DE2319176C - Method and device for producing ceramic bodies - Google Patents
Method and device for producing ceramic bodiesInfo
- Publication number
- DE2319176C DE2319176C DE2319176C DE 2319176 C DE2319176 C DE 2319176C DE 2319176 C DE2319176 C DE 2319176C
- Authority
- DE
- Germany
- Prior art keywords
- drying
- mouthpiece
- strand
- ceramic
- pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
oben gebogen wird, also entgegengesetzt der Biegung, die sich ohne Vorspannung beim Trocknen ergeben würde, und anschließend der Massestrang geradegebogen wird.is bent at the top, i.e. opposite to the bend, which would result without pre-tensioning during drying, and then the strand of mass is straightened will.
Trocknen der Körper erfolgt. In der Praxis kann diese Vorspannung z. B. dadurch erzeugt werden, daß der keramische Massestrang nach dem Austritt aus dem Mundstück in Längsrichtung nach oben gebogen wird, also entgegengesetzt der Biegung, die sich ohne Vorspannung beim Trocknen ergeben würde, und anschließend der Massestrang geradegebogen wird.Drying the body takes place. In practice this can Bias z. B. can be generated in that the ceramic After exiting the mouthpiece, the strand of mass is bent upwards in the longitudinal direction, that is, opposite to the bend that would result during drying without pre-tensioning, and then the strand of mass is straightened.
Die Erfindung hat ferner eine Vorrichtung zur Durchführung des geschilderten Verfahrens in verschiedenen Ausführungsformen zum Gegenstand. In einer Ausführurigsform ist das Mundstück um einen Winkel geneigt zum Preßkopf angeordnet, und es ist zwischen einem Bändertisch und dem Mundstück eine kurvenförmig gestaltete Rollenbahn angeordnet. Durch das anschließende Geradebiegen des Stranges auf dem Bändertisch wird in der unteren Zone dtj Stranges eine Druck- und in der oberen Zone eine Zugvorspannung erzeugt, welche der unerwünschten Abwärtsbiegung beim Trocknen entgegenwirken. Die Höhe der Vorspannung kann durch Variieren des Neigungswinkels des Mundstücks und durch Variieren der Strangkrümmung auf der Rollenbahn entsprechend verändert werden, so daß außer abwärts gebogenen oder geraden auch aufwärts gebogene keramische Körper hergestellt werden können. Der für möglichst große Formhaltigkeit nötige Neigungswinkel bzw. die nötige Strangkrümmung kann durch wenige Produktionsve< suche leicht festgestellt werden.The invention also has an apparatus for performing the method described in various ways Embodiments to the subject. In one embodiment, the mouthpiece is around one Angle arranged inclined to the press head, and there is one between a belt table and the mouthpiece Curved roller conveyor arranged. By then straightening the strand on the Belt table becomes a strand in the lower zone Compression and tensile prestressing in the upper zone, which causes the undesired downward bending counteract when drying. The amount of preload can be adjusted by varying the angle of inclination of the mouthpiece and by varying the curvature of the strand on the roller conveyor can be changed accordingly, so that besides downwardly curved or straight ceramic bodies also upwardly curved ceramic bodies are produced can be. The angle of inclination or the necessary strand curvature required for the greatest possible dimensional stability can easily be determined by a few production searches.
Die Vorteile des erfindungsgemäßen Verfahrens liegen darin, daß die Formhaltigkeit von keramischen Körpern mit minimalen Kosten außerordentlich stark verbessert werden kann. So können mit dem Verfahren 5 ohne besondere Schwierigkeit keramische Platten in den Maßen von etwa 220 χ 380 mm hergestellt werden, deren Längs- und Querbiegung kleiner als 0.5 mm ist.The advantages of the process according to the invention lie in the fact that the shape retention sta r k can be improved greatly from ceramic bodies with minimal cost. Thus, with the method 5, ceramic plates with dimensions of about 220 × 380 mm can be produced without any particular difficulty, the longitudinal and transverse bending of which is less than 0.5 mm.
Die zur Anwendung des Verfahrens notwendigenThe ones necessary for the application of the procedure
•o Vorrichtungen können außerdem in fast allen Fällen ohne Schwierigkeit an den vorhandenen Maschinen bzw. Mundstücken nachträglich angebracht werden.• Devices can also be used in almost all cases can be retrofitted to the existing machines or mouthpieces without difficulty.
In der Zeichnung sind Ausführungsbeispiele der Vorrichtung nach der Erfindung dargestellt.In the drawing, exemplary embodiments of the device according to the invention are shown.
>5 F i g. 1 zeigt in Seitenansicht eine Vorrichtung zur Durchführung des erfindungsgemäßen Verfahrens in einer Ausführungsform. Ein Mundstück 9 ist um einen Winkel 10 geneigt an einem Preßkopf 11 angebracht. Ein keramischer Strang 12 läuft auf einer kurvenförmig gestalteten Rollenbahn 13 zu einem Bändertisch 14, auf welchem durch das Geradebiegen des Stranges in einer unteren Zone 15 desselben eine Druckvorspannung und in einer oberen Zone 16 desselben eine Zugvorspannung erzeugt wird.> 5 F i g. 1 shows a side view of a device for Carrying out the method according to the invention in one embodiment. A mouthpiece 9 is around one Angle 10 inclined attached to a press head 11. A ceramic strand 12 runs on a curve designed roller conveyor 13 to a belt table 14, on which by straightening the strand in a lower zone 15 of the same a compressive prestress and in an upper zone 16 of the same a tensile prestress is produced.
F i g. 2 zeigt wiederum in Seitenansicht eine abgewandelte Ausführungsform einer Vorrichtung zur Durchführung des erfindungsgemäßen Verfahrens. In dieser Ausführungsform entfällt die Rollenbahn 13 der Ausführungsform nach Fig. 1. Der Strang 12 gelangtF i g. 2 again shows in a side view a modified embodiment of a device for Implementation of the method according to the invention. In this embodiment, the roller conveyor 13 is omitted Embodiment according to FIG. 1. The strand 12 arrives
vielmehr unmittelbar nach dem Austritt aus dem Mundstück 9 auf einen Bändertisch 14. Dabei wird dem Strang 12 ein leichter Knick 17 erteilt.rather, immediately after exiting the mouthpiece 9 on a belt table 14. This is the Strand 12 was given a slight kink 17.
Hierzu 1 Blatt Zeichnungen1 sheet of drawings
Claims (5)
Herstellen stranggepreßter keramischer Körper, die 35 Trockenvorgangs zu wechseln, so daß die UmströmungG
Manufacture of extruded ceramic bodies that change the drying process so that the flow around them
schwindung von etwa 6 bis 10% ist nämlich bei hohem Aus »Sprechsaal für Keramik — Glas — Email«,What all processes have in common is the still inadequate shape retention and the sometimes extremely high effort required to improve them. How significant the difficulties are to ensure good dimensional stability in the manufacture of ceramic bodies is clear from DIN 456, "Roof tiles", according to which z. B. the winged blanks during drying, thereby partly lack of beaver tails (size 155x375mm), that the material moisture during pressing is 6 mm and the wingedness of hollow sockets is kept very low. The thickest dry (size 235 χ 400 mm) may even be 12 mm,
shrinkage of around 6 to 10% is namely at high levels of »consulting room for ceramic - glass - enamel«,
Bei den üblichen Verfahren wird der gepreßte, plastische Rohling auf Rahmen, Rähmchen, Förderbändern,is between 15 to 25%. If the mixing water content is lower, the shrinkage is often only a fraction of it. The disadvantages of the re-pressing process are in particular the additionally necessary pressing process on punch presses, the disadvantages of dry pressing are the high power consumption and machine wear and the still poor shape retention.
In the usual process, the pressed, plastic blank is placed on frames, frames, conveyor belts,
rci gebracht wird. Da die Trocknungsluft die Auflage- Erfindungsgemäß wird diese Aufgabe dadurch gelöst, fläche = Unterfläche des Rohlings nicht ebenso gut daß dem Massestrang am Mundstücksaustritt und/oder umströmen kann wie die übrigen Flächen, insbesondere nach Verlassen des Mundstücks eine der Biegeverfordie Oberfläche, trocknet die Oberseite des Rohlings mung beim Trocknen entgegenwirkende Vorspannung früher an, beginnt zu schwinden und wird lederhart, 65 erteilt wird, bevor das Trocknen der Körper erfolgt. In während dadurch die noch plastische Unterseite ge- der Praxis kann diese Vorspannung z. B. dadurch erstaucht und verkürzt wird. Wenn im weiteren Verlauf zeugt werden, daß der keramische Massestrang nach des Trocknungsvorgangs dann auch die Unterseite dem Austritt aus dem Mundstück in Längsrichtung nachRolls or the like, placed on which it is compensated for errors caused by the dryer,
rci is brought. According to the invention, this object is achieved by the fact that the surface = lower surface of the blank is not as good as that the mass strand at the mouthpiece outlet and / or can flow around as the other surfaces, especially after leaving the mouthpiece one of the bending verfordie surface, the top of the dries Pre-tensioning, which counteracts the drying process, begins to dwindle and becomes leather-hard, 65 before the body is dried. In practice, while the still plastic underside is this preload can e.g. B. is thereby astonished and shortened. If in the further course it is shown that the ceramic mass strand after the drying process then also the underside after the exit from the mouthpiece in the longitudinal direction
Family
ID=