DE2546781B2 - Brandschutzkitt - Google Patents

Brandschutzkitt

Info

Publication number
DE2546781B2
DE2546781B2 DE2546781A DE2546781A DE2546781B2 DE 2546781 B2 DE2546781 B2 DE 2546781B2 DE 2546781 A DE2546781 A DE 2546781A DE 2546781 A DE2546781 A DE 2546781A DE 2546781 B2 DE2546781 B2 DE 2546781B2
Authority
DE
Germany
Prior art keywords
fire
binder
polymer
chlorine
fire protection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE2546781A
Other languages
English (en)
Other versions
DE2546781A1 (de
DE2546781C3 (de
Inventor
Karl Dieter 5021 Sinnersdorf Cremer
Hans Herbert 5030 Huerth Kurth
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Axalta Coating Systems Germany GmbH and Co KG
Original Assignee
Herberts GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Herberts GmbH filed Critical Herberts GmbH
Priority to DE2546781A priority Critical patent/DE2546781C3/de
Priority to NL7611305A priority patent/NL7611305A/xx
Priority to FI762934A priority patent/FI762934A/fi
Priority to BR7606914A priority patent/BR7606914A/pt
Priority to NO763522A priority patent/NO763522L/no
Priority to AT768376A priority patent/AT352847B/de
Priority to SE7611508A priority patent/SE7611508L/xx
Priority to DK465376A priority patent/DK465376A/da
Priority to CH1317576A priority patent/CH606376A5/xx
Priority to GB43119/76A priority patent/GB1567315A/en
Priority to FR7631234A priority patent/FR2328029A1/fr
Priority to BE171600A priority patent/BE847399A/xx
Publication of DE2546781A1 publication Critical patent/DE2546781A1/de
Publication of DE2546781B2 publication Critical patent/DE2546781B2/de
Application granted granted Critical
Publication of DE2546781C3 publication Critical patent/DE2546781C3/de
Expired legal-status Critical Current

Description

Dämmschichtbildende Brandschutzfarben sind bekannt. Sie werden auf Stahl-, Beton- und Holzkonstruktionsteile wie Anstriche aufgetragen und bilden bei Feuereinwirkung eine porös aufgeblähte, wärmedämmende Schicht, die die Aufheizung des darunterlegenden Materials verzögert, so daß Stahl- und Betonteile ihre Festigkeit im Brandfall erst später verlieren als ungeschützte Teile, und bei Holz die Entflammung verzögert wird.
Diese Farben eignen sich aber nur zum Schutz von flächigen Gebilden. Für die feuerhemmende Absperrung von Fugen, beispielsweise Dehnfugen in Decken, oder für die Sicherung von Durchbrüchen oder Hohlräumen sind sie von ihrer Natur her ungeeignet.
Für diese Zwecke dienen bisher verschiedene Systeme, beispielsweise Glasfaserlaminate, Kombinationen von Glasfasern oder geschäumten Kunststoffgranulaten, die mit Butylkautschukstreifen verbunden werden (GB-PS 1080170), Dichtungsmassen aus Umsetzungsprodukten von Schwefel mit Diphenyldithiophosphat und Styrol (FR-PS 1 502687) und vulkanisierte Silicon-Elastomere (JA-PS 094385).
Zum Teil können diese Massen nur zum Abdichten von Fugen dienen, nicht aber zur Sicherung größerer Hohlräume. Gemeinsam ist ihnen, daß sie zwar schwer- oder nichtentflammbar sind, daß sie aber keine Dämmschichten bilden und bei Feuereinwirkung verspröden und die Haftung verlieren, so daß kein sicherer Abschluß mehr gewährleistet ist.
Durch die vorliegende Erfindung wird nun eine dämmschichtbildende Dichtungsmasse geschaffen, die auch über lange Zeit nicht versprödet, und die Fugen u. dgl. im Brandfall für längere Zeit feuer- und rauchdicht absperrt.
Erfindungsgegenstand ist eine feuerhemmende Dichtungsmasse nach den Ansprüchen.
Die Stabilisatoren für das Polymerisatgemisch sind insbesondere organische Zinnverbindungen. Als Dämmschichtbildner enthält die Dichtungsmasse für diesen Zweck bekannte Stoffe, insbesondere Ammoniumpolyphosphat, Melamin, Pentaerythrit und Stärke. Daneben kann die Masse zur Einstellung der Verarbeitbarkeit und der Standfestigkeit anorganische Füllstoffe wie Calciumcarbonat, Bariumsulfat und Glas- oder Mineralfasern enthalten.
Es ist zwar bekannt, Vinylchloridpolymerisate und Weichmacher als Bindemittel für die Herstellung von Kitten oder Dichtungsmassen einzusetzen, und daß derartige chlorhaltige Polymerisate schwer brennbar sind. Diese thermoplastischen Bindemittel schmelzen jedoch bei Temperaturen, wie sie im Brandfalle auftreten. Zum Beispiel bei Temperaturen ab etwa 130° C laufen desh&lb damit ausgefüllte Fugen aus. Der Fachmann hätte annehmen müssen, daß derartige Kitte und Dichtungsmassen auch dann im Brandfalle auslaufen, wenn sie dämmschichtbildende Zusätze enthalten, und daß deshalb eine Dämmschutzwirkung überhaupt nicht erzielt werden kann. Überraschenderweise wurde gefunden, daß die Dichtungsmasse gemäß der Erfindung im Brandfalle nicht abläuft, sondern daß zwar eine ganz erhebliche Erweichung und in gewissem Umfang ein Schmelzen des Bindemittels eintritt, jedoch ein Ablaufen nicht erfolgt. Anscheinend erfolgt bei diesen relativ niedrigen Temperaturen in geringem Umfang bereits eine Gasblasenbildung aufgrund des Gehalts an dämmschichtbildenden Zusätzen, und diese Gasblasen scheinen überraschenderweise ein Ablaufen der Masse zu verhindern. Es kann sich somit im gesamten Bereich der Dichtungsmasse ein Schaum bilden, der die Dämmschichtwirkung hervorruft, wobei gleichzeitig die Abdichtung gewährleistet ist, die durch die Dichtungsmasse erfolgen soll.
Als vinylchloridhaltige Polymerisate kommen beispielsweise Mischpolymerisate aus Vinylchlorid und Maleinsäureestern, insbesondere Dibutylmaleinat oder Vinylacetat in Frage, die im Handel als Rohstoffe für die Lack- und Kunststoffindustrie erhältlich sind. Als chlorhaltiges Polymerisat kann beispielsweise auch Polychlorbutadien verwendet werden.
Weichmacher, die das Polymerisatgemisch lösen und gelatinieren sind beispielsweise aliphatische oder aromatische Ester der Phthalsäure, Adipinsäure, Benzoesäure, Sebazinsäure und der Phosphorsäure, ferner schwerflüchtige chlorierte Paraffine mit einem Chlorgehalt von mindestens 50%. Phosphorsäureester und halogenierte Kohlenwasserstoffe, die der Entflammbarkeit der Masse entgegenwirken, sind dabei bevorzugt.
Weichmacher, die das Polymerisat nicht lösen und zum Ausschwitzen neigen, haben die Aufgabe, die Masse vor allem in der Oberfläche dauerplastisch zu halten. Zu dieser Klasse gehören beispielsweise nichttrocknende Fettsäureester, z. B. Rizinusöl, chlorierte Paraffine mit einem Chlorgehalt von ca. 40%, Trichloräthylphosphat, Mineralöle, Dibenzyltoluol.
Die erfindungsgemäßen Massen enthalten keine leichtflüchtigen Stoffe. Sie haften gut, auch an glatten Untergründen. Sie können von Hand verarbeitet werden oder auch mit Druckluftpistolen. Im letzten Fall soll die Verarbeitungstemperatur etwa 90° C nicht übersteigen.
Die Feuerwiderstandsdauer nach DIN 4102 beträgt mehr als 90 Minuten. Im Brandfall bilden die Massen eine wärmedämmende, mechanisch stabile Schutzschicht, die vorwiegend aus gasgefüllten Kohlenstoffzellen besteht und selbst nicht brennbar ist. Sie schützt das darunterliegende Material vor Erwärmung und bildet eine wirksame Sperre gegen das Durchtreten von Rauchgasen.
Im folgenden werden Beispiele für die Bindemittel der erfindungsgemäßen Massen und für die Zusammensetzung der gebrauchsfertigen Massen gegeben:
Beispiel 1: Bindemittel
28,0 Diäthylhexylphthalat (DOP) Trikresylphosphat Chloriertes Paraffin (ca. 50% Chlor) epoxidierte Fettsäuren organische Zinnverbindung PVC-Michpolymerisat K-Wert 56-58 80% VC 20% div. Maleinsäureester PVC-Mischpolymerisat K-Wert ca. 65 90% VC, 10% VAC Rizinusöl 13,5 Rizinusöl
33,0 5,0 3,0 0,5 !2,0
5,0
13,5
100,0 Bindemittel wie 1
Ammoniumpolyphosphat
Beispiel la: Gebrauchsfertige Masse Melamin
32,0 Pentaerythrit
15,7 Slärke
14,0 Calziumcarbonat
10,6 Bariumsulfat
5,0 Mineralfaser
10,0
y,7
3,0
100,0
Beispiel 2: Bindemittel 30,0 Dioctylsebacat 30,0 Trichlorüthylphosphat 5,0 Diiithylhexylphosphat 3.0 epoxidierte Fettsäuren 0,5 organ. Zinnverbindungen 13.0 PVC-Mischpolymerisat 40% VAC 60% VC K-Wcri
5,0 PVC-Mischpolymerisat 10% VAC W% VC K-Wert
100,0 Bindemittel wie 2 Trichloräthylphosphat Bindemittel wie 3
Ammoniumpolyphosphat Benzylbutylphthalat Ammoniumpolyphosphat
Beispiel 2 a: Gebrauchsfertige Masse Melamin Dibutylphthalat Melamin
36,0 Pentaerythrit epoxidierte Fettsäuren Pentaerythrit
14,6 Stärke organ. Zinnverbindungen Stärke
13,2 Calziumcarbonat PVC Copolymer 85% VC K-Wert 65 Calziumcarbonat
10,0 Bariumsulfat Polychlorbutadien Bariumsulfat
4,7 Mineralfaser Rizinusöl Mineralfaser
4,4
y,3 Beispiel 3: Bindemittel Beispiel 3a: Gebrauchsfertige Masse
2,8 30,0 28.0
100,0 20,0 16,0
18,5 14,5
3,0 11,0
0,5 5,5
10,0 11,0
3,0 11,0
15,0 3,0
100,0
100,0

Claims (2)

Patentansprüche:
1. Feuerhemmende dauerplastischc Dichtungsmasse aus einem Bindemittel und bekannten, dämmschichtbildenden Zusätzen sowie ggf. anorganischen Füllstoffer., dadurch gekennzeichnet, daß das Bindemittel ein Gemisch ist aus
a) einem vinylchloridhaltigc Mischpolymerisat mit einem K-Wert von über 60,
b) einem chlorhaltigen Polymerisat,
c) mindestens einem Weichmacher, der das Polymerisatgemisch lost und gelatiniert und
d) mindestens einem Weichmacher, der das Polymerisatgemisch nicht löst und zum Ausschwitzen neigt, sowie
e) üblichen Stabilisatoren für das Polymerisatgemisch.
2. Dichtungsmasse nach Anspruch 1, dadurch gekennzeichnet, daß das chlorhaltige Polymerisat b) ein weiteres vinylchloridhaltiges Mischpolymerisat mit einem K-Wert von etwa 50-60 ist.
DE2546781A 1975-10-18 1975-10-18 Brandschutzkitt Expired DE2546781C3 (de)