DE2359011A1 - COOL AND TEMPERED LOW-ALLOY STEEL - Google Patents

COOL AND TEMPERED LOW-ALLOY STEEL

Info

Publication number
DE2359011A1
DE2359011A1 DE19732359011 DE2359011A DE2359011A1 DE 2359011 A1 DE2359011 A1 DE 2359011A1 DE 19732359011 DE19732359011 DE 19732359011 DE 2359011 A DE2359011 A DE 2359011A DE 2359011 A1 DE2359011 A1 DE 2359011A1
Authority
DE
Germany
Prior art keywords
max
low
alloy steel
molybdenum
manganese
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19732359011
Other languages
German (de)
Other versions
DE2359011B2 (en
Inventor
William C Clark
Richard C Ottobre
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Babcock and Wilcox Co
Original Assignee
Babcock and Wilcox Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Babcock and Wilcox Co filed Critical Babcock and Wilcox Co
Publication of DE2359011A1 publication Critical patent/DE2359011A1/en
Publication of DE2359011B2 publication Critical patent/DE2359011B2/en
Withdrawn legal-status Critical Current

Description

PATENTANWALTPATENT ADVOCATE

26. Ιόν. 1973 Anw.-Akte: 27.6226. Ιόν. 1973 Application files: 27.62

PATEIf ΑΪΙΕΙΒϋΗPATEIf ΑΪΙΕΙΒϋΗ

Anmelder: The Babcock & Wilcox Company, Applicant: The Babcock & Wilcox Company,

161 East 42nd Street, lew York, I.Y. 10017-161 East 42nd Street, lew York, I.Y. 10017-

USA -UNITED STATES -

Titel; Abgeschreckter und angelassener niedriglegierter Stahl Title; Quenched and tempered low alloy steel

Die Erfindung betrifft niedriglegierte Stähle, die auf hohe Streckfestigkeit und Zerreißfestigkeit abgeschreckt und angelassen werden können und gleichzeitig dabei auch eine im wesentlichen gleichmäßige Härtbarkeit im gesamten Querschnitt aufweisen.The invention relates to low-alloy steels which are quenched for high yield strength and tensile strength and can be tempered and at the same time also a substantially uniform hardenability throughout Have cross-section.

Seit einiger Zeit besteht für verschiedene Verwendungszwecke Bedarf an niedriglegierten Stählen mit einem Minimum an teuren Legierungsbestandteilen, die durch Y/ärmebehandlung auf Streckfestigkeiten im Bereich von 6 000 bis 11 000 kg/cm gebracht werden können und dabei im wesentlichen gleichmäßige Härtbarkeitsmerkmale haben.For some time there has been a need for low alloy steels with a minimum for various uses of expensive alloy components produced by Y / heat treatment can be brought to tensile strengths in the range of 6,000 to 11,000 kg / cm and thereby im have substantial uniform hardenability characteristics.

- 2 409836/0692 - 2 409836/0692

Die Erfindung offenbart einen niedriglegierten Stahl, der auf mittlere, Zwischen- und hohe Festigkeitseigenschaften abgeschreckt und angelassen oder normalgeglüht und angelassen werden kann. Diese Stahllegierung kann nach Abschrecken angelassen werden zu beschränkten Streckfestigkeit sbereichen mit den verschiedenen Zugfestigkeitswerten wie in der nachstehenden Tabelle angegeben:The invention discloses a low alloy steel that has medium, intermediate and high strength properties quenched and tempered or normalized and tempered can be. This steel alloy can be tempered after quenching to a limited yield strength ranges with the different tensile strength values as indicated in the table below:

Typische Eigenschaften in begrenzten ZugfestigkeitsbereichenTypical properties in limited tensile strength ranges

99

Streckfestigkeit (kg/cm) Zugfestigkeit (kg/cm )Tensile strength (kg / cm) tensile strength (kg / cm) Min. Max. Min. Max.Min. Max. Min. Max.

(Miiilere Festigkeitsbereiche)(Multiple strength ranges)

5625 6679 66795625 6679 6679

5976 7030 70305976 7030 7030

6327 7382 73826327 7382 7382

6679 7733 77336679 7733 7733

(Zwischen-Festigkeitsbereiche) ( Intermediate strength ranges)

7030 8437 8437 9491 7733 9140 9140 10194 8437 9443 9443 108977030 8437 8437 9491 7733 9140 9140 10194 8437 9443 9443 10897

(Hohe Festigkeitsbereiche) ( High strength ranges)

9140 10546 - 112499140 10546 - 11249

9491 10897 - 116009491 10897-11600

- 3 409836/0692 - 3 409836/0692

23Η9Π1123Η9Π11

-D--D-

Außerdem ergibt, wenn notwendig, der erfindungsgemäße legierte Stahl gute Kerbschlagzähigkeitseigenschaften nach Charpy "bei Temperaturen unter Null bei den mittleren Festigkeitswerten. -Bei den Zwischen- und hohen Festigkeitswerten sind die Kerbschlagzähigkeitswerte nach Gharpy angemessen für Anforderungen, die normalerweise bei Umgebungstemperaturen gestellt werden. lach dem Abschrecken zeigt diese Legierung auch eine ausgezeichnete Reaktion auf Wärmebehandlung für Anforderungen wie z. B. kontrollierte maximale Härte und Feingefüge in Verbindung mit relativ großen Dicken bis zu und einschließlich ca 5 cm.In addition, if necessary, the alloy of the present invention can be obtained Steel has good Charpy impact strength properties at subzero temperatures in the middle Strength values. -At the intermediate and high strength values Gharpy impact strength values are appropriate for requirements normally encountered at ambient temperatures be asked. After quenching, this alloy also shows an excellent response on heat treatment for requirements such as B. controlled maximum hardness and fine structure in connection with relative large thicknesses up to and including approx. 5 cm.

Die Erfindung eignet sieh besonders zur Anwendung bei der Herstellung von dickwandigen, miteinander verbundenen Grlattrohrprodukten«, bei denen genau kontrollierte Eigenschaften und gleichmäßiges Feingefüge im ganzen Querschnitt erforderlich sind» Es sind zo B. in den mittleren und ZwischenfestigkeitsbereiciieH Ölbohrrohrleitungen sowohl mit glatten als auch mit gestauchten Bnden raid in verschiedenen (xrößenkombinationen hergestellt worden,, Ein einzigartiges Merkmal dieser Legierung ist ihre Fähigkeit, ein gleichmäßiges abgeschrecktes Feingefüge in verhältnismäßig starken Rohrquerschnitten durch Abschrecken des Außendurchmessers mit Wassersprühung zu ergeben. Mit dieser Legierung können bei Behälter-Abschrecken hohe Festigkeitswerte erzielt werden, die für die Anwendung bei Rohren für hohe Drücke und hohe Festigkeitsanforderungen geeignet sind.The invention look is particularly suitable for use in the production of thick-walled, interconnected Grlattrohrprodukten "in which precisely controlled properties and uniform microstructure throughout the cross-section required" There are, o as in the middle and ZwischenfestigkeitsbereiciieH Ölbohrrohrleitungen both with smooth and with upset bands raid in various combinations of sizes. A unique feature of this alloy is its ability to produce a uniform quenched fine structure in relatively thick pipe cross-sections by quenching the outer diameter with water spray. With this alloy, high strength values can be achieved in container quenching, which are suitable for use in pipes for high pressures and high strength requirements.

409838/0692409838/0692

ORIGINAL INSPECTEDORIGINAL INSPECTED

Die Erfindung und die damit verbundenen Grundsätze sind auch bei der Herstellung und l/ärmebehandlung von Schmiedestücken und Fittings sowie von Merkstoffen, aus denen diese hergestellt werden, anwendbar.The invention and the principles associated with it apply to the manufacture and heat treatment of forgings and fittings as well as memory materials from which they are made, can be used.

Der Bereich der chemischen Zusammensetzung, den die Erfindung umfaßt, ist wie folgt:The range of chemical composition covered by the invention is as follows:

Bereich der ehem. Zusammen- Beispiele bevorzugter Setzung in Gewichtsprozent Ziele Range of the former. Examples of preferred setting in percent by weight goals

0,15 -0.15 - 0,400.40 Bevorzugter BereichPreferred area - 0,26- 0.26 0,150.15 - 0,30- 0.30 1 - Bereich 21 - area 2 Kohlenstoffcarbon 1,10 -1.10 - 1,901.90 0,200.20 - 1,60- 1.60 0,00050.0005 Min.Min. 0,30 - 0,360.30-0.36 Manganmanganese 0,0600.060 Max.Max. 1,301.30 —- EestEest 1,40 - 1,701.40 - 1.70 Schwefel **Sulfur ** 0,0400.040 Max.Max. —- -- Phosphor **Phosphorus ** 0,10 -0.10 - 1,001.00 - 0,35- 0.35 —- Siliziumsilicon 0,00 -0.00 - 1,101.10 0,200.20 - 0,60- 0.60 0,20 - 0,350.20-0.35 Chrom *Chrome * 0,250.25 Max.Max. 0,400.40 niedriglow -- Nickelnickel 0,10 -0.10 - 0,750.75 niedriglow Molybdän *Molybdenum * 0,00050.0005 Min.Min. 0,45 - 0,550.45-0.55 Borboron Restrest 0,0005 Min.0.0005 min. Eiseniron Restrest

* Einer der wichtigsten Grundzüge dieser erfindungsgemäßen Zusammensetzung betrifft das Gleichgewicht zwischen dem Chrom und den Molybdän, Wenn z. Be das Chrom, ein Minimum von gleichmäßig 0 ?° ist, müßte das Molybdän 0,40 - 0,60* One of the most important features of this composition according to the invention relates to the balance between the chromium and the molybdenum. If the chromium is a minimum of uniformly 0 ? ° , the molybdenum should be 0.40-0.60

409836/0692409836/0692

sein. In gleicher Weise müßte das Chrom, wenn das Molybdän ein Minimum von gleichmäßig 0,10 ;* ist, 0,50 0,70 ^ sein.be. In the same way, the chromium would have to be, if the molybdenum is a minimum of uniformly 0.10; *, 0.50 0.70 ^ be.

** Schwefel und Phosphor können auch maximal je 0,025 "betragen, wie es im allgemeinen für Elektrostähle vorgeschrieben ist. .** Sulfur and phosphorus can also be a maximum of 0.025 "each, as is generally prescribed for electrical steels. .

Die genaue bevorzugte Analyse hängt von einer Anzahl von Faktoren ab wie z. B. dem gewünschten Festigkeitswert, dem Grad der Begrenzung der Eigenschaften, der Bohrgröße und besonders der erforderlichen landdicke, sowie von den Wärmebehandlungseinrichtungens die beim Absohrecken und Anlassen verwendet werden sollen. Diese niedriglegierten Schmelzen können je nach Grad und Tiefe der erforderlichen Härtbarkeit mit einem Zusatz von Bor hergestellt werden, der je nach diesen Faktoren auch wegfallen kann0 Andere Zusätze wie zc B4, Kalzium können ebenfalls verwendet werden, um die Schlagbiegeeigenschaften und/oder die Bearbeitbarkeit zu verbessern.The exact preferred analysis will depend on a number of factors such as: B. the desired strength value, the degree of limitation of the properties, the drilling size and especially the required land thickness, as well as the heat treatment equipment s to be used during suction cornering and tempering. These low-melting may be prepared with an addition of boron, which can also be omitted, depending on these factors depending on the degree and depth of the required hardenability 0 Other additives such as c B 4, calcium can also be used to measure the impact characteristics and / or the Improve machinability.

Die Bereiche der mittleren Festigkeitswerte können zusätzlich zu den begrenzten Streckfestigkeitswerten maximale Härtewerte haben, z« B. maxc Rockwellhärte C 22 bei Streckfestigkeiten bis zu 7 000 kg/cm , Die kontrollierten mittleren Härtewerte von Viertelbogen zu Viertelbogen rundThe ranges of the mean strength values can have maximum hardness values in addition to the limited yield strength values, e.g. max c Rockwell hardness C 22 with tensile strengths of up to 7,000 kg / cm, the controlled mean hardness values from quarter arch to quarter arch round

409836/0692409836/0692

um den Rohrquerschnitt und in der ganzen Wanddicke können zusätzlich vorgeschrieben sein. Bei bestimmten umgebungsabhängigen Anwendungen sind gute Kerbzähigkeitswerte nach Charpy bei Temperaturen unter lull erzielbar· Diese Legierung verspricht zufriedenstellende Eigenschaften bei niedrigen Temperaturen, wie sie z, B. in arktischen Gebieten auftreten. Bei diesen kontrollierten mittleren Festigkeit swerten hat sicL· dieser Stahl unter Laboratoriumsversuchsbedingungen als spannungsrißkorrosionsfest in Schwefelwasserstoffumgebung erwiesen.around the pipe cross-section and in the entire wall thickness must also be prescribed. In certain environment-dependent applications, good notch toughness values are achieved Charpy achievable at temperatures below lull · This alloy promises satisfactory properties at low temperatures such as those found in arctic regions appear. With these controlled mean strength values, sicL · this steel has under laboratory test conditions proven to be stress corrosion cracking resistant in a hydrogen sulfide environment.

Zusätzlich zu den kontrollierten Festigkeitseigenschaften bei Zwischen- und hohen Festigkeitswerten läßt sich bei Umgebungstemperatur angemessene Kerbschlagsähigkeit nach Gharpy nachweisen, die den üblicherweise bei diesen Festigkeitswerten gestellten Betriebsanforderungen sowie den Druckanforderungen entsprechen.In addition to the controlled strength properties at intermediate and high strength values, Ambient temperature, provide evidence of Gharpy impact strength that is appropriate to the normal for these strength values the operational requirements as well as the printing requirements.

Bei allen Festigkeitswerten ergibt eine Kombination der gewählten chemischen Zielzusammensetzung, des Abschreckmediums und des Abschreckverfahrens und des richtigen Anlassens ein ausgezeichnetes Ansprechen auf Wärmebehandlung. Bei diesen äußerst gut gesteuerten Bedingungen ergeben die gewählten chemischen Zielsusamniensetzungen begrenzte Bereiche der Eigenschaften und damit zu vereinbarende Verhältnisse ζγ/lschen Streokfestigkeit und Zugfestigkeit und maximale Härte innerhalb gesteuerter Begrenzungen sowie ein gleichmäßigea Feingefüge im Quer-For all strength values, a combination of the selected chemical target composition results in the quenching medium and quenching method and proper tempering, excellent heat treatment response. Under these extremely well controlled conditions, the target chemical compositions chosen result in limited ones Ranges of properties and the ratios to be reconciled with ζγ / lschen resistance to stress and tensile strength and maximum hardness within controlled limits as well as a uniforma fine structure in the transverse

- 7 409836/0692 - 7 409836/0692

schnitt des Produktes· Der Bereich des Legierungsgehaltes, je nach Erfordernis mit oder ohne Bor, ist die Grundlage der ausgezeichneten Eigenschaften in Bezug auf Absehrekken, Tief-Härten und gesteuertes Anlassen,cut of the product the range of alloy content, with or without boron, depending on the requirements, is the basis of the excellent properties in relation to remote corners, Deep hardening and controlled tempering,

Die in der nachstehenden Tabelle aufgeführten Daten zeigen typische Ergebnisse bei einem Produktionsauftrag für Ölbohr-Eohre, die an beiden Enden gestaucht sinde The data listed in the table below shows typical results for a production order for oil well pipes that are upset at both ends e

Datenprotokoll eines Produktionsauftrages für Eohre für ÖlbohrungenData log of a production order for Eohre for Oil drilling

Rohrkörpergröße 3 1/2 " ä. 0 χ 0,254" Wand Stauchendengröße 4,070" ä, 0 χ 0,643 fand χ 2,785" i« 0 Pipe body size 3 1/2 "ä. 0 χ 0.254" wall upsetting size 4.070 "ä, 0 χ 0.643 found χ 2.785" i « 0

Schmelze Nr.Melt no. 37742 (75 t)37742 (75 t) 37743 (75 t)37743 (75 t) Kohlenstoffcarbon 0f210 f 21 0,240.24 Manganmanganese 1,411.41 1,481.48 Schwefelsulfur 0,0220.022 0?0120 ? 012 Phosphorphosphorus 0,0190.019 0?0150 ? 015 Siliziumsilicon 0,160.16 0,260.26 Chromchrome 0,570.57 0,500.50 Nickelnickel 0,160.16 0,090.09 Molybdänmolybdenum 0,230.23 0,240.24 Borboron 0,00150.0015 0,00120.0012

409836/0692409836/0692

(Zug-)(Train-)

Festigkeits- Körper Stauchende Körper Stauch-Strength Body Compression Body Compression

Ergebnisse endeResults end

Zerreißfestigkeit 107929 105834 106030 105329 104983 109390Tensile strength 107929 105834 106030 105329 104983 109390

StreckgrenzeStretch limit

(0t2fo Dehnung) 94126 93153 89246 88838 88534 92907 (0 t 2fo expansion) 94126 93153 89246 88838 88534 92907

Dehnung in 2" 21# 24£ 24# 23# 26/»Stretch in 2 "21 # 24 lbs 24 # 23 # 26 /»

HärtebereiohHardness range

Bockwell "C" 18-20 19-20 19-20 18-19 18-20 18-20Bockwell "C" 18-20 19-20 19-20 18-19 18-20 18-20

Wärmebehandlung Außendurchmesser Wassersprüh-algschrecktHeat treatment outside diameter water spray algae quench

von 1650° Ffrom 1650 ° F

Anlassen ' 1300° F eine Stunde bei der Temperatur Tempering '1300 ° F one hour at temperature

Letztes Spannungsfreiglühen nach rotierendem Eichten 1050° F dreißig Minuten mindestens bei Temperatur Last stress relief anneal after rotating calibration 1050 ° F for thirty minutes at least at temperature

Bei dem beschriebenen legierten Stahl ist das richtige Gleichgewichtsverhältnis zwischen Mangan, Chrom und Molybdän von Bedeutung, um Tief-Härtbarkeit zu erzielen«, Wie zu ersehen ist, wird vorzugsweise Bor zugesetzt, um die gewünschten Merkmale zu erzielen; es wurde jedoch festgestellt, daß eine minimale Menge eines Borzusatzes in dünnen Querschnitten nicht erforderlich ist, um die gewünschten Eigenschaften zu erhalten,, Zum Beispiel kann bei der Herstellung von Rohren von einer Wanddicke von maximal 1/4 Zoll das BorThe alloy steel described is the right one Equilibrium ratio between manganese, chromium and molybdenum important to achieve deep hardenability «, How to As can be seen, boron is preferably added to achieve the desired characteristics; however, it was found that a minimal amount of a boron additive in thin cross-sections is not required to achieve the desired properties For example, when manufacturing pipes with a wall thickness of 1/4 inch or less, the boron

- 9 409836/0692 - 9 409836/0692

weggelassen werden. Es ist auch festgestellt worden, daß der Zusatz von mehr als etwa 0,003 Gewichtsprozent Bor zu der chemischen Zusammensetzung selbst bei Produkten mit dickem Querschnitt, d. h. 2" Rohrwand, unnötig ist·can be omitted. It has also been found that the addition of greater than about 0.003 weight percent boron to the chemical makeup of even products with a thick cross-section, d. H. 2 "pipe wall, is unnecessary

Bei der Herstellung des beschriebenen legierten Stahles wird das Bor in der Pfanne durch Zusatz von G-rainal (Warenzeichen) oder von Ferrobor zugegeben,, Damit das Bor wirksam ist, muß das gelöste Op und Up in der Schmelze auf ein Minimum reduziert sein, da ja Bor eine Affinität zu beiden hat, G-rainal enthält kleine Mengen von sowohl Ti als auch Al, Es wurde auch festgestellt, daß innerhalb der Grenzen der angegebenen Analyse eine Verringerung des Molybdäns in der Legierung eine Vergrößerung der Chrommenge erfordert^ damit die gewünschten Härtbarkeitseigenschaften erhalten bleiben, und umgekehrt.In the production of the alloyed steel described, the boron is added to the pan by adding G-rainal (trademark) or added by ferroboron, so that the boron is effective, the dissolved Op and Up must be in the melt must be reduced to a minimum, since boron has an affinity for both, G-rainal contains small amounts of both Ti as well as Al, It was also found that, within the limits of the stated analysis, a reduction in Molybdenum in the alloy requires an increase in the amount of chromium, thus achieving the desired hardenability properties are preserved and vice versa.

Mit der beschriebenen Legierung kann Härtbarkeit erzielt werden durch Sprüh- oder Behälter-Abschrecken mit Wasser, oder durch Abschrecken mit Öl oder sogar Abschrecken mit Luft wie beim Normalisieren,Hardenability can be achieved with the alloy described are made by spray or container quenching with water, or by quenching with oil or even quenching with Air like normalization,

- 10 -- 10 -

409 8 3 6/0692409 8 3 6/0692

Claims (1)

- ίο -- ίο - PATENTANSPRÜCHE :PATENT CLAIMS: Abgeschreckter und angelassener niedriglegierter Stahl, der eine Mindest-Streckfestigkeit von 5 625 kg/cm hat und durch eine im wesentlichen gleichmäßige Härtbarkeit in Querschnittsdicken von bis zu cao zwei Zoll ausgezeichnet ist, gekennzeichnet durch folgende Zusammensetzung - nach Gewichtsprozent - : Kohlenstoff: etwa 0,15 bis 0,40Quenched and tempered low-alloy steel, which has a minimum yield strength of 5 625 kg / cm and is characterized by an essentially uniform hardenability in cross-section thicknesses of up to about o two inches, characterized by the following composition - by weight percent -: Carbon: about 0 , 15 to 0.40 Mangan: etwa 1,10 bis 1,90Manganese: about 1.10 to 1.90 Schwefel: max. 0,060Sulfur: 0.060 max Phosphor: max. 0,040Phosphorus: 0.040 or less Silizium: etwa 0,10 bis 1,00Silicon: about 0.10 to 1.00 Chrom: etwa 0,00 bis 1,10Chromium: about 0.00 to 1.10 Nickel: max. 0,25Nickel: max. 0.25 Molybdän: etwa 0,10 bis 0,75Molybdenum: about 0.10 to 0.75 Bor: min. 0,0005Boron: min.0.0005 Se st Eisen und restliche Verunreinigungen.Se st iron and residual impurities. Abgeschreckter und angelassener niedriglegierter Stahl nach Anspruch 1, gekennzeichnet durch folgende Zusammensetzung - nach Grewichtsprozent -:Quenched and tempered low-alloy steel according to claim 1, characterized by following composition - according to weight percent -: Kohlenstoff: etwa 0,20 bis 0,26Carbon: about 0.20 to 0.26 Mangan: etwa 1,30 bis 1,60Manganese: about 1.30 to 1.60 Schwefel: max. 0,060Sulfur: 0.060 max Phosphor: max. 0,040Phosphorus: 0.040 or less Silizium: etwa 0,20 bis 0,35Silicon: about 0.20 to 0.35 Chrom: etwa 0,40 bis 0,60Chromium: about 0.40 to 0.60 409836/0692 - 11 -409836/0692 - 11 - Hickel: niedrigHickel: low Molybdän: etwa 0,15 bis 0,30 Bor: min. 0,0005Molybdenum: about 0.15 to 0.30 Boron: at least 0.0005 mit dem Best Eisen und Restverunreinigungen.with the best iron and residual impurities. Abgeschreckter und angelassener niedriglegierter Stahl nach Anspruch 1, gekenn ze ichne t durch folgende Zusammensetzung - nach Gewichtsprozent - :Quenched and tempered low alloy steel according to claim 1, characterized by the following composition - by weight percent -: Kohlenstoff:Carbon: etwa 0,30 bisabout 0.30 to 0,360.36 Mangan:Manganese: etwa -1,40 bisabout -1.40 to 1,701.70 Schwefel:Sulfur: max« 0,060 .max «0.060. Phosphor:Phosphorus: max. 0,040max. 0.040 Silizium:Silicon: etwa 0,20 bisabout 0.20 to 0,350.35 Chrom:Chrome: —_—_ Mckel:Mckel: niedriglow Molybdän:Molybdenum: etwa 0,45 bisabout 0.45 to 0s550 s 55 Bor:Boron: min. On0005min. O n 0005
mit dem Best als Eisen und Restverunreinigungen«with the best as iron and residual impurities « Abgeschreckter und angelassener niedriglegierter Stahl,Quenched and tempered low alloy steel, ο der eine Mndest-Streokfestigkeit von 5 625 kg/cm hat und durch eine im wesentlichen gleichmäßige Härtbarkeit in Querschnittsdicken von maximal 1/4 Zoll ausgezeichnet istj, gekennzeichnet durch folgende Zusammensetzung - nach Gewichtsprozent - : Kohlenstoff: etwa 0,15 bis 0,40ο the minimum stress resistance of 5 625 kg / cm and is characterized by a substantially uniform hardenability in cross-section thicknesses of a maximum of 1/4 inch istj, characterized by the following composition - by weight percent -: carbon: about 0.15 to 0.40 - 12 -- 12 - 409836/0692409836/0692 Mangan: etwa 1,10 bis 1,90Manganese: about 1.10 to 1.90 Schwefel: max. 0,060Sulfur: 0.060 max Phosphor: max. 0,040Phosphorus: 0.040 or less Silizium: etwa 0,10 bis 1,00Silicon: about 0.10 to 1.00 Chrom: " etwa 0,10 bis 1,10Chromium: "about 0.10 to 1.10 Nickel: max. 0,25Nickel: max. 0.25 Molybdän etwa 0,10 bis 0,75Molybdenum about 0.10 to 0.75 .mit dem Rest als Eisen und Restverunreinigungen..with the remainder as iron and residual impurities. 5. Abgeschreckter und angelassener niedriglegierter Stahl nach Anspruch 4, gekennzeichnet durch folgende Zusammensetzung - nach Gewichtsprozent - : Kohlenstoff: etwa 0,20 bis 0,26 -5. Quenched and tempered low-alloy steel according to claim 4, characterized by the following composition - by weight percent -: carbon: about 0.20 to 0.26 - Mangan: etwa 1,30 bis 1,60Manganese: about 1.30 to 1.60 Schwefel: . max. 0,060Sulfur:. max. 0.060 Phosphor: max. 0,040Phosphorus: 0.040 or less Silizium: etwa 0,20 bis 0,35Silicon: about 0.20 to 0.35 Chrom: etwa 0,40 bis 0,60Chromium: about 0.40 to 0.60 Nickel: niedrigNickel: low Molybdän: · etwa 0,50 bis 0,30Molybdenum: about 0.50 to 0.30 mit dem Rest als Eisen und Restverunreinigungen.with the rest as iron and residual impurities. 6. Abgeschreckter und angelassener niedriglegierter Stahl nach Anspruch 4, gekennzeichnet durch folgende Zusammensetzung - nach Gewichtsprozent -: Kohlenstoff: etwa 0,30 bis 0,366. Quenched and tempered low-alloy steel according to claim 4, characterized by the following composition - by weight percent -: carbon: about 0.30 to 0.36 Mangan: etwa 1,40 bis 1,70Manganese: about 1.40 to 1.70 -- 409836/0692409836/0692 Schwefel: max. 0,060Sulfur: 0.060 max Phosphor: max. 0,040Phosphorus: 0.040 or less Silizium: etwa 0,20 bis O935Silicon: about 0.20 to O 9 35 Chrom: Chrome: Nickel: . niedrigNickel:. low Molybdän etwa 0,45 bis 0^55Molybdenum about 0.45 to 0 ^ 55 mit dem Rest als Eisen und Rest¥erunreinigungen0 with the remainder as iron and residual impurities 0 7. Normalisierter und angelassener -niedriglegierter Stahl, der eine Mindest-Streckfestigkeit von 5 625 kg/cm hat und durch eine im wesentlichen gleichmäßige Härtbarkeit in Querschnittsdicken bis zu zwei Zoll ausgezeichnet ist, gekennzeichnet duroh folgende Zusammensetzung - nach" Gewichtsprozent - ζ 7. Normalized and tempered low-alloy steel, which has a minimum yield strength of 5 625 kg / cm and is characterized by a substantially uniform hardenability in cross-section thicknesses of up to two inches, characterized by the following composition - according to "weight percent - ζ Kohlenstoff: etwa 0,15 bis 0P40Carbon: about 0.15 to 0 P 40 Mangan: etwa 1,10 bis 1P9ÖManganese: about 1.10 to 1 P 90 Schwefel: max. 0,060Sulfur: 0.060 max Phosphor: maxe 0,040Phosphorus: max e 0.040 Silizium: etwa 0,10 bis I9OOSilicon: about 0.10 to I 9 OO Chrom: etwa 0,00 bis 1910Chromium: about 0.00 to 1 9 10 Nickel: max. 0,25Nickel: max. 0.25 Molybdän: etwa 0,10 bis 0J5Molybdenum: about 0.10 to 0J5 Bor: miü. 0,0005Bor: miü. 0.0005 mit dem Rest als Eisen und Restverunreinigungen.with the rest as iron and residual impurities. 409836/0692409836/0692
DE19732359011 1973-02-22 1973-11-27 Thick-walled pipes made of quenched and tempered low-alloy steel Withdrawn DE2359011B2 (en)