CN1793027A - Process for preparing porous titanium dioxide ceramic - Google Patents
Process for preparing porous titanium dioxide ceramic Download PDFInfo
- Publication number
- CN1793027A CN1793027A CN 200510119837 CN200510119837A CN1793027A CN 1793027 A CN1793027 A CN 1793027A CN 200510119837 CN200510119837 CN 200510119837 CN 200510119837 A CN200510119837 A CN 200510119837A CN 1793027 A CN1793027 A CN 1793027A
- Authority
- CN
- China
- Prior art keywords
- tio
- suspension
- preparation
- controlled
- suspension liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a multi-hole titanium dioxide manufacture method. The feature is that it uses spherical polymethacrylic acid methyl ester and TiO<SUB>2</SUB> as raw material, polyethylene imine and glycol as assistant material; adding distilled water into spherical polymethacrylic acid methyl ester and TiO<SUB>2</SUB> to make suspension liquid, and strictly controlling the pH value of the suspension liquid; adding polyethylene imine into the suspension liquid to take ultrasound; adding the suspension liquid into spherical polymethacrylic acid methyl ester suspension liquid, whisking slowly and adding glycol; taking the process of filtering in vacuum, drying, and scarifying, the material would be gained. The invention has simple producing device, and is easy to be controlled. It has the feature of controllable hole size and hole diameter uniform distribution.
Description
Technical field
The present invention relates to a kind of preparation method of micrometer level porous titanium dioxide ceramic, the preparation method of the micrometer level porous titanium dioxide ceramic that particularly a kind of even aperture distribution and aperture size are controlled.
Background technology
Because TiO
2Porous ceramics is in catalysis, separates, and more and more attracting people's interest in the widespread use aspect lightweight structural material and the biomaterial, particularly at water treatment research field, TiO
2That porous ceramics has is efficient, energy-conservation, cleaning, nontoxic, advantage such as the catalysis scope is wide, has broad application prospects aspect environment.At present, preparation TiO
2The porous ceramics method is a lot, and what wherein people were with the most use is to add pore-forming material, foam impregnation method, sol-gel method.Wherein people are with the most use is to add pore-forming material, and by the dry pressing preparation, but the prepared porous ceramics size distribution of this technology is inhomogeneous, and pore size presents randomness, and the employed organic pore-forming agents of this kind method can produce a large amount of tiny cracks.
Summary of the invention
The object of the present invention is to provide the preparation method of the controlled micrometer level porous titanium dioxide ceramic of a kind of even aperture distribution and aperture size.
The present invention utilizes the polymer suspension polymerization technique, with TiO
2Ceramic particle and spherical polymethylmethacrylate are made suspension respectively, as template, have successfully prepared even aperture distribution, the TiO of controllable aperture with single dispersive pore-forming material polymethylmethacrylate
2Porous ceramics.
Concrete preparation process may further comprise the steps:
(1) selects satisfactory spherical polymethyl methacrylate, TiO for use
2Be main raw material, polymine and ethylene glycol are auxiliary material;
(2) with above-mentioned main raw material polymethyl methacrylate and TiO
2Adding distil water is made suspension respectively, and the pH that adjusts separately is 7-9; At TiO
2Adding polymine in the suspension makes its dispersion agent and carries out ultrasonic; With ultrasonic good TiO
2Suspension adds in the suspension of polymethylmethacrylate at leisure, slowly stirs and adds ethylene glycol;
(3) above-mentioned mixed suspension is passed through vacuum filtration, in air, dry in the shade, thereby obtain polymethylmethacrylate and TiO
2Complex body; When treating that complex body moisture is fewer, it is dry that it is put into loft drier, and heating is then put into electric furnace in 200 ℃ of calcining 1.5-3h down with complex body, and 500 ℃ are continued behind the calcining 3-4h naturally cooling in electric furnace down, thus the TiO that obtains having even aperture distribution
2Micrometer level porous pottery.
Above-mentioned polymine molecular weight is 10000; The void content of porous ceramics can be by changing polymkeric substance and TiO
2The volume ratio of particle suspension liquid is controlled; The pore dimension of porous ceramics can be controlled by the size that changes polymkeric substance, to satisfy the requirement of different aperture size.
Production unit of the present invention is simple, and is easy to operate, easily control; Prepared TiO
2Porous ceramics has the controlled and equally distributed characteristics in aperture of aperture size.
Embodiment
Embodiment one
(1) selects spherical polymethyl methacrylate of 700nm and 500nmTiO for use
2Be main raw material, polymine and ethylene glycol are auxiliary material;
(2) with above-mentioned main raw material polymethyl methacrylate and TiO
2Adding distil water is made suspension respectively, and adjusts pH value separately, by potential measurement, selects for use the pH=7.8 can be so that both can be good at sticking; Wherein at TiO
2Adding the 0.05wt% polymine in the suspension makes its dispersion agent and carried out ultrasonic 10 minutes;
(3) consider controllable aperture, select for use suspension vol to compare TiO
2/ polymethylmethacrylate=0.3
With ultrasonic good TiO
2Suspension adds in the suspension of polymethylmethacrylate at leisure, slowly stirs and adds 0.1wt% ethylene glycol;
(4) above-mentioned mixed suspension is passed through vacuum filtration, in air, dry in the shade, thereby obtain polymethylmethacrylate and TiO
2Complex body;
When (5) treating that above-mentioned complex body moisture is fewer, it is dry that it is put into loft drier, with the rate of heating of 1 ℃/min, complex body put into electric furnace calcine 2h down in 200 ℃ then, 500 ℃ continue down calcining 4h after in electric furnace naturally cooling, thereby the TiO that obtains having even aperture distribution
2Micrometer level porous pottery, the sample gas porosity behind the sintering is measured as 78.2% by Archimedes's method, and scanning electron microscopic observation is to the about 600nm of pore dimension size.
Embodiment two
(1) selects the spherical polymethyl methacrylate of about 600nm and about 400nmTiO for use
2Be main raw material, polymine and ethylene glycol are auxiliary material;
(2) with above-mentioned main raw material polymethyl methacrylate and TiO
2Adding distil water is made suspension respectively, and adjusts pH value separately, by potential measurement, selects for use the pH=7.8 can be so that both can be good at sticking; Wherein at TiO
2Adding the 0.05wt% polymine in the suspension makes its dispersion agent and carried out ultrasonic 10 minutes;
(3) consider controllable aperture, select TiO for use
2/ polymethylmethacrylate (suspension vol ratio)=0.4
With ultrasonic good TiO
2Suspension adds in the suspension of polymethylmethacrylate at leisure, and slowly stir and add 0.1wt% ethylene glycol,
(4) above-mentioned mixed suspension is passed through vacuum filtration, in air, dry in the shade, thereby obtain polymethylmethacrylate and TiO
2Complex body;
When (5) treating that above-mentioned complex body moisture is fewer, it is dry that it is put into loft drier, with the rate of heating of 1 ℃/min, complex body put into electric furnace calcine 2h down in 200 ℃ then, 500 ℃ continue down calcining 4h after in electric furnace naturally cooling, thereby the TiO that obtains having even aperture distribution
2Micrometer level porous pottery, the sample gas porosity behind the sintering is measured as 74.8% by Archimedes's method, and scanning electron microscopic observation is to the about 450nm of pore dimension size.
Claims (5)
1. the preparation method of a porous titanium dioxide ceramic is characterized in that the steps include:
(1) with spherical polymethyl methacrylate and TiO
2Be main raw material, polymine and ethylene glycol are auxiliary material;
(2) with polymethyl methacrylate and TiO
2Adding distil water is made suspension respectively, and the pH value of two kinds of suspension of strict control; At TiO
2Adding polymine in the suspension makes its dispersion agent and carries out ultrasonic; With ultrasonic good TiO
2Suspension adds in the suspension of polymethylmethacrylate at leisure, slowly stirs and adds ethylene glycol;
(3) above-mentioned mixed suspension is passed through vacuum filtration, drying, incinerating technology, it is controlled to prepare aperture size, the TiO of even aperture distribution
2Micrometer level porous pottery.
2. preparation method as claimed in claim 1 is characterized in that spherical polymethyl methacrylate and TiO
2The pH value of suspension is controlled to be 7-9.
3. preparation method as claimed in claim 1 is characterized in that the polymine molecular weight is 10000.
4. preparation method as claimed in claim 1 is characterized in that the void content of porous ceramics can be by changing polymkeric substance and TiO
2The volume ratio of particle suspension liquid is controlled.
5. preparation method as claimed in claim 1 is characterized in that the pore dimension of porous ceramics can be controlled by the size that changes polymkeric substance, to satisfy the requirement of different aperture size.