DE102007055667A1 - Arc extinguishing-resin molded body, useful for extinguishing electric arc in the circuit breaker, comprises a resin composition comprising a polyolefin resin, and a reactive, organic phosphorus based flame retardant

Info

Publication number: DE102007055667A1
Application number: DE102007055667A
Authority: DE
Inventors: Hironori Hino Yanase; Toshiyuki Hino Kanno; Syuichi Hino Sugiyama; Kiyotaka Fuchu Shigehara
Original assignee: Fuji Electric Holdings Ltd
Current assignee: Fuji Electric Co Ltd
Priority date: 2006-11-21
Filing date: 2007-11-21
Publication date: 2008-05-29
Anticipated expiration: 2027-11-22
Also published as: DE102007055667B4; CN101186728B; JP2008130375A; JP4817316B2; CN101186728A

Abstract

Arc extinguishing-resin molded body comprises a resin composition comprising: a polyolefin resin (A), in which a portion of the hydrogen atom in a methyl chain is substituted by hydroxyl group (0.2-0.7 mole, 1 mole of the methyl groups), and a reactive, organic phosphorus based flame retardants (B) with an unsaturated terminal bond, where the resin molded body, after a shaping process, is exposed to an irradiation for its cross-linkage. An independent claim is included for a circuit breaker comprising: a fixed contact section (5) with a fixed contact piece (7); movable contact section (1) with a movable contact piece (6) to contact the fixed contact section and for the development of closing- and opening processes with the fixed contact section; and an arc extinguishing-device, which extinguishes the opening- and closing processes between the fixed contact section and the movable contact section of formed arc.

Description

Technisches Gebiet der ErfindungTechnical field of the invention

Die vorliegende Erfindung betrifft einen Lichtbogenlösch-Harzformkörper mit flammhemmenden Eigenschaften, der zum Auslöschen eines elektrischen Lichtbogens, der ausgehend von Kontaktteilen bei Stromunterbrechung in einem Trennschalter oder dergl. entsteht, verwendet wird, sowie einen Trennschalter unter Verwendung des Lichtbogenlösch-Harzformkörpers.The The present invention relates to an arc extinguishing resin molded article having Flame-retardant properties, the extinguishing an electric arc, the starting of contact parts in case of power interruption in one Disconnector or the like arises, is used, as well as a Disconnector using the arc extinguishing resin molding.

Hintergrund der ErfindungBackground of the invention

Ein elektrischer Lichtbogen entsteht zwischen einem Kontaktstück eines beweglichen Kontaktabschnitts und einem Kontaktstück eines fixierten Kontaktabschnitts eines Trennschalters, wenn die Kontaktstücke mit hindurchfließendem Überstrom oder Nennstrom geöffnet werden. Um den Lichtbogen auszulöschen, wird im allgemeinen ein Trennschalter mit einem Lichtbogenlösch-Bauelement vorgesehen, das eine Lichtbogen-Kammer aufweist, die aus einem Lichtbogenlösch-Element rings um den Lichtbogenerzeugungsort besteht. Das Lichtbogenlösch-Element wird thermisch durch den Lichtbogen zersetzt und das durch die thermische Zersetzung aus dem Lichtbogenlösch-Element erzeugte Gas löscht den Lichtbogen aus.One electric arc is formed between a contact piece of a movable contact portion and a contact piece of a fixed contact portion of a circuit breaker when the contacts with flowing overcurrent or rated current open become. To extinguish the arc, will In general, a circuit breaker provided with an arc extinguishing component, which has an arc chamber consisting of an arc extinguishing element around the arc generation place exists. The arc extinguishing element is thermally decomposed by the arc and that by the thermal Decomposition from the arc extinguishing element generated gas extinguishes the arc out.

Vorwiegend verwendete Matrixharze des Lichtbogenlösch-Elements umfassen hitzehärtende Harze wie ungesättigte Polyesterharze (Patentdokument 1) und Melaminharze (Patentdokument 2) und thermoplastische Harze, wie Polyolefinharze, Polyamidharze und Polyacetalharze (Patentdokument 3).mainly used matrix resins of the arc-extinguishing element include thermosetting resins such as unsaturated Polyester resins (Patent Document 1) and melamine resins (Patent Document 2) and thermoplastic resins such as polyolefin resins, polyamide resins and polyacetal resins (Patent Document 3).

Hitzehärtende Harze sind jedoch insofern mit einem Problem behaftet, als ihre Formgebungseigenschaften schlechter als die von thermoplastischen Harzen sind, da das hitzehärtende Harz beim Formgebungsverfahren zur Bildung eines Grats (mold flash) neigt. Beim Lichtbogen-Auslöschungsvorgang erhöht das durch thermische Zersetzung aus dem Lichtbogenlösch-Element erzeugte Gas den Druck im Lichtbogenlösch-Bauelement. Das hitzehärtende Harz, das eine geringe Druckfestigkeit aufweist und leicht bricht, während es eine relativ hohe Härte besitzt, eignet sich kaum zur Miniaturisierung des Lichtbogenlösch-Bauelements.Thermosetting resins however, have a problem insofar as their shaping properties worse than that of thermoplastic resins, since the thermosetting resin in the molding process for forming a mold flash. In the arc extinguishing process elevated by thermal decomposition from the arc extinguishing element Gas generated the pressure in the arc extinguishing component. The thermosetting resin, which has a low compressive strength and breaks easily while it is a relatively high hardness own, hardly suitable for miniaturization of the arc extinguishing component.

Andererseits weisen thermoplastische Harze, bei denen es kaum zur Gratbildung kommt, eine geringere Festigkeit, eine geringere Druckbeständigkeit und eine geringere Wärmebeständigkeit auf, so dass das Lichtbogenlösch-Element im Laufe der Zeit zur Verformung oder Zersetzung neigt. Ein thermoplastisches Harz, das zahlreiche aromatische Ringe enthält, wie ein aromatisches Polyamidharz, weist eine relativ hohe Festigkeit, hohe Druckbeständigkeit und hohe Wärmebeständigkeit auf, gibt jedoch bei der Verbrennung leicht freien Kohlenstoff ab. Infolgedessen kann das Lichtbogenlösch-Bauelement durch Kohlenstoff verunreinigt und in Bezug auf die elektrische Isolierung beeinträchtigt werden.on the other hand have thermoplastic resins, which hardly burrs comes, a lower strength, a lower pressure resistance and lower heat resistance on, leaving the arc extinguishing element over time tends to deform or decompose. A thermoplastic resin, containing numerous aromatic rings, such as an aromatic polyamide resin, has a relatively high strength, high pressure resistance and high heat resistance but gives off easily carbon during combustion. As a result, the arc extinguishing component can be replaced by carbon contaminated and impaired in terms of electrical insulation.

Zur Verbesserung der Festigkeit, der Druckbeständigkeit und der Wärmebeständigkeit der thermoplastischen Harze und der hitzehärtenden Harze wurden einige Versuche unternommen (Patentdokumente 1 bis 4), wobei im Harz ein anorganisches Füllstoffmaterial, wie verstärkende Fasern, enthalten sind. Durch Erhöhung des Anteils an anorganischen Füllstoffen nimmt jedoch die Menge des durch thermische Zersetzung erzeugten Gases ab, woraus die Schwierigkeit entsteht, dass das Lichtbogen-Auslöschungsverhalten beeinträchtigt wird.to Improvement of strength, pressure resistance and heat resistance the thermoplastic resins and the thermosetting resins became some Attempts (Patent Documents 1 to 4), wherein in the resin inorganic filler material, like reinforcing Fibers are included. By increasing the proportion of inorganic fillers However, it takes the amount of thermal decomposition generated Gases from which the difficulty arises that the arc extinguishing behavior impaired becomes.

Das Patentdokument 5 beschreibt einen Trennschalter unter Verwendung eines Harzformkörpers, der durch Elektronenbestrahlung von thermoplastischen Harzen, wie Polyestern und Polyamiden, erhalten wird.The Patent Document 5 describes a circuit breaker using a resin molding, by electron irradiation of thermoplastic resins, such as Polyesters and polyamides.

In letzter Zeit werden an den Grad der flammhemmenden Beschaffenheit, die für in Trennschaltern verwendete Harzmaterialien erforderlich ist, höhere Anforderungen gestellt. Um diese Anforderungen zu erfüllen, ist die Verwendung eines flammhemmenden Harzes als Matrixharz eines lichtbogenlöschenden Materials denkbar. Es ist bekannt, dass eine Verbindung mit einem Gehalt an einem Halogen, wie Brom, in einem Harz zur Erzielung einer flammhemmenden Beschaffenheit wirksam ist. Harze mit einem Gehalt an Additiven in Form einer Halogenverbindung werden für flammhemmende Harze für allgemeine Zwecke verwendet. Jedoch kann ein flammhemmendes Harz, das eine große Menge an einer Halogenverbindung enthält, unter bestimmten Verbrennungsbedingungen Dioxin erzeugen. Im Hinblick auf die Belastung der Umwelt wird seit einigen Jahren die Verwendung eines halogenfreien flammhemmenden Harzes, in dem keine Halogenverbindung enthalten ist, verlangt.In lately, the degree of flame-retardant nature, the for In resin circuit breakers used resin materials is required, higher requirements posed. To meet these requirements, the use of a flame retardant resin as the matrix resin of an arc extinguishing Materials conceivable. It is known that a connection with a Content of a halogen, such as bromine, in a resin to obtain a flame retardant nature is effective. Resins with a salary of additives in the form of a halogen compound are used for flame-retardant Resins for used for general purposes. However, a flame retardant resin, that's a big one Contains amount of a halogen compound, under certain combustion conditions Produce dioxin. With regard to the burden on the environment is going on some years ago the use of a halogen-free flame retardant Resin, in which no halogen compound is included, requires.

Patentdokument 1Patent Document 1

Japanisches Patent3098042 und entsprechende Patentveröffentlichungen in anderen Ländern: US-Patent 6 046 258 , DE-Patent 69717433 und EP-Patent 0 897 955 . Japanese Patent 3098042 and related patent publications in other countries: U.S. Patent 6,046,258 . DE patent 69717433 and European Patent 0 897 955 ,

Patentdokument 2Patent Document 2

Japanische Offenlegungsschrift H02-256110 . Japanese Laid-Open Patent H02-256110 ,

Patentdokument 3Patent Document 3

Japanische Offenlegungsschrift H07-302535 und entsprechende Patentveröffentlichungen in anderen Ländern: US-Patent 5 841 088 , EP-A-0 694 940 und CN-1 124 402 . Japanese Laid-Open Patent H07-302535 and related patent publications in other countries: U.S. Patent 5,841,088 . EP-A-0 694 940 and CN-1 124 402 ,

Patentdokument 4Patent Document 4

Japanische Offenlegungsschrift H08-171847 und entsprechende Patentveröffentlichungen in anderen Ländern: US-Patent 6 361 848 , DE-Patent 69532063 , EP-Patent 0 718 356 und CN-Patent 1 169 866 . Japanese Laid-Open Patent H08-171847 and related patent publications in other countries: U.S. Patent 6,361,848 . DE patent 69532063 . European Patent 0 718 356 and CN patent 1 169 866 ,

Patentdokument 5Patent Document 5

Die internationale Patentanmeldung WO-2003-044818 und entsprechende Patentveröffentlichungen in anderen Ländern: EP-A-1 475 817 und CN-Patent 1 255 839 .The international patent application WO-2003-044818 and related patent publications in other countries: EP-A-1 475 817 and CN Patent 1 255 839 ,

Offenbarung der ErfindungDisclosure of the invention

Durch die Erfindung zu lösende AufgabenProblems to be solved by the invention

Durch Vernetzungsbehandlung eines thermoplastischen Harzes wird zwar eine gewisse Verbesserung in Bezug auf Festigkeit, Wärmebeständigkeit und Druckbeständigkeit festgestellt, jedoch verbessert sich das Lichtbogen-Auslöschungsverhalten nicht. Ferner wird der Druckanstieg im Lichtbogenlösch-Bauelement aufgrund des durch thermische Zersetzung erzeugten Gases beim Auslöschungsvorgang kaum unterdrückt und das Lichtbogenlösch-Bauelement geht aufgrund des Druckanstiegs beim Lichtbogen-Auslöschungsvorgang leicht zu Bruch. Ferner gehört die flammhemmende Beschaffenheit noch zu den ungelösten Problemen.By Although crosslinking treatment of a thermoplastic resin becomes a some improvement in terms of strength, heat resistance and pressure resistance however, the arc extinguishing behavior improves Not. Further, the pressure increase in the arc extinguishing component due the gas generated by thermal decomposition in the extinguishing process hardly suppressed and the arc extinguishing component due to the pressure increase in the arc extinguishing process easy to break. Furthermore belongs the flame-retardant texture still to the unsolved problems.

Eine Aufgabe der Erfindung besteht daher in der Bereitstellung eines Lichtbogenlösch-Harzformkörpers, das ein thermisches Zersetzungsgas bei einem geringen Druckanstieg und mit hohem Wirkungsgrad beim Auslöschen eines elektrischen Lichtbogens, der beim Ausschalten entsteht, erzeugt, wobei der Formkörper gegen den beim Ausschaltvorgang auftretenden Temperaturanstieg und Druckanstieg beständig ist und eine gute flammhemmende Beschaffenheit aufweist. Eine weitere Aufgabe besteht in der Bereitstellung eines Trennschalters unter Verwendung des Lichtbogenlösch-Harzformkörpers.A The object of the invention is therefore to provide a Arc quenching resin molding, the a thermal decomposition gas at a small pressure rise and with high efficiency at extinction of an electric arc generated when it is switched off, wherein the shaped body against the temperature rise occurring during the switch-off and Pressure increase resistant is and has a good flame retardant nature. Another Task is to provide a circuit breaker under Use of the arc extinguishing resin molding.

Lösung der AufgabenSolution of the tasks

Zur Lösung der vorstehenden Aufgaben umfasst ein erfindungsgemäßer Lichtbogenlösch-Harzformkörper eine Harzzusammensetzung, die ein Polyolefinharz (A) enthält, bei dem ein Teil der Wasserstoffatome in einer Methylenkette durch Hydroxylgruppen ersetzt ist und die Hydroxylgruppen in einer Menge im Bereich von 0,2 bis 0,7 Mol, bezogen auf 1 Mol Methylengruppen, enthalten sind, wobei die Harzzusammensetzung ferner ein reaktives, organisches flammhemmendes Mittel auf Phosphorbasis (B) enthält, das eine ungesättigte Endbindung aufweist, wobei der Harzformkörper nach dem Formgebungsverfahren einer Bestrahlung zur Vernetzung unterworfen wird.to solution The above objects include an arc extinguishing resin molded body according to the present invention A resin composition containing a polyolefin resin (A) at a part of the hydrogen atoms in a methylene chain by hydroxyl groups is replaced and the hydroxyl groups in an amount ranging from 0.2 to 0.7 mol, based on 1 mol of methylene groups, are included, wherein the resin composition further comprises a reactive, organic Phosphorus-based flame retardant (B) containing an unsaturated end bond wherein the resin molded body after the molding process, subjected to irradiation for crosslinking becomes.

Im vorstehend beschriebenen Lichtbogenlösch-Harzformkörper werden Vernetzungen in einer dreidimensionalen Netzkonfiguration durch chemische Reaktion zwischen den ungesättigten Endbindungen des reaktiven, organischen flammhemmenden Mittels auf Phosphorbasis (B) und dem Polyolefinharz (A) unter Zuhilfenahme von Bestrahlung gebildet. Infolgedessen werden die flammhemmenden Komponenten in stabiler Weise in das Harz eingebaut. Daher kommt es kaum zu einem Ausbluten des flammhemmenden Mittels und die flammhemmende Beschaffenheit lässt sich für eine lange Zeitspanne aufrechterhalten. Da die Vernetzungen in der dreidimensionalen Netzkonfiguration im Polyolefinharz (A) ausgebildet werden, werden auch die Festigkeit, die Wärmebeständigkeit und die Druckbeständigkeit verbessert.in the above-described arc extinguishing resin moldings Networking in a three-dimensional network configuration chemical reaction between the unsaturated end bonds of the reactive, organic phosphorus based flame retardant (B) and the Polyolefin resin (A) formed with the aid of irradiation. As a result, the flame-retardant components become stable built into the resin. Therefore, it hardly comes to a bleeding of the Flame retardant and the flame retardant texture can be for one maintained for a long period of time. Because the interconnections in the three-dimensional Network configuration can be formed in the polyolefin resin (A), are also the strength, the heat resistance and the pressure resistance improved.

Das Polyolefinharz (A), das eine Seitenketten-OH-Gruppe aufweist, die einer Dissoziation durch Pyrolyse zugänglich ist, erzeugt ein thermisches Zersetzungsgas, das Wasserstoffgas, H₂O, O₂ und O in hoher Konzentration enthält und somit den Lichtbogen sofort auslöscht. Das Polyolefinharz (A), das Komponenten, wie Teer, die wenig zur Lichtbogen-Auslöschungsfunktion beitragen, in geringer Konzentration enthält, steuert den Druckanstieg im Lichtbogenlösch-Bauelement. Ferner kommt es beim Vorgang der Lichtbogenauslöschung kaum zu einem Verkleben der Komponenten im Lichtbogenlösch-Bauelement. Daher wird die elektrische Isolierung im Lichtbogenlösch-Bauelement gewährleistet.The polyolefin resin (A) having a side chain OH group which is susceptible to dissociation by pyrolysis generates a thermal decomposition gas containing hydrogen gas, H ₂ O, O ₂ and O in a high concentration, thus extinguishing the arc immediately. The polyolefin resin (A), which contains components such as tars that contribute little to the arc extinguishing function in low concentration, controls the pressure increase in the arc extinguishing device. Furthermore, it hardly comes in the process of arc extinction to stick the components in the arc extinguishing component. Therefore, the electrical insulation in the arc extinguishing component is ensured.

Vorzugsweise enthält die Harzzusammensetzung im erfindungsgemäßen Lichtbogenlösch-Harzformkörper ein Polyacetalharz (C) in einer Menge von 5 bis 90 Gew.-teilen, bezogen auf 100 Gew.-teile des Polyolefinharzes (A), wobei das Polyacetalharz (C) von Oxyethylen abgeleitete Struktureinheiten in einem Anteil von 75 bis 100 Mol-% enthält. Obgleich ein Polyacetalharz im allgemeinen ein thermisches Zersetzungsgas erzeugt, das in Bezug auf die Lichtbogenauslöschung sehr wirkungsvoll ist, ergeben sich Schwierigkeiten bei der Formgebung durch Schmelzkneten, d. h. es weist ein schlechtes Formgebungsverhalten auf. Da ein Polyacetalharz reichliche Mengen an thermischem Zersetzungsgas erzeugt, was einen relativ großen Beitrag zum Druckanstieg ergibt, besteht die Tendenz, dass der Druck im Lichtbogenlösch-Bauelement ansteigt. Bei diesem Aspekt der Erfindung wird jedoch das Polyolefinharz (A) in Kombination mit einem Polyacetalharz (C) verwendet, so dass das Lichtbogen-Auslöschungsverhalten verbessert wird, ohne dass die Formgebungseigenschaften der Harzzusammensetzung beeinträchtigt werden.Preferably contains the resin composition in the arc extinguishing resin molded article of the present invention Polyacetal resin (C) in an amount of 5 to 90 parts by weight, based to 100 parts by weight of the polyolefin resin (A), wherein the polyacetal resin (C) oxyethylene derived structural units in a proportion of Contains 75 to 100 mol%. Although a polyacetal resin generally generates a thermal decomposition gas, that is very effective in arc extinguishing, Difficulties in shaping due to melt kneading, d. H. it has a poor shaping behavior. As a polyacetal resin Generated abundant amounts of thermal decomposition gas, which is a relatively large Contribution to the pressure increase, there is a tendency that the pressure in the arc extinguishing component increases. However, in this aspect of the invention, the polyolefin resin becomes (A) used in combination with a polyacetal resin (C), so that the arc extinction behavior is improved without the molding properties of the resin composition impaired become.

Vorzugsweise enthält die Harzzusammensetzung im erfindungsgemäßen Lichtbogenlösch-Harzformkörper einen oder mehrere Typen eines anorganischen Füllstoffes (D), der aus der Gruppe ausgewählt ist, die aus Glasfasern, Bariumtitanat-Whiskers, feinen Kieselgelteilchen, Boehmit, Talcum, Magnesiumcarbonat und einem Metallhydroxid besteht, und zwar in einer Menge von 1 bis 70 Gew.-%. Gemäß diesem Aspekt der Erfindung werden die Festigkeit und die Druckbeständigkeit des Harzformkörpers erhöht.Preferably contains the resin composition in the arc-quenching resin molded article of the present invention or several types of inorganic filler (D) derived from the Group selected made of glass fibers, barium titanate whiskers, fine particles of silica gel, Boehmite, talcum, magnesium carbonate and a metal hydroxide, and in an amount of 1 to 70 wt .-%. According to this aspect of the invention the strength and the pressure resistance of the resin molding are increased.

Vorzugsweise weist das Polyolefinharz (A) im erfindungsgemäßen Lichtbogenlösch-Harzformkörper eine latente Zersetzungswärme von mindestens 30 cal/g auf.Preferably For example, the polyolefin resin (A) in the arc-quench resin molded article of the present invention has one latent decomposition heat of at least 30 cal / g.

Vorzugsweise handelt es sich beim Polyolefinharz (A) im erfindungsgemäßen Lichtbogenlösch-Harzformkörper um ein Ethylen-Vinylalkohol-Copolymeres.Preferably is the polyolefin resin (A) in the inventive arc extinguishing resin molded body to an ethylene-vinyl alcohol copolymer.

Gemäß diesen Aspekten der Erfindung wird ein thermisches Zersetzungsgas mit hervorragendem Lichtbogen-Auslöschungsvermögen zur sofortigen Lichtbogenauslöschung erzeugt. Somit wird die Lichtbogenspannung aufrechterhalten.According to these Aspects of the invention is a thermal decomposition gas having excellent arc extinguishing capability instant arc extinction generated. Thus, the arc voltage is maintained.

Vorzugsweise handelt es sich im erfindungsgemäßen Lichtbogenlösch-Harzformkörper bei den reaktiven, organischen flammhemmenden Mitteln auf Phosphorbasis (B) um eine organische Phosphorverbindung der Formel (I) und/oder der Formel (II), wobei die Mittel in der Harzzusammensetzung in einer Menge im Bereich von 0,5 bis 20 Gew.-% enthalten sind. Chemische Formel 1

wobei die Reste R¹ bis R⁴ jeweils die Bedeutung CH₂=CY¹-Y²- haben oder eine monofunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, bedeuten und R⁵ eine difunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, bedeutet, die Reste X¹ bis X⁴ jeweils eine Gruppe bedeuten, die aus -O-, -NH-, -(CH₂=CY¹-Y²)N- ausgewählt ist und mindestens eine der Reste X¹ bis X⁴ die Gruppe -NH- oder die Gruppe -(CH₂=CY¹-Y²)Nenthält;
mindestens einer der Reste R¹ bis R⁴ und der Reste X¹ bis X⁴ die Gruppe CH₂=CY¹-Y²- enthält;
Y¹ ein Wasserstoffatom oder eine Methylgruppe bedeutet; und
Y² eine Alkylengruppe mit 1 bis 5 Kohlenstoffatomen oder -COO-Y³- bedeutet, wobei Y³ eine Alkylengruppe mit 1 bis 5 Kohlenstoffatomen bedeutet. Chemische Formel 2

wobei in einem Molekül mindestens eine P-C-Bindung enthalten ist;
die Reste Ar¹ und Ar² jeweils eine difunktionelle aromatische Kohlenwasserstoffgruppe mit höchstens 20 Kohlenstoffatomen bedeuten, die kein mobiles Wasserstoffatom enthält, und n eine ganze Zahl mit einem Wert von 0, 1 oder 2 ist; die Reste R⁶ bis R¹⁰ jeweils eine Gruppe bedeuten, die aus -NHCH₂CH=CH₂, -N(CH₂CH=CH₂)₂, -OCH₂CH=CH₂, -CH₂CH=CH₂, -CH₂CH₂OCH=CH₂, -(C₆H₄)-CH=CH₂, -O(C₆H₄)-CH=CH₂, -CH₂(C₆H₄)-CH=CH₂, -NH(C₆H₄)-CH=CH₂, -N(CH₂CH=CH₂)-(C₆H₄)-CH=CH₂, -O-R-OOC-C(R')=CH₂, -NH-R-NHCO-C(R')=CH₂ und einer Arylgruppe mit höchstens 12 Kohlenstoffatomen ausgewählt ist, wobei R eine Alkylengruppe mit 2 bis 5 Kohlenstoffatomen bedeutet und R' ein Wasserstoffatom oder eine Methylgruppe bedeutet;
mindestens eine der Reste R⁶ bis R¹⁰ eine -CH=CH₂-Gruppe oder eine -C(CH₃)=CH₂-Gruppe enthält.Preferably, in the arc extinguishing resin molded article of the present invention, the phosphorus-based reactive organic flame retardant (B) is an organic phosphorus compound of the formula (I) and / or the formula (II), wherein the agents are present in the resin composition in an amount within the range from 0.5 to 20 wt .-% are included. Chemical formula 1

where R ¹ to R ⁴ each have the meaning CH ₂ = CY ¹ -Y ² - or a monofunctional aromatic hydrocarbon group which may contain a heteroatom, and R ⁵ denotes a difunctional aromatic hydrocarbon group which may contain a heteroatom, the radicals X ¹ to X ⁴ each represent a group which is selected from -O-, -NH-, - (CH ₂ = CY ¹ -Y ² ) N- and at least one of the radicals X ¹ to X ^{4 is} the group NH- or the group - (CH ₂ = CY ¹ -Y ² ) N;
at least one of the radicals R ¹ to R ⁴ and the radicals X ¹ to X ^{4 contains} the group CH ₂ = CY ¹ -Y ² -;
Y ^{1 represents} a hydrogen atom or a methyl group; and
Y ^{2 represents} an alkylene group having 1 to 5 carbon atoms or -COO-Y ³ -, wherein Y ^{3 represents} an alkylene group having 1 to 5 carbon atoms. Chemical formula 2

wherein at least one PC bond is contained in a molecule;
the radicals Ar ¹ and Ar ² each represent a difunctional aromatic hydrocarbon group having at most 20 carbon atoms which does not contain a mobile hydrogen atom, and n is an integer having a value of 0, 1 or 2; the radicals R ⁶ to R ¹⁰ each denote a group consisting of -NHCH ₂ CH =CH ₂ , -N (CH ₂ CH =CH ₂ ) ₂ , -OCH ₂ CH =CH ₂ , -CH ₂ CH =CH ₂ , -CH ₂ CH ₂ OCH = CH ₂ , - (C ₆ H ₄ ) -CH = CH ₂ , -O (C ₆ H ₄ ) -CH = CH ₂ , -CH ₂ (C ₆ H ₄ ) -CH = CH ₂ , -NH (C ₆ H ₄ ) -CH = CH ₂ , -N (CH ₂ CH = CH ₂ ) - (C ₆ H ₄ ) -CH = CH ₂ , -OR-OOC-C (R ') CH ₂ , -NH-R-NHCO-C (R ') = CH ₂ and an aryl group having at most 12 carbon atoms, wherein R represents an alkylene group having 2 to 5 carbon atoms and R' represents a hydrogen atom or a methyl group;
at least one of R ⁶ to R ^{10 contains} a -CH = CH ₂ group or a -C (CH ₃ ) = CH ₂ group.

Das reaktive, organische flammhemmende Mittel auf Phosphorbasis (B) ist in seinem Energiezustand stabil, verdampft beim Einkneten in das Harz und bei der Formgebung kaum und wird ferner aufgrund von Wärme- und Scherkrafteinwirkung kaum zersetzt. Daher werden die Formgebungseigenschaften nicht beeinträchtigt.The reactive organic phosphorus-based flame retardants (B) is stable in its energy state, evaporates when kneaded in the resin and the molding hardly and is also due to Warmth- and shear force hardly decomposed. Therefore, the molding properties become not impaired.

Vorzugsweise handelt es sich beim Polyacetalharz (C) im erfindungsgemäßen Lichtbogenlösch-Harzformkörper um ein Oxymethylen-Oxyethylen-Copolymeres oder um ein Oxymethylen-Polymeres. Gemäß diesen Aspekten der Erfindung wird ein thermisches Zersetzungsgas mit hervorragendem Lichtbogen-Auslöschungsvermögen erzeugt, so dass der Lichtbogen sofort ausgelöscht wird. Daher wird die Lichtbogenspannung aufrechterhalten.Preferably is the polyacetal resin (C) in the arc extinguishing resin molding according to the invention to an oxymethylene-oxyethylene copolymer or an oxymethylene polymer. According to these Aspects of the invention will be a thermal decomposition gas with excellent Generates arc extinguishing capability, so that the arc is extinguished immediately. Therefore, the arc voltage maintained.

Vorzugsweise ist im erfindungsgemäßen Lichtbogenlösch-Harzformkörper das Polyacetalharz (C) im Polyolefinharz (A) unter Bildung einer Mikrophasen-Trennstruktur dispergiert. Gemäß diesem Aspekt der Erfindung unterliegt das Polyacetalharz (C) bereitwillig einer Pyrolyse und emittiert ein thermisches Zersetzungsgas, das beim Vorgang der thermischen Zersetzung des Lichtbogenlösch-Harzformkörpers ein hochwertiges Lichtbogen-Auslöschungsverhalten zeigt. Daher wird der Lichtbogen sofort ausgelöscht.Preferably is in the inventive arc extinguishing resin moldings the Polyacetal resin (C) in the polyolefin resin (A) to form a microphase separation structure dispersed. According to this Aspect of the invention is readily subject to the polyacetal resin (C) a pyrolysis and emits a thermal decomposition gas, the in the process of thermal decomposition of the arc extinguishing resin molded body high quality arc extinction behavior shows. Therefore, the arc is extinguished immediately.

Ein erfindungsgemäßer Trennschalter umfasst einen fixierten Kontaktabschnitt mit einem fixierten Kontaktstück, einen beweglichen Kontaktabschnitt mit einem beweglichen Kontaktstück zur Kontaktbildung mit dem fixierten Kontaktabschnitt und zur Durchführung von Schließ- und Öffnungsvorgängen mit dem fixierten Kontaktabschnitt sowie ein Lichtbogenlösch-Bauelement, das einen Lichtbogen auslöscht, der bei den Öffnungs- und Schließvorgängen zwischen dem fixierten Kontaktabschnitt und dem beweglichen Kontaktabschnitt entsteht, wobei das Lichtbogenlösch-Bauelement einen Lichtbogenlösch-Harzformkörper gemäß den vorstehenden Ausführungen umfasst. Im erfindungsgemäßen Trennschalter lässt sich in wirksamer Weise der zwischen den Kontaktstücken beim Stromunterbrechungsvorgang entwickelte Lichtbogen auslöschen und der Druckanstieg im Lichtbogenlösch-Bauelement kontrollieren. Daher weist der Trennschalter geringe Abmessungen auf und zeigt ein hervorragendes Verhalten beim Stromunterbrechungsvorgang, einschließlich einer Überlastunterbrechung und einer Kurzschlussunterbrechung.One inventive disconnector includes a fixed contact portion with a fixed contact piece, a movable contact portion with a movable contact piece for contact formation with the fixed contact portion and for performing closing and opening operations with the fixed contact portion and an arc extinguishing component, that extinguishes an arc, at the opening and closing operations between the fixed contact portion and the movable contact portion arises, wherein the arc extinguishing component a Arc quenching resin molding according to the above versions includes. In the circuit breaker according to the invention let yourself effectively between the contact pieces in the current interruption process extinguish developed arc and check the pressure increase in the arc extinguishing component. Therefore, the circuit breaker has small dimensions and shows excellent behavior during power interruption, including overload interruption and a short-circuit break.

Wirkungen der ErfindungEffects of the invention

Der erfindungsgemäße Lichtbogenlösch-Harzformkörper weist eine zufriedenstellende Beschaffenheit in Bezug auf Festigkeit, Druckbeständigkeit, Wärmebeständigkeit, flammhemmende Beschaffenheit und Formgebungseigenschaften auf. Außerdem emittiert der Harzformkörper ein thermisches Zersetzungsgas, das ein hohes Lichtbogen-Auslöschungsvermögen aufweist. Infolgedessen wird der Lichtbogen, der zwischen den Kontaktstücken beim Stromunterbrechungsvorgang entsteht, in wirksamer Weise ausgelöscht und der Druck in der Lichtbogen-Auslöschungsvorrichtung wird auf einen geringen Wert kontrolliert. Ein erfindungsgemäßer Trennschalter, der sich des Lichtbogenlösch-Harzformkörpers bedient, ist der Miniaturisierung zugänglich und weist ein hervorragendes Verhalten bei der Stromunterbrechung, einschließlich einer Überlastunterbrechung und einer Kurzschlussunterbrechung, auf.Of the Arc quench resin molding according to the invention has a satisfactory texture in terms of strength, Pressure resistance, Heat resistance, Flame-retardant texture and shaping properties. In addition, emitted the resin molding a thermal decomposition gas having a high arc extinguishing ability. As a result, the arc that occurs between the contact pieces Power interruption process arises, effectively extinguished and the pressure in the arc extinguishing device is controlled to a low value. An inventive circuit breaker, which uses the arc extinguishing resin molding, is accessible to miniaturization and has excellent power interruption behavior, including an overload interruption and a short-circuit break.

Kurze Beschreibung der ZeichnungenBrief description of the drawings

1 ist eine teilweise im Schnitt dargestellte perspektivische Ansicht eines Beispiels für einen erfindungsgemäßen Trennschalter, 1 is a partially sectional perspective view of an example of an inventions Disconnector according to the invention,

2 ist eine perspektivische Darstellung einer im erfindungsgemäßen Trennschalter verwendeten Lichtbogen-Löschkammer. 2 is a perspective view of an arc-extinguishing chamber used in the circuit breaker according to the invention.

3 ist eine Querschnittansicht eines im erfindungsgemäßen Trennschalter verwendeten Lichtbogen-Auslöschbauelements. 3 is a cross-sectional view of an arc extinguishing device used in the circuit breaker according to the invention.

Beste Ausführungsform der ErfindungBest embodiment of the invention

Ein erfindungsgemäßer Lichtbogenlösch-Harzformkörper umfasst eine Harzzusammensetzung, die ein Polyolefinharz (A), bei dem ein Teil der Wasserstoffatome in einer Methylenkette durch Hydroxylgruppen (-OH) ersetzt ist und die Hydroxylgruppen in einer Menge im Bereich von 0,2 bis 0,7 Mol, bezogen auf 1 Mol der Methylengruppen (-CH₂-), enthalten sind, und ferner ein reaktives, organisches flammhemmendes Mittel auf Phosphorbasis (B), das eine ungesättigte Endbindung aufweist, enthält. Diese Harzzusammensetzung wird nach einem Formgebungsverfahren einer Vernetzungsbehandlung durch Bestrahlung unterworfen.An arc extinguishing resin molded article according to the present invention comprises a resin composition comprising a polyolefin resin (A) in which a part of hydrogen atoms in a methylene chain is replaced by hydroxyl groups (-OH) and hydroxyl groups in an amount ranging from 0.2 to 0.7 mol , based on 1 mole of the methylene groups (-CH ₂ -), and further containing a reactive organic phosphorus-based flame retardant (B) having an unsaturated end bond. This resin composition is subjected to a crosslinking treatment by irradiation after a molding process.

Das Polyolefinharz (A) enthält Hydroxylgruppen in einer Menge von 0,2 bis 0,7 Mol und vorzugsweise von 0,2 bis 0,65 Mol, bezogen auf 1 Mol der Methylengruppen. Wenn der Anteil der Hydroxylgruppen beim vorstehend definierten Verhältnis weniger als 0,2 beträgt, ist es schwierig, ein thermisches Zersetzungsgas zu erzeugen, das ein gutes Lichtbogen-Auslöschungsverhalten beim thermischen Zersetzungsvorgang aufweist, so dass der Lichtbogen nicht sofort ausgelöscht werden kann. Ferner besteht die Tendenz, dass der Druck im Lichtbogenlösch-Bauelement beim Lichtbogen-Auslöschungsvorgang ansteigt. Zugleich wird das Lichtbogenlösch-Bauelement durch eine erhöhte Menge freien Kohlenstoffs verschmutzt, was die elektrische Isoliervermögen des Bauelements beeinträchtigt. Wenn der Anteil der Hydroxylgruppen im Polyolefinharz (A) 0,7 Mol übersteigt, ist die Stärke der Wasserstoffbindungen zwischen den Molekülen starker als im Fall von 0,7 Mol oder weniger. Wenn die Wasserstoffbindungen starker sind, kommt der Schmelzpunkt des Polyolefinharz näher an die Zersetzungstemperatur heran. Dadurch wird der Formgebungsprozess infolge einer thermischen Zersetzung beim Kneten schwierig.The Polyolefin resin (A) contains Hydroxyl groups in an amount of 0.2 to 0.7 mol, and preferably from 0.2 to 0.65 mol, based on 1 mol of the methylene groups. If the Proportion of hydroxyl groups at the ratio defined above less than 0.2, it is difficult to produce a thermal decomposition gas that a good arc extinction behavior during the thermal decomposition process, so that the arc not extinguished immediately can be. Furthermore, there is a tendency that the pressure in the arc extinguishing component in the arc extinguishing process increases. At the same time, the arc extinguishing component by an increased amount free carbon pollutes what the electrical insulation of the Affected component. When the proportion of hydroxyl groups in the polyolefin resin (A) exceeds 0.7 mol, is the strength the hydrogen bonds between the molecules stronger than in the case of 0.7 mol or less. If the hydrogen bonds are stronger, the melting point of the polyolefin resin comes closer to the decomposition temperature approach. Thereby, the molding process due to thermal decomposition when kneading difficult.

Das Polyolefinharz (A) weist eine latente Zersetzungswärme von vorzugsweise mindestens 30 cal/g und insbesondere von mindestens 40 cal/g auf. Die latente Zersetzungswärme des Polyolefinharzes (A) lässt sich durch Erhöhen des Anteils der Hydroxylgruppen im Harz steigern. Die latente Zersetzungswärme des Polyolefinharzes, bei dem ein Teil der Wasserstoffatome in einer Methylenkette durch Hydroxylgruppen ersetzt ist und das die Hydroxylgruppen in einer Menge von 0,2 bis 0,7 Mol, bezogen auf 1 Mol der Methylengruppen, enthält, liegt im Bereich von 30 bis 50 cal/g. Die latente Zersetzungswärme eines Harzes lässt sich durch Erwärmen messen, um das Probenharz in einer Inertgasatmosphäre zu zersetzen.The Polyolefin resin (A) has a latent heat of decomposition of preferably at least 30 cal / g and in particular at least 40 cal / g. The latent decomposition heat of the polyolefin resin (A) let yourself by elevating increase the proportion of hydroxyl groups in the resin. The latent heat of decomposition of the Polyolefin resin in which a part of the hydrogen atoms in one Methylene chain is replaced by hydroxyl groups and that the hydroxyl groups in an amount of 0.2 to 0.7 mol, based on 1 mol of the methylene groups contains in the range of 30 to 50 cal / g. The latent decomposition heat of a Resin leaves by heating measure to decompose the sample resin in an inert gas atmosphere.

Bei einem bevorzugten Polyolefinharz handelt es sich um ein Ethylen-Vinylalkohol-Copolymeres, das aufgrund seiner hervorragenden Lichtbogen-Auslöschungseigenschaften sich besonders günstig verhält. Während Polyethylen ein geringes Lichtbogen-Auslöschungsverhalten zeigt, kann Poly-(vinylalkohol) nur begrenzt in einem Formgebungsverfahren zugesetzt werden.at a preferred polyolefin resin is an ethylene-vinyl alcohol copolymer, because of its excellent arc extinguishing properties especially cheap behaves. While polyethylene a low arc extinction behavior shows poly (vinyl alcohol) limited to be added in a molding process.

Beim reaktiven, organischen flammhemmenden Mittel auf Phosphorbasis (B) handelt es sich um eine organische Phosphorverbindung, die eine ungesättigte Endbindung aufweist, und vorzugsweise handelt es sich um eine Verbindung der Formeln (I) oder (II). Chemische Formel 3

wobei die Reste R¹ bis R⁴ jeweils die Bedeutung CH₂=CY¹-Y²- haben oder eine monofunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, bedeuten und R⁵ eine difunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, bedeutet; die Reste X¹ bis X⁴ jeweils eine Gruppe bedeuten, die aus –O-, -NH-, -(CH₂=CY¹-Y²)N- ausgewählt ist und mindestens einer der Reste X¹ bis X⁴ die Gruppe -NH- oder die Gruppe -(CH₂=CY¹-Y²)Nenthält;
mindestens eine der Reste R¹ bis R⁴ und der Reste X¹ bis X⁴ die Gruppe CH₂=CY¹-Y²- enthält;
Y¹ ein Wasserstoffatom oder eine Methylgruppe bedeutet; und
Y² eine Alkylengruppe mit 1 bis 5 Kohlenstoffatomen oder den Rest -COO-Y³- bedeutet, wobei Y³ eine Alkylengruppe mit 1 bis 5 Kohlenstoffatomen bedeutet. Chemische Formel 4

wobei in einem Molekül mindestens eine P-C-Bindung enthalten ist;
die Reste Ar¹ und Ar² jeweils eine difunktionelle aromatische Kohlenwasserstoffgruppe mit höchstens 20 Kohlenstoffatomen bedeuten, die kein mobiles Wasserstoffatom enthält, und n eine ganze Zahl mit einem Wert von 0, 1 oder 2 ist; die Reste R⁶ bis R¹⁰ jeweils eine Gruppe bedeuten, die aus -NHCH₂CH=CH₂, -N(CH₂CH=CH₂)₂, -OCH₂CH=CH₂, -CH₂CH=CH₂, -CH₂CH₂OCH=CH₂, -(C₆H₄)-CH=CH₂, -O(C₆H₄)-CH=CH₂, -CH₂(C₆H₄)-CH=CH₂, -NH(C₆H₄)-CH=CH₂, -N(CH₂CH=CH₂)-(C₆H₄)-CH=CH₂, -O-R-OOC-C(R')=CH₂, -NH-R-NHCO-C(R')=CH₂ und einer Arylgruppe mit höchstens 12 Kohlenstoffatomen ausgewählt ist, wobei R eine Alkylengruppe mit 2 bis 5 Kohlenstoffatomen bedeutet und R ein Wasserstoffatom oder eine Methylgruppe bedeutet;
mindestens einer der Reste R⁶ bis R¹⁰ eine -CH=CH₂-Gruppe oder eine -C(CH₃)=CH₂-Gruppe enthält.The phosphorus-based reactive organic flame retardant (B) is an organic phosphorus compound having an unsaturated end bond, and is preferably a compound of the formulas (I) or (II). Chemical formula 3

wherein the radicals R ¹ to R ⁴ each have the meaning CH ₂ = CY ¹ -Y ² - or a monofunctional aromatic hydrocarbon group which may contain a heteroatom, and R ^{5 is} a difunctional aromatic hydrocarbon group which may contain a heteroatom means; the radicals X ¹ to X ⁴ each represent a group selected from -O-, -NH-, - ⁽¹ -Y ² CH ₂ = CY) N- is selected and at least one of X ¹ to X ⁴ is the group - NH- or the group - (CH ₂ = CY ¹ -Y ² ) N;
at least one of the radicals R ¹ to R ⁴ and the radicals X ¹ to X ^{4 contains} the group CH ₂ = CY ¹ -Y ² -;
Y ^{1 represents} a hydrogen atom or a methyl group; and
Y ^{2 represents} an alkylene group having 1 to 5 carbon atoms or the group -COO-Y ³ -, wherein Y ^{3 represents} an alkylene group having 1 to 5 carbon atoms. Chemical formula 4

wherein at least one PC bond is contained in a molecule;
the radicals Ar ¹ and Ar ² each represent a difunctional aromatic hydrocarbon group having at most 20 carbon atoms which does not contain a mobile hydrogen atom, and n is an integer having a value of 0, 1 or 2; the radicals R ⁶ to R ¹⁰ each denote a group consisting of -NHCH ₂ CH =CH ₂ , -N (CH ₂ CH =CH ₂ ) ₂ , -OCH ₂ CH =CH ₂ , -CH ₂ CH =CH ₂ , -CH ₂ CH ₂ OCH = CH ₂ , - (C ₆ H ₄ ) -CH = CH ₂ , -O (C ₆ H ₄ ) -CH = CH ₂ , -CH ₂ (C ₆ H ₄ ) -CH = CH ₂ , -NH (C ₆ H ₄ ) -CH = CH ₂ , -N (CH ₂ CH = CH ₂ ) - (C ₆ H ₄ ) -CH = CH ₂ , -OR-OOC-C (R ') CH ₂ , -NH-R-NHCO-C (R ') = CH ₂ and an aryl group having at most 12 carbon atoms, wherein R represents an alkylene group having 2 to 5 carbon atoms and R represents a hydrogen atom or a methyl group;
at least one of R ⁶ to R ^{10 contains} a -CH = CH ₂ group or a -C (CH ₃ ) = CH ₂ group.

Die organische Phosphorverbindung enthält mindestens eine der Gruppen -CH=CH₂ oder -C(CH₃)=CH₂, d. h. eine ungesättigte Endbindung. Diese funktionelle Gruppe soll bei Bestrahlung mit radioaktiven Strahlen eine Bindung mit dem Polyolefinharz (A) eingehen. Vorzugsweise sind in einem Molekül zwei oder mehr ungesättigte Endbindungen enthalten.The organic phosphorus compound contains at least one of -CH = CH ₂ or -C (CH ₃ ) = CH ₂ , that is, an unsaturated end bond. This functional group should undergo binding with the polyolefin resin (A) upon irradiation with radioactive rays. Preferably, two or more unsaturated end bonds are contained in one molecule.

Die Gruppe CH₂=CY¹-Y²- in der Verbindung der Formel (I) kann beispielsweise folgende spezielle Bedeutungen haben: CH₂=CH-CH₂-, CH₂=CH-CH₂CH₂CH₂-, CH₂=C(CH₃)-CH₂-, CH₂=CHCOO-CH₂CH₂- und CH₂=C(CH₃)COO-CH₂CH₂-The group CH ₂ = CY ¹ -Y ² - in the compound of the formula (I) may have, for example, the following special meanings: CH ₂ = CH-CH ₂ -, CH ₂ = CH-CH ₂ CH ₂ CH ₂ -, CH ₂ = C (CH ₃ ) -CH ₂ -, CH ₂ = CHCOO-CH ₂ CH ₂ - and CH ₂ = C (CH ₃ ) COO-CH ₂ CH ₂ -

Die monofunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, im Rahmen von R¹ bis R⁴ ist vorzugsweise eine aromatische Kohlenwasserstoffgruppe mit 6 bis 14 Kohlenstoffatomen. Speziell gehören hierzu folgende Gruppen: -C₆H₅ (Phenylgruppe), -C₆H₅OH (Hydroxyphenylgruppe), C₆H₅-C₆H₅OH (Hydroxybiphenylgruppe), -CH₂C₆H₅ (Benzylgruppe), -α-C₁₀H₇-(α-Naphthylgruppe) und -β-C₁₀H₇ (β-Naphthylgruppe).The monofunctional aromatic hydrocarbon group which may contain a hetero atom in the scope of R ¹ to R ⁴ is preferably an aromatic hydrocarbon group having 6 to 14 carbon atoms. Specifically, these include the following groups: -C ₆ H ₅ (phenyl group), -C ₆ H ₅ OH (hydroxyphenyl group), C ₆ H ₅ -C ₆ H ₅ OH (hydroxybiphenyl group), -CH ₂ C ₆ H ₅ (benzyl group), -α-C ₁₀ H ₇ - (α-naphthyl group) and -β-C ₁₀ H ₇ (β-naphthyl group).

Die difunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, im Rahmen von R₅, ist vorzugsweise eine aromatische Kohlenwasserstoffgruppe mit 10 bis 14 Kohlenstoffatomen. Zu speziellen Beispielen für derartige Gruppen gehören: -p-C₆H₄-p-C₆H₄-, -p-C₆H₄-CH₂-p-C₆H₄-, -p-C₆H₄-C(CH₃)₂-p-C₆H₄, -p-C₆H₄-C(=O)-p-C₆H₄-, -p-C₆H₄-SO₂-p-C₆H₄- und 2,6-C₁₀H₆< (2,6-Naphthylengruppe).The difunctional aromatic hydrocarbon group which may contain a hetero atom in the scope of R ₅ is preferably an aromatic hydrocarbon group having 10 to 14 carbon atoms. Specific examples of such groups include: -pC ₆ H ₄ -pC ₆ H ₄ -, -pC ₆ H ₄ -CH ₂ -pC ₆ H ₄ -, -pC ₆ H ₄ -C (CH ₃ ) ₂ -pC ₆ H ₄ , -pC ₆ H ₄ -C (= O) -pC ₆ H ₄ -, -pC ₆ H ₄ -SO ₂ -pC ₆ H ₄ - and 2,6-C ₁₀ H ₆ <(2,6-) naphthylene).

Die in der Beschreibung und in den Ansprüchen erwähnte aromatische Kohlenwasserstoffgruppe umfasst nicht nur eine rein aromatische Kohlenwasserstoffgruppe, wie die Phenylgruppe und die -p-C₆H₄-p-C₆H₄-Gruppe, sondern auch eine aromatische Kohlenwasserstoffgruppe, die ein Sauerstoff- oder Schwefelatom als Heteroatom enthält, z. B. die Hydroxyphenylgruppe und die -p-C₆H₄-SO₂-p-C₆H₄-Gruppe.The aromatic hydrocarbon group mentioned in the specification and in the claims includes not only a purely aromatic hydrocarbon group such as the phenyl group and the -pC ₆ H ₄ -pC ₆ H ₄ group but also an aromatic hydrocarbon group having an oxygen or sulfur atom as Heteroatom contains, for. The hydroxyphenyl group and the -pC ₆ H ₄ -SO ₂ -pC ₆ H ₄ group.

Als spezielle Beispiele für die organische Phosphorverbindung der Formel (I) lassen sich die Verbindungen der folgenden Strukturformeln (I-1) bis (I-18) aufführen. Chemische Formel 5

Chemische Formel 6

Chemische Formel 7

As specific examples of the organic phosphorus compound of the formula (I), the compounds of the following structural formulas (I-1) to (I-18) can be listed. Chemical formula 5

Chemical formula 6

Chemical formula 7

Die vorstehend aufgeführten Verbindungen lassen sich gemäß den in WO-2005/012415 beschriebenen Verfahren herstellen. Beispielsweise lässt sich die Verbindung (I-1) erhalten, indem man Phosphoroxychlorid an Dimethylacetamid (DMAc) addiert und in diese Lösung eine DMAc-Lösung, die gelösten 4,4'-Biphenylalkohol und gelöstes Triethylamin enthält, tropft, um die Bestandteile miteinander umzusetzen, wonach sich die Umsetzung mit einer Mischlösung aus Allylamin und Triethylamin anschließt.The compounds listed above can be prepared according to the in WO-2005/012415 produce described method. For example, the compound (I-1) can be obtained by adding phosphorus oxychloride to dimethylacetamide (DMAc) and dropping into this solution a DMAc solution containing dissolved 4,4'-biphenylalcohol and dissolved triethylamine to react the components with each other after which the reaction is followed by a mixed solution of allylamine and triethylamine.

In den Verbindungen der Formel (II) kann es sich bei speziellen Beispielen für die Arylgruppe mit höchstens 12 Kohlenstoffatomen um folgende Gruppen handeln: -C₆H₅ (Phenylgruppe), -C₆H₅OH (Hydroxylphenylgruppe), -C₆H₅-C₆H₅OH (Hydroxybiphenylgruppe), -α-C₁₀H₇ (α-Naphthylgruppe) und -β-C₁₀H₇ (β-Naphthylgruppe).In the compounds of the formula (II), specific examples of the aryl group having not more than 12 carbon atoms may be the following groups: -C ₆ H ₅ (phenyl group), -C ₆ H ₅ OH (hydroxylphenyl group), -C ₆ H ₅ -C ₆ H ₅ OH (hydroxybiphenyl group), -α-C ₁₀ H ₇ (α-naphthyl group) and -β-C ₁₀ H ₇ (β-naphthyl group).

Bei speziellen Beispielen der difunktionellen aromatischen Kohlenwasserstoffgruppe mit höchstens 20 Kohlenstoffatomen, die kein mobiles Wasserstoffatom enthält, im Rahmen von Ar¹ und Ar² kann es sich um folgende Gruppen handeln: -p-C₆H₄-, -p-C₆H₄-O-, -O-p-C₆H₄-O-, -p-C₆H₄-p-C₆H₄-, -p-C₆H₄-CH₂-p-C₆H₄-, -p-C₆H₄-C(CH₃)₂-p-C₆H₄-, -p-C₆H₄-C(=O)-p-C₆H₄-, -p-C₆H₄-SO₂-p-C₆H₄- und 2,6-C₆H₄< (2,6-Naphthylengruppe). Unter einem mobilen Wasserstoffatom ist ein hochgradig reaktives Wasserstoffatom, das in einer funktionellen Gruppe enthalten ist, zu verstehen, z. B. in – OH (Hydroxylgruppe), -NHCO- (Amidbindung) oder -NHCOO- (Urethanbindung), das leicht eine Wasserstoffbrückenbindung bildet und bei Raumtemperatur bereitwillig mit metallischem Natrium und Natriumhydrid unter Erzeugung von Wasserstoff reagiert.Specific examples of the difunctional aromatic hydrocarbon group having at most 20 carbon atoms which does not contain a mobile hydrogen within Ar ¹ and Ar ² may be the following groups: -pC ₆ H ₄ -, -pC ₆ H ₄ -O-, -OpC ₆ H ₄ -O-, -pC ₆ H ₄ -pC ₆ H ₄ -, -pC ₆ H ₄ -CH ₂ -pC ₆ H ₄ -, -pC ₆ H ₄ -C (CH ₃ ) ₂ -pC ₆ H ₄ -, -pC ₆ H ₄ -C (= O) -pC ₆ H ₄ -, -pC ₆ H ₄ -SO ₂ -pC ₆ H ₄ - and 2,6-C ₆ H ₄ <(2, 6-naphthylene group). By a mobile hydrogen atom is meant a highly reactive hydrogen atom contained in a functional group, e.g. In-OH (hydroxyl group), -NHCO- (amide bond) or -NHCOO- (urethane bond), which readily forms a hydrogen bond and readily reacts at room temperature with metallic sodium and sodium hydride to produce hydrogen.

Zu speziellen Beispielen für die organische Phosphorverbindung der Formel (II) gehören die Verbindungen der Strukturformeln (II-1) bis (II-23). Unter diesen Verbindungen stellen die Verbindungen (II-1) bis (II-12) Beispiele für n=0 dar, d. h. Beispiele, die zwei Phosphoratome in einem Molekül enthalten. Bei den Verbindungen (II-13) bis (II-20) handelt es sich um Beispiele mit n=1, d. h. um Beispiele, die drei Phosphoratome in einem Molekül enthalten. Die Verbindungen (II-21) bis (II-23) sind Beispiele für n=2, wobei vier Phosphoratome in einem Molekül enthalten sind. Chemische Formel 8

Chemische Formel 9

Chemische Formel 10

Chemische Formel 11

Specific examples of the organic phosphorus compound of the formula (II) include the compounds of the structural formulas (II-1) to (II-23). Among these compounds, compounds (II-1) to (II-12) represent examples of n = 0, that is, examples containing two phosphorus atoms in one molecule. The compounds (II-13) to (II-20) are examples of n = 1, that is, examples containing three phosphorus atoms in one molecule. The compounds (II-21) to (II-23) are examples of n = 2, wherein four phosphorus atoms are contained in one molecule. Chemical formula 8

Chemical formula 9

Chemical formula 10

Chemical formula 11

Die vorstehend aufgeführten Verbindungen lassen sich gemäß einem in WO-2005-087852 beschriebenen Verfahren herstellen. Beispielsweise lässt sich die Verbindung (II-1) durch Umsetzung der Ausgangsmaterialien 4,4'-Dichlorbiphenyl mit Phosphoroxychlorid unter anschließender Umsetzung mit Allylbromid zur Einführung einer ungesättigten Gruppe am Ende herstellen.The compounds listed above can be according to a in WO-2005-087852 produce described method. For example, the compound (II-1) can be produced by reacting the starting materials 4,4'-dichlorobiphenyl with phosphorus oxychloride, followed by reaction with allyl bromide to introduce an unsaturated group at the end.

Das reaktive, organische flammhemmende Mittel auf Phosphorbasis (B) ist in der Harzzusammensetzung vorzugsweise in einer Menge von 0,5 bis 20 Gew.-% und insbesondere von 4 bis 12 Gew.-% enthalten. Wenn der Anteil des reaktiven, organischen flammhemmenden Mittels auf Phos phorbasis (B) weniger als 0,5 Gew.-% beträgt, werden die flammhemmenden Eigenschaften kaum verbessert und daneben ergibt sich aus der geringen Vernetzungsdichte der Harzzusammensetzung der Umstand, dass die physikalischen Eigenschaften in bezug auf Festigkeit, Druckbeständigkeit und Wärmebeständigkeit kaum verbessert werden. Wenn der Anteil 20 Gew.-% übersteigt, ist das organische flammhemmende Mittel auf Phosphorbasis in so starkem Überfluss vorhanden, dass nicht-umgesetztes Monomeres und Zersetzungsgase des reaktiven organischen flammhemmenden Mittels auf Phosphorbasis vorliegen und es zum Ausbluten von oligomeren Substanzen kommen kann.The reactive organic phosphorus-based flame retardants (B) is preferably in the amount of 0.5 in the resin composition to 20 wt .-% and in particular from 4 to 12 wt .-%. If the proportion of the reactive organic flame retardant Phos phorbasis (B) is less than 0.5 wt .-%, the flame retardant Properties hardly improved and beside it results from the small one Crosslinking density of the resin composition of the circumstance that the physical properties in terms of strength, pressure resistance and heat resistance hardly be improved. If the proportion exceeds 20% by weight, is the organic phosphorus-based flame retardant in so strong abundance present, that unreacted monomer and decomposition gases of the phosphorus-based reactive organic flame retardant be present and it comes to bleeding of oligomeric substances can.

Vorteilhafterweise enthält die Harzzusammensetzung, die im erfindungsgemäßen Lichtbogenlösch-Harzformkörper verwendet wird, ferner ein Polyacetalharz (C). Obgleich ein Polyacetalharz im allgemeinen ein thermisches Zersetzungsgas erzeugt, das zum Auslöschen eines Lichtbogens sehr wirksam ist, bereitet es Schwierigkeiten bei der Formgebung durch Schmelzkneten, d. h. es weist eine schlechte Verformbarkeit auf. Da ein Polyacetalharz eine reichliche Menge an thermischem Zersetzungsgas erzeugt, das einen relativ hohen Beitrag zum Druckanstieg liefert, nimmt der Druck in einem Lichtbogenlösch-Bauelement tendenziell zu. Durch Verwendung des Polyacetalharzes in Kombination mit dem Polyolefinharz (A) wird das Lichtbogen-Auslöschungsverhalten verbessert, ohne dass die Verformbarkeit der Harzzusammensetzung beeinträchtigt wird. Außerdem wird auch der Druckanstieg in einem Lichtbogenlösch-Bauelement beim Lichtbogen-Auslöschungsvorgang unterdrückt.advantageously, contains the resin composition used in the arc extinguishing resin molded article of the present invention and a polyacetal resin (C). Although a polyacetal resin In general, generates a thermal decomposition gas, which is used to extinguish a Arc is very effective, it causes difficulties in the Shaping by melt-kneading, d. H. it has a poor deformability. Since a polyacetal resin is an ample amount of thermal decomposition gas generated, which provides a relatively high contribution to the pressure increase, the pressure in an arc extinguishing component tends to increase to. By using the polyacetal resin in combination with the Polyolefin resin (A) improves the arc extinction behavior without affecting the ductility of the resin composition. In addition, will also the pressure increase in an arc extinguishing component during the arc extinguishing process suppressed.

Das Polyacetalharz (C) enthält Struktureinheiten, die sich von Oxymethylen ableiten, in einem Anteil von vorzugsweise 75 bis 100 Mol-% und insbesondere im Bereich von 80 bis 100 Mol-%. Wenn der Anteil der Struktureinheiten weniger als 75 Mol-% beträgt, so ergibt sich ein schlechtes Lichtbogen-Auslöschungsverhalten und ein rascher Auslöschungsvorgang lässt sich nicht durchführen.The Polyacetal resin (C) contains Structural units derived from oxymethylene in a proportion of preferably 75 to 100 mol% and especially in the range of 80 to 100 mol%. If the proportion of structural units is less than 75 mole%, this results in a poor arc extinction behavior and a rapid extinguishing process let yourself do not perform.

Bei einem bevorzugten Polyacetalharz handelt es sich um ein Oxymethylen-Oxyethylen-Copolymeres oder um ein Oxymethylen-Polymeres, das aufgrund seiner hervorragenden Lichtbogen-Auslöschungseigenschaften besonders bevorzugt ist. Dagegen zeigt Polyoxyethylen ein schlechtes Lichtbogen-Auslöschungsverhalten.at a preferred polyacetal resin is an oxymethylene-oxyethylene copolymer or to an oxymethylene polymer, due to its excellent Arc extinguishing properties is particularly preferred. In contrast, polyoxyethylene shows a bad Arc extinguishing behavior.

Das Polyacetalharz (C) ist vorzugsweise in einer Menge im Bereich von 5 bis 90 Gew.-teilen und insbesondere im Bereich von 7 bis 88 Gew.-teilen, bezogen auf 100 Gew.-teile des Polyolefinharzes (A), enthalten. Wenn der Anteil des Polyacetalharzes (C) weniger als 5 Gew.-teile gemäß dem vorstehend definierten Verhältnis beträgt, lässt sich nur eine geringe Wirkung durch das Polyacetalharz (C) erwarten und das Lichtbogen-Auslöschungsverhalten lässt sich kaum verbessern. Wenn der Anteil 90 Gew.-teile übersteigt, nimmt die Menge des thermischen Zersetzungsgases zu, wodurch der Druck im Lichtbogenlösch-Bauelement steigt.The Polyacetal resin (C) is preferably in an amount in the range of 5 to 90 parts by weight and in particular in the range of 7 to 88 parts by weight, based on 100 parts by weight of the polyolefin resin (A). When the proportion of the polyacetal resin (C) is less than 5 parts by weight according to the above defined ratio is, let yourself expect only a small effect by the polyacetal resin (C) and the arc extinction behavior let yourself hardly improve. If the proportion exceeds 90 parts by weight, the amount decreases of the thermal decomposition gas, causing the pressure in the arc extinguishing component increases.

Die Harzzusammensetzung, die im erfindungsgemäßen Lichtbogenlösch-Harzformkörper verwendet wird, kann ferner die vorerwähnten Harze umfassen, wobei beispielsweise ein thermoplastisches Harz für allgemeine Zwecke enthalten sein kann. Der Anteil eines derartigen Harzes liegt vorzugsweise im Bereich von 0 bis 15 Gew.-teilen und insbesondere im Bereich von 0 bis 12 Gew.- teilen, bezogen auf 100 Gew.-teile des Polyolefinharzes (A).The Resin composition used in the arc extinguishing resin molding of the present invention can also the aforementioned Resins include, for example, a thermoplastic resin for general Purposes may be included. The proportion of such a resin is preferably in the range of 0 to 15 parts by weight and in particular in the range of 0 to 12 parts by weight, based on 100 parts by weight of the polyolefin resin (A).

Vorteilhafterweise enthält die Harzzusammensetzung, die im erfindungsgemäßen Lichtbogenlösch-Harzformkörper verwendet wird, ferner ein Strahlungsvernetzungsmittel (C). Das enthaltene Strahlungsvernetzungsmittel geht bei Bestrahlung mit radioaktiven Strahlen eine chemische Bindung mit dem Harz ein, wodurch das Harz in einer dreidimensionalen Netzstruktur vernetzt wird und die Vernetzungsdichte erhöht wird. Dadurch werden die physikalischen Eigenschaften, einschließlich Festigkeit, Druckbeständigkeit und Wärmebeständigkeit, verbessert.advantageously, contains the resin composition used in the arc extinguishing resin molded article of the present invention and a radiation crosslinking agent (C). The included Radiation crosslinking agent is when irradiated with radioactive Blend a chemical bond with the resin, causing the resin is networked in a three-dimensional network structure and the crosslink density is increased. This will change the physical properties, including strength, pressure resistance and heat resistance, improved.

Zu geeigneten Strahlungsvernetzungsmitteln gehören Verbindungen, die keinen aromatischen Ring enthalten und bereitwillig Wasserstoffgas erzeugen, wobei es sich um Melaminverbindungen mit einer reaktiven funktionellen Gruppe mit einer difunktionellen oder höheren Funktionalität handelt, einschließlich Trimethallylacrylat, Triallylacrylat und Isocyanato-tri-(methyl)-acrylat. Insbesondere lässt sich ein Strahlungsvernetzungsmittel unter folgenden Produkten auswählen: Triallylisocyanurat, Trimethallylisocyanurat, ein durch radikalische Oligomerisation dieser Isocyanurate erhaltenes Oligomeres, Triallyltrimellitat, Trimethallyltrimellitat, Tetraallylpyromellitat, Tetramethallylpyromellitat, N,N,N',N',N'',N''-Hexaallylmelamin, N,N,N',N',N'',N''-Hexamethallylmelamin und dergl.To Suitable radiation crosslinking agents include compounds that have no contain aromatic ring and readily generate hydrogen gas, which are melamine compounds with a reactive functional Group with a difunctional or higher functionality, including Trimethallyl acrylate, triallyl acrylate and isocyanato-tri (methyl) acrylate. In particular, lets choose a radiation curing agent from the following products: triallyl isocyanurate, Trimethallyl isocyanurate, one by radical oligomerization oligomer obtained from these isocyanurates, triallyl trimellitate, Trimethallyl trimellitate, tetraallyl pyromellitate, tetramethallyl pyromellitate, N, N, N ', N', N '', N '' - Hexaallylmelamin, N, N, N ', N', N '', N '' - Hexamethallylmelamin and the like

Das Strahlungsvernetzungsmittel (C) ist in der Harzzusammensetzung in einer Menge von vorzugsweise 0,5 bis 20 Gew.-% und insbesondere von 1 bis 12 Gew.-% enthalten. Wenn der Anteil des Strahlungsvernetzungsmittels weniger als 0,5 Gew.-% beträgt, lässt sich die Vernetzung des Harzverbundstoffes kaum verbessern. Wenn der Anteil 20 Gew.-% übersteigt, kann es zu einem Ausbluten des Strahlungsvernetzungsmittels kommen.The Radiation crosslinking agent (C) is in the resin composition in an amount of preferably 0.5 to 20% by weight, and especially from 1 to 12% by weight. When the proportion of the radiation crosslinking agent is less than 0.5% by weight, let yourself hardly improve the cross-linking of the resin composite. If the Proportion exceeds 20% by weight, it may come to a bleeding of the radiation crosslinking agent.

Vorteilhafterweise enthält die Harzzusammensetzung, die im erfindungsgemäßen Lichtbogenlösch-Harzformkörper verwendet wird, einen oder mehrere Typen eines anorganischen Füllstoffes (D), der aus der Gruppe verstärkende Fasern, Bariumtitanat-Whiskers, feine Kieselgelteilchen, Boehmit, Talcum, Magnesiumcarbonat und ein Metallhydroxid ausgewählt ist. Das Vorliegen des anorganischen Füllstoffes verbessert die Maßhaltigkeit sowie die Intensität, die Druckbeständigkeit und die Wärmebeständigkeit des Lichtbogenlösch-Harzformkörpers.Advantageously, the resin composition used in the arc-quench resin molded article of the invention contains one or more types of inorganic filler (D) selected from the group consisting of reinforcing fibers, barium titanate whiskers, silica fine particles, boehmite, talc, magnesium carbonate and a metal hydroxide. Improves the presence of the inorganic filler the dimensional stability as well as the intensity, the pressure resistance and the heat resistance of the arc extinguishing resin molding.

Die Verstärkungsfasern können beispielsweise aus Glasfasern, Kohlenstofffasern und Metallfasern ausgewählt werden, wobei Glasfasern aufgrund ihrer Festigkeit und Haftfähigkeit am Harz und am anorganischen Füllstoffmaterial bevorzugt werden. Die Verstärkungsfasern können allein oder in Kombination aus zwei oder mehr Arten verwendet werden. Ferner können die Fasern mit einem bekannten Oberflächenbehandlungsmittel, z. B. einem Silan-Haftmittel, behandelt werden. Die Glasfasern werden vorzugsweise einer Oberflächenbehandlung unterzogen und ferner mit einem Harz beschichtet. Diese Maßnahme verbessert die Haftfähigkeit des Harzes in der Harzzusammensetzung.The reinforcing fibers can For example, be selected from glass fibers, carbon fibers and metal fibers, being glass fibers due to their strength and adhesiveness on the resin and on the inorganic filler material to be favoured. The reinforcing fibers can used alone or in combination of two or more species. Furthermore, can the fibers with a known surface treatment agent, for. B. a silane coupling agent. The glass fibers become preferably a surface treatment and further coated with a resin. This measure improves the adhesion of the resin in the resin composition.

Das Metallhydroxid wird aufgrund seiner Fähigkeit zur Unterdrückung des Druckanstiegs vorzugsweise im Polyolefinharz (A) dispergiert. Das Metallhydroxid wird vorzugsweise aus der Gruppe, umfassend Aluminiumhydroxid, Boehmit und Magnesiumhydroxid mit einem Korndurchmes ser im Bereich von 1 bis 10 μm ausgewählt.The Metal hydroxide is used because of its ability to suppress the Pressure increase preferably in the polyolefin resin (A) dispersed. The Metal hydroxide is preferably selected from the group comprising aluminum hydroxide, Boehmite and magnesium hydroxide with a grain diameter in the range selected from 1 to 10 μm.

Der anorganische Füllstoff (D) ist in der Harzzusammensetzung vorzugsweise in einem Anteil von 1 bis 70 Gew.-% und insbesondere von 20 bis 70 Gew.-% enthalten. Wenn der Anteil des anorganischen Füllstoffes (D) weniger als 1 Gew.-% beträgt, lässt sich die Wirkung des anorganischen Füllstoffes kaum erhalten. Wenn der Anteil 70 Gew.-% übersteigt, nimmt die Menge des thermischen Zersetzungsgases ab, was das Lichtbogen-Auslöschungsvermögen beeinträchtigt.Of the inorganic filler (D) is preferably in a proportion in the resin composition from 1 to 70 wt .-% and in particular from 20 to 70 wt .-%. When the content of the inorganic filler (D) is less than 1 Wt .-%, let yourself the effect of the inorganic filler barely received. When the proportion exceeds 70% by weight, the amount decreases of the thermal decomposition gas, which affects the arc extinguishing ability.

Die Harzzusammensetzung des erfindungsgemäßen Lichtbogenlösch-Harzformkörpers kann ferner üblicherweise verwendete Additive, die von den vorerwähnten Substanzen abweichen, enthalten, sofern das Additiv nicht in erheblichem Umfang die erfindungsgemäß angestrebten Eigenschaften beeinträchtigt, d. h. die Wärmebeständigkeit, die Druckbeständigkeit, das Lichtbogen-Auslöschungsvermögen, die Festigkeit und die flammhemmende Beschaffenheit. Die Additive umfassen beispielsweise Kristallisationskeime, farbgebende Mittel, Antioxidationsmittel, Formtrennmittel, Weichmacher, Wärmestabilisatoren, Gleitmittel, UV-Absorber und dergl.The Resin composition of the arc extinguishing resin molding according to the invention can furthermore usually used additives that differ from the aforementioned substances, contain, if the additive is not to a considerable extent the invention sought Properties impaired, d. H. the heat resistance, the pressure resistance, the arc extinguishing ability, the Firmness and flame-retardant texture. The additives include for example, nuclei, colorants, antioxidants, Mold release agents, plasticisers, heat stabilizers, Lubricant, UV absorber and the like.

Der erfindungsgemäße Lichtbogenlösch-Harzformkörper wird fertiggestellt, indem man die geformte Harzzusammensetzung mit radioaktiven Strahlen bestrahlt.Of the Arc quench resin molding according to the invention is Finished by using the molded resin composition with radioactive Radiation irradiated.

Die Formgebung der Harzzusammensetzung kann nach einem bekannten Verfahren durchgeführt werden. Beispielsweise kann nach dem Schmelzkneten der Harzzusammensetzung zur Bildung von Pellets die Formgebung nach einem bekannten Verfahren des Spritzgießens, des Extrudierens, der Vakuumformgebung, der Blasformgebung und dergl. durchgeführt werden. Das Schmelzkneten kann unter Verwendung einer üblicherweise verwendeten Schmelzknetmaschine, z. B. eines Einzelschnecken- oder Doppelschneckenextruders, eines Banbury-Mischers, eines Kneters, einer Mischwalze oder dergl., durchgeführt werden. Der Knetvorgang wird vorzugsweise bei einer Temperatur im Bereich von 170 bis 230 °C durchgeführt. Wenn die Temperatur unter 170 °C liegt, lässt sich das Schmelzkneten kaum durchführen. Bei einer Temperatur von über 230 °C dissoziiert die Hydroxylgruppe in der Harzzusammensetzung, wodurch das Auslöschungsverhalten verringert wird. Insbesondere erweist sich das nachstehend geschilderte Verfahren erfindungsgemäß als günstig. Eine Harzzusammensetzung, die das Polyolefinharz (A) und das Polyacetalharz (C) enthält, wird unter einer Inertgasatmosphäre bei einer Temperatur von 180 bis 220 °C geknetet und geformt, wonach sich eine Abkühlung auf eine Temperatur von 40 bis 60 °C anschließt. Durch dieses Formgebungsverfahren lässt sich ein Harzformkörper mit einer Mikrophasen-Trennstruktur erhalten, bei dem das Polyacetalharz (C) mit einer Submikrongröße von 0,1 bis 0,9 μm im Polyolefinharz (A) dispergiert ist, und zwar in der Konfiguration eines Sees mit Inseln, eines hexagonalen Zylinders oder von Lamellen. Durch Bildung der Mikrophasen-Trennstruktur lässt sich das Polyacetalharz (C) leicht thermisch zersetzen, wobei es ein thermisches Zersetzungsgas mit starkem Lichtbogen-Auslöschungsvermögen emittiert, wodurch der Lichtbogen rasch ausgelöscht wird. Da die Vernetzung in diesem Stadium noch nicht begonnen hat, können Reste, die beim Formgebungsverfahren anfallen, einem Recycling zugeführt werden.The Shaping of the resin composition can be carried out by a known method be performed. For example, after melt kneading, the resin composition to form pellets the shaping according to a known method injection molding, extruding, vacuum forming, blow molding and the like. carried out become. The melt-kneading can be carried out using a conventional used Schmelzknetmaschine, z. B. a single screw or Twin-screw extruder, a Banbury mixer, a kneader, a mixing roller or the like., Are performed. The kneading process is preferably carried out at a temperature in the range of 170 to 230 ° C. If the temperature below 170 ° C lies, lets the melt kneading hardly perform. At a temperature from above 230 ° C dissociated the hydroxyl group in the resin composition, resulting in the extinction behavior is reduced. In particular, the below described Process according to the invention as favorable. A A resin composition containing the polyolefin resin (A) and the polyacetal resin Contains (C) is under an inert gas atmosphere kneaded and molded at a temperature of 180 to 220 ° C, followed by a cool down connected to a temperature of 40 to 60 ° C. Through this molding process let yourself a resin molding obtained with a microphase separation structure in which the polyacetal resin (C) with a submicron size of 0.1 up to 0.9 μm in the polyolefin resin (A) is dispersed, in the configuration a lake with islands, a hexagonal cylinder or lamellae. By forming the microphase separation structure, the polyacetal resin can be formed (C) decompose easily thermally, being a thermal decomposition gas emitted with strong arc extinguishing capability, whereby the arc is extinguished quickly. Because the networking at this stage has not yet begun, residues may be present during the molding process incurred, recycled become.

Nachdem der Harzformkörper erhalten worden ist, wird eine Bestrahlung mit radioaktiven Strahlen durchgeführt, wodurch man den erfindungsgemäßen Lichtbogenlösch-Harzformkörper erhält. Die Mikrophasen-Trennstruktur wird durch den Vernetzungsvorgang, der durch die Bestrahlung herbeigeführt wird, fixiert.After this the resin molding received, irradiation with radioactive radiation is carried out, whereby to obtain the arc extinguishing resin molding according to the invention. The Microphase separation structure is determined by the crosslinking process, the caused by the irradiation is fixed.

Zur Bestrahlung des Harzformkörpers können α-Strahlen, γ-Strahlen, Röntgenstrahlen oder UV-Strahlen verwendet werden, worunter γ-Stahlen bevorzugt werden, da sie ein intensives Eindringverhalten zeigen und eine homogene Bestrahlung zulassen.For irradiating the resin molded body, α rays, γ rays, X-rays or UV rays can be used, of which γ-steels are preferred since they show an intensive penetration property and allow a homogeneous irradiation.

Die Bestrahlungsdosis beträgt vorzugsweise mindestens 10 kGy und insbesondere 10 bis 45 kGy. Durch Bestrahlung in diesem Bereich lässt sich ein Lichtbogenlösch-Harzformkörper mit den vorerwähnten günstigen Eigenschaften aufgrund der durch die Bestrahlung erzielten Vernetzung erreichen. Wenn die Bestrahlungsdosis unter 10 kGy liegt, ist die dreidimensionale Netzstruktur, die durch die Vernetzungsbindungen gebildet wird, inhomogen und nicht-umgesetztes Vernetzungsmittel kann ausbluten. Wenn die Dosis 45 kGy übersteigt, bleiben nach der Bestrahlung innere Spannungen zurück, was auf Oxidationszersetzungsprodukte im Harzformkörper zurückzuführen ist, wodurch es zu Verzerrungen und Kontraktionen kommen kann.The Irradiation dose is preferably at least 10 kGy and in particular 10 to 45 kGy. By Irradiation in this area leaves an arc extinguishing resin molding with the aforementioned favorable Properties due to the crosslinking achieved by the irradiation to reach. If the irradiation dose is below 10 kGy, the three-dimensional network structure formed by the crosslink bonds Inhomogeneous and unreacted crosslinker can bleed out. If the dose exceeds 45 kGy, remain after the irradiation internal tensions back, what due to oxidation decomposition products in the resin molding, causing distortion and contractions can come.

Ein auf diese Weise erhaltener erfindungsgemäßer Lichtbogenlösch-Harzformkörper weist eine hervorragende Beschaffenheit in Bezug auf Festigkeit, Druckbeständigkeit, Wärmebeständigkeit, Lichtbogen-Auslöschungsverhalten und flammhemmende Beschaffenheit auf und kann daher vorteilhafterweise in einem Lichtbogenlösch-Bauelement eines Trennschalters verwendet werden.One in this way obtained inventive arc extinguishing resin moldings exhibits an excellent quality in terms of strength, pressure resistance, Heat resistance, Arc extinguishing behavior and flame retardant and therefore can be advantageously in an arc extinguishing component a circuit breaker can be used.

Nachstehend wird ein erfindungsgemäßer Trennschalter beschrieben.below becomes an inventive disconnector described.

Der erfindungsgemäße Trennschalter umfasst einen fixierten Kontaktabschnitt mit einem fixierten Kontaktstück, einen beweglichen Kontaktabschnitt mit einem beweglichen Kontaktstück, das in Kontakt mit dem fixierten Kontaktabschnitt kommen kann und Öffnungs- und Schließvorgänge zusammen mit dem fixierten Kontaktabschnitt durchführen kann und ein Lichtbogenlösch-Bauelement, das einen bei den Öffnungs- und Schließvorgängen zwischen dem fixierten Kontaktabschnitt und dem beweglichen Kontaktabschnitt erzeugten Lichtbogen auslöscht, wobei das Lichtbogenlösch-Bauelement den vorstehend beschriebenen Lichtbogenlösch-Harzformkörper umfasst.Of the inventive circuit breaker includes a fixed contact portion with a fixed contact piece, a movable contact portion with a movable contact piece, the can come in contact with the fixed contact section and opening and closing operations together can perform with the fixed contact portion and an arc extinguishing component, the one at the opening and closing operations between the fixed contact portion and the movable contact portion extinguished arc, wherein the arc extinguishing component the above described arc quench resin moldings.

Ein spezielles Beispiel für einen derartigen Trennschalter ist in den 1 bis 3 dargestellt. 1 ist eine perspektivische Ansicht, die teilweise einen Schnitt zeigt. 2 ist eine perspektivische Ansicht des Lichtbogenlösch-Bauelements. 3 ist eine Schnittansicht des Trennschalters.A specific example of such a circuit breaker is in the 1 to 3 shown. 1 is a perspective view partially showing a section. 2 is a perspective view of the arc extinguishing component. 3 is a sectional view of the circuit breaker.

Gemäß 1 umfasst der Trennschalter einen fixierten Kontaktabschnitt 5 mit einer monolithischen Struktur, wobei ein Stromversorgungsanschluss 4 an einem Ende und eine U-förmige Biegung entlang eines beweglichen Kontaktabschnitts 1 am anderen Ende vorgesehen sind. Ferner umfasst der Trennschalter den beweglichen Kontaktabschnitt 1 mit einem beweglichen Kontaktstück 6, das mit einem fixierten Kontaktstück 7, das an der Spitze der U-Biegung 5a des fixierten Kontaktabschnittes vorgesehen ist, in Kontakt kommt. Am fixierten Kontaktabschnitt 5 ist ein Lichtbogenhorn 9 angebracht, das den zwischen dem beweglichen Kontaktstück 6 und dem fixierten Kontaktstück 7 entwickelten Lichtbogen in Richtung zum Lichtbogenlösch-Bauelement lenkt.According to 1 the circuit breaker comprises a fixed contact section 5 having a monolithic structure, wherein a power supply terminal 4 at one end and a U-shaped bend along a movable contact portion 1 are provided at the other end. Further, the circuit breaker comprises the movable contact portion 1 with a movable contact piece 6 that with a fixed contact piece 7 that is at the top of the U-bend 5a the fixed contact portion is provided, comes in contact. At the fixed contact section 5 is an arcing horn 9 attached, that between the movable contact piece 6 and the fixed contact piece 7 developed arc in the direction of the arc extinguishing component directs.

Das Lichtbogenlösch-Bauelement besteht aus einem Gitter 2 und einer Lichtbogen-Löschkammer 13. Das Gitter 2 ist aus einer Mehrzahl von Lagen (fünf Lagen in den Figuren) zusammengesetzt, die unter Einhaltung eines vorgegebenen Abstands zum Isolierkörper 12 gestapelt sind. Der bewegliche Kontaktabschnitt 1 übt eine Öffnungs- und Schließbewegung zwischen einer mit einer ausgezogenen Linie angegebenen geschlossenen Position und einer mit einer strichpunktierten Linie angegebenen geöffneten Position durch die V-förmige Kerbe 2a, die im Gitter 2 ausgebildet ist, aus. Die Lichtbogenlösch-Kammer 13, die aus einem erfindungsgemäßen Lichtbogenlösch-Harzformkörper gebildet ist, ist zwischen dem beweglichen Kontaktabschnitt 1 und dem Gitter 2 vorgesehen.The arc extinguishing component consists of a grid 2 and an arc quenching chamber 13 , The grid 2 is composed of a plurality of layers (five layers in the figures), which, while maintaining a predetermined distance to the insulator 12 are stacked. The movable contact section 1 performs an opening and closing movement between a closed position indicated by a solid line and an open position indicated by a one-dot chain line through the V-shaped notch 2a in the grid 2 is formed, out. The arc extinguishing chamber 13 formed of an arc extinguishing resin molded body according to the invention is between the movable contact portion 1 and the grid 2 intended.

Der in 1 und 3 dargestellte Isolierkörper 12 umfasst ein Paar von Seitenwänden 12a auf der linken und der rechten Seite und Verbindungsteile 12b und 12c, die die Seitenwände oben und unten verbinden. Der Isolierkörper ist monolithisch aus einem Melamin-Formharz, das gegen den Lichtbogen beständig ist, gebildet. Eine Mehrzahl von Rillen 14 mit rechteckigem Querschnitt ist auf den gegenüberliegenden Flächen des Paars von Seitenwänden 12a ausgebildet. Die Rillen steigen schräg vom Beladungsseitenende (rechtes Seitenende in 3) an. Die einzelnen Lagen des Gitters 2 sind durch Presspassung an die Rillen 14 angepasst und stellen eine Brücke zwischen den linken und rechten Seitenwänden 12a dar.The in 1 and 3 illustrated insulating body 12 includes a pair of side walls 12a on the left and right side and connecting parts 12b and 12c that connect the side walls above and below. The insulator is monolithically formed of a melamine resin molding which is resistant to the arc. A plurality of grooves 14 with rectangular cross-section is on the opposite faces of the pair of side walls 12a educated. The grooves rise obliquely from the load side end (right side end in 3 ) at. The individual layers of the grid 2 are by press fitting to the grooves 14 adapted and provide a bridge between the left and right side walls 12a represents.

Die Lichtbogen-Löschkammer 13 umfasst ein Paar von linken und rechten Seitenwänden 13a und eine Vorderwand 13b mit einer Bogenform, die die oberen Bereiche der linken und rechten Seitenwände 13a entlang der V-förmigen Kerbe 2a im Gitter 2 verbindet. Die Lichtbogen-Löschkammer 13 umfasst ferner eine Trennwand 15, die das Lichtbogen-Auslöschbauelement von einem Öffnungs-Schließ-Mechanismus trennt, und eine Isolierabdeckung 16, die den fixierten Kontaktabschnitt 5 bedeckt, wobei die Trennwand und die Isolierabdeckung monolithisch in der Lichtbogen-Löschkammer ausgebildet sind. Die Trennwand 15 ist mit einem Schlitz 15a versehen, der entlang des Wegs der Öffnungs-Schließ-Bewegung des beweglichen Kontaktabschnitts ausgebildet ist. Die Isolierabdeckung 16 ist mit einem Fenster 16a versehen, das das fixierte Kontaktstück 7 freigibt. Die Lichtbogen-Löschkammer 13 ist innen im Isolierkörper 12 auf der rechten Seite von 3 montiert, wobei die Trennwand 15 in Kontakt mit der rechten Endfläche der Seitenwände 12a des Isolierkörpers 12 steht. Die Lichtbogen-Löschkammer 13 ruht auf dem fixierten Kontaktabschnitt 5, wobei sich dazwischen die Isolierabdeckung 16 befindet, und wird von einer Hauptkörperabdeckung (in den Figuren nicht dargestellt) des Trennschalters angepresst und fixiert. In diesem montierten Zustand bedecken die Seitenwände 13a der Lichtbogen-Löschkammer 13 die Schenkelbereiche des Gitters 2 (die Bereiche an beiden Seiten der V-förmigen Kerbe), das an beiden Seiten des beweglichen Kontaktabschnitts auf der Innenseite positioniert ist. Die Vorderwand 13b befindet sich hinter der V-förmigen Kerbe 2a der obersten Lage des Gitters 2, wie in 3 dargestellt ist.The arc extinguishing chamber 13 includes a pair of left and right side walls 13a and a front wall 13b with an arched shape covering the upper areas of the left and right sidewalls 13a along the V-shaped notch 2a in the grid 2 combines. The arc extinguishing chamber 13 further comprises a partition wall 15 which separates the arc extinguishing member from an opening-closing mechanism, and an insulating cover 16 that the fixed contact section 5 covered, with the partition and the Iso lierabdeckung monolithically formed in the arc-quenching chamber. The partition 15 is with a slot 15a provided along the path of the opening-closing movement of the movable contact portion. The insulating cover 16 is with a window 16a provided that the fixed contact piece 7 releases. The arc extinguishing chamber 13 is inside in the insulator 12 on the right side of 3 mounted, with the dividing wall 15 in contact with the right end surface of the sidewalls 12a of the insulating body 12 stands. The arc extinguishing chamber 13 resting on the fixed contact section 5 , with the insulating cover between them 16 is and is pressed by a main body cover (not shown in the figures) of the circuit breaker and fixed. In this mounted condition, the side walls cover 13a the arc extinguishing chamber 13 the leg portions of the grid 2 (the regions on both sides of the V-shaped notch) positioned on both sides of the movable contact portion on the inside. The front wall 13b is located behind the V-shaped notch 2a the topmost layer of the grid 2 , as in 3 is shown.

Beim Stromunterbrechungsvorgang entsteht in der vorstehend beschriebenen Struktur ein Lichtbogen zwischen den beweglichen und fixierten Kontaktstücken 6 und 7, und der Lichtbogen bewegt sich zum Gitter 2 hin und wird dort ausgelöscht. Da die beiden Schenkelbereiche des Gitters 2 durch die Seitenwände 13a der Lichtbogen-Löschkammer 13 abgedeckt und gegen den Lichtbogen bei diesem Stromunterbrechungsvorgang abgeschirmt sind, wird ein Schmelzen und Zerstäuben dieser Bereiche des Gitters durch den Lichtbogen verhindert, und ferner wird ein thermisches Zersetzungsgas von den Seitenwänden 13a in der Nähe des Lichtbogens erzeugt und emittiert, was ein Abkühlen des Lichtbogens und dessen rasches Auslöschen fördert.In the current interruption process, in the structure described above, an arc is generated between the movable and fixed contact pieces 6 and 7 , and the arc moves to the grid 2 there and is wiped out there. Since the two leg portions of the grid 2 through the side walls 13a the arc extinguishing chamber 13 are shielded and shielded against the arc in this current interruption process, melting and sputtering of these areas of the grid by the arc is prevented, and further, a thermal decomposition gas from the side walls 13a generated and emitted in the vicinity of the arc, which promotes cooling of the arc and its rapid extinction.

BeispieleExamples

Nachstehend wird die vorliegende Erfindung ausführlich unter Bezugnahme auf einige bevorzugte Ausführungsformen beschrieben. Die Erfindung ist jedoch nicht auf diese Beispiele beschränkt.below The present invention will be described in detail with reference to some preferred embodiments described. However, the invention is not limited to these examples limited.

Beispiel 1example 1

Zunächst wurden 67 Gew.-teile Polyolefinharz (EVAL-L104B, Produkt der Fa. Kuraray Co., Ltd.) mit einem Gehalt an 0,58 Mol Hydroxylgruppen, bezogen auf 1 Mol Methylengruppen, und 25 Gew.-teile eines Polyoxymethylen-Oxyethylen-Copolymeren (Tenac-C 4520, Produkt der Fa. Asahi Kasei Corporation) mit einem Gehalt an 90 Mol-% Struktureinheiten, die sich von Oxymethylen ableiten, geschmolzen und vermischt. Anschließend wurden 8 Gewichtsteile der Verbindung der Formel (I-14) als reaktives, organisches flammhemmendes Mittel auf Phosphorbasis zugesetzt. Das erhaltene Gemisch wurde bei 220 °C unter Verwendung eines Doppelschneckenextruders vom Seitenstromtyp (Produkt der Fa. Japan Steel Works, Ltd.) zur Bildung von Harzpellets verknetet. Die Harzpellets wurden 7 Stunden bei 80 °C getrocknet und sodann bei einer Harztemperatur von 215 °C und einer Werkzeugtemperatur von 50 °C unter Verwendung einer Spritzgießmaschine (Typ α50C der Fa. FANUC Ltd.) verformt. Der Querschnitt des Formkörpers wurde durch Rasterelektronenmikroskopie betrachtet. Es wurde die Bildung einer Mikrophasen-Trennstruktur bestätigt, wobei sich eine Spherulit-Struktur mit einer Lamellenkonfiguration und eine homogene See-Insel-Struktur zeigten.At first were 67 parts by weight of polyolefin resin (EVAL-L104B, product of Kuraray Co., Ltd.) containing 0.58 moles of hydroxyl groups to 1 mole of methylene groups, and 25 parts by weight of a polyoxymethylene-oxyethylene copolymer (Tenac-C 4520, product of the company Asahi Kasei Corporation) with a content at 90 mol% of structural units derived from oxymethylene, melted and mixed. Subsequently, 8 parts by weight the compound of the formula (I-14) as a reactive organic flame retardant Phosphorus-based agent added. The resulting mixture was at 220 ° C using a twin-screw extruder of the sidestream type (Product of Japan Steel Works, Ltd.) for forming resin pellets kneaded. The resin pellets were dried at 80 ° C for 7 hours and then at a resin temperature of 215 ° C and a mold temperature from 50 ° C using an injection molding machine (type α50C Fa. FANUC Ltd.) deformed. The cross section of the shaped body was determined by scanning electron microscopy considered. It was the formation of a microphase separation structure approved, wherein a spherulite structure with a lamellar configuration and showed a homogeneous sea-island structure.

Anschließend wurde der Formkörper mit γ-Strahlen aus einer Kobalt 60-Quelle mit einer Dosis von 25 kGy bestrahlt. Auf diese Weise wurde der Lichtbogenlösch-Harzformkörper von Beispiel 1 erhalten. Der Querschnitt dieses Lichtbogenlösch-Harzformkörpers wurde mit einem Rasterelektronenmikroskop betrachtet. Die Bildung einer Mikrophasen-Trennstruktur wurde bestätigt, wobei sich eine Spherulit-Struktur mit einer Lamellenkonfiguration und eine homogene See-Insel-Struktur zeigten.Subsequently was the molded body with γ-rays irradiated from a cobalt 60 source at a dose of 25 kGy. In this way, the arc extinguishing resin molded body of Example 1 obtained. The cross section of this arc extinguishing resin molding was viewed with a scanning electron microscope. The formation of a Microphase separation structure was confirmed to be a spherulite structure with a lamella configuration and a homogeneous sea-island structure showed.

Beispiel 2Example 2

Zunächst wurden 50 Gew.-teile eines Polyolefinharzes (EVAL-L104B, Produkt der Fa. Kuraray Co., Ltd.) mit einem Gehalt an 0,58 Mol Hydroxylgruppen, bezogen auf 1 Mol Methylengruppen, und 20 Gew.-teile eines Polyoxymethylen-Oxyethylen-Copolymeren (Tenac-C 4520, Produkt der Fa. Asahi Kasei Corporation) mit einem Gehalt an 90 Mol-% Struktureinheiten, die sich von Oxymethylen ableiteten, geschmolzen und vermischt. Anschließend wurden 10 Gew.-teile Boehmit (BMT-10, Produkt der Fa. Kawai Lime Co., Ltd.), 15 Gew.-teile mit Silan behandelte Glasfasern (03.JAFT2Ak25, Produkt der Fa. Asahi Fiber Glass Co., Ltd.) als anorganische Füllstoffmaterialien und 5 Gew.-teile der Verbindung der Formel (II-3) als reaktives, organisches flammhemmendes Mittel auf Phosphorbasis zugesetzt. Das erhaltene Gemisch wurde bei 220 °C unter Verwendung eines Doppelschneckenextruders vom Seitenstromtyp (Produkt der Fa. Japan Steel Works, Ltd.) zur Bildung von Harzpellets verknetet. Die Pellets wurden 7 Stunden bei 80 °C getrocknet und sodann bei einer Harztemperatur von 215 °C und einer Werkzeugtemperatur von 50 °C unter Verwendung einer Spritzgießmaschine (Typ α50C, Produkt der Fa. FANUC Ltd.) verformt. Der Querschnitt des Formkörpers wurde mit einem Rasterelektronenmikroskop betrachtet. Es wurde die Bildung einer Mikrophasen-Trennstruktur bestätigt, die eine Spherulit-Struktur mit einer Lamellenkonfiguration und eine homogene See-Insel-Struktur zeigte.First, 50 parts by weight of a polyolefin resin (EVAL-L104B, product of Kuraray Co., Ltd.) containing 0.58 mole of hydroxyl groups based on 1 mole of methylene groups and 20 parts by weight of a polyoxymethylene were used. Oxyethylene copolymers (Tenac-C 4520, product of Asahi Kasei Corporation) containing 90 mol% of structural units derived from oxymethylene are melted and mixed. Subsequently, 10 parts by weight of boehmite (BMT-10, product of Kawai Lime Co., Ltd.), 15 parts by weight of silane-treated glass fibers (03.JAFT2Ak25, product of Asahi Fiber Glass Co., Ltd.) as inorganic filler materials and 5 parts by weight of the compound of the formula (II-3) as a phosphorus-based reactive organic flame retardant. The resulting mixture was kneaded at 220 ° C using a side-flow type twin-screw extruder (product of Japan Steel Works, Ltd.) to form resin pellets. The pellets were dried at 80 ° C for 7 hours and then at a resin temperature of 215 ° C and a mold temperature of 50 ° C using a Spritzgießma machine (type α50C, product of FANUC Ltd.) deformed. The cross section of the molded article was observed with a scanning electron microscope. The formation of a microphase separation structure confirming spherulite structure with a lamellar configuration and a homogeneous sea-island structure was confirmed.

Anschließend wurde der Formkörper mit γ-Strahlen aus einer Kobalt 60-Quelle in einer Dosis von 25 kGy bestrahlt. Auf diese Weise wurde der Lichtbogenlösch-Harzformkörper von Beispiel 2 erhalten. Der Querschnitt dieses Lichtbogenlösch-Harzformkörpers wurde mit einem Rasterelektronenmikroskop betrachtet. Die Bildung einer Mikrophasen-Trennstruktur wurde bestätigt, wobei sich eine Spherulit-Struktur mit einer Lamellenkonfiguration und eine homogene See-Insel-Struktur zeigten.Subsequently was the molded body with γ-rays irradiated from a cobalt 60 source at a dose of 25 kGy. In this way, the arc extinguishing resin molded body of Example 2 obtained. The cross section of this arc extinguishing resin molding was viewed with a scanning electron microscope. The formation of a Microphase separation structure was confirmed to be a spherulite structure with a lamella configuration and a homogeneous sea-island structure showed.

Beispiel 3Example 3

Zunächst wurden 53 Gew.-teile eines Polyolefinharzes (EVAL-L104B, Produkt der Fa. Kuraray Co., Ltd.) mit einem Gehalt an 0,58 Mol Hydroxylgruppen, bezogen auf 1 Mol Methylengruppen, und 20 Gew.-teile eines Polyoxymethylen-Oxyethylen-Copolymeren (Tenac-C 4520, Produkt der Fa. Asahi Kasei Corporation) mit einem Gehalt an 90 Mol-% Struktureinheiten, die sich von Oxymethylen ableiteten, bei 220 °C unter einer Stickstoffgasatmosphäre geschmolzen und vermischt. Anschließend wurden 15 Gew.-teile Boehmit (BMT-10, Produkt der Fa. Kawai Lime Co., Ltd.) als anorganische Füllstoffmaterialien und 12 Gew.-teile der Verbindung der Formel (I-18) als reaktives, organisches flammhemmendes Mittel auf Phosphorbasis zugesetzt. Das erhaltene Gemisch wurde bei 220 °C unter Verwendung eines Doppelschneckenextruders vom Seitenstromtyp (Produkt der Fa. Japan Steel Works, Ltd.) unter Stickstoffgas zur Bildung von Harzpellets verknetet. Die Pellets wurden 7 Stunden bei 80 °C getrocknet und sodann unter Stickstoffgasatmosphäre bei einer Harztemperatur von 215 °C und einer Werkzeugtemperatur von 50 °C unter Verwendung einer Spritzgießmaschine (Typ α50C, Produkt der Fa. FANUC Ltd.) verformt. Der Querschnitt des Formkörpers wurde mit einem Rasterelektronenmikroskop betrachtet. Es wurde die Bildung einer Mikrophasen-Trennstruktur bestätigt, wobei sich eine Spherulit-Struktur mit einer Lamellenkonfiguration und eine homogene See-Insel-Struktur zeigten.At first were 53 parts by weight of a polyolefin resin (EVAL-L104B, product of the Fa. Kuraray Co., Ltd.) containing 0.58 moles of hydroxyl groups, based on 1 mole of methylene groups, and 20 parts by weight of a polyoxymethylene-oxyethylene copolymer (Tenac-C 4520, product of the company Asahi Kasei Corporation) with a Content of 90 mol% of structural units derived from oxymethylene, at 220 ° C under a nitrogen gas atmosphere melted and mixed. Subsequently, 15 parts by weight of boehmite (BMT-10, product of Kawai Lime Co., Ltd.) as inorganic filler and 12 parts by weight of the compound of formula (I-18) as a reactive, organic phosphorus-based flame retardant added. The The resulting mixture was at 220 ° C using a twin-screw extruder of the side stream type (product from Japan Steel Works, Ltd.) under nitrogen gas for formation kneaded by resin pellets. The pellets were dried at 80 ° C for 7 hours and then under a nitrogen gas atmosphere at a resin temperature of 215 ° C and a mold temperature of 50 ° C using an injection molding machine (type α50C, product Fa. FANUC Ltd.) deformed. The cross section of the molding was viewed with a scanning electron microscope. It was the education of a microphase separation structure confirming a spherulite structure with a lamella configuration and a homogeneous sea-island structure showed.

Anschließend wurde der Formkörper mit γ-Strahlen aus einer Kobalt 60-Quelle in einer Dosis von 25 kGy bestrahlt. Auf diese Weise wurde der Lichtbogenlösch-Harzformkörper von Beispiel 3 erhalten. Der Querschnitt dieses Lichtbogenlösch-Harzformkörpers wurde mit einem Rasterelektronenmikroskop betrachtet. Es wurde die Bildung einer Mikrophasen-Trennstruktur bestätigt, wobei sich eine Spherulit-Struktur mit einer Lamellenkonfiguration und eine homogene See-Insel-Struktur zeigten.Subsequently was the molded body with γ-rays irradiated from a cobalt 60 source at a dose of 25 kGy. In this way, the arc extinguishing resin molded body of Example 3 obtained. The cross section of this arc extinguishing resin molding was viewed with a scanning electron microscope. It was the education of a microphase separation structure confirming a spherulite structure with a lamella configuration and a homogeneous sea-island structure showed.

Vergleichsbeispiel 1Comparative Example 1

Die Harzpellets von Vergleichsbeispiel 1 wurden durch Verkneten unter den gleichen Bedingungen wie in Beispiel 1 erhalten, mit der Ausnahme, dass kein reaktives, organisches flammhemmendes Mittel auf Phosphorbasis zugemischt wurde. Die erhaltenen Pellets wurden 7 Stunden bei 80 °C getrocknet und sodann bei einer Harztemperatur von 215 °C und einer Werkzeugtemperatur von 50 °C unter Verwendung einer Spritzgießmaschine (Typ α50C, Produkt der Fa. FANUC Ltd.) verformt. Auf diese Weise wurde der Lichtbogenlösch-Harzformkörper von Vergleichsbeispiel 1 erhalten.The Resin pellets of Comparative Example 1 were by kneading under the same conditions as in Example 1, with the exception that that is not a reactive organic phosphorus-based flame retardant was mixed. The obtained pellets were dried at 80 ° C for 7 hours and then at a resin temperature of 215 ° C and a mold temperature from 50 ° C using an injection molding machine (type α50C, product Fa. FANUC Ltd.) deformed. In this way, the arc extinguishing resin molded body of Comparative Example 1 obtained.

Vergleichsbeispiel 2Comparative Example 2

Die Harzpellets von Vergleichsbeispiel 2 wurden durch Verkneten unter den gleichen Bedingungen wie in Beispiel 2 erhalten, mit der Ausnahme, dass kein reaktives, organisches flammhemmendes Mittel auf Phosphorbasis zugemischt wurde. Die erhaltenen Pellets wurden 7 Stunden bei 80 °C getrocknet und sodann bei einer Harztemperatur von 215 °C und einer Werkzeugtemperatur von 50 °C unter Verwendung einer Spritzgießmaschine (Typ α50C, Produkt der Fa. FANUC Ltd.) verformt. Auf diese Weise wurde der Lichtbogenlösch-Harzformkörper von Vergleichsbeispiel 2 erhalten.The Resin pellets of Comparative Example 2 were by kneading under the same conditions as in example 2, with the exception that is not a reactive organic phosphorus-based flame retardant was mixed. The obtained pellets were dried at 80 ° C for 7 hours and then at a resin temperature of 215 ° C and a mold temperature from 50 ° C using an injection molding machine (type α50C, product Fa. FANUC Ltd.) deformed. In this way, the arc extinguishing resin molded body of Comparative Example 2 obtained.

Vergleichsbeispiel 3Comparative Example 3

Der Lichtbogenlösch-Harzformkörper von Vergleichsbeispiel 3 wurde auf die gleiche Weise wie in Beispiel 2 erhalten, mit der Ausnahme, dass das in Beispiel 2 verwendete reaktive, organische flammhemmende Mittel auf Phosphorbasis durch ein organisches flammhemmendes Mittel auf Phosphorbasis ersetzt wurde, bei dem es sich um einen Additivtyp handelte und das keine Reaktivität aufwies ("HCA-HQ", Produkt der Firma Sanko Chemical Industry Co., Ltd.)Of the Arc quenching resin molding of Comparative Example 3 was carried out in the same manner as in Example 2, with the exception that used in Example 2 reactive organic phosphorus-based flame retardants replaced a phosphorus-based organic flame retardant which was an additive type and none Reactivity ("HCA-HQ", product of Sanko Chemical Industry Co., Ltd.)

Vergleichsbeispiel 4Comparative Example 4

Der Lichtbogenlösch-Harzformkörper von Vergleichsbeispiel 4 wurde auf die gleiche Weise wie in Beispiel 2 erhalten, mit der Ausnahme, dass das in Beispiel 2 verwendete reaktive, organische flammhemmende Mittel auf Phosphorbasis durch ein bromhaltiges flammhemmendes Mittel ersetzt wurde ("Great Lakes pdbs-80", Produkt der Firma Great Lakes Chemical Corporation).Of the Arc quenching resin molding of Comparative Example 4 was carried out in the same manner as in Example 2, with the exception that used in Example 2 reactive organic phosphorus-based flame retardants a bromine-containing flame retardant was replaced ("Great Lakes pdbs-80", product of the company Great Lakes Chemical Corporation).

Vergleichsbeispiel 5Comparative Example 5

Der Lichtbogenlösch-Harzformkörper von Vergleichsbeispiel 5 wurde auf die gleiche Weise wie in Beispiel 2 erhalten, mit der Ausnahme, dass das Polyolefinharz (EVAL-L104B, Produkt der Fa. Kuraray Co., Ltd.) mit einem Gehalt an 0,58 Mol Hydroxylgruppen, bezogen auf 1 Mol Methylengruppen, das in Beispiel 2 verwendet worden war, durch ein Polyethylenharz (HJ362, Produkt der Fa. Nippon Polyethylene Corporation) ersetzt wurde.Of the Arc quenching resin molding of Comparative Example 5 was carried out in the same manner as in Example 2, with the exception that the polyolefin resin (EVAL-L104B, Product of the company Kuraray Co., Ltd.) containing 0.58 mol Hydroxyl groups, based on 1 mol of methylene groups, in Example 2 was replaced by a polyethylene resin (HJ362, product from Nippon Polyethylene Corporation).

Vergleichsbeispiel 6Comparative Example 6

Zunächst wurden 25 Gew.-teile eines ungesättigten Polyesterharzes (7527, Produkt der Fa. Japan U-PiCA Co., Ltd.), 35 Gew.-teile Al(OH)₃, 5 Gew.-teile eines Styrol-Vinylacetat-Copolymeren, 0,3 Gew.-teile des Polymerisationsinitiators tert.-Butylperoxid-Z und 4,7 Gew.-teile eines Mittels zur Einstellung der Viskosität unter Verwendung eines Kneters verknetet. Beim Knetvorgang wurden 35 Gew.-teile eines anorganischen Füllstoffes in Form von mit Silan behandelten Glasfasern (03.JAFT2Ak25, Produkt der Fa. Asahi Fiber Glass Co., Ltd.) zugesetzt und dispergiert. Man erhielt eine Formmasse. Die Formmasse wurde bei einer Temperatur im Bereich von 140 bis 150 °C verformt und polymerisiert. Auf diese Weise erhielt man den Lichtbogenlösch-Harzformkörper von Vergleichsbeispiel 6.First, 25 parts by weight of an unsaturated polyester resin (7527, product of Japan U-PiCA Co., Ltd.), 35 parts by weight of Al (OH) ₃ , 5 parts by weight of a styrene-vinyl acetate copolymer 0.3 part by weight of the polymerization initiator is kneaded with tert-butyl peroxide-Z and 4.7 parts by weight of a viscosity adjusting agent using a kneader. In the kneading process, 35 parts by weight of an inorganic filler in the form of silane-treated glass fibers (03.JAFT2Ak25, product of Asahi Fiber Glass Co., Ltd.) was added and dispersed. A molding material was obtained. The molding compound was molded and polymerized at a temperature in the range of 140 to 150 ° C. Thus, the arc extinguishing resin molded body of Comparative Example 6 was obtained.

Vergleichsbeispiel 7Comparative Example 7

Harzpellets wurden durch Verkneten von 99,8 Gew.-teilen Nylon 6-Harz (UBE-Nylon 1015B, Produkt der Fa. UBE Industries, Ltd.) und 0,2 Gew.-teilen eines Antioxidationsmittels (IRGANOX 1010, Produkt der Fa. Nihon Ciba-Geigy K.K) erhalten. Die Harzpellets wurden 4 Stunden bei 105 °C getrocknet und sodann bei einer Harztemperatur von 260 °C und einer Werkzeugtemperatur von 85 °C unter Verwendung einer Spritzgießmaschine (Typ α50C, Produkt der Fa. FANUC Ltd.) verformt. Auf diese Weise erhielt man den Lichtbogenlösch-Harzformkörper von Vergleichsbeispiel 7.resin pellets were kneaded by kneading 99.8 parts by weight of nylon 6 resin (UBE nylon 1015B, product of UBE Industries, Ltd.) and 0.2 parts by weight an antioxidant (IRGANOX 1010, product of Nihon Ciba-Geigy K.K). The resin pellets were dried at 105 ° C for 4 hours and then at a resin temperature of 260 ° C and a mold temperature of 85 ° C using an injection molding machine (type α50C, product Fa. FANUC Ltd.) deformed. In this way, there was obtained the arc-quenching resin molded article of Comparative Example 7.

Die Formgebungseigenschaften der Lichtbogenlösch-Harzformkörper der Beispiele 1 bis 3 und der Vergleichsbeispiele 1 bis 7 wurden bewertet. Die Lichtbogenlösch-Harzformkörper wurden Kurzschlusstests, Wärmebeständigkeitstests und Tests auf die flammhemmende Beschaffenheit unterworfen, wobei die Formkörper für die Lichtbogen-Löschkammer 13 eines Trennschalters gemäß Darstellung in 1 verwendet wurden.The molding properties of the arc-extinguishing resin moldings of Examples 1 to 3 and Comparative Examples 1 to 7 were evaluated. The arc extinguishing resin moldings were subjected to short circuit tests, heat resistance tests, and flame retardant tests wherein the moldings for the arc quenching chamber 13 a circuit breaker as shown in 1 were used.

Beim Kurzschlusstest wurde ein elektrischer Strom von 3-Phasen 440 V/50 kA durch die Kontaktstücke im geschlossenen Zustand geleitet. Anschließend wurde der bewegliche Kontaktabschnitt geöffnet, um einen Lichtbogenstrom zu erzeugen. Die Prüfung umfasste die Unterbrechungseigenschaften des Lichtbogenstroms (Lichtbogen-Auslöschverhalten), den Bruch und die Beschädigung des Lichtbogen-Auslöschbauelements (Druckbeständigkeit) und die Oberflächenbedingungen (Wärmebeständigkeit).At the Short circuit test was an electric current of 3-phase 440 V / 50 Not specified by the contact pieces passed in the closed state. Subsequently, the movable contact portion became open, to generate an arc current. The test included the interruption characteristics the arc current (arc extinguishing behavior), the rupture and the damage of the arc extinguishing component (Pressure resistance) and the surface conditions (Heat resistance).

Die Stromunterbrechungseigenschaften wurden als "akzeptabel" bezeichnet, wenn der Kurzschlussstrom in erfolgreicher Weise unterbrochen wurde.The Power interruption characteristics were termed "acceptable" when the short circuit current was successfully interrupted.

Die Formgebungseigenschaften wurden als "akzeptabel" bezeichnet, wenn bei visueller Betrachtung keine Erzeugung von Bläschen oder "Drooling" erfolgten.The Shaping properties were termed "acceptable" when visual Generation of bubbles or "drooling".

Die flammhemmenden Eigenschaften wurden gemäß dem UL-94-Test folgendermaßen bewertet. Ein Prüfkörper (Länge 5 Zoll, Breite 1/2 Zoll und Dicke 3,2 mm) wurde gemäß UL-94 hergestellt. Der Prüfkörper wurde vertikal angeordnet und 10 Sekunden in Kontakt mit der Flamme eines Bunsenbrenners gebracht. Die Entzündungszeit wurde aufgezeichnet. Nach Auslöschen wurde der Prüfkörper erneut 10 Sekunden in Kontakt mit der Flamme gebracht und die Entzündungszeit wurde wieder aufgezeichnet. Eine Bewertung wurde gemäß UL-94 auf der Grundlage der gesamten Entzündungszeit, der Nachglühzeit nach dem zweiten Auslöschen und das brennende Abtropfen (Entzündung von Watte) vorgenommen.The Flame retardant properties were evaluated according to the UL-94 test as follows. A specimen (length 5 inches, Width 1/2 inch and thickness 3.2 mm) was made according to UL-94. The test specimen was arranged vertically and in contact with the flame of a 10 seconds Bunsen burner brought. The inflammation time was recorded. After extinguishing the specimen was again Brought into contact with the flame for 10 seconds and the inflammation time was recorded again. A rating was made according to UL-94 based on the total inflammation time, afterglow time after the second extinguishing and the burning dripping (inflammation of cotton wool) made.

Der Metallverunreinigungszustand wurde durch Messen des Kontaktwiderstands nach 300-stündigem Belassen des Prüfkörpers in einer Umgebung von 120 °C bewertet. Wenn der Kontaktwiderstand nicht höher als 50 mΩ war, wurde der Metallverunreinigungszustand als "akzeptabel" bezeichnet.Of the Metal contamination state was determined by measuring the contact resistance after leaving for 300 hours of the test specimen in an environment of 120 ° C rated. If the contact resistance was not higher than 50mΩ, then the metal contamination state is called "acceptable".

Die Ergebnisse der vorstehend beschriebenen Tests sind in Tabelle 1 zusammengestellt. Tabelle 1 Kurzschlusstest Stromunterbrechungseigenschaft (Lichtbogen-Auslöschungsverhalten) Bruch und Beschädigung (Druckbeständigkeit) Oberflächenzustand (Wärmebeständigkeit) Formgebungseigenschaften Flammhemmende Beschaffenheit (UL-94) Metallverunreinigung Beispiel 1 Akzeptabel (gute Stromunterbrechungseigenschaften) Akzeptabel (keine Schädigung) Gut Gut V-0 Akzeptabel Beispiel 2 Akzeptabel (gute Stromunterbrechungseigenschaften) Akzeptabel (keine Schädigung) Gut Gut V-0 Akzeptabel Beispiel 3 Akzeptabel (gute Stromunterbrechungseigenschaften) Akzeptabel (keine Schädigung) Gut Gut V-0 Akzeptabel Vergl.-bsp. 1 Akzeptabel (gute Stromunterbrechungseigenschaften) Schädigung Gut Gut HB Akzeptabel Vergl.-bsp. 2 Akzeptabel (gute Stromunterbrechungseigenschaften) Schädigung Gut Gut HB Akzeptabel Vergl.-bsp. 3 Akzeptabel (gute Stromunterbrechungseigenschaften) Schädigung Gut Gut V-2 Inakzeptabel Vergl.-bsp. 4 Akzeptabel (gute Stromunterbrechungseigenschaften) Schädigung Gut Gut V-0 Inakzeptabel Vergl.-bsp. 5 inakzeptabel Schädigung Gut Gut HB Akzeptabel Vergl.-bsp. 6 Akzeptabel (gute Stromunterbrechungseigenschaften) Schädigung Gut Schlecht (Gratbildung) V-1 Akzeptabel Kurzschlusstest Stromunterbrechungseigenschaft (LichtbogenAuslöschungsverhalten) Bruch und Beschädigung (Druckbeständigkeit) Oberflächenzustand (Wärmebeständigkeit) Formgebungseigenschaften Flammhemmende Beschaffenheit (UL-94) Metallverunreinigung Vergl.-bsp. 7 Akzeptabel (gute Stromunterbrechungseigenschaften) Schädigung Gut Schlecht ("Drooling") HB Akzeptabel The results of the tests described above are summarized in Table 1. Table 1 Short-circuit test Power interruption characteristic (Arc extinguishing behavior) Breakage and damage (pressure resistance) Surface condition (heat resistance) molding properties Flame Retardant Texture (UL-94) metal contamination example 1 Acceptable (good current interruption properties) Acceptable (no damage) Well Well V-0 Acceptable Example 2 Acceptable (good current interruption properties) Acceptable (no damage) Well Well V-0 Acceptable Example 3 Acceptable (good current interruption properties) Acceptable (no damage) Well Well V-0 Acceptable Comparative Ex. 1 Acceptable (good current interruption properties) damage Well Well HB Acceptable Comparative Ex. 2 Acceptable (good current interruption properties) damage Well Well HB Acceptable Comparative Ex. 3 Acceptable (good current interruption properties) damage Well Well V-2 Unacceptable Comparative Ex. 4 Acceptable (good current interruption properties) damage Well Well V-0 Unacceptable Comparative Ex. 5 unacceptable damage Well Well HB Acceptable Comparative Ex. 6 Acceptable (good current interruption properties) damage Well Bad (burrs) V-1 Acceptable Short-circuit test Power interruption characteristic (arc extinction behavior) Breakage and damage (pressure resistance) Surface condition (heat resistance) molding properties Flame Retardant Texture (UL-94) metal contamination Comparative Ex. 7 Acceptable (good current interruption properties) damage Well Bad ("Drooling") HB Acceptable

Aus den Ergebnissen von Tabelle 1 geht hervor, dass die Lichtbogenlösch-Harzformkörper der Beispiele 1 bis 3 eine gute Beschaffenheit in bezug auf flammhemmende Eigenschaften, Wärmebeständigkeit und Formgebungseigenschaften aufwiesen. Die Trennschalter unter Verwendung der Lichtbogenlösch-Bauelemente aus diesen Lichtbogenlösch-Harzformkörpern führen in wirksamer Weise zu einer Auslöschung des zwischen den Kontaktstücken beim Stromunterbrechungsvorgang entwickelten Lichtbogens. Es wurde keine Beschädigung der Lichtbogen-Löschkammer aufgrund des Lichtbogen-Auslöschvorgangs festgestellt.Out From the results of Table 1, it can be seen that the arc extinguishing resin moldings of Examples 1 to 3 a good condition with respect to flame retardant Properties, heat resistance and molding properties. The circuit breaker under Use of arc extinguishing components lead from these arc extinguishing resin moldings in effective way to extinction of between the contact pieces during the power interruption process developed arc. It was no damage the arc extinguishing chamber due to the arc extinguishing process detected.

Claims

Lichtbogenlösch-Harzformkörper, umfassend eine Harzzusammensetzung, die ein Polyolefinharz (A) enthält, bei dem ein Teil der Wasserstoffatome in einer Methylenkette durch Hydroxylgruppen ersetzt ist und die Hydroxylgruppen in einer Menge im Bereich von 0,2 bis 0,7 Mol, bezogen auf 1 Mol der Methylengruppen, enthalten sind, wobei die Harzzusammensetzung zusätzlich ein reaktives, organisches flammhemmendes Mittel auf Phosphorbasis (B) mit einer ungesättigten Endbindung enthält, wobei der Harzformkörper nach einem Formgebungsvorgang einer Bestrahlung zur Vernetzung ausgesetzt wurde.Arc quenching resin molding, comprising a resin composition containing a polyolefin resin (A) a part of the hydrogen atoms in a methylene chain by hydroxyl groups is replaced and the hydroxyl groups in an amount ranging from 0.2 to 0.7 mol, based on 1 mol of the methylene groups are, wherein the resin composition additionally a reactive, organic Phosphorus-based flame retardant (B) with an unsaturated compound Contains end binding, wherein the resin molded body exposed to radiation after a molding operation for irradiation has been.

Lichtbogenlösch-Harzformkörper nach Anspruch 1, bei dem die Harzzusammensetzung ferner ein Polyacetalharz (C) in einer Menge im Bereich von 5 bis 90 Gew.-teilen, bezogen auf 100 Gew.-teile des Polyolefinharzes (A) enthält, wobei das Polyacetalharz (C) Struktureinheiten, die von Oxymethylen abgeleitet sind, in einem Anteil im Bereich von 75 bis 100 Mol-% enthält.Arc extinguishing resin moldings after Claim 1, wherein the resin composition further comprises a polyacetal resin (C) in an amount ranging from 5 to 90 parts by weight, based to 100 parts by weight of the polyolefin resin (A), wherein the polyacetal resin (C) Structural units derived from oxymethylene in one Contains fraction in the range of 75 to 100 mol%.

Lichtbogenlösch-Harzformkörper nach einem der Ansprüche 1 oder 2, bei dem die Harzzusammensetzung ferner einen oder mehrere Arten eines anorganischen Füllstoffes (D) enthält, der aus der Gruppe ausgewählt ist, die aus Glasfasern, Bariumtitanat-Whiskers, feinen Silicagel-Teilchen, Boehmit, Talcum, Magnesiumcarbonat und einem Metallhydroxid besteht, wobei der Anteil des anorganischen Füllstoffes im Bereich von 1 bis 70 Gew.-% liegt.Arc extinguishing resin moldings after one of the claims 1 or 2, wherein the resin composition further comprises one or more Types of inorganic filler Contains (D) who is selected from the group made of glass fibers, barium titanate whiskers, fine silica gel particles, boehmite, Talcum, magnesium carbonate and a metal hydroxide, wherein the proportion of the inorganic filler in the range of 1 to 70 wt .-% is.

Lichtbogenlösch-Harzformkörper nach einem der Ansprüche 1 bis 3, bei dem das Polyolefinharz (A) eine latente Zersetzungswärme von mindestens 30 cal/g aufweist.Arc extinguishing resin moldings after one of the claims 1 to 3, wherein the polyolefin resin (A) has a latent heat of decomposition of at least 30 cal / g.

Lichtbogenlösch-Harzformkörper nach einem der Ansprüche 1 bis 4, bei dem es sich beim Polyolefinharz (A) um ein Ethylen-Vinylalkohol-Copolymeres handelt.Arc extinguishing resin moldings after one of the claims 1 to 4, wherein the polyolefin resin (A) is an ethylene-vinyl alcohol copolymer is.

Lichtbogenlösch-Harzformkörper nach einem der Ansprüche 1 bis 5, bei dem es sich beim reaktiven, organischen flammhemmenden Mittel auf Phosphorbasis (B) um eine organische Phosphorverbindung der Formel (I) und/oder der Formel (II) handelt und dieses Mittel in der Harzzusammensetzung in einer Menge im Bereich von 0,5 bis 20 Gew.-% enthalten ist. Chemische Formel 1

wobei die Reste R¹ bis R⁴ jeweils die Bedeutung CH₂=CY¹-Y²- haben oder eine monofunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, bedeuten, und R⁵ eine difunktionelle aromatische Kohlenwasserstoffgruppe, die ein Heteroatom enthalten kann, bedeutet, die Reste X¹ bis X⁴ jeweils eine Gruppe bedeuten, die aus -O-, -NH-, -(CH₂=CY¹-Y²)N- ausgewählt ist und mindestens einer der Reste X¹ bis X⁴ die Gruppe -NH- oder die Gruppe -(CH₂=CY¹-Y²)Nenthält; mindestens einer der Reste R¹ bis R⁴ und der Reste X¹ bis X⁴ die Gruppe CH₂=CY¹-Y²- enthält; Y¹ ein Wasserstoffatom oder eine Methylgruppe bedeutet; und Y² eine Alkylengruppe mit 1 bis 5 Kohlenstoffatomen oder -COO-Y³- bedeutet, wobei Y³ eine Alkylengruppe mit 1 bis 5 Kohlenstoffatomen bedeutet; Chemische Formel 2

wobei in einem Molekül mindestens eine P-C-Bindung enthalten ist; die Reste Ar¹ und Ar² jeweils eine difunktionelle aromatische Kohlenwasserstoffgruppe mit höchstens 20 Kohlenstoffatomen bedeuten, die kein mobiles Wasserstoffatom enthält, und n eine ganze Zahl mit einem Wert von 0, 1 oder 2 ist; die Reste R⁶ bis R¹⁰ jeweils eine Gruppe bedeuten, die aus -NHCH₂CH=CH₂ _, -N(CH₂CH=CH₂)₂, -OCH₂CH=CH₂, -CH₂CH=CH₂, -CH₂CH₂OCH=CH₂, -(C₆H₄)-CH=CH₂, -O(C₆H₄)-CH=CH₂, -CH₂(C₆H₄)-CH=CH₂, -NH(C₆H₄)-CH=CH₂, -N(CH₂CH=CH₂)-(C₆H₄)-CH=CH₂, -O-R-OOC-C(R')=CH₂, -NH-R-NHCO-C(R')=CH₂ und einer Arylgruppe mit höchstens 12 Kohlenstoffatomen ausgewählt ist, wobei R eine Alkylengruppe mit 2 bis 5 Kohlenstoffatomen bedeutet und R' ein Wasserstoffatom oder eine Methylgruppe bedeutet; und mindestens einer der Reste R⁶ bis R¹⁰ eine -CH=CH₂-Gruppe oder eine -C(CH₃)=CH₂- Gruppe enthält.An arc extinguishing resin molded article according to any one of claims 1 to 5, wherein the phosphorus-based reactive organic flame retardant (B) is an organic phosphorus compound of the formula (I) and / or the formula (II) and this agent in the resin composition is contained in an amount in the range of 0.5 to 20 wt .-%. Chemical formula 1

wherein the radicals R ¹ to R ⁴ each have the meaning CH ₂ = CY ¹ -Y ² - or a monofunctional aromatic hydrocarbon group which may contain a heteroatom, and R ^{5 represents} a difunctional aromatic hydrocarbon group which may contain a heteroatom means the radicals X ¹ to X ⁴ each represent a group selected from -O-, -NH-, - (CH ₂ = CY ¹ Y ²⁾ N- is selected and at least one of X ¹ to X ^4, the group -NH- or the group - (CH ₂ = CY ¹ -Y ² ) N; at least one of the radicals R ¹ to R ⁴ and the radicals X ¹ to X ^{4 contains} the group CH ₂ = CY ¹ -Y ² -; Y ^{1 represents} a hydrogen atom or a methyl group; and Y ^{2 represents} an alkylene group having 1 to 5 carbon atoms or -COO-Y ³ -, wherein Y ^{3 represents} an alkylene group having 1 to 5 carbon atoms; Chemical formula 2

wherein at least one PC bond is contained in a molecule; the radicals Ar ¹ and Ar ² each represent a difunctional aromatic hydrocarbon group having at most 20 carbon atoms which does not contain a mobile hydrogen atom, and n is an integer having a value of 0, 1 or 2; the radicals R ⁶ to R ¹⁰ each denote a group consisting of -NHCH ₂ CH =CH ₂ _, -N (CH ₂ CH =CH ₂ ) ₂ , -OCH ₂ CH =CH ₂ , -CH ₂ CH =CH ₂ , -CH ₂ CH ₂ OCH = CH ₂ , - (C ₆ H ₄ ) -CH = CH ₂ , -O (C ₆ H ₄ ) -CH = CH ₂ , -CH ₂ (C ₆ H ₄ ) -CH = CH ₂ , -NH (C ₆ H ₄ ) -CH = CH ₂ , -N (CH ₂ CH = CH ₂ ) - (C ₆ H ₄ ) -CH = CH ₂ , -OR-OOC-C (R ') CH ₂ , -NH-R-NHCO-C (R ') = CH ₂ and an aryl group having at most 12 carbon atoms, wherein R represents an alkylene group having 2 to 5 carbon atoms and R' represents a hydrogen atom or a methyl group; and at least one of R ⁶ to R ^{10 contains} a -CH = CH ₂ group or a -C (CH ₃ ) = CH ₂ group.

Lichtbogenlösch-Harzformkörper nach einem der Ansprüche 2 bis 6, bei dem es sich beim Polyacetalharz (C) um ein Oxymethylen-Oxyethylen-Copolymeres oder um ein Oxymethylen-Polymeres handelt.Arc extinguishing resin moldings after one of the claims 2 to 6, wherein the polyacetal resin (C) is an oxymethylene-oxyethylene copolymer or an oxymethylene polymer is.

Lichtbogenlösch-Harzformkörper nach einem der Ansprüche 2 bis 7, bei dem das Polyacetalharz (C) im Polyolefinharz (A) unter Bildung einer Mikrophasen-Trennstruktur dispergiert ist.Arc extinguishing resin moldings after one of the claims 2 to 7, in which the polyacetal resin (C) in the polyolefin resin (A) under Forming a microphase separation structure is dispersed.

Trennschalter, umfassend einen fixierten Kontaktabschnitt mit einem fixierten Kontaktstück, einen beweglichen Kontaktabschnitt mit einem beweglichen Kontaktstück zum Kontakt mit dem fixierten Kontaktabschnitt und zur Durchführung von Schließ- und Öffnungsvorgängen mit dem fixierten Kontaktabschnitt, und ein Lichtbogenlösch-Bauelement, das einen bei den Öffnungs- und Schließvorgängen zwischen dem fixierten Kontaktabschnitt und dem beweglichen Kontaktabschnitt gebildeten Lichtbogen auslöscht, wobei das Lichtbogenlösch-Bauelement den Lichtbogenlösch-Harzformkörper nach einem der Ansprüche 1 bis 8 umfasst.Disconnector comprising a fixed contact portion with a fixed contact piece, a movable contact portion with a movable contact piece for contact with the fixed contact portion and for performing closing and opening operations with the fixed contact portion, and an arc extinguishing component, the one at the opening and closing operations between the fixed contact portion and the movable contact portion extinguished arc, wherein the arc extinguishing component the arc extinguishing resin molding after one of the claims 1 to 8.