DE2426953A1 - Decorative textured plasterboard - having a coating layer of adhesively bonded short textile fibres - Google Patents

Abstract

A decorative, textured plasterboard has a flock layer of short textile fibres firmly bonded to the substrate by an adhesive layer. Flocking may be effected immediately after the plasterboard is mfd. The fibres used for the flocking may be polyamide, polyester, PVC or polyacrylonitrile; and the adhesive may be based on PVAc. Fibres 0.2-5.0, esp. 0.3-4.0 mm long, 2-25 denier, are suitable, and should esp. be of uniform length.

Description

Düsseldorf, den 29.Mai 197'i Henkel&CieGmbHDüsseldorf, May 29, 197'i Henkel & CieGmbH

Henkelstraße 67 PatentabteilungHenkelstrasse 67 patent department

Dr.SchOe/BkDr SchOe / Bk

PatentanmeldungPatent application

und Qebrauchsmusterhilfsanmeldung D and utility model auxiliary application D

Mit dekorativer Schicht versehene Gipskarton-PlattePlasterboard with a decorative layer

Es ist bekannt, daß Gipskarton-Platten nach ihrer Herstellung in weiteren Arbeitsgängen veredelt werden. So können sie mit dekorativen Folien,beispielsweise aus Polyvinylchlorid oder.auch mit Gewebebahnen kaschiert werden. Für die Verklebung der Folien oder dergleichen werden exakt einzuhaltende Bedingungen benötigt. Auch ist die Herstellung von Folien selbst gemessen an der einfachen Herstellung von Gipskarton-Platten recht aufwendig. It is known that plasterboard panels are refined in further operations after their production. So they can be made with decorative foils, for example Polyvinyl chloride or laminated with fabric strips will. Precise conditions that must be adhered to are required for the adhesive bonding of the films or the like. Even The production of foils is quite complex compared to the simple production of plasterboard panels.

Es ist ferner bekannt, die verschiedensten Materialien, insbesondere Folien für Polsterherstellung, das Täschnerhandwerk, Kunstleder, Schuhwaren, Spielzeug, Verpackungsmaterialien, Dichtungsprofile, Schallschluckflächen, Boden- und Wandbelege, elektrostatisch zu beflocken. Bei dem Beflocken von Wandflächen ist es aber erforderlich, daß nach der Fertigstellung bzvr. Vorbereitung der Wand an Ort und Stelle mit einer transportablen Beflockungsanlage gearbeitet wird. Außerdem ist es bei dieser Art des Verfahrens nicht bzw. nur sehr schlecht möglich, Beflockungen aus verschiedenen Sorten von Fasern und insbesondere Beflockungen mit dekorativen Mustern aufzubringen.■It is also known to use a wide variety of materials, in particular foils for upholstery production, the bag-making trade, Artificial leather, footwear, toys, packaging materials, Sealing profiles, sound-absorbing surfaces, floor and wall coverings, to be flocked electrostatically. With the flocking of wall surfaces, however, it is necessary that after completion of the bzvr. Prepare the wall in place and Place is worked with a transportable flocking machine. Plus, it is with this type of procedure not possible or only very poorly possible, flocking from different types of fibers and especially flocking to be applied with decorative patterns. ■

Gegenstand der vorliegenden Neuerung ist eine dekorative Gipskarton-Platte,wobei die Gipskarton-Platte eine Beflockung von kurzgeschnittenen Textilfasern aufweist, die mit der Gipskarton-Platte durch'eine Klebeschicht fest verbunden ist.The subject of the present innovation is a decorative plasterboard panel, the plasterboard panel being flocked of short-cut textile fibers, which is firmly connected to the plasterboard by'eine adhesive layer.

509851/0525509851/0525

24260532426053

Henkel &Cie GmbHHenkel & Cie GmbH

Blatt Z zur Patentanmeldung D 4 9^ 5 J Sheet Z for patent application D 4 9 ^ 5 J PatentabteilungPatent department

Die Gipskarton-Platten, die nach der Neuerung veredelt sein können, werden in bekannter Weise hergestellt. Die Gipskartonplatte.wird durch mindestens zwei Kartonbahnen gebildet, zwischen denen sich eine mehr oder minder dicke Gipsschicht befindet. Unmittelbar nach Fixierung der fertigen Gipskartonplatte können bei Verwendung von wasserhaltigen Dispersionsklebstoffen die Klebeschichten aufgetragen werden. Dies geschieht in bekannter Weise durch Streichen, Spritzen oder mittels Rollen.The plasterboard panels, which will be finished after the innovation can be prepared in a known manner. The plasterboard. Will formed by at least two cardboard sheets, between which there is a more or less thick layer of plaster is located. Immediately after fixing the finished plasterboard, the adhesive layers can be applied when using water-based dispersion adhesives. this happens in a known manner by brushing, spraying or rolling.

Unmittelbar nach dem Auftragen des Klebstoffs soll beflockt werden. Dies geschieht in an sich ebenfalls bekannter Weise, indem beispielsweise über einen Flockbehälter und eine Verteilerbürste die Fasern auf die mit Klebstoff bestrichenen Gipskarton-Platten aufgebracht werden. Die Fasern sollen eine Länge zwischen etwa 0,2 und 5,0 mm, insbesondere 0,3 bis 4,0 mm aufweisen und einen Titer zwischen 2 und 25 den haben. Es hat sieh als vorteilhaft erwiesen, Fasern von einer praktisch einheitlichen Flockenlänge zu verwenden. Fasern aus Polyamiden, wie sie aus Polycaprolactam herstellbar sind, ober Polyesterfasern, beispielsweise aus Polyäthylenglykoltherphthalat, oder auch aus Polyacrylnitril oder PVC, kommen infrage und sind aufgrund ihrer Widerstandsfähigkeit, insbesondere in chemischer Hinsicht, bevorzugt. Selbstverständlich können auch Kunstfasern auf Basis von Polypropylen oder Polycarbonaten eingesetzt werden.Immediately after applying the adhesive, flocking should be carried out. This is done in a manner known per se, for example by applying glue to the fibers using a flock container and a distributor brush Plasterboard panels are applied. The fibers should have a length between about 0.2 and 5.0 mm, in particular 0.3 to 4.0 mm and have a titer between 2 and 25 den. It has proven to be beneficial to fibers from a practical one to use a uniform flake length. Fibers made of polyamides, as can be produced from polycaprolactam, or polyester fibers, For example, from polyethylene glycol therphthalate, or from polyacrylonitrile or PVC, are possible and are preferred because of their resistance, especially from a chemical point of view. Of course, synthetic fibers can also be used based on polypropylene or polycarbonates can be used.

Eine Variation besteht darin, daß man die Beflockung mit verschiedenen Sorten von unterschiedlich gefärbten bzw. 2 oder mehr unterschiedlich langen - aber einheitlich langen - Fasern vornimmt. Dadurch kann man in an sich bekannter Weise einen sogenannten Felleffekt erzielen, wobei das Unterfell aus andersgefärbten Fasern besteht als die Beflockung aus langen Fasern. -Durch Auftragen des Klebstoffs in Mustern und nachfolgendem verschiedenartigem Beflockungs- und Klebeauftrag kann man die verschiedensten Muster erzielen.One variation is that you can use different flocking Varieties of differently colored or 2 or more different lengths - but of the same length - makes fibers. In this way, a so-called fur effect can be achieved in a manner known per se, the undercoat being made of differently colored As flocking, fibers consist of long fibers. -By applying the adhesive in patterns and following Different types of flocking and adhesive application can be used to achieve a wide variety of patterns.

509851/0525509851/0525

2426S532426S53

Henkel &Cie GmbHHenkel & Cie GmbH

Blatt xzur Patentanmeldung D if π 2j c «J Patentabteilung Sheet x to the patent application D if π 2j c «J Patent Department

Die Wahl des Klebstoffs ist nicht kritisch und kann durch einfache Versuche ermittelt werden. Beispielsweise sind geeignet thermoplastische Klebstoffe auf der Basis von Polyvinylacetat bzw. Mischpolymerisaten ^des Polyvinylacetats mit anderen Comonomeren wie Acrylestern oder Yinylestern längerkettiger < Alkohole. Mit gutem Erfolg können auch wäßrige Dispersionen von Polyacrylat-Klebstoffen eingesetzt werden. Die erwähnten wäßrigen Dispersionen sollen gut streichfähig sein und werden zweckmäßig mit einem Gehalt zwischen etwa 45 und 25 % an Thermoplast verwendet.The choice of adhesive is not critical and can be determined by simple experiments. For example, suitable thermoplastic adhesives based on polyvinyl acetate or copolymers ^of polyvinyl acetate with other comonomers such as Acrylestern Yinylestern or longer-chain <alcohols. Aqueous dispersions of polyacrylate adhesives can also be used with good success. The aqueous dispersions mentioned should be easy to spread and are expediently used with a thermoplastic content between about 45 and 25%.

Darüber hinaus können Klebstoffe auf Basis von 2-Komponentenklebern eingesetzt werden. Geeignet sind beispielsweise sogenannte Epoxidharzkleber auf Basis des Diglycidyläthers von Diphenylolpropan. Sie sollen ein Epoxidäquivalent zwischen etwa l80 bis 250 aufweisen und in flüssiger Form vorliegen. Diese Epoxidharze werden zweckmäßig mit bei Raumtemperatur wirksamen Härtungsmitteln verwendet. Dabei handelt es sich in erster Linie um freie Aminogruppen aufweisende Amide polymerisierter Fettsäuren sowie aliphatischen oder cycloaliphatischen Aminen wie etwa Äthylendiamin, Diäthylentriamin, Dicyclohexylamin oder ^,^-Diaminodicyclohexylmethan. Weiterhin können auch Polyurethanklebstoffe als Bindemittel eingesetzt werden. Diese bestehen aus mehrwertigen Isocyanaten und mit Isocyanaten reaktionsfähige OH-Gruppen enthaltende Verbindungen. Es ist auch möglich, freie Isocyanatgruppen enthaltende Voraddukte aus Polyestern oder Polyäthern einzusetzen, bei. denen die in geringer Menge in der Gipskartonplatte oder der Atmosphäre vorhandene Feuchtigkeit als Vernetzungs- bzw. Härtungskomponente wirkt. Die genannten 2-Komponentenkleber können gegebenenfalls ohne Lösungsmittel aufgetragen werden. Es hat sich aber als zweckmäßig .erwiesen, Lösungsmittel, wie Ketone (Aceton, Methyläthylketon) oder Kohlenwasserstoff, wie Toluol oder Xylol zu verwenden. Werden Lösungen von Klebstoffen verwendet, so soll der Anteil an Feststoff etwa zwischen 20 und 50 % liegen.In addition, adhesives based on 2-component adhesives can be used. For example, so-called epoxy resin adhesives based on the diglycidyl ether of diphenylolpropane are suitable. They should have an epoxy equivalent between about 180 to 250 and be in liquid form. These epoxy resins are suitably used with curing agents effective at room temperature. These are primarily amides of polymerized fatty acids containing free amino groups and aliphatic or cycloaliphatic amines such as ethylene diamine, diethylene triamine, dicyclohexylamine or ^, ^ - diaminodicyclohexylmethane. Polyurethane adhesives can also be used as binders. These consist of polyvalent isocyanates and isocyanate-reactive compounds containing OH groups. It is also possible to use pre-adducts of polyesters or polyethers containing free isocyanate groups. where the moisture present in small quantities in the plasterboard or the atmosphere acts as a crosslinking or hardening component. The mentioned 2-component adhesives can optionally be applied without a solvent. However, it has proven expedient to use solvents such as ketones (acetone, methyl ethyl ketone) or hydrocarbons such as toluene or xylene. If solutions of adhesives are used, the proportion of solids should be between 20 and 50 % .

509851/0525509851/0525

Henke! &Cie GmbHHang! & Cie GmbH

Blatt Jf zur Patentanmeldung D 1} 9 4 ^ £· Patentabteilung Sheet Jf to patent application D 1} 9 4 ^ £ · Patent Department

Selbstverständlich können den Bindern auch in bekannter Weise Farbstoffe wie Phthalocyaninfarbstoffe oder Pigmente wie Titandioxid,, Eisenoxids Kreide, Bleichromat und dgl» zugesetzt werden»Of course, dyes such as phthalocyanine dyes or pigments such as titanium dioxide can also be added to the binders in a known manner. Iron oxide chalk, lead chromate and the like »are added»

Hinsichtlich des elektrostatischen Beflockungsverfahrens hat es sich häufig als zweckmäßig erwiesen, wenn die Binder noch Zusätze enthalten, die die Leitfähigkeit verbessern. Hier können etwa sulfatierte Fettamine, wobei die Kettenlänge des Fettsäureesters etwa zwischen 12 und 22 Kohlenstoffatomen liegt, oder auch quaternäre Ammoniumverbindungen₉ wie etwa Benzyltetramethylammoniumchlorid, eingesetzt werden.With regard to the electrostatic flocking process, it has often proven to be useful if the binders also contain additives that improve conductivity. Sulphated fatty amines, for example, the chain length of the fatty acid _{ester being between 12 and 22 carbon atoms, or quaternary ammonium compounds 9} such as benzyltetramethylammonium chloride, for example, can be used here.

Zur Verbesserung des Verlaufs der Binder können gegebenenfalls auch übliche von der Lackherstellung bekannte Verlaufsmittel zugefügt werden. Geeignet ist beispielsweise Silikonöl in einer Menge von etwa O₃OO5 bis 0,02 % oder auch höhere Alkohole oder Terpenkohlenwasserstoffe sowie OH-Gruppen enthaltendes Polyvinylchlorid. In diesen Fällen können die Zusätze etwas höher sein und bewegen sich zwischen "etwa 0,05 bis 1 Jf, bezogen auf die Gesamtmenge des Binders.To improve the leveling of the binders, customary leveling agents known from paint production can optionally also be added. For example, silicone oil in an amount of about O ₃ OO5 to 0.02 % or higher alcohols or terpene hydrocarbons and polyvinyl chloride containing OH groups is suitable. In these cases the additions can be somewhat higher and range between "about 0.05 to 1 Jf, based on the total amount of the binder.

Das Aufbringen des Flockmaterials auf die äußere Oberfläche bzw. die Oberflächenteile der Gipskartonplatte erfolgt nach bekannten Verfahren unter Verwendung eines elektrischen Feldes, welches die Ausrichtung und Beschleunigung der Flocken bewirkt (siehe Ullmanns Encyklopädie, Band 11, i960, Seite 93). Selbstverständlich kann auch einfacher durch Ausnutzung der Schwerkraft verfahren werden, indem das Flockmaterial lediglich auf der vorher mit dem erfindungsgemäß zu verwendenden Binder bestrichenen Fläche aufgestreut wird. Allerdings eignet sich dieses Verfahren praktisch nur bei gemahlenem Flockmaterial, wobei die Ausrichtung der Flocken auf der Oberfläche keine Rolle spielt. Bei Flocken von gewisser Länge, welche bis zu einigen Millimetern betragen kann, bewirkt die Anwendung eines hochgespannten elektrischen Feldes deren Parallelstellung senkrecht zur beflockten Plattenschicht. The application of the flock material to the outer surface or the surface parts of the plasterboard is carried out according to known methods using an electric field, which brings about the alignment and acceleration of the flakes (see Ullmanns Encyklopadie, Volume 11, 1960, page 93). Of course, it is also possible to proceed more simply by utilizing the force of gravity, in that the flock material is merely sprinkled on the surface previously coated with the binder to be used according to the invention. However, this method is practically only suitable for ground flock material, whereby the orientation of the flocks on the surface is irrelevant. In the case of flakes of a certain length, which can be up to a few millimeters, the application of a high-tension electrical field causes them to be positioned parallel to the flocked sheet layer.

- 509851/0525- 509851/0525

Henkel &Cie GmbHHenkel & Cie GmbH

Blatt |f zur Patentanmeldung D 49^5 ζ PatentabteilungSheet | f to the patent application D 49 ^ 5 ζ Patent Department

Nach dem Aufbringen des Flockmaterials auf den Binder werden dann eventuell nicht befestigte Flocken pneumatisch abgesaugt.After the flock material has been applied to the binder, any flakes that may not be attached are then pneumatically sucked off.

Im allgemeinen wird man nur eine Fläche der Gipskartonplatte mit einer Beflockung versehen. Es besteht aber auch die Möglichkeit, die andere Fläche in einem weiteren Arbeitsgang zu beflocken. Generally one will only get one face of the plasterboard provided with a flocking. But there is also the possibility of flocking the other surface in a further work step.

In der beiliegenden Skizze bedeutet Abbildung 1 einen Schnitt durch eine beflockte Gipskarton-Platte, wobei A und A¹ die Kartonlage darstellt, während B die Gipsbeschichtung und D die durch den Klebstoff (C) gehaltene Beflockung darstellt. Die Abbildung 2 stellt die Aufsicht auf eine beflockte Gipskarton-Platte dar, wobei D und D¹ Beflockungen verschiedener Art darstellen, während C einen unbeflockten Anteil des erhärteten Klebers bedeutet.In the accompanying sketch, Figure 1 means a section through a flocked plasterboard panel, where A and A ^{1 represent} the cardboard layer, while B represents the plaster coating and D represents the flocking held by the adhesive (C). Figure 2 shows a top view of a flocked plasterboard panel, with D and D ^{1 representing} different types of flocking, while C means an unblocked portion of the hardened adhesive.

50985 1/052550985 1/0525

Claims (6)

Henke! &Cie GmbHHang! & Cie GmbH Blatt if zur Patentanmeldung D 49II5 £ PatentabteilungSheet if for patent application D 49II5 £ Patent Department PatentansprücheClaims l; Mit dekorativer Schicht versehene Gipskarton-Platte, dadurch gekennzeichnet, daß die dekorative Schicht aus einer Beflockung von kurzgeschnittenen Textilfasern besteht, die mit der Gipskarton-Platte durch eine Klebeschicht fest verbunden ist.l; Plasterboard panel provided with a decorative layer, thereby characterized in that the decorative layer consists of a flocking of short-cut textile fibers, which with the plasterboard is firmly connected by an adhesive layer. 2. Mit dekorativer Schicht versehene Glpskarton-Platte nach Patentanspruch 1, dadurch gekennzeichnet, daß die Beflockung mit kurz geschnittenen Textilfasern unmittelbar nach Herstellung der Gipskarton-Platte erfolgte.2. Glps cardboard panel provided with a decorative layer after Patent claim 1, characterized in that the flocking with short-cut textile fibers immediately after production the plasterboard was made. 3. Mit dekorativer Schicht versehene Gipskarton-Platte nach Patentanspruch 1 und 2, dadurch gekennzeichnet, daß Pasern eine Länge zwischen 0,2 und 5,0 mm, insbesondere 0,3 bis 4,0 mm, aufweisen und einen Titer zwischen 2 und 25 den haben. -3. With a decorative layer provided plasterboard according to claim 1 and 2, characterized in that Pasern a length between 0.2 and 5.0 mm, in particular 0.3 to 4.0 mm, and a titer between 2 and 25 den to have. - 4. Mit dekorativer Schicht versehene Gipskarton-Platte nach Patentanspruch 1 bis 3_S dadurch gekennzeichnet, daß die Beflockung von Fasern einer praktisch einheitlichen Flockenlänge besteht.4. With a decorative layer provided plasterboard according to claim 1 to 3 _S, characterized in that the flocking of fibers consists of a practically uniform flake length. 5. Mit dekorativer Schicht versehene Gipskarton-Platte nach Patentanspruch 1 bis 4, dadurch gekennzeichnet, daß die Beflockung aus Fasern aus Polyamid, Polyestern oder PVC oder Polyacrylnitril bestehen.5. With a decorative layer provided plasterboard according to claim 1 to 4, characterized in that the Flocking consists of fibers made of polyamide, polyester or PVC or polyacrylonitrile. 6. Mit dekorativer Schicht versehene Gipskarton-Platte nach Patentanspruch 1 bis 5, dadurch gekennzeichnet, daß die Beflockung aus verschiedenen Sorten von unterschiedlich gefärbten bzw. unterschiedlich langen aber einheitlich langen Fasern besteht.6. With a decorative layer provided plasterboard according to claim 1 to 5, characterized in that the Flocking from different types of different colored or different lengths but uniform long fibers. -509851/0525-509851/0525 HenkeT&CieGmbHHenkeT & CieGmbH Blatt % zur Patentanmeldung D 49^5 2 ' PatentabteilungSheet % to the patent application D 49 ^ 5 2 ' patent department Mit dekorativer Schicht versehene Gipskarton-Platte nach Patentanspruch i bis 6, dadurch gekennzeichnet, daß die Beflockung in Form von Mustern und gegebenenfalls verschiedenartigen Flocken (D, DM₅ wobei gegebenenfalls Teile zwischen den beflockten Flächen mit einer erhärteten Klebe- bzw. Kunststoffschicht (C) versehen sind.Plasterboard panel provided with a decorative layer according to patent claims i to 6, characterized in that the flocking in the form of patterns and optionally different types of flakes (D, DM _5, with parts between the flocked surfaces with a hardened adhesive or plastic layer (C) are provided. 50985 1/052550985 1/0525 LeerseiteBlank page