DE1494544B - Composite three-dimensional crimped threads and cords and processes for their manufacture - Google Patents
Composite three-dimensional crimped threads and cords and processes for their manufactureInfo
- Publication number
- DE1494544B DE1494544B DE1494544B DE 1494544 B DE1494544 B DE 1494544B DE 1494544 B DE1494544 B DE 1494544B
- Authority
- DE
- Germany
- Prior art keywords
- fibers
- vinyl chloride
- shrinkage
- polymers
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
1 21 2
Die Erfindung betrifft zusammengesetzte dreidimen- eines der Polymeren eine größere reversible Längensionalgekräuselte Fäden und Fasern aus mindestens änderung als die andere Komponente aufweisen muß, zwei nebeneinander angeordneten Polymeren mit einer unterscheiden sich die Komponenten der erfindungsunterschiedlichen Wärmeschrumpfung, wobei alle in gemäßen Fäden bzw. Fasern durch eine verschiedene den Fäden bzw. Fasern enthaltenen Polymerkompo- 5 Wärmeschrumpfung.The invention relates to composite three-dimensional one of the polymers having a larger reversible longitudinally crimped one Threads and fibers must have at least one change than the other component, two polymers arranged next to one another with one, the components of the different ones according to the invention differ Heat shrinkage, all in accordance with threads or fibers through a different the filaments or fibers contained polymer composite 5 heat shrinkage.
nenten mindestens einen Teil des Querschnitts bilden, Zwischen reversibler Längenänderung und Wärme-elements form at least part of the cross-section, between reversible change in length and heat
sowie ein Verfahren zu ihrer Herstellung. schrumpfung besteht keine Beziehung, es sind vielmehrand a method for their production. Shrinkage is not a relationship, rather it is
Aus der USA.-Patentschrift 3 038 237 ist bereits ein bereits Produkte bekannt, bei denen eine verschiedene Verfahren zur Herstellung von gekräuselten und reversible Längenänderung trotz gleicher Schrumpfung kräuselfähigen zusammengesetzten Fäden durch Ex- io feststellbar ist.A product is already known from US Pat. No. 3,038,237 in which a different Process for producing curled and reversible change in length despite the same shrinkage crimpable composite threads can be determined by Ex- io.
trusion von einzelnen Polymeren durch eine gemein- Da es bisher nicht möglich war, unmodifizierte Vinyl-trusion of individual polymers through a common As it was previously not possible to use unmodified vinyl
same Öffnung, Strecken und Erhitzen der Fäden be- chloridpolymere in größerem Umfang für die Herkannt, um die Komponenten unterschiedlich zu stellung von Fäden und Fasern zu verwenden, bei schrumpfen und dadurch eine Kräuselung der Fäden denen es auf gute Schrumpfeigenschaften ankommt, zu bewirken. Eine der Komponenten der Polymeren 15 wird erfindungsgemäß ein erheblicher technischer muß mindestens 50 Milliäquivalente an ionisierbaren Fortschritt erreicht.the same opening, stretching and heating of the filaments of chlorinated polymers to a greater extent for the to use the components differently to position threads and fibers shrink and thereby crimp the threads which require good shrinkage properties, to effect. According to the invention, one of the components of the polymers 15 becomes a considerable technical one must have achieved at least 50 milliequivalents of ionizable progress.
Gruppen pro Kilogramm des Polymeren enthalten. Die Vinylchloridpolymerisatkomponenten der erfin-Contain groups per kilogram of polymer. The vinyl chloride polymer components of the invention
Diese Gruppen sind chemisch an die Polymerkette der dungsgemäßen Fäden unterscheiden sich voneinander genannten Komponente gebunden und in einem Quell- in ihren chemischen und/oder physikalischen Eigenmittel für die genannte Komponente ionisierbar, um 20 schäften und besitzen nach einer kurzen, entweder in eine reversible Längenänderung in der Komponente zu siedendem Wasser oder unter Dampf oder in irgendermöglichen, einer anderen heißen Flüssigkeit vorgenommenenThese groups are chemically attached to the polymer chain of the threads according to the invention differ from one another named component bound and in a source in their chemical and / or physical own resources ionizable for the mentioned component, around 20 shafts and after a short, either in a reversible change in length in the component under boiling water or under steam or in any way another hot liquid
Die notwendige unterschiedliche reversible Längen- Wärmebehandlung wegen der unterschiedlichen Eigenänderung zwischen den Komponenten wird leicht da- schäften ihrer Dimensionshaltigkeit gegenüber Wärme durch bewirkt, daß der Gehalt an ionisierbaren 25 eine Kräuselfähigkeit.The necessary different reversible length heat treatment because of the different intrinsic changes between the components it is easy to lose their dimensional stability against heat by causing the content of ionizable 25 a crimp ability.
Gruppen in den beiden Polymeren geändert wird. Die Der syndiotaktische Grad der Vinylchloridpolymeri-Groups in the two polymers is changed. The syndiotactic degree of vinyl chloride polymer
ionisierbaren Gruppen werden durch Copolymerisation satkomponenten der erfindungsgemäßen Fäden ist von Vinylpolymeren, wie Acrylnitril, ζ. B. mit Mono- durch das Absorptionsverhältnis der Infrarotbanden meren mit sauren oder basischen Gruppen geschaffen. D 635 und D 692 cm"1 bestimmt, wie in J. A. C. S.,ionizable groups are made by copolymerization of the threads according to the invention is made of vinyl polymers, such as acrylonitrile, ζ. B. created with mono- through the absorption ratio of the infrared bands mers with acidic or basic groups. D 635 and D 692 cm " 1 determined as in JACS,
Die Erfindung vermeidet die Notwendigkeit der 3° 82, S. 749, beschrieben ist. Als Vinylchloridhomopoly-Modifikation einer der Polymerkomponenten durch mere mit einem syndiotaktischen Grad von mehr als 1,6 die Zugabe von sauren oder basischen Gruppen. Erfin- können beispielsweise solche verwendet werden, die dungsgemäß sind die beiden als Komponenten ver- bei niedriger Temperatur und vorzugsweise bei etwa 0 wendeten Polymeren nicht modifizierte, hochsyndio- bis etwa -6O0C hergestellt worden sind, taktische Vinylchloridpolymere, deren syndiotaktischer 35 Es ist bekannt, daß die aus der Spinndüse austreten-Grad verschieden ist xmd die eine unterschiedliche den synthetischen Fasern glatt und gerade und damit Wärmeschrumpfung aufweisen. So sind zusammenge- für die anschließende Textilbehandlung, wie Karden, setzte dreidimensionalgekräuselte Fäden der eingangs Spinnen u. dgl., nicht geeignet sind, da die Fasern bebeschriebenen Art erfindungsgemäß dadurch gekenn- kanntlich für diese Behandlungen eine Art Wellung zeichnet, daß die Polymerkomponenten Vinylchlorid- 40 oder Kräuselung aufweisen müssen, homopolymere oder mindestens 85 Gewichtsprozent In der Textilindustrie sind zahlreiche Versuche unter-The invention avoids the necessity of the 3 ° 82, p. 749, is described. As a vinyl chloride homopoly modification of one of the polymer components by mers with a syndiotactic degree of more than 1.6 the addition of acidic or basic groups. In the invention, for example, those can be used which are the two polymers used as components at low temperature and preferably at about 0, unmodified, highly syndio- to about -6O 0 C, tactical vinyl chloride polymers whose syndiotactic 35 It is known that the degree of exit from the spinneret is different xmd which have a different smooth and straight synthetic fibers and thus heat shrinkage. For the subsequent textile treatment, such as carding, three-dimensional crimped threads of the initially spinning and the like are not suitable, since the fibers of the type described are characterized according to the invention for these treatments characterized in that the polymer components vinyl chloride 40 or crimp, homopolymeric or at least 85 percent by weight. In the textile industry, numerous attempts are under-
einpolymerisiertes Vinylchlorid enthaltende Copoly- nommen worden, eine gekräuselte synthetische Faser mere oder Polymerengemische mit mindestens 85 Ge- herzustellen, die das Aussehen von Naturfasern aufwichtsprozent Polyvinylchlorid verschiedenen syndio- weist und insbesondere der Wolle ähnelt. Dies ist bistaktischen Grades von mehr als 1,6 sind und die Fäden 45 her auf verschiedene Weise, beispielsweise durch oder Fasern eine Trockenfestigkeit von mehr als mechanisches Kräuseln der Fasern, erreicht worden. 2,5 g/den, eine Schrumpfung in siedendem Wasser von Die so erhaltene Kräuselung erfolgte jedoch nur in weniger als 2% und eine Schrumpfung in Trichlor- einer Ebene und war irreversibel, d. h., sie konnte nicht äthylen bei 40° C von weniger als 1 % aufweisen. wiederhergestellt werden, wenn sie bei der anschließen-A copolymer containing polymerized vinyl chloride, a crimped synthetic fiber to produce mers or polymer mixtures with at least 85 Ge, which weight percent the appearance of natural fibers Polyvinyl chloride has various syndio-shows and is particularly similar to wool. This is bistactic Degree of greater than 1.6 and the threads 45 forth in various ways, for example through or fibers have a dry strength greater than mechanical crimping of the fibers. 2.5 g / den, a shrinkage in boiling water of. However, the crimp obtained in this way only occurred in less than 2% and a shrinkage in trichloro one level and was irreversible, i.e. i.e., she couldn't have ethylene of less than 1% at 40 ° C. can be restored if they are
Durch eine solche Auswahl der Vinylchloridkompo- 50 den Textilbehandlung und beispielsweise beim Färben nenten wird nach gemeinsamer Extrusion, Strecken verschwindet.With such a selection of vinyl chloride composites, textile treatment and, for example, dyeing nenten is after common extrusion, stretching disappears.
und Erhitzen eine dreidimensionalgekräuselte Poly- Demgegenüber ist die dreidimensionale (d. h. spiral-and heating a three-dimensional curled poly- In contrast, the three-dimensional (i.e. spiral
vinylchloridfaser erhalten, die elastisch, beständig und förmige) Kräuselung der erfindungsgemäßen Fäden gleichförmig ist. dauerhaft und in jedem Maß reversibel und bringt einevinyl chloride fiber obtained, the elastic, stable and shaped) crimping of the threads according to the invention is uniform. permanent and reversible in every degree and brings a
Die zusammengesetzten dreidimensionalgekräusel- 55 ausgezeichnete Verarbeitbarkeit der Fäden bzw. Fasern ten Fäden der vorstehend gekennzeichneten Art wer- auf Textilmaschinen mit sich bzw. führt zu einem Garn den durch Verspinnen von mindestens zwei Polymeren mit hoher Deckfähigkeit, Weichheit und großem mit einer unterschiedlichen Wärmeschrumpfung durch Volumen.The composite three-dimensional crimped 55 excellent processability of the threads or fibers th threads of the type identified above are carried with them on textile machines or lead to a yarn that by spinning at least two polymers with high covering power, softness and large with a different heat shrinkage by volume.
die gleiche Öffnung einer Spinndüse, Strecken und an- Die für die Herstellung der erfindungsgemäßenthe same opening of a spinneret, stretching and an- die for the manufacture of the invention
schließende thermische Behandlung der Fasern zum 60 Fäden bzw. Fasern geeigneten Vinylchloridpolymeren Kräuseln hergestellt, wobei erfindungsgemäß als Poly- verschiedenen syndiotaktischen Grades von mehr als merkomponenten Vinylchloridhomopolymere oder 1,6 werden durch Polymerisation bei tiefer Temperatur mindestens 85 Gewichtsprozent einpolymerisiertes erhalten und ergeben Fäden bzw. Fasern mit einer Vinylchlorid enthaltende Copolymere oder Polymeren- Maßhaltigkeit in der Wärme, die von der Temperatur gemische mit mindestens 85 Gewichtsprozent Poly- 65 abhängt, bei der die Polymeren erhalten worden sind, vinylchlorid verschiedenen syndiotaktischen Grades In der Tabelle sind die Beziehungen aufgeführt, diesubsequent thermal treatment of the fibers to form vinyl chloride polymers suitable for 60 threads or fibers Crimping produced, according to the invention as poly- different syndiotactic degrees of more than merkomponenten vinyl chloride homopolymers or 1,6 are made by polymerization at low temperature at least 85 percent by weight polymerized and result in threads or fibers with a Copolymers or polymers containing vinyl chloride - dimensional stability in heat caused by temperature mixtures with at least 85 percent by weight of poly-65, in which the polymers have been obtained, vinyl chloride of various syndiotactic degrees The table shows the relationships that
von mehr als 1,6 verwendet werden. zwischen der Polymerisationstemperatur des PoIy-greater than 1.6 can be used. between the polymerization temperature of the poly
Während nach dem obigen bekannten Verfahren meren und der Schrumpfung der durch MaßspinnenWhile according to the above known method meren and the shrinkage by dimensional spinning
aus einer Cyclohexanlösung erhaltenen Fasern bestehen, die in ein aus einer Mischung von Cyclohexanon, Äthylalkohol und Wasser bestehendes Koagulationsbad extrudiert und anschließend in siedendem Wasser mit einem Streckverhältnis von 1: 8 gestreckt wurden.consist of a cyclohexane solution obtained fibers, which are in a mixture of cyclohexanone, Ethyl alcohol and water existing coagulation bath extruded and then in boiling Water at a draw ratio of 1: 8.
in siedendem Wassershrinkage
in boiling water
-1O0C
-150C
-30°C
-400C+ 5O 0 C
-1O 0 C
-15 0 C
-30 ° C
-40 0 C
etwa 15%
etwa 12%
etwa 10%
etwa 7 %about 50%
about 15%
about 12%
about 10%
about 7%
Die Schrumpfung wurde auf der Grundlage der Längsänderung in Prozent einer Garnsträhne gemessen, nachdem diese 5 Minuten in siedendes Wasser getaucht wurde, und zwar nach der Formel:The shrinkage was measured based on the percentage change in length of a strand of yarn, after immersing it in boiling water for 5 minutes, according to the formula:
Li-Lf LiLi-Lf Li
•100,• 100,
wobei Li die ursprüngliche Länge der Faser vor dem Eintauchen in Wasser und Lf die Länge der Faser nach dem 5minutigen Eintauchen in Wasser darstellt. Als Folge dieser unterschiedlichen Schrumpfung der Polyvinylchloridpolymeren in der Wärme kräuseln sich die entstandenen, zusammengesetzten Fasern bei Wärmebehandlung entsprechend der einzelnen Enden einheitlich in drei Dimensionen, wenn durch dieselbe Extrusionsöffnung der Spinndüse gleichzeitig zwei Spinnlösungen mit im wesentlichen gleicher Viskosität ; extrudiert werden, die jedoch aus zwei verschiedenen j Polymeren, beispielsweise das eine bei -4O0C und das j andere bei -150C erhalten, bestehen.where Li is the original length of the fiber before immersion in water and Lf is the length of the fiber after immersion in water for 5 minutes. As a result of this different heat shrinkage of the polyvinyl chloride polymers, the resulting composite fibers curl in three dimensions according to the individual ends uniformly in the heat treatment when two spinning solutions with essentially the same viscosity are simultaneously passed through the same extrusion opening of the spinneret; are extruded, which, however, consist of two different polymers, for example one obtained at -4O 0 C and the other at -15 0 C.
Während der Textilbehandlung neigt die Kräuselung wegen der Streckwirkung an den Enden dazu, zu ver-During the textile treatment, the crimp tends to become twisted because of the stretching action at the ends.
f/ schwinden, dies wird jedoch nach einer anschließenden Wärmebehandlung wie beispielsweise dem Färben oder einem einfachen Kochen oder Erwärmen völlig wieder aufgehoben.f / dwindle, but this will after a subsequent Heat treatment such as dyeing or simply boiling or heating completely again canceled.
Eine dauernde und reversible Kräuselung kannA permanent and reversible crimp can
! durch eine Wärmebehandlung oder in einer oder in mehreren aufeinanderfolgenden Phasen und durch abwechselndes Strecken in Abhängigkeit von den Behandlungen oder der nachfolgenden Verarbeitung erfolgen, die die so erhaltenen Fasern durchlaufen müssen.! by a heat treatment or in one or more successive phases and by alternating Routes are made depending on the treatments or subsequent processing, which the fibers thus obtained must pass through.
Dieses Verfahren wird gemäß der Erfindung unter Verwendung von zwei Vinylchloridpolymeren mit unterschiedlichem syndiotaktischem Grad dank der vollkommenen Verträglichkeit dieser Polymeren untereinander in befriedigender Weise durchgeführt.This process is carried out according to the invention using two vinyl chloride polymers with different syndiotactic degrees thanks to the perfect compatibility of these polymers with one another carried out in a satisfactory manner.
Nach einer bevorzugten und vorteilhaften Ausführungsform der Erfindung werden Lösungen zweier oder mehrerer Vinylchloridpolymerer mit hohem syndiotaktischem Grad, die bei verschiedenen Polymerisationstemperaturen erhalten worden sind, gleichzeitig entweder im Naß- oder im Trockenspinnverfahren versponnen und zur Bildung einer zusammengesetzten Faser, in der die verschiedenen Polymeren nebeneinanderliegen, anschließend gestreckt.According to a preferred and advantageous embodiment of the invention, solutions are two or several vinyl chloride polymers of high syndiotactic degree which are at different polymerization temperatures have been obtained, spun at the same time either in the wet or in the dry spinning process and to form a composite fiber in which the different polymers are juxtaposed, then stretched.
Es wurde gefunden, daß zur Herstellung einer dauerhaften Kräuselung in den erfindungsgemäßen Fäden bzw. Fasern vorteilhafterweise Vinylchloridpolymerisatkomponenten verwendet werden, die eine am extrudierten und gestreckten Polymeren bestimmte unterschiedliche Schrumpfung von mindestens 1% und vorzugsweise mindestens 2% besitzen. Außerdem hat es sich als zweckmäßig erwiesen, daß die zur Herstellung der erfindungsgemäßen Fäden bzw. FasernIt has been found that for producing a permanent crimp in the threads according to the invention or fibers advantageously vinyl chloride polymer components are used, which one on the extruded and stretched polymers determined different shrinkage of at least 1% and preferably have at least 2%. In addition, it has been found to be useful that the of the threads or fibers according to the invention
ίο verwendeten zwei oder mehreren Vinylchloridpolymeren
bei verschiedener Polymerisationstemperatur hergestellt worden sind. Diesbezüglich hat es sich als
vorteilhaft erwiesen, wenn das eine Vinylchloridpolymere durch Polymerisieren bei Temperaturen zwischen
—50 und —300C hergestellt worden ist, während das
andere Vinylchloridpolymere durch Polymerisieren bei einer Temperatur zwischen —20 und —10°C hergestellt
worden ist.
Die erfindungsgemäßen gekräuselten, zusammengesetzten Fasern weisen alle Vorteile von Polyvinylchloridfasern
mit hohem syndiotaktischem Grad im Vergleich zu normalem Polyvinylchlorid auf, wie beispielsweise
große Zähigkeit (mehr als 2,5 g/den), Schrumpfung in siedendem Wasser von weniger als
2 0J0, ausgezeichnete Widerstandsfähigkeit gegen zur
Trockenreinigung verwendete organische Lösungsmittel wie Trichloräthylen, Perchloräthylen usw. und
die Möglichkeit, mit beim Sieden dispergierten Farbstoffen zu färben.ίο used two or more vinyl chloride polymers have been prepared at different polymerization temperatures. In this respect it has proved to be advantageous if the has been a vinyl chloride polymers prepared by polymerizing at temperatures from -50 to -30 0 C, while the other vinyl chloride polymers prepared by polymerizing at a temperature between -20 and -10 ° C.
The crimped composite fibers of the present invention have all the advantages of polyvinyl chloride fibers with a high syndiotactic degree compared to normal polyvinyl chloride, such as high toughness (more than 2.5 g / den), boiling water shrinkage of less than 2 0 J 0 , excellent Resistance to organic solvents used for dry cleaning such as trichlorethylene, perchlorethylene, etc. and the possibility of coloring with dyes dispersed during boiling.
Zur besseren Erläuterung der vorliegenden Erfindung dienen die folgenden Beispiele, in denen die Fasern nach bekannten Verfahren erhalten werden.The following examples serve to better illustrate the present invention, in which the Fibers can be obtained by known methods.
. 100 Gewichtsteile Polyvinylchlorid mit hohem syndiotaktischem Grad, das durch Polymerisation von
Vinylchlorid bei -4O0C erhalten wurde und eine
grundmolare Viskositätszahl [η] = 1,3 g/dl aufweist, wurde unter 30 Minuten Rühren bei 1350C in 450 Gewichtsteilen
Cyclohexanon gelöst.
- 100 Gewichtsteile Polyvinylchlorid mit hohem syndiotaktischem Grad, das durch Polymerisieren von
Vinylchlorid bei —150C erhalten wurde und eine
grundmolare Viskositätszahl [η] = 1,5 g/dl aufweist, /wurde unter 30 Minuten Rühren bei 135°C in 400 Gewichtsteilen
Cyclohexanon gelöst.
Die beiden so erhaltenen Lösungen haben eine absolute Viskosität von etwa 50 Poise bei 130° C und werden
einer Spinndüse mit 80 Löchern von 150 μ Durchmesser zugeführt, so daß an jedem Loch die gleiche
Menge der beiden Polymeren vorliegt.
Die extrudierten Fäden werden in einem geeigneten Bad koaguliert. Nach dem Koagulieren wird das so erhaltene
Fadenbündel gewaschen, mit einem Streckverhältnis von 1: 7 gestreckt, auf die erforderliche
Größe gebracht und unter Spannung bei einer Temperatur zwischen 120 und 130° C getrocknet.. 100 parts by weight of polyvinyl chloride, syndiotactic degrees, obtained by polymerization of vinyl chloride at -4o 0 C and an intrinsic viscosity [η] = 1.3 g / has dl, was dissolved with stirring for 30 minutes at 135 0 C in 450 parts by weight of cyclohexanone .
- 100 parts by weight of polyvinyl chloride, syndiotactic degrees, obtained by polymerizing vinyl chloride at -15 0 C and an intrinsic viscosity [η] = 1.5 g / has dl / was stirring for 30 minutes at 135 ° C in 400 parts by weight Cyclohexanone dissolved.
The two solutions thus obtained have an absolute viscosity of about 50 poise at 130 ° C. and are fed to a spinneret with 80 holes of 150 μm diameter, so that the same amount of the two polymers is present at each hole.
The extruded filaments are coagulated in a suitable bath. After coagulation, the thread bundle obtained in this way is washed, stretched with a stretching ratio of 1: 7, brought to the required size and dried under tension at a temperature between 120 and 130.degree.
Die so erhaltene, kontinuierliche Faser zeigt:The continuous fiber thus obtained shows:
einen Titer von 240 dena titer of 240 den
eine Zähigkeit von 3,9 g/dena tenacity of 3.9 g / den
eine Bruchdehnung von 18 %an elongation at break of 18%
eine Schrumpfung in siedendem HoOa shrinkage in boiling HoO
von ".. 10%of 10%
Durch die Behandlung in siedendem Wasser bei freier Schrumpfung kräuseln sich die Fäden, und nachTreatment in boiling water with free shrinkage causes the threads to pucker, and gradually
dem Trocknen mit Heißluft von 6O0C wurden die
Kräuseleigenschaften geprüft, sie zeigen dann:
Zahl der Wellen pro Zentimeter .... 7drying with hot air at 6O 0 C were tested the crimp, then they show:
Number of waves per centimeter .... 7
Kräuselungsbetrag = 0,15Amount of curl = 0.15
wobeiwhereby
L2 = Länge des gestreckten Fadens,
L1 = Länge des gekräuselten Fadens.
Die mechanischen Eigenschaften der Fasern nach L 2 = length of the stretched thread,
L 1 = length of the crimped thread.
The mechanical properties of the fibers according to
dem Schrumpfen in siedendem Wasser für 30 Minuten sind folgende:shrinking in boiling water for 30 minutes are the following:
Titer 260 denTiter 260 den
Zähigkeit 3,2 g/denTenacity 3.2 g / den
Bruchdehnung 32%Elongation at break 32%
Schrumpfung in siedendem Wasser.. 0 %
Schrumpfung in Trichlorethylen beiShrinkage in boiling water .. 0%
Shrinkage in trichlorethylene
40°C 0,2%40 ° C 0.2%
Schrumpfung in Luft bei 130° C ... 4%Shrinkage in air at 130 ° C ... 4%
Ein Querschnitt einer Faser wurde unter dem Mikroskop geprüft, und es wurde festgestellt, daß alle Enden konjugiert sind und jeder Querschnitt etwa 50% des einen Polymeren und etwa 50% des anderen Polymeren beträgt.A cross section of a fiber was examined under a microscope and it was found that all Ends are conjugated and each cross section is about 50% of one polymer and about 50% of the other Polymers is.
Die so erhaltene Faser wurde dann im kalten Zustand mit einem Streckverhältnis von 1:1,15 gestreckt, um die Kräuselung zu entfernen. Es konnte gezeigt werden, daß durch eine anschließende Behandlung in siedendem Wasser die ursprüngliche Kräuselung praktisch wiederhergestellt werden konnte.The fiber thus obtained was then drawn in the cold state with a draw ratio of 1: 1.15, to remove the frizz. It could be shown that a subsequent treatment in The original ripple could practically be restored by boiling water.
100 Gewichtsteile Polyvinylchlorid mit hohem syndiotaktischem Grad, das durch Polymerisation von Vinylchlorid bei -300C erhalten wurde und eine grundmolare Viskositätszahl [η] = 1,5 g/dl aufweist, wurde unter 30 Minuten Rühren bei 135° C in 450 Gewichtsteilen Cyclohexanon gelöst.100 parts by weight of polyvinyl chloride, syndiotactic degrees, obtained by polymerization of vinyl chloride at -30 0 C and an intrinsic viscosity [η] = 1.5 g / has dl, was dissolved with stirring for 30 minutes at 135 ° C in 450 parts by weight of cyclohexanone .
100 Gewichtsteile Polyvinylchlorid mit hohem syndiotaktischem Grad, das durch Polymerisieren von Vinylchlorid bei — 100C erhalten wurde und eine grundmolare Viskositätszahl [η] = 1,7 g/dl aufweist, wurde unter 30 Minuten Rühren bei 135 0C in 400 Gewichtsteilen Cyclohexanon gelöst.100 parts by weight of polyvinyl chloride, syndiotactic degrees, obtained by polymerizing vinyl chloride at - 10 was obtained 0 C and an intrinsic viscosity [η] = 1.7 g / has dl, was dissolved with stirring for 30 minutes at 135 0 C in 400 parts by weight of cyclohexanone .
Die beiden Lösungen wurden durch eine Spinndüse mit 20 Löchern von 250 μ. Durchmesser gezogen. Die extrudierten Fäden wurden mit einem Streckverhältnis von 1: 6 gestreckt.The two solutions were through a spinneret with 20 holes of 250 μ. Diameter drawn. the extruded filaments were drawn with a draw ratio of 1: 6.
Die erhaltene Faser zeigte:The fiber obtained showed:
Titer 55 denTiter 55 den
Zähigkeit 3,8 g/denToughness 3.8 g / den
Bruchdehnung 20%Elongation at break 20%
Schrumpfung in siedendem H2O ... 12 %Shrinkage in boiling H 2 O ... 12%
Während der Behandlung in siedendem Wasser beiDuring the treatment in boiling water
freier Schrumpfung kräuselt sich der Faden und zeigt nach dem Trocknen mit Heißluft bei 60° C die gleichenfree shrinkage, the thread curls and shows after drying with hot air at 60 ° C the same
ίο Eigenschaften wie der gemäß Beispiel 1 erhaltene Faden.ίο Properties like that obtained according to Example 1 Thread.
Claims (2)
Family
ID=