CN106048893A - Anti-siphon non-woven fabric and manufacturing method thereof - Google Patents
Anti-siphon non-woven fabric and manufacturing method thereof Download PDFInfo
- Publication number
- CN106048893A CN106048893A CN201610567083.1A CN201610567083A CN106048893A CN 106048893 A CN106048893 A CN 106048893A CN 201610567083 A CN201610567083 A CN 201610567083A CN 106048893 A CN106048893 A CN 106048893A
- Authority
- CN
- China
- Prior art keywords
- siphon
- adhesive
- bonded fabric
- shredding
- web
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-siphon non-woven fabric and manufacturing method thereof. Raw materials of the anti-siphon non-woven fabric includes the following components in parts by weight: 50 to 70 parts of polyester fiber and 30 to 50 parts of low-melting cotton, wherein the polyester fiber includes two dimensions of 16D*51mm and 6D*51mm, and the dimension of the low-melting cotton is 4D*51mm. Common polyester fiber and low-melting cotton are subjected mixed opening according to proportion, then enter a carding machine to be carded to form a web, are then subjected to lapping stacking through a lapping machine, are then subjected to high-speed needle punching interweaving, and are then subjected to hot-pressing shaping, thereby obtaining a base fabric, and the base fabric is put in a soaking pool of a waterproof blending agent to be soaked and are dried, thereby obtaining the anti-siphon non-woven fabric. The anti-siphon non-woven fabric has the characteristics of high tension and tear resistance, good bending performance and good waterproof effect, and satisfies requirements of outdoor equipment products.
Description
Technical field
The present invention relates to textile material field, a kind of anti-siphon adhesive-bonded fabric and manufacture method thereof.
Background technology
Along with the raising of people's living standard, outdoor activity as the motion mode of a kind of health increasingly by people's
Like.It is generally required to carry the outdoor gear product of some necessity when carrying out outdoor activity, such as outdoor tent and outdoor shoe are just
It it is the most the more commonly used outdoor equipment product.In prior art, the adjuvant of the outdoor gear product such as outdoor tent, outdoor shoe,
Common non-woven fabrics or cardboard is usually used to make, but common non-woven fabrics or cardboard, its pulling force, tear resistance, complications
Property and water resistance are poor, it is impossible to meet the demand of outdoor gear product.
Summary of the invention
In order to overcome the deficiencies in the prior art, the present invention provides a kind of anti-siphon adhesive-bonded fabric and manufacture method thereof, and it can carry
Relatively strong for a kind of pulling force, tear resistance, tortuous performance is good and the preferable anti-siphon adhesive-bonded fabric of waterproof effect.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of anti-siphon adhesive-bonded fabric, its raw materials by weight portion includes following component: polyster fibre 50～70 parts, eutectic is cotton
30～50 parts, described polyster fibre includes 16D × 51mm and two kinds of dimensions of 6D × 51mm, and described eutectic cotton dimensions is
4D×51mm。
As the improvement of technique scheme, 16D × 51mm and two kinds of dimensions of 6D × 51mm in described polyster fibre
Weight ratio be 1: (1～2).
The manufacture method of above-mentioned anti-siphon adhesive-bonded fabric, comprises the following steps:
(1) shredding: washing fiber and eutectic cotton mix homogeneously are sent into cotton storage tank, be then fed into opener carry out loosening,
Dissociation, reaches shredding uniform；
(2) combing: the raw material of shredding step (1) obtained is sent into carding machine and carried out carding；
(3) lapping: web step (2) obtained carries out, by lapping machine, the number of plies that lapping is laminated to set；
(4) pin is pricked: web step (3) being paved into pricks, by needing machine pin the most repeatedly, sizing of tangling；
(5) thermocompression forming: web step (4) obtained obtains base fabric after thermocompression forming, rolling；
(6) base fabric is soaked by fermentation vat, fermentation vat is placed with waterproof intermixture；
(7) carry out drying and described anti-siphon can being obtained by layering rolling not knitting by baking oven by soaked base fabric
Cloth.
Further, in step (1), shredding operation includes thick shredding operation and essence shredding operation.
Further, in step (3), the number of described web stacking be 20 layers or more than.
Further, in step (4), pin mutual aid system devised for poor peasants sequence includes pre-thorn operation and main thorn operation, and web first passes around pre-thorn operation,
Carrying out main thorn operation the most again, in main thorn operation, web is by upper and lower repeated puncture.
Further, in step (6), described its raw materials by weight portion of waterproof intermixture includes following component: waterproofing agent 6
～10 parts, water based emulsion 0.5～2 parts, water 50～70 parts, carry out each component in proportion disperseing, stir after obtain described waterproof
Intermixture.
Further, in step (7), in baking operation, the temperature of baking oven is 140～180 DEG C.
Further, by negative-pressure pipeline, the raw material after essence shredding being entered into air pressure cotton box, air pressure cotton box is with equilibrium
Raw material constant volume is given to carding machine and carries out combing by the mode of pressure.
The invention has the beneficial effects as follows: the one anti-siphon adhesive-bonded fabric of the present invention and manufacture method thereof, by will commonly wash
Synthetic fibre fiber and eutectic cotton are mixed in proportion shredding, carry out carding subsequently into carding machine, then carry out lapping by lapping machine
Stacking, then passes through high speed pin and pricks intertexture, then obtain base fabric through thermocompression forming, by base fabric by being placed with waterproof intermixture
Carrying out after soaking in fermentation vat drying and obtain this anti-siphon adhesive-bonded fabric, this anti-siphon adhesive-bonded fabric has pulling force, tear resistance
By force, tortuous performance is good and the feature of good water-proof effect, and its longitudinal pulling force is up to 280～320N/5cm, and lateral pull is up to 380
～400N/5cm, longitudinal extension rate up to 50%～70%, horizontal expansion rate up to 60%～70%, its pulling force characteristic and tear
Performance relatively common adhesive-bonded fabric tool have greatly improved, simultaneously because base fabric is soaked through waterproof intermixture so that this anti-rainbow
Inhale adhesive-bonded fabric and there is good water resistance, and this anti-siphon adhesive-bonded fabric has reasonable tortuous performance after pin is pricked,
The demand of outdoor gear product can be met.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further.
Embodiment 1
A kind of anti-siphon adhesive-bonded fabric, its raw materials by weight portion includes following component: polyster fibre 60 parts, eutectic cotton 40
Part, polyster fibre includes 16D × 51mm and two kinds of dimensions of 6D × 51mm, and eutectic cotton dimensions is 4D × 51mm.
Wherein, in polyster fibre, the weight ratio of 16D × 51mm and two kinds of dimensions of 6D × 51mm is 1: 1.
The manufacture method of above-mentioned anti-siphon adhesive-bonded fabric, comprises the following steps:
(1) shredding: washing fiber according to the above ratio and eutectic cotton mix homogeneously are sent into cotton storage tank, is then fed into shredding
Machine carries out loosening, dissociating, and reaches shredding uniform；
(2) combing: the raw material of shredding step (1) obtained is sent into carding machine and carried out carding；
(3) lapping: the web that step (2) is obtained by lapping machine carry out lapping be laminated to 20 layers or more than；
(4) pin is pricked: web step (3) being paved into pricks, by needing machine pin the most repeatedly, sizing of tangling；
(5) thermocompression forming: web step (4) obtained obtains base fabric after thermocompression forming, rolling；
(6) base fabric is soaked by fermentation vat, fermentation vat is placed with waterproof intermixture；
(7) carry out drying and can being obtained by layering rolling at 140～180 DEG C by baking oven by soaked base fabric
Described anti-siphon adhesive-bonded fabric.
In step (1), shredding operation includes thick shredding operation and essence shredding operation, is passed through by the raw material after essence shredding
Negative-pressure pipeline enters into air pressure cotton box, and raw material constant volume is given to carding machine in the way of counterpressure and combs by air pressure cotton box
Reason.
In step (4), pin mutual aid system devised for poor peasants sequence includes pre-thorn operation and main thorn operation, and web first passes around pre-thorn operation, the most again
Carrying out main thorn operation, in main thorn operation, web is by upper and lower repeated puncture.
In step (6), described its raw materials by weight portion of waterproof intermixture includes following component: waterproofing agent 8 parts, aqueous
Latex 1 part, 60 parts of water, carry out each component in proportion disperseing, stir after obtain described waterproof intermixture.
The anti-siphon adhesive-bonded fabric above-mentioned manufacture method obtained compares, such as following table with the performance of common adhesive-bonded fabric:
Visible, the anti-siphon adhesive-bonded fabric of the present invention has stronger pulling force, a tear resistance, and its tortuous performance and anti-
Water effectiveness comparison is good.
Embodiment 2
A kind of anti-siphon adhesive-bonded fabric, its raw materials by weight portion includes following component: polyster fibre 70 parts, eutectic cotton 30
Part, polyster fibre includes 16D × 51mm and two kinds of dimensions of 6D × 51mm, and eutectic cotton dimensions is 4D × 51mm.
Wherein, in polyster fibre, the weight ratio of 16D × 51mm and two kinds of dimensions of 6D × 51mm is 1: 1.5.
The manufacture method of above-mentioned anti-siphon adhesive-bonded fabric, comprises the following steps:
(1) shredding: washing fiber according to the above ratio and eutectic cotton mix homogeneously are sent into cotton storage tank, is then fed into shredding
Machine carries out loosening, dissociating, and reaches shredding uniform；
(2) combing: the raw material of shredding step (1) obtained is sent into carding machine and carried out carding；
(3) lapping: the web that step (2) is obtained by lapping machine carry out lapping be laminated to 20 layers or more than；
(4) pin is pricked: web step (3) being paved into pricks, by needing machine pin the most repeatedly, sizing of tangling；
(5) thermocompression forming: web step (4) obtained obtains base fabric after thermocompression forming, rolling；
(6) base fabric is soaked by fermentation vat, fermentation vat is placed with waterproof intermixture；
(7) carry out drying and can being obtained by layering rolling at 140～180 DEG C by baking oven by soaked base fabric
Described anti-siphon adhesive-bonded fabric.
In step (1), shredding operation includes thick shredding operation and essence shredding operation, is passed through by the raw material after essence shredding
Negative-pressure pipeline enters into air pressure cotton box, and raw material constant volume is given to carding machine in the way of counterpressure and combs by air pressure cotton box
Reason.
In step (4), pin mutual aid system devised for poor peasants sequence includes pre-thorn operation and main thorn operation, and web first passes around pre-thorn operation, the most again
Carrying out main thorn operation, in main thorn operation, web is by upper and lower repeated puncture.
In step (6), described its raw materials by weight portion of waterproof intermixture includes following component: waterproofing agent 7 parts, aqueous
Latex 1 part, 50 parts of water, carry out each component in proportion disperseing, stir after obtain described waterproof intermixture.
Embodiment 3
A kind of anti-siphon adhesive-bonded fabric, its raw materials by weight portion includes following component: polyster fibre 50 parts, eutectic cotton 50
Part, polyster fibre includes 16D × 51mm and two kinds of dimensions of 6D × 51mm, and eutectic cotton dimensions is 4D × 51mm.
Wherein, in polyster fibre, the weight ratio of 16D × 51mm and two kinds of dimensions of 6D × 51mm is 1: 2.
The manufacture method of above-mentioned anti-siphon adhesive-bonded fabric, comprises the following steps:
(1) shredding: washing fiber according to the above ratio and eutectic cotton mix homogeneously are sent into cotton storage tank, is then fed into shredding
Machine carries out loosening, dissociating, and reaches shredding uniform；
(2) combing: the raw material of shredding step (1) obtained is sent into carding machine and carried out carding；
(3) lapping: the web that step (2) is obtained by lapping machine carry out lapping be laminated to 20 layers or more than；
(4) pin is pricked: web step (3) being paved into pricks, by needing machine pin the most repeatedly, sizing of tangling；
(5) thermocompression forming: web step (4) obtained obtains base fabric after thermocompression forming, rolling；
(6) base fabric is soaked by fermentation vat, fermentation vat is placed with waterproof intermixture；
(7) carry out drying and can being obtained by layering rolling at 140～180 DEG C by baking oven by soaked base fabric
Described anti-siphon adhesive-bonded fabric.
In step (1), shredding operation includes thick shredding operation and essence shredding operation, is passed through by the raw material after essence shredding
Negative-pressure pipeline enters into air pressure cotton box, and raw material constant volume is given to carding machine in the way of counterpressure and combs by air pressure cotton box
Reason.
In step (4), pin mutual aid system devised for poor peasants sequence includes pre-thorn operation and main thorn operation, and web first passes around pre-thorn operation, the most again
Carrying out main thorn operation, in main thorn operation, web is by upper and lower repeated puncture.
In step (6), described its raw materials by weight portion of waterproof intermixture includes following component: waterproofing agent 10 parts, water
Property latex 1.5 parts, 70 parts of water, carry out each component in proportion disperseing, stir after obtain described waterproof intermixture.
The present invention, by ordinary polyester fiber and eutectic cotton are mixed in proportion shredding, carries out combing subsequently into carding machine
Become net, then carry out lapping stacking by lapping machine, then pass through high speed pin and prick intertexture, then obtain base fabric through thermocompression forming, will
Base fabric by be placed with the fermentation vat of waterproof intermixture soaks after carry out dry obtain this anti-siphon adhesive-bonded fabric, this anti-rainbow
Inhaling adhesive-bonded fabric, to have pulling force, tear resistance strong, and tortuous performance is good and the feature of good water-proof effect, and its longitudinal pulling force is up to 280
～320N/5cm, lateral pull up to 380～400N/5cm, longitudinal extension rate up to 50%～70%, horizontal expansion rate up to
60%～70%, its pulling force characteristic and the relatively common adhesive-bonded fabric tool of tear resistance have greatly improved, simultaneously because base fabric warp
Cross waterproof intermixture to soak so that this anti-siphon adhesive-bonded fabric has good water resistance, and this anti-siphon adhesive-bonded fabric passes through
Pin has reasonable tortuous performance after pricking, can meet the demand of outdoor gear product.
The above, the simply better embodiment of the present invention, but the present invention is not limited to above-described embodiment, as long as
It reaches the technique effect of the present invention with any same or similar means, all should fall under the scope of the present invention.
Claims (9)
1. an anti-siphon adhesive-bonded fabric, it is characterised in that raw materials by weight portion includes following component: polyster fibre 50～70
Part, cotton 30～50 parts of eutectic, described polyster fibre includes 16D × 51mm and two kinds of dimensions of 6D × 51mm, and described eutectic is cotton
Dimensions is 4D × 51mm.
One the most according to claim 1 anti-siphon adhesive-bonded fabric, it is characterised in that: 16D × 51mm in described polyster fibre
It is 1:(1～2 with the weight ratio of two kinds of dimensions of 6D × 51mm).
The manufacture method of a kind of anti-siphon adhesive-bonded fabric the most according to claim 1 and 2, it is characterised in that include following step
Rapid:
(1) shredding: will wash fiber and eutectic cotton mix homogeneously sends into cotton storage tank, being then fed into opener carries out loosening, dissociating,
Reach shredding uniform；
(2) combing: the raw material of shredding step (1) obtained is sent into carding machine and carried out carding；
(3) lapping: web step (2) obtained carries out, by lapping machine, the number of plies that lapping is laminated to set；
(4) pin is pricked: web step (3) being paved into pricks, by needing machine pin the most repeatedly, sizing of tangling；
(5) thermocompression forming: web step (4) obtained obtains base fabric after thermocompression forming, rolling；
(6) base fabric is soaked by fermentation vat, fermentation vat is placed with waterproof intermixture；
(7) carry out drying and described anti-siphon adhesive-bonded fabric can being obtained by layering rolling by baking oven by soaked base fabric.
The manufacture method of a kind of anti-siphon adhesive-bonded fabric the most according to claim 3, it is characterised in that: in step (1), shredding
Operation includes thick shredding operation and essence shredding operation.
The manufacture method of a kind of anti-siphon adhesive-bonded fabric the most according to claim 3, it is characterised in that: in step (3), described
The number of web stacking be 20 layers or more than.
The manufacture method of a kind of anti-siphon adhesive-bonded fabric the most according to claim 3, it is characterised in that: in step (4), pin is pricked
Operation includes pre-thorn operation and main thorn operation, and web first passes around pre-thorn operation, carries out main thorn operation the most again, in main thorn operation
Middle web is by upper and lower repeated puncture.
The manufacture method of a kind of anti-siphon adhesive-bonded fabric the most according to claim 3, it is characterised in that: in step (6), described
Its raw materials by weight portion of waterproof intermixture include following component: waterproofing agent 6～10 parts, water based emulsion 0.5～2 parts, water 50
～70 parts, carry out each component in proportion disperseing, stir after obtain described waterproof intermixture.
The manufacture method of a kind of anti-siphon adhesive-bonded fabric the most according to claim 3, it is characterised in that: in step (7), dry
In operation, the temperature of baking oven is 140～180 DEG C.
The manufacture method of a kind of anti-siphon adhesive-bonded fabric the most according to claim 4, it is characterised in that: will be after essence shredding
Raw material enter into air pressure cotton box by negative-pressure pipeline, raw material constant volume is given to combing in the way of counterpressure by air pressure cotton box
Machine carries out combing.