DE3039728A1 - SUCTIONABLE DEVICE - Google Patents
SUCTIONABLE DEVICEInfo
- Publication number
- DE3039728A1 DE3039728A1 DE19803039728 DE3039728A DE3039728A1 DE 3039728 A1 DE3039728 A1 DE 3039728A1 DE 19803039728 DE19803039728 DE 19803039728 DE 3039728 A DE3039728 A DE 3039728A DE 3039728 A1 DE3039728 A1 DE 3039728A1
- Authority
- DE
- Germany
- Prior art keywords
- absorbent
- fibers
- embossing
- fusible
- secretion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Description
Beschreibungdescription
Die Erfindung betrifft eine saugfähige bzw. Sekret absorbierende Einrichtung, sie betrifft insbesondere eine Einrichtung, in der eine integrale Einheit gebildet wird durch Gaufrieren bzw. Prägen unter hohen Temperatur- und Druckbedingungen, sowie deren Verwendung in Damenbinden, Windeln, Wundverbänden, Inkontinenz-Polstern und Pantilinern (Schlüpfereinlagen).The invention relates to an absorbent or secretion absorbing device, it relates in particular to a device in which a An integral unit is formed by embossing or embossing under high temperature and pressure conditions, as well as their use in Sanitary towels, diapers, wound dressings, incontinence pads and pantiliners (Panty insoles).
Seit kurzem gibt es Produkte auf dem Markt,'die dazu bestimmt sind, Vaginalausflüsse zwischen den Menstruationsperioden und auch geringe Mengen Menstruationsflüssigkeit aufzusaugen bzw. zu absorbieren. Ein Beispiel für ein solches Produkt sind KOTEX LIGHTDAYS-Pantiliners (KOTEX LIGHTDAYS ist ein Warenzeichen der Firma Kimberly-Clark Corporation, Neenah, Wisconsin 54956/USA). Dieses Polster (Kissen) weist eine saugfähige bzw. absorbierende Komponente aus einem üblicherweise verwendeten Cellulosematerial, wie Holzpulpe, und eine flüssigkeitsundurchlässige Unterlagenschicht auf. Diese Unterlagenschicht enthält Klebestreifen auf ihrer Unterseite für die Befestigung an Damenunterkleidern. Der saugfähige bzw. absorbierende Anteil weist ein darauf angeordnetes, für Feuchtigkeit durchlässiges Hüllenmaterial (Überzugsmaterial) auf, das mit dem Dammbereich in Kontakt kommt. Die für Feuchtigkeit durchlässige Schicht ist an der Flaumkomponente befestigt mittels einer Klebstoffschicht, die dem Flaum zugesetzt wird. Dieses Polster (Kissen) wird dann gaufriert bzw. geprägt, um dem Flaum eine Integrität zu verleihen und um auch Kanäle für den Durchfluß der Flüssigkeit während der Sekretion zu schaffen. Die Unterlage wird dann angeklebt.Recently there have been products on the market which are intended to To suck up or absorb vaginal discharge between menstrual periods and also small amounts of menstrual fluid. A An example of such a product are KOTEX LIGHTDAYS pantiliners (KOTEX LIGHTDAYS is a trademark of the Kimberly-Clark Corporation, Neenah, Wisconsin 54956 / USA). This cushion (pillow) has an absorbent or absorbent component made of a commonly used cellulose material, such as wood pulp, and a liquid-impermeable component Backing layer on. This backing layer contains adhesive strips on its underside for attachment to Women's underwear. The absorbent or absorbent part has a moisture-permeable casing material (covering material) arranged thereon, which comes into contact with the perineal area. the the moisture permeable layer is attached to the fluff component by means of an adhesive layer added to the fluff. This pad (cushion) is then embossed to give integrity to the fluff and also around channels for flow of creating fluid during secretion. The base is then glued on.
13001 8/088813001 8/0888
Obgleich sich dieses Polster (Kissen) wegen seiner relativ geringen Dicke und seiner kleinen Gesamtkonfiguration als außerordentlich populär erwiesen hat, werden durch die Anwesenheit des Klebstoffes die Elastizität und Weichheit in nachteiliger Weise beeinflußt, so daß der mit dem Tragen eines solchen Polsters (Kissens) verbun» dene Komfort begrenzt ist. Außerdem könnte die Herstellung wesentlich vereinfacht werden, wenn eine für Feuchtigkeit durchlässige Uberzugsschicht vermieden werden könnte.Although this cushion (pillow) is because of its relatively small Thickness and its small overall configuration have proven extremely popular due to the presence of the adhesive affects the elasticity and softness in a disadvantageous way, so that the wearing of such a pad (pillow) is connected to the » whose comfort is limited. In addition, the production could be significantly simplified if a moisture-permeable coating layer could be avoided.
Die üblichen, verhältnismäßig billigen Flaummaterialien (Flockenmaterialien), die traditionell für diese Polster (Kissen), andere Polster (Kissen), Windeln und dgl. verwendet werden, verlieren dann, wenn sie feucht werden, ihre Integrität und sind wegen des Wunsches, ihre Saugfähigkeit maximal zu gestalten, im allgemeinen so konstruiert, daß sie über den nicht-gaufrierten bzw. nicht-geprägten Bereichen ein maximales Volumen aufweisen. Diese nicht-gaufrierten Bereiche beeinflussen zwar positiv die Saugfähigkeit bzw. das Absorptionsvermögen, sie beeinflussen aber die Integrität der saugfähigen Watte in nachteiliger Weise, d.h. sie erleichtern die Abtrennung der einzelnen Fasern von der Masse des Wattebausches. Dieses Phänomen, allgemein als Abschürfung bzw. Ablösung (sloughing) bezeichnet, ist immer unerwünscht und insbesondere dort nachteilig, wo sich die abgeschürften Fasern selbst in dem Dammbereich oder, falls dieses saugfähige Material als Komponente eines chirurgischen Wundverbandes verwendet wird, in einer Wunde ablagern.The usual, relatively cheap fluff materials (flake materials), which are traditionally used for these cushions (pillows), other cushions (pillows), diapers, and the like, lose when they become moist, their integrity and, because of the desire to maximize their absorbency, are generally designed so that they have a maximum over the non-embossed or non-embossed areas Have volume. Although these non-embossed areas have a positive effect on the absorbency or absorption capacity, they do influence but the integrity of the absorbent wadding is detrimental, i.e. it facilitates the separation of the individual fibers from the mass of the cotton ball. This phenomenon, commonly referred to as sloughing, is always undesirable and in particular disadvantageous where the abraded fibers are themselves in the perineal area or, if this absorbent material is a component of a A surgical dressing used is deposited in a wound.
Im Idealfalle wäre es auf dem Gebiet der saugfähigen bzw. absorptionsfähigen Systeme ein großer Fortschritt, wenn eine saugfähige bzw. absorptionsfähige Verbundmatrix entwickelt werden könnte, bei der das Abschürfen bzw. Ablösen eliminiert und die Integrität aufrechterhalten werden könnte bei gleichzeitiger Aufrechterhaltung der Vorteile derIdeally, it would be a great step forward in the field of absorbent or absorbent systems if an absorbent or absorbent system was used. absorbent composite matrix could be developed that eliminates abrasion or peel and maintains integrity Could be while maintaining the benefits of the
130018/0888130018/0888
OR1GlNALOR 1 GlNAL
traditionellen saugfähigen bzw. absorptionsfähigen Materialien und der niedrigen Kosten und der leichten Zugänglichkeit, die diese Materialien über Jahre hinweg zu einem Standardmaterial (einer Stütze) gemacht haben. Mit der vorliegenden Erfindung wird ein solches saugfähiges bzw. absorptionsfähiges Medium geschaffen.traditional absorbent materials and the low cost and easy accessibility that has made these materials a standard material (a support) over the years have made. The present invention provides such an absorbent medium.
Die vorliegende Erfindung betrifft ein saugfähiges bzw. Sekret absorbierendes Material mit einer ausgezeichneten Integrität, das eine gute Benetzbarkeit und Flexibilität besitzt und verhältnismäßig billig ist. Ein solches Material ist insbesondere verwendbar als Pantiliner (Schlüpfereinlage), kann aber auch in den verschiedensten anderen Produkten verwendet werden, die saugfähig bzw. absorptionsfähig sein müssen.The present invention relates to an absorbent or secretion absorbent material having an excellent integrity that has a good Possesses wettability and flexibility and is relatively inexpensive. Such a material is particularly useful as a pantiliner (Slip insert), but can also be used in a wide variety of other products that are absorbent or absorbent have to.
Unter dem hier verwendeten Ausdruck "saugfähiges bzw. Sekret absorbierendes Material" ist ein saugfähiges bzw. absorptionsfähiges Material zu verstehen, das verschiedene biologische Flüssigkeiten mit ähnlichem Wirkungsgrad absorbiert (aufsaugt). Dieser Ausdruck umfaßt in dem hier gebrauchten Sinne Materialien, die sowohl Urinsekrete als auch Menstruationsausflüsse sowie Ausflüsse aus chirurgischen Wunden aufsaugen bzw. absorbieren.As used herein, "absorbent material" means an absorbent material to understand that different biological fluids with similar efficiency absorbs (soaks up). That term includes in that here used sensory materials that absorb both urinary secretions and menstrual discharge as well as discharge from surgical wounds or absorb.
Gegenstand der Erfindung ist eine saugfähige bzw. Sekret absorbierende Einrichtung mit einer innigen Mischung aus nicht-schmelzbaren saugfähigen bzw. absorbierenden Fasern und verhältnismäßig leicht schmelzbaren Fasern. Die Fasern werden in einer integralen Einheit zusammengehalten durch Verschmelzen der in der Wärme schmelzbaren Fasern durch Gaufrieren bzw. Prägen. Das Gaufrieren bzw. Prägen wird unter verhältnismäßig niedrigen Temperatur- und Druckbedingungen durchgeführt. Die Einrichtung kann als saugfähiges bzw. absorbierendes Material für dieThe invention relates to an absorbent or secretion absorbent Device with an intimate mixture of non-meltable absorbent fibers and relatively easily meltable fibers. The fibers are held together in an integral unit by fusing the heat-fusible fibers Embossing or embossing. Embossing is carried out under relatively low temperature and pressure conditions. the Device can be used as an absorbent or absorbent material for the
130018/088 8130018/088 8
verschiedensten Anwendungszwecke eingesetzt werden.various application purposes can be used.
Das erfindungsgemäße saugfähige bzw. Sekret absorbierende Material wird auf konventionellen Textilherstellungsvorrichtungen hergestellt und die Herstellung erfolgt durch Vermischen von Fasern gleichartiger oder nicht gleichartiger Lange einer ersten Gruppe von Fasern, wie z.B. aus Reyon, Holzpulpe oder einem anderen traditionellen saugfähigen bzw. absorbierenden Material auf Cellulosebasis, und einer zweiten Gruppe von Fasern, die in einem milden Verfahren schmelzbar sind. Die dabei erhaltene gemischte Faserwatte wird anschließend unter Anwendung von Wärme und Druck gaufriert bzw. geprägt. Durch das Gaufrieren (Prägen) wird der Watte Integrität verliehen durch Komprimieren des saugfähigen bzw. absorbierenden Flaummaterials in bestimmten Bereichen, außerdem verschmelzen aber auch die schmelzbaren Fasern miteinander unter Bildung einer wesentlich stärkeren Integrität als sie bisher vorlag. Durch die Einwirkung von Wärme und Druck während des Gaufrierens bzw. Prägens wird die Möglichkeit, daß sich ein wesentlicher Anteil der Fasern abschürft bzw. ablöst fast vollständig eliminiert«The absorbent or secretion-absorbing material according to the invention is made on conventional textile manufacturing equipment and is made by blending fibers of the same type or a non-uniform length of a first group of fibers, such as rayon, wood pulp or some other traditional absorbent or cellulosic absorbent material, and a second Group of fibers that can be melted in a mild process. the The resulting mixed fiber wadding is then embossed or embossed using heat and pressure. By embossing (Embossing) the wadding is given integrity by compressing the absorbent or absorbent fluff material in certain areas, in addition, however, the fusible fibers also fuse with one another, forming a much stronger integrity than they have before Template. The action of heat and pressure during embossing or embossing increases the possibility that a significant proportion the fibers abraded or peeled off almost completely eliminated «
Obgleich in anderen Patentschriften Kombinationen von Fasertypen for verschiedene Verwendungszwecke beschrieben sind, beispielsweise in der US-Patentschrift 3 976 074, in der hydrophile-hydrophobe Faserkombinationen beschrieben sind, wobei letztere dazu verwendet werden, Differenzen zwischen den Fasern aufrechtzuerhalten, und in der britischen Patentschrift 1 071 191 sowie in der US-Patentschrift 4 054 141 r ist aus keiner dieser Patentschriften das der vorliegenden Erfindung zugrundeliegende Konzept zu entnehmen.Although other patents describe combinations of fiber types for different uses, for example U.S. Patent 3,976,074, which describes hydrophilic-hydrophobic fiber combinations, the latter being used to maintain differences between fibers, and British Patent 1 071 191 as well as in US Pat. No. 4,054,141 r , the concept on which the present invention is based cannot be inferred from any of these patents.
Es ist natürlich offensichtlich, daß die Menge der abgeschürften bzw. abgelösten Fasern sowie der Grad der Integrität eine direkte FunktionIt is of course obvious that the amount of abraded resp. detached fibers as well as the degree of integrity have a direct function
13 0 0 18/088813 0 0 18/0888
>■-■-' ■ .■■-■■-..-: ORIGINAL INSPECTED> ■ - ■ - '■. ■■ - ■■ -..-: ORIGINAL INSPECTED
des Mengenverhältnisses zwischen den schmelzbaren Fasern und den nicht-schmelzbaren Fasern und ihrer Länge sind, wobei längere Fasern eine geringere Abschürfung bzw. Ablösung ergeben. Es ist allgemein bevorzugt, daß die Menge der schmelzbaren Fasern zwischen etwa 20 und etwa 35 Gew.-% liegt, obgleich auch Mengen oberhalb und unterhalb dieses bevorzugten Bereiches verwendbar sind. Schmelzbare Fasern in einer Menge von bis zu 50 Gew.-% der Mischung wurden untersucht und haben sich als geeignet erwiesen, wobei jedoch darauf hingewiesen wird, daß eine Abnahme der Saugfähigkeit bzw. des Absorptionsvermögens auftritt, die mit einer Zunahme des Prozentsatzes· an schmelzbaren Fasern in dem erfindungsgemäßen saugfähigen bzw. Sekret absorbierenden Material verbunden ist.the proportion of the fusible fibers to the non-fusible fibers and their length, with longer fibers giving less abrasion or peeling. It is generally preferred that the amount of fusible fibers be between about 20 and about 35 weight percent, although amounts above and below this preferred range are also useful. Fusible fibers in an amount of up to 50 wt -.% Of the mixture were tested and have proved to be suitable, but it is noted that a decrease in absorbency and in absorbance occurs, the fusible with an increase in the percentage · on Fibers in the absorbent or secretion absorbent material according to the invention is connected.
Je nach der saugfähigen bzw. absorbierenden Faserkomponente, der schmelzbaren Faserkomponente, der Faserlänge und anderen Faktoren, wie sie auf dem Gebiet des Saugvermögens bzw. der Absorptionsfähigkeit bekannt sind, kann eine erfindungsgemäße saugfähige bzw. Sekret absorbierende Einrichtung durch geeignete Auswahl und geeignete Anwendung dieser gleichen Parameter an die Gewohnheiten bzw. Wünsche der Verbraucher angepaßt werden.Depending on the absorbent or absorbent fiber component, the fusible fiber component, the fiber length and other factors such as those in the field of absorbency or absorbency are known, an inventive absorbent or secretion absorbing device by suitable selection and appropriate application of these same parameters to the habits or desires of the Consumers are adapted.
Bisher wurden die erfindungsgemäß verwendeten Fasern als in einem milden Verfahren schmelzbare Fasern (mild-process-fusible fibers) beschrieben. Für die Zwecke der vorliegenden Erfindung werden diese Fasern als solche definiert, die bei Temperaturen zwischen etwa 107 und etwa 191 C (225 bis 375 F) bei einem linearen Gaufrier- bzw. Prägedruck von bis zu 53,62 kg/cm (300 pli) schmelzen. Der minimale lineare Gaufrier- bzw. Prägedruck hängt von den jeweils gewählten schmelzbaren Fasern ab, wobei die niedriger schmelzenden Fasern einen geringeren Druck erfordern. Bei der praktischen Durchführung derSo far, the fibers used according to the invention were considered in one mild-process-fusible fibers. For the purposes of the present invention, these Fibers are defined as those which are stored at temperatures between about 107 and about 191 C (225 to 375 F) in a linear Gaufrier or Melt embossing pressures of up to 53.62 kg / cm (300 pli). The minimum linear embossing or embossing pressure depends on the fusible fibers selected in each case, the lower-melting fibers being one require less pressure. In the practical implementation of the
130018/0888 *130018/0888 *
ÖRIQINAL INSPECTEDORIQINAL INSPECTED
Erfindung wurden Drucke von nur 8,94 kg/cm (50 pli) angewendet und es sind auch noch niedrigere Drucke anwendbar, es ist dann jedoch erforderlich, daß ein gewisser positiver Gaufrier- bzw. Prägedruck angewendet wird, um die für die Bildung des saugfähigen Polsters bzw. Kissens erforderliche Bindung zu erzielen.In the invention, pressures as low as 8.94 kg / cm (50 pli) were applied and lower pressures can also be used, but it is then necessary that a certain positive embossing pressure be applied is used to achieve the bond required for the formation of the absorbent pad or pillow.
Es ist klar, daß ein wesentlicher Beitrag sowohl zum Saugvermögen bzw. zur Absorptionsfähigkeit als auch zur Abschürfung bzw. Ablösung bei der Verwendung des erfindungsgemäßen saugfähigen bzw. Sekret absorbierenden Polsters von dem Grad der Prägung kommt, der ein solches Polster unterworfen wird. Im allgemeinen ist ein beliebiges Prägebzw. Gaufriermuster, das sich über die gesarate Oberfläche des Polsters erstreckt, bevorzugt, obgleich für bestimmte spezielle Ausführungsformen lokal mehr gebündelte oder dichtere Präge- bzw. Gaufriermuster erwünscht sein können. Außerdem ist es für die Zwecke der Integrität erwünscht, daß die einzelnen Komponenten des Prägemusters oder die Komponenten der Prägelinien, wenn das Muster aus einer Reihe von geraden oder welligen Linien besteht, einen geringeren Abstand voneinander haben als die einzelnen Fasern lang sind. Wenn die Mehrzahl dieser Prägelinien auf diese Weise angeordnet sind, wird dadurch die aus dem Prägen bzw. Gaufrieren resultierende Integrität erhöht. Wenn andererseits eine Prägung von mehr als 25 % der Fläche des Polsters auftritt, wird dadurch das Saugvermögen bzw. die Absorptionsfähigkeit stark beeinträchtigt und es ist daher erwünscht, daß die Prägung unterhalb dieses 25 ^-Wertes liegt. It is clear that a significant contribution both to the absorbency or to the absorption capacity and to the abrasion or detachment when using the absorbent or secretion-absorbing pad according to the invention comes from the degree of embossing to which such a pad is subjected. In general, any kind of embossing or marking is possible. Embossing pattern that extends over the entire surface of the pad is preferred, although for certain special embodiments more locally more bundled or denser embossing or embossing patterns may be desired. In addition, for the sake of integrity, it is desirable that the individual components of the embossed pattern, or the components of the embossed lines, if the pattern consists of a series of straight or wavy lines, be spaced less than the length of the individual fibers. Having the plurality of these embossed lines arranged in this way increases the integrity resulting from embossing. If, on the other hand, an embossing of more than 25 % of the area of the pad occurs, the absorbency or the absorption capacity is severely impaired and it is therefore desirable that the embossing is below this 25 ^ value.
Was die Vereinigung von absorptionsfähigen und nicht-absorptionsfähigen Fasern ohne Klebstoff anbetrifft, so ist diese in der US-Patentschrift 4 100 324 ausführlich beschrieben. In dieser Patentschrift ist die Herstellung von kohärenten integrierten Faserstrukturen aus thermo-As for the union of absorbent and non-absorbent As for fibers without adhesive, this is described in the US patent 4 100 324 described in detail. In this patent specification is Production of coherent, integrated fiber structures from thermo-
130018/0888130018/0888
plastischen Mikrofasern und Holzpulpenfasern beschrieben, wobei die Fasern durch Vermischen eines primären Luftstromes, der schmelzgeblasene thermoplastische Mikrofasern enthält, und eines sekundären Luftstromes, der die Holzpulpenfasern enthält, miteinander vereinigt werden· Die Ströme werden für die Zwecke, die in dieser speziellen Patentschrift angegeben sind, unter turbulenten Bedingungen miteinander vereinigt. Es sei jedoch darauf hingewiesen, daß zum Schmelzblasen wesentlich höhere Temperaturbedingungen erforderlich sind und daß zum Vereinigen der beiden Luftströme in Verbindung mit dem Schmelzblasen wesentlich ausgeklügeltere Apparaturen erforderlich sind als sie beim willkürlichen Vermischen der schmelzbaren Fasern und der saugfähigen bzw. absorbierenden Fasern, die das erfindungsgemäße saugfähige bzw. Sekret absorbierende Material aufbauen, angewendet werden. In der Tat kann die erfindungsgemäße saugfähige bzw. Sekret absorbierende Einrichtung hergestellt werden unter Verwendung einer Vorrichtung, wie z.B. eines Rando-Webber oder anderer konventioneller TextiIherStellungsvorrichtungen.plastic microfibers and wood pulp fibers described, the Fibers are combined by mixing a primary air stream containing meltblown thermoplastic microfibers and a secondary air stream containing the wood pulp fibers. The streams are combined under turbulent conditions for the purposes set forth in this particular patent united. It should be noted, however, that much higher temperature conditions are required for meltblowing and that for Combining the two air streams in connection with the meltblowing much more sophisticated equipment is required than with arbitrary mixing of the fusible fibers and the absorbent fibers that make up the inventive absorbent fibers Build up secretion absorbent material, are applied. Indeed, the absorbent device of the present invention can be made using a device such as e.g. a Rando-Webber or other conventional fabric-making apparatus.
Es sei darauf hingewiesen, daß die erfindungsgemäße saugfähige bzw. Sekret absorbierende Einrichtung für viele Anwendungszwecke eingesetzt werden kann, daß sie jedoch insbesondere auf dem Gebiet der Fa ntiliner (Schlüpfereinlagen) verwendet wird.It should be noted that the inventive absorbent or Secretion absorbent device used for many purposes it can be that they are, however, particularly in the field of fan-assistants (Panty insoles) is used.
Ein erfindungsgemäßerPanti liner (Schlüpf ereihlage) kann ohne ein getrenntes, für Flüssigkeit durchlässiges Uberzugsmaterial hergestellt werden und der Pantiliner selbst besteht deshalb nur aus einer für Flüssigkeit undurchlässigen Schutzabdeckung und die Klebstoffbindung, die bisher zwischen der Hülle und dem saugfähigen bzw. absorptionsfähigen Material des Pantiliners erforderlich war, wird dadurch völlig eliminiert. Die Steifheit und die Störung des Saugvermögens (der Absorptionsfähigkeit),A pantiliner according to the invention (slip layer) can be produced without a separate, liquid-permeable coating material and the Pantiliner itself therefore only consists of a protective cover that is impermeable to liquids and the adhesive bond that was previously used between the shell and the absorbent or absorbent material of the pantiliner was required is completely eliminated. the Stiffness and the disturbance of the pumping speed (the absorption capacity),
130018/0888130018/0888
die mit dem Klebstoff verbunden waren, werden dadurch ebenfalls eliminiert und als Folge davon wird die Herstellung vereinfacht. Da die für Flüssigkeit undurchlässige Schutzabdeckung ein thermoplastisches Material sein kann, kann die saugfähige bzw. Sekret absorbierende Einrichtung direkt an die Schutzabdeckung angeschmolzen werden, wodurch der gesamte Strukturklebstoff, der für einen Pantiliner bei einer speziellen bevorzugten Ausführungsform verwendet wird, eliminiert wird.that were connected to the adhesive are thereby also eliminated and, as a result, manufacture is simplified. Since the for liquid impermeable protective cover a thermoplastic Can be material, the absorbent or secretion-absorbing device can be fused directly to the protective cover, whereby the entire structural adhesive that is required for a pantiliner of a specific preferred embodiment is used, is eliminated.
Nachfolgend werden einige Beispiele für erf^ndungsgeroäße saugfähige bzw. Sekret absorbierende Einrichtungen angegeben. In allen Fällen wurden die verschiedenen Fasermischungen in Bezug auf die einzelnen Komponenten ausgewogen und auf einer RANDO-Opener Blender-Einheit gemischt unter Bildung einer einheitlichen Faserwatte. Die Watte wurde auf dem RANDO-WEB Processor hergestellt, bei dem es sich um ein konventionelles Teil einer Vorrichtung handelt, die für die Watteherstellung in der Faserherstellungsindustrie verwendet wird. Die fertig gemischte Rolle aus dem RANDO-WEB Processor wird in die erhitzten Gaufrier- bzw. Prägewalzen eingeführt, in denen die Fasern zu der Faserwatte miteinander verschmolzen werden, welche die Basis der vorliegenden Erfindung bildet (alle vorstehend und nachstehend beschriebenen Verarbeitungsvorrichtungen werden hergestellt von der Firma Rondo Machine Corporation, Macedon, New York/USA.Below are some examples of invention devices absorbent or secretion-absorbing devices. In all cases the different fiber blends were related to each Components balanced and mixed on a RANDO-Opener Blender unit to form a uniform fiber wadding. The cotton wool was Manufactured on the RANDO-WEB Processor, which is a conventional part of an apparatus used for wad making in the fiber manufacturing industry. The done The mixed roll from the RANDO-WEB Processor is fed into the heated embossing or embossing rollers, in which the fibers are added to the Fused together fiber wadding, which forms the basis of the present invention (all processing devices described above and below are manufactured by the company Rondo Machine Corporation, Macedon, New York / USA.
Die Erfindung wird durch die folgenden Beispiele näher erläutert, ohne jedoch darauf beschränkt zu sein.The invention is illustrated in more detail by the following examples, but without being limited to it.
130018/OS88130018 / OS88
aus 70 % Reyon-Stapelfasern und 30 % Vinyon-Stapelfasern bestand. Die Vinyon-Stapelfasern werden hergestellt von der Firma Avtex Fibers, Inc. und dabei handelt es sich um thermoplastische Vinylharzfasern, hergestellt aus einem Vinylchlorid/Vinylacetat-Copolymeren. Nach der Verarbeitung in dem RANDO-WEBBER betrug die Dichte der Basisbahn 0,040 g/cm . Die hergestellte Bahn wurde dann bei einer Temperatur von 138°C (280°F) und einem Druck von 16,09 kg/cm (90 pli) wärmegeprägt. Das Prägen in diesem und in allen folgenden Beispielen wurde unter Verwendung einer konventionellen Prägewalze durchgeführt, die in Verbindung mit einer Stahl-Amboßwalze verwendet, wurde. Nach dem Prägen betrug die Gesamtdichte der geprägten Bahn 0,096 g/cm , während die Dichte der Bahn in dem geprägten Bereich 0,637 g/cm betrug. Die Länge der Fasern des Ausgangsmaterials betrug bei Reyon-Stapelfasern 3,97 cm (1-9/16 inch) und bei Vinyon-Stapelfasern 5,08 cm (2 inch).consisted of 70 % rayon staple fibers and 30 % vinyon staple fibers. The vinyon staple fibers are manufactured by Avtex Fibers, Inc. and are thermoplastic vinyl resin fibers made from a vinyl chloride / vinyl acetate copolymer. After processing in the RANDO-WEBBER, the density of the base web was 0.040 g / cm. The fabricated web was then heat embossed at a temperature of 138 ° C (280 ° F) and a pressure of 16.09 kg / cm (90 pli). Embossing in this and all of the following examples was carried out using a conventional embossing roll used in conjunction with a steel anvil roll. After embossing, the overall density of the embossed web was 0.096 g / cm while the density of the web in the embossed area was 0.637 g / cm. The stock fiber length was 3.97 cm (1-9 / 16 inches) for rayon staple fibers and 5.08 cm (2 inches) for vinyon staple fibers.
Das in Beispiel 2 hergestellte Polster (Kissen) wurde unter Verwendung eines Handle-0-Meter mit dem Material verglichen, wie es derzeit in einem KOTEX LIGHTDAYS-Pad verwendet wird. Die Größe der abgemessenen Proben betrug 5,08 cm χ 7,62 cm (2 inch χ 3 inch) und die an dem Handle-0-Meter eingestellte Spaltbreite betrug 2,54 cm (l inch). Nach dem Durchlaufenlassen von fünf Proben erhielt man Durchschnittswerte von 95,7 g für das Material, wie es in dem Lightdays-Pad zu finden ist, und von 29,9 g für das erfindungsgemäß hergestellte Material. Bei dem Handle-0-Meter handelt es sich bekanntlich um eine anerkannte Testvorrichtung zur Durchführung eines Standardtests, der ein Maß für die Flexibilität ergibt, bei der es sich um einen anerkannten Komfortfaktor handelt, hergestellt von der Firma Thwing Albert Instrument Company, Philadelphia, Pennsylvania/USA. Der Test ist im InstructionThe cushion (pillow) made in Example 2 was used of a Handle-0-Meter compared to the material as it is currently in a KOTEX LIGHTDAYS pad is used. The size of the measured Samples were 5.08 cm by 7.62 cm (2 inches by 3 inches) and the one on the Handle-0-meter set gap width was 2.54 cm (1 inch). To running five samples gave average values of 95.7 g for the material as found in the Lightdays pad, and of 29.9 g for the material made in accordance with the invention. As is known, the Handle-0-Meter is a recognized test device for carrying out a standard test which is a measure of the Flexibility, which is a recognized comfort factor, manufactured by Thwing Albert Instrument Company, Philadelphia, Pennsylvania / USA. The test is in the instruction
. 130018/0388. 130018/0388
Manual dieser Firma beschrieben. Je niedriger der auf dem Handle-O-Meter gemessene Wert ist, um so komfortabler ist im allgemeinen das Polster (Kissen). Wie daraus zu ersehen ist, bestand ein wesentlicher Größenordnungsmäßiger Unterschied in Bezug auf die Weichheit und Elastizität, demonstriert durch den Handle-O-Meter-Test, zwischen dem konventionellen Pdntiliner-Polster und dem damit verglichenen erfindungsgemäß hergestellten Polster.Manual of this company. The lower the one on the Handle-O-Meter measured value, the more comfortable the cushion (pillow) in general. As can be seen from this, there was an essential one Order of magnitude difference in softness and resilience demonstrated by the Handle-O-Meter test between the conventional Pdntiliner pad and the one compared to it pad made according to the invention.
Es wurden einige andere Mischungen als in Beispiel 1 angegeben hergestellt. Die Art der Mischungen ist in der folgenden Tabelle angegeben. Some other mixtures than indicated in Example 1 were made. The type of mixtures is given in the following table.
Tabelle Fasermischung Table of fiber mixtures (%)(%)
Reyon 70/Polypropylen 30Rayon 70 / polypropylene 30
Reyon 60/Polypropylen 40Rayon 60 / polypropylene 40
Reyon 50/Polypropylen 50Rayon 50 / polypropylene 50
Reyon 30/Holzpulpe 30/Polypropylen 40 Reyon 25/Baumwollfasern 50/fcolypropylen 25 Reyon 75/Chisso ES 25Rayon 30 / wood pulp 30 / polypropylene 40 Rayon 25 / cotton fibers 50 / fcolypropylene 25 Reyon 75 / Chisso ES 25
Reyon 60/Vinyon 40Reyon 60 / Vinyon 40
In allen in der Tabelle angegebenen Fällen betrug die Länge der Reyonfasern 3,97 cm (l-9/ΐό inch), während diejenige der Polypropylenfasern 3,81 cm (1-1/2 inch) und diejenige der Chisso- und Vinyon-Fasern jeweils 5,08 cm (2 inch) betrug. Die Holzpulpen- und Baumwollfasern waren jeweils 3,97 cm (l-9/l6 inch) lang. Bei Chisso ES handelt es sich um ein Warenzeichen der Firma Chisso Corporation of Wyckoff,In all cases given in the table, the rayon fibers were 3.97 cm (l-9 / ΐό inch), while that of the polypropylene fibers 3.81 cm (1-1 / 2 inch) and that of the Chisso and Vinyon fibers each was 5.08 cm (2 inches). The wood pulp and cotton fibers were each 3.97 cm (l-9 / l6 inches) long. Chisso ES is a trademark of Chisso Corporation of Wyckoff,
130018/0888130018/0888
New Jersey/USA, für eine Bikomponentenfaser, bei der eine Seite aus Polypropylen besteht, während die andere Seite aus Polyäthylen besteht. Diese Fasern schmelzen zwischen 138 und H9°C (280 und 300°F) und dies " war die Verfahrenstemperatur, die während der Wärmeprägung bei ihrer Herstellung angewendet wurde. Polypropylen schmilzt bei 160 bis 171 C (320 bis 34O°F) und die Behandlungstemperatur wurde innerhalb dieses Bereiches gehalten.New Jersey / USA, for a bicomponent fiber with one side out Is made of polypropylene while the other side is made of polyethylene. These fibers melt between 138 and H9 ° C (280 and 300 ° F) and this " was the process temperature used during the heat embossing in their manufacture. Polypropylene melts at 160 to 171 ° C (320 to 340 ° F) and the treatment temperature was within that Area held.
Wie aus der vorstehenden Tabelle ersichtlich, kann es sich bei den einen Gegenstand der Erfindung bildenden Fasern um thermoplastische Verbundfasern sowie um Gemische von saugfähigen (absorptionsfähigen) Fasern handeln.In der Praxis können unter den erfindungsgemäßen Bedingungen auch andere Typen von saugfähigen (absorptionsföhigen) Fasern und Gemische von schmelzbaren Fasern verwendet werden, so lange die schmelzbaren Fasern innerhalb etwa des gleichen Temperaturbereiches schmelzen, und diese können für bestimmte Anwendungszwecke, in denen ■spezielle Eigenschaften einer Vielzahl von thermoplastischen Materialien ausgenutzt werden, sogar erwünscht sein.As can be seen from the table above, the an object of the invention to thermoplastic fibers Composite fibers as well as mixtures of absorbent fibers. In practice, under the conditions according to the invention other types of absorbent fibers and mixtures of fusible fibers can be used as long the fusible fibers melt within approximately the same temperature range, and these can be used for certain applications in which ■ special properties of a wide variety of thermoplastic materials be exploited, even be desired.
Jedes dieser saugfähigen Polster (Kissen) wurde unter Anwendung eines Sinuswellenmusters geprägt. Die wiederkehrenden Sinuswellenformen waren über die Länge der Polsterprobe in einem Abstand voneinander angeordnet. Each of these absorbent pads (pillows) was made using one Sine wave pattern embossed. The repeating sine waveforms were spaced apart over the length of the upholstery sample.
Obgleich nicht mit jedem dieser Verbundmaterialien Handle-O-Meter-Tests durchgeführt wurden, zeigte eine subjektive Inspektion, daß sie dem Produkt des Beispiels 1 in Bezug auf die Elastizität und die empfundene Weichheit viel näher standen als das KOTEX LIGHTDAYS-Pad, das zu 100 % aus Holzpulpenfasern als saugfähiger Komponente bestand. Obgleich vorläufige Absorptionstests zeigten, daß die SaugfähigkeitAlthough Handle-O-Meter tests were not carried out on each of these composite materials, a subjective inspection showed that they were much closer to the product of Example 1 in terms of elasticity and perceived softness than the KOTEX LIGHTDAYS pad, the 100% % consisted of wood pulp fibers as an absorbent component. Although preliminary absorption tests showed that the absorbency
130018/0888130018/0888
(das Absorptionsvermögen) etwas geringer war als bei dem KOTEX LIGHTDAYS-Pad und der Effekt mit der Menge des vorhandenen thermoplastischen Materials im Zusammenhang stand, war das Ausmaß der Abnahme der Saugfähigkeit (des Absorptionsvermögens) minimal und könnte logisch durch Einführung einer geringen Menge eines Materials vom supersaugfähigen Typ entweder in Pulverform während der Formungs— stufe oder sonst in Form einer zusätzlichen Faser wöhrend der Formungsstufe überwunden werden. Supersaugfähige Materialien sind an sich be- kannt und brauchen hier nicht naher erörtert zu werden.(the absorption capacity) was slightly lower than with the KOTEX LIGHTDAYS pad and the effect with the amount of thermoplastic present Material related, the extent of the decrease in absorbency (absorbency) was minimal and could be logical by introducing a small amount of a material of the superabsorbent type either in powder form during molding stage or otherwise be overcome in the form of an additional fiber during the shaping stage. Superabsorbent materials are known per se and need not be discussed further here.
Die Erfindung wurde zwar vorstehend unter Bezugnahme auf bevorzugte Ausführungsformen näher erläutert, es ist jedoch für den Fachmann selbstverständlich, daß sie darauf keineswegs beschränkt ist, sondern daß diese in vielfacher Hinsicht abgeändert und modifiziert werden können, ohne daß dadurch der Rahmen der vorliegenden Erfindung verlassen wird.Although the invention has been preferred with reference to FIG Embodiments explained in more detail, but it is for those skilled in the art it goes without saying that it is by no means restricted to this, but that these are changed and modified in many ways can without thereby departing from the scope of the present invention will.
130018/0888130018/0888
Claims (10)