DE102006057633A1 - Making multi-axial material from laid carbon fibers, for use in e.g. aerospace industry, rotates supply reels around plane held at angle with respect to vertical - Google Patents

Making multi-axial material from laid carbon fibers, for use in e.g. aerospace industry, rotates supply reels around plane held at angle with respect to vertical Download PDF

Info

Publication number
DE102006057633A1
DE102006057633A1 DE102006057633A DE102006057633A DE102006057633A1 DE 102006057633 A1 DE102006057633 A1 DE 102006057633A1 DE 102006057633 A DE102006057633 A DE 102006057633A DE 102006057633 A DE102006057633 A DE 102006057633A DE 102006057633 A1 DE102006057633 A1 DE 102006057633A1
Authority
DE
Germany
Prior art keywords
winding plane
angle
gravity
winding
plane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102006057633A
Other languages
German (de)
Inventor
Friedhelm Scholten
Klaus Szukat
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fibraforce Ag Ch
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE102006057633A priority Critical patent/DE102006057633A1/en
Priority to PCT/DE2007/001379 priority patent/WO2008014784A2/en
Priority to EP09009974.8A priority patent/EP2141011B1/en
Priority to CA2851567A priority patent/CA2851567C/en
Priority to EP09009975.5A priority patent/EP2141012B1/en
Priority to CA2659555A priority patent/CA2659555C/en
Priority to EP09009973.0A priority patent/EP2141010B1/en
Priority to US12/376,144 priority patent/US8205425B2/en
Priority to DE502007006963T priority patent/DE502007006963D1/en
Priority to CN 200910135106 priority patent/CN101531073B/en
Priority to AT07785685T priority patent/ATE505573T1/en
Priority to JP2009522087A priority patent/JP5049345B2/en
Priority to CN2007800337598A priority patent/CN101516612B/en
Priority to EP07785685A priority patent/EP2102400B1/en
Priority to CN 200910135105 priority patent/CN101531072B/en
Publication of DE102006057633A1 publication Critical patent/DE102006057633A1/en
Priority to US12/364,597 priority patent/US7921629B2/en
Priority to US12/364,602 priority patent/US7921630B2/en
Withdrawn legal-status Critical Current

Abstract

Individually monoaxial lays (2a, 2b) from supply reels (3a, 3b) are wound around a winding plane or panel (4). The plane and reels rotate around each other for this purpose. The longitudinal axis (5) of the winding plane is set at an angle of 30[deg] - 50[deg] to the vertical (6). The winding plane is stationary, or alternatively rotates about its longitudinal axis. The angle of inclination is varied through between 5[deg] and 85[deg], during relative rotation of winding plane and supply reels. An independent claim IS INCLUDED FOR corresponding equipment.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung eines multiaxialen Geleges, bevorzugt aus Kohlefaserstoffen, in welchem ein monoaxiales Gelege von mindestens einer Bevorratung um eine Wickelebene gewickelt wird, wobei die Wickelebene und die mindestens eine Bevorratung umeinander rotieren, um das monoaxiale Gelege um die Wickelebene zu wickeln und eine Vorrichtung zur Durchführung des erfindungsgemäßen Verfahrens.The The invention relates to a method for producing a multiaxial Geleges, preferably made of carbon fiber materials, in which a monoaxial Scrim of at least one supply wound around a winding plane is, wherein the winding plane and the at least one storage rotate around each other, around the monoaxial scrim around the winding plane to wind and a device for carrying out the method according to the invention.

Zur Herstellung von faserverstärkten Kunststoffen werden Gelege aus Fasern verwendet, die mit einem Kunststoff umgossen werden. Der Verbund aus Kunststoff und den Fasern verleiht dabei dem faserverstärkten Kunststoff eine hohe Stabilität gegenüber Zugspannung, wobei die Zugspannungsstabilität von der Ausrichtung der in dem Gelege vorhandenen Fasern abhängig ist. Faserverstärkte Kunststoffe werden vor allem dort eingesetzt, wo eine hohe Belastbarkeit in Kombination mit geringem Gewicht gefordert ist, wie beispielweise im Flugzeug- oder Schiffsbau. Um faserverstärkten Kunststoffen mit einem möglichst geringen Gewicht auszustatten, ist es notwendig, die Menge des auf die Faser aufgetragenen Kunststoffes so gering wie möglich zu halten, wobei der Kunststoff die Fasern vollständig umschließen soll. Bei der Verwendung von gewebten Fasern trägt die Faserschicht im Vergleich zur Stärke der einzelnen Fasern relativ stark auf und hat dadurch einen erhöhten Kunststoffanspruch, der zu einem faserverstärkten Kunststoffbauteil mit hoher Schichtdicke führt und daher ein hohes Gewicht aufweist. In der Praxis ist man daher dazu übergegangen, Gelege aus Fasermaterialien zu verwenden, in welchen die einzelnen Fasern gleichmäßig angeordnet sind und sich gegenseitig nicht überkreuzen, um damit eine Erhöhung der Schichtdicke des Fasermaterials und damit den Kunststoffanspruch des Fasermaterials möglichst gering zu halten. Da bekannt ist, dass der Kunststoff nur in der Faserrichtung eine hohe Zugfestigkeit aufweist, werden multiaxiale Gelege verwendet, in welchen Fasern in mehreren Ebenen gelegt sind, wobei in jeder Ebene die Fasern eine Vorzugsrichtung aufweisen und sich gegenseitig nach Möglichkeit nicht überkreuzen.to Production of fiber reinforced Plastics are used scrims made from fibers that are made with a plastic to be poured over. The composite of plastic and the fibers gives doing the fiber reinforced Plastic a high stability across from Tensile stress, with the tension stability of the orientation of in depends on the scrub existing fibers. Become fiber reinforced plastics especially used where a high load capacity in combination low weight is required, such as in the aircraft or shipbuilding. To fiber reinforced Plastics with one possible to equip low weight, it is necessary to increase the amount of the fiber applied plastic as low as possible hold, with the plastic to completely enclose the fibers. When using woven fibers, the fiber layer bears in comparison to strength the individual fibers relatively strong and thus has an increased plastic claim, to a fiber reinforced Plastic component with high layer thickness leads and therefore a high weight having. In practice, therefore, one has gone over to it, scrims made of fiber materials to use in which the individual fibers arranged uniformly are and do not cross each other, order an increase the layer thickness of the fiber material and thus the plastic claim the fiber material as possible to keep low. Since it is known that the plastic only in the Fiber direction has a high tensile strength, be multi-axial Used in which fibers are laid in several levels, wherein in each plane the fibers have a preferred direction, and each other as possible do not cross over.

Das einfachste so hergestellte multiaxiale Gelege ist ein Gelege, in dem zwei Bahnen einer Faseranordnung überkreuzt übereinander gelegt werden. Derartige Gelege werden dadurch hergestellt, in dem Teile einer Gelegebahn unter einem Winkel zur Bahn einzeln aneinander gelegt werden, wobei zunächst eine untere und darauf folgend eine obere Schicht aus einzelnen Teilen zusammengelegt wird. Hierbei werden einzelne, aus Parallelogrammen bestehende Einzelteile zu langen Bahnen zusammengelegt. Dieses Verfahren ist jedoch nicht geeignet, größere Mengen, so wie sie in industriellen Fertigungsprozessen benötigt werden, wirtschaftlich herzustellen. In einem anderen Verfahren ist man daher dazu übergegangen, eine oder zwei Bahnen unter einem Winkel um eine Platte zu wickeln und den so entstandenen Wickel von einer Platte abzuziehen. Dieser Prozess kann kontinuierlich durchgeführt werden, wobei der Wickel von der Platte abgezogen wird und im Anschluss daran zu einem Gelege verdichtet wird. Ein derartiges Verfahren hat sich in der Praxis als schwer beherrschbar herausgestellt, vor allem, wenn wie im Fall von Kohlefasern, die Fasern ein nahezu fließendes Verhalten aufweisen. Dies bedeutet, dass die Fasern aufgrund ihres geringen Gewichtes und ihrer geringen Reibung auf Oberflächen leicht zusammenfallen und somit der Ausbildung einer gleichmäßig geformten Gelegebahn entgegenwirken. Je fluider das Verhalten eines Geleges, desto schwieriger ist dabei die Herstellung eines gleichmäßig geformten multiaxialen Geleges. Da die Platte, um die ein uniaxiales Gelege gewickelt wird, eine endliche Breite aufweist, entsteht am Ende der Platte, an welchem der Wickel von der Platte gezogen wird, ein Schlauch, der zu einer gleichmäßigen Bahn aus zwei Ebenen zusammengelegt werden muss. Das fließende Verhalten des so hergestellten Geleges macht dabei die Faltung des Schlauches mit der Querschnittsgeometrie des Querschnitts der Platte zu einem ebenen Gelege aus zwei Bahnen schwer kontrollierbar, weil an den Seiten der Platte Verwerfungen im Gelege entstehen, die zu einer ungleichmäßig geformten Kante des Geleges führen und daher die Fasern in einer Ebene des multiaxialen Geleges einander überkreuzen lassen.The The simplest multiaxial clutch thus produced is a clutch, in the two tracks of a fiber array are crossed over one another. Such scrims are thereby produced, in the parts of a Gelegebahn at an angle to the track individually laid together be, first a lower and then an upper layer of individual Parts is merged. Here are individual, from parallelograms existing items merged into long tracks. This method is not suitable for larger quantities, as needed in industrial manufacturing processes, produce economically. In another procedure one is therefore transferred to to wind one or two webs at an angle around a board and subtract the resulting wrap from a plate. This Process can be carried out continuously, with the winding is pulled off the plate and then to a scrim is compressed. Such a method has in practice as difficult to control, especially if, as in the case of carbon fibers, the fibers have a nearly flowing behavior. This means that the fibers due to their low weight and their low friction on surfaces easily coincide and thus counteract the formation of a uniformly shaped fabric web. The more fluid the behavior of a clause, the more difficult it is the preparation of a uniformly shaped multiaxial matter. Because the plate around which a uniaxial clutch is wound, has a finite width, arises at the end the plate on which the winding is pulled from the plate, a Hose, which turns into a uniform web two levels must be merged. The flowing behavior of the so produced Much of this makes the folding of the tube with the cross-sectional geometry the cross section of the plate to a flat clutch of two tracks difficult to control because of faults on the sides of the plate arise in the clutch, leading to an irregularly shaped edge of the jelly to lead and therefore the fibers in one plane of the multiaxial web cross each other to let.

Aufgabe der Erfindung ist es daher, ein Verfahren und eine Vorrichtung zur Verfügung zu stellen, welches beziehungsweise welche es ermöglicht, den Wickel aus Fasern von einer Platte abzuziehen, sodass ein gleichmäßig geformtes multiaxiales Gelege aus zwei Ebenen entsteht, wobei das Abziehen nicht zu Verwerfungen oder zu Verdrillungen der einzelnen Fasern eines monoaxialen Geleges führen soll.task The invention is therefore a method and an apparatus for disposal which or which makes it possible Peel the filament of fibers from a plate, so that a uniformly shaped multiaxial clutch of two levels arises, with the peeling not to distortions or twists of the individual fibers a monoaxial Geleges lead should.

Erfindungsgemäß wird die Aufgabe durch eine Schrägstellung der Längsachse der Wickelebene in Bezug auf die Schwerkraftrichtung gelöst. Die korrespondierende Vorrichtung zur Durchführung des erfindungsgemäßen Verfahrens zeichnet sich dadurch aus, dass die Wickelebene schräg in Bezug zur Schwerkraftrichtung ausgerichtet ist. Weitere vorteilhafte Ausgestaltungen der Verfahrens- und Vorrichtungserfindung ergeben sich aus den Unteransprüchen.According to the invention Task by an inclination the longitudinal axis the winding plane with respect to the direction of gravity dissolved. The corresponding Device for carrying out the inventive method is characterized by the fact that the winding plane obliquely with respect to Gravity direction is aligned. Further advantageous embodiments the process and device invention will become apparent from the dependent claims.

Durch eine Schrägstellung der Längsachse der Wickelebene in Bezug auf die Schwerkraftrichtung wird erreicht, dass die Fasern mit einem fluiden Verhalten und geringer Reibung auf der Oberfläche der Wickelebene durch die Schwerkraft von der Wickelebene abgleiten. Im Stand der Technik war bisher bekannt, den Wickel von einer in der Waagerechten befindlichen Wickelebene abzuziehen, die Wickelebene um eine waagerecht verlaufende Längsachse zu rotieren und die Wickelebene durch ein drittes monoaxiales Gelege, welches eine Faserausrichtung in Längsrichtung des herzustellenden multiaxialen Geleges aufweist, zur Verfügung zu stellen, wobei dieses Gelege mit senkrechter Längsachsenausrichtung, also in Schwerkraftrichtung, in der Vorrichtung zur Herstellung des multiaxialen Geleges verwendet wird.By an inclination of the longitudinal axis of the winding plane with respect to the direction of gravity is achieved that the fibers slide with a fluid behavior and low friction on the surface of the winding plane by gravity from the winding plane. In the prior art was so far known to subtract the winding from a lying in the horizontal winding plane, the winding plane to rotate about a horizontally extending longitudinal axis and to provide the winding plane through a third monoaxial clutch, which has a fiber orientation in the longitudinal direction of the produced multiaxial Geleges, this clutch is used with vertical longitudinal axis alignment, ie in the direction of gravity, in the apparatus for producing the multiaxial Geleges.

Gegenüber den oben genannten Verfahren hat das erfindungsgemäße Verfahren den Vorteil, dass die Schrägstellung an das Gewicht und die tatsächliche Reibungskraft der Fasern auf der Wickelebene angepasst werden kann. Je nach Höhe der Reibungskraft kann die Wickelebene unter einem Winkel zur Schwerkraft angestellt werden, sodass im Idealfall eine gleichmäßige Gleitreibung zwischen der Faser und der Wickelebene entsteht, die zu einem gleichmäßigen Abgleiten des monoaxialen Geleges von der Wickelebene führt.Compared to the above-mentioned method, the inventive method has the advantage that the inclination on the weight and the actual Frictional force of the fibers can be adapted to the winding plane. Depending on height The frictional force may be the winding plane at an angle to gravity be employed, so ideally a uniform sliding friction between the fiber and the winding plane, resulting in a smooth sliding the monoaxial Geleges leads from the winding plane.

In einer Ausführungsform des erfindungsgemäßen Verfahrens und in der korrespondierenden Vorrichtung zur Durchführung des Verfahrens ist vorgesehen, dass die Wickelebene stationär gehalten ist. Hierbei kann die stationär gehaltene Wickelebene so angeordnet sein, dass die Längsachse der Wickelebene unter einem Winkel zur Schwerkraft ausgerichtet ist, wobei die Ober- und Unterfläche der Wickelebene senkrecht oder auch waagerecht ausgerichtet sein kann. Bei der senkrechten Ausrichtung der Ober- und Unterfläche der Wickelebene wirkt die Schwerkraft so, dass das monoaxiale Gelege vor allem durch eine obenliegende und schräg zur Richtung der Schwerkraft verlaufende Kante getragen wird. Dabei ist in vorteilhafter Weise der Winkel der Wickelebene so eingestellt, dass die gewickelten Fasern lotrecht in Richtung der Schwerkraft zeigen. Hierdurch wird gewährleistet, dass sich die Fasern von selbst richtig ausrichten und stets einen korrekten und gewünschten Winkel in dem herzustellenden monoaxialen Gelege aufweisen.In an embodiment the method according to the invention and in the corresponding device for carrying out the Method is provided that the winding plane is held stationary. Here, the stationary held winding plane be arranged so that the longitudinal axis the winding plane aligned at an angle to gravity is, with the top and bottom surfaces the winding plane should be perpendicular or horizontal can. In the vertical orientation of the top and bottom of the Winding plane acts gravity so that the monoaxial scrim especially by an overhead and oblique to the direction of gravity extending edge is worn. It is advantageous the angle of the winding plane adjusted so that the wound Point fibers perpendicular to gravity. This will guaranteed that the fibers align themselves correctly and always one correct and desired Have angle in the produced monoaxial scrim.

Bei einer Ausrichtung der Wickelebene, die zu einer Ausrichtung der Seitenkanten führt, deren Ebene senkrecht auf einer in allen Richtungen horizontal ausgerichteten Ebene steht, führt zu einer Wickelebene, deren Ober- und Unterfläche unter einem Winkel zur Schwerkraft ausgerichtet sind. Hierbei wird das monoaxiale Gelege auf der schrägen Ebene gewickelt und gleitet gleichmäßig von dieser schrägen Ebene herab. Auch hier ist es möglich, durch Feinstrukturierung der Oberfläche und durch Einstellung des Winkels der Wickelebene, die an der Längsachse in Bezug zur Schwerkraftrichtung gemessen wird, die Reibungskraft und den Anstellwinkel der Wickelebene aufeinander anzupassen, sodass das monoaxiale Gelege gleichmäßig von der Wickelebene abgleitet.at an orientation of the winding plane, which leads to an alignment of Side edges leads, whose plane is perpendicular to a horizontally oriented in all directions Level stands, leads to a winding plane whose top and bottom surfaces at an angle to Gravity are aligned. This is the monoaxial clutch on the sloping Layer wrapped and glides evenly from this sloping plane down. Again, it is possible by fine structuring of the surface and by adjustment of the Angle of the winding plane on the longitudinal axis with respect to the direction of gravity is measured, the friction force and the angle of attack of the winding plane adjust so that the monoaxial scrim evenly from the winding plane slides off.

In einer alternativen Ausführungsform des erfindungsgemäßen Verfahrens und der dazu korrespondierenden Vorrichtung zur Durchführung des Verfahrens ist vorgesehen, dass die Platte nicht stationär gehalten wird, sondern um ihre eigene Längsachse rotiert. Eine Rotation um die Längsachse der Wickelebene, wobei die Wickelebene schräg zur Schwerkraftrichtung ausgerichtet ist und die schräge Ausrichtung gemessen wird an der Längsachse, die einen Winkel zur Schwerkraftrichtung bildet, ist es möglich, das Gelege von stationär gehaltenen Bevorratungen abzuwickeln, sodass das monoaxiale Gelege um die sich rotierende Wickelebene gewickelt wird. Dabei ist vorgesehen, dass der Winkel der Wickelebene so gewählt ist, dass auch hier die Reibungskraft des monoaxialen Geleges auf der Wickelebene und der Anstellwinkel miteinander korrespondieren, sodass das monoaxiale Gelege gleichmäßig von der Wickelebene abgleitet. Am Ende der Wickelebene ist eine Vorrichtung vorgesehen, die das multiaxiale Gelege von der Wickelebene abnimmt und aufrollt.In an alternative embodiment the method according to the invention and the device corresponding thereto for carrying out the method is provided that the plate is not kept stationary, but to their own longitudinal axis rotates. A rotation about the longitudinal axis the winding plane, wherein the winding plane oriented obliquely to the direction of gravity is and the oblique orientation is measured at the longitudinal axis, which forms an angle to the direction of gravity, it is possible that Clutch of stationary unwinded stored supplies, so that the monoaxial clutch is wound around the rotating winding plane. It is intended that the angle of the winding plane is chosen so that here Frictional force of the monoaxial Geleges on the winding plane and the Anstellwinkel correspond with each other, so that the monoaxial Scratch evenly from the winding plane slides off. At the end of the winding plane is a device provided, which decreases the multi-axial clutch of the winding plane and rolls up.

In vorteilhafter Ausgestaltung der Erfindung ist eine Wickelebene vorgesehen, die rotiert und eine Schrägstellung der Längsachse der Wickelebene in Bezug auf die Schwerkraft aufweist, wobei die Schrägstellung innerhalb einer Rotationsperiode von einem Minimalwinkel bis zu einem Maximalwinkel variiert. Hierdurch wird eine unterschiedliche Reibkraft ausgeglichen, die dadurch entsteht, dass das monoaxiale Gelege mal flächig auf der Wickelebene und mal flächig auf der Seitenkante der Wickelebene zuliegen kommt und dazwischen sowohl auf der Ober- und Unterfläche der Wickelebene zuliegen kommt und auch gleichzeitig auf der Seitenkante zuliegen kommt. Bei den verschiedenen Ausrichtungen der monoaxialen Gelege auf der Wickelebene ist es somit notwendig, den Anstellwinkel an die jeweils unterschiedlichen Reibkräfte durch die unterschiedlichen Stellungen der Wickelebene anzupassen. Durch die taumelnde Wickelebene wird außerdem erreicht, dass der Abwickelvorgang erleichtert wird und dass das monoaxiale Gelege durch die Kanten der Wickelebene gespannt und wieder gelockert wird. Auf diese Weise ist ein besonders gleichmäßiges Legen der monoaxialen Gelege auf der Wickelebene erreichbar.In Advantageous embodiment of the invention, a winding plane is provided, which rotates and a skew the longitudinal axis the winding plane with respect to gravity, wherein the inclination within a rotation period from a minimum angle to a maximum angle varies. This will be a different Frictional force compensated by the fact that the monoaxial Plot times flat on the winding plane and sometimes flat on the side edge of the winding plane zuliegen comes and in between both on the top and bottom surfaces The Wickele lie and come at the same time on the side edge come on. At the different alignments of monoaxial Clutches on the winding plane, it is therefore necessary to adjust the angle of attack to the respective different frictional forces due to the different positions adapt to the winding plane. By the tumbling winding plane is Furthermore ensures that the unwinding process is facilitated and that the monoaxiale scrim stretched through the edges of the winding plane and is loosened again. In this way is a particularly uniform laying reach the monoaxial clutch on the winding plane.

In vorteilhafter Weise wird eine Schrägstellung von 5° bis 85° in Bezug auf die Schwerkraftrichtung gewählt, bevorzugt eine Schrägstellung von 20° bis 70° und ganz besonders bevorzugt ein Winkel von 30° bis 50°. Überraschender Weise hat sich gezeigt, dass in diesen Winkelintervallen allein durch die Schwerkraft das Gelege von der Wickelebene abgleitet und dabei ein hochgradig homogenes und gleichmäßiges multiaxiales Gelege bildet.In Advantageously, an inclination of 5 ° to 85 ° in relation chosen in the direction of gravity, preferably an inclination from 20 ° to 70 ° and most preferably an angle of 30 ° to 50 °. Surprisingly, it has become shown in these angular intervals solely by gravity the scrim drains off the winding plane and thereby a high grade homogeneous and even multiaxial Clutch forms.

Die Erfindung wird anhand der folgenden Figuren näher erläutert.The The invention will be explained in more detail with reference to the following figures.

Es zeigtIt shows

1 eine Skizze zur Erläuterung des erfindungsgemäßen Verfahrens und der Vorrichtung zur Durchführung des erfindungsgemäßen Verfahrens. 1 a sketch for explaining the inventive method and the apparatus for performing the method according to the invention.

In 1 ist eine Skizze zur Verdeutlichung des Verfahrens zur Herstellung eines multiaxialen Geleges 1 dargestellt, in welchem ein monoaxiales Gelege 2a und 2b von mindestens einer Bevorratung 3a und 3b um eine Wickelebene 4 gewickelt wird. Die Wickelebene 4 und die beiden Bevorratungen 3a und 3b rotieren umeinander. Erfindungsgemäß ist vorgesehen, dass sich die Bevorratungen 3a und 3b um die Wickelebene 4 drehen. Es ist aber auch möglich, dass die Bevorratungen 3a und 3b stationär gehalten werden und dass sich die Wickelebene 4 um ihre eigene Längsachse 5 dreht. Daneben ist es auch möglich, dass eine kombinierte Bewegung von Wickelebene 4 und den beiden Bevorratungen 3a und 3b vorgesehen ist. Bei der relativen Rotation der Bevorratung 3a und 3b und der Wickelebene 4 kommt das monoaxiale Gelege 2a und 2b auf je einer Seite der Wickelebene 4 zuliegen, wobei das monoaxiale Gelege 2a und 2b durch die Schrägstellung der Längsachse 5 in Relation zur Schwerkraftrichtung 6 von der Wickelebene 4 gleichmäßig abgleitet und so kann das multiaxiale Gelege 1 von der Wickelebene 4 abgezogen werden, ohne dass die Fasern des monoaxialen Geleges 2a, 2b an der Wickelebene 4 durch Haftreibung verkeilen und somit nicht zu einem gleichmäßigen multiaxialen Gelege 1 abgezogen werden können.In 1 is a sketch to illustrate the method for producing a multiaxial Geleges 1 in which a monoaxial scrim 2a and 2 B of at least one stock 3a and 3b around a winding plane 4 is wound. The winding plane 4 and the two supplies 3a and 3b rotate around each other. According to the invention, it is provided that the stocks 3a and 3b around the winding plane 4 rotate. But it is also possible that the stocks 3a and 3b be held stationary and that the winding plane 4 around its own longitudinal axis 5 rotates. Besides, it is also possible that a combined movement of winding plane 4 and the two stocks 3a and 3b is provided. In the relative rotation of stockpiling 3a and 3b and the winding plane 4 comes the monoaxial clutch 2a and 2 B on each side of the winding plane 4 with the monoaxial clutch 2a and 2 B by the inclination of the longitudinal axis 5 in relation to the direction of gravity 6 from the winding plane 4 evenly slips off and so can the multiaxial clutch 1 from the winding plane 4 be deducted without the fibers of the monoaxial Geleges 2a . 2 B at the winding level 4 stuck together by static friction and thus not to a uniform multiaxial clutch 1 can be deducted.

11
Gelegescrim
2a2a
monoaxiales Gelegeuniaxial scrim
2b2 B
monoaxiales Gelegeuniaxial scrim
3a3a
Bevorratungstocking
3b3b
Bevorratungstocking
44
Wickelebenewinding plane
55
Längsachselongitudinal axis
66
SchwerkraftrichtungThe direction of gravity

Claims (10)

Verfahren zur Herstellung eines multiaxialen Geleges (1), bevorzugt aus Kohlefaserstoffen, in welchem ein monoaxiales Gelege (2a, 2b) von mindestens einer Bevorratung (3a, 3b) um eine Wickelebene (4) gewickelt wird, wobei die Wickelebene (4) und die mindestens eine Bevorratung (3a, 3b) umeinander rotieren, um das monoaxiale Gelege (2a, 2b) um die Wickelebene (4) zu wickeln, gekennzeichnet durch eine Schrägstellung der Längsachse (5) der Wickelebene (4) in Bezug auf die Schwerkraftrichtung (6).Process for producing a multiaxial gel ( 1 ), preferably of carbon fiber materials, in which a monoaxial scrim ( 2a . 2 B ) of at least one stockpile ( 3a . 3b ) around a winding plane ( 4 ), wherein the winding plane ( 4 ) and the at least one stockpile ( 3a . 3b ) to rotate around the monoaxial scrim ( 2a . 2 B ) around the winding plane ( 4 ), characterized by an oblique position of the longitudinal axis ( 5 ) of the winding plane ( 4 ) with respect to the direction of gravity ( 6 ). Verfahren nach Anspruch 1, gekennzeichnet durch eine stationäre Wickelebene (4).Method according to claim 1, characterized by a stationary winding plane ( 4 ). Verfahren nach einem der Ansprüche 1 oder 2, gekennzeichnet durch eine rotierende Wickelebene (4), wobei die Wickeleben (4) um die Längsachse (5) rotiert.Method according to one of claims 1 or 2, characterized by a rotating winding plane ( 4 ), wherein the winding life ( 4 ) about the longitudinal axis ( 5 ) rotates. Verfahren nach einem der Ansprüche 1 bis 3 gekennzeichnet durch eine Schrägstellung von 5° bis 85° in Bezug auf die Schwerkraftrichtung (6), vorzugsweise 20° bis 70°, ganz besonders bevorzugt von 30° bis 50° in Bezug auf die Schwerkraftrichtung (6).Method according to one of claims 1 to 3, characterized by an inclination of 5 ° to 85 ° with respect to the direction of gravity ( 6 ), preferably 20 ° to 70 °, most preferably from 30 ° to 50 ° with respect to the direction of gravity ( 6 ). Verfahren nach einem der Ansprüche 1 bis 4 gekennzeichnet durch eine Variation der Schrägstellung während einer relativen Umdrehung von Wickelebene (4) und Bevorratung (3a, 3b), wobei der Winkel der Schrägstellung von 5° bis 85° variiert.Method according to one of claims 1 to 4 characterized by a variation of the inclination during a relative rotation of the winding plane ( 4 ) and stocking ( 3a . 3b ), wherein the angle of inclination varies from 5 ° to 85 °. Vorrichtung zur Durchführung des Verfahrens nach einem der Ansprüche 1 bis 5, zur Herstellung eines multiaxialen Geleges (1), bevorzugt aus Kohlefasern, aufweisend mindestens eine Bevorratung (3a, 3b) für ein monoaxiales Gelege (2a, 2b) und eine Wickelebene (4), wobei die mindestens eine Bevorratung (3a, 3b) und die Wickelebene (4) umeinander rotieren und dabei das monoaxiale Gelege (2a, 2b) von der mindestens einen Bevorratung (3a, 3b) um die Wickelebene (3) wickeln, dadurch gekennzeichnet, dass die Wickelebene (4) schräg in Bezug zur Schwerkraftrichtung (6) ausgerichtet ist.Device for carrying out the method according to one of claims 1 to 5, for the production of a multiaxial gel ( 1 ), preferably made of carbon fibers, comprising at least one storage ( 3a . 3b ) for a monoaxial scrim ( 2a . 2 B ) and a winding plane ( 4 ), the at least one stock ( 3a . 3b ) and the winding plane ( 4 ) rotate around each other while the monoaxial scrim ( 2a . 2 B ) of the at least one stockpile ( 3a . 3b ) around the winding plane ( 3 ), characterized in that the winding plane ( 4 ) obliquely in relation to the direction of gravity ( 6 ) is aligned. Vorrichtung nach Anspruch 6 dadurch gekennzeichnet, dass die Wickelebene (4) stationär gehalten ist.Apparatus according to claim 6, characterized in that the winding plane ( 4 ) is held stationary. Vorrichtung nach einem der Ansprüche 6 oder 7 dadurch gekennzeichnet, dass die Wickelebene (4) um ihre eigene Längsachse (5) rotiert.Device according to one of claims 6 or 7, characterized in that the winding plane ( 4 ) about its own longitudinal axis ( 5 ) rotates. Vorrichtung nach einem der Ansprüche 6 bis 8, dadurch gekennzeichnet, dass eine Schrägstellung von 5° bis 85° in Bezug auf die Schwerkraftrichtung (6), vorzugsweise 20° bis 70°, ganz besonders bevorzugt von 30° bis 50° in Bezug auf die Schwerkraftrichtung (6) erfolgt.Device according to one of claims 6 to 8, characterized in that an inclination of 5 ° to 85 ° with respect to the direction of gravity ( 6 ), preferably 20 ° to 70 °, most preferably from 30 ° to 50 ° with respect to the direction of gravity ( 6 ) he follows. Vorrichtung nach einem der Ansprüche 6 bis 9, dadurch gekennzeichnet, dass eine Variation der Schrägstellung während einer relativen Umdrehung von Wickelebene (4) und Bevorratung (3a, 3b) erfolgt, wobei der Winkel der Schrägstellung von 5° bis 85° variiert.Device according to one of claims 6 to 9, characterized in that a variation of the inclination during a relative rotation of winding plane ( 4 ) and stocking ( 3a . 3b ), wherein the angle of inclination varies from 5 ° to 85 °.
DE102006057633A 2006-08-04 2006-12-05 Making multi-axial material from laid carbon fibers, for use in e.g. aerospace industry, rotates supply reels around plane held at angle with respect to vertical Withdrawn DE102006057633A1 (en)