DE3111536A1 - Process for producing lightweight concrete - Google Patents
Process for producing lightweight concreteInfo
- Publication number
- DE3111536A1 DE3111536A1 DE19813111536 DE3111536A DE3111536A1 DE 3111536 A1 DE3111536 A1 DE 3111536A1 DE 19813111536 DE19813111536 DE 19813111536 DE 3111536 A DE3111536 A DE 3111536A DE 3111536 A1 DE3111536 A1 DE 3111536A1
- Authority
- DE
- Germany
- Prior art keywords
- concrete
- foam
- mixed
- plastic
- foam plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
Beschreibung description
Die Erfindung bezieht sich auf ein Verfahren der in Oberbegriff von Anspruch 1 erläuterten Art.The invention relates to a method in the preamble of Claim 1 explained Art.
Bei einem bekannten Verfahren dieser Art wird in den feuchten Beton ein Kunststoffschaumbildner in flüssiger Form eingespritzt.In a known method of this type is in the wet concrete a plastic foaming agent is injected in liquid form.
Ein derartiges Verfahren führt jedoch, zumindest beim Mischen von kleineren Mengen von Beton bzw. in kleineren Betonwerken, wo diese Schaumbildner mit Spritzpistolen in den Mischer eingespritzt werden, nicht zu befriedigenden Ergebnissen. Es lassen sich Feinrisse in den Fertigteilen und eine bröckelige Betonstruktur nicht vermeiden. Bei armierten Betonteilen müssen weiterhin zusätzliche Vorkehrungen für den Rostschutz der Stahlbewehrung getroffen werden.However, such a method leads, at least when mixing smaller amounts of concrete or in smaller concrete plants, where these foaming agents are injected into the mixer with spray guns, unsatisfactory results. There are no fine cracks in the prefabricated parts and a crumbly concrete structure avoid. In the case of reinforced concrete parts, additional precautions for the rust protection of the steel reinforcement can be taken.
Es ist ferner bekannt, dem Beton Füllstoffe, in der Regel einporige mineralische Stoffe, wie z.B. Blähton und -schiefer, Bims oder Schlacke, beizumischen. Alle diese Stoffe sind spezifisch leichter als der Beton; ein zufriedenstellender Vermischungsgrad wird demnach nur bei relativ trockener Vrarbeitung, d.h. bei zähen Betonen, (K1) erreicht. In feuchteren Betonen (ab K2) schwimmen die leichteren Füllstoffe auf und lassen sich nicht dauerhaft einmischen.It is also known that concrete fillers, usually single-pore Add mineral substances such as expanded clay and slate, pumice or slag. All of these substances are specifically lighter than concrete; a satisfactory one Accordingly, the degree of mixing is only achieved with relatively dry processing, i.e. with tough processing Emphasize, (K1) achieved. The lighter fillers float in more humid concretes (from K2) and do not allow themselves to be interfered permanently.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren aufzuzeigen, mit dem auf einfache tfeise auch bei relativ feuchter Verarbeitung ein leichter Beton mit homogener Leichtstoffverteilung hergestellt werden kann, der gute Baueigenschaften aufweist.The invention is based on the object of showing a method with the easy dry process even with relatively moist processing Concrete can be produced with a homogeneous distribution of lightweight materials, which has good building properties having.
Die Aufgabe wird durch die im Anspruch 1 angegebene Erfindung gelöst.The object is achieved by the invention specified in claim 1.
Da sich die offenporigen Schaumkunststoffpartikel beim Einbringen in den feuchten Beton vollsaugen, findet eine Entmischung durch das unterschiedliche spezifische Gewicht nicht statt; die Schaunkunststoffpartikel lassen sich homogen verteilen. Trotzdem wird eine überraschend hohe Gewichtsverringerung erzielt. Mit diesen Verfahren lassen sich auch kleinste Mengen Betons mischen, ohne daß. nach dem Abbinden Risse auftreten. Der nach dem Verfahren hergestellte leichte Beton ist feuerfest und sägbar. Er weist sowohl eine ausreichende Druckfestigkeit, so daß er als statischer Beton eingesetzt werden kann, als auch eine hohe Formbeständigkeit, gute Wärmedämmung und einen hohen Tausalzwiderstand auf.Since the open-pored plastic foam particles are removed when they are introduced Soak in the damp concrete, there is a segregation through the different specific gravity does not take place; the foam plastic particles can be homogeneous to distribute. Nevertheless, a surprisingly high weight reduction is achieved. With This process can be used to mix even the smallest quantities of concrete without. after cracks appear after setting. The light concrete produced by the process is fireproof and sawable. He has both sufficient compressive strength, so that it can be used as static concrete, as well as high dimensional stability, good thermal insulation and high resistance to de-icing salt.
Die in Unteranspruch 2 aufgeführten Schaumkunststoffe haben sich als besonders vorteilhaft erwiesen. Außerdem fallen derartige Schaumstoffflocken in jedem kunstschaumstoffverarbeitenden Betrieb, beispielsweise bei der Polsterherstellung, als Abfall an und sind somit relativ billig verfügbar.The foamed plastics listed in dependent claim 2 have proven to be proved particularly advantageous. In addition, such foam flakes fall into every plastic foam processing company, for example in the manufacture of upholstery, as waste and are therefore available relatively cheaply.
Besonders vorteilhafte Ergebnisse werden erzielt, wenn das Raumgewicht des verwendeten Schaumkunststoffs in den aus den Unteransprüchen 3 und 4 ersichtlichen Bereichen liegt.Particularly advantageous results are achieved when the density of the foam plastic used in the from the dependent claims 3 and 4 apparent Areas.
Bevorzugt werden Schaumkunststoff und Beton in den in Unteranspruch 5 angegebenen Verhältnissen gemischt.Foamed plastic and concrete are preferred in the dependent claim 5 given proportions mixed.
Besonders günstige Ergebnisse werden erzielt, wenn gemäß Unteranspruch 6 das erfindungsgemäße Verfahren mit der Zugabe von Mitteln zum Erhöhen des Gasgehalts kombiniert wird. Insbesondere kann das eingangs erwähnte, bekannte Verfahren, bei dem flüssige Kunststoff-Schaumbildner in den Beton eingespritzt werden, dadurch erheblich verbessert werden, daß die Schaumkunststoffpartikel nicht anstelle des flüssigen Schaumbildners, sondern zusätzlich zu diesem in den Beton eingeführt werden. Möglicherweise werden die Gasblaschen des Schauns von den Kunststoffpartikeln "eingefawgwen" und in der offenporigen Struktur eingeschlossen, wodurch der Zusammenhalt der eigentlichen Betonbestandteile nicht gestört wird. Jedenfalls wird durch den Zusatz der Schaunkunststoffpartikel der Nachteil dieses bekannten Verfahens, die Rissebildung und geringe Festigkeit sowie Bröcheligkeit, des erzeugten Betons, der einen wirtschaftlichen Einsatz in größerem Umfang bisher verhindert hat, überraschenderweise beseitigt.Particularly favorable results are achieved if according to the dependent claim 6 shows the method according to the invention with the addition of agents for increasing the gas content is combined. In particular, the known method mentioned at the outset can be used in the liquid plastic foaming agent can be injected into the concrete, thereby can be significantly improved that the foam plastic particles do not replace the liquid foaming agent, but in addition to this are introduced into the concrete. Possibly the gas bubbles of the show from the plastic particles "enclosed" and enclosed in the open-pored structure, creating cohesion the actual concrete components are not disturbed. In any case, the Addition of foam plastic particles the disadvantage of this known method, the Cracking and poor strength and fragility of the concrete produced, the has hitherto prevented economic use on a larger scale, surprisingly eliminated.
Der nach dem erfindungsgemäßen Verfahren gemischte leichte Beton kann sowohl als Ortbeton als auch zum Herstellen von Fertigteilen eingesetzt werden.The light concrete mixed by the method according to the invention can can be used both as in-situ concrete and for the production of prefabricated parts.
Nach dem erfindungsgemäßen Verfahren hergestellte Betonteile, insbesondere Bauplatten, sind aus in vergrößerten Ausschnitten aus der Zeichnung ersichtlich. Es zeigen: Fig. 1 eine nach den erfindungsgemäßen Verfahren hergestellte Platte ohne zusätzliche Erhöhung des Gasgehaltes, und Fig. 2 eine nach dem erfindungsgemäßen Verfahren hergestellte Platte mit zusätzlicher Erhöhung des Gasgehalts.Concrete parts produced by the method according to the invention, in particular Building panels can be seen in enlarged excerpts from the drawing. The figures show: FIG. 1 a plate produced by the method according to the invention without an additional increase in the gas content, and FIG. 2 shows one according to the invention Method manufactured plate with additional increase in gas content.
In Fig. 1 besteht die Platte aus einer Betonmatrix 1 mit eingeschlosenen, mit Beton vollgesogenen Schaumkunststoff-Flocken 2, die zur Veranschaulichung hier deutlich gezeichnet sind, obwohl sie im fertigen Beton kaum mehr in Erscheinung treten. Die Schaumkunststoff-Flocken bestehen insbesondere aus Polyurethan.In Fig. 1, the plate consists of a concrete matrix 1 with enclosed, Foam plastic flakes soaked with concrete 2, which are illustrated here are clearly drawn, although they are hardly visible in the finished concrete step. The foam plastic flakes consist in particular of polyurethane.
Aber auch mit Polyäthylen bzw. Polyester wurden gute Ergebnisse erzielt. Die Schaumkunststoff-Flocken sind offenporig bzw. offenzellig geschäumt. Die Poren, die sich zum Teil mit Zementschlempe vollsaugen, sind mit 3 bezeichnet.But good results have also been achieved with polyethylene or polyester. The plastic foam flakes are open-pored or open-celled. The pores, some of which are soaked with cement pulp are denoted by 3.
Das Raumgewicht des verwendeten Schaunkunststoffes soll ca.The density of the foam plastic used should be approx.
13 bis 60 kg/ 3 bevorzugt 28 bis 30 kg/m3, betragen. Er wird durch den Mischungsvorgang wie ein Schwamm komprimiert und saugt sich mit Zementschlempe voll.13 to 60 kg / 3, preferably 28 to 30 kg / m3. He will by the mixing process compresses like a sponge and soaks up with cement slurry fully.
Das Verhältnis von Schaumkunststoff zu Beton läßt sich innerhalb weiterer Grenzen variieren. Pro n3 fertigen Betons werden zwischen ca. 30 und 800 1 Schaumkunststoff-Flocken eingemischt.The ratio of foam plastic to concrete can be further Limits vary. For every n3 of finished concrete, between approx. 30 and 800 1 foam plastic flakes are required mixed in.
Je nach Mischungsverhältnis erhält man, bei einem größeren Schaumkunststoffanteil, einen Beton mit einer höheren Wärmedämmung bzw., bei einem größeren Betonanteil, einen konstruktiven Beton, der in der Lage ist, höhere Druckkräfte aufzunehmen.Depending on the mixing ratio, with a larger proportion of foam plastic you get a concrete with a higher thermal insulation or, with a larger proportion of concrete, a constructive concrete that is able to withstand higher compressive forces.
Die Platte nach Fig. 2 enthält zusätzlich ein Mittel zum Erhöhen des Gasgehalts. Dadurch bilden sich Gasporen , 7 die größtenteils in der Porenstruktur der Schaumkunststoff-Flocken enthalten sind, sich jedoch auch in der Betonmatrix finden.The plate of Fig. 2 additionally contains a means for increasing the Gas content. This creates gas pores, 7 mostly in the pore structure The foam plastic flakes are contained, but also in the concrete matrix Find.
Das Verfahren wird durchgeführt, indem die Schaunkunststoffpartikel im gewünschten Gewichtsverhältnis einfach in den Beton eingemischt werden. Maximal- bzw. Mindestmengen an Beton, bei deren Über- bzw. Unterschreiten durch das Einmischen der Schaumkunststoffpartikel Nachteile im Endprodukt auftraten, konnten nicht festgestellt werden. Besonders feuchtere Betone (ab K2) ließen sich gut durchmischen; eine Entmischung trat auch während des Abbindens nicht auf.The procedure is carried out by removing the foam plastic particles simply mixed into the concrete in the desired weight ratio. Maximum- or minimum quantities of concrete, if they are exceeded or not reached by mixing of the foam plastic particles, there were no disadvantages in the end product will. Particularly moist concretes (from K2) could be mixed well; a segregation also did not occur during setting.
Werden Mittel zur Erhöhung des Gasgehalts eingesetzt, so werden diese ebenso während des Mischvorgangs eingebracht. Besonders zweckmäßig ist das Einspritzen eines flüssigen Schaumbildners auf Kunststoffbasis.If means are used to increase the gas content, these are also introduced during the mixing process. Injection is particularly useful of a liquid plastic-based foaming agent.
Da sich der mit dem erfindungsgemäßen Verfahren hergestellte Beton ohne weitere Vorkehrungen wie die bekannten Leichtbetone verarbeiten läßt, soll sich der Schutz auch auf daraus hergestellte Fertigteile, wie z.B. Bauplatten, erstrecken.Since the concrete produced with the method according to the invention can be processed without further precautions as the well-known lightweight concrete should The protection also extends to prefabricated parts made from them, such as building boards.
Claims (6)