DE2438487A1 - Production of dressing tool for grinding discs - has grooves produced on homogeneous base which is then covered with diamond film - Google Patents

Abstract

Production of a dressing tool, especially a rotating dressing tool for grinding discs, with a base which carries projections effective as cutting elements where grooves are machined into the outside of the homogenous base to form regularly spaced, like projections. Following this, with the projections and grooves, a diamond film is evaporated onto the outside by cathodic gas discharge in a thickness of 0.01 to 5 mm. The grooves can be produced mechanically or they can be chemically produced by the anodic etching of the base by means of an acid using a template.

Description

Verfahren zum Herstellen eines Abrichtwerkzeuges, insbesondere für Schleifscheiben und danach hergestelltes Erzeugnis Die Erfindung betrifft ein Verfahren zum Herstellen eines Abrichtwerkzeuges, insbesondere eines rotierenden Abrichtwerkzeuges für Schleifscheiben, mit einem Grundkörper, der als Schneidelemente wirksame Vorsprünge trägt sowie ein danach hergestelltes Erzeugnis.Method for producing a dressing tool, in particular for Grinding Wheels and Product Manufactured therefrom The invention relates to a method for producing a dressing tool, in particular a rotating dressing tool for grinding wheels, with a base body, the projections effective as cutting elements carries as well as a product manufactured according to it.

Es sind rotierende Abrichtwerkzeuge für Schleifscheiben bekannt, die auf ihrer Arbeitsfläche einen einschichtigen Satz von Diamanten aufweisen und ein Profil der Arbeitsfläche, das dem zu erzeugenden Profil der Arbeitsfläche der Schleifscheibe angepaßt ist. Die in der Arbeitsfläche des Abrichtwerkzeuges liegenden Diamanten sind bei einem solchen bekannten Werkzeug beispielsweise durch eine metallische Bindung gehalten oder durch ein Bindemittel, das aus einem Kunstharz oder einem keramischen Stoff besteht. Die Verteilung der Diamanten auf der Arbeitsfläche entspricht dabei entweder einer stochastischen Verteilung mit dichtestmöglichem Oberflächenbesatz, oder die einzelnen Diamanten befinden sich in festgelegten geometrisch bestimmten Positionen, Das gilt auch für solche Werkzeuge, deren Abrichtkörner aus kubisch-kristallinem Bornitrid bestehen, Sollen sich dabei die Diamanten in einer bestimmten Position befinden, so werden sie beispielsweise von Hand an vorgegebenen Stellen in einen Formring eingesetzt, der das Negativprofil des zu fertigenden Abrichtwerkzeuges enthält. Die Zwischenräume zwischen den Diamantkörnern werden danach mit einem metallischen Bindemittel oder einem solchen aus einem anderen Material ausgefüllt, so daß ein Körper entsteht, der auf seiner äußeren Fläche die Diamanten enthält, Anschließend wird der äußere Formring entfernt.There are rotating dressing tools for grinding wheels known that have a single-layer set of diamonds and a Profile of the working surface, the profile of the working surface of the grinding wheel to be generated is adapted. The diamonds lying in the working surface of the dressing tool are in such a known tool, for example, by a metallic one Bond held or by a binder made of a synthetic resin or a ceramic material. The distribution of the diamonds on the work surface corresponds either a stochastic distribution with the densest possible surface coverage, or the individual diamonds are geometrically determined Positions, that also applies to those Tools, their dressing grains consist of cubic crystalline boron nitride, should the diamonds be in are located in a certain position, they are specified by hand, for example Set in a form ring, which is the negative profile of the dressing tool to be manufactured contains. The spaces between the diamond grains are then covered with a metallic Binder or such a filled out of another material, so that a Body emerges, which then contains the diamonds on its outer surface the outer molded ring is removed.

Für eine Abfuhr der abgerichteten Schleifscheibenpartikel aus der Berührungszone zwischen dem Abrichtwerkzeug und der Schleifscheibe ist ein Überstand der wirksamen Diamantspitzen über das Niveau der Bindung erforderlich. Im Verlaufe des Einsatzes des rotierenden Abrichtwerkzeuges wird dieses Niveau der Bindung infolge der abrasiven Wirkung der abgerichteten Schleifscheibenpartikel auf die Bindung in der Kontaktzone zurückverlagert.For a removal of the dressed grinding wheel particles from the The contact zone between the dressing tool and the grinding wheel is a protrusion of effective diamond tips beyond the level of bond required. During the use of the rotating dressing tool will result in this level of bond the abrasive effect of the dressed grinding wheel particles on the bond shifted back in the contact zone.

Das Ende eines möglichen Einsatzes des Diamantwerkzeuges ergibt sich, wenn das Bindungsniveau gegenüber den wirksamen Diamantspitzen so weit zurückversetzt ist, daß der verbleibende Bindungsst nicht mehr ausreicht, die Diamanten unter den beim Abrichten auftretenden Kräften im Bindungsverband zu halten, so daß die Diamanten aus dem Bindungsverband herausfallen. Dabei ergibt sich ein Verlust dergeometrischen Form der abzurichtenden Schleifscheibe, die eine Toleranzüberschreitung der geforderten Werkstückabmessungen bewirken kann und keinen weiteren Einsatz des Abrichtwerkzeuges zuläßt. Hierbei ist zu berücksichtigen, daß die rotierenden Abrichtwerkzeuge für Schleifscheiben eine sehr hohe Maßgenauigkeit aufweisen müssen, wobei allgemein Toleranzen von lediglich 0,002 mm hinsichtlich der Größe des Durchmessers bei der Herstellung zulässig sind. Dadurch ergibt sich ein erheblicher Arbeitsaufwand in der Herstellung dieser bekannten Abrichtwerkzeuge.The end of a possible use of the diamond tool results, when the bond level is so far set back from the effective diamond tips is that the remaining bond is no longer sufficient, the diamonds under the To keep forces occurring during dressing in the bond bond, so that the diamonds fall out of the binding bandage. This results in a loss of the geometric Shape of the grinding wheel to be dressed that exceeds the tolerance required Can cause workpiece dimensions and no further use of the Dressing tool allows. It should be noted that the rotating dressing tools for Grinding wheels must have a very high dimensional accuracy, with general Tolerances of only 0.002 mm in terms of the size of the diameter of the Manufacturing are permitted. This results in a considerable amount of work in the manufacture of these known dressing tools.

Ein weiterer Mangel der bekannten Abrichtwerkzeuge ist darin zu sehen, daß die wirksame Gesamtoberfläche der einzelnen Schneidelemente nicht von gleichmäßiger Härte ist, da bei Verwendung einzeln eingesetzter Diamantkörner aufgrund der unterschiedlichen Orientierung der Kristalle, durch die sich eine undrschiedliche d.h. eine Härte,/Anisotropie,ergibt, da jeder einzelne Diamant in verschiedenen Richtungen unterschiedlich hart ist,hinsichtlich ihrer Wirksamkeit die einzelnen Schneidelemente insgesamt also von unterschiedlicher Härte sind. Eine solche unterschiedliche Härte in den verschiedenen Richtungen der einzelnen Diamantkörner kann nämlich nicht berücksichtigt werden bei ihrem Einsatz.Another shortcoming of the known dressing tools can be seen in that the effective total surface of the individual cutting elements is not of more uniform Hardness is because when using individually inserted diamond grains due to the different Orientation of the crystals, which results in an indifferent i.e. a hardness / anisotropy, since every single diamond is differently hard in different directions, regarding the effectiveness of the individual cutting elements is therefore altogether different Hardness are. Such different hardness in the different directions of the This is because individual diamond grains cannot be taken into account when they are used.

Aufgabe der Erfindung ist es, ein Abrichtwerkzeug zu schaffen, das bei verhältnismäßig geringem Fertigungsaufwand eine sehr hohe Maßge#nauigkeit in der Herstellung zuläßt und eine gleichförmige Wirkung bei seinem Einsatz aufgrund einer gleichförmigen Beschaffenheit aller Schneidelemente. Gemäß der Erfindung ist dafür vorgesehen, daß in die Außenseite des homogenen Grundkörpers Rillen zur Ausbildung von in gleichmäßigem Abstand zueinander stehenden gleichförmigen Vorsprüngen eingearbeitet werden und danach auf die Außenseite mit den Vorsprüngen und Rillen ein Film aus Diamant in einer Stärke von 0,01 bis 5 ym durch kathodische Gasentladung aufgedampft wird. Die einzelnen Schneidelemente bestehen in diesem Fall also aus gleichförmigen Vorsprüngen, die jeweils mit Diamant beschichtet sind, wobei keine Gefahr des Ausbrechens einzelner Schneidelemente gegeben ist, da die gesamte Arbeitsfläche des Abrichtwerkzeuges in gleichförmiger Stärke, also nicht nur die Vorsprünge selber, sondern auch deren Zwischenräume, mit dem zum Abrichten allein wirksamen Diamant beschichtet sind. Dadurch lassen sich Abrichtwerkzeuge mit einer äusserst präzisen Abmessung herstellen unter verhältnismäßig geringem Aufwand, denn die Rillen können entweder mechanisch in den Grundkörper eingearbeitet werden, und zwar beispielsweise durch Fräsen oder unter Verwendung einer Schablone auch durch Sandstrahlen oder die Rillen zwischen den einzelnen Vorsprüngen, durch welche die Vorsprünge überhaupt erzeugt werden, können chemisch durch anodisches Ätzen des Grundkörpers mittels einer Säure wie einer Salzsäure oder Salpetersäure unter Verwendung einer Schablone erzeugt werden. Der Grundkörper kann dafür beispielsweise aus Stahl bestehen. Infrage kommen jedoch auch fü#ie Herstellung des Grundkörpers Nichteisenmetalle oder keramische Materialien.The object of the invention is to create a dressing tool that a very high dimensional accuracy in the manufacture and a uniform effect due to its use a uniform quality of all cutting elements. According to the invention is provided that in the outside of the homogeneous body grooves for training of equally spaced from each other standing uniform Projections are incorporated and then on the outside with the projections and grooving a film of diamond in a thickness of 0.01 to 5 μm by cathodic Gas discharge is vaporized. The individual cutting elements consist in this So the case of uniform projections, each coated with diamond, there is no risk of individual cutting elements breaking out, since the entire working surface of the dressing tool in uniform thickness, i.e. not only the projections themselves, but also the spaces between them, with that for dressing only effective diamond are coated. This allows dressing tools Manufacture with extremely precise dimensions at a relatively low cost Effort, because the grooves can either be mechanically incorporated into the base body , for example by milling or using a template also by sandblasting or the grooves between the individual protrusions which the protrusions are ever generated can be chemically by anodic Etching of the base body using an acid such as hydrochloric acid or nitric acid can be generated using a template. The main body can for this purpose, for example made of steel. However, they are also suitable for manufacturing the base body Non-ferrous metals or ceramic materials.

Zum Zwecke einer besseren Haftung des Diamanten auf einem Grundkörper, dessen Material für ein Aufdampfen von Diamant durch kathodische Gasentladung weniger geeignet ist, kann der Grundkörper zunächst mit einer Trägerschicht versehen werden, wie beispielsweise aus Nickel oder einem anderen Material, das vorzugsweise galvanisch auf den Grundkörper aufgetragen ist.For the purpose of better adhesion of the diamond to a base body, its material for a vapor deposition of diamond by cathodic gas discharge less is suitable, the base body can first be provided with a carrier layer, like for example made of nickel or any other material that is preferably applied galvanically to the base body.

Als vorteilhaft wurde es weiterhin erkannt, wenn zum Zwecke der Herstellung von in ihren Abmessungen verhältnismäßig großen Abrichtwerkzeugen diese aus mehreren Segmenten zusammengesetzt werden, die jeweils aus einem Grundkörper bestehen, der auf seiner Außenseite im gleichmäßigen Abstand zueinanderstehende,gleichförmige Vorsprünge trägt und einen durch kathodische Gasentladung aufgetragenen Film aus Diamant in einer Stärke von O,O# bis 5 rom, der sowohl die Vorsprünge allseitig wie auch ihre Zwischenräume überdeckt. Ein Zusammenfügen derartiger Segmente kann dann durch Kleben, Löten oder andere Verfahren erfolgen, die an sich bekannt sind0 Durch ein derartiges Zusammensetzen eines Abrichtwerkzeuges aus mehreren gleichförmigen Segmenten besiht die Möglichkeit, in verhältnismäßig kleinen Gaskammern die Bestandteile bzw. die wirksame Außenseite der Teilsegmente des Grundkörpers mit der Diamantschicht zu bedampfen, die danach zu Werkzeugen inveiner Größe zusammenzusetzen sind, welche nicht geeignet wäre für die Aufnahme in einer handelsüblichen relativ kleinen Gaskammer.It has also been recognized as advantageous if, for the purpose of producing dressing tools that are relatively large in size, they are made up of several Segments are assembled, each consisting of a base body, which carries uniformly spaced, uniform projections on its outside and a film of diamond applied by cathodic gas discharge in a thickness of O, O # to 5 rom, which both the projections on all sides as also covers their interstices. Such segments can then be joined by gluing, soldering or other methods that are known per se0 By combining a dressing tool in this way from several uniform segments, there is the possibility of the components or the effective outer side of the sub-segments of the base body in relatively small gas chambers to vaporize the diamond layer, which are then to be assembled into tools in a size which would not be suitable for inclusion in a commercially available, relatively small gas chamber.

Ein weiterer Vorteil des erfindungsgemäßen Abrichtwerkzeuges ist darin zu sehen, daß es durch das nachträgliche Aufdampfen des Diamantfilmes in einer genau vorherbestimmbaren Durchmessergrösse zu erstellen ist, denn es ist verhältnismäßig einfach, die gewünschten Abmessungen durch eine zeitliche Steuerung des Aufdampfens vom Diamanten hervorzurufen.Another advantage of the dressing tool according to the invention is therein to see that it is exactly due to the subsequent vapor deposition of the diamond film A predeterminable diameter size is to be created, because it is proportionate simply, the desired dimensions through a timing of the vapor deposition from the To evoke diamonds.

Ein weiterer Vorteil liegt in dem Umstand, daß die durchgehende äußere Diamantschicht zu einer vollständig gleichmäßigen Härte der wirksamen Arbeitsfläche führt im Gegensatz zu der Verwendung einzelner Diamantkörner unterschiedlicher Orientierung.Another advantage lies in the fact that the continuous outer Diamond layer to a completely uniform hardness of the effective work surface in contrast to the use of individual diamond grains with different orientations.

Ein Ausführungsbeispiel der Erfindung ist nachstehend unter Bezugnahme auf eine Zeichnung erläutert. In der Zeichnung zeigen: Figur 1: einen Teilausschnitt einer Profilabrichtrolle in der Seitenansicht, Figur 2: einen Teilausschnitt der Profilabrichtrolle von Fig. 1 in vergrößertem Maßstab, teilweise im Schnitt, Figur 3; die Teildraufsicht auf den Grundkörper der Profilabrichtrolle in vergrößertem Maßstab und Figur 4: einen Schnitt nach der Linie IV-IV der Figur 3.An embodiment of the invention is hereinafter referred to explained on a drawing. The drawing shows: FIG. 1: a partial section a profile dressing roller in the side view, Figure 2: a partial section of the Profile dressing roller of FIG. 1 on an enlarged scale, partly in section, FIG 3; the partial top view of the base body of the profile dressing roller in enlarged Scale and FIG. 4: a section along the line IV-IV in FIG. 3.

Die in den Figuren wiedergegebene Profil-Abrichtrolle für Schleifscheiben besitzt einen Grundkörper 1 dessen äußere Umfangsfläche mit einem gleichförmigen Netz von Rillen versehen ist, die sich diagonal kreuzen. Die Rillen 2 haben eine Tiefe von 0,7 mm gemäß der Darstellung von Figur 4, welche eine zwanzigfache Vergrösserung der Diamantabrichtrolle gemäß Figur 1 im Ausschnitt zeigt.The profile dressing roller for grinding wheels shown in the figures has a base body 1 whose outer peripheral surface with a uniform Network of grooves is provided that cross diagonally. The grooves 2 have one Depth of 0.7 mm as shown in FIG. 4, which is a twenty-fold magnification the diamond dressing roller according to Figure 1 shows in detail.

Durch die Anordnung der sich diagonal kreuzenden Rillen 2 werden auf dem Grundkörper 1 der Abrichtrolle radial vorstehende,gleichförmige und im gleichen Abstand zueinander stehende Vorsprünge 3 geschaffen, die jeweils einen viereckigen Querschnitt aufweisen, Die Hervorbringung dieser Rillen 2 und damit der Vorsprünge 3 kann durch Fräsen des Grundkörpers 1 erfolgen, insbesondere wenn dieser beispielsweise aus Stahl besteht,oder unter Verwendung einer Schablone, wie beispielsweise eines Nylonnetzes, durch chemisches Ätzen mittels einer Säure.Due to the arrangement of the diagonally crossing grooves 2 are on the base body 1 of the dressing roller radially protruding, uniform and in the same Spaced projections 3 are created, each of which is a square Have cross-section, the production of these grooves 2 and thus the projections 3 can be done by milling the base body 1, especially if this is for example made of steel, or using a template such as a Nylon mesh, by chemical etching with an acid.

Nach Herstellung der Vorsprünge auf den Grundkörper 1 erfolgte bei dem in der Zeichnung wiedergegebenen Ausführungsbeispiel eine Beschichtung des Grundkörpers 1 mit einer als Zwischenschicht wirksamen Trägerschicht 5, die beispielsweise aus Nickel, Kupfer oder Kobalt bestehen kann und galvanisch auf dem Grundkörper niedergeschlagen wurde. Diese Trägerschicht 5 trägt einen Diamantfilm 4, der im vorliegenden Beispiel eine Stärke von 2,0/um aufweist. Das Aufdampfen des Diamantfilmes 4 erfolgt in einer Gaskammer durch kathodische Gasentladung unter einem Vakuum von 10 3 bis 10 5 Torr unter niedrigen Temperaturen.After the projections were produced on the base body 1, at the embodiment shown in the drawing, a coating of the base body 1 with a carrier layer 5 that acts as an intermediate layer and is composed, for example, of Nickel, copper or cobalt can be made and deposited galvanically on the base body became. This carrier layer 5 carries a diamond film 4, which in the present example has a thickness of 2.0 / µm. The vapor deposition of the diamond film 4 takes place in a Gas chamber by cathodic gas discharge under a vacuum of 10 3 to 10 5 Torr under low temperatures.

Weitere Größenverhältnisse ergeben sich aus der Figur 3O Danach beträgt die Beite der einzelnen Vorsprünge 3 0,4 mm und ihr gegenseitiger Abstand nahezu 2 mm.Further size ratios result from FIG. 3O thereafter the width of the individual projections 3 0.4 mm and their mutual distance almost 2 mm.

Der Figur 1 ist weiterhin andeutungsweise zu entnehmen, daß eine Profil-Abrichtrolle auch aus mehreren unterschiedlichen Segmenten 6, 6', 6'' zusammengesetzt sein kann, die jeweils aus einem Grundkörper bestehen, der auf seiner Außenseite im gleichmäßigen Abstand zueinanderstehende, gleichförmige Vorsprünge 3 trägt und einen durch Gasentladung aufgetragenen Film aus Diamant, welcher die Vorsprünge und ihre Zwischenräume überdeckt, Die einzelnen Segmente 6, 6' und 6 " sowie weitere Segment#e können dafür miteinander nach herkömmlichen bekannten Verfahren verbunden sein.FIG. 1 also indicates that a profile dressing roller also from several different segments 6, 6 ', 6' 'assembled can be, each consisting of a base body on its outside uniformly spaced, uniform projections 3 carries and a gas discharge deposited film of diamond covering the protrusions and their spaces covered, the individual segments 6, 6 'and 6 "and others For this purpose, segments # e can be connected to one another using conventionally known methods be.

Es versteht sich aber, daß sie selbstverständlich auch gleichfrmig beschaffen sein können, um ein beispielsweise zylindrisches Abrichtwerkzeug zu schaffen, das eine Größe aufweist, welche ungeeignet wäre für die Aufnahme in einer Gaskammer zum Auftragen des Diamantfilmes.It goes without saying, however, that they are of course also uniform can be designed to create a cylindrical dressing tool, for example, which is of a size which would be unsuitable for inclusion in a gas chamber for applying the diamond film.

- Ansprüche -- Expectations -

Claims (10)

Ansprüche 1. Verfahren zum Herstellen eines Abrichtwerkzeuges, insbesondere eines rotierenden Abrichtwerkzeuges für Schleifscheiben, mit einem Grundkörper, der als Schneidelemente wirksame Vorsprünge trägt, dadurch gekennzeichnet, daß in die Außenseite des homogenen Grundkörpers Rillen zur Ausbildung von in gleichmäßigem Abstand zueinander stehenden gleichförmigen Vorsprüngen eingearbeitet werden und danach auf die Außenseite mit den Vorsprüngen und Rillen ein Film aus Diamant in einer Stärke von 0,01 bis 5#m durch kathodische Gasentladung aufgedampft wird. Claims 1. A method for producing a dressing tool, in particular a rotating dressing tool for grinding wheels, with a base body, which carries projections effective as cutting elements, characterized in that in the outside of the homogeneous body grooves for the formation of in uniform Spaced uniform projections are incorporated and then put a film of diamond in on the outside with the protrusions and grooves a thickness of 0.01 to 5 # m is vapor deposited by cathodic gas discharge. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die Rillen mechanisch eingearbeitet werden. 2. The method according to claim 1, characterized in that the grooves mechanically incorporated. 3o Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die Rillen chemisch durch anodisches Ätzen des Grundkörpers mittels einer Säure unter Verwendung einer Schablone erzeugt werden0 3o method according to claim 1, characterized in that the grooves chemically by anodic etching of the base body using an acid a template 0 4. Verfahren nach einem oder mehreren der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß nach dem Herstellen der Rillen die Vorsprünge und Rillen mit einer Trägerschicht beschichtet werden und danach der Diamantfilm auf die Trägerschicht aufgedampft wird.4. The method according to one or more of the preceding Claims, characterized in that after the grooves have been produced, the projections and grooves with a Carrier layer are coated and thereafter the diamond film is vapor-deposited onto the carrier layer. 5. Abrichtwerkzeug, insbesondere rotierendes Abrichtwerkzeug für Schleifscheiben, gekennzeichnet durch einen Grundkörper (1), der auf seiner Außenseite im gleichmäßigen Abstand zueinander stehende, gleichförmige Vorsprünge (3) trägt und einen durch kathodische Gasentladung aufgetragenen Film (4) aus Diamant in einer Stärke von 0,01 bis 5#m, der die Vorsprünge (3) und ihre Zwischenräume (2) überdeckt.5. Dressing tool, especially rotating dressing tool for grinding wheels, characterized by a base body (1) which is uniform on its outside Distance to each other, uniform projections (3) carries and one through cathodic gas discharge applied film (4) made of diamond in a thickness of 0.01 to 5 # m, which covers the projections (3) and their spaces (2). 6. Abrichtwerkzeug nach Anspruch 5, dadurch gekennzeichnet, daß die Höhe der Vorsprünge (3) 0,05 bis 1 mm beträgt.6. dressing tool according to claim 5, characterized in that the Height of the projections (3) is 0.05 to 1 mm. 7. Abrichtwerkzeug nach einem oder beiden vorhergehenden Ansprüche, dadurch gekennzeichnet, daß die Vorsprünge (3) einen viereckigen Querschnitt aufweisen.7. Dressing tool according to one or both of the preceding claims, characterized in that the projections (3) have a square cross-section. 8. Abrichtwerkzeug nach einem oder mehreren der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß die Vorsprünge (3) in einem gegenseitigen Abstand von 0,5- 4 mm zueinander stehen.8. dressing tool according to one or more of the preceding claims, characterized in that the projections (3) at a mutual distance of 0.5-4 mm to each other. 9O Abrichtwerkzeug nach einem oder mehreren der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß der Grundkörper (1) mit einer galvanisch ausgetragenen Trägerschicht (5) versehen ist, auf der der Diamantfilm (4) aufgedampft ist.9O dressing tool according to one or more of the preceding claims, characterized in that the base body (1) with a galvanically discharged Carrier layer (5) is provided on which the diamond film (4) is vapor-deposited. 10. Abrichtwerkzeug nach einem oder mehreren der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß das Abrichtwerkzeug aus Segmenten ( 6,6') zusammengesetzt ist, die jeweils aus einem Grundkörper (1) bestehen, der auf seiner Außenseite im gleichmäßigen Abstand zueinander stehende gleichförmige Vorsprünge (3) trägt und einen durch kathodische Gasentladung aufgetragenen Film (4) aus Diamant in einer Stärke von 0,01 bis 5#m, der die Vorsprünge (3) und ihre Zwischenräume (2) überdeckt.10. Dressing tool according to one or more of the preceding claims, characterized in that the dressing tool is composed of segments (6,6 ') is, each of which consists of a base body (1) which is on its outside in uniform spacing from one another standing uniform projections (3) carries and a deposited by cathodic gas discharge film (4) of diamond in a Thickness of 0.01 to 5 # m, which covers the projections (3) and their spaces (2).