DE202008012433U1 - Molded part using fiber fabric - Google Patents

Molded part using fiber fabric Download PDF

Info

Publication number
DE202008012433U1
DE202008012433U1 DE200820012433 DE202008012433U DE202008012433U1 DE 202008012433 U1 DE202008012433 U1 DE 202008012433U1 DE 200820012433 DE200820012433 DE 200820012433 DE 202008012433 U DE202008012433 U DE 202008012433U DE 202008012433 U1 DE202008012433 U1 DE 202008012433U1
Authority
DE
Germany
Prior art keywords
matrix material
motif
molding according
molded part
molding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE200820012433
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FIRST COMPOSITES GmbH
Original Assignee
FIRST COMPOSITES GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FIRST COMPOSITES GmbH filed Critical FIRST COMPOSITES GmbH
Priority to DE200820012433 priority Critical patent/DE202008012433U1/en
Publication of DE202008012433U1 publication Critical patent/DE202008012433U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Formteil unter Verwendung eines Verbundes aus Fasergewebe und einem aushärtbaren Matrixmaterial, welches insbesondere im Resin Transfer Moulding (RTM) Verfahren hergestellt ist und mit Motiven (Beschriftungen, Bildern, Logos usw.) gestaltet ist, wobei das Fasergewebe mit den Motiven versehen ist und das Matrixmaterial in das Fasermaterial infiltriert ist und zumindest die Motive bedeckt.molding using a composite of fibrous tissue and a curable Matrix material, which in particular in Resin Transfer Molding (RTM) procedure is prepared and with motifs (inscriptions, Pictures, logos, etc.) is designed, wherein the fiber fabric with the Motives is provided and the matrix material in the fiber material is infiltrated and at least covered the motives.

Figure 00000001
Figure 00000001

Description

Die Erfindung betrifft ein Formteil unter Verwendung von Fasergewebe, welches insbesondere im Resin Transfer Moulding (RTM) Verfahren hergestellt ist. Das RTM-Verfahren ist ein Verfahren zur Herstellung von Formteilen aus Duroplasten und Elastomeren. Dabei wird die Formmasse mittels einer Pumpe von einer meist beheizten Vorkammer über Verteilerkanäle in das Formnest eingespritzt, worin sie unter Wärme und Druck aushärtet. Als Formmasse bzw. Matrixmaterial können Formaldehydharze (PF, MF usw.) und Reaktionsharze (UP, EP) mit kleinen Füllstoffpartikeln und Elastomere verwendet werden. Um auch Faserhalbzeuge (Prewovens/Preform) zu verarbeiten, werden diese zuvor in das Werkzeug eingelegt und anschließend die Formmasse eingespritzt und für eine bestimmte Zeit im Werkzeug belassen. Bei dieser Verweilzeit kommt es zum Reagieren oder Vulkanisieren der Formmasse. Sie ist dabei von verschiedenen Faktoren abhängig (Harztyp, Füllstoff, Verarbeitungsdruck und -temperatur). Ist die Verweilzeit beendet, kann das Werkzeug geöffnet und das Formteil entnommen werden. Durch das RTM-Verfahren können komplexe Bauteile aus faserverstärkten Kunststoffen hergestellt werden, wobei jedoch die farbige Gestaltung der Oberfläche dieser Formteile aus Glasfaser- oder Carbonfaserwerkstoffen nur eingeschränkt farbig/dekorativ gestaltet werden kann.The Invention relates to a molded article using fibrous fabric, which in particular in Resin Transfer Molding (RTM) method is made. The RTM process is a process for production of molded parts made of thermosets and elastomers. This is the molding material by means of a pump from a mostly heated prechamber over Manifolds injected into the mold cavity, wherein they Cures under heat and pressure. As a molding material or matrix material can formaldehyde resins (PF, MF, etc.) and reactive resins (UP, EP) with small filler particles and elastomers are used. To also semi-finished fiber products (Prewovens / Preform) to be processed, these are previously inserted in the tool and then the molding compound injected and for leave a certain amount of time in the tool. At this residence time it comes to reacting or vulcanizing the molding material. she is depends on various factors (type of resin, filler, Processing pressure and temperature). When the residence time has ended, the tool can be opened and the molded part removed. By The RTM process can be complex components made of fiber reinforced However, the colored design the surface of these molded parts made of glass fiber or carbon fiber materials only limited color / decorative can be designed.

Aus EP 1 055 512 B1 ist ebenfalls ein Formteil sowie ein Verfahren zu seiner Herstellung bekannt. Damit wird ein farbiger geformter Gegenstand hergestellt, der eine äußere Kunststoffschicht aufweist, über welcher eine Folienschicht angeordnet ist, wodurch ein Verbundschichtstoff gebildet wird. Ein Verstärkungsmatrial aus Metall, Kunststoff, Kohlenstofffasern, Glasfaserstoff oder Gewebe wird an die Innenfläche der äußeren Folienschicht geklebt. Aus der Außenfläche der äußeren Folienschicht ist eine Zierschicht mit einheitlicher Farbe angebracht. Das Formteil wird mit einem Formwerkzeug hergestellt, in dem es unter Druckbeaufschlagung mit Extruder Heißkunststoff hinerspritzt wird, wobei es sich an die Gravur des Formenhohlraumes anlegt.Out EP 1 055 512 B1 is also known a molding and a method for its preparation. Thus, a colored molded article is made having an outer plastic layer over which a film layer is disposed, thereby forming a composite laminate. A reinforcing matrix of metal, plastic, carbon fibers, fiberglass or fabric is adhered to the inner surface of the outer film layer. From the outer surface of the outer film layer, a decorative layer of uniform color is attached. The molding is made with a mold in which it is injected under pressure with extruder hot plastic, wherein it applies to the engraving of the mold cavity.

Aus DE 42 42 148 A1 ist ein Verfahren zur Herstellung von Formteilen aus glasfaserverstärkten Kunststoffen bekannt, wobei eine Folie in eine Form zur Anlage gebracht wird, bevor der glasfaserverstärkte Kunststoff in Mattenform eingelegt wird. Weiterhin kann nach dieser Lösung ein Formteil aus glasfaserverstärktem Kunststoff hergestellt werden, bei dem ein mittels Nasspressen hergestelltes Verbundlaminat aus GFK an seiner Außenfläche eine von einer Tiefziehfolie gebildete Außenhaut hat, die mit einem Designaufdruck versehen sein kann.Out DE 42 42 148 A1 is a method for the production of molded parts made of glass fiber reinforced plastics known, wherein a film is brought into a mold to the plant before the glass fiber reinforced plastic is inserted in mat form. Furthermore, according to this solution, a molded part made of glass fiber reinforced plastic can be produced, in which a composite laminate produced by wet pressing made of fiberglass on its outer surface has an outer skin formed by a thermoforming foil, which can be provided with a design imprint.

Ein Kunststoff-Formteil und ein Verfahren zu dessen Herstellung wird in DE 10 2004 060 810 A1 beschrieben. Das Kunststoff-Formteil wird aus einem transparenten Kunststofffolienmaterial gebildet, welches einseitig bedruckt und dann durch ein Tiefziehverfahren umgeformt wird. Nach dem Umformen wird es von der transparenten Seite her mit transparentem Kunststoff hinterspritzt. Weiterhin wird das Folienmaterial auf seiner von der bedruckten Seite abgewandten Seite mit einer kratzfesten Schicht versehen.A plastic molding and a method for its production is in DE 10 2004 060 810 A1 described. The plastic molding is formed from a transparent plastic film material, which is printed on one side and then formed by a deep drawing process. After forming, it is back-injected from the transparent side with transparent plastic. Furthermore, the film material is provided on its side facing away from the printed side with a scratch-resistant layer.

Bei allen vorgenannten Lösungen weisen die bedruckten Formteile einen mehrschichtigen Aufbau auf, womit ein erhöhter fertigungstechnischer Aufwand bei deren Herstellung verbunden ist.at All the above solutions have the printed moldings a multi-layered construction, whereby an increased manufacturing technology Expense associated with their production.

Aufgabe der Erfindung ist es, ein Formteil unter Verwendung von Fasergeweben und Formmasse/Matrixmaterial, welches insbesondere im Resin Transfer Moulding (RTM) Verfahren hergestellt ist, zu entwickeln, welches farbig (mit Motiven, Beschriftungen, Bildern, Logos usw.) gestaltet ist.task The invention is a molded part using fiber fabrics and molding material / matrix material, which in particular in the resin transfer Molding (RTM) process is made to develop which colored (with motifs, inscriptions, pictures, logos, etc.) designed is.

Diese Aufgabe wird mit den Merkmalen des ersten Schutzanspruchs gelöst, vorteilhafte Ausgestaltungen ergeben sich aus den Unteransprüchen.These Problem is solved with the features of the first patent claim advantageous embodiments will become apparent from the dependent claims.

Das Formteil besteht erfindungsgemäß aus einem Verbund von Fasergewebe und einem aushärtbaren Matrixmaterial/Formmasse und ist insbesondere im Resin Transfer Moulding (RTM) Verfahren hergestellt und farbig mit Motiven (Beschriftungen, Bildern, Logos usw.) gestaltet, wobei das Fasergewebe mit den Motiven versehen und das Matrixmaterial in das Fasermaterial infiltriert ist und zumindest die Motive bedeckt.The Molded part according to the invention consists of a composite fiber fabric and a curable matrix material / molding compound and is particularly in the Resin Transfer Molding (RTM) process produced and colored with motives (inscriptions, pictures, logos etc.), wherein the fiber fabric provided with the motifs and the matrix material is infiltrated into the fibrous material and at least the motives covered.

Dabei wird das Motiv auf das ungeformte mattenartige Ausgangs-Fasergewebe insbesondere aufgedruckt, aufgesprüht, aufgemalt oder anderweitig aufgebracht. Bevorzugt wird das Motiv durch Farbgebung mittels Tintenstrahldruckverfahren auf das mattenartige Ausgangs-Fasergewebe aufgedruckt oder z. B. mittels einer Schablone aufgesprüht.there the motif is applied to the unshaped mat-like starting fibrous tissue especially imprinted, sprayed, painted or otherwise applied. The motif is preferred by coloring by means of inkjet printing process printed on the mat-like starting fiber fabric or z. B. sprayed by means of a stencil.

Weiterhin kann das Motiv auch aus den verschiedensten Materialien bestehen, die auf dem mattenartigen Ausgangs-Fasergewebe positioniert werden. Dies können Papier oder Pappe, Holz, textile Gewebe, Pflanzenbestandteile oder andere Bestandteile sein, die zur Erzeugung eines gewünschten Motivs geeignet sind. Zur Fixierung an dem mattenartigen Ausgangs-Fasergewebe werden diese Materialien angeklebt oder angesteckt.Farther the motif can also be made of a variety of materials, which are positioned on the mat-like parent fibrous web. This can be paper or cardboard, wood, textile fabrics, plant components or other ingredients necessary to produce a desired Motive are suitable. For fixing to the mat-like starting fibrous tissue These materials are glued or infected.

Selbstverständlich kann auch eine Farbgebung mit diesen unterschiedlichen Motivmaterialien kombiniert sein.Of course can also be a color combination combined with these different motif materials be.

Als Fasergewebe wird insbesondere Glasfasermaterial oder Carbonmaterial in Mattenform eingesetzt und als aushärtendes Matrixmaterial (Formmasse) Formaldehydharze, Reaktionsharze (UP, EP) oder Elastomere verwendet. Bevorzugt ist das Matrixmaterial farbloses und durchsichtiges Epoxydharz. Es ist möglich, dem Matrixmaterial Füllstoffpartikel beizufügen, wobei das Matrixmaterial und/oder die Füllstoffpartikel farbig sein können. In Verbindung mit den auf die Matten aufgedruckten Motiven können so zusätzliche dekorative Effekte entstehen.As a fiber fabric is in particular Glasfa sermaterial or carbon material used in mat form and as a hardening matrix material (molding material) formaldehyde resins, reactive resins (UP, EP) or elastomers used. Preferably, the matrix material is colorless and transparent epoxy resin. It is possible to add filler particles to the matrix material, wherein the matrix material and / or the filler particles may be colored. In combination with the motifs printed on the mats, additional decorative effects can be created.

Das Matrixmaterial bedeckt das Fasergewebe insbesondere mit einer Schichtdicke von gewöhnlich 0,05 bis 0,2 mm.The Matrix material covers the fiber fabric, in particular with a layer thickness usually 0.05 to 0.2 mm.

Mit der erfindungsgemäßen Lösung wird ein Formteil geschaffen, welches erstmalig eine direkt auf die fasermatten aufgebrachtes Motiv aufweist, welches durch die Verwendung des RTM-Verfahrens mittels des Matrixmaterials infiltriert ist, wobei das Matrixmaterial das Motiv bedeckt. Dadurch wird ein überraschender 3D-Effekt beim Betrachten des Motivs hervorgerufen. Dieser Effekt kann durch die Verwendung von farbigen Partikeln, die sich dann zwischen der Sichtoberfläche des Bauteils und dem Motiv auf dem Fasergewebe befinden, noch verstärkt.With the solution according to the invention becomes a molded part created, which for the first time applied directly to the fiber mats Motif, which by the use of the RTM method by means of of the matrix material is infiltrated, the matrix material containing the Motif covered. This will be a surprising 3D effect caused by looking at the subject. This effect can be through the use of colored particles, which are then between the Visual surface of the component and the motif on the fiber fabric are still intensified.

Dadurch dass sich die Motive direkt in dem Formteil befinden, können diese nicht beschädigt werden.Thereby that the motifs are located directly in the molding can these are not damaged.

Überraschend dabei ist ebenfalls, dass die durch Tintenstrahldruck auf das Fasergewebe aufgebrachte Beschichtung bei der Durchführung des RTM-Verfahrens nicht beeinträchtigt wird, da das Matrixmaterial bei einer Temperatur von gewöhnlich 25 bis 50°C in die Form injiziert wird, in die vorher das bedruckte Fasergewebe eingelegt wurde.Surprised It is also the case that by ink jet printing on the fiber fabric applied coating in the implementation of the RTM method is not affected, since the matrix material in a Temperature of usually 25 to 50 ° C in the mold is injected, previously inserted in the printed fiber fabric has been.

Die Erfindung wird nachfolgend anhand von Ausführungsbeispielen und zugehörigen Zeichnungen näher erläutert.The Invention will be described below with reference to embodiments and associated drawings explained in more detail.

Es zeigen:It demonstrate:

1: dreidimensionale Darstellung eines erfindungsgemäßen Formteils, 1 : three-dimensional representation of a molded part according to the invention,

2: Draufsicht auf ein erfindungsgemäßes Formteil mit einem Motiv, wobei die Matrix durchsichtig ist, 2 : Top view of a molded part according to the invention with a motif, the matrix being transparent,

3: Draufsicht auf ein Formteil mit einem Motiv gem. 2, wobei die Matrix farbige Füllstoffpartikel enthält. 3 : Top view of a molded part with a motif acc. 2 wherein the matrix contains colored filler particles.

Die dreidimensionale Darstellung eines erfindungsgemäßen Formteils F ist in 1 dargestellt. Das Formteil wurde aus Fasergewebe 1 in Form einer Carbonfasermatte hergestellt, die an ihrer nach außen sichtbaren Seite durch Tintenstrahldruck (mit einer unter UV-Licht aushärtbaren Tinte) mit einem Motiv 2 versehen wurde, welches aus einer Beschriftung und aus grafischen Elementen besteht. Anschließend wurde das Fasergewebe 1 in eine Form (nicht dargestellt) eingelegt und die Form mittels des RTM-Verfahres mit einem aushärtbaren Harz 3, welches eine Temperatur von 40°C aufweist, ausgespritzt. Durch den dabei auftretenden Druck wird das Harz 3 um das Fasergewebe 1 herum und durch das Fasergewebe 1 hindurch (und somit durch das Motiv hindurch) an die Innenwand der Form (nicht dargestellt) gepresst, so dass zwischen Innenwand der Form und Fasergewebe eine Schicht aus Harz 3 aufgebaut und das Fasergewebe mit dem aushärtbaren Harz infiltriert wird. Nach dem Aushärten des Harzes 3 wird das Formteil 1 entnommen. Dieses weist gem. 1 eine im Harz 3 eingebettete Lage aus Fasergewebe 1 (hier eine Carbonfasermatte) auf, die auf ihrer Oberseite das Motiv 2 aufweist, über welchem sich eine Schicht 4 aus Harz 3 befindet. Die Schicht 4 weist bevorzugt eine Dicke 0,05 bis 0,2 mm auf. Da das Harz durchsichtig ist ergibt sich im Zusammenhang mit dem Design der Oberseite der Carbonfasermatte beim Betrachten der Außenseite 5 des Formteils F ein überraschender 3D-Effekt. Die dünne Harzschicht schützt gleichzeitig das Motiv 2 vor Beschädigungen.The three-dimensional representation of a molded part F according to the invention is shown in FIG 1 shown. The molding was made of fiber fabric 1 in the form of a carbon fiber mat, which on its outwardly visible side by inkjet printing (with a UV-curable ink) with a motif 2 which consists of a label and graphic elements. Subsequently, the fibrous tissue was 1 placed in a mold (not shown) and the mold by means of the RTM process with a thermosetting resin 3 , which has a temperature of 40 ° C, injected. Due to the pressure that occurs, the resin becomes 3 around the fiber tissue 1 around and through the fibrous tissue 1 pressed through (and thus through the subject) to the inner wall of the mold (not shown), so that between inner wall of the mold and fiber fabric, a layer of resin 3 built and the fiber fabric is infiltrated with the thermosetting resin. After curing the resin 3 becomes the molding 1 taken. This has gem. 1 one in the resin 3 embedded layer of fibrous tissue 1 (here a carbon fiber mat) on top of which the motif 2 over which a layer 4 made of resin 3 located. The layer 4 preferably has a thickness of 0.05 to 0.2 mm. Because the resin is translucent, the design of the top of the carbon fiber mat results in viewing the outside 5 of the molding F a surprising 3D effect. The thin resin layer protects the motif at the same time 2 from damage.

2 zeigt die Draufsicht auf ein erfindungsgemäßes Formteil F mit einem Motiv 2 in Form einer Grafik, wobei die Matrix in Form des Harzes 3 durchsichtig ist. Man erkennt dadurch die Oberfläche des Fasergewebes sowie das darauf abgebildete Motiv 2 2 shows the top view of an inventive molding F with a motif 2 in the form of a graphic, the matrix being in the form of the resin 3 is transparent. It recognizes the surface of the fiber fabric as well as the motif depicted on it 2

Draufsicht auf ein Formteil F mit einem Motiv 2 wie in 2, wobei jedoch die Matrix in Form des Harzes 3 farbige Füllstoffpartikel 6 enthält, ist in 3 dargestellt. Durch die Füllstoffpartikel 6 ergibt sich ein anderer Gesamteindruck der Außenseite 5 des Formteils F. Gleichzeitig können die Partikel zur Veränderung der Eigenschaften des Formteiles beitragen.Top view of a molded part F with a motif 2 as in 2 but where the matrix is in the form of the resin 3 colored filler particles 6 contains is in 3 shown. Through the filler particles 6 results in a different overall impression of the outside 5 At the same time, the particles can contribute to changing the properties of the molded part.

Mit der Erfindung ist es erstmalig möglich, ohne zusätzliche Folien oder Schichten durch das RTM-Verfahren ein Formteil mit einem Motiv herzustellen, wobei gleichzeitig ein 3D-Effekt erzeugt wird und das Motiv vor Beschädigungen geschützt ist.With For the first time it is possible to use the invention without additional Films or layers by the RTM process a molding with a Create motif, while a 3D effect is generated and the subject is protected from damage.

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • - EP 1055512 B1 [0002] - EP 1055512 B1 [0002]
  • - DE 4242148 A1 [0003] - DE 4242148 A1 [0003]
  • - DE 102004060810 A1 [0004] DE 102004060810 A1 [0004]

Claims (13)

Formteil unter Verwendung eines Verbundes aus Fasergewebe und einem aushärtbaren Matrixmaterial, welches insbesondere im Resin Transfer Moulding (RTM) Verfahren hergestellt ist und mit Motiven (Beschriftungen, Bildern, Logos usw.) gestaltet ist, wobei das Fasergewebe mit den Motiven versehen ist und das Matrixmaterial in das Fasermaterial infiltriert ist und zumindest die Motive bedeckt.Molded part using a composite Fiber fabric and a curable matrix material, which produced in particular by the Resin Transfer Molding (RTM) process is and is designed with motifs (captions, images, logos, etc.), wherein the fibrous web is provided with the motifs and the matrix material infiltrated into the fiber material and at least covered the subjects. Formteil nach Anspruch 1, dadurch gekennzeichnet, dass das Motiv auf das Ausgangs – Fasergewebe durch Farbgebung aufgebracht ist.Molding according to claim 1, characterized that the subject on the initial fibrous tissue by coloring is applied. Formteil nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass das Motiv aufgedruckt, aufgesprüht, aufgemalt oder anderweitig aufgebracht ist.Molding according to claim 1 or 2, characterized that the motif is printed, sprayed, painted or otherwise applied. Formteil nach Anspruch 3, dadurch gekennzeichnet, dass das Motiv auf das Ausgangs – Fasergewebe mittels eines Tintenstrahldruckverfahrens oder durch Aufsprühen unter Verwendung einer Schablone aufgebracht ist.Molding according to claim 3, characterized that the motif on the initial fibrous tissue by means of a Ink jet printing process or by spraying under Using a stencil is applied. Formteil nach Anspruch 1, dadurch gekennzeichnet, dass das Motiv aus einem oder mehreren Bestandteilen gleicher oder unterschiedlicher Materialien besteht, die auf dem mattenartigen Ausgangs-Fasergewebe positioniert werden.Molding according to claim 1, characterized that the motif consists of one or more components of the same or consists of different materials, which on the mat-like Starting fibrous tissue are positioned. Formteil nach Anspruch 5, dadurch gekennzeichnet, dass die Bestandteile des Motivs aus Papier, Pappe, Holz, textilen Gewebe, Pflanzenbestandteilen oder andere Bestandteile sein, die zur Erzeugung eines gewünschten Motivs geeignet sind, bestehen.Molding according to claim 5, characterized in that that the components of the motif of paper, cardboard, wood, textile Be tissue, plant components or other ingredients that are suitable for generating a desired motif exist. Formteil nach Anspruch 5 oder 6, dadurch gekennzeichnet, dass das/die Bestandteil/e des Motivs zur Fixierung an dem mattenartigen Ausgangs-Fasergewebe angeklebt oder angesteckt ist/sind.Molding according to claim 5 or 6, characterized that the component (s) of the motif for fixing to the mat-like Starting fiber fabric glued or infected is / are. Formteil nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass das Fasergewebe Glasfasermaterial oder Carbonmaterial in Mattenform ist.Molded part according to one of claims 1 to 7, characterized in that the fiber fabric glass fiber material or carbon mat material. Formteil nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass Matrixmaterial Formaldehydharze, Reaktionsharze (UP, EP) oder Elastomere sind.Molded part according to one of claims 1 to 8, characterized in that matrix material formaldehyde resins, Reaction resins (UP, EP) or elastomers are. Formteil nach Anspruch 9, dadurch gekennzeichnet, dass Matrixmaterial Epoxydharz ist.Molding according to claim 9, characterized that matrix material is epoxy resin. Formteil nach Anspruch einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass das Matrixmaterial Füllstoffpartikel enthält.A molding according to claim any of the claims 1 to 10, characterized in that the matrix material filler particles contains. Formteil nach Anspruch 11, dadurch gekennzeichnet, dass das Matrixmaterial und/oder die Füllstoffpartikel farbig sind.Molding according to claim 11, characterized in that that the matrix material and / or the filler particles are colored. Formteil nach einem der Ansprüche 1 bis 12, dadurch gekennzeichnet, dass das Matrixmaterial das Fasergewebe mit einer Schichtdicke von 0,05 bis 0,2 mm bedeckt.Molded part according to one of claims 1 to 12, characterized in that the matrix material, the fiber fabric covered with a layer thickness of 0.05 to 0.2 mm.
DE200820012433 2008-09-18 2008-09-18 Molded part using fiber fabric Expired - Lifetime DE202008012433U1 (en)