DE10331474A1 - Vehicle component corrosion simulation method in which a component under test is placed in a test chamber that is used to simulate the engine space and a programmable controller used to control environmental test conditions - Google Patents
Vehicle component corrosion simulation method in which a component under test is placed in a test chamber that is used to simulate the engine space and a programmable controller used to control environmental test conditions Download PDFInfo
- Publication number
- DE10331474A1 DE10331474A1 DE2003131474 DE10331474A DE10331474A1 DE 10331474 A1 DE10331474 A1 DE 10331474A1 DE 2003131474 DE2003131474 DE 2003131474 DE 10331474 A DE10331474 A DE 10331474A DE 10331474 A1 DE10331474 A1 DE 10331474A1
- Authority
- DE
- Germany
- Prior art keywords
- test chamber
- temperature
- component
- chamber
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die Erfindung betrifft ein Verfahren zur Simulation der Korrosionsbelastung mit den im Oberbegriff des Patenanspruches 1 genannten Merkmalen sowie eine dazugehörige Vorrichtung mit den im Oberbegriff des Patenanspruches 8 genannten Merkmalen.The The invention relates to a method for simulating the corrosion load with the features mentioned in the preamble of claim 1 as well as an associated one Device with those mentioned in the preamble of claim 8 Features.
Um
die Korrosionsbeständigkeit
von Prüfteilen
gegenüber
feuchter und insbesondere salzhaltiger Luft zu ermitteln, ist es
gemäß der
Aus
der
Nachteilig ist, dass durch die Anordnung der Temperiereinrichtung innerhalb der Prüfkammer diese ebenfalls dem aggressiven salzhaltigen Nebel ausgesetzt ist. Um Schäden an der Temperiereinrichtung zu vermeiden, müssen diese aus korrosionsfestem Material hergestellt werden.adversely is that by the arrangement of the temperature control within the test chamber this is also exposed to the aggressive salty fog. To damage To avoid the tempering, they must be made of corrosion resistant Material to be produced.
Aus
der
Nachteilig ist, dass die Temperatur des Bauteils bei diesen Prüfverfahren nicht berücksichtigt wird, bei der das Bauteil einer tatsächlichen Belastung durch salzhaltige Flüssigkeiten ausgesetzt ist. Insbesondere die im Motorraumbereich eines Kraftfahrzeuges angeordneten Bauteile werden durch Kalt- und Warmstarts des Motors häufigen Temperaturwechseln ausgesetzt. Im Winterbetrieb werden diese Bauteile zusätzlich durch salzhaltiges Spritzwasser belastet, das entweder auf noch kalte oder bereits heiße Bauteile auftrifft. Das auf die heißen Bauteile auftreffende salzhaltige Spritzwasser wirkt stark korrosiv, so dass eine erhöhte Korrosionsbelastung auftritt. Mit den bekannten Verfahren und Vorrichtungen sind die in der Praxis eintretenden unterschiedlichen Umweltbelastungen der Bauteile im Motorraum eines Kraftfahrzeuges nicht reproduzierbar.adversely is that the temperature of the component in these test methods is not taken into account, in which the component of an actual Exposure to saline liquids is exposed. In particular, in the engine compartment of a motor vehicle arranged components are caused by cold and warm starts of the engine frequent Temperature changes exposed. In winter operation, these components additionally contaminated by salty spray that is either still on cold or already hot Components impinges. The saline on the hot components Splashing water is highly corrosive, resulting in increased corrosion occurs. With the known methods and devices are the in practice occurring different environmental pollution of the Components in the engine compartment of a motor vehicle not reproducible.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren und eine dazugehörige Vorrichtung zur Simulation der Korrosionsbelastung der im Motorraum eines Kraftfahrzeuges angeordneten und einer aggressiven Umweltbelastung ausgesetzten Bauteile zu schaffen, wobei realitätsnahe Einsatzbedingungen berücksichtigt werden sollen, um somit Rückschlüsse auf eine Alterung der Bauteile abzuleiten.Of the Invention is based on the object, a method and an associated device for simulating the corrosion load in the engine compartment of a motor vehicle arranged and exposed to an aggressive environmental impact To create components, taking into account realistic conditions of use should be in order to draw conclusions derive an aging of the components.
Diese Aufgabe wird entsprechend dem gattungsgemäßen Verfahren erfindungsgemäß durch die kennzeichnenden Merkmale des Patentanspruches 1 und entsprechend der gattungsgemäßen Vorrichtung erfindungsgemäß durch die kennzeichnenden Merkmale des Patentanspruches 8 gelöst.These Task is according to the generic method according to the invention by the characterizing features of claim 1 and corresponding the generic device according to the invention the characterizing features of claim 8 solved.
Erfindungsgemäß wird mittels einer programmierbaren Steuerung die Umgebungstemperatur in der Prüfkammer derart regelbar eingestellt, dass sie dem Temperaturverlauf des zu prüfenden Bauteils während des Betriebs des Motors entspricht und dass mittels der programmierbaren Steuerung die Sprühdüsen derart angesteuert werden, dass in vorgegebenen Zeitintervallen das Bauteil mit Sprühflüssigkeit besprüht wird. Die Prüfkammer ist dabei in einer Klimakammer angeordnet, in der der Temperaturverlauf des Bauteils den realitätsnahen Bedingungen angepasst wird.According to the invention by means of a programmable controller the ambient temperature in the test chamber adjusted so that they match the temperature profile of to be tested component while corresponds to the operation of the engine and that by means of programmable Control the spray nozzles so be controlled that at predetermined time intervals, the component with spray liquid sprayed becomes. The test chamber is arranged in a climatic chamber in which the temperature profile of the component the realistic Conditions is adjusted.
Der Vorteil der erfindungsgemäßen Lösung besteht darin, dass in der Prüfkammer realitätsnahe Umweltverhältnisse eingestellt werden, die den tatsächlichen Belastungen der Bauteile im Motorraum eines Fahrzeuges während dessen Betriebs durch Salz- und Spritzwasser nahezu entsprechen. Mit dem vorgeschlagenen Verfahren und der dazugehörigen Vorrichtung lassen sich auch die Belastungen der Bauteile durch aggressive Umwelteinflüsse während den Temperaturwechseln durch Kalt- und Warmlaufphasen des Motors ermitteln und entsprechend darstellen. Außerdem besteht die Möglichkeit, Fahrzeugkomponenten unter realitätsnahen Bedingungen im Zeitraffer altern zu lassen, um daraus Erkenntnisse hinsichtlich ihrer Lebensdauer zu erhalten. Durch Einstellung entsprechender Temperaturverhältnisse in der Klimakammer lassen sich an den zu untersuchenden Bauteilen Temperaturbelastungen zwischen –40°C bis +150°C verwirklichen.The advantage of the solution according to the invention is that in the test chamber realistic environmental conditions are set, which did the neural loads of the components in the engine compartment of a vehicle during its operation by salt and spray almost match. With the proposed method and the associated device, the stresses of the components can be determined by aggressive environmental influences during the temperature changes by cold and warm-up phases of the engine and represent accordingly. In addition, it is possible to age vehicle components under real-life conditions in fast motion in order to obtain information about their service life. By setting the appropriate temperature conditions in the climate chamber, temperature loads between -40 ° C and + 150 ° C can be achieved on the components to be examined.
Ein weiterer Vorteil der erfindungsgemäßen Lösung besteht darin, dass in der Prüfkammer auch Untersuchungen von einzelnen Bauteilen durchgeführt werden können. Es ist nicht erforderlich, für entsprechende Prüfungen jeweils ein komplettes Fahrzeug einem Test zu unterziehen. Die Bedingungen, denen das Bauteil während des normalen Betriebs ausgesetzt ist, können in der Prüfkammer entsprechend eingestellt werden. Außerdem lassen sich durch die erfindungsgemäße Lösung bei reproduzierbaren Prüfbedingungen kürzere Prüfzeiten realisieren, da die unterschiedlichen Betriebsbedingungen ohne Umbau in der Simulationsanlage durchgeführt werden können.One Another advantage of the solution according to the invention is that in the test chamber also investigations of individual components are carried out can. It is not necessary for appropriate tests in each case to subject a complete vehicle to a test. The conditions that the component during exposed to normal operation, may be in the test chamber be adjusted accordingly. In addition, let through the inventive solution reproducible test conditions shorter testing times realize because the different operating conditions without conversion can be performed in the simulation system.
Weitere vorteilhafte Ausgestaltungen sind in den Unteransprüchen beschrieben, sie werden in der Beschreibung zusammen mit ihren Wirkungen erläutert.Further advantageous embodiments are described in the subclaims, they are explained in the description together with their effects.
Nachfolgend wird die Erfindung anhand eines Ausführungsbeispiels der Erfindung näher beschrieben. In der dazugehörigen Zeichnung ist schematisch eine Vorrichtung zur Simulation der Korrosionsbelastung an Bauteilen dargestellt.following the invention is based on an embodiment of the invention described in more detail. In the corresponding Drawing is schematically a device for simulating the corrosion load represented on components.
Die erfindungsgemäße Lösung wird erläutert am Beispiel der Simulation der Korrosionsbelastung an Bauteilen, die im Motorraum eines Kraftfahrzeuges den aggressiven Umweltbelastungen ausgesetzt sind. Die erfindungsgemäße Lösung ist aber nicht auf dieses Beispiel eingeschränkt. Sie lässt sich überall dort anwenden, wo eine Ermittlung der Korrosionsbelastung von Bauteilen durch aggressive Umweltbedingungen sinnvoll ist.The solution according to the invention explained on Example of the simulation of the corrosion load on components, the in the engine compartment of a motor vehicle the aggressive environmental pollution are exposed. The solution according to the invention is not on this Example restricted. She lets Everywhere apply where an investigation of the corrosion load of components makes sense through aggressive environmental conditions.
Die
erfindungsgemäße Vorrichtung
zur Simulation der Korrosionsbelastungen an Bauteilen
In
die Prüfkammer
Es
besteht auch die Möglichkeit,
dass die Spüldüsen
Weiterhin
ist innerhalb der Prüfkammer
Zur
Absaugung der in der Prüfkammer
Die Wirkungsweise der erfindungsgemäßen Vorrichtung wird nachfolgend im Zusammenhang mit dem erfindungsgemäßen Verfahren näher erläutert.The Mode of operation of the device according to the invention is hereinafter in connection with the method according to the invention explained in more detail.
Es wird angenommen, dass ein Fahrzeug bei einer Außentemperatur von –5°C gestartet wird. Das bedeutet, dass im Motorraum bei kaltem Motor die Bauteile ebenfalls eine Temperatur von –5°C haben. Durch die Inbetriebnahme des Motors wird dieser langsam mit an sich bekannten Aufheizgradienten auf Betriebstemperaturen von ca. 70°C erwärmt. Gleichzeitig erfolgt auch eine Erwärmung der im Motorraum angeordneten Bauteile mit ebenfalls bekannten Aufheizgradienten. Nach einer bestimmten Zeit durchfährt das Fahrzeug eine salzhaltige Wasserlache. Der Motor und die im Motorraum befindlichen Anbauteile werden mit Salzwasser bespritzt. Das Fahrzeug fährt weiter, wobei an den heißen Bauteilen eine Trocknung des Salzwassers stattfindet.It is assumed that a vehicle is started at an outside temperature of -5 ° C. This means that in the engine compartment when the engine is cold, the components also have a temperature of -5 ° C. By putting the motor into operation, it is slowly heated up to operating temperatures of about 70 ° C. with heating gradients known per se. At the same time there is also a heating of arranged in the engine compartment components also known th heating gradient. After a certain time, the vehicle passes through a salty water pool. The engine and attachments in the engine compartment are splashed with salt water. The vehicle continues, with salt water drying on the hot components.
Dieser
oben beschriebene Vorgang wird erfindungsgemäß in der Prüfkammer
Nach
einer vorgegebenen Zeit wird eine salzhaltige Sprühflüssigkeit über die
von der Steuerung
Erfindungsgemäß sind die
Temperaturen in der Prüfkammer
- 11
- Klimakammerclimatic chamber
- 22
- Prüfkammertest chamber
- 33
- Ventilatorfan
- 44
- Sprühdüsespray nozzle
- 55
- Spüldüserinsing nozzle
- 66
- Heiz- und Kühleinrichtungheating and cooling device
- 77
- Steuerungcontrol
- 88th
- TemperaturmessfühlerTemperature sensor
- 99
- TemperaturmessfühlerTemperature sensor
- 1010
- Abzugsrohrexhaust pipe
- 1111
- Bauteilcomponent
- 1212
- Gitterrostgrating
- 1313
- PrüfteilträgerPrüfteilträger
- 1414
- Datenleitungdata line
- 1515
- Datenleitungdata line
- 1616
- Steuerleitungcontrol line
- 1717
- Steuerleitungcontrol line
- 1818
- Steuerleitungcontrol line
- 1919
- Hochdruckpumpehigh pressure pump
- 2020
- Magnetventilmagnetic valve
- 2121
- Steuerleitungcontrol line
- 2222
- Steuerleitungcontrol line
Claims (16)