CN1804167A - Fine denier modal fiber mixed color spinning yarn and production method thereof - Google Patents
Fine denier modal fiber mixed color spinning yarn and production method thereof Download PDFInfo
- Publication number
- CN1804167A CN1804167A CNA2005101117704A CN200510111770A CN1804167A CN 1804167 A CN1804167 A CN 1804167A CN A2005101117704 A CNA2005101117704 A CN A2005101117704A CN 200510111770 A CN200510111770 A CN 200510111770A CN 1804167 A CN1804167 A CN 1804167A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fine
- denier modal
- fiber
- blended
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a blended color spun yarn of fine denier modal fiber pure spinning or blended spinning with other fibers and a production method thereof. The fine denier modal fiber blended yarn is characterized in that the yarn is formed by blended spinning of two or more fibers with different colors, and the content of the fine denier modal fiber in the blended yarn is 40-100%. Compared with the prior art, the invention does not need special equipment for production, the fine denier modal yarn produced by the invention has bright color, various colors, soft hand feeling, full luster, good heat retention, high strength elongation and small cylinder difference, solves the problems of flooding, fading, staining, color aging and the like, most importantly solves the problem of strength reduction of the fine denier modal yarn after dyeing and finishing, and provides bright and colorful fabrics and clothes for the market.
Description
Technical field
The present invention relates to that a kind of fine denier modal pure fibers is spun or with the blended color spinning yarn and the production method thereof of other fiber blend, belong to the spinning engineering technical field in the caused by spinning industrial production.
Background technology
Fine denier modal fiber and common model all are the tModified Cellulose Fibers of a kind of high wet modulus of producing of Austrian Lenzin company, and its fibre fineness is 0.9D, and length is 38mm.This products material all is natural material, and is harmless, and can natural decomposition, and environmental sound belongs to the green ecological Recycled Fibers.The fine denier modal fiber is more very thin and soft than common Modal fibre, so have the better uniformity, high gloss, more a softer and smoother touch characteristic, good hand feeling and drapability; Its silk quality sense is stronger, wears more comfortable.The fine denier modal fiber yarn can be woven into high-grade linings such as emulation silk, peach face, suede nap, polar fleece, is the first-selection of weaving more high-grade knitting, woven fabric, and the product application prospect is boundless.Its product suit producing high-grade underwear, Ms's overcoat, high-grade leisure clothes, sportswear and household textiles can satisfy the pursuit of environmental protectionization, comfortableization, leisureization, and bright development prospect is arranged.But because the fine denier modal fibre number is very thin, has only 0.9 DENIER, the brute force of fiber itself is very little, utilize traditional dyeing and finishing processing method that fiber is sustained damage, very thin during dyeing because of fiber number, thereby not high for common dyestuff tinctorial yield, and dyefastness is not fine, therefore, the yarn color structure of producing with conventional method is single, can not adapt to the needs of consumer personalityization.
Summary of the invention
One of purpose of the present invention provide that a kind of fine denier modal pure fibers is spun or with the blended color spinning yarn of other fiber blend.
Another object of the present invention provides the production method of above-mentioned this blended color spinning yarn.
Fine-denier Modal fiber blended color yarn of the present invention, it is that fiber by two or more different colours forms by blended colour yarn, the fine denier modal fiber content is 40%~100% in the blended yarn.
Described fine denier modal fiber blended color spinning, spinning count is single thread or the strand of 20Ne~80Ne, and single twist is 500~1500T/m, and strand twist is 270~1500T/m.
Described fine denier modal fiber blended color spinning, other fiber can be various chemical fibres or cotton fiber etc.For the fabric that this yarn is knitted make has good wearability, prevent from dress, use, washing process, to occur phenomenons such as stretcher strain, can in blended color spinning yarn, add spandex filament, make spandex core-spun yarn or wrap yarn.
The present invention makes traditional spinning process that spins after stain earlier into technology that elder generation dyes and afterwards spins.Described fine-denier Modal fiber blended color yarn, its production method are the processing of earlier fine denier modal fiber and other fiber being dyeed, and then carry out look and spin production.
Described fine denier modal stock-dye treatment step comprises the boiling-off of fine denier modal fiber or bleaching, dyeing, three steps of post processing.
1, to the pre-treatment of fine denier modal fiber, i.e. boiling-off:
Bath raio is in 5~20 the water at normal temperatures, adds chelated dispersants (2~3 grams per liter), and biology enzyme scouring agent 1% directly is warming up to 55~60 ℃ then, is incubated 30~60 fens kinds; Bleed off whole pin water, washing again cools to the temperature that dyeing needs, as adopts traditional boiling-off fiber strength to reduce greatly.
Or the fine denier modal bulk fibre bleached pre-treatment:
Bath raio is in 5~20 the water at normal temperatures, adds chelated dispersants (2~3 grams per liter), uses NaCO
3Regulate PH=8.5~9.5; Add hydrogen peroxide (6~10g/l) then; hydrogen peroxide stabilizer 197 (3g/L) is warming up to 60~70 ℃ with the speed of 1~2 ℃ of per minute, is incubated 30~60 fens kinds; the raffinate of draining; washed 8~12 minutes, and adding deoxidation enzyme (2~4g/L), in 8~12 fens kinds of 35~45 ℃ of insulations; washing again; cool to the temperature that dyeing needs at last, the selection of SC alkaline agent can be selected special efficacy hydrogen peroxide stabilizer 197 for use in the bleaching process, can play the effect of protection fiber.
2, to the fine denier modal loose stock dyeing: according to different color and luster requirements, the dye ligand ratio, in dye vat, add chelated dispersants, glauber salt, sodium bicarbonate, soda ash, dyeing is 40~60 minutes when putting into fine denier modal bulk fibre through pre-treatment (boiling-off or bleaching) at 60~70 ℃ again.Because the fine denier modal fibre number is very thin, has only 0.9 DENIER, the brute force of fiber itself is very little, utilize traditional dyeing and finishing processing method that fiber is sustained damage, therefore each the road link in dyeing and finishing processing all is noted that because fiber number is very thin, thereby it is not high for common dyestuff tinctorial yield, and dyefastness is not fine, can be with low salt dyestuff, and as the LS type of vapour crust etc.
3, to the post processing of fine denier modal bulk fibre: under 45 ℃~60 ℃, carry out neutralisation treatment earlier, adding concentration is 98% glacial acetic acid (0.4~0.8 grams per liter), then under 70 ℃~80 ℃, soaped 10~20 minutes, add soaping agent RS (2 grams per liter), washed 5~10 minutes 45 ℃~60 ℃ heat, look shade and do 1~2 time, under 45 ℃~60 ℃, carried out the fixation soft treatment 10~20 minutes at last, add hydrophilic softener (2~5 grams per liter) on color-fixing agent (2~3 grams per liter) back.Fine denier modal stock-dye fastness is bad, and the general traditional color-fixing agent such as the color-fixing agent fastness of dicyanamide class can't guarantee and have certain look and become, and therefore need select color-fixing agent such as vapour Ba Gu ECO etc. preferably for use; Its alkali resistance and heat resistance are not fine yet, thereby consumption is no more than 10g/l as far as possible during with the soda ash fixation, can add sodium bicarbonate elder generation fixation, and temperature should not surpass 80 degree.
Because the fine denier modal fibre number is very thin, has only 0.9 DENIER, in the carding machine process, shift difficulty, easily twine cylinder, licker-in and doffer cause cotton knot increase in the carded sliver, and fiber directionality in web is poor; Fine denier modal fiber rigidity is little, fineness carefully, easily twist together and damage, therefore reduce cotton junction grain number, improve the extended parallelization of fiber in web, be the key during carding step is produced.Adopt novel thin dawn chemical fibre card clothing model, the short angle of the rare base of its card clothing tooth is big, helps abundant transfer; Adopting tightly spaces helps the raising of fiber separation extended parallelization, reduces the mutual afterturn kink of fiber, makes fiber that directionality preferably be arranged in web.Suitably lengthening feed plate face length can reduce fibre damage; Adopt between cylinder and doffer and tightly space, help the doffer fiber on the cylinder is well on commentaries on classics enough.
Novel thin dawn chemical fibre card clothing model configuration is as follows:
The card clothing model | Height overall | Operating angle | Vertical tooth pitch | Base is thick | Tooth is close | |
Bearded-needle knitted cloth | AC2520×01660 | 2.5mm | 70° | 1.6mm | 0.6mm | 713 tooth/square inches |
Taker-in clothing | AT5605×05011 | 5.6mm | 85° | 5mm | 1.09mm | 41 tooth/square inches |
Doff clothing | AD4532×02075 | 4.5mm | 58° | 2mm | 0.75mm | 430 tooth/square inches |
Flat-clothing | MCZ30 | - | - | - | - | 300 tooth/square inches |
Characteristics according to the super fine denier Modal fibre, number of fiber is many in the yarn unit cross section, fiber drafting force in drawing-off is bigger, for guaranteeing that enough grasping forces and drafting force adapt, suitably increase pressure, make fiber stable motion in drafting process, it is flat to improve ripe rule solid carbon dioxide, suitably reduce roller speed, to reduce fiber because of the high-speed friction formation cotton knot of twisting together mutually; At the characteristics of drafting force, add major part and with two and back zone drafting multiple, to improve the straightening of fibers depth of parallelism.To reduce slubbing and to improve bar and do; Reduce end and back area draft simultaneously, to improve bar evenness.
For the bar that further improves yarn is done, powerful level, reduce filoplume, when spinning, can adopt the match network to spin or closely spin and process.
Described fine denier modal pure fibers is spun or the blended color spinning yarn of blending, and the concrete steps of its spinning are followed successively by:
1, fine denier modal is pure spins or the blended color spinning yarn kind of fine denier modal and other chemical fibre blending: raw material (different performance, different colours) is mixed, blowing, comb and parallel cotton fibers prior to spinning, three road draftings (toning complementary color), rove, spun yarn, winder, twist thread, winder.
2, the blended color spinning yarn kind of fine denier modal fiber and cotton blending:
Fine denier modal raw material (different colours) is mixed, blowing, comb and parallel cotton fibers prior to spinning, pre-drawing, cotton fiber material (different colours) is mixed, blowing, comb and parallel cotton fibers prior to spinning, pre-bar, silver lap, combing, then three road draftings (toning complementary color), rove, spun yarn, winder, twist thread, winder.
As adopted comber web and distributed cotton, then the cotton fiber part can be without silver lap and combing process.
Beneficial effect of the present invention: the invention provides that a kind of fine denier modal pure fibers is spun or with the blended color spinning yarn and the production method thereof of other fiber blend.At different cultivars and color, with various fiber reasonable cottons, technological method for processing according to the look spinning spins, the fine denier modal fiber fiber dyed yarn that processes can adapt to knitting or woven processing, the product ecological, environmental protective, sericeous soft gloss and touch sense, frivolous elegant, ventilative moisture absorption, the meticulousst knit product of comfortable and easy to wear, suitable production, and color scheme is innumerable, farthest having satisfied personalized demand, is a kind of environmental protection and healthy textiles that market prospects are arranged very much.
Description of drawings
Fig. 1: the present invention is to fine denier modal bulk fibre pre-treatment boiling-off process curve figure
Fig. 2: the present invention is to fine denier modal bulk fibre pre-treatment bleaching process curve map
Fig. 3: the present invention is to fine denier modal loose stock dyeing process curve figure
Fig. 4: the present invention is to fine denier modal bulk fibre aftertreatment technology curve map
Label declaration:
1, expression normal temperature
2, expression adds chelated dispersants
3, expression adds the biology enzyme scouring agent
4, expression washing
5, expression adds hydrogen peroxide stabilizer 197
6, expression adds hydrogen peroxide
7, expression slowly adds Na
2CO
3Transfer to PH and be about 8.5~9.5
8, expression adds the deoxidation enzyme
9, expression adds dyestuff
10, expression adds 1/5 glauber salt
11, expression adds 2/5 glauber salt
12, expression adds 1/7 soda ash
13, expression adds remaining 2/5 glauber salt
14, expression adds 2/7 soda ash
15, expression adds remaining 4/7 soda ash
16, expression adds glacial acetic acid
17, expression adds softener, color-fixing agent
18, expression oven dry
19, soaping agent
20, fiber protective agent
21, add sodium bicarbonate
The specific embodiment
Specify the present invention by the following examples, but embodiment only is used for explanation, does not limit the scope of the invention.
The A Processing Example 1 that dyes
Select 160 kilograms of fine denier modal bulk fibres for use, putting into bath raio at normal temperatures is 1: 8, and contains in the solution of 1% chelated dispersants, and 1% biology enzyme scouring agent is warmed up to 55 ℃ of insulations 30 minutes, bleeds off pin water, and the water overflow is clean.
Adopt REACTIVE DYES; according to different color and luster requirements; the dye ligand ratio; poured dyestuff and 1/5 glauber salt into the dye vat material together 20 minutes; the fiber protective agent of normal temperature running adding 1% after 10 minutes and 2/5 glauber salt; continue running and add remaining 2/5 glauber salt after 10 minutes; be warmed up to the required temperature of dyeing with 1 ℃/minute then; select the suitable alkali rate curve that adds to add sodium bicarbonate and soda ash according to different dye characteristics, sodium bicarbonate adds operation 5 minutes earlier, as shown in Figure 3; adding alkali speed wants slow earlier back fast; be 40 minutes add-subtract time, holds warm 15 minutes with regard to discharge opeing, and post processing is included under 50 ℃; in and 10 minutes; add 0.8 grams per liter glacial acetic acid (concentration is 98%), then under 75 ℃, soaped 20 minutes, add the soaping agent of 2 grams per liters; under 60 ℃; heat was washed 5 minutes, looked shade and did 2 times, at last under 50 ℃; fixation soft treatment 20 minutes adds behind the color-fixing agent of 3 grams per liters and 4 grams per liter softeners.
B spinning processing and implementation example 2~3
The concrete steps of spinning are as follows:
1, to after fine denier modal fiber and other various chemical fibres or the pre-shredding of cotton fiber, the processing of dyeing comprises boiling-off or bleaching, dyeing, post-treating and other steps.
2, according to the product colour requirement, match the ratio of different colours fiber, take by weighing various fibers in proportion.
3, to be carried out in accordance with regulations shop layer mixed for the fiber of the variety classes that will take by weighing, different colours, and 1~3 layer of each color shop if lot volume in material input is bigger, then is divided into and somely mixes in small batches.
4, after raw material mixes well, carry out further mixed and quantitative rolling at cotton cleaning process.It quantitatively is 300~550 gram/rice that lap is done; Lap length is 33~45 meters.
5, go up lap combing slivering at carding machine (FA201B).It quantitatively is/5 meters of 12~22 grams that the carded sliver is done; 45~65 meters/minute of sliver exporting speeds.
6, carry out three roads and close drawing-off on drawing frame (FA311F), make ribbon quantitatively consistent, bar is done evenly, and fiber is parallel straight.Doing quantitatively is/5 meters of 14~25 grams; Number of doubling is 6~8; 6~8 times of drawing-offs; Roller gauge 10/5/15mm; The speed of a motor vehicle 150~300m/min.
7, go up drawing-off at Speed frames (FA421A) and become rove, add certain twist simultaneously, so that rove has certain cohesive force.Rove is done/10 meters of quantitative 2~6.5 grams; 5~12 times of drawing-offs; Roller gauge 9/23/29mm; Twist factor 60~80; 600~1000 rev/mins of ingot speed.
8, on fine spining machine (FA507A), be spun into spun yarn.Spun yarn is done/100 meters of quantitative 0.72~2.72 grams; 15~45 times of drawing-offs; The twist 500~1500T/m; 9000~15000 rev/mins of ingot speed; Roller gauge 18/25mm; Can adopt simultaneously the match network to spin or closely spin and process,, powerful level dried with the bar that improves yarn reduce filoplume.
9, go up the tapered tube of network yarn at automatic winder (Auto Coner-338).800~1800 meters/minute of winding speeds.
10, on twisting machine (FA721), carry out doubling twisting.The twist 270~1500T/m; 7000~12000 rev/mins of ingot speed.
11, go up the tapered tube of network yarn at automatic winder (Auto Coner-33g) again.800~1800 meters/minute of winding speeds.
Table one
| Embodiment | 2 | Embodiment 3 |
Spinning system | The match network spins | Closely spin | |
Material rate | Fine denier modal 100% | Fine denier modal 50%/cotton 50% | |
Spinning count | 40 S/2 | 30 S | |
Roving twist factor | 70 | 80 | |
Single twist | 910T/m | 760T/m | |
Strand twist | 490T/m | - |
The technological design of embodiment kind sees Table two.
Table two
Flow process | Technological parameter | Span | Embodiment 2 (the match network spins) | Embodiment 3 (closely spinning) |
Blowing | Lap is done quantitatively (gram/rice) | 300~550 | 360 | 380 |
Lap length (rice) | 33~45 | 35.2 | 35.2 | |
Comb and parallel cotton fibers prior to spinning | The carded sliver is done quantitatively (restraining/5 meters) | 12~22 | 15.0 | 16.7 |
Doffer speed (rice/minute) | 45~65 | 50 | 50 | |
Drafting (three roads also close) | Do quantitatively (restraining/5 meters) | 14~25 | 15.9/12.4/12.4 | 17.2/16.3/16.3 |
Number of doubling (root) | 6~8 | 6/6/8 | 6/78 | |
Drafting multiple | 6~8 | 5.7/7.7/8.0 | 5.8/7.4/8.0 | |
The speed of a motor vehicle (m/min) | 150~300 | 200/180/180 | 200/180/180 | |
Rove | Do quantitatively (restraining/10 meters) | 2.0~6.5 | 2.74 | 4.70 |
Drafting multiple | 5~12 | 9.03 | 6.92 | |
Twist factor | 60~80 | 70 | 80 | |
Ingot speed (rev/min) | 600~1000 | 750 | 850 | |
Spun yarn | Do quantitatively (restraining/100 meters) | 0.72~2.72 | 1.31 | 1.78 |
Drafting multiple | 15~45 | 41.9 | 26.4 | |
The twist (T/m) | 500~1500 | 910 | 760 | |
Ingot speed (rev/min) | 9000~15000 | 12100 | 14000 | |
Winder | Winding speed (rice/minute) | 800~1800 | 1200 | 1500 |
Twist thread | The twist (T/m) | 270~1500 | 490 | - |
Ingot speed (rev/min) | 7000~12000 | 8000 | - | |
Winder | Winding speed (rice/minute) | 800~1800 | 1200 | - |
Fine denier modal yarn through the present invention's production, bright-colored, color is various, soft, gloss is plentiful, warmth retention property good, strength and elongation is high, the cylinder difference is little and solved loose colour, faded, problems such as staining, look old degree, most critical be to have solved fine denier modal through the powerful situation that descends in dyeing and finishing processing back, carry the lake for market and supplied gorgeous colorful clothes and lining.Be fit to produce meticulous knit product, make as luxurious Lingerie and nightwear, and color scheme be innumerable, has farthest satisfied personalized demand, is a kind of fabric product that market prospects are arranged very much.
Claims (10)
1, a kind of fine-denier Modal fiber blended color yarn is characterized in that, is that the fiber by two or more different colours forms by blended colour yarn, and fine denier modal fiber quality content is 40~100% in the blended yarn.
2, fine-denier Modal fiber blended color yarn as claimed in claim 1 is characterized in that, spinning count is single thread or the strand of 20Ne~80Ne, and single twist is 500~1500T/m, and strand twist is 270~1500T/m.
3, fine-denier Modal fiber blended color yarn as claimed in claim 1 is characterized in that, also has various chemical fibres or cotton fiber in the blended yarn.
4, fine-denier Modal fiber blended color yarn as claimed in claim 3 is characterized in that, contains spandex filament in the blended yarn, makes spandex core-spun yarn or wrap yarn.
5, as the preparation method of the described arbitrary fine-denier Modal fiber blended color yarn of claim 1~4, it is characterized in that: the processing of earlier fine denier modal fiber and other fiber being dyeed, and then carry out the processing that look spins production.
6, the preparation method of fine-denier Modal fiber blended color yarn as claimed in claim 5 is characterized in that: described dyeing processing is meant carries out boiling-off or bleaching earlier to fine denier modal fiber and other fiber, dyes, carries out at last post processing again.
7, the preparation method of fine-denier Modal fiber blended color yarn as claimed in claim 6, it is characterized in that: described boiling-off be meant with fiber at normal temperatures bath raio be to add chelated dispersants and biology enzyme scouring agent in 5~20 the water, be warming up to 30~60 fens kinds of 55~60 ℃ of insulations then, bleed off whole pin water, washing again cools to the temperature that dyeing needs; Described bleaching is meant that bath raio at normal temperatures is to add chelated dispersants in 5~20 the water, and adjusting PH=8.5~9.5, add hydrogen peroxide, hydrogen peroxide stabilizer 197 then, be warming up to 30~60 fens kinds of 60~70 ℃ of insulations, the raffinate of draining, washing, add the deoxidation enzyme, in 8~12 fens kinds of 35~45 ℃ of insulations, washing again cools to the temperature that dyeing needs at last.
8, the preparation method of fine-denier Modal fiber blended color yarn as claimed in claim 6, it is characterized in that: described dyeing is meant according to different color and luster requirements, the dye ligand ratio, add chelated dispersants, glauber salt, sodium bicarbonate, soda ash are put into boiling-off again or the fine denier modal bulk fibre bleached dyeed 40~60 minutes in the time of 60~70 ℃.
9, the preparation method of fine-denier Modal fiber blended color yarn as claimed in claim 6, it is characterized in that: described post processing is meant carries out neutralisation treatment at 45 ℃~60 ℃ following adding glacial acetic acid earlier, then adding soaping agent down at 70 ℃~80 ℃ soaps, wash 45 ℃~60 ℃ heat again, add color-fixing agent and hydrophilic softener down at 45 ℃~60 ℃ at last and carry out the fixation soft treatment.
10, the preparation method of fine-denier Modal fiber blended color yarn as claimed in claim 5 is characterized in that: described look spins production and processing and in turn includes the following steps:
Fine denier modal or, blowing, comb and parallel cotton fibers prior to spinning, three road draftings (toning complementary color), rove, spun yarn, winder mixed with the blended color spinning yarn raw material (different performance, different colours) of other chemical fibre blending, twist thread, winder; The blended color spinning yarn of fine denier modal fiber and the cotton blending steps in sequence of then spinning is in this way: fine denier modal fibrous raw material (different colours) is mixed, blowing, comb and parallel cotton fibers prior to spinning, pre-bar; Cotton fiber material (different colours) is mixed, blowing, comb and parallel cotton fibers prior to spinning, pre-bar, silver lap, combing; Then three road draftings (toning complementary color), rove, spun yarn, winder, twist thread, winder.