CN85104269A - 硅锌矿结晶釉的定位定形技术 - Google Patents

硅锌矿结晶釉的定位定形技术 Download PDF

Info

Publication number
CN85104269A
CN85104269A CN198585104269A CN85104269A CN85104269A CN 85104269 A CN85104269 A CN 85104269A CN 198585104269 A CN198585104269 A CN 198585104269A CN 85104269 A CN85104269 A CN 85104269A CN 85104269 A CN85104269 A CN 85104269A
Authority
CN
China
Prior art keywords
willemite
glaze
location setting
crystal seed
crystalline glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
CN198585104269A
Other languages
English (en)
Other versions
CN85104269B (zh
Inventor
赵效忠
张桂英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Silicate Research Inst Liaoning Prov
Original Assignee
Silicate Research Inst Liaoning Prov
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Silicate Research Inst Liaoning Prov filed Critical Silicate Research Inst Liaoning Prov
Priority to CN85104269A priority Critical patent/CN85104269B/zh
Publication of CN85104269A publication Critical patent/CN85104269A/zh
Publication of CN85104269B publication Critical patent/CN85104269B/zh
Expired legal-status Critical Current

Abstract

一种日用陶瓷艺术釉的定位定形工艺技术，该技术为在预定部位放置氧化锆、硅锌矿及氧化锌等晶种，以达到晶花定位定形的目的。不仅大幅度提高了产品合格率，而且提高了产品外观的艺术效果。

Description

硅锌矿结晶釉的定位定形技术
本发明属于日用陶瓷生产工艺技术领域。
硅锌矿结晶釉是巨晶结晶釉的一个典型品种。由于釉高温粘度小，釉往往大量流淌到制品底部，而晶花也极量分布在制品底部，严重影响了合格率的提高。为改善晶花分布状态，诺顿（Norton）于1937年在《J、Am、Ceram、Soc）上提出了高温点种的定位结晶方法，但实际操作工序繁琐，没有工业实施价值，70年代末，本所成功地解决了定位结晶的问题。晶花可以在予定的部位生长，扩大了析晶温度范围，大幅度提高了合格率，但是定位晶花呈园盘状，花形单调，影响了外观效果。
本发明的目的，在于用定位结晶方法，采用不同种类的晶种，烧制出晶花位置固定而形态不同的结晶釉陶瓷产品。
本发明的要点在于采用玻璃粉、长石、氧化锌来配制结晶釉料，其化学成份为：
SiO255.17%、TiO20.03%、AlO33.79%、Fe2O20.29%、CaO 3.98%、MgO 2.56%、K2O、1.75%、Na2O 7.44%、ZnO 24.92%、NiO 1.00%
其釉式为：
0.031 K2O
0.202 Na2O
0.120 CaO 0.063 Al2O3
1.553 SiO2
0.107 MgO 0.003 Fe2O3
0.517    ZnO
0.023    NiO
其釉料需经球磨机充分磨细，过筛后其颗粒组成为：
63-10μ    40.36%    10-5μ    22.42%
5-2μ    17.94%    ＜2μ    19.28%
以氧化锆、硅锌矿及氧化锌为晶种。氧化锆晶种采用市售工业级氧化锆筛分即可，硅锌矿晶种采用由氧化锌和二氧化硅，经高温焙烧而得的合成硅锌矿，氧化锌晶种采用焙烧1300℃的工业纯氧化锌即可，颗粒度全部控制在0.16～0.42mm
点种的方式有三种：其一为釉下点种，即将晶种直接粘在坯体上;其二为釉上施种，即将晶种粘在釉面上;其三为釉面嵌种，即将晶种压入釉层中。上述三种方式，以釉面嵌种为最佳。
烧成制度：室温～1000℃    1000～1260℃
10℃/min    5℃/min
保温温度控制在1140℃～1120℃之间，如再低，则全部形成园盘状晶花。
根据本发明，可以在同一件制品上获得二种形态的晶花，硅锌矿或氧化锌晶种生长成园盘状晶花，氧化锆晶种生成石柱花状晶花。
本发明与现有技术比较，具有操作简单、合格率高，产品外外富于美感的优点。

Claims (2)

1、一种日用陶瓷生产工艺中的硅锌矿结晶釉的定位定形技术，在选用晶种时，不但使用硅锌矿和二氧化锌为晶种，而且其特征在于：使用工业纯氧化锆颗粒为晶种。
2、按权利要求1所述的日用陶瓷生产工艺中的硅锌矿结晶釉的定位定形技术，其保温温度控制在1140℃～1120℃之间。
CN85104269A 1985-05-27 1985-05-27 硅锌矿结晶釉的定位定形技术 Expired CN85104269B (zh)