CN207032571U - High performance water proof thermal insulation system - Google Patents
High performance water proof thermal insulation system Download PDFInfo
- Publication number
- CN207032571U CN207032571U CN201720499100.2U CN201720499100U CN207032571U CN 207032571 U CN207032571 U CN 207032571U CN 201720499100 U CN201720499100 U CN 201720499100U CN 207032571 U CN207032571 U CN 207032571U
- Authority
- CN
- China
- Prior art keywords
- layer
- wall
- water proof
- high performance
- performance water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of high performance water proof thermal insulation system, including：Exterior wall finish layer, polymer waterproof layer, high-strength light screed-coat, self heat insulation wall, inner thermal insulating layer, anti-cracking protective layer and inner wall finishing layer, the outside of described self heat insulation wall covers high-strength light screed-coat, polymer waterproof layer and exterior wall finish layer successively outward from interior, and the inner side of described self heat insulation wall is from outside inside successively covered with inner thermal insulating layer, anti-cracking protective layer and inner wall finishing layer.Polymer waterproof layer, lifting system water resistance are set on the outside of the utility model, and building energy conservation is based on self-insurance temperature technique and inside holding technology, is aided with high-strength light leveling mortar, combination reaches power conservation requirement.
Description
Technical field
Building material field is the utility model is related to, more particularly to a kind of high performance water proof thermal insulation system.
Background technology
Because heat insulating material for external market is more chaotic, product quality is uneven, the insulation of external wall alien invasion and dress
Decorations engineering is in the prevalence of different degrees of cracking, infiltration, hollowing, the quality problems such as come off, not only heavy damage building
Outward appearance and energy-saving effect, be also greatly reduced the life-span of building and the quality of life of occupant.Therefore utility model one
It is very necessary that kind, which has waterproof and the building heat insulation system of heat insulation function concurrently,.
Utility model content
The utility model disclosure satisfy that mainly solving the technical problems that provide a kind of high performance water proof thermal insulation system
Building energy conservation requirement, the quality problems such as the cracking, leak of exterior wall heat-preserving system are avoided, the waterproof and energy-conservation for lifting building are imitated
Fruit.
In order to solve the above technical problems, the technical scheme that the utility model uses is：A kind of high performance water proof is provided
Thermal insulation system, including：Exterior wall finish layer, polymer waterproof layer, high-strength light screed-coat, self heat insulation wall, inner thermal insulating layer,
Anti-cracking protective layer and inner wall finishing layer, the outside of described self heat insulation wall from it is interior cover successively outward high-strength light screed-coat,
Polymer waterproof layer and exterior wall finish layer, the inner side of described self heat insulation wall is from outside inside successively covered with inner thermal insulating layer, anti-
Split overcoat and inner wall finishing layer.
In one preferred embodiment of the utility model, described self heat insulation wall is autoclave aerated concrete building block wall
Or self-insulating concrete composite block wall.
In one preferred embodiment of the utility model, described inner thermal insulating layer is spraying hard-foam polyurethane heat-insulation layer.
In one preferred embodiment of the utility model, described anti-cracking protective layer is that the cement base of surface press-in screen cloth resists
Split mortar.
In one preferred embodiment of the utility model, described exterior wall finish layer is external wall putty and coating.
In one preferred embodiment of the utility model, described inner wall finishing layer is architecture indoor putty and coating.
In one preferred embodiment of the utility model, the thickness of described exterior wall finish layer is 3 ~ 7mm, polymer waterproof
Thickness degree is 3 ~ 5mm, high-strength light screed-coat thickness is 15 ~ 25mm, inner thermal insulating layer thickness is 15 ~ 30mm, anti-cracking protective layer is thick
It is 3 ~ 7mm to spend for 8 ~ 15mm, inner wall finishing thickness degree.
The beneficial effects of the utility model are：
1st, the utility model takes into account the waterproof of construction wall, heat insulation function, and outside sets polymer waterproof layer, lifting system
Water resistance, building energy conservation are based on self-insurance temperature technique and inside holding technology, are aided with high-strength light leveling mortar, combination reaches
Power conservation requirement.
2nd, high-strength light screed-coat and polymerization waterproof layer are provided with the outside of the utility model wall, is had with self heat insulation wall
There is more excellent matching, there is the technical characteristics such as high intensity, water-proofing anticracking, while also have certain heat insulation function, beam column etc. cold
Bridge position meets power conservation requirement, can cancel conventional external thermal insulation system, reduces external-wall heat-insulation material and ftractures, comes off, permeates
Quality problems.
3rd, the utility model inner side of outer wall use spraying hard-foam polyurethane heat-insulation layer, mechanized construction steady quality, with oneself
Heat-preserving wall cohesive force is strong, avoids the common quality defects such as self heat insulation wall hollowing, cracking；Inside holding technology can significantly improve Indoor Thermal
Environment, improve residence comfort.
Brief description of the drawings
, below will be to needed for embodiment description in order to illustrate more clearly of the technical scheme in the embodiment of the utility model
The accompanying drawing to be used is briefly described, it should be apparent that, drawings in the following description are only some realities of the present utility model
Example is applied, for those of ordinary skill in the art, on the premise of not paying creative work, can also be according to these accompanying drawings
Other accompanying drawings are obtained, wherein：
Fig. 1 is the structural representation of the preferred embodiment of the utility model high performance water proof thermal insulation system one；
The mark of each part is as follows in accompanying drawing：1st, exterior wall finish layer, 2, polymer waterproof layer, 3, high-strength light screed-coat,
4th, self heat insulation wall, 5, inner thermal insulating layer, 6, anti-cracking protective layer, 7, inner wall finishing layer.
Embodiment
The technical scheme in the embodiment of the utility model will be clearly and completely described below, it is clear that described
Embodiment is only part of the embodiment of the present utility model, rather than whole embodiments.Based on the implementation in the utility model
Example, all other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, is belonged to
The scope of the utility model protection.
Referring to Fig. 1, embodiment 1
A kind of high performance water proof thermal insulation system, including：Exterior wall finish layer 1, polymer waterproof layer 2, high-strength light are looked for
Flat bed 3, self heat insulation wall 4, inner thermal insulating layer 5, anti-cracking protective layer 6 and inner wall finishing layer 7, the outside of described self heat insulation wall 4
From interior outward successively covered with high-strength light screed-coat 3, polymer waterproof layer 2 and exterior wall finish layer 1, described self heat insulation wall
4 inner side is from outside inside successively covered with inner thermal insulating layer 5, anti-cracking protective layer 6 and inner wall finishing layer 7.Described self heat insulation wall 4
For autoclave aerated concrete building block wall, described inner thermal insulating layer 5 is spraying hard-foam polyurethane heat-insulation layer, and described cracking resistance is protected
Layer 6 is the cement base anticracking grout that surface is pressed into screen cloth, and described exterior wall finish layer 1 is external wall putty and coating, described
Inner wall finishing layer 7 be architecture indoor putty and coating, the thickness of described exterior wall finish layer 1 is 5mm, polymer waterproof layer 2
Thickness is 4mm, the thickness of high-strength light screed-coat 3 is 20mm, the thickness of inner thermal insulating layer 5 is 22mm, the thickness of anti-cracking protective layer 6 is
12mm, the thickness of inner wall finishing layer 7 are 5mm.
Described polymer waterproof layer 2 is made up of the raw material of following parts by weight：18 parts of cement, acrylic latex powder 17
Part, 45 parts of fine sand, 19 parts of metakaolin, 0.3 part of defoamer, 0.2 part of polycarboxylate water-reducer, 1.0 parts of organosilicon moisture repellent.
Described high-strength light screed-coat 3 is made up of the raw material of following parts by weight：64 parts of cement, 10 parts of flyash, firmly
4 parts of gypsum, 6 parts of lightweight aggregate, 12 parts of fine sand, 0.15 part of cellulose ether, 0.6 part of wood-fibred, 4 parts of vinyl acetate emulsion powder.
Described cement base anticracking grout is made up of the raw material of following parts by weight：28 parts of cement, 7 parts of flyash, light bone
4 parts of material, 55 parts of fine sand, 0.3 part of cellulose ether, 0.4 part of polypropylene fibre, 5 parts of vinyl acetate emulsion powder.
Referring to Fig. 1, embodiment 2
A kind of high performance water proof thermal insulation system, including：Exterior wall finish layer 1, polymer waterproof layer 2, high-strength light are looked for
Flat bed 3, self heat insulation wall 4, inner thermal insulating layer 5, anti-cracking protective layer 6 and inner wall finishing layer 7, the outside of described self heat insulation wall 4
From interior outward successively covered with high-strength light screed-coat 3, polymer waterproof layer 2 and exterior wall finish layer 1, described self heat insulation wall
4 inner side is from outside inside successively covered with inner thermal insulating layer 5, anti-cracking protective layer 6 and inner wall finishing layer 7.Described self heat insulation wall 4
For self-insulating concrete composite block wall, described inner thermal insulating layer 5 is spraying hard-foam polyurethane heat-insulation layer, and described cracking resistance is prevented
Sheath 6 is the cement base anticracking grout that surface is pressed into screen cloth, and described exterior wall finish layer 1 is external wall putty and coating, institute
The inner wall finishing layer 7 stated is architecture indoor putty and coating, and the thickness of described exterior wall finish layer 1 is 3mm, polymer waterproof layer
2 thickness are 3mm, the thickness of high-strength light screed-coat 3 is 15mm, the thickness of inner thermal insulating layer 5 is 15mm, the thickness of anti-cracking protective layer 6 is
8mm, the thickness of inner wall finishing layer 7 are 3mm.
Described polymer waterproof layer 2 is made up of the raw material of following parts by weight：20 parts of cement, acrylic latex powder 20
Part, 40 parts of fine sand, 18 parts of metakaolin, 0.5 part of defoamer, 0.3 part of polycarboxylate water-reducer, 1.5 parts of organosilicon moisture repellent.
Described high-strength light screed-coat 3 is made up of the raw material of following parts by weight：70 parts of cement, 5 parts of flyash, admant
3 parts of cream, 5 parts of lightweight aggregate, 13 parts of fine sand, 0.2 part of cellulose ether, 1 part of wood-fibred, 3 parts of vinyl acetate emulsion powder.
Described cement base anticracking grout is made up of the raw material of following parts by weight：35 parts of cement, 8 parts of flyash, light bone
3 parts of material, 50 parts of fine sand, 0.5 part of cellulose ether, 0.5 part of polypropylene fibre, 4 parts of vinyl acetate emulsion powder.
Referring to Fig. 1, embodiment 3
A kind of high performance water proof thermal insulation system, including：Exterior wall finish layer 1, polymer waterproof layer 2, high-strength light are looked for
Flat bed 3, self heat insulation wall 4, inner thermal insulating layer 5, anti-cracking protective layer 6 and inner wall finishing layer 7, the outside of described self heat insulation wall 4
From interior outward successively covered with high-strength light screed-coat 3, polymer waterproof layer 2 and exterior wall finish layer 1, described self heat insulation wall
4 inner side is from outside inside successively covered with inner thermal insulating layer 5, anti-cracking protective layer 6 and inner wall finishing layer 7.Described self heat insulation wall 4
For autoclave aerated concrete building block wall, described inner thermal insulating layer 5 is spraying hard-foam polyurethane heat-insulation layer, and described cracking resistance is protected
Layer 6 is the cement base anticracking grout that surface is pressed into screen cloth, and described exterior wall finish layer 1 is external wall putty and coating, described
Inner wall finishing layer 7 be architecture indoor putty and coating, the thickness of described exterior wall finish layer 1 is 7mm, polymer waterproof layer 2
Thickness is 5mm, the thickness of high-strength light screed-coat 3 is 25mm, the thickness of inner thermal insulating layer 5 is 30mm, the thickness of anti-cracking protective layer 6 is
15mm, the thickness of inner wall finishing layer 7 are 7mm.
Described polymer waterproof layer 2 is made up of the raw material of following parts by weight：15 parts of cement, acrylic latex powder 15
Part, 50 parts of fine sand, 20 parts of metakaolin, 0.2 part of defoamer, 0.1 part of polycarboxylate water-reducer, 0.5 part of organosilicon moisture repellent.
Described high-strength light screed-coat 3 is made up of the raw material of following parts by weight：60 parts of cement, 8 parts of flyash, admant
5 parts of cream, 7 parts of lightweight aggregate, 15 parts of fine sand, 0.1 part of cellulose ether, 0.2 part of wood-fibred, 5 parts of vinyl acetate emulsion powder.
Described cement base anticracking grout is made up of the raw material of following parts by weight：20 parts of cement, 9 parts of flyash, light bone
5 parts of material, 60 parts of fine sand, 0.2 part of cellulose ether, 0.2 part of polypropylene fibre, 6 parts of vinyl acetate emulsion powder.
The performance of polymer waterproof layer in 1 ~ embodiment of embodiment 3 is as shown in table 1, light in 1 ~ embodiment of embodiment 3
The performance of the high-strength screed-coat of matter is as shown in table 2, and the performance of the cement base anticracking grout in 1 ~ embodiment of embodiment 3 is as shown in table 3.
Table 1
| Project | Unit | Performance indications | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Impermeability pressure | MPa | ≥1.0 | 1.1 | 1.4 | 1.0 |
| Compression strength | MPa | ≥24 | 26.5 | 27.9 | 25.6 |
| Rupture strength | MPa | ≥8 | 10.2 | 11.4 | 9.7 |
| Pliability（Transversal deformability） | mm | ≥1.0 | 1.3 | 1.1 | 1.4 |
| Adhesion strength | MPa | ≥1.0 | 1.6 | 1.3 | 1.2 |
| Alkali resistance | — | Without cracking, peel off | Without cracking, peel off | Without cracking, peel off | Without cracking, peel off |
| Heat resistance | — | Without cracking, peel off | Without cracking, peel off | Without cracking, peel off | Without cracking, peel off |
| Frost resistance | — | Without cracking, peel off | Without cracking, peel off | Without cracking, peel off | Without cracking, peel off |
| Shrinkage factor | % | ≤0.15 | 0.11 | 0.13 | 0.09 |
Table 2
Table 3
The beneficial effect of the utility model high performance water proof thermal insulation system is：The utility model takes into account construction wall
Waterproof, heat insulation function, outside set polymer waterproof layer, lifting system water resistance, building energy conservation be with self-insurance temperature technique and
Based on inside holding technology, it is aided with high-strength light leveling mortar, combination reaches power conservation requirement.The outside of the utility model wall is set
There are high-strength light screed-coat and polymerization waterproof layer, there is more excellent matching with self heat insulation wall, there is high intensity, water-proofing anticracking
Deng technical characteristic, while also there is the cold bridge such as certain heat insulation function, beam column position to meet power conservation requirement, can cancel outside conventional exterior wall
Heat-insulation system, reduce external-wall heat-insulation material and the quality problems such as ftracture, come off, permeating.The utility model inner side of outer wall is using spraying
Hard-foam polyurethane heat-insulation layer, mechanized construction steady quality is strong with self heat insulation wall cohesive force, avoid self heat insulation wall hollowing,
The common quality defects such as cracking；Inside holding technology can significantly improve indoor thermal environment, improve residence comfort.
Embodiment of the present utility model is the foregoing is only, not thereby limits the scope of the claims of the present utility model, it is every
The equivalent structure or equivalent flow conversion made using the utility model description, or directly or indirectly it is used in other phases
The technical field of pass, similarly it is included in scope of patent protection of the present utility model.
Claims (7)
- A kind of 1. high performance water proof thermal insulation system, it is characterised in that including：Exterior wall finish layer, polymer waterproof layer, lightweight High-strength screed-coat, self heat insulation wall, inner thermal insulating layer, anti-cracking protective layer and inner wall finishing layer, the outside of described self heat insulation wall From interior outward successively covered with high-strength light screed-coat, polymer waterproof layer and exterior wall finish layer, described self heat insulation wall Inner side is from outside inside successively covered with inner thermal insulating layer, anti-cracking protective layer and inner wall finishing layer.
- 2. high performance water proof thermal insulation system according to claim 1, it is characterised in that described self heat insulation wall is Autoclave aerated concrete building block wall or self-insulating concrete composite block wall.
- 3. high performance water proof thermal insulation system according to claim 1, it is characterised in that described inner thermal insulating layer is spray Apply hard-foam polyurethane heat-insulation layer.
- 4. high performance water proof thermal insulation system according to claim 1, it is characterised in that described anti-cracking protective layer is Surface is pressed into the cement base anticracking grout of screen cloth.
- 5. high performance water proof thermal insulation system according to claim 1, it is characterised in that described exterior wall finish layer is External wall putty and coating.
- 6. high performance water proof thermal insulation system according to claim 1, it is characterised in that described inner wall finishing layer is Architecture indoor putty and coating.
- 7. high performance water proof thermal insulation system according to claim 1, it is characterised in that described exterior wall finish layer Thickness is 3 ~ 7mm, polymer waterproofing layer thickness is 3 ~ 5mm, high-strength light screed-coat thickness is 15 ~ 25mm, inner thermal insulating layer thickness Be 8 ~ 15mm for 15 ~ 30mm, anti-cracking protective layer thickness, inner wall finishing thickness degree be 3 ~ 7mm.