht voll transparent und besitzt die gleiche Farbe wie die Siebdruckschicht oder ist farblos.Contains turpentine oil, esters, etc. The quantitative composition can vary within wide limits; the adhesive layers can e.g. B. one of the cover emails or have a composition corresponding or similar to the enamel screen printing inks. The color of the adhesive layer can differ from that of the screen printing layer; preferably the adhesive layer is fully transparent and has the same colour like the screen printing layer or is colorless.

Zur Bildung der Haftschicht kann auch eine mit der für den Siebdruck verwendeten Druckfarbe gleiche oder verschiedene Siebdruckfarbe verwendet werden. Die Dicke der Haftschicht beträgt in der Regel zwei Zehntel bis vier Zehntel der Dicke der Siebdruckfarbenschicht. Insbesondere bei nicht voll transparenten Haftschichten soll sie möglichst dünn sein, um den Farbeffekt der Siebdruckfarbenschicht nicht nennenswert zu reduzieren.To form the adhesive layer, one can also use one for screen printing the same or different screen printing inks can be used. The thickness of the adhesive layer is usually two tenths to four tenths of that Thickness of the screen printing ink layer. Especially with not fully transparent adhesive layers it should be as thin as possible so as not to affect the color effect of the screen printing ink layer to reduce significantly.

Die reflektierenden Glaskügelchen besitzen vorzugsweise einen Berechnungsindex (nD20) von etwa 1,5 bis 2,2. Ihr Durchmesser beträgt vorzugsweise 30 bis 600 #m, und insbesondere 200 bis 450 #m. Im allgemeinen werden besonders gute Effekte erzielt, wenn der Durchmesser der Glaskügelchen der Dicke der Druckfarbenschicht entspricht oder größer ist, und vorzugsweise das 2- bis 15-fache, insbesondere das 5- bis 10-fache der Dicke der Druckfarbenschicht beträgt. Zur Erzielung besonderer Effekte können die Glaskügelchen auch eingefärbt sein; in der Regel sind sie aber ungefärbt. Besonders starke Reflexionen mit hoher Signalwirkung lassen sich z. B. mit ungefärbten Glaskügelchen auf einer weißen, gelben und insbesondere roten Druckfarbenschicht erzielen. Die Dichte der Glaskügelchen auf ihrer Unterlage liegt zwischen der dichtestmöglichen einschichtigen Flächenpackung und einer Dichte von einem Kügelchen/1 mm2.The reflective glass beads preferably have a refractive index (nD20) from about 1.5 to 2.2. Their diameter is preferably 30 to 600 #m, and especially 200 to 450 #m. In general, particularly good effects are achieved when the diameter of the glass beads corresponds to the thickness of the ink layer or more, and preferably 2 to 15 times, particularly 5 to 10 times is the thickness of the ink layer. To achieve special effects you can the glass beads also be colored; as a rule, however, they are uncolored. Particularly strong reflections with a high signaling effect can e.g. B. with uncolored glass beads on a white, yellow and especially red ink layer. the The density of the glass beads on their base is between the closest possible single-layer area packing and a density of one bead / 1 mm2.

Gemäß einer Abwandlung der Erfindung weist das reflektierende Emailschild anstelle der Siebdruckfarbenschicht eine Schicht aus einem eingebrannten keramischen Abziehbild auf. Einbrennbare keramische Abziehbilder sind bekannt und im Handel erhältlich. Es hat sich überraschenderweise gezeigt, daß derartige keramische Abziehbilder ebenfalls als Träger für die reflektierenden Glaskügelchen geeignet sind. Bezüglich der einzuhaltenden Beziehungen zwischen dem Durchmesser der Glaskügelchen und der Dicke der einbrennbaren keramischen Abziehbildschicht gelten die obigen Ausführungen hinsichtlich der Sieberuckfarbenschicht sinngemäß.According to a modification of the invention, the reflective enamel sign instead of the screen printing ink layer, a layer of a burnt-in ceramic Decal on. Burn-in ceramic decals are known and commercially available available. It has Surprisingly shown that such ceramic decals also as a carrier for the reflective glass beads are suitable. Regarding the relationships to be observed between the diameter the glass beads and the thickness of the burn-in ceramic decal layer the above statements apply accordingly with regard to the screen back color layer.

Gegenstand der Anmeldung ist auch ein Verfahren zur Herstellung der erfindungsgemäßen Schilder. Das Verfahren ist dadurch gekennzeichnet, daß man auf in der Emaillierungstechnik übliche Weise die Emailbeschichtung einfarbig oder auch mehrfarbig schabloniert oder gebürstet aufbringt und einfach oder mehrfach einbrennt, auf die Emailbeschichtung dann die Zeichnung unter Verwendung von Siebdruckfarben aufbringt und entweder die noch feuchte Bedruckung mit den Glaskügelchen versieht und dann unter Feueremaillierungsbedingungen einbrennt, oder die Bedruckung einbrennt, auf die so hergestellte Bedruckung eine Haftschicht aufbringt, die noch feuchte Haftschicht mit den Glaskügelchen versieht und dann unter Feueremaillierungsbedingungen einbrennt.The application also relates to a method for producing the signs according to the invention. The method is characterized in that one on In the enamelling technique usual way the enamel coating monochrome or also applies multi-colored stencils or brushes and burns in one or more times, then apply the drawing to the enamel coating using screen printing inks applies and either provides the still moist printing with the glass beads and then stoved under fire enamelling conditions, or the printing stoved, applies an adhesive layer to the printing produced in this way, which is still moist Adhesive layer provided with the glass beads and then under fire enamelling conditions burns in.

Das Aufbringen der Siebdruckfarbe erfolgt vorzugsweise im Siebdruckverfahren. Andere Druck- und Spritzmethoden können jedoch ebenfalls angewendet werden.The screen printing ink is preferably applied using the screen printing process. However, other printing and spraying methods can also be used.

Zur Herstellung der Zeichnung werden die Siebdruckfarben im gewünschten Muster z. B. im Siebdruckverfahren aufgebracht. Vor ihrem Aufbringen werden die Siebdruckfarben mit Siebdrucköl auf die für die Verarbeitung erforderliche Konsistenz eingestellt. Wird keine Haftschicht verwendet, so werden die Glaskügelchen auf die noch feuchte Emailsiebdruckfarbenschicht aufgebracht, was zweckmäßigerweise durch Bestreuen (Bestäuben) geschieht, und dann wird die bestreute Emailsiebdruckfarbenschicht nach dem Trocknen bei Raumtemperatur oder etwas erhöhter Temperatur unter Feueremaillierungsbedingungen eingebrannt.To produce the drawing, the screen printing inks are used in the desired Pattern z. B. applied by screen printing. Before they are applied, the Screen printing inks with screen printing oil to the consistency required for processing set. If no adhesive layer is used, the glass beads are placed on the still moist enamel screen printing ink layer applied, what expedient is done by sprinkling (dusting), and then the sprinkled enamel screen printing ink layer is made after drying at room temperature or slightly elevated temperature under fire enamelling conditions burned in.

Das Einbrennen der Emailsiebdruckfarbenschicht und der mit den Kügelchen bestreuten Emailsiebdruckfarbenschicht oder Haftschicht kann unter den in der Feueremaillierungstechnik üblichen Bedingungen erfolgen. In der Regel erfolgt das Brennen bei Temperaturen zwischen 700 und 800 °C, vorzugsweise bei 750 bis 780 OC. Die Emailsiebdruckfarben sintern aufgrund ihrer geringeren Teilchengröße im allgemeinen bereits bei niedrigeren Temperaturen als die Emailbeschichtung, zweckmäßigerweise werden jedoch Emailschicht und die Emailsiebdruckfarbe und gegebenenfalls Haftschicht bei den gleichen Temperaturen, aber meist mit verschiedener Brenndauer, eingebrannt.The baking of the enamel screen printing ink layer and that with the beads sprinkled enamel silk-screen ink layer or adhesive layer can be used in the fire enamelling technique usual conditions. As a rule, the firing takes place at temperatures between 700 and 800 ° C, preferably at 750 to 780 OC. The enamel screen printing inks sinter due to their smaller particle size in general already at lower Temperatures than the enamel coating, however, the enamel layer is expedient and the enamel screen printing ink and optionally adhesive layer at the same temperatures, but mostly with different burn times, branded.

Unter den erfindungsgemäß angewandten Temperatur- und Zeitbedingungen schmelzen bzw. sintern die Glaskügelchen noch nicht in einem Ausmaß, das die Reflexionsverbesserung beeinträchtigen würde. Eine höhere Temperatur als 800 °C ist jedoch nicht anwendbar, weil dann in zunehmendem Maße Trübungen und Blasenbildung auftreten und die Kügelchen von der Emailschicht überzogen und abgedeckt werden, wodurch sich eine merkliche Verschlechterung der Reflexion ergibt. Als Brennöfen werden die handelsüblichen Emaillieröfen verwendet.Under the temperature and time conditions used according to the invention the glass beads do not yet melt or sinter to an extent that the improvement in reflection would affect. However, a temperature higher than 800 ° C is not applicable, because cloudiness and blistering then occur to an increasing extent and the globules be covered and covered by the enamel layer, creating a noticeable Reflection deterioration results. The standard kilns are used as kilns Enamelling ovens used.

Gemäß einer Abwandlung des Verfahrens der Erfindung wird anstelle von einbrennbaren keramischen Siebdruckfarben ein einbrennbares keramisches Abziehbild verwendet. Dieses wird in der bei Abziehbildern üblichen Weise angefeuchtet, auf die Emailbeschichtung aufgebracht und nach Abziehen der Trägerfolie- bzw. des Trägerpapiers wird auf die noch feuchte einbrennbare Abziehbildschicht die Glaskügelchenschicht aufgebracht.According to a modification of the method of the invention, instead of a burn-in ceramic decal of burn-in ceramic screen printing inks used. This is done in the usual way for decals moistened, applied to the enamel coating and after peeling off the carrier film or the carrier paper is stoved onto the still moist stoving transfer layer the glass bead layer applied.

Das Einbrennen erfolgt dann wie oben bei der Siebdruckfarbenschicht näher erläutert.The stoving is then carried out as above for the screen printing ink layer explained in more detail.

Die erfindungsgemäßen Schilder weisen, auch ohne Zwischenschaltung einer Haftschicht, eine überraschend gute Haftung und eine sehr gleichmäßige Einbettung der reflektierenden Glaskügelchen auf, wodurch sehr gute Reflexionswerte erreicht werden. Dies gewährleistet eine sehr gute Wahrnehmbarkeit und Unterscheidbarkeit auch auf weite Entfernung und unter schlechten Sichtbedingungen. Aufgrund dieser Eigenschaften eignen sich die erfindungsgemäßen Schilder deshalb insbesondere hervorragend zur Verwendung für Warn- und Signaleinrichtungen, Werbemittel, Hinweisschilder und dergleichen.The signs according to the invention show, even without interposition an adhesive layer, surprisingly good adhesion and very even embedding the reflective glass beads, which achieves very good reflection values will. This ensures a very good perceptibility and distinguishability even over long distances and under poor visibility conditions. Based on these The signs according to the invention are therefore particularly outstandingly suitable for properties for use for warning and signaling devices, advertising material, information signs and like that.

Gegenüber den bekannten Reflexfolien liegt eine bessere Dauerhaftigkeit und Haltbarkeit vor.Compared to the known reflective films, there is better durability and shelf life before.

Das folgende Beispiel erläutert die Erfindung näher, ohne sie darauf zu beschränken.The following example explains the invention in more detail without it being dependent on it to restrict.

Beispiel Auf ein in üblicher Weise emailliertes Stahlblech (60 x 30 cm, Blechstärke 1,5 mm) wird rote handelsübliche Emailsiebdruckfarbe im gewünschten Muster durch Aufrakeln im Siebdruck aufgebracht. Dicke der Farbschicht 40 bis 50 #m. Die noch feuchte Siebdruckfarbenschicht wird mit reflektierenden Glaskügelchen (Kügelchenfraktion mit einem Durchmesser von 230 bis 420 #m) bestreut, wobei die nicht haften gebliebenen Kügelchen ablaufen gelassen werden. Die bestreute Schicht wird bei Raumtemperatur getrocknet und bei 760 + 10 °C in einem besonders üblichen Emailierofen eingebrannt. Einbrenndauer 0,5 bis 2 Minuten. Es wird ein Schild erhalten, dessen Muster eine gut haftende, sehr gut und gleichmäßig reflektierende Schicht aufweist.Example On a steel sheet enamelled in the usual way (60 x 30 cm, sheet thickness 1.5 mm) standard red enamel screen printing ink is used in the desired Pattern applied by screen printing with a doctor blade. Thickness of the paint layer 40 to 50 #m. The still damp screen printing ink layer is covered with reflective glass beads (Bead fraction with a diameter of 230 to 420 #m) sprinkled, with the Any beads that have not adhered are allowed to drain. The sprinkled layer is dried at room temperature and at 760 + 10 ° C in a particularly common Burned-in enamel furnace. Burn-in time 0.5 to 2 minutes. A shield will be given whose pattern is a well-adhering, very good and evenly reflective layer having.

Claims (15)

Emailschild mit reflektierenden Oberflächen Patentansprüche 1. Emailschild mit reflektierenden Oberflächen, bestehend aus einer Unterlage, die eine Emailbeschichtung trägt, und einer auf dieser Emailbeschichtung aufgebrachten Zeichnung aus eingebrannten keramischen Siebdruckfarben, d a d u r c h g e k e n n z e i c h n e t , daß die Siebdruckfarbenschicht an ihrer Oberfläche Glaskügelchen trägt. Enamel sign with reflective surfaces Patent claims 1. Enamel sign with reflective surfaces, consisting of a base that has an enamel coating and a drawing made from burned-in on this enamel coating ceramic screen printing inks, noting that the Screen printing ink layer carries glass beads on its surface. 2. Schild nach Anspruch 1, d a d u r c h g e k e n n z e i c h n e t , daß die Dicke der Siebdruckfarbenschicht 30 bis 60 #m beträgt.2. Sign according to claim 1, d a d u r c h g e k e n n z e i c h n e t that the thickness of the screen printing ink layer is 30 to 60 µm. 3. Schild nach Anspruch 1 oder 2, d a d u r c h g e k e n n z e i c h n e t , daß die Glaskügelchen mit der Siebdruckfarbenschicht über eine Haftschicht verbunden sind.3. Sign according to claim 1 or 2, d a d u r c h g e k e n n z e i c h n e t that the glass beads with the screen printing ink layer over an adhesive layer are connected. 4. Schild nach Anspruch 3, d a d u r c h g e k e n n z e i c h n e t , daß die Haftschicht aus einer Email-Siebdruckfarbe gebildet ist.4. Shield according to claim 3, d a d u r c h g e k e n n z e i c h n e t that the adhesive layer is formed from an enamel screen printing ink. 5. Schild nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß die Glaskügelchen einen Brechungsindex (n20) von 1,5 bis 2,2 besitzen.5. Shield according to one of claims 1 to 4, characterized in that that the glass beads have a refractive index (n20) of 1.5 to 2.2. 6. Schild nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß die Glaskügelchen einen Durchmesser von 30 bis 600 #m, insbesondere von 200 bis 450 #m besitzen.6. Shield according to one of claims 1 to 5, characterized in that that the glass beads have a diameter of 30 to 600 #m, in particular of 200 up to 450 #m. 7. Schild nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß der Durchmesser der Glaskügelchen das 2- bis 15-fache, insbesondere das 5- bis 10-fache der Dicke der Siebdruckfarbenschicht trägt.7. Shield according to one of claims 1 to 6, characterized in that that the diameter of the glass beads 2 to 15 times, especially 5 to 10 times the thickness of the screen printing ink layer. 8. Schild nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß die Dichte der Glaskügelchen auf ihrer Unterlage zwischen der dichtestmöglichen einschichtigen Flächenpackung und einer Dichte von 1 Kügelchen/l mm2 liegt.8. Shield according to one of claims 1 to 7, characterized in that that the density of the glass beads on their base between the closest possible single-layer area packing and a density of 1 globule / l mm2. 9. Schild nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, daß es mit einer Schutzschicht überzogen ist.9. Shield according to one of claims 1 to 8, characterized in that that it is covered with a protective layer. 10. Schild nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß es anstelle einer Siebdruckfarbenschicht eine keramische Abziehbildschicht aufweist.10. Shield according to one of the preceding claims, characterized in that that it has a ceramic decal layer instead of a screen printing ink layer. 11. Verfahren zur Herstellung eines Schilds nach einem der Ansprüche 1 bis 9, d a d u r c h g e k e n n z e i c h n e t , daß man auf der Unterlage auf übliche Weise die Emailbeschichtung einfarbig oder auch mehrfarbig schabloniert oder gebürstet aufbringt und einfach oder mehrfach einbrennt, auf die Emailbeschichtung dann die Zeichnung unter Verwendung von einbrennbaren keramischen Siebdruckfarben aufbringt und entweder die noch feuchte Bedruckung mit den Glaskügelchen versieht und dann unter Feueremaillierungsbedingungen einbrennt, auf die so hergestellte Bedruckung eine Haftschicht aufbringt, die noch feuchte Haftschicht mit den Glaskügelchen versieht und dann unter Feueremaillierungsbedingungen einbrennt.11. A method for producing a sign according to any one of the claims 1 to 9, d u r c h e k e n nn z e i c h n e t that one on the pad on Usually, the enamel coating is stenciled in one or more colors or brushed and stoved once or several times onto the enamel coating then the drawing using burn-in ceramic screen printing inks applies and either provides the still moist printing with the glass beads and then baked under fire enamelling conditions onto the one so produced Printing applies an adhesive layer, the still moist adhesive layer with the glass beads and then baked under fire enamelling conditions. 12. Verfahren nach Anspruch 11, d a d u r c h g e k e n n z e i c h n e t , daß man die Haftschicht im Siebdruckverfahren aufbringt.12. The method according to claim 11, d a d u r c h g e k e n n z e i c It does not mean that the adhesive layer is applied by screen printing. 13. Verfahren nach Anspruch 11 oder 12, dadurch gekennzeichnet, daß man bei einer Temperatur von 700 bis 800 °C, insbesondere bei 750 bis 780 °C einbrennt.13. The method according to claim 11 or 12, characterized in that baking is carried out at a temperature of 700 to 800.degree. C., in particular 750 to 780.degree. 14. Verfahren nach einem der Ansprüche 11 bis 13, d a d u r c h g e k e n n z e i c h n e t daß man auf die oberste Schicht eine Schutzschicht aufbringt. 14. The method according to any one of claims 11 to 13, d a d u r c h g It is not noted that a protective layer is applied to the top layer. 15. Abwandlung des Verfahrens nach Anspruch 11 zur Herstellung eines Schildes nach Anspruch 10, d a d u r c h g e k e n n z e i c h n e t , daß anstelle von einbrennbaren keramischen Siebdruckfarben einbrennbare keramische Abziehbilder verwendet werden. 15. Modification of the method according to claim 11 for the production of a Sign according to claim 10, d u r c h g e n n n z e i c h n e t that instead Burn-in ceramic decals from burn-in ceramic screen printing inks be used.
DE19833325664 1983-07-15 1983-07-15 Enamel badge with reflecting surfaces Ceased DE3325664A1 (en)