CN1861715A - 一种环保型彩色热熔胶 - Google Patents
一种环保型彩色热熔胶 Download PDFInfo
- Publication number
- CN1861715A CN1861715A CN 200610087202 CN200610087202A CN1861715A CN 1861715 A CN1861715 A CN 1861715A CN 200610087202 CN200610087202 CN 200610087202 CN 200610087202 A CN200610087202 A CN 200610087202A CN 1861715 A CN1861715 A CN 1861715A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermosol
- environment protection
- protection type
- type colour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环保型彩色热熔胶,采用石蜡、EVA(乙烯-醋酸乙烯共聚物)、颜料、萜烯、松香、SLS(热塑性橡胶[苯乙烯-异戊=烯-苯乙烯])、抗氧剂、增亮剂制成;其配比为石蜡20~30份、EVA(乙烯-醋酸乙烯共聚物)20~30份、颜料3~5份、萜烯20~30份、松香20~30份、SLS 6~10份、抗氧剂0.5~2份、增亮剂0.5~2份。该胶把有机的各种颜料加入到指定配比的化工有机原料中,使之成为各种颜色的热熔胶,既不降低其原有的各种性能,又使得胶更加的光亮、鲜艳、美观、大方。本发明可广泛应用于工艺密封领域,尤其是彩色密封工艺领域。
Description
技术领域
本发明属于化工行业胶粘剂技术领域,特别涉及一种热熔胶。
背景技术
热熔胶本身是由各种原材料组成的一种胶粘剂。目前,在市场上销售的热熔胶品种很多,但颜色单一,通常呈黄色或无色。随着人类社会文明的快速发展,市场要求热熔胶与被粘接物色彩协调一致,既不减弱粘接强度,又要美观、耐久、光亮、鲜艳,工艺品行业尤为突出。
发明内容
本发明的目的是提供一种能满足市场需求的环保型彩色热熔胶。
本发明采用石蜡、EVA(乙烯-醋酸乙烯共聚物)、颜料、萜稀、松香、SLS(热塑性橡胶[苯乙烯-异戊=烯-苯乙烯])、抗氧剂、增亮剂制成;其配比为石蜡20~30份、EVA(乙烯-醋酸乙烯共聚物)20~30份、颜料3~5份、萜稀20~30份、松香20~30份、SLS 6~10份、抗氧剂0.5~2份、增亮剂0.5~2份。
本发明的工艺流程为:把配好的原料按先后顺序投入到已升温到180℃±2℃的反应釜中,加温搅拌2~3小时后加入颜料充分加热化合均匀,再通过过滤,进入挤出机挤出,经过冷却造型造粒、淋干、选料、袋装。
在本发明中,各种原料的作用简述如下:
1、石蜡起流动性好,光滑的作用;
2、EVA是胶粘剂必不可少的主料,增大和调整胶的粘接强度、粘度、硬度、韧力;
3、萜稀树脂和松香是增粘剂;
4、SLS增强胶的粘接强度,降低胶的冷脆性,增大韧性;
5、抗氧剂可减少胶的老化,增强各原料的活性;
6、颜料使热熔胶呈现各种各样的彩色;
7、增亮剂加大彩胶的亮度,光滑美观。
本发明把有机的各种颜料加入到指定配比的化工有机原料中,使之成为各种颜色的热熔胶,既不降低其原有的各种性能,又使得胶更加的光亮、鲜艳、美观、大方。本发明可广泛应用于工艺密封领域,尤其是彩色密封工艺领域。
具体实施方式
本发明的酒红色彩胶实施例采用石蜡、EVA(乙烯-醋酸乙烯共聚物)、酒红色颜料、萜稀、松香、SLS(热塑性橡胶)、抗氧剂(防老剂264)、增亮剂制成;其配比为石蜡20份、EVA21份、酒红色颜料4份、萜稀22份、松香23份、SLS 8份、抗氧剂1份、增亮剂1份。
本发明的酒红色彩胶实施例工艺流程为:把配好的原料按先后顺序投入到已升温到180℃±2℃的反应釜中,加温搅拌2小时后加入颜料充分加热化合均匀,再通过过滤,进入挤出机挤出,经过冷却造型造粒、淋干、选料、袋装。
本发明的酒红色彩胶实施例技术参数:
检验项目 | 技术要求 | 检验结果 |
180°剥离强度 | ≥10N/25mm | 37N/25mm |
·环境条件:22℃--23℃
·相对湿度:50%--55%
·180°剥离强度按JC/T438-1991(96)检验
Claims (3)
1.一种环保型彩色热熔胶,其特征在于:采用石蜡、EVA(乙烯-醋酸乙烯共聚物)、颜料、萜稀、松香、SLS(热塑性橡胶[苯乙烯-异戊=烯-苯乙烯])制成;其配比为石蜡20~30份、EVA(乙烯-醋酸乙烯共聚物)20~30份、颜料3~5份、萜稀20~30份、松香20~30份、SLS 6~10份。
2.根据权利要求1所述的一种环保型彩色热熔胶,其特征在于:还添加抗氧剂、增亮剂制成;其配比为抗氧剂0.5~2份、增亮剂0.5~2份。
3.根据权利要求1或2所述的一种环保型彩色热熔胶,其特征在于:把配好的原料按先后顺序投入到已升温到180℃±2℃的反应釜中,加温搅拌2~3小时后加入颜料充分加热化合均匀,再通过过滤,进入挤出机挤出,经过冷却造型造粒、淋干、选料、袋装。