DE10022404A1 - Textile fabric provided with ultraviolet radiation filter, useful for clothing, is obtained by depositing filter on fabric or fibers by impregnation with solution, dispersion or suspension - Google Patents
Textile fabric provided with ultraviolet radiation filter, useful for clothing, is obtained by depositing filter on fabric or fibers by impregnation with solution, dispersion or suspensionInfo
- Publication number
- DE10022404A1 DE10022404A1 DE2000122404 DE10022404A DE10022404A1 DE 10022404 A1 DE10022404 A1 DE 10022404A1 DE 2000122404 DE2000122404 DE 2000122404 DE 10022404 A DE10022404 A DE 10022404A DE 10022404 A1 DE10022404 A1 DE 10022404A1
- Authority
- DE
- Germany
- Prior art keywords
- fabric
- textile
- radiation filter
- filter
- radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die vorliegende Erfindung betrifft ein mit UV-Strahlenfiltern beaufschlagtes textiles Gewebe sowie ein Verfahren zu dessen Herstellung.The present invention relates to a textile fabric to which UV radiation filters have been applied and a process for its production.
Die potentielle Schädigung der menschlichen Haut durch Sonneneinstrahlung wird seit Jahren intensiv untersucht, insbesondere seit man einen Zusammenhang zwischen intensiver Sonnenbestrahlung und Bildung von Hautkrebs festgestellt hat. Verantwortlich für die Schädigung der Haut sind insbesondere die ultravioletten Strahlen, die etwa 5% der Sonnenstrahlung ausmachen. Als UV-Strahlen bezeichnet man elektromagnetische Strahlung im Wellenlängenbereich von 400 nm bis 10 nm. Je kürzer die Wellenlänge ist, um so energiereicher ist die Strahlung. Der UV-Bereich wird üblicherweise in drei Unterbereiche eingeteilt, nämlich UV-A-Strahlen im Bereich von 400 bis 320 nm, UV-B-Strahlen im Bereich von 320 bis 290 nm und UV-C-Strahlen im Bereich von 290 bis 10 nm.The potential damage to human skin from sun exposure has been going on since Years of intensive research, especially since there is a connection between more intense Sun exposure and skin cancer formation has been noted. Responsible for the Skin damage is particularly the ultraviolet rays, which make up about 5% of the Make out solar radiation. UV rays are electromagnetic Radiation in the wavelength range from 400 nm to 10 nm. The shorter the wavelength is, um the radiation is so energetic. The UV range is usually divided into three sub-ranges classified, namely UV-A rays in the range of 400 to 320 nm, UV-B rays in the range from 320 to 290 nm and UV-C rays in the range from 290 to 10 nm.
Am schädlichsten für die menschliche Haut sind die UV-C-Strahlen, die in der Regel durch die Ozonschicht gefiltert werden und die Erdoberfläche nicht erreichen. Die längerwelligen UV-A-Strahlen führen durch Umwandlung von Melaninvorstufen zur sogenannten Sofortpigmentierung, die innerhalb weniger Stunden eintritt, jedoch nur sehr gering ist und nicht lange Bestand hat. Diese Strahlen dringen allerdings tief in die Lederhaut ein und führen zu einer vorzeitigen Hautalterung. Die kürzerwelligen, aber energiereicheren UV-B-Strahlen dringen wenige Millimeter in die Haut ein und führen zur Bildung eines relativ beständigen Pigments, das in den Zellen der Epidermis abgelagert wird und die Langzeitbräunung bewirkt. Die UV-B-Strahlen können jedoch Sauerstoffmoleküle freisetzen, die aufgrund ihrer Aktivität zur Schädigung der Haut führen, was als Sonnenbrand und bei wiederholtem Auftreten vor allem bei Kindern und Jugendlichen, das Risiko für die Entstehung eines Melanoms in den späteren Lebensjahren erheblich erhöhen kann. Die UV-C-Strahlen werden zwar durch die Ozonschicht abgefiltert, ihre Strahlungsdosis, die die Erdoberfläche erreicht, kann jedoch durch die Verdünnung der Ozonschicht, langläufig auch als Ozonloch bezeichnet, erhöht werden. The most harmful to human skin are the UV-C rays, which are usually caused by the ozone layer is filtered and does not reach the earth's surface. The longer wave UV-A rays lead to the so-called by converting melanin precursors Immediate pigmentation that occurs within a few hours, but is very low and doesn't last long. However, these rays penetrate deep into the dermis and lead premature skin aging. The shorter-wave but higher-energy UV-B rays penetrate the skin a few millimeters and lead to the formation of a relatively permanent Pigments that are deposited in the cells of the epidermis and cause long-term tanning. However, the UV-B rays can release oxygen molecules due to their activity lead to skin damage, what as sunburn and recurrence before especially in children and adolescents, the risk of developing melanoma in the later years of life can increase significantly. The UV-C rays are caused by the Filtered ozone layer, however, their radiation dose that reaches the earth's surface can due to the thinning of the ozone layer, also known as the ozone hole become.
Die hohe Zahl von Hautkrebserkrankungen und die Gefahr, dass sich die Verringerung der Ozonschicht noch erhöht verlangen nach einem Schutz vor all zu großer UV-Strahlung. Insbesondere Menschen, die im Freien arbeiten oder sich über längere Zeit dort aufhalten, müssen sich schützen, um die UV-Strahlendosis zu verringern, die sich im Laufe eines Menschenlebens akummuliert.The high number of skin cancers and the risk of reducing them The ozone layer, even higher, requires protection from excessive UV radiation. Especially people who work outdoors or stay there for a long time, need to protect themselves in order to reduce the UV radiation dose that is Human life accumulated.
Bis jetzt schützen sich die Menschen vor all zu großer Sonneneinwirkung durch sogenannte Sonnenschutzmittel, die UV-Filter beziehungsweise -Absorber enthalten. Die UV-Absorber oder UV-Schutzfilter sind organische Substanzen, welche in der Lage sind, elektromagnetische Strahlung im UV-Bereich zu absorbieren. Die Moleküle gehen hierbei in einen energetisch angeregten Zustand über. Beim Rückgang in den Grundzustand wird die aufgenommene Energie wieder vollständig, allerdings in einer für die Haut weniger oder nicht schädlichen Form wieder abgegeben, z. B. in Form von Wärme oder Licht größerer Wellenlänge und geringerer Frequenz.So far, people have been protecting themselves from too much sun exposure through so-called Sunscreens containing UV filters or absorbers. The UV absorber or UV protection filters are organic substances that are able to to absorb electromagnetic radiation in the UV range. The molecules go in here an energetically excited state. When returning to the basic state, the The energy absorbed again completely, but less or not for the skin released harmful form again, e.g. B. larger in the form of heat or light Wavelength and lower frequency.
Eine weitere Möglichkeit, sich vor Sonnenstrahlung zu schützen, ist das Bedecken der Haut mit Textilien. Es wurde jedoch festgestellt, dass die Vorstellung, die Textilien könnten die Haut vor schädigenden UV-Strahlen schützen, nicht richtig ist. In Abhängigkeit von der Faserdichte der Textilien können die UV-Strahlen durch das Gewebe durchtreten und zur Schädigungen auf der Haut führen. Auf dem Bereich der Textilien wurden bereits spezielle Fasermaterialien mit hohen UV-Lichtschutzfaktoren entwickelt. Ein Beispiel wird von M. Foessel et al., Melliand Textilber.; 78; 1997, S. 515 beschrieben.Another way to protect yourself from the sun's rays is to cover your skin with textiles. However, it was found that the notion that the textiles could Protect skin from damaging UV rays is not correct. Depending on the Fiber density of the textiles can penetrate the UV rays through the fabric and lead to Cause damage to the skin. In the field of textiles have already been special Fiber materials developed with high UV protection factors. An example is given by M. Foessel et al., Melliand Textilber .; 78; 1997, p. 515.
Die Schutzwirkung von Textilien kann analog des UV-Schutzfaktors von Kosmetika definiert werden als UPF-Faktor (UV-Protection Factor). D. Knittel et al., wieder Melliand Textilber.; 4/1999; S. 281, beschreiben, dass Gewebe mit einem UPF-Faktor < 50 nur noch ca. 1% der auftretenden Strahlung durchlassen. Derartige Gewebe können quasi als UV-undurchlässig bezeichnet werden, da der durchtretende Anteil der Strahlung als unbedenklich einzustufen ist.The protective effect of textiles can be defined analogously to the UV protection factor of cosmetics are called UPF factor (UV protection factor). D. Knittel et al., Again Melliand Textilber .; 4/1999; P. 281, describe that tissue with a UPF factor <50 only about 1% of the allow radiation to pass through. Such fabrics can be quasi UV-impermeable can be designated because the penetrating portion of the radiation can be classified as harmless is.
Die hohe Zahl der Hautkrebserkrankungen und die Verringerung der Ozonschicht verlangen nach weiteren Möglichkeiten, textile Gewebe mit UV-Schutzmitteln auszustatten, um die UV- Strahlendosis für Menschen, die sich im Freien aufhalten, zu minimieren.The high number of skin cancers and the reduction in the ozone layer demand for further possibilities of equipping textile fabrics with UV protection agents in order to Minimize radiation dose for people who are outdoors.
Der vorliegenden Erfindung lag demgemäß die Aufgabe zugrunde, Textilien, in Form von Fasern oder Geweben, zur Verfügung zu stellen, die einen Schutz gegen schädliche UV- Strahlen bieten, wobei bei den Textilien auch auf herkömmliche Fasern und Gewebe wie Naturtextilien etc. zurückgegriffen werden sollte.The present invention was accordingly based on the object, textiles, in the form of Fibers or fabrics to provide protection against harmful UV Offer rays, with the textiles also on conventional fibers and fabrics such as Natural textiles etc. should be used.
Überraschenderweise wurde festgestellt, dass, wenn man Textilien, Fasern oder fertige Gewebe mit einem UV-Strahlenfilter beaufschlagt, sich der UPF-Faktor deutlich verbessern lässt. Als textile Gewebe können sowohl natürliche als auch synthetische Textilien eingesetzt werden.Surprisingly, it was found that when you make textiles, fibers or finished A UV radiation filter is applied to the fabric, and the UPF factor improves significantly leaves. Both natural and synthetic textiles can be used as textile fabrics become.
Gegenstand der vorliegenden Erfindung ist demgemäß ein Textil, das sich dadurch auszeichnet, dass es mit einem UV-Strahlenmittel beaufschlagt ist.The present invention accordingly relates to a textile which is characterized by distinguishes that it is exposed to a UV radiation agent.
Der hier verwendete Begriff Textil umfasst sowohl Fasern als auch fertige Gewebe, die z. B. als Stoff oder als bereits verarbeitetes Produkt vorliegen. Das Textil kann aus beliebigen, bekannten Materialien bestehen, wie natürlichen und synthetischen Textilien, z. B. Baumwolle, Leinen, Seide, Hanf, Jute, Sisal, Viskose, Polyamid, Polyester, sowie beliebige weitere bekannte textile Materialien.The term textile used here includes both fibers and finished fabrics, e.g. B. available as a substance or as an already processed product. The textile can be made from any known materials exist, such as natural and synthetic textiles, e.g. B. Cotton, linen, silk, hemp, jute, sisal, viscose, polyamide, polyester, as well as any other well-known textile materials.
Als UV-Strahlenfilter können beliebige aus dem Stand der Technik bekannte Substanzen eingesetzt werden. Vorzugsweise sollten sie, sofern das Textil zu Bekleidungszwecken verarbeitet werden soll, keine schädigende oder allergene Wirkung auf die Haut ausüben. Beispiele für geeignete UV-Strahlenfilter sind p-Aminobenzoesäure, Trimonium benzylidencamphorsulfat, Homosalate, Benzophenon-3, 2-Phenylbenzimidazol-5-sulfonsäure und deren Salze, Terephtalydene-dicamphor-sulfonsäure und deren Salze, Butyl-methoxy dibenzoylmethan, Ester der p-Aminobenzoesäure, Campherderivate, Salicylsäureester, Benzophenon-4, Octyltriazone, Urocaninsäure, 2-Cyano-3,3diphenylacrylsäure ethylhexylester, Titandioxid, Al2O3 sowie deren beliebigen Gemische.Any substances known from the prior art can be used as the UV radiation filter. If the textile is to be processed for clothing, they should preferably have no harmful or allergenic effect on the skin. Examples of suitable UV radiation filters are p-aminobenzoic acid, trimonium benzylidene camphorsulfate, homosalates, benzophenone-3, 2-phenylbenzimidazole-5-sulfonic acid and its salts, terephthalate-dicamphor-sulfonic acid and its salts, butyl-methoxy dibenzoylmethane benzoic acid, ester of p-amine , Camphor derivatives, salicylic acid esters, benzophenone-4, octyltriazone, urocanic acid, 2-cyano-3,3-diphenylacrylic acid ethylhexyl ester, titanium dioxide, Al 2 O 3 and any mixtures thereof.
Es hat sich als besonders vorteilhaft erwiesen, wenn die UV-Strahlenfilter in fester Form vorliegen, insbesondere wenn sie nicht wasserlöslich sind. Eine geringe Wasserlöslichkeit beziehungsweise -unlöslichkeit hat den Vorteil, dass, wenn das Textil mit Wasser in Berührung kommt, wie z. B. im Regen oder beim Waschen, der UV-Strahlenfilter nicht sofort wieder herausgelöst wird. Besonders vorteilhaft ist es, wenn der UV-Strahlenfilter eine Teilchengröße zwischen 1 und 1.000 nm, besonders bevorzugt zwischen 5 und 300 nm und insbesondere zwischen 10 und 80 nm aufweist. Eine derartige Teilchengröße ist besonders vorteilhaft, weil sich der UV-Strahlenfilter quasihomogen auf dem Textil verteilen lässt, so dass die UV-Absorption nahezu flächendeckend bis in den mikroskopischen Bereich erfolgen kann. Ein weiterer Vorteil ist, dass die hohe Oberfläche der Strahlenfilterpartikel zu einer besonders effektiven UV-Absorption führt.It has proven to be particularly advantageous if the UV radiation filter in solid form are present, especially if they are not water-soluble. A low water solubility or insolubility has the advantage that if the textile with water in Comes into contact, such as B. in the rain or when washing, the UV radiation filter not immediately is released again. It when the UV radiation filter is a particularly advantageous Particle size between 1 and 1,000 nm, particularly preferably between 5 and 300 nm and has in particular between 10 and 80 nm. Such a particle size is special advantageous because the UV radiation filter can be distributed virtually homogeneously on the textile, so that UV absorption takes place almost across the board down to the microscopic range can. Another advantage is that the high surface area of the radiation filter particles becomes one leads to particularly effective UV absorption.
Auch werden durch die spezielle Partikelgröße Griff und Optik des Gewebes nicht nachhaltig verändert. Noch ein weiterer Vorteil ist, dass Partikel mit einer Teilchengröße im Nanobereich eine verbesserte Haftung an das Textilgewebe verglichen mit Partikeln mit geringerer spezifischer Oberfläche, also höherer Teilchengröße, aufweist.The special particle size also means that the feel and appearance of the fabric are not sustainable changed. Yet another advantage is that particles with a particle size in the nano range improved adhesion to the textile fabric compared to particles with less specific surface, that is, larger particle size.
Ein weiterer Gegenstand der vorliegenden Erfindung ist ein Verfahren zur Herstellung eines mit einem UV-Strahlenfilter beaufschlagten Textils, worin das Textil in eine Lösung, Dispersion oder Aufschlämmung eines UV-Strahlenfilters eingebracht wird, dort über einen ausreichenden Zeitraum belassen wird, damit sich der UV-Strahlenfilter auf dem Textil absetzen kann und anschließend getrocknet und gegebenenfalls in an sich bekannter Weise verarbeitet wird.Another object of the present invention is a method for producing a textile applied with a UV radiation filter, in which the textile is in a solution, Dispersion or slurry of a UV radiation filter is introduced, there over a sufficient time is left so that the UV radiation filter on the textile can settle and then dried and optionally in a manner known per se is processed.
In einer weiteren Ausgestaltung der vorliegenden Erfindung kann das mit UV-Strahlenfilter beaufschlagte Textil auch hergestellt werden, in dem das Textil mit einer Vorstufe eines UV- Strahlenfilters getränkt wird und die Vorstufe durch chemische Reaktion in den UV- Strahlenfilter überführt wird.In a further embodiment of the present invention, this can be done with a UV radiation filter loaded textile can also be produced in which the textile with a precursor of a UV Radiation filter is soaked and the precursor by chemical reaction in the UV Radiation filter is transferred.
Das Aufbringen der UV-Strahlenfilter kann z. B. durch gezielte Koagulation durch pH-Wert- Änderung oder Temperaturänderung erfolgen.The application of the UV radiation filter can, for. B. by targeted coagulation by pH Change or change in temperature.
Die in-situ-Bildung des UV-Strahlenfilters auf dem Textil ist insbesondere für solche Strahlenfilter geeignet, die sich durch einfache Reaktion auf ihren Vorstufen bilden lassen. Beispiele hierfür sind die Oxidvorstufen von anorganischen Strahlenfiltern, wie wässerige Al- oder Ti-Lösungen, die durch Hydrolyse beziehungsweise durch Änderung des pH-Wertes sich einfach in die Oxide überführen lassen. Die Bindung des UV-Strahlenfilters kann ohne zusätzliche Hilfs- und Bindemittel an das Textil gebunden werden. Insbesondere wenn der Strahlenfilter eine Teilchengröße im Nanobereich aufweist, können auf Bindemittel verzichtet werden.The in-situ formation of the UV radiation filter on the textile is especially for such Radiation filters are suitable, which can be formed by simply reacting to their preliminary stages. Examples of this are the oxide precursors of inorganic radiation filters, such as aqueous aluminum or Ti solutions by hydrolysis or by changing the pH can be easily converted into the oxides. The UV radiation filter can be bound without additional auxiliary and binding agents are bound to the textile. Especially if the Radiation filters with a particle size in the nano range can dispense with binders become.
In einer weiteren Ausgestaltung kann Bindung der UV-Strahlenfilter unter Einsatz von Bindemitteln unterstützt werden. Als Bindemittel können beispielsweise Polymerlösungen- bzw. -dispersionen auf wässeriger Basis, vorzugsweise von filmbildenden Polymeren, eingesetzt werden, die nach dem Aufbringen und Trocknen auf der Faser einen Film bilden. In a further embodiment, the UV radiation filter can be bound using Binders are supported. As a binder, for example, polymer solutions water-based dispersions or dispersions, preferably of film-forming polymers, are used, which form a film on the fiber after application and drying.
In einer bevorzugten Ausgestaltung der vorliegenden Erfindung werden UV-Strahlenfilter oder eine Vorstufe davon in Mittel zur Textilwäsche, -vor- oder -nachbehandlung eingesetzt.In a preferred embodiment of the present invention, UV radiation filters or a preliminary stage of it used in agents for textile washing, pre- or post-treatment.
Ein weiterer Gegenstand der vorliegenden Erfindung sind demgemäß Mittel für die Textilwäsche, Textilvor- oder -nachbehandlung, enthaltend übliche Inhaltsstoffe, die dadurch gekennzeichnet sind, dass sie mindestens einen UV-Strahlenfilter oder eine Vorstufe davon enthalten.Another object of the present invention are accordingly means for Textile laundry, textile pretreatment or aftertreatment, containing the usual ingredients are characterized in that they have at least one UV radiation filter or a precursor thereof contain.
Als weitere übliche Inhaltsstoffe, die in den Mitteln zur Textilwäsche-, -vor- oder -behandlung enthalten sein können, kommen z. B. Tenside, Builder, Cobuilder, Säuren bevorzugt Citronensäure, Amidosulfonsäure oder saure Salze wie Hydrogensulfat, Enzyme, Duftstoffe, Farbstoffe Bleichmittel auf Halogen- oder Sauerstoffbasis nebst Bleichaktivatoren bzw. - katalysatoren, Komplexbildner, wie z. B. Phosphonate, einschließlich komplexierender Tenside in Betracht. Maschinelle Geschirrspülmittel enthalten zusätzlich insbesondere Klarspültenside und Korrosionsinhibitoren. Textilwaschmittel enthalten üblicherweise neben den genannten Komponenten als Wirkstoffe Fluoreszenzmittel, optische Aufheller, Einlaufverhinderer, Textilavivage Knitterschutzmittel, antimikrobielle Wirkstoffe, Germizide, Fungizide, Antioxidantien, Antistatika, Enzyme, Bügelhilfsmittel, Phobier- und Imprägniermittel, UV-Absorber und/oder Duftstoffe in Betracht.As other common ingredients in the agents for textile washing, pretreatment or treatment can be included, come z. B. surfactants, builders, cobuilders, acids preferred Citric acid, amidosulfonic acid or acidic salts such as hydrogen sulfate, enzymes, fragrances, Dyes Bleaching agents based on halogen or oxygen together with bleach activators or - catalysts, complexing agents, such as. B. phosphonates, including complexing Surfactants into consideration. Machine dishwashing detergents additionally contain in particular Rinse aid surfactants and corrosion inhibitors. Textile detergents usually contain in addition the components mentioned as active ingredients fluorescent agents, optical brighteners, Enema preventers, textile anti-crease agents, antimicrobial agents, germicides, Fungicides, antioxidants, antistatic agents, enzymes, ironing aids, phobing and Impregnating agents, UV absorbers and / or fragrances into consideration.
Die erfindungsgemäßen Mittel sind vorzugsweise Textilweichspüler. Die Textilweichspüler enthalten als Tenside insbesondere kationische Tenside.The agents according to the invention are preferably fabric softeners. The fabric softener contain in particular cationic surfactants as surfactants.
UV-Schutzausrüstung von blauem Baumwollgewebe mit Al2O3/SiO2, das unbehandelt einen SPF = 18.1 aufwies.UV protective equipment of blue cotton fabric with Al 2 O 3 / SiO 2 , which had an SPF = 18.1 untreated.
0,68 g Aluminium-sec.-butylat und 7.9 g Tetraisopropylorthotitanat wurden mit 198 ml Isopropylalkohol vermischt. In einem zweiten Rundkolben wurde durch Mischen von 4,1 g Sulfobernsteinsäure-bis-2-ethylhexylester-Natriumsalz (AOT), 4,9 g n-Heptan und 3,0 g entionsiertem Wasser eine transparente W/O-Mikroemulsion hergestellt. In dieser Mikroemulsion wurde der Baumwollstoff getränkt. Das so vorbehandelte Textil wurde in die alkoholische Mischung überführt und darin 19 h belassen. Hierbei wurde das Aluminium- und das Titanalkoholat durch das im Mikroemulsionssystem stabilisierte Wasser hydrolysiert und nanoskaliges Oxid bildete sich auf dem Textil. Letzteres wurde 1 Minute unter fließendem Wasser gespült. Nach Trocknung des Textils wurde die Gewichtszunahme zu 1,5 Gew.-% bestimmt. Es wurde ein SPF von 73,0 ermittelt.0.68 g of aluminum sec-butoxide and 7.9 g of tetraisopropyl orthotitanate were mixed with 198 ml Isopropyl alcohol mixed. In a second round bottom flask was mixed by mixing 4.1 g Bis-2-ethylhexyl sulfosuccinate sodium salt (AOT), 4.9 g n-heptane and 3.0 g a transparent W / O microemulsion. In this The cotton fabric was soaked in microemulsion. The textile pretreated in this way was used in the Transfer the alcoholic mixture and leave it there for 19 hours. Here, the aluminum and the titanium alcoholate is hydrolyzed by the water stabilized in the microemulsion system and Nanoscale oxide formed on the textile. The latter was under running for 1 minute Rinsed water. After the textile had dried, the weight gain became 1.5% by weight. certainly. An SPF of 73.0 was determined.
UV-Schutzausrüstung von weißem Baumwollgewebe durch Behandeln mit einer nano-TiO2- Suspension, das unbehandelt einen von SPF = 5,1 aufwies.UV protection of white cotton fabric by treatment with a nano-TiO 2 suspension, which had an untreated one of SPF = 5.1.
Eine Titandioxidsuspension Tioveil® AQ-G (Fa. Tioveil) wurde mit entionsiertem Wasser bis auf eine Feststoffkonzentration von 0,1 Gew.-% verdünnt. Die Baumwollprobe wurde 5 h in der Suspension gerührt, anschließend ausgewrungen und im Trockenschrank bei 40°C und 50 mbar getrocknet. Die Gewichtszunahme betrug 0,6%. Es wurde ein SPF von 17,3 ermittelt.A titanium dioxide suspension Tioveil® AQ-G (from Tioveil) was mixed with deionized water diluted to a solids concentration of 0.1% by weight. The cotton sample was in 5 h the suspension stirred, then wrung out and in the drying cabinet at 40 ° C and 50 mbar dried. The weight gain was 0.6%. The SPF was 17.3 determined.
UV-Schutzausrüstung von weißem Baumwollgewebe durch Behandeln mit einer nano-TiO2- Suspension, das unbehandelt einen von SPF = 5,1 aufwies.UV protection of white cotton fabric by treatment with a nano-TiO 2 suspension, which had an untreated one of SPF = 5.1.
Eine Titandioxidsuspension Tioveil® AQ-G (Fa. Tioveil) wurde mit entionsiertem Wasser verdünnt bis auf eine Feststoffkonzentration von 0,5 Gew.-%. Die Baumwollprobe wurde 5 h in der Suspension gerührt, anschließend ausgewrungen und im Trockenschrank bei 40°C und 50 mbar getrocknet. Die Gewichtszunahme betrug 1,2%, es wurde ein SPF von 28.2 ermittelt.A titanium dioxide suspension Tioveil® AQ-G (from Tioveil) was mixed with deionized water diluted to a solids concentration of 0.5% by weight. The cotton sample was 5 hours stirred in the suspension, then wrung out and in a drying cabinet at 40 ° C and dried 50 mbar. The weight gain was 1.2%, the SPF was 28.2 determined.
UV-Schutzausrüstung von weißem Baumwollgewebe durch Behandeln mit einer nano-TiO2- Suspension, das unbehandelt einen von SPF = 5,1 aufwies. UV protection of white cotton fabric by treatment with a nano-TiO 2 suspension, which had an untreated one of SPF = 5.1.
Eine Titandioxidsuspension Tioveil® AQ-G (Fa. Tioveil) wurde mit entionsiertem Wasser bis auf eine Feststoffkonzentration von 1,0 Gew.-% verdünnt. Die Baumwollprobe wurde 5 h in der Suspension gerührt, anschließend ausgewrungen und im Trockenschrank bei 40°C und 50 mbar getrocknet. Die Gewichtszunahme betrug 3,5%, es wurde ein SPF von 43,0 ermittelt.A titanium dioxide suspension Tioveil® AQ-G (from Tioveil) was mixed with deionized water diluted to a solids concentration of 1.0% by weight. The cotton sample was in 5 h the suspension stirred, then wrung out and in the drying cabinet at 40 ° C and 50 mbar dried. The weight gain was 3.5% and the SPF was 43.0 determined.
UV-Schutzausrüstung von weißem Baumwollgewebe durch Behandeln mit einer nano-TiO2- Suspension, das unbehandelt einen von SPF = 5,1 aufwies.UV protection of white cotton fabric by treatment with a nano-TiO 2 suspension, which had an untreated one of SPF = 5.1.
Eine Titandioxidsuspension Tioveil® AQ-G (Fa. Tioveil) wurde mit entionsiertem Wasser bis auf eine Feststoffkonzentration von 2,0 Gew.-% verdünnt. Die Baumwollprobe wurde 5 h in der Suspension gerührt, anschließend ausgewrungen und im Trockenschrank bei 40°C und 50 mbar getrocknet. Die Gewichtszunahme betrug 5,5%, es wurde ein SPF von 64,9 ermittelt.A titanium dioxide suspension Tioveil® AQ-G (from Tioveil) was mixed with deionized water diluted to a solids concentration of 2.0% by weight. The cotton sample was in 5 h the suspension stirred, then wrung out and in the drying cabinet at 40 ° C and 50 mbar dried. The weight gain was 5.5% and the SPF was 64.9 determined.
UV-Schutzausrüstung von blauem Baumwollgewebe durch Aufziehen einer TiO2-Suspension und anschießende Koagulation durch pH-Erhöhung. Das unbehandelte Gewebe wies einen von SPF = 18,1 auf.UV protection of blue cotton fabric by pulling on a TiO 2 suspension and subsequent coagulation by raising the pH. The untreated tissue had one of SPF = 18.1.
Durch Verdünnung wurde mittels einer TiO2-Suspension Tioveil® AQ-G eine 1-gew.-%ige Suspension hergestellt. Der pH-Wert wurde auf 3 eingestellt. Das blaue Textilstück wurde mit der Suspension getränkt, anschließend ausgewrungen und getrocknet. Anschließend wurde das getrocknete Textil in eine Lösung des pH-Wertes gleich 6 eingebracht. Die Gewichtszunahme nach dem Trocknen betrug 7,6 Gew.-% und der SPF 64,9.A 1% by weight suspension was prepared by dilution using a TiO 2 suspension Tioveil® AQ-G. The pH was adjusted to 3. The blue textile piece was soaked in the suspension, then wrung out and dried. The dried textile was then introduced into a solution with a pH of 6. The weight gain after drying was 7.6% by weight and the SPF 64.9.
Eine 5 gew.-%ige wässrige Suspension von nanoskalarem Neo Heliopan® BB (10-100 nm) wurde auf 0,1 Gew.-% mit entionisiertem Wasser verdünnt. Die Textilprobe wurde in die Suspension gegeben und 5 Stunden gerührt. Anschließend wurde das Textil unter fließendem Wasser gespült und getrocknet. Die Gewichtszunahme betrug 1,4% und der SPF 85,6. A 5% by weight aqueous suspension of nanoscalar Neo Heliopan® BB (10-100 nm) was diluted to 0.1% by weight with deionized water. The textile sample was in the Suspension and stirred for 5 hours. Then the textile was under running water rinsed and dried. The weight gain was 1.4% and the SPF 85.6.
UV-Schutzausrüstung von weißem Gewebe mit dem organischen UV-Schutzmittel Neo Heliopan® (SPF-Wert vor der Behandlung 5,1).UV protection equipment of white fabric with the organic UV protection agent Neo Heliopan® (SPF value before treatment 5.1).
Eine 5 gew.-%ige wässrige Suspension von nanoskalarem Neo Heliopan® BB (10-100 nm) wurde auf 0,5 Gew.-% mit entionisiertem Wasser verdünnt. In die Suspension wurde die Textilprobe gegeben und es wurde 5 Stunden gerührt. Das Textil wurde unter fließendem Wasser gespült und getrocknet. Die Gewichtszunahme betrug 2,4% und der SPF 227,2.A 5% by weight aqueous suspension of nanoscalar Neo Heliopan® BB (10-100 nm) was diluted to 0.5% by weight with deionized water. In the suspension was the Textile sample was given and it was stirred for 5 hours. The textile was under flowing Rinsed water and dried. The weight gain was 2.4% and the SPF 227.2.
UV-Schutzausrüstung von weißem Gewebe mit dem organischen UV-Schutzmittel Neo Heliopan® (SPF des Gewebes vor der Behandlung 5,1).UV protection equipment of white fabric with the organic UV protection agent Neo Heliopan® (SPF of the tissue before treatment 5.1).
Eine 5 gew.-%ige wässrige Suspension von nanoskalarem Neo Heliopan® BB (10-100 nm) wurde auf 2,0 Gew.-% mit entionisiertem Wasser verdünnt. In die Suspension wurde die Textilprobe gegeben und es wurde 5 Stunden gerührt. Das Textil wurde unter fließendem Wasser gespült und getrocknet. Die Gewichtszunahme betrug 3,6% und der SPF 562,7.A 5% by weight aqueous suspension of nanoscalar Neo Heliopan® BB (10-100 nm) was diluted to 2.0% by weight with deionized water. In the suspension was the Textile sample was given and it was stirred for 5 hours. The textile was under flowing Rinsed water and dried. The weight gain was 3.6% and the SPF 562.7.
Claims (13)