CN1974796A - 复合脱氧剂-铝镁钙铁合金及其制备方法 - Google Patents
复合脱氧剂-铝镁钙铁合金及其制备方法 Download PDFInfo
- Publication number
- CN1974796A CN1974796A CNA2006101348900A CN200610134890A CN1974796A CN 1974796 A CN1974796 A CN 1974796A CN A2006101348900 A CNA2006101348900 A CN A2006101348900A CN 200610134890 A CN200610134890 A CN 200610134890A CN 1974796 A CN1974796 A CN 1974796A
- Authority
- CN
- China
- Prior art keywords
- alloy
- steel
- calcium powder
- magnesium
- magnesium metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及用于炼钢用的脱氧剂技术领域,特别是一种新型复合脱氧剂—铝镁钙铁合金及其制备方法,其化学成份(重量%)为:Si 0~1%,Al 20~50%,Mg 1~6%,Ca 1~6%,余量为Fe和不可避免的杂质。制备方法包括下列步骤:a)称取下列配比(重量%)的原料:含铝95~98%的工业铝锭26~56%,含镁90~98%金属镁2~10%、含钙75~90%的钙粉2~10%及废钢40~50%,b)将上述金属镁和钙粉分别加工包装备用,c)首先取上述配比的废钢和总铝量2/3的铝锭放入炉底,然后加入金属包装的钙粉,进行加热熔融,待全部熔化后再加入剩余工业铝锭和金属镁,搅拌熔融后出炉即可。该复合脱氧剂结晶细致、坚硬、熔点低,比重大。用于此冶炼的低合金结构钢和碳素钢时,钢中[0]达25ppm以下;[S]达到0.02%以下,抗拉强度提高50~80MPa;断面伸长率提高5~10%。
Description
技术领域
本发明涉及用于炼钢用的脱氧剂技术领域,特别是一种新型复合脱氧剂—铝镁钙铁合金及其制备方法。
背景技术
金属铝作为炼钢用首选的脱氧材料,至今仍在使用,因为它对氧具有很强的亲和力,是其它金属所不能完全替代的。然而,铝的比重轻、熔点低、易烧损,用纯铝脱氧,收得率和有效利用率都很低,特别是在空气中和钢渣中氧接触以后,有近70~90%的铝被氧化,因而,钢中残余的铝既低又不稳定。
镁也是一种脱氧剂,而且是钢液脱硫的最佳原料。但镁的蒸汽压很高,极易气化和燃烧,所以直接用于炼钢的脱氧和脱硫是很困难的。
钙在钢中溶解度很小,但它与氧、硫的亲和力都很强。在钢的脱氧过程中,钙和铝有互补增益的共同作用,很像硅和锰的共同作用。氧化钙可以和氧化铝复合成易熔的铝酸钙,甚至在炼钢温度下可以是液相,钙使钢液脱氧的同时,还能与溶于钢中的夹杂物中的氧反应,降低钢中硫化物的溶解度,使其在钢液的凝固初期析出,呈球状,对钢的力学性能影响很小。
用钙脱氧虽有很多好处,但实施时却有不少困难。钙的沸点为1492℃,密度仅是钢的1/5,在炼钢温度下,不仅会漂浮在钢渣表面上,而且很快就会气化、挥发。所以,在炼钢条件下用钙脱氧,必须配合其他元素降低其活性,以避免过多的烧损。
发明内容
本发明的目的在于克服上述单一金属脱氧的不足,通过对现有各种铝镁铁、硅钙镁、硅钡钙铝等合金进行新的组合,提供一种以铝、镁、钙金属为主要原料配加废钢生产的新的复合脱氧剂—铝镁钙铁合金及其制备方法。
按照本发明的炼钢用复合脱氧剂—铝镁钙铁合金,其化学成份(重量%)为:Si 0~1%,Al 20~50%,Mg 1~6%,Ca 1~6%,余量为Fe和不可避免的杂质。
本发明炼钢用复合脱氧剂—铝镁钙铁合金的制备方法是:
a)称取下列配比(重量%)的原料:
含铝95~98%的工业铝锭26~56%,含镁90~98%金属镁2~10%、含钙75~90%的钙粉2~10%及废钢40~50%,
b)将上述金属镁和钙粉分别用金属加工包装备用,
c)采用中频炉或工频炉,首先取上述配比的废钢和总铝量2/3的铝锭放入炉底,然后加入经过加工包装的钙粉,进行加热熔融,待全部熔化后再加入剩余工业铝锭和经过加工包装的金属镁,经充分搅拌、熔融后出炉,即可制得所需化学成分的铝镁钙铁合金。合金中的硅来自废钢,硅不是脱氧剂的必要成分而是限制成分。各种原料的用量百分比均大于最终产品的各种成分的量百分比,这是因为各种原料均含有一定比例的杂质,以及在加热熔融过程中有一定量的烧损。
本发明提供的复合脱氧剂中的铝是一种较强的亲氧元素,而钙在脱氧元素中排在第一位,与硫的亲和力也很强,所以钙逼近可以提高脱氧效果,也能起到脱硫作用,从而可使钢中的夹杂物变性,对提高钢材的综合性能十分有利。另外,钙还使脱氧产物形成较低熔点的钙铝酸盐,在钢水中容易上浮除掉,避免钢水浇筑时水口堵塞,对连铸十分有利。镁也是强脱氧剂,形成合金态防止了镁在空气中和渣中的氧燃烧。由于钙的缓冲作用抑制了镁的溶解剂反应速度,从而消除了喷溅的危险,同时还能增强脱氧剂脱硫能力,并进一步改善夹杂物的形态。
本发明具有比重大(3.0~4.0g/cm3),熔点低(1000~1100℃),结晶细致、坚硬等优点,尤其是在冶炼低合金结构钢和碳素钢时使用该复合脱氧剂,能有效地提高钢材的综合性能。
具体实施方式
下面结合实施例进一步说明本发明的具体实施方式。
按照本发明的复合脱氧剂—铝镁钙铁合金,其化学成份(重量%)为:
Si 0~1%,Al 20~50%,Mg 1~6%,Ca 1~6%,余量为Fe和不可避免的杂质。
本发明炼钢用复合脱氧剂—铝镁钙铁合金的制备方法是:
a)称取下列配比(重量%)的原料:
含铝95~98%的工业铝锭26~56%,含镁90~98%金属镁2~10%、含钙75~90%的钙粉2~10%及废钢40~50%,
b)将上述金属镁和钙粉分别用金属加工包装备用,
c)采用中频炉或工频炉,首先取上述配比的废钢和总铝量2/3的铝锭放入炉底,然后加然后加入经过加工包装的钙粉,进行加热熔融,待全部熔化后再加入剩余工业铝锭和经过加工包装的金属镁,经充分搅拌、熔融后出炉,即可制得所需化学成分的铝镁钙铁合金。合金中的硅来自废钢。
实施例1:
所述的合金化学成份(重量%)为:Si<0.50%,Al 42~46%,Ca 2.0~4.0%,Mg 2.0~4.0%,其余为Fe。
其制备方法是:
a)称取下列配比(重量%)的原料:
含铝95~98%的工业铝锭43~47%,含镁90~98%金属包装的金属镁3~5%、含钙75~90%的金属包装的钙粉3~6%及废钢40~50%,
b)加入工频炉中熔融,首先将上述比例的废钢和工业铝锭2/3比例放入炉底,进行加热熔融,待全部熔化后加入金属包装的钙粉和剩余工业铝锭,经充分搅拌、熔融后加入金属包装的金属镁,出炉浇铸,冷却后进一步破碎至20~50mm,即制成化学成份(重量%)为:Si<0.50%,Al42~46%,Ca 2.0~4.0%,Mg 2.0~4.0%,其余为Fe的复合脱氧剂—铝镁钙铁合金。合金中的硅来自废钢。
该复合脱氧剂结晶细致、坚硬、熔点低(1000~1100℃),比重3.0~4.0g/cm3。用此复合脱氧剂冶炼的低合金结构钢和碳素钢,钢中的[O]可达到25ppm以下;[S]含量可以达到0.02%以下,晶粒度10级以上达85%以上,力学性能明显提高,抗拉强度比用其他脱氧剂提高50~80MPa;断面伸长率提高5~10%。
Claims (4)
1,一种炼钢用复合脱氧剂-铝镁钙铁合金,其特征在于其化学成份重量%为:Si 0~1%,Al 20~50%,Mg 1~6%,Ca 1~6%,余量为Fe和不可避免的杂质。
2、根据权利要求1所述的炼钢用复合脱氧剂-铝镁钙铁合金,其特征在于所述的合金化学成份重量%为:Si<0.50%,Al 42-46%,Ca 2-4%,Mg 2-4%,其余为铁。
3、一种用于权利要求1所述的炼钢用复合脱氧剂-铝镁钙铁合金的制备方法,其特征在于包括下列步骡:
a)称取下列配比重量%的原料:
含铝95~98%的工业铝锭26~56%,含镁90~98%金属镁2~10%、含钙75~90%的钙粉2~10%及废钢40~50%,
b)将上述金属镁和钙粉分别加工包装备用,
c)采用中频炉或工频炉,首先取上述配比的废钢和总铝量2/3的铝锭放入炉底,然后加入经过加工包装的钙粉,进行加热熔融,待全部熔化后再加入剩余工业铝锭和经过加工包装的金属镁,经充分搅拌、熔融后出炉,即可制得所需化学成分的铝镁钙铁合金。
4、根据权利要求3所述的炼钢用复合脱氧剂-铝镁钙铁合金,其特征在于包括下列步骡:
a)称取下列配比重量%的原料:
含铝95~98%的工业铝锭43~47%,含镁90~98%金属包装的金属镁3~4%、含钙75~90%的金属包装的钙粉3~4%及废钢40~50%,
b)加入工频炉中熔融,首先将上述比例的废钢和工业铝锭2/3比例放入炉底,进行加热熔融,待全部熔化后加入金属包装的钙粉和剩余工业铝锭,经充分搅拌、熔融后加入金属包装的金属镁,出炉浇铸,冷却后进一步破碎至40~60mm,即制成化学成份(重量%)为:Si<0.50%,Al42-46%,Ca 2.0-4.0%,Mg 2.0-4.0%,其余为铁的复合脱氧剂-铝镁钙铁合金。