CN208219128U - A kind of tridimensional spunlace non-woven cloth - Google Patents
A kind of tridimensional spunlace non-woven cloth Download PDFInfo
- Publication number
- CN208219128U CN208219128U CN201820214895.2U CN201820214895U CN208219128U CN 208219128 U CN208219128 U CN 208219128U CN 201820214895 U CN201820214895 U CN 201820214895U CN 208219128 U CN208219128 U CN 208219128U
- Authority
- CN
- China
- Prior art keywords
- spunlace non
- woven cloth
- thin area
- tridimensional
- tridimensional spunlace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a kind of tridimensional spunlace non-woven cloths, including multiple big salient points (2), the first thin area (3) and the second thin area (4) are installed between the adjacent big salient point (2) respectively, it is offered between the thin area of adjacent second (3) aperture (5), and the aperture (5) is between the second adjacent thin area (4).Tridimensional spunlace non-woven cloth described in the utility model has big salient point, the rough structure of three gradients and mesh, and using good hand feeling, wiping effect is good, is ideal purity material.
Description
Technical field
The utility model relates to a kind of tridimensional spunlace non-woven cloths, belong to hydro-entangled non-woven fabric field.
Background technique
The good water imbibition of hydro-entangled non-woven fabric and superior physical property, are widely used in wipe area.With
Domestic is horizontal and to the raising that wiper requires, and traditional wiper feel is not plentiful, wiping effect is undesirable, cloth cover is more smooth
The disadvantages of be suggested.
Utility model content
In order to solve the above-mentioned technical problem, the purpose of the utility model is to provide a kind of tridimensional spunlace non-woven cloths.
The utility model provides a kind of tridimensional spunlace non-woven cloth, including multiple big salient points, the adjacent big salient point
Between be installed with the first thin area and the second thin area respectively, offer aperture between the thin area of adjacent second, and the aperture is located at
Between the thin area of adjacent second.
Further, wherein being equipped with the first thin area between the longitudinally adjacent big salient point;Laterally adjacent is described big convex
The second thin area is equipped between point.
Further, wherein the surrounding of the aperture is connected with the described second thin area and the second thin area respectively.
Further, wherein the big salient point and the first thin area are rectangle respectively, are diamond shape, trapezoidal or round, but not only
It is limited to above-mentioned shape.
Further, wherein the aperture is ellipse, circle or rectangular through-hole, but it is not limited only to above-mentioned shape
Through-hole.
Further, wherein the punching rate of the aperture is 5-15 mesh.
Further, wherein the thickness of the tridimensional spunlace non-woven cloth is greater than 0.8mm.
Further, wherein the quantitative grammes per square metre of the tridimensional spunlace non-woven cloth is 40-200g/m2;Longitudinal fracture strength
Greater than 70N/ (5cm × 10cm);Cross breaking strength is greater than 14N/ (5cm × 10cm).
The utility model can reach following technical effect:
Tridimensional spunlace non-woven cloth described in the utility model using its big salient point, three rough structures of gradient with
And the features such as mesh, increase with by the area of cleaning piece and friction, there is good hand feeling, dust containing capacity is big, wiping effect is good etc.
Feature is ideal purity material.
Detailed description of the invention
Fig. 1 is the side view of tridimensional spunlace non-woven cloth described in an embodiment of the present invention;
Fig. 2 is the top view of tridimensional spunlace non-woven cloth described in an embodiment of the present invention.
Specific embodiment
The utility model is described in further detail with attached drawing combined with specific embodiments below, so that those skilled in the art
The utility model can be better understood and can be practiced, but illustrated embodiment is not as the restriction to the utility model.
Unless stated otherwise, following material or reagent are commercially available.
Embodiment 1
As Figure 1-Figure 2, a kind of tridimensional spunlace non-woven cloth 1, including multiple big salient points 2, phase are present embodiments provided
It is installed with the first thin area 3 and the second thin area 4 respectively between the adjacent big salient point 2, is offered between the thin area 3 of adjacent second small
Hole 5, and the aperture 5 is between the second adjacent thin area 4.And it is thin that first is equipped between the longitudinally adjacent big salient point 2
Area 3;The second thin area 4 is equipped between the laterally adjacent big salient point 2.The surrounding of the aperture 5 respectively with the described second thin area 3
And second thin area 4 be connected, design in this way first is that highlight big salient point, be exactly hole and Bao Qu around salient point big in this way, play
Stereoscopic effect;Play the role of increasing friction when such stereoscopic effect wiping object, while increasing dust containing capacity.The big salient point
2 and first thin area 3 can be rectangle, is diamond shape, trapezoidal or round, but be not limited only to above-mentioned shape.The aperture 5 can design
For ellipse, round or rectangular through-hole, but it is not limited only to the through-hole of above-mentioned shape, the purpose designed in this way is to increase
Dust containing capacity and frictional force.The punching rate of the aperture 5 had both made sample have preferable physical property item in this way between 5-15 mesh
Part, and make tridimensional spunlace non-woven cloth that there is good wiping effect;If punching rate is less than 5 mesh, tridimensional spunlace non-woven cloth
Hole it is too big, strength it is bad;If punching rate is greater than 15 mesh, the wiping effect of tridimensional spunlace non-woven cloth is undesirable, holds
Dust quantity is also restrained.The thickness of the tridimensional spunlace non-woven cloth is greater than 0.8mm, if thickness is less than 0.8mm, the solid water
The three-dimensional sense of spunlaced nonwoven is not easy to embody, and concave-convex effect is unobvious, and frictional force dust containing capacity is all affected.
The preparation method of above-mentioned tridimensional spunlace non-woven cloth 1, includes the following steps:
(1) each conjugate fiber (is selected into viscose rayon, specification 1.5D × 40mm, mass percent 30%;Terylene is fine
Dimension, specification 1.4D × 40mm, mass percent 70%) it is fed, shredding, mixing, combing networking;
(2) web the punching of spun lacing solid is carried out to reinforce;
(3) spun lacing reinforcement fiber web is subjected to impregnation arrangement with adhesive;
(4) it dries, wind, cutting, packaging.
Raw material: viscose rayon, specification 1.5D × 40mm, mass percent 50% are selected;Polyester fiber, specification 1.4D ×
40mm, mass percent 50%.
Feeding, shredding, mixing: it by manually proportionally feeding viscose rayon and polyester fiber respectively, is sent to out later
Loose machine carries out shredding, make fiber block and big cotton-wool dissipate from, mixing, abundant shredding.Composite fibre after thick shredding is through air-flow
It is transported to blending box, composite fibre is subjected to second of shredding and mixing using the wind-force effect of blower.
Combing networking: the composite fibre in above-mentioned blending box is transported to the mixed and disorderly carding machine of high speed through air-flow, to fiber into
Row combs and upsets fiber alignment, then transfers out web, and web grammes per square metre is 66g/m2。
Spun lacing: web into the net will be combed and reinforced using positive and negative plain net mode spun lacing, totally eight water jets.Reverse side plain net
Support net is plain weave net, and the pressure of spun lacing Dao Shuo tetra-, first of water jet are 20bar, and the pressure of second water jet is
50bar, the pressure of third road water jet are 70bar, and the pressure of the 4th water jet is 90bar;Front plain net support net is vertical for 8 mesh
Body net, spun lacing Dao Shuo tetra-, the pressure of the 5th water jet are 80bar, and the pressure of the 6th water jet is 100bar;7th
The pressure of plain net water jet is 110bar;The pressure of 8th plain net water jet is 110bar.
Impregnation arranges:
The ingredient and its mass percent of finishing agent are as follows:
It after each components in certain proportion of above-mentioned finishing agent is mixed, is sufficiently stirred, generates foam using foam-making apparatus;It
The base fabric that spun lacing is come out afterwards carries out the arrangement of foam impregnation, and liquid outlet quantity is controlled in 100L/h.
Drying: removal is dried to the moisture retained during spun lacing using hot-air through type dryer in this process, makes
Tridimensional spunlace non-woven cloth 1 is more convenient to be used, and drying temperature is 165 DEG C, drying rate 38m/min.
Winding: the tridimensional spunlace non-woven cloth 1 after drying is wound using coiling machine;
Cutting: three-dimensional hydro-entangled non-woven fabric 1 is cut according to the requirement specification of client;
Packaging: the tridimensional spunlace non-woven cloth 1 cut is packed.
Embodiment 2
Properties of product test has been carried out to tridimensional spunlace non-woven cloth 1 prepared in the above embodiments below.
Test process and result are as follows:
(1) quantitative grammes per square metre test
Test equipment: electronic balance, test method: GB/T24218.1-2009, test result are as shown in table 1.
A kind of quantitative grammes per square metre test result of the tridimensional spunlace non-woven cloth of table 1
Sample | Quantitative grammes per square metre (g/m2) |
A kind of tridimensional spunlace non-woven cloth | 70 |
(2) thickness is tested
Test equipment: YG141 fabric thickness tester, test method: GB/T24218.2-2009, test result such as table 2
It is shown.
A kind of thickness test result of the tridimensional spunlace non-woven cloth of table 2
Sample | Thickness (mm) |
A kind of tridimensional spunlace non-woven cloth | 1.27 |
(3) strength and elongation test
Test equipment: electronics strength tester, test method: GB/T24218.3-2010, test result are as shown in table 3.
The strength and elongation test result of a kind of tridimensional spunlace non-woven cloth of table 3
(4) wiping is tested
Binding dust spunlace non-woven material prepared by above-described embodiment 1 is cut into 25cm × 25cm sample, is supplied to family
Personnel carry out assessment on probation.Person on probation's feedback information are as follows: good hand feeling, wiping dust work well.
By above embodiments and test it can be found that the tridimensional spunlace non-woven cloth production in the utility model is simple,
Cost is relatively low, and have the characteristics that with good hand feeling, easy to use, dust containing capacity is big, wiping effect is good, be ideal cleaning
Material.
Embodiment described above be only for absolutely prove the utility model and for embodiment, the protection of the utility model
Range is without being limited thereto.Those skilled in the art made equivalent substitute or transformation on the basis of the utility model, exist
Within the protection scope of the utility model.The protection scope of the utility model is subject to claims.
Claims (8)
1. a kind of tridimensional spunlace non-woven cloth, which is characterized in that including multiple big salient points (2), the adjacent big salient point (2) it
Between be installed with the first thin area (3) and the second thin area (4) respectively, offered aperture (5) between the thin area of adjacent second (4), and institute
Aperture (5) are stated between the second adjacent thin area (4).
2. tridimensional spunlace non-woven cloth as described in claim 1, which is characterized in that the longitudinally adjacent big salient point (2) it
Between be equipped with the first thin area (3);The second thin area (4) is equipped between the laterally adjacent big salient point (2).
3. tridimensional spunlace non-woven cloth as described in claim 1, which is characterized in that the surrounding of the aperture (5) respectively with institute
It states the first thin area (3) and the second thin area (4) is connected.
4. tridimensional spunlace non-woven cloth as described in claim 1, which is characterized in that the big salient point (2) and the first thin area (3)
It is rectangle respectively, is diamond shape, trapezoidal or round.
5. tridimensional spunlace non-woven cloth as described in claim 1, which is characterized in that the aperture (5) is ellipse, it is round or
Rectangular through-hole.
6. tridimensional spunlace non-woven cloth as claimed in claim 5, which is characterized in that the punching rate of the aperture (5) is 5-15
Mesh.
7. tridimensional spunlace non-woven cloth as described in claim 1, which is characterized in that the thickness of the tridimensional spunlace non-woven cloth
Greater than 0.8mm.
8. such as the described in any item tridimensional spunlace non-woven cloths of claim 1-7, which is characterized in that the tridimensional spunlace is non-woven
The quantitative grammes per square metre of cloth is 40-200g/m2;Longitudinal fracture strength is greater than 70N/ (5cm × 10cm);Cross breaking strength is greater than 14N/
(5cm×10cm)。