DE2541747A1 - Strong porous concrete for underwater constructions - withstanding press. of underground waters and erosion by waves - Google Patents

Abstract

Materials for underwater constructions, contg. fillers such as cement, gravel or the like and a binder such as cement, or cement-lime are improved in that the filler particles show irregular size distribution so that pores are formed in the resulting concrete rendering it water-permeable. The compsn. pref. contains 0.05-30.00 wt. % (w.r.t. the water) of a polymeric addition, pref. a cellulose ether, polyacrylamide or polyethylene oxide. Alternatively it may contain 0.08-2.5 wt. % (w.r.t. the water) of an alginate or casein. This water-permeable concrete is suitable for underwater constructions exposed to pressure of underground waters such as walled canals, coast strengthening constructions, wells. etc. Water penetrated into the concrete and the pressure is relieved. The addition of polymers improves the strength of the concrete, esp in early stages so that it can be moulded in situ under water, it also improves the erosion resistance, esp. in sailing canals and coastal structures. The water retention capability is increased.

Description

Baustoffmischung für Unterwasser-Bauten Building material mix for underwater structures

Die Erfindung betrifft eine Baustoffmischung für Unterwasser-Bauten, bestehend aus Zuschlagstoffen wie Sand, Kies od. dgl.The invention relates to a building material mixture for underwater structures, consisting of aggregates such as sand, gravel or the like.

und einem Bindemittel wie Zement, Zement-Kalk od. dgl.and a binder such as cement, cement-lime or the like.

Baustoffmischungen für Unterwasser-Bauten sind in zahlreichen Rezepturen bekannt. So ist es z.B. bekannt, Beton unter Wasser einzubringen, der mit Zement als hydraulisch (unter Wasser) härtendem Bindemittel in seiner Druckfestigkeit steuerbar ist und Schwind- und Quellvorgängen bei Unterwasserlagerung nicht unterliegt. Die bekannten Betone bildenrach ihrem Aushärten Festbetonkörper, in die Wasser nur in einem an die Oberfläche angrenzenden Schichtbereich eindringen kann,+jedoch mit Hilfe von Rohren oder Betonpumpen unmittelbar auf einer Auflagefläche an der Unterwasser-Baustelle aufgebracht werden, um durch den Transport des Betons im Schutze der Rohre oder anderer Ummantelungen sicherzustellen, daß ein Kontakt mit dem erodierenden Wasser erst nach dem Einbringen, und auch dann nur an der Oberfläche des Betons, stattfindet. Bei Einsatz +müssen solcher Betone für Baukörper in beispielsweise Schiffahrtskanälen sind diese hohen Erosionskräften durch Schraubensog und Wasserverdrängung von auf diesen verkehrenden schnellfahrenden Wasserfahrzeugen ausgesetzt, so daß der Baukörper bis zu seinem Aushärten ohne gesonderte Schutzmaßnahmen erhebliche Form-und Gefügeveränderungen erfahren kann.Building material mixtures for underwater structures are available in numerous recipes known. For example, it is known to pour concrete under water using cement As a hydraulically (under water) hardening binder, its compressive strength can be controlled and is not subject to shrinkage and swelling processes in underwater storage. the known concretes form solid concrete bodies after their hardening, in which water only in can penetrate a layer area adjacent to the surface, + but with With the help of pipes or concrete pumps directly on a support surface at the underwater construction site be applied to by transporting the concrete under the protection of the pipes or other sheaths ensure that there is contact with the eroding water only after it has been introduced, and then only on the surface of the concrete. When using + must such concretes for structures in, for example Shipping canals are these high erosion forces due to screw suction and water displacement exposed on these moving high-speed watercraft, so that the structure is considerable until it has hardened without any special protective measures Can experience changes in shape and structure.

Für Unterwasser-Dichtungsschichten werden als Baustoffmischungen z.B. Tone natürlichen Vorkommens, Quelltone vom Montmorillonit-Typ mit und ohne Zuschlagstoffe, z.B. Sand oder Flugasche, sowie mit und ohne weitere Bindemittel, z.B. Kalkhydrat und Zement verwendet. Auch werden Baustoffmischungen mit Bindemitteln auf Teer- oder Bitumenbasis eingesetzt, die sich ebenfalls für den Unterwassereinbau eignen. Solche Baustoffmischungen sind zwar erosionsbeständig, jedoch in ihrer Druckfestigkeit begrenzt. So bleiben z.B. Bentonit-Schichten immer weich und auch Baustoffmischungen aus Ton mit oder ohne Zement oder Kalkhydrat erreichen nur Druckfestigkeitswerte unter 100 kp/cm2.For underwater sealing layers, e.g. Clays of natural occurrence, swelling clays of the montmorillonite type with and without additives, e.g. sand or fly ash, as well as with and without other binders, e.g. hydrated lime and cement used. Building material mixtures with binders are also used on tar or bitumen base, which are also suitable for underwater installation. Such building material mixtures are erosion-resistant, but in terms of their compressive strength limited. Bentonite layers, for example, always remain soft, as do building material mixtures made of clay with or without cement or hydrated lime only achieve compressive strength values below 100 kp / cm2.

Die bekannten Baustoffmischungen sind sämtlich für Einsatzzwecke ungeeignet, bei denen auf den Baukörper Wasserdruckdifferenzen einwirken, die diesel einen unerwünschten Auftrieb vermitteln oder allgemein Belastungen aussetzen, die auf die Dauer unerwünschte Auswirkungen zeitigen. Dies ist beispielsweise bei Unterwasser-Bauten der Fall, bei denen Grundwasser auf die Baukörper mit zum Teil erheblichen Drücken einwirken. Fälle dieser Art treten bei Unterwasser-Bauten in Schiffahrtskanälen, sonstigen Kanalbauten, Uferbefestigungen, Talsperren, Schleusen, Brunne etc. auf und erfordern bisher umfangreiche und teure Schutzmaßnahmen, um trotz Fortbestand der Belastungen die Baukörper in ihrer vorbestimmten Lage zu halten, Untergrundveränderungen durch Auswaschungen etc. zu vermeiden und sonstige Beschädigungen auszuschließen. Dies gilt insbesondere bei Sohl- bzw. Deckwerken oder Wänden, welche erhebliche Flächenabmessungen darbieten. In bestimmten Fällen können daher nur Mineralfilter aus Steinschüttungen verschiedener Korngrößen, die teure Verklammerungsmaßnahmen erfordern, oder Filterschichten aus Matten vorgesehen werden, die einen Druckausgleich infolge Wasserdurchtritts erbringen, jedoch zusätzlich durch Aufbringen schwerer Lasten, z.B. großformatiger Schütt- oder Formsteine, gegenüber hydromechanischen Kräften des Wassers, die insbesondere bei Schifffahrtswegen durch Schraubensog und Wasserverdrängung von Wasserfahrzeugen erheblich sein können, geschützt und belastet werden müssen.The known building material mixtures are all unsuitable for purposes where water pressure differences act on the building structure, which makes diesel undesirable Provide buoyancy or generally expose loads that are undesirable in the long run Have an impact. This is the case, for example, with underwater structures, where groundwater affects the building structure with sometimes considerable pressures. Cases of this kind occur with underwater structures in shipping canals, others Canal construction, Bank reinforcements, dams, sluices, wells, etc. and have so far required extensive and expensive protective measures to keep the structures in to maintain their predetermined position, changes in the subsoil due to leaching etc. and to exclude other damage. This is especially true in the case of base or revetments or walls, which have considerable surface dimensions. In certain cases, therefore, only mineral filters made from rock fillings of various types can be used Grain sizes that require expensive interlocking measures, or filter layers Mats are provided that equalize the pressure as a result of the passage of water, but also by applying heavy loads, e.g. large-format bulk or shaped stones, against hydromechanical forces of the water, in particular on shipping routes due to screw suction and displacement of water from watercraft can be significant, need to be protected and encumbered.

Der Erfindung liegt die Aufgabe zugrunde eine Baustoffmischung für Unterwasser-Bauten zu schaffen, mit der in'einem einzigen Arbeitsgang auf einfache Weise Unterwasser-Baukörper herstellbar sind, die in vorgegebenem Maß wasserdurchlässig+und zugleich ein hohes Maß an Erosionsfestigkeit gegenüber den hydromechanischen Kräften des Wassers besitzen.The invention is based on the object of a building material mixture for To create underwater structures in a single operation with ease Way underwater structures can be produced, which are water-permeable to a given extent + and at the same time a high degree of resistance to erosion against the hydromechanical forces of the water.

Ausgehend von einer Baustoffmischung für Unterwasser-Bauten, bestehend aus Zuschlagstoffen wie Sand, Kies, od. dgl. und einem +sind Bindemittel wie Zement, Zement-Kalk od. dgl.wird dies nach der Erfindung erreicht durch einen Zusatzstoff, der der Baustoffmischung eine vorgegebene, erhöhte Wasserretention und Erosionsfestigkeit vermittelt, und durch eine Kornzusammensetzung des Zuschlagstoffgemenges mit derart unstetiger Sieblinie, daß in dem von der Baustoffmischung gebildeten fertigen Baukörper untereinander verbundene, dem Baukörper eine vorgegebene Wasserdurchlässigkeit vermittelnde Haufwerksporen vorhanden sind.Based on a mix of building materials for underwater structures Made of aggregates such as sand, gravel, or the like. And a + are binder such as cement, cement-lime or the like, this is achieved according to the invention by a Additive that gives the building material mixture a predetermined, increased water retention and resistance to erosion mediated, and by a grain composition of the aggregate mixture with such discontinuous grading curve that in that formed by the building material mixture finished building structure interconnected, the building structure a given water permeability mediating heap pores are present.

Aufgrund der der Baustoffmischung durch den Zusatzstoff vermittelten erhöhten Wasserretentionbesitzt die Mischung bereits im Grünzustand> d.h. im frisch zubereiteten und noch nicht erhärteten Zustand, trotz ihrer besonderen Kornzusammensetzung ein solches Maß an Erosionsfestigkeit gegenüber Wasser, daß es möglich ist, die Mischung im Grünzustand im freien Fall durch das Wasser z.B. auf die Sohle eines Gewässers, wie eines Schifffahrtskanals, aufzubringen, ohne daß durch die dabei auftretenden hydromechanischen Kräfte die Ausgangseigenschaften der Mischung verändert werden. Insbesondere tritt, auch bei einer hohen freien Fallhöhe durch das Wasser, keine Trennung der Bestandteile der Mischung trotz verschiedener Dichte ihrer Bestandteile, vor allem kein Auswaschen oder Auftreiben des Bindemittels entsprechend dem Stoke'schen Gesetz, ein, gemäß dem sich sonst beim freien Fall durch Wasser die gröberen Bestandteile einer Mischung von den feineren trennen und zuerst auf den Untergrund gelangen. Vielmehr bleibt die Homogenität des Bindemittel-Zuschlagstoff-Gemisches beim freien Fall durchs Wasser im vollen Umfang erhalten, so daß mangels irgendwelcher Sedimentationserscheinungen,die die die für die Wasserdurchlässigkeit gewünschte Haufwerksporigkeit der Mischung während des Einbringens unkontrolliert verändern könnten, ein Unter-wasserbaukörper in einem einzigen Arbeitsgang gebildet werden kann, dessen Wasserdurchlässigkeit bzw. Filtereigenschaft exakt dem bei der Bereitung der Baustoffmischung vorherbestimmten Durchlässigkeitsgrad entspricht. Da die Baustoffmischung nach der Erfindung schon im Grün-zustand erosionsfest ist und beim Einbringen durchs Wasser keinerlei Bindemittel wie Zement, Zement-Kalk od. dgl., durch Entmischung verliert, besitzt der mittels der erfindungsgemäßen Baustoffmischung hergestellte Baukörper nach dem hydraulischen Erhärten seines Bindemittels auch eine entsprechend vorherbestimmbare hohe Festigkeit und Beständigkeit gegenüber den hydromechanischen Kräften des Wassers im eingebauten Zustand. Daher ist es nicht erforderlich, den Baukörper in weiteren Arbeitsgängen gegenüber den unter Wasser auftretenden Beanspruchungen zu sichern.Because of the mix of building materials mediated by the additive The mixture already has increased water retention in the green state> i.e. in Freshly prepared and not yet hardened, despite their special grain composition such a level of erosion resistance to water that it is possible that Mixture in the green state in free fall through the water e.g. onto the sole of a Waters, like a shipping canal, to be applied without being through the thereby occurring hydromechanical forces change the initial properties of the mixture will. In particular, even with a high free fall height through the water, no separation of the components of the mixture despite the different densities of their components, especially no washing out or swelling of the binder according to Stoke's Law, according to which the coarser constituents are otherwise in free fall through water Separate a mixture from the finer ones and get onto the substrate first. Rather, the homogeneity of the binder-aggregate mixture remains in the free Fall through the water in full Preserved scope, so that for lack of any Sedimentation phenomena that are the ones that are desired for water permeability Uncontrolled change in the pore size of the mixture while it is being poured in an underwater structure could be formed in a single operation can, whose water permeability or filter property exactly that of the preparation the building material mix corresponds to the predetermined degree of permeability. Because the building material mix According to the invention, it is erosion-proof even in the green state and through when it is introduced Water no binding agents such as cement, cement-lime or the like, due to segregation loses, has the one produced by means of the building material mixture according to the invention Building structure after the hydraulic hardening of its binding agent also one accordingly predictable high strength and resistance to the hydromechanical Forces of water when installed. Therefore it is not necessary to use the Building structure in further work steps against the stresses occurring under water to secure.

Zur Erzielung erhöhter Wasserre-tention und Erosionsfestigkeit enthält die Baustoffmischung vorzugsweise 0,05 bis 3,00 Gew.%, bezogen auf den Wassergehalt der einbaufertig zubereiteten Mischung, eines polymeren Zusatzstoffes, der der Mischung eine Wasserretention und Erosionsfestigkeit vermittelt, welche ein Liter Zement-Wasser-Mischung mit einem Wasserzementwert von 0,5 bei einer Wasserabgabe von 60 cm3 unter Wasserstrahl-Vakuum von 12 Torr in 60 sec. als unterem Grenzwert darbietet.Contains to achieve increased water retention and erosion resistance the building material mixture is preferably 0.05 to 3.00% by weight, based on the water content the ready-to-install mixture, a polymer additive, the mixture water retention and erosion resistance are imparted by a liter of cement-water mixture with a water-cement ratio of 0.5 with a water release of 60 cm3 under a water jet vacuum of 12 Torr in 60 sec. as the lower limit.

Zwar ist schon eine Baustoffmischung für Unterwasser-Bauten, bestehend aus Zuschlagstoffen wie Sand, Kies od. dgl., einem Bindemittel wie Zement, Zement-Kalk od. dgl. und einem Zusatzstoff dieser Art, der der Baustoffmischung eine vorgegebene, erhöhte Wasserretention und Erosionsfestigkeit vermittelt, bekannt, jedoch bildet diese Baustoffmischung einen Baukörper mit Festbetoneigenschaften und entsprechender Wasserundurchlässigkeit.There is already a mix of building materials for underwater structures from aggregates such as sand, gravel or the like, a binding agent such as cement, cement-lime or the like and an additive of this type, which gives the building material mixture a predetermined, increased water retention and resistance to erosion mediated, known, but forms this building material mixture has a structure with hardened concrete properties and corresponding Impermeability to water.

Als Zuschlagstoffe kommen gebräuchliche Zuschlagstoffe wie Quarzite, Sand Kies etc. in allen Korngrößen für die erfindungsgemäße Baustoffmischung in Betracht, sofern nur die verwendeten Sieblinie für die Kornzusammensetzung die untereinander verbundenen Haufwerksporen in der Mischung sichern. )h der Regel werden hierzu Ausfallkörnungen, d.h. Zuschlaggemische, denen einzelne Korn gruppen fehlen, bzw. Einkornbeton-Mischungen verwendet.Common additives such as quartzite, Sand gravel etc. in all grain sizes for the building material mixture according to the invention in Consider, provided that only the grading curve used for the grain composition, the one with the other Secure connected heap pores in the mix. ) h as a rule, failure grains are used for this purpose, i.e. aggregate mixtures lacking individual grain groups or single-grain concrete mixtures used.

Als Beispiel für eine erfindungsgemäße Baustoffmischung sei die nachfolgende Rezeptur genannt: 320 kg/m3 Zement PZ 350 F, 150 kg/m3 Sand 0/2 mm, 3 1400 kg/m3 Kies 8/16 mm, 2 kg/m3 polymerer Zusatzstoff und 100 1 Wasser.The following is an example of a building material mixture according to the invention Recipe mentioned: 320 kg / m3 cement PZ 350 F, 150 kg / m3 sand 0/2 mm, 3 1400 kg / m3 Gravel 8/16 mm, 2 kg / m3 polymeric additive and 100 l water.

Es versteht sich, daß die obige, lediglich als Beispiel angeführte Rezeptur je nach der geforderten Wasserdurchlässigkeit bzw Filtereigenschaft und Festigkeit des Baukörpers, insbesondere durch Variation des K*ngefüges und/oder des von dem Bindemittel und dem im Betonzuschlag enthaltenen Kornanteils O - 0,25 mm gebildeten Mehlkorngehaltes, mannigfaltige Abwandlungen erfahren kann. Dabei muß jedoch der maximale Mehlkorn- bzw. Bindemittelanteil bei gewünschter hoher Festigkeit des Baukörpers zur Aufrechterhaltung einer gewissen Wasserdurchlässigkeit des Baukörpers unterhalb einer die untereinander verbundenen Haufwerksporen des Zuschlagstoffgemenges aus füllenden Menge liegen, während+andererseits bei geringen Anforderungen an die Festigkeit des Baukörpers bis auf Null herabgesetzt werden kann, in welchem Fall dann allein der polymere Zusatzstoff den entmischungsfreien Zusammenhalt des Zuschlagstoffgemenges bewirkt.It goes without saying that the above is given as an example only Recipe depending on the required water permeability or filter properties and strength of the building, in particular by varying the structure and / or of the Binder and the grain fraction O - 0.25 mm contained in the concrete aggregate Flour grain content, can experience manifold modifications. However, the maximum flour grain or binder content with the desired high strength of the structure to maintain a certain water permeability of the structure below one of the interconnected heap pores of the aggregate mixture filling amount, while + on the other hand, with low demands on the strength of the structure can be reduced to zero, in which case then alone the polymeric additive ensures that the aggregate mixture is held together without segregation causes.

Der der Baustoffmischung die erhöhte Wasserretention und Erosions festigkeit vermittelnde polymere Zusatzstoff kann im übrigen in an sich bekannter Weise von Zelluloseäther, Polyacrylamiden oder Polyäthylenoxiden hohen Nolekulargewichts gebildet sein. Stattdessen können als Zusatzstoff auch Alginate oder Kaseine, insbesondere in einer Menge von 0,08 bis 2,5 Gew.%, bezogen auf den Wassergehalt der Mischung, enthalten sein. Zur Abbindebeschleunigung kann die Baustoffmischung zusätzlich Kalziumchlorid, Natrmmiluminat oder Tonerdeschmelzzement enthalten. Schließlich kann in der Mischung auch Tonmehl, Bentonit oder Kieselgur in einer Menge von 0,5 bis 3%, bezogen auf die Gesamtmischung, enthalten sein.That of the building material mix the increased water retention and erosion strength-imparting polymer additive can also be known per se Way of cellulose ethers, polyacrylamides or polyethylene oxides of high molecular weight be educated. Instead, alginates or caseins, in particular in an amount of 0.08 to 2.5% by weight, based on the water content of the mixture, be included. To accelerate the setting, the building material mixture can also contain calcium chloride, Contains sodium siluminate or high-alumina cement. Finally can be in the mix also powdered clay, bentonite or kieselguhr in an amount of 0.5 to 3%, based on the total mix.

+er Mittels der erfindungsgemäßen Baustoffmischung ist es erstmals möglich, erosionsfeste und eine vorgegebene Wasserdurchlässigkeit gewährleistende Baukörper wie Sohlen, Deckwerke und Wände von Unterwasserbauten zu errichten, und dies darüber hinaus mit einem Höchstmaß an Wirtschaftlichkeit aufgrund der Möglichkeit eines Einbringens der im Grünzustand befindlichen Mischung im freien Fall durch das Wasser. Je nach der Einstellung der Konsistenz und des Korngerüstes der Baustoffmischung schmiegt sich diese hierbei in vorgebbarer Beschichtungsstärke Unebenheiten des Untergrundes an, wobei infolge des der Baustoffmischung durch den polymeren Zusatzstoff vermittelten hohen Zusammenhalts sich eine solche gleichmäßige Schichtstärke nicht nur auf horizontalen sondern auch auf geneigten Auflageflächen erreichen läßt, gleichgültig ob diese in sich mehr oder weniger zerklüftet oder wellig sind. Daher ist die Baustoffmischung auch besonders gut alls Verklammerungsmaterial einsetzbar.+ he By means of the building material mixture according to the invention it is possible for the first time to be erosion-proof and with a given water permeability guaranteeing structures such as floors, revetments and walls of underwater structures to erect, and in addition, with a maximum of economic efficiency due to the possibility of introducing the mixture in the green state in free fall through the water. Depending on the setting of the consistency and the The grain structure of the building material mixture nestles here in a specifiable coating thickness Unevenness of the subsurface, whereby as a result of the building material mixture through the polymeric additive imparted high cohesion to such a uniform Layer thickness not only on horizontal but also on inclined contact surfaces can be achieved, regardless of whether this is more or less fissured or are wavy. Therefore, the building material mix is also particularly good as a clamping material applicable.

Claims (1)

Patentansprüche: 1. Baustoffmischung fUr Unterwasser-Bauten, bestehend aus Zuschlagstoffen wie Sand, Kies od. dgl. und einem Bindemittel wie Zement, Zement-Kalk od. dgl., gekennzeichnet durch einen Zusatzstoff, der der Baustoffmischung eine vorgegebene, erhöhte Wasserretention und Erosionsfestigkeit vermittelt, und durch eine Kornzusammensetzung des Zuschlagstoffgemenges mit derart unstetiger Sieblinie, daß in dem von der Baustoffmischung gebildeten fertigen Baukörper untereinander verbundene, dem Baukörper eine vorgegebene Wasserdurchlässigkeit vermittelnde Haufwerksporen vorhanden sind. Claims: 1. Building material mixture for underwater structures, consisting of aggregates such as sand, gravel or the like and a binding agent such as cement, cement-lime Od. The like., characterized by an additive that the building material mixture a given, increased water retention and resistance to erosion mediated, and through a grain composition of the aggregate mixture with such an unsteady grading curve, that in the finished structure formed by the building material mixture with one another connected heap pores that give the building a given level of water permeability available. 2. Baustoffmischung nach Anspruch 1, dadurch gekennzeichnet, daß die Baustoffmischung 0,05 bis 3,00 Gew.g,bezogen auf den Wassergehalt der einbaufertig zubereiteten Ivlischung, eines polymeren Zusatzstoffes enthält, der der Mischung eine Wasserretention und Erosionsfestigkeit vermittelt, welche ein Liter Zement-Wasser-Mischung mit einem Wasserzementwert von 0,5 bei einer Wasserabgabe von 60 cm3 unter Wasserstrahl-Vakuum von 12 Torr in 60 sec. als unterem Grenzwert darbietet.2. Building material mixture according to claim 1, characterized in that the Building material mixture 0.05 to 3.00 g by weight, based on the water content of the ready-to-install prepared mixture, a polymeric additive that makes up the mixture water retention and erosion resistance are imparted by a liter of cement-water mixture with a water-cement ratio of 0.5 with a water release of 60 cm3 under a water jet vacuum of 12 Torr in 60 sec. as the lower limit. 3. Baustoffmischung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Baustoffmischung als Zusatzstoff Zelluloseäther, Polyacrylamide oderPolyäthylenoxide hohen Molekulargewichts enthält 4. - Baustoffinischung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Mischung als Zusatzstoff'Alginate oder Kaseine enthält.3. Building material mixture according to claim 1 or 2, characterized in that that the building material mixture as an additive cellulose ethers, polyacrylamides or polyethylene oxide contains high molecular weight 4. - Mixture of building materials according to claim 1 or 2, characterized in that the mixture as Zusatzstoff'Alginate or Contains caseins. 5. Baustoffmischung nach Anspruch 4, dadurch gekennzeichnet, daß die Alginate oder Kaseine in der Mischung in einer Menge von 0,08 bis 2,5 Gew.%, bezogen auf den Wassergehalt der Mischung, enthalten sind.5. Building material mixture according to claim 4, characterized in that the Alginates or caseins in the mixture in an amount of 0.08 to 2.5% by weight, based on on the water content of the mixture. 6. Baustoffmischung nach einem oder mehreren der Ansprüche 1 bis 5, dadurch gekennzeichnet,daß die Baustoffmischung zur Abbindebeschleunigung Kalziumchlorid, Natrium-Aluminat oder Tonerdeschmelzzement enthält.6. Building material mixture according to one or more of claims 1 to 5, characterized in that the building material mixture to accelerate the setting is calcium chloride, Contains sodium aluminate or high-alumina cement. 7. Baustoffmischung nach einem oder mehreren der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die Baustoffmischung Tonmehl, Bentonit oder Kieselgur in einer Menge-von 0,5 bis 3%, bezogen auf die Gesamtmischung, enthält.7. building material mixture according to one or more of claims 1 to 6, characterized in that the building material mixture is powdered clay, bentonite or kieselguhr in an amount of 0.5 to 3%, based on the total mixture.