CN1803351A - 一种无机物载纳米银溶胶的制备方法 - Google Patents

一种无机物载纳米银溶胶的制备方法 Download PDF

Info

Publication number
CN1803351A
CN1803351A CN 200510062319 CN200510062319A CN1803351A CN 1803351 A CN1803351 A CN 1803351A CN 200510062319 CN200510062319 CN 200510062319 CN 200510062319 A CN200510062319 A CN 200510062319A CN 1803351 A CN1803351 A CN 1803351A
Authority
CN
China
Prior art keywords
inorganic
preparation
nanometer silver
nano
carried nanometer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510062319
Other languages
English (en)
Other versions
CN100384572C (zh
Inventor
黄德欢
韩东生
赵斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Huashi Nano Material Co., Ltd.
Original Assignee
黄德欢
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 黄德欢 filed Critical 黄德欢
Priority to CNB2005100623198A priority Critical patent/CN100384572C/zh
Publication of CN1803351A publication Critical patent/CN1803351A/zh
Application granted granted Critical
Publication of CN100384572C publication Critical patent/CN100384572C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种无机物载纳米银溶胶的制备方法，步骤如下：1)用去离子水配制还原剂水溶液，于0～8℃下冷冻；2)用去离子水配制无机物粉体水溶液，加入分散剂，制得无机物水分散体；3)将硝酸银与保护剂加入无机物水分散体中，搅拌，再加入还原剂水溶液，超声振荡处理，得到无机物载纳米银溶胶。本发明制备方法简单，由于无机物水分散体能负载纳米银粒子，对高浓度纳米银胶体具有分散和稳定作用，因此采用本发明方法可以获得高浓度分散均匀的纳米银胶体，银含量最高可达3％。

Description

一种无机物载纳米银溶胶的制备方法
技术领域
本发明涉及一种纳米银溶胶的制备方法，尤其是涉及一种无机物载纳米银溶胶的制备方法。
背景技术
纳米银溶胶具有良好的抗菌性能，在蛋白质表面增强拉曼效应中的应用也很广泛。然而高浓度的纳米银溶胶性能很不稳定，因此纳米银溶胶在实际应用、运输中很不方便。
发明内容
本发明的目的是提供一种性能稳定、高浓度的无机物载纳米银溶胶的制备方法。
本发明的无机物载纳米银溶胶的制备方法，包括以下步骤：
(1)用去离子水配制重量浓度为0.1～10％的还原剂水溶液，于0～8℃下冷冻0.5小时以上；
(2)将纳米级无机物粉体用去离子水配制重量浓度为1～30％的无机物粉体水溶液，加入分散剂，分散剂用量为无机物粉体水溶液重量的0.05～1％，搅拌至少0.5小时、超滤，制得无机物水分散体；
(3)按照重量比1∶1～10称取硝酸银与保护剂，依次加入步骤(2)的无机物水分散体中，搅拌，使其溶解在无机物水分散体中，硝酸银与无机物水分散体的重量比为1∶15～2000；
(4)将步骤(1)的还原剂水溶液按体积比1～10％加入到步骤(3)的混合液中，超声振荡0.5小时以上，得到无机物载纳米银溶胶。
本发明中，所说的还原剂可以是单宁、硼氢化钠、硼氢化钾、抗坏血酸、葡萄糖、柠檬酸钠中的一种或多种。
所说的纳米无机物可以是纳米二氧化钛、纳米二氧化硅、纳米碳酸钙或它们的混合物。
所说的保护剂可以为聚乙烯醇、AEO-7、聚乙烯吡硌烷酮中的一种或几种。
所说的分散剂可以为十二烷基磺酸钠、十二烷基硫酸钠、六偏磷酸钠中的一种或几种。
本发明制备过程中，制得无机物水分散体是淡蓝色或无色透明液体，分散体的稳定性与pH值无关。
本发明制备方法简单，由于无机物水分散体能负载纳米银粒子，对高浓度纳米银胶体具有分散和稳定作用，因此采用本发明方法可以获得高浓度分散均匀的纳米银胶体，银含量最高可达3％。
附图说明
图1是本发明实施例1中纳米二氧化硅水分散体载纳米银溶胶的粒度分布，银含量为0.2％，银平均粒度为10.7nm；
图2是本发明实施例2中纳米二氧化钛水分散体载纳米银溶胶的粒度分布，银含量为3％，银平均粒度为29nm。
具体实施方式
实施例1
(1)将硼氢化钠溶于去离子水，配制重量浓度为0.1％的硼氢化钠水溶液，于0℃下冷冻2小时；
(2)称取纳米二氧化硅粉体，用去离子水配制重量浓度为1％的二氧化硅粉体水溶液，再加入0.1％二氧化硅粉体水溶液重量的六偏磷酸钠，搅拌1h后超滤，制得淡蓝色透明状的二氧化硅水分散体；
(3)按照重量比1∶2称取硝酸银与聚乙烯醇，依次加入二氧化硅水分散体中，搅拌，使其溶解在二氧化硅水分散体中，硝酸银与二氧化硅水分散体重量比为1∶500；
(4)将硼氢化钠水溶液按体积比1％加入到步骤(3)的混合液中，再超声振荡2小时，得到暗黄色的二氧化硅载纳米银溶胶；
纳米二氧化硅水分散体载纳米银溶胶的粒度分布见图1，银含量为0.2％，银平均粒度为10.7nm。
实施例2
(1)将抗坏血酸溶于去离子水，配制重量浓度为0.1％的抗坏血酸水溶液，于8℃下冷冻4小时；
(2)称取纳米二氧化钛粉体，用去离子水配制重量浓度为30％的二氧化钛粉体水溶液，再加入0.1％二氧化钛粉体水溶液重量的十二烷基磺酸钠，搅拌2h后超滤，制得无色透明状的二氧化钛水分散体；
(3)按照重量比1∶1称取硝酸银与聚乙烯吡硌烷酮，依次加入纳米二氧化钛水分散体中，搅拌，使其溶解在二氧化钛水分散体中，硝酸银与二氧化钛水分散体重量比为1∶15；
(4)将抗坏血酸水溶液按体积比10％加入到步骤(3)的混合液中，再超声振荡1小时，得到黑色的二氧化钛载纳米银溶胶；
纳米二氧化钛水分散体载纳米银溶胶的粒度分布见图2，银含量为3％，银平均粒度为29nm。
实施例3
(1)将硼氢化钾溶于去离子水，配制重量浓度为0.1％的硼氢化钾水溶液，于2℃下冷冻2小时；
(2)称取纳米碳酸钙粉体，用去离子水配制重量浓度为10％的碳酸钙粉体水溶液，再加入0.5％碳酸钙粉体水溶液重量的十二烷基硫酸钠，搅拌0.5h后超滤，制得淡蓝色透明状的纳米碳酸钙水分散体；
(3)按照重量比1∶5称取硝酸银与AEO-7，依次加入碳酸钙水分散体中，搅拌，使其溶解在碳酸钙水分散体中，硝酸银与碳酸钙水分散体重量比为1∶100；
(4)将硼氢化钾水溶液按体积比2.5％加入到步骤(3)的混合液中，再超声振荡0.5小时，得到深黄棕色的碳酸钙载纳米银溶胶。

Claims (5)

1、一种无机物载纳米银溶胶的制备方法，其特征在于步骤如下：
(1)用去离子水配制重量浓度为0.1～10％的还原剂水溶液，于0～8℃下冷冻0.5小时以上；
(2)将纳米级无机物粉体用去离子水配制重量浓度为1～30％的无机物粉体水溶液，加入分散剂，分散剂用量为无机物粉体水溶液重量的0.05～1％，搅拌至少0.5小时、超滤，制得无机物水分散体；
(3)按照重量比1∶1～10称取硝酸银与保护剂，依次加入步骤(2)的无机物水分散体中，搅拌，使其溶解在无机物水分散体中，硝酸银与无机物水分散体的重量比为1∶15～2000；
(4)将步骤(1)的还原剂水溶液按体积比1～10％加入到步骤(3)的混合液中，超声振荡0.5小时以上，得到无机物载纳米银溶胶。
2、根据权利要求1所述的无机物载纳米银溶胶的制备方法，其特征在于所说的还原剂是单宁、硼氢化钠、硼氢化钾、抗坏血酸、葡萄糖、柠檬酸钠中的一种或多种。
3、根据权利要求1所述的无机物载纳米银溶胶的制备方法，其特征在于所说的纳米无机物为纳米二氧化钛、纳米二氧化硅、纳米碳酸钙中的一种或它们的混合物。
4、根据权利要求1所述的无机物载纳米银溶胶的制备方法，其特征在于所说的保护剂是聚乙烯醇、AEO-7、聚乙烯吡硌烷酮中的一种或几种。
5、根据权利要求1所述的无机物载纳米银溶胶的制备方法，其特征在于所说的分散剂为十二烷基磺酸钠、十二烷基硫酸钠、六偏磷酸钠中的一种或几种。
CNB2005100623198A 2005-12-29 2005-12-29 一种无机物载纳米银溶胶的制备方法 Expired - Fee Related CN100384572C (zh)