DE19702760A1 - Fire-resistant polyurethane foam for building applications - Google Patents
Fire-resistant polyurethane foam for building applicationsInfo
- Publication number
- DE19702760A1 DE19702760A1 DE1997102760 DE19702760A DE19702760A1 DE 19702760 A1 DE19702760 A1 DE 19702760A1 DE 1997102760 DE1997102760 DE 1997102760 DE 19702760 A DE19702760 A DE 19702760A DE 19702760 A1 DE19702760 A1 DE 19702760A1
- Authority
- DE
- Germany
- Prior art keywords
- weight
- percent
- polyurethane foam
- fire
- foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die Erfindung bezieht sich auf einen brandhemmenden Po lyurethanschaum, basierend auf Polyolen und Isocyanaten, mit einem die Entflammbarkeit erschwerenden Mittel.The invention relates to a fire retardant bottom lyurethane foam, based on polyols and isocyanates, with a flammability aggravating agent.
Ein brandhemmendes Polyurethan mit den vorgenannten Merkmalen ist aus dem Deutschen Gebrauchsmuster 295 09 033 bekannt. Dieses bekannte Polyurethan weist ABC-Löschpulver auf, um eine Schwerentflammbarkeit gemäß der Brandklassifi zierung B1 nach DIN 4102 zu erreichen. ABC-Löschpulver eignet sich zum Löschen von Bränden der Brandklassen A,B und C. Es ist ein Gemisch aus Natriumhydrogencarbonat, Alkaliphosphat und dergleichen. Es muß zum Beeinflussen der Entflammbarkeit von Polyurethan nicht optimal angesehen werden. Denn der mehr oder weniger feste Polyurethanschaum ist nicht zum Löschen von Bränden bestimmt, wie das ABC-Löschpulver, sondern soll schwer entflammbar sein.A fire retardant polyurethane with the aforementioned Characteristics is from the German utility model 295 09 033 known. This well-known polyurethane has ABC extinguishing powder to a flame retardancy according to the fire classification decoration B1 according to DIN 4102. ABC powder is suitable to extinguish fires of fire classes A, B and C. Es is a mixture of sodium bicarbonate, alkali phosphate and the same. It has to influence the flammability not optimally viewed by polyurethane. Because the more or less rigid polyurethane foam is not erasable of fires determined how the ABC extinguishing powder, but should flame retardant.
Demgegenüber liegt der Erfindung die Aufgabe zugrunde, einen brandhemmenden Polyurethanschaum mit den eingangs ge nannten Merkmalen so zu verbessern, daß die zu fordernde schwere Entflammbarkeit und ein verbesserter Brandschutz mit optimalen Mitteln erreicht werden und eine Anwendung mit un terschiedlichen Systemen ermöglicht wird. In contrast, the invention is based on the object a fire-retardant polyurethane foam with the ge mentioned features to improve so that the required flame retardancy and improved fire protection with optimal means can be achieved and an application with un different systems is made possible.
Diese Aufgabe wird dadurch gelöst, daß der Schaum ein im Brandfall aufschäumendes Mittel zusätzlich zu dem die Ent flammbarkeit erschwerenden Mittel aufweist.This object is achieved in that the foam in In the event of fire, foaming agent in addition to the ent has flammability aggravating agents.
Im Brandfall wird das die Entflammbarkeit erschwerende Mittel des Polyurethanschaums dafür sorgen, daß letzterer den Vorschriften der Brandklassifizierung B1 nach DIN 4102 ge nügt. Bei einer Flammbeaufschlagung wird sich also der Poly urethanschaum nicht so schnell verzehren, wie wenn er das die Entflammbarkeit erschwerende Mittel nicht aufweist. Ein er heblicher Teil des Volumens des Polyurethanschaums wird je doch durch die Flammbeaufschlagung verzehrt, so daß es infol gedessen zu einer Minderung des Brandschutzes kommen kann, obwohl der brandhemmende Polyurethanschaum den Anforderungen genügt. Die vorerwähnte Minderung des Brandschutzes kann aus der Konstruktion herrühren. Es können sich beispielsweise Fu genverhältnisse zwischen Fensterrahmen und Wandlaibung erge ben, die nur eine geringe Dicke der Polyurethanschaumschicht gestatten. Die Fugenverhältnisse können auch so sein, daß ge wisse Fugenbereiche nicht komplett ausgeschäumt wurden. In all diesen Fällen ist zu befürchten, daß der effektive Brand schutz nicht ausreicht. Unter Einwirkung des im Brandfall aufschäumenden Mittels wird ein solcher Schutz jedoch er reicht. Je nach Konstruktion können die Schichtdicken des Schaums im Brandfall vergrößert werden, so daß sich die Schaumverzehrung verringert bzw. das brandbeaufschlagte Schaumvolumen vergrößert und der Verzehrungsvorgang verlang samt wird. Ferner wird auch erreicht, daß die Fugendichtig keit verbessert wird, weil das im Brandfall aufschäumende Mittel die Fugen schließt. Feuer- oder Rauchdurchtritt wird entsprechend erschwert oder verhindert. Die Wirkung des brandhemmenden Polyurethanschaums wird insgesamt verbessert.In the event of a fire, the flammability becomes more difficult Means of polyurethane foam ensure that the latter Fire classification regulations B1 according to DIN 4102 ge is enough. If the flame is applied, the poly Do not consume urethane foam as quickly as if he did Does not have flammability aggravating agents. A he considerable part of the volume of the polyurethane foam is ever but consumed by exposure to flame, so that it follows there may be a reduction in fire protection, although the fire retardant polyurethane foam meets the requirements enough. The aforementioned reduction in fire protection can derive from the construction. For example, Fu relations between window frames and wall reveal ben, only a small thickness of the polyurethane foam layer allow. The joint ratios can also be such that ge white joint areas were not completely foamed. In In all these cases there is a fear that the effective fire protection is not enough. Under the influence of in the event of a fire however, such a protection becomes foaming agent enough. Depending on the construction, the layer thicknesses of the Foam are enlarged in the event of fire, so that the Foam consumption reduced or the fire-prone Foam volume increases and the consumption process demands velvet. It is also achieved that the joints are sealed speed is improved because the foam in the event of fire Agent closes the joints. Passage of fire or smoke accordingly difficult or prevented. The effect of fire-retardant polyurethane foam is improved overall.
Die Wirkung des im Brandfall aufschäumenden Mittels läßt sich auf alle brandhemmenden Polyurethanschäume anwenden. Ei ne besondere Verbesserung ergibt sich jedoch dadurch, daß der Schaum Blähgraphit und/oder Blähglimmer enthält. Blähgraphite bzw. -Graphitverbindungen und Blähglimmer enthalten Graphite bzw. Graphitverbindungen und Glimmer, die in Bezug auf den Polyurethanschaum brandhemmend sind. Sie lassen sich nicht bzw. nicht so leicht durch das Feuer verzehren, wie Polyure thanschaum. Es ist daher grundsätzlich möglich, beliebigen Polyurethanschaum mit Blähgraphit und/oder Blähglimmer zu vermischen und auf diese Weise einen brandhemmenden Polyure thanschaum herzustellen. Hierzu reicht es aus, wenn als Mi schungsbestandteil ein Polyurethanschaum der Brandklassifi zierung B2 eingesetzt wird, der also an sich nicht schwer entflammbar ist, weil er die vorerwähnten Mittel zur Erschwe rung der Entflammbarkeit nicht aufweist. Auch in diesem Fall findet eine beispielsweise 10%ige Volumenvergrößerung statt, mit der die vorbeschriebene Volumenvergrößerung bzw. Fugen füllung erfolgt. Vor allem ist jedoch von Bedeutung, daß das Graphit bzw. der Glimmer im Brandfall zusätzliche Wirkung entfalten. Der Verzehrvorgang des Polyurethanschaums findet so statt, daß der Graphit bzw. der Glimmer über die infolge des Verzehrvorgangs relativ zurückweichende Außenfläche des Schaums vorstehen. Sie bilden eine Art Igelstruktur, die den Zutritt der Flammen zu der Schaumoberfläche erschwert. Es tritt eine Verlangsamung des Verzehrvorganges ein und damit eine Brandhemmung.The effect of the foaming agent in the event of fire leaves apply to all fire-retardant polyurethane foams. Egg ne particular improvement results from the fact that Contains expanded graphite and / or expanded mica. Expandable graphite graphite compounds and expanded mica contain graphite or graphite compounds and mica, which in relation to the Polyurethane foam is fire retardant. You don't let yourself or not as easily consumed by fire as polyure than foam. It is therefore basically possible to choose any Polyurethane foam with expanded graphite and / or expanded mica mix and in this way a fire retardant polyure to produce than foam. For this it is sufficient if as Mi a polyurethane foam of the fire classification ornament B2 is used, which is not difficult in itself is flammable because it is the aforementioned means for silence flammability. In this case, too there is, for example, a 10% increase in volume, with the above-mentioned volume increase or joints filling takes place. Above all, it is important that the Graphite or the mica in the event of fire additional effect unfold. The process of eating the polyurethane foam takes place so instead that the graphite or mica over the result of the eating process relatively receding outer surface of the Protrude foam. They form a kind of hedgehog structure that the It is difficult for the flames to access the foam surface. It there is a slowdown in the consumption process and thus a fire retardant.
Als Blähmittel kommen chemische Verbindungen zum Ein satz, die unter dem Einfluß von Wärme Gase abspalten, z. B. Stickstoffgase oder Kohlendioxyd, welche sich ausdehnen und das von ihnen besetzte Volumen vergrößern.Chemical compounds are used as blowing agents rate, which split off gases under the influence of heat, e.g. B. Nitrogen gases or carbon dioxide, which expand and increase the volume they occupy.
Die Flammhemmung hängt von der Formulierung des Polyure thanschaums ab. Es ist vorteilhaft, den Polyurethanschaum so auszubilden, daß der Schaum das im Brandfall aufschäumende Mittel zu 10 bis 78 Gewichtsprozent enthält. Je nach spezifi schem Gewicht des eingesetzten, im Brandfall aufschäumenden Mittels wird der Gewichtsanteil dieses Mittels am Schaum größer oder kleiner sein. Um die gewünschte Verbesserung der Brandhemmung zu erreichen, kommt es wegen der spezifischen Wirkung des Mittels entsprechend dem sogenannten Igeleffekt vor allem darauf an, daß hinreichendes Volumen zur Verfügung steht. Ein schwereres Mittel wird also mit einem Anteil grö ßerer Gewichtsprozente vorhanden sein müssen. The flame retardancy depends on the formulation of the polyure than foam. It is advantageous to use the polyurethane foam like this to train that the foam foams in the event of fire Contains 10 to 78 percent by weight. Depending on the specific weight of the foam used in the event of fire The percentage by weight of this agent in the foam is be bigger or smaller. To improve the desired To achieve fire retardation, it happens because of the specific Effect of the agent according to the so-called hedgehog effect especially that sufficient volume is available stands. A heavier medium therefore becomes larger with a portion greater weight percentages must be present.
Mit den vorbeschriebenen Mitteln ist es möglich, brand hemmenden Polyurethanschaum so auszubilden, daß er den Anfor derungen an die Brandklassifizierung B1 nach DIN 4102 er reicht. Es kann jedoch auch vorteilhaft sein, die dafür ein zusetzenden Mittel zu verringern oder mit anderen brandhem menden Mitteln zu kombinieren. Beispielsweise kann die Aus bildung des brandhemmenden Polyurethanschaums so beschaffen sein, daß nur ein geringer Anteil von im Brandfall aufschäu mendem Mittel erforderlich ist, weil die Fugenstruktur im Ausschäumbereich eher unkritisch ist. Der Polyurethanschaum kann daher so ausgebildet werden, daß er phosphat- und/oder halogenhaltig ist. Phosphate und Halogene bewirken eine Redu zierung der Brandempfindlichkeit.With the means described above, it is possible to fire inhibiting polyurethane foam so that it meets the requirements changes to fire classification B1 according to DIN 4102 enough. However, it can also be beneficial to use one reducing additives or with other brandhem to combine funds. For example, the off the formation of the fire-retardant polyurethane foam be that only a small proportion of foam in the event of fire is required because the joint structure in the Foaming area is rather uncritical. The polyurethane foam can therefore be designed so that it is phosphate and / or contains halogen. Phosphates and halogens cause a reduction adornment of fire sensitivity.
Eine besonders vorteilhafte und wirksame Formulierung
des brandhemmenden Polyurethanschaums ergibt sich dann, wenn
der nicht aus im Brandfall aufschäumendes Mittel aufweisende
Restbestandteil des Schaums zu
40 bis 65 Gewichtsprozent aus einem Isocyanat und zu
35 bis 55 Gewichtsprozent aus einer Polyolmischung herge
stellt ist, die sich folgendermaßen zusammensetzt:
A particularly advantageous and effective formulation of the fire-retardant polyurethane foam is obtained when the residual component of the foam which does not contain foaming agents in the event of a fire
40 to 65 weight percent of an isocyanate and
35 to 55 percent by weight is from a polyol mixture, which is composed as follows:
- a) 10 bis 20 Gewichtsprozent Polyether- und/oder Poly esterpolyol,a) 10 to 20 weight percent polyether and / or poly ester polyol,
-
b) 30 bis 50 Gewichtsprozent phosphat- und/oder halo
genhaltiges Polyetherpolyol, letzteres
- b1) mit einem Phosphatanteil von 10 bis 20 Gewichtsprozent, bedarfsweise ergänzt mit einem Halogenanteil von 15 bis 35 Ge wichtsprozent, oder
- b2) mit einem Halogenanteil von 30 bis 50 Ge wichtsprozent, und
- b1) with a phosphate content of 10 to 20 weight percent, if necessary supplemented with a halogen content of 15 to 35 weight percent, or
- b2) with a halogen content of 30 to 50% by weight, and
-
c) 35 bis 65 Gewichtsprozent phosphat- und/oder halo
genhaltiger Weichmacher, letzterer
- c1) mit einem Phosphatanteil von 5 bis 25 Ge wichtsprozent und/oder
- c2) mit einem Halogenanteil von 25 bis 35 Ge wichtsprozent.
- c1) with a phosphate content of 5 to 25% by weight and / or
- c2) with a halogen content of 25 to 35 percent by weight.
Bei dieser Ausgestaltung des Polyurethanschaums ist von Bedeutung, daß auf die Grundbestandteile Einfluß genommen wird, aus denen der nicht aus im Brandfall aufschäumendes Mittel aufweisende Restbestandteil des Schaums hergestellt wird. Insbesondere wird Einfluß genommen auf die Zusammenset zung der Polyolmischung, deren Polyether- und Weichmacherbe standteile brandhemmend ausgerüstet werden, und zwar im Um fang der vorangegebenen Zusammensetzungen. Es werden also phosphat- und/oder halogenhaltige Polyole bzw. Weichmacher eingesetzt, um die Brandhemmung des Polyurethanschaums zu er reichen. Das nicht feuerhemmend modifizierte Polyether- und/ oder Polyesterpolyol wird für die Stabilität der Mischung be nötigt, während mit dem feuerhemmend modifizierten Polyether polyol das spezifische Brandverhalten beeinflußt wird.In this configuration of the polyurethane foam is from Meaning that influenced the basic components from which the non-foaming in the event of fire Medium-containing residual component of the foam becomes. In particular, the composition is influenced tion of the polyol mixture, its polyether and plasticizer components are fire-retardant, in the order catch the given compositions. So there will be phosphates and / or halogen-containing polyols or plasticizers used to fire resistance of the polyurethane foam pass. The non-fire retardant modified polyether and / or polyester polyol is used for the stability of the mixture necessary while using the fire retardant modified polyether polyol the specific fire behavior is influenced.
In vorteilhafter Weise wird der Restbestandteil des Po lyurethanschaums so ausgebildet, daß das Isocyanat ein Diphe nylmethandiisocyanat ist. Das vorgenannte Diisocyanat, insbe sondere das Diphenylmethan-4.4'-Diisocyanat läßt sich in Po lyadditionsverfahren mit einem Polyol besonders gut verschäu men, wobei das Vorhandensein von Feuchtigkeit zur Abspaltung von schaumbildend wirkendem Kohlendioxyd führt.Advantageously, the remaining part of the bottom lyurethane foam so that the isocyanate is a diphe is nylmethane diisocyanate. The aforementioned diisocyanate, esp especially the diphenylmethane 4,4'-diisocyanate can be found in Po foaming lyaddition process with a polyol particularly well men, the presence of moisture for elimination leads to foaming carbon dioxide.
Die Polyolmischung zur Herstellung des Restbestandteils des Polyurethanschaums kann so ausgebildet werden, daß der Weichmacher Trialkylphosphat ist.The polyol mixture for the production of the remaining component of the polyurethane foam can be formed so that the Plasticizer is trialkyl phosphate.
Zur Herstellung des Restbestandteils des Polyurethan schaums kann so vorgegangen werden, daß die Polyolmischung zu 0,5 bis 5 Gewichtsprozent einen Katalysator aufweist. Mit Hilfe des Katalysators wird die Herstellung des Schaums ver bessert. Der Katalysator wird den Reaktionsbestandteilen an gepaßt und kann ein Amine- oder ein Metallkatalysator sein.To produce the remaining component of the polyurethane can be proceeded so that the polyol mixture 0.5 to 5 weight percent of a catalyst. With The catalyst is used to produce the foam improves. The catalyst becomes the reaction components fit and can be an amine or a metal catalyst.
Es ist möglich, den Restbestandteil des brandhemmenden Polyurethanschaums dadurch herzustellen, daß den Reaktions partnern für die Polyaddition schaumbildende Bestandteile zu gegeben werden, so daß also beispielsweise CO2 abgespalten wird. Um von dieser Art der Schaumbildung unabhängig zu sein, kann es jedoch vorteilhaft sein, den Restbestandteil des Po lyurethanschaums so auszubilden, daß er mit 10 bis 25 Ge wichtsprozent Treibmittel hergestellt ist, wobei der Isocya natanteil 35 bis 50 Gewichtsprozent und der Anteil der Poly olmischung 30 bis 45 Gewichtsprozent beträgt. Durch den Ein satz des Treibmittels im Umfang der angegebenen Gewichtspro zente verändern sich die prozentualen Gewichtsanteile des Isocyanats und der Polyolmischung, die ohne Vorhandensein ei nes Treibmittels eingesetzt würden, wie angegeben.It is possible to produce the remaining constituent of the fire-retardant polyurethane foam by adding foam-forming constituents to the reaction partners for the polyaddition, so that, for example, CO 2 is eliminated. In order to be independent of this type of foam formation, however, it may be advantageous to design the remaining component of the polyurethane foam so that it is made with 10 to 25 percent by weight of blowing agent, the isocyanate portion being 35 to 50 percent by weight and the portion of the polyol mixture 30 to 45 percent by weight. By using the blowing agent to the extent of the stated percentages by weight, the percentages by weight of the isocyanate and the polyol mixture which would be used without the presence of a blowing agent change as indicated.
Der Polyurethanschaum kann so ausgebildet werden, daß er vor seiner Anwendung in einer Aerosoldose gelagert ist. Hier handelt es sich um einen stabilen, daß heißt lagerfähigen 1-Komponentenschaum, der bei Temperaturen oberhalb des Ge frierpunkts und bis zu Raumtemperaturen mehrere Monate lager fähig ist.The polyurethane foam can be designed so that it stored in an aerosol can before use. Here it is a stable, that is, storable 1-component foam, which at temperatures above the Ge freezing point and store for several months at room temperatures is capable.
Das Treibmittel wird entsprechend den Anforderungen an das Aufschäumen ausgewählt. Von bewährten Eigenschaften wird Gebrauch gemacht, wenn als Treibmittel ein Fluorkohlenwasser stoff und/oder komprimierte Luft und/oder ein gering entzünd liches Alkan-Gasgemisch vorhanden ist. Die vorgenannten Treibmittel sind die vorteilhaftesten. Fluorkohlenwasserstoff hat nicht die Ozonschädlichkeit, wie beispielsweise Fluor chlorkohlenwasserstoffe. Komprimierte Luft ist vollkommen um weltneutral und preiswert. Gering entzündliche Alkan-Gasgemi sche können aus industriell verfügbaren Gasen hergestellt werden.The blowing agent is applied according to the requirements the foaming selected. Proven properties Used when a fluorocarbon is used as the blowing agent substance and / or compressed air and / or a low level of ignition Lich alkane gas mixture is present. The aforementioned Blowing agents are the most beneficial. Fluorocarbon does not have ozone depletion, such as fluorine chlorinated hydrocarbons. Compressed air is completely gone world neutral and inexpensive. Low flammable alkane gas mixture can be made from industrially available gases will.
Eine Schaumstabilisierung ist in vielen Anwendungsfällen wünschenswert und notwendig. Sie unterstützt die Brandbestän digkeit bzw. Formbeständigkeit des Polyurethanschaums, auch für den Brandfall. Es ist daher besonders vorteilhaft, wenn ein Polysiloxan-Schaumstabilisator vorhanden ist.Foam stabilization is in many applications desirable and necessary. It supports the fire resistance density or dimensional stability of the polyurethane foam, too in case of fire. It is therefore particularly advantageous if a polysiloxane foam stabilizer is available.
Der brandhemmende Polyurethanschaum zeigt ein schwer
entflammbares Brandverhalten gemäß DIN 4102 B1. Infolgedessen
kann ein bedeutend besserer Brandschutz erreicht werden, als
wenn Standardpolyurethanschaum eingesetzt wird. Spezielle An
wendungen für den schwer entflammbaren Polyurethanschaum sind
insbesondere im Baubereich zu finden. Genannt werden bei
spielsweise
The fire-retardant polyurethane foam shows fire resistance in accordance with DIN 4102 B1. As a result, significantly better fire protection can be achieved than when using standard polyurethane foam. Special applications for the flame retardant polyurethane foam can be found particularly in the construction sector. Are mentioned in example
- - die Auskleidung zwischen Rahmen und Mauerwerk bei Brand schutzverglasungen;- the lining between frame and masonry in the event of fire protective glazing;
- - die Hinterfüllung von Zargen zwischen Mauerwerk und Holz zarge bei Brandschutztüren;- the backfilling of frames between masonry and wood frame for fire doors;
- - die Hinterfüllung zwischen Mauerwerk und Stahlzargen bei Brandschutztüren mit sowohl herkömmlichen, als auch thermisch getrennten Stahlzargen;- The backfill between masonry and steel frames Fire doors with both conventional and thermal separate steel frames;
- - die Füllung von Brandschutzfugen unterschiedlicher Breite und Länge in Wänden unterschiedlicher Dicke und unterschied licher Materialien des Mauerwerks, wie diverse Betonsorten, leichte Trennwände etc.;- The filling of fire protection joints of different widths and length in walls of different thickness and difference materials of the masonry, such as various types of concrete, light partition walls etc .;
- - die Erstellung von Kabelschotts;- the creation of cable bulkheads;
- - das Ausfüllen von Mauerdurchbrüchen generell und Mauer durchbrüchen, durch die verlegte Leitungen führen;- Filling out wall openings in general and wall breakthroughs through which cables are laid;
- - das generelle Ausschäumen von Öffnungen, Hohlräumen und Spalten, die brandhemmend ausgerüstet werden sollen.- the general foaming of openings, cavities and Columns that should be fire-retardant.
Um die beispielsweise genannten Anwendungen durchführen
zu können, wird der Schaum unterschiedlich ausgerüstet, näm
lich beispielsweise durch Einstellung der Viskosität der Mi
schung oder durch die Anwendung unterschiedlich wirkender
Treibmittel oder Treibmechanismen. Der Polyurethanschaum kann
in folgenden Systemen angewendet werden:
In order to be able to carry out the applications mentioned, for example, the foam is equipped differently, namely by adjusting the viscosity of the mixture, for example, or by using blowing agents or blowing mechanisms which act differently. The polyurethane foam can be used in the following systems:
- - 1-Komponentensystem, z. B.:- 1-component system, e.g. B .:
- - 1-Komponentensystem, feuchtaushärtend, in Aerosolverpackung, unter Einsatz eines Treibgases, Applizierung mittels einer Dosierpistole oder direkt aus der Verpackung mittels eines Schlauchs.- 1-component system, moisture-curing, in aerosol packaging, using a propellant gas, application by means of a dispensing gun or directly from the packaging of a hose.
- - 1 1/2-Komponentensystem, also wie vor, wobei ein Härter zusätzlich eingesetzt wird. Als Härter wird beispielsweise ein kurzkettiges Polyol, wie Diol, angewendet.- 1 1/2 component system, so as before, with a hardener is also used. As a hardener, for example a short chain polyol such as diol is used.
- - 2-Komponentensystem, z. B. aus Aerosolverpackungen oder mit Kunststoffbehältern.- 2-component system, e.g. B. from aerosol packaging or with plastic containers.
Ein Beispiel für eine Zusammensetzung von Komponenten
zur Herstellung eines brandhemmenden Polyurethanschaums wird
wie folgt angegeben:
10 bis 78 Gewichtsprozent Blähgraphit und/oder Blähglimmer
22 bis 80 Gewichtsprozent Restbestandteil, dieser bestehend
aus:
35 bis 50 Gewichtsprozent Isocyanat (Diphenylme
thandiisocyanat)
30 bis 45 Gewichtsprozent Polyolmischung:
An example of a composition of components for producing a fire retardant polyurethane foam is given as follows:
10 to 78% by weight expanded graphite and / or expanded mica
22 to 80 percent by weight of residual component, consisting of:
35 to 50 percent by weight isocyanate (diphenylmethane diisocyanate)
30 to 45 weight percent polyol blend:
- a) 10 bis 20 Gewichtsprozent Polyether- und/oder Polyesterpolyol,a) 10 to 20 weight percent polyether and / or Polyester polyol,
-
b) 30 bis 50 Gewichtsprozent phosphat- und/oder
halogenhaltiges Polyether
polyol, letzteres
- b1) mit einem Phosphatanteil von 10 bis 20 Gewichtsprozent, oder
- b2) mit einem Halogenanteil von 30 bis 50 Gewichtsprozent, und
- b1) with a phosphate content of 10 to 20 percent by weight, or
- b2) with a halogen content of 30 to 50 percent by weight, and
-
c) 35 bis 65 Gewichtsprozent phosphat- und/
oder halogenhaltiges Trialkyl
phosphat, letzteres
- c1) mit einem Phosphatanteil von 5 bis 25 Gewichtsprozent und/oder
- c2) mit einem Halogenanteil von 25 bis 35 Gewichtsprozent.
- c1) with a phosphate content of 5 to 25 percent by weight and / or
- c2) with a halogen content of 25 to 35 percent by weight.
- d) 0,5 bis 10 Gewichtsprozent Polysiloxan- Schaumstabilisator.d) 0.5 to 10 percent by weight of polysiloxane Foam stabilizer.
- e) 0,5 bis 5 Gewichtsprozent Aminekatalysa tor.e) 0.5 to 5 percent by weight of amine catalyst gate.
10 bis 25 Gewichtsprozent Treibmittel, nämlich Fluorkohlenwasserstoff, insbesondere 1,1,1,2-Tetrafluorethan.10 to 25 percent by weight of blowing agent, namely Fluorocarbon, in particular 1,1,1,2-tetrafluoroethane.
Der vorstehend beispielsweise beschriebene Polyurethan schaum befindet sich als Prepolymer in einer Aerosoldose, die mit einer Dosierpistole zu bedienen ist, oder aus der das Prepolymer mittels Schlauch direkt angewendet wird. Blähgra phit und/oder Blähglimmer sind derart fein verteilt im Schaum, daß die vorerwähnten Anwendungen behinderungsfrei möglich sind. Blähglimmer ist beispielsweise unter der Han delsbezeichnung Vermiculit erhältlich. Plättchenförmige Struktur von Blähglimmer muß vor dem Zumischen pulverisiert werden.The polyurethane described above, for example As a prepolymer, foam is contained in an aerosol can can be operated with a dosing gun, or from which Prepolymer is applied directly using a hose. Expandable gray phit and / or expanded mica are so finely divided in Foam that the aforementioned applications are unobstructed possible are. Expanded mica is, for example, under the Han Vermiculite available. Platelet-shaped Structure of expanded mica must be pulverized before mixing will.
Claims (12)
- a) 10 bis 20 Gewichtsprozent Polyether- und/oder Polyesterpolyol,
- b) 30 bis 50 Gewichtsprozent phosphat- und/oder
halogenhaltiges Polyetherpolyol,
letzteres
- b1) mit einem Phosphatanteil von 10 bis 20 Gewichtsprozent, bedarfsweise er gänzt mit einem Halogenanteil von 15 bis 35 Gewichtsprozent, oder
- b2) mit einem Halogenanteil von 30 bis 50 Gewichtsprozent, und
- c) 35 bis 65 Gewichtsprozent phosphat- und/oder
halogenhaltiger Weichmacher, letzte
rer
- c1) mit einem Phosphatanteil von 5 bis 25 Gewichtsprozent und/oder
- c2) mit einem Halogenanteil von 25 bis 35 Gewichtsprozent.
- a) 10 to 20 percent by weight of polyether and / or polyester polyol,
- b) 30 to 50 percent by weight phosphate and / or halogen-containing polyether polyol, the latter
- b1) with a phosphate content of 10 to 20 percent by weight, if necessary it complements with a halogen content of 15 to 35 percent by weight, or
- b2) with a halogen content of 30 to 50 percent by weight, and
- c) 35 to 65 weight percent phosphate and / or halogenated plasticizer, last rer
- c1) with a phosphate content of 5 to 25 percent by weight and / or
- c2) with a halogen content of 25 to 35 percent by weight.