DE195400C - - Google Patents

Description

KAISERLICHESIMPERIAL

PATENTAMT.PATENT OFFICE.

Seitdem der weiße Phosphor der Giftigkeit wegen nicht mehr zur Herstellung von Zündwaren Verwendung finden darf, hat man vielfache Versuche gemacht, roten amorphen Phosphor zur Herstellung der Zündmassen zu verwenden. Man benutzte gewöhnlich eine Mischung aus amorphem Phosphor, Kaliumchlorat und einem Bindemittel, jedoch hat man bisher noch keine ZusammensetzungSince then the white phosphorus has not been used in the manufacture of igniters because of its toxicity May be used, multiple attempts have been made to red amorphous To use phosphorus for the production of the ignition masses. A mixture of amorphous phosphorus was usually used, Potassium chlorate and a binder, but no composition has yet been made

ίο gefunden, durch welche das Zündband sicher bei Reibung der Zündmasse entzündet wurde. Die meisten derartigen bekannten Zündmassen waren zu leicht entzündlich und brannten zu schnell ab, so daß die paraffinieren Bänder häufig nicht entflammten. Diesem Ubelstande suchte man dadurch zu begegnen, daß man Zündmassen von verschiedener Zusammensetzung übereinander auf das Zündband auftrug, was jedoch das Herstellungsverfahren der Bänder sehr umständlich und auch teuer machte. Der vorliegenden Erfindung gemäß wird die Zündmasse in einem ganz bestimmten Verhältnis der Bestandteile zusammengesetzt, wodurch man eine sicher und langsam brennende Masse erhält, die das paraffinierte Band sicher entzündet, dabei ist die Herstellung des Zündbandes sehr einfach. Das Verfahren besteht darin, daß man 1 kg amorphen Phosphors mit ungefähr 550 g Kaliumchlorat, 800 g Bleisuperoxyd und ungefähr 600 g Kreide in feinster Pulverform mit einer Lösung von Gummiarabikum, Dextrin oder Leim oder Tragantgummi in kaltem oder warmem Wasser zu einem flüssigen Brei vermischt. Die Substanzen werden durch andauerndes Rühren zu einer vollkommen homogenen Masse vermengt, welche dann in beliebiger Weise, beispielsweise mit Hilfe von Walzen, auf Bänder oder Papierstreifen aufgetragen werden kann. Die soweit fertiggestellten Bänder werden sodann getrocknet und mit einem Überzug aus hellem Lack, in dem Stearin, Paraffin o. dgl. enthalten ist, versehen, um dann nach abermaligem Trocknen in bekannter Weise aufgerollt zu werden.ίο found through which the detonating tape is secure was ignited by friction of the ignition mass. Most of such known priming masses were too flammable and burned off too quickly, so that the paraffinic ribbons often not inflamed. One tried to counteract this disadvantage by Applied ignition masses of different compositions one on top of the other to the ignition tape, However, this made the manufacturing process of the tapes very cumbersome and also expensive. According to the present invention the ignition mass is composed in a very specific proportion of the components, whereby one obtains a safe and slow burning mass that the paraffinized The tape is safely ignited, and the production of the ignition tape is very simple. The procedure consists in mixing 1 kg of amorphous phosphorus with about 550 g of potassium chlorate, 800 g lead peroxide and approx. 600 g chalk in the finest powder form with a solution of gum arabic, dextrin or Glue or gum tragacanth mixed in cold or warm water to form a liquid paste. The substances are through constant stirring to a completely homogeneous mass, which then in any way, for example with the help can be applied by rollers, to belts or strips of paper. The so far completed Tapes are then dried and covered with a light varnish, in the stearin, paraffin or the like. Is provided, to then after repeated drying to be rolled up in a known manner.

An Stelle des Bleisuperoxyds könnte man auch ein anderes Bleipräparat verwenden, welches leicht Sauerstoff abgibt, und ferner könnte man an Stelle der Kreide einen anderen Füllkörper, ζ. Β. Glaspulver, Bimsstein, Zinkoxyd ο. dgl., in Anwendung bringen.Instead of the lead peroxide one could also use another lead preparation, which gives off oxygen easily, and furthermore, instead of the chalk, one could use another Packing, ζ. Β. Glass powder, pumice stone, zinc oxide ο. Like., bring into use.

Claims (1)

Patent-Anspruch:Patent claim: Verfahren zur Herstellung von Zündbändern, dadurch gekennzeichnet, daß man ι kg amorphen Phosphor, ungefähr 550 g Kaliumchlorat, ungefähr 800 g Bleisuperoxyd oder ein anderes Bleipräparat und ungefähr 600 g eines Füllkörpers, wijs Kreide, Glaspulver usw., mit in Wasser gelöstem Gummiarabikum oder Dextrin oder Tragantgummi vermischt, die so erhaltene Zündmasse in üblicher Weise auf das Band aufträgt und dieses nach dem Trocknen mit einem Lack und eventuell Paraffin überzieht.Process for the production of ignition tapes, characterized in that one ι kg of amorphous phosphorus, about 550 g of potassium chlorate, about 800 g of lead peroxide or another lead preparation and about 600 g of a filler, wijs Chalk, glass powder, etc., mixed with gum arabic or dextrin or tragacanth gum dissolved in water, the so The ignition compound obtained is applied to the tape in the usual way and this after drying with a varnish and possibly paraffin coated.