CN1791707A - Fiber excellent in magnetic field responsiveness and conductivity and product consisting of it - Google Patents
Fiber excellent in magnetic field responsiveness and conductivity and product consisting of it Download PDFInfo
- Publication number
- CN1791707A CN1791707A CN200480013786.5A CN200480013786A CN1791707A CN 1791707 A CN1791707 A CN 1791707A CN 200480013786 A CN200480013786 A CN 200480013786A CN 1791707 A CN1791707 A CN 1791707A
- Authority
- CN
- China
- Prior art keywords
- fiber
- magnetic material
- fabric
- mentioned
- brush roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A fiber which consists of polymer containing a spherical magnetic material with a saturation magnetic flux density of at least 0.5 Tesla and having a fiber forming capability, and which is excellent in magnetic field responsiveness and conductivity. In a preferable mode, (a) an average particle size of a spherical magnetic material is up to 5 mum, (b) an coercive force of a spherical magnetic material is up to 1000 A/m, and (c) a fiber is a composite fiber consisting of a magnetic layer containing 20-90 wt.% of a spherical magnetic material and a protection layer containing less than 20 wt.% of a spherical magnetic material. Clothing such as a woven fabric and a short fiber using the above fiber, a brush roller consisting of the fibers, and electrophotographic device comprising the brush roller.
Description
Technical field
The goods that the present invention relates to magnetic field responsiveness and high conductive fiber and constitute by fiber.Very good, the fiber that possesses magnetic and electric conductivity of the stability of electric conductivity when the present invention relates to heat resistance in applying the device in magnetic field and magnetic field responsiveness or humidity in more detail and changing.In addition, the present invention relates to use cloth and silks such as above-mentioned fibroplastic fabric, braided fabric and nonwoven fabric, staple fibre, the brush roll that constitutes by above-mentioned fiber, use electric photographic apparatus that above-mentioned brush roll forms etc.
Background technology
At present, studying magnetic fibre affected by magnetic fields.For example, disclose, obtained being applicable to the technology (referring to following patent documentation 1) of the magnetic fiber of magnetic recording media purposes or dress material purposes by suitably selecting the kind and the addition of magnetic particle.
Particularly, at first,, proposed to be added with the fiber of the high magnetic particle of magnetic remanence rate as the fiber that is used for magnetic recording media.In the above-mentioned fiber,, must use the high needle-like magnetic particle of magnetic remanence rate in order to form fiber with magnetic.But owing to the needle-like that is shaped as of employed magnetic particle, therefore magnetic particle is difficult to be disposed densely in fiber, is included in the fiber with being difficult to make the magnetic particle high concentration.In addition, because of the relation of purposes, it is opaque to become optics for fear of the fiber itself that obtains, and the composite rate that does not improve magnetic particle is necessary.Therefore, the fiber of above-mentioned motion can't comprise to high concentration magnetic particle, lacks magnetic field responsiveness.
Be applicable to the example of the magnetic fiber of dress material purposes as another kind, proposed to add the fiber of the low magnetic particle of magnetic remanence rate.For above-mentioned fiber is used for the dress material purposes, on attractive in appearance, 30 weight % must as far as possible the magnetic particle amount be reduced to or below the 30 weight %.In addition, as purposes, use above-mentioned fiber to make braided fabric after, carry out tufting and cut-out, obtain pile (pile) braided fabric after, in magnetic field, handle, make artificial fur, the fiber that above-mentioned technology obtains is not suitable for use in the high mechanical component fiber of design accuracy fully.And therefore the result can't make fiber itself have electric conductivity because the magnetic particle amount is a low concentration.
In addition, proposed to relate to the technology (referring to following patent documentation 2) of the composite fibre that is combined with magnetic material.The structure of above-mentioned composite fibre is as follows: with low concentration be combined with magnetic material first composition be core, second composition that is combined with magnetic material and use fusing point to be lower than fiber formation property polymer of first composition is configured in the sheath with using high concentration, composite fibre to said structure is heat-treated, and can make it have magnetic.But, because it is low that high concentration ground is combined with the fusing point of fiber formation property polymer of second composition of magnetic material, so the heat resistance and the poor rigidity of above-mentioned composite fibre, in addition, in the use of this composite fibre, fibrous physical property such as also take place that magnetic material peels off easily through the time change, the poor durability the when result uses for a long time can't be used as the mechanical component fiber.
And, also propose in fiber, to be dispersed with the magnetic fibre of magnetic or used this fibroplastic electric photographic apparatus brush roll (referring to following patent documentation 3 and 4).Disclosed magnetic fibre is to make the magnetic magnetization that comprises in the fiber in the above-mentioned patent documentation, is used for controlling adhering to of toner that electric photographic apparatus uses.But, in the such scheme, for being used for controlling the toner cleaning process or utilizing the magnetic scale of construction of the fiber of the developing process that toner adheres to not provide concrete technological guidance, so the magnetization characteristic of magnetic fibre etc. and unclear.In addition, have electric conductivity, need in addition and use conductive powders in order to make fiber itself.Therefore, only by the technology of such scheme can't thoroughly realize making the brush roll that has magnetic and electric conductivity concurrently with fiber, and make the purpose of the good brush roll of cleaning property or development.
[patent documentation 1] spy opens clear 57-167416 communique (claims)
[patent documentation 2] spy opens clear 59-173312 communique (claims, embodiment)
[patent documentation 3] spy opens flat 2-193176 communique (claims, embodiment)
[patent documentation 4] spy opens flat 2-193180 communique (claims, embodiment)
Summary of the invention
Problem of the present invention is for solving above-mentioned prior art problems, a kind of fiber is provided, the magnetic field responsiveness of this fiber is very good, promptly, fiber itself is also magnetized strongly when applying magnetic field, and the back fiber itself that disappears in magnetic field is not magnetized (being difficult to become magnet), even be small magnetic field in addition, also response magnetic field sensitively, in addition, heat resistance when being assembled into it in device, the durability when using for a long time and humidity when changing stable ratio resistance value etc. very good, have magnetic field responsiveness and electric conductivity.
In addition, other problems of the present invention are for providing fibres such as using above-mentioned fibroplastic fabric or cloth and silks such as braided fabric or nonwoven fabric, staple fibre, dress material and using goods such as brush roll that above-mentioned fibre forms, assemble the various devices that these goods form.
The inventor etc. have carried out research repeatedly for the fiber that obtains having good magnetic field responsiveness and electric conductivity, in research process, find to comprise the shortcoming that the material with given shape and rerum natura can solve prior art in the fiber by making, and can obtain more advantages that prior art can't realize, thereby finish the present invention.
That is, that fiber of the present invention is served as reasons is that polymer with fiber forming property power constitutes, magnetic field responsiveness and high conductive fiber, and it is the above spherical magnetic material of 0.5 tesla or 0.5 tesla that above-mentioned fiber contains saturation flux density.
In addition, fiber of the present invention has following preferred version.
(a) average grain diameter of above-mentioned spherical magnetic material is 5 μ m or below the 5 μ m.
(b) coercive force of above-mentioned spherical magnetic material is 1000A/m or below the 1000A/m.
(c) composite fibre that constitutes by the protective layer that contains quantity not sufficient 20 weight % of magnetosphere that contains the above-mentioned spherical magnetic material of 20~90 weight % and above-mentioned spherical magnetic material.
(d) above-mentioned magnetosphere is that core composition, above-mentioned protective layer are that sheath composition and above-mentioned magnetosphere are the core-sheath-type composite fibre of 5~95 volume %.
(e) above-mentioned spherical magnetic material is the metal of chosen from Fe, nickel and cobalt more than purity 98% or 98%.
Shrinkage factor when (f) keeping 15 minutes in 98 ℃ of boiling water is below 10% or 10%.
(g) the permanent elongation rate is 5~30%.
(h) the initial stage tensile elasticity rate is 15cN/dtex or more than the 15cN/dtex.
(i) above-mentioned polymer with fiber forming property power is to be selected from the polymer that fusing point is polyester polymer, polyamide polymers, polyolefin polymers and polyacrylonitrile base polymer more than 150 ℃ or 150 ℃.
(j) be 10 than resistance value
3~10
9Ω cm.
(k) fracture strength is 0.5cN/dtex or more than the 0.5cN/dtex.
(l) the ratio resistance value that is made of above-mentioned fiber is 10
6~10
9The staple fibre of Ω cm.
(m) fibre length that is made of above-mentioned fiber is the staple fibre of 0.05~150mm.
Among the present invention, can use above-mentioned fiber or staple fibre to make cloth and silks such as fabric, braided fabric and nonwoven fabric.And cloth and silk of the present invention has following preferred version.
(a) fabric tissue is a pile weave construction.
(b) be selected from knit stitches and handle braided fabric in the braided fabric that makes textile surface have pile shape fiber by the braided fabric of back side napping organizational composition and through napping.
In addition, among the present invention, with above-mentioned fiber or staple fibre is bonding and flocking (flock) at least a portion of substrate, can make the flocking thing thus.In addition, above-mentioned cloth and silk can be bonded at least a portion of substrate, make the cloth and silk complex.In addition, can use above-mentioned fiber or staple fibre to make dress material.
Among the present invention, at least a portion of above-mentioned cloth and silk can be bonded on the bar-shaped object and make brush roll.In addition, at least a portion of bar-shaped object, can make brush roll by above-mentioned staple fibre is bonding and flocking.In addition,, can use mainly bar-shaped object that constitutes by metal or the bar-shaped object that mainly constitutes, be covered at least a portion of metal of above-mentioned intermediate layer by metal and intermediate layer as bar-shaped object.
Among the present invention, the clearing apparatus, Charging system, developing apparatus and the discharge system that use above-mentioned brush roll can be made, in addition, the electric photographic apparatus that uses above-mentioned clearing apparatus and/or Charging system and/or developing apparatus and/or discharge system can be made.
Fiber of the present invention has good magnetic field responsiveness, promptly, fiber is also by hard magnetization when applying magnetic field, apply in magnetic field magnetic field, back disappear after fiber itself do not keep the state of being magnetized (promptly being difficult to become magnet), even be also response magnetic field etc. sensitively of small magnetic field in addition.In addition, not yielding under the high temperature when installing to group of fibers of the present invention in the device, that is, in addition excellent heat resistance, also is difficult for forfeiture magnetic field responsiveness or electric conductivity when using for a long time, that is, the durability when using for a long time is also good.And, even fiber of the present invention also has stable ratio resistance value when humidity changes, that is, can keep electric conductivity etc., owing to have very good magnetic field responsiveness or electric conductivity, therefore can be used in various uses.
This is because in the present invention, by using average grain diameter is 5 μ m or the spherical magnetic material below the 5 μ m, when making fiber middle and high concentration ground comprise spherical magnetic material, spherical magnetic material has the most closely knit interstitital texture, therefore can comprise to high concentration above-mentioned spherical magnetic material.Therefore and the employed magnetic material of fiber of the present invention is spherical, adds in the cut-out of fiber the wearing and tearing or the wearing and tearing of the guide plate in the operation of cutter to be suppressed at bottom line man-hour.And fiber of the present invention has improved spherical magnetic material and has formed compatibility between the polymer of fiber, therefore also has the good advantage of carrying out property of operation when breaking end considerably less such fiber process when operation is carried out.
Fiber of the present invention can be made staple fibre, and, because fiber of the present invention is made of the fiber with very good magnetic field responsiveness or electric conductivity as mentioned above, therefore staple fibre is included in liquid or solid or the polymer etc., as giving the additive of magnetic field responsiveness or electric conductivity, in addition, also can be used as following electric flocking fiber.When particularly staple fibre of the present invention being used for electric flocking,, can easily be controlled to be the desirable resistance value that compares by controlling the content of the spherical magnetic material that adds.That is, can control the easiness of electric flocking.
The specific embodiment
It is the above spherical magnetic material of 0.5 tesla or 0.5 tesla that fiber of the present invention must contain saturation flux density.Saturation flux density is represented the reactivity in the magnetic field of certain intensity (sensitivity).The saturation flux density of spherical magnetic material is 0.5 tesla or 0.5 tesla when above, and fiber reacts (replying) to magnetic field easily, though therefore do not use high-intensity magnetic field but in more weak magnetic field also replying of controlling fiber easily.But, during saturation flux density less than 0.5 tesla, a little less than the response of fiber to magnetic field, must apply high-intensity magnetic field when fiber is used in magnetic field.The saturation flux density of spherical magnetic material is preferably 1.0 teslas or more than 1.0 teslas, more preferably more than 1.5 or 1.5 teslas.In addition, though the upper limit of the saturation flux density of above-mentioned spherical magnetic material is high more preferred more, be preferably below 4.0 or 4.0 teslas.
In addition, the coercive force of the spherical magnetic material that contains in the fiber of the present invention is preferably 1000A/m or below the 1000A/m.Coercive force be meant for the intensity of magnetization in the magnetization curve that makes magnetic material be the zero backing field intensity (diamagnetic) that applies.The coercive force of spherical magnetic material is 1000A/m or 1000A/m when following among the present invention, is difficult to become magnet.That is, its implication is for to apply magnetic field, and magnetic field is released and after disappearing, fiber itself is not magnetized, and magnetic field responsiveness is good.Coercive force is during greater than 1000A/m, even be released in magnetic field and after disappearing, fiber still keeps the state that is magnetized, so fiber adheres to each other sometimes.Therefore, according to the purposes of using fiber of the present invention, when for example making following brush roll, can't be as clearing apparatus with member or developing apparatus member.Among the present invention, above-mentioned coercive force is 500A/m or below the 500A/m more preferably, and 100A/m or below the 100A/m more preferably is preferably 20A/m or below the 20A/m especially.In addition, above-mentioned coercive force is for low value is preferred more more, is preferably 0A/m or more than the 0A/m.
In addition, the preferred average grain diameter of spherical magnetic material that contains in the fiber of the present invention is following spherical of 5 μ m or 5 μ m.The fiber of the present invention synthetic fiber that polymer with fiber forming property power constitutes of serving as reasons.The magnetic material that contains in the fiber is an average grain diameter when being following spherical of 5 μ m or 5 μ m, owing to be spherical, so the surface area of particle is little, and is also good with the wettability (compatibility) of the polymer of formation fiber.In addition, the most closely knit filling effect also has the advantage of the guide plate wearing and tearing when reducing fiber process except very good aspect fiber middle and high concentration ground contains spherical magnetic material.Particularly in the fiber process, when fiber of the present invention is used as staple fibre, cut off the fiber that forms fibre bundle with cutter and make staple fibre.At this moment, because the magnetic material that cooperates be spherical, so little to the influence of the sword of cutter, the wearing and tearing of sword become very little, excellent processability.
Herein, for the average grain diameter of spherical magnetic material, the value of obtaining with the method for the C. item of following embodiment record is as average grain diameter.In addition, whether the shape for particle is spherical, similarly adopt the method for the C. item record of following embodiment to measure the maximum gauge (R) and the minimum diameter (r) of each particle itself of spherical magnetic material, by its ratio (R/r) calculating circularity, R/r be judged to be below 1.5 or 1.5 spherical.But, poor when magnetic material is not spherical with the wettability (compatibility) of polymer, be included in the fiber with being difficult to high concentration, the magnetic field responsiveness of fiber is poor.
The average grain diameter of spherical magnetic material also can be greater than 5 μ m, when but average grain diameter is excessive, sometimes poor with the miscibility of polymer, in addition, the cut-out of fiber adds the cutter in man-hour or the guide plate in the operation weares and teares sometimes easily, in addition, sometimes this magnetic particle itself become fiber owe to fall into part.For example, in the manufacturing procedure of the stretching process of making fiber of the present invention or use fiber, shortcomings such as broken string appear sometimes taking place easily.In the present invention, consider that the average grain diameter of spherical magnetic material is preferably 4 μ m or below the 4 μ m, more preferably 3 μ m or below the 3 μ m from making spherical magnetic material be included in the fiber aspect more to high-density.Though the lower limit of average grain diameter is the smaller the better,, consider from making it stably be included in the fiber aspect, be preferably 0.001 μ m or more than the 0.001 μ m, more preferably 0.005 μ m or more than the 0.005 μ m, more preferably more than the 0.01 or 0.01 μ m.
In addition, in the scope that does not influence main idea of the present invention, can exist on the surface of spherical magnetic material particle the degree of depth be particle diameter below 1/10th or 1/10th and/or size for the ditch below 1/10th or 1/10th of particle diameter, jog or do not influence the magnetic of spherical magnetic material itself or the lining portion of the scope of electric conductivity etc.Herein, the thickness of this lining portion is preferably below 1/10th or 1/10th of diameter of spherical magnetic material.
Can have the electric conductivity aspect from fiber itself and consider that the spherical magnetic material that contains in the fiber of the present invention preferably has electric conductivity.As long as the performance of the electric conductivity of spherical magnetic material has the electric conductivity that is higher than the polymer that forms fiber, that is,, have littler ratio resistance value (in other words being specific insulation) and get final product as its index.Consider that from better electric conductivity being given the fiber aspect ratio resistance value of this spherical magnetic material is preferably 5000 Ω cm or below the 5000 Ω cm, 1 Ω cm or below the 1 Ω cm more preferably, more preferably 100 μ Ω cm or below the 100 μ Ω cm.In addition, though more the smaller the better than the lower limit of resistance value, be not particularly limited, be preferably 1n Ω cm or more than the 1n Ω cm.
As mentioned above, the spherical magnetic material that contains in the fiber of the present invention is that saturation flux density is the above spherical magnetic material of 0.5 tesla or 0.5 tesla.As the spherical magnetic material that uses among the present invention, for example can enumerate the material that constitutes by single metals such as pure iron, pure nickel, pure cobalt and pure molybdenums, in addition, can also enumerate silicon steel or be the spherical magnetic material that high-permeability alloy etc. constitutes, can suitably adopt above-mentioned material by permalloy, superalloy and the Po Mingde iron cobalt of the multiple element of chosen from Fe, nickel, cobalt and molybdenum.And, in the above-mentioned spherical magnetic material, the little and very broad aspect consideration of saturation flux density from coercive force, preferred purity 95% or 95% above iron, nickel and cobalt, more preferably purity is whole pure iron, pure nickel and the pure cobalt more than 98% or 98%.Particularly to adopt the pure iron of carbonyl process manufacturing or the common purity of pure nickel be more than 99% or 99% and it is spherical to have, and is particularly preferred therefore.The purity of above-mentioned pure iron, pure nickel or pure cobalt is high more preferred more, and preferably using purity is 100% material.Above-mentioned spherical magnetic material can use a kind separately, perhaps also can also use multiple material as required in the scope that does not influence the invention main idea.
For fiber of the present invention,, can adopt any means of in component of polymer, adding spherical magnetic material with fiber forming property power as making spherical magnetic material be included in method in the polymer.Particularly, for example can enumerate (A) in inert gas atmosphere as its method, molten polymer, add spherical magnetic material therein, utilize extruder or static mixer and so on mixing roll, under normal pressure or decompression, carry out mixing method, and (B) in the polymerisation of common polymer, any stage before polymerisation stops makes it contain spherical magnetic material, carries out mixing method etc.Owing to can finish mixingly easily, and spherical magnetic material and component of polymer be by mixing more imperceptibly, the therefore preferred method that adopts above-mentioned (A).Particularly, can preferably use the above multishaft extruder of single shaft, twin shaft or twin shaft about extruder.Polymer and spherical magnetic material when mixing, from the mixing imperceptibly aspect of spherical magnetic material is considered, are preferably adopted the above multishaft extruder of twin shaft or twin shaft.And the ratio 1/w of the length (1) of the axle of extruder and the thickness (w) of axle is not particularly limited, and considers that from improving mixing property aspect 1/w is preferably more than 10 or 10, more preferably more than 20 or 20, more preferably more than 30 or 30.
In addition, the interpolation of spherical magnetic material can be carried out dry type the stage before offering extruder and mix, and perhaps also can use the side-fed machine that is provided on the extruder, coexists with molten polymer one and mixes in the extruder.In addition, particularly about static mixer, for example, so long as the stream of molten polymer is divided into a plurality of more than 2 or 2 and the static mixing elements of the operation unified once more (to be operating as 1 grade from above-mentioned 1 time of cutting apart till the unification) gets final product, be not particularly limited.Consider that from having better mixing property aspect the progression of static mixer is preferably more than 5 grades or 5 grades, more preferably more than 10 grades or 10 grades.In addition, though also depend on the necessary length of stream, its progression is preferably below 50 grades or 50 grades.
Fiber of the present invention is made of the polymer with fiber forming property power that comprises spherical magnetic material basically.Fiber is meant the material of elongated shape, can be general alleged long fiber (long filament, filaments), can for length the staple fibre (staple fibre of 0.05~150mm also, staples), perhaps also can be generally 10mm or the staple fibre below the 10mm, so long as the fiber that is made of the polymer with fiber forming property power that can access above-mentioned fiber shape is promptly applicable to fiber of the present invention for the length of using in the electric flocking processing etc.Fibre length can suitably be selected according to using method or purposes as purpose.For example, the fibre length of the staple fibre that uses in the electric flocking processing is preferably 0.1~10mm, more preferably 0.2~5mm.
In the present invention, from utilizing electric flocking processing effectively to use the aspect to consider that the ratio resistance value of staple fibre is preferably 10
6~10
9Ω cm.Owing to contain spherical magnetic material to fiber high concentration of the present invention, the staple fibre that cuts into fibre length and be 0.1~10mm have and cut before the identical ratio resistance value of fiber, therefore than the common less than 10 of resistance value
6Ω cm.But the ratio resistance value that is used as the fiber of electric flocking is generally 10
6~10
9Ω cm, more preferably 10
7~10
8Ω cm.For staple fibre of the present invention,,, preferably staple fibre is handled with conducting electricity modulator etc. in order to obtain having preferably staple fibre than resistance value herein.As the conduction modulator, for example can enumerate the aqueous solvent or the organic kind solvent that have mixed silica-based particle.The particle diameter of the silica-based particle of this moment is generally 1nm~200 μ m, more preferably adopts the particle diameter of 3nm~100 μ m sizes.
As the polymer that uses in the fiber of the present invention, for example can enumerate polyester polymer, polyamide polymers, polyimides base polymer, polyolefin polymers or other through the addition polymerization of vinyl and synthetic polyvinylss such as for example polyacrylonitrile base polymer, fluorine-based polymer, cellulosic polymer, silicon base polymer, aromatic series or elastomers such as aliphatic ketone polymer, natural rubber or synthetic rubber, and other diversified engineering plastics etc. with fiber forming property power.
As polymer, particularly, for example can enumerate the synthetic polyolefin polymers of mechanism that generates polymer based on monomer through sudden reactions such as radical polymerization, anionic polymerisation or cationic polymerizations with vinyl with fiber forming property power.As other polyvinylss, can enumerate polyethylene, polypropylene, polybutene, polymethylpentene, polystyrene, polyacrylic acid, polymethylacrylic acid, polymethyl methacrylate, polyacrylonitrile, polytetrafluoroethylene (PTFE), polyvinylidene fluoride, polyvinylidene chloride and polyvinylene dicyan etc.Above-mentioned polymer for example can be polyethylene or the independent like this polymer that is polymerized of polypropylene, or carries out the copolymer that polymerisation forms under the situation of a plurality of monomer coexistences.For example,, then generate poly-(styrene-methacrylate) such copolymer, among the present invention, also can adopt polymer as above-mentioned copolymer if under the coexistence of styrene and methyl methacrylate, carry out polymerization.
In addition, as polymer, for example, can enumerate the polyamide polymers that the reaction of carboxylic acid or carboxyl acyl chloride and amine forms with fiber forming property power.Particularly, can enumerate nylon 6, nylon 7, nylon 9, nylon 11, nylon 12, nylon 6,6, nylon 4,6, nylon 6,9, nylon 6,12, nylon 5,7 and nylon 5,6 etc.In addition, in the scope that does not influence main idea of the present invention, the polyamide polymers that also can serve as reasons other aromatic series, aliphatic or alicyclic dicarboxylic acid and aromatic series, aliphatic or alicyclic diamine composition constitute.In addition, aromatic series, aliphatic and alicyclic etc. at least a kind of compound can have the polymer of carboxylic acid and amino amino carboxylic acid compounds simultaneously for use separately, or the polyamide polymers that forms of the 3rd or the 4th copolymer composition copolymerization.
In addition, as polymer, for example can enumerate the polyester polymer that carboxylic acid and alcohol form through esterification with fiber forming property power.As polyester polymer, for example can enumerate the polymer of the ester bond formation of dicarboxylic acid compound and diol compound.As above-mentioned polyester polymer, can enumerate polyethylene terephthalate, polytrimethylene terephthalate (being also referred to as poly terephthalic acid trimethylene ester), polybutylene terephthalate (PBT) (being also referred to as the poly terephthalic acid tetramethylene ester), PEN and poly terephthalic acid cyclohexanedimethanoester ester, and be principal component with the aromatic hydroxy-carboxylic, have a liquid crystal polyester of fused solution crystallinity etc.
The polyester polymer that forms by the ester bond of dicarboxylic acid compound and diol compound for example can the copolymerization dicarboxylic acid compound etc. other compositions.As above-mentioned dicarboxylic acid compound, for example, can enumerate terephthalic acid (TPA), M-phthalic acid, naphthalenedicarboxylic acid, biphenyl dicarboxylic acid, the anthracene dioctyl phthalate, luxuriant and rich with fragrance dioctyl phthalate, the diphenyl ether dioctyl phthalate, the biphenoxyl ethane dioctyl phthalate, the diphenylethane dioctyl phthalate, adipic acid, decanedioic acid, 1, the 4-cyclohexane cyclohexanedimethanodibasic, 5-sulfoisophthalic acid sodium, 5-4-butyl-phosphonium M-phthalic acid, azelaic acid, dodecanedioic acid, six hydrogen terephthalic acid (TPA)s and so on aromatic series, aliphatic, the alkyl of alicyclic dicarboxylic acid and above-claimed cpd, alkoxyl, allyl, aryl, amino, imino group, derivatives such as halide, addition product, constitutional isomer and optical isomer.Among the present invention, can use a kind in the above-mentioned dicarboxylic acid compound, perhaps also can will be used in combination more than 2 kinds or 2 kinds.
In addition, as the copolymer composition of polyester polymer, can make the diol compound copolymerization.As above-mentioned diol compound, for example can enumerate ethylene glycol, propylene glycol, butanediol, pentanediol, hexylene glycol, 1,4-cyclohexanedimethanol, neopentyl glycol, quinhydrones, resorcinol, dihydroxybiphenyl, naphthalene glycol, anthracene glycol, luxuriant and rich with fragrance glycol, 2,2-two (4-hydroxy phenyl) propane, 4, derivative, addition product, constitutional isomer and optical isomers such as the alkyl of 4 '-dihydroxy diphenyl ether, bisphenol S and so on aromatic series, aliphatic, alicyclic diol compound and above-claimed cpd, alkoxyl, allyl, aryl, amino, imino group, halide.Among the present invention, can use a kind in the above-mentioned diol compound, perhaps also can will be used in combination more than 2 kinds or 2 kinds.
In addition,, can enumerate the compound that has hydroxyl and carboxylic acid in a kind of compound as the copolymer composition of polyester polymer, that is, and hydroxycarboxylic acid.As above-mentioned hydroxycarboxylic acid, for example can enumerate derivative, addition product, constitutional isomer and the optical isomer such as alkyl, alkoxyl, allyl, aryl, amino, imino group, halide of lactic acid, 3-hydroxy propionate, 3-butyric ester, 3-butyric ester valerate, hydroxybenzoic acid, hydroxynaphthoic acid, hydroxyl anthroic acid, hydroxyl phenanthrenecarboxylic acid, (hydroxy phenyl) vinylformic acid and so on aromatic series, aliphatic, alicyclic diol compound and above-claimed cpd.Among the present invention, can use a kind in the above-mentioned hydroxycarboxylic acid, perhaps also can will be used in combination more than 2 kinds or 2 kinds.
In addition, as polyester polymer, aromatic series, aliphatic and alicyclic etc. in a kind of compound can be for the hydroxy carboxylic acid compound that has carboxylic acid and hydroxyl simultaneously polymer for main repetitive.As the polymer that constitutes by above-mentioned hydroxycarboxylic acid, for example can enumerate birds of the same feather flock together (hydroxycarboxylic acid) of PLA, poly-(3-hydroxy propionate), poly-(3-butyric ester), poly-(3-butyric ester valerate) etc.In addition, also can use aromatic series, aliphatic and alicyclic dicarboxylic acid or aromatic series, aliphatic and alicyclic diol composition in above-mentioned poly-(hydroxycarboxylic acid), perhaps also can make multiple hydroxycarboxylic acid copolymerization.
In addition, as the polymer that uses in the fiber of the present invention, can enumerate the polybenzimidazoles base polymer of pure and mild carbonic acid derivative through polyimides base polymer, dicarboxylic ester and the diamine reactant formation of the cyclic polycondensation formation of polycarbonate polymer, carboxylic acid anhydrides and the diamines of ester exchange reaction formation with fiber forming property power.In addition, can enumerate polymer such as polysulfones-like polymer, polyethers polymer, polyphenylene sulfide base polymer, polyether-ether-ketone polymer, PEKK base polymer, aliphatic polyketone, can also enumerate the derivative etc. of cellulosic polymer or chitin, chitosan and above-claimed cpd and derive from polymer of natural polymer etc.
As the purposes of fiber of the present invention, particularly also may be assembled in the machinery, in high temperature, to use, the change of shape under the preferred high temperature is little, that is, and excellent heat resistance.Therefore, preferably using fusing point is the polymer that polyester polymer more than 150 ℃ or 150 ℃ and/or polyamide polymers and/or polyolefin polymers and/or polyacrylonitrile base polymer constitute.Especially preferably using fusing point is polyester polymer and/or polyamide polymers more than 200 ℃ or 200 ℃.Herein, fusing point is meant the peak temperature of the method mensuration of putting down in writing by the B. item of following embodiment.
As fusing point is polyester polymer and/or polyamide polymers and/or polyolefin polymers more than 150 ℃ or 150 ℃, for example can enumerate polyethylene terephthalate, polytrimethylene terephthalate (being also referred to as poly terephthalic acid trimethylene ester), polybutylene terephthalate (PBT) (being also referred to as the poly terephthalic acid tetramethylene ester), PEN, the poly terephthalic acid cyclohexanedimethanoester ester, polyester and/or above-mentioned copolyesters such as PLA, nylon 6, nylon 11, nylon 12, nylon 6,6, nylon 4,6, nylon 6,9, nylon 6,12, nylon 5,7 and nylon 5,6 polyamide such as grade and/or above-mentioned copolyamide, polypropylene and polymethylpentene etc.Wherein, especially preferably using with polyethylene terephthalate and/or ethylene glycol terephthalate is copolymer and nylon 6 and/or its copolymer of main repetitive.Be that the hygroscopicity of copolymer of main repetitive is low particularly with polyethylene terephthalate and/or ethylene glycol terephthalate, be assembled into when using in the following electric photographic apparatus, with respect to environmental changes such as humidity variations, change hardly than resistance value, therefore can stably keep the desirable resistance value that compares.
In fiber of the present invention, can use a kind of polymer that is selected from above-mentioned example, perhaps also can use multiple polymers.
The polymer that uses in the fiber of the present invention can use the polymer with viscosity that is generally used for synthetic fiber.For example, when using the polyethylene terephthalate as one of polyester polymer, intrinsic viscosity (IV) is preferably 0.4~1.5, and more preferably 0.5~1.3.In addition, when using polytrimethylene terephthalate, IV is preferably 0.7~2.0, and more preferably 0.8~1.8.When using polybutylene terephthalate (PBT), IV is preferably 0.6~1.5, and more preferably 0.7~1.4.In addition, when using the nylon 6 as one of polyamide polymers, limiting viscosity (η) is preferably 1.9~3.0, and more preferably 2.1~2.8.
In addition, the melt viscosity of the polymer that uses in the fiber of the present invention is not particularly limited, and under the spinning temperature of employed polymer, uses shear rate to be 10sec usually
-1The time shear viscosity be 10~100,000 the pool polymer, preferably use 100~50,000 the pool polymer.
The fiber of the present invention fiber that the single component that contains spherical magnetic material equably constitutes of serving as reasons.In addition, in order to have good response and electric conductivity and fiber with excellent the carrying out property of operation or the operability that add man-hour to magnetic field concurrently, fiber of the present invention also can be for bearing the fiber of above-mentioned effect respectively.Therefore, fiber of the present invention is preferably the composite fibre that the protective layer that contains quantity not sufficient 20 weight % by the magnetosphere of the spherical magnetic material that contains 20~90 weight % and spherical magnetic material constitutes.
Because the ground of the magnetosphere high concentration in the composite fibre contains spherical magnetic material, therefore be the composition of bearing mainly that fiber itself has to the response or the electric conductivity in magnetic field.And protective layer does not contain or contain spherical magnetic material on a small quantity, is to bear to make that to utilize fiber of the present invention to add the carrying out property of operation in man-hour good or do not have the composition of the fibrous physical property of bad situation degree when handling fiber.Very good or have the high conductivity aspect and consider that the magnetosphere of fiber of the present invention preferably contains the spherical magnetic material of 30~85 weight %, more preferably contains the spherical magnetic material of 40~80 weight % from the magnetic field responsiveness of the fiber that obtains.In addition; for protective layer; consider that from the more good aspect of rerum natura of the fracture strength that makes carrying out property of above-mentioned operation and fiber itself of the present invention or elongation at break etc. the content of spherical magnetic material is preferably 10 weight % or below the 10 weight %, does not especially preferably contain spherical magnetic material.
In addition, if enumerate preferred complex morphological, then can enumerate the bimetal type composite fibre that (a) magnetosphere and protective layer are fitted and formed by fibroplastic composite fibre of the present invention; (b) has half core-sheath-type composite fibre of following structure, promptly, magnetosphere is partly exposed at fiber top layer formation core, the magnetospheric magnetosphere except that this exposed portions serve of protective layer lining, or protective layer partly exposes at fiber top layer formation core the protective layer except that this exposed portions serve of magnetosphere lining protective layer; (c) have the core-sheath-type composite fibre of following structure, that is, be core, be sheath, magnetosphere is covered fully with the protective layer with the magnetosphere, or be core with the protective layer, be sheath with the magnetosphere, protective layer is covered fully; (d) have the islands-in-sea bicomponent fibre of following structure, that is, magnetosphere forms the island, is the sea with the protective layer, a plurality of islands are covered fully, or protective layer forms the island, be the sea with the magnetosphere, a plurality of islands are covered fully; Reach the mixing composite fibre of the mixing formation of composition that (e) will form magnetospheric composition and formation protective layer etc.
From making the fiber that obtains have carrying out property of better operation and the consideration of processability aspect; be core preferably with the magnetosphere, be sheath with the protective layer, core-sheath-type composite fibre that magnetosphere is covered fully, or magnetosphere forms the island, be the sea with the protective layer, islands-in-sea bicomponent fibre that a plurality of islands are covered fully.Consider from manufacture view more easily, preferred especially be core with the magnetosphere, be sheath with the protective layer, core-sheath-type composite fibre that magnetosphere is covered fully.
In addition, the structure of core-sheath-type composite fibre is not particularly limited so long as sheath fully comprises the structure of core gets final product, and can be the concentric circles core-sheath-type, also can be the eccentric type core-sheath-type, preferred concentric circles core-sheath-type.And, for the compound ratio of core-sheath-type composite fibre, consider that from making the better aspect of magnetic field responsiveness and electric conductivity magnetosphere is preferably 5~95 volume %, more preferably 30~90 volume % are preferably 50~85 volume % especially.
When the ratio of the spherical magnetic material that contains in the fiber of the present invention was great, it is big that the proportion of the fiber that obtains also becomes easily.Therefore, when fiber of the present invention is for example used fiber as electric flocking,, must have suitable fiber proportion sometimes in order to adapt to using method or purposes.Herein, in order to obtain suitable fiber proportion, can be arranged on the hollow bulb that the fiber axis direction is communicated with, or the space that is not communicated with is set at fibrous inside.As the method that hollow bulb or space are set, for example can enumerate the tube head that (a) uses the special squit hole shape of the circle can form crack with seam when fibre spinning and so on hollow, hollow bulb is set in fiber; Or (b) in water, hot water or organic solvent, together carry out spinning with the ease of solubility composition, and make this ease of solubility composition stripping, generate hollow bulb or space; Or (c) the fiber high magnification is stretched the method that the polymer that forms fiber and spherical magnetic material is peeled off generate the space etc.The mixing materials that particularly the ease of solubility composition can make water, hot water, other dissolvings are organic and/or the aqueous solution of inorganic compound or organic solvent or the multiple solvent selected from above-mentioned solvent combine etc. are with its stripping and remove.Among the present invention, preferred water, hot water, other dissolvings aqueous solution organic and/or inorganic compound carry out stripping.
As above-mentioned stripping composition, for example can enumerate easy acrylic acid dissolubility polyester, hot water solubility's polyester, polyethylene glycol, polyethylene glycol oxide, water insoluble thermoplastic polyvinyl alcohol, ethylene-vinyl alcohol copolymer and polysaccharide compound etc. herein.Among the present invention, the aspect easy and simple to handle when carrying out melt spinning considers, preferred easily acrylic acid dissolubility polyester or be soluble in hot water solubility's polyester of hot water.
Because fiber of the present invention also may the environment when using be exposed in the high temperature more than 50 ℃ or 50 ℃, therefore preferred excellent heat resistance.Therefore, the shrinkage factor when fiber of the present invention keeps 15 minutes in 98 ℃ of boiling water is preferably below 10% or 10%, and more preferably shrinkage factor is below 5% or 5%.Shrinkage factor is low more preferred more, can use to be low to moderate 0% fiber.Shrinkage factor herein adopts according to following embodiment E. the value that the method for item records.
The little aspect of distortion when using considers that the permanent elongation rate of fiber of the present invention is preferably more than 5~30% or 30%, permanent elongation rate more preferably 5~15%.The numerical value that herein permanent elongation rate adopts the method according to following embodiment D. item to record.
Can resist when using magnetic field and consider aspect the big stress of moment, the initial stage tensile elasticity rate of fiber of the present invention is preferably 15cN/dtex or more than the 15cN/dtex, is preferably 20cN/dtex especially or more than the 20cN/dtex.The initial stage tensile elasticity rate is high more preferred more, preferably uses the following fiber of 1000cN/dtex or 1000cN/dtex.Herein, this tensile elasticity rate adopts the numerical value that the method according to following embodiment D. item records at initial stage.
In order to make fiber of the present invention in various uses, all stably satisfy shape or characteristic, its fracture strength is preferably 0.3cN/dtex or more than the 0.3cN/dtex, its fracture strength is 0.5cN/dtex or more than the 0.5cN/dtex more preferably, more preferably 1.0cN/dtex or more than the 1.0cN/dtex.Fracture strength is high more preferred more, preferably uses the following fiber of 25cN/dtex or 25cN/dtex.Herein, this fracture strength adopts the numerical value that the method according to following embodiment D. item records.
Can be by the ratio resistance value of the content controlling fiber of the spherical magnetic material that contains in the fiber of the present invention itself.Therefore, can suitably set this according to purposes or purpose and compare resistance value.In addition, in order to guarantee the fibrous physical property that above-mentioned permanent elongation rate or fracture strength etc. are stable or when following purposes for example is assembled in the electric photographic apparatus, can to keep considering that the ratio resistance value of fiber of the present invention is preferably 10 aspect the stable conductive characteristic
2~10
9Ω cm is than resistance value more preferably 10
3~10
9Ω cm.Herein, this numerical value that can adopt the method according to following embodiment G. item to record than resistance value.
Illustrate the preferable production process of fiber of the present invention below.
Fiber of the present invention can adopt the spinning process of various synthetic fiber such as solvent spinning such as melt spinning, dry spinning, wet type spinning and dry-and wet-type spinning to make.For example, when stating the polyacrylonitrile base polymer in the use, can adopt solvent spinning, in addition, owing to can easily make fiber middle and high concentration ground contain spherical magnetic material, and controlling fiber shape critically, so also preferably make by melt spinning.Fiber of the present invention can carry out melt spinning separately and make by the component of polymer that will contain spherical magnetic material.In addition, fiber of the present invention also can be used as above-mentioned composite fibre and makes.Particularly; make high concentration ground contain the composition fusion separately respectively of magnetospheric composition with the protective layer that does not contain or contain on a small quantity spherical magnetic material of spherical magnetic material; in the stage before the ejection of tube head hole; obtain magnetosphere and form core/protective layer and form the compound melt spinning of the core sheath of sheath or obtain magnetosphere and form the compound melt spinning in island that island/protective layer forms the sea, from tube head ejection fiber.
The fiber of ejection is cooled to vitrification point (Tg) or the following temperature of this temperature, after making it adhere to finishing agent as required, the draw rate of dividing with 100~10000m/, be preferably that 4000m/ divides or 4000m/ divide following, more preferably 3000m/ divide or 3000m/ divide following, more preferably 2500m/ divide or 2500m/ divide following, be preferably that 2000m/ divides or 2000m/ divides following draw rate to carry out tractive especially.In addition, consider productivity ratio, divide above draw rate to carry out tractive with 50m/ branch or 50m/.Herein, the bar number (the ribbon number of strand) of a bundle fiber that sprays from the tube head hole is as long as suitably select according to using method or purposes as purpose.Fiber can be 1 monofilament state, also can be the multifilament of the formation of the multifibres bar below 3000 or 3000.Consider that from obtaining the stable fiber aspect of each rerum natura the bar number of a bundle fiber is preferably 4~500, is preferably 6~150 especially.In addition, the finishing agent that adheres to can suitably be selected to use according to the purposes of fiber.As finishing agent, can use the finishing agent of the property of water-bearing or the non-property of water-bearing, in order to prevent spherical magnetic material generation deterioration, preferred non-property of water-bearing finishing agent.
Behind the tractive fibre bundle, in a single day after not batching or batching, be heated to the vitrification point (Tg)+100 ℃ or the following temperature of this temperature of the polymer that constitutes fiber, more preferably be heated to the temperature range of vitrification point Tg-20 ℃~Tg+80 ℃, with the permanent elongation rate of drawn yarn reach 5~30% multiplying power, the permanent elongation rate that is preferably drawn yarn reaches 5~15% multiplying power and stretches.Herein, for the fiber that has carried out spinning, preferably be heated to the following temperature of the vitrification point (Tga)+100 ℃ that constitutes magnetospheric polymer or this temperature, more preferably constitute in the temperature range of vitrification point Tga-20 ℃ of magnetospheric polymer~Tga+80 ℃, stretch.In addition, in case the 2nd section stretching can be carried out with the multiplying power more than 1 times or 1 times, below 2 times or 2 times again in the back (after promptly the 1st section stretching finished) that stretches.
After the stretching, preferably fiber is heat-treated under Tg+10 ℃ or this more than temperature, fusing point (Tm) or the temperature below the fusing point (Tm), heat-treat particularly preferably under Tg+50 ℃ or this more than temperature, Tm-10 ℃ or this temperature below temperature.By after stretching, heat-treating, can make more fiber with excellent of heat resistance in high temperature.For the fiber that obtains herein; preferably constituting vitrification point Tga+10 ℃ of magnetospheric polymer or this more than temperature, constituting under the fusing point (Tmb) of polymer of protective layer or this temperature temperature below and heat-treat, heat-treating under, Tmb above or the temperature below the Tmb particularly preferably in the fusing point (Tma) that constitutes magnetospheric polymer or this temperature.
As above-mentioned drawing process or the heat treatment method after stretching, for example can use the direct contact heaters such as spicule, roll and plate object after the heating.In addition, also can adopt contact heat treatment groove that uses the liquid after heating or the contactless heat medium that uses heated air, heating steam and electromagnetic wave etc. etc.Because device is easy, the efficiency of heating surface is high, therefore preferred direct contact heater and contact heat treatment groove, the roll after the preferred especially heating.
Fiber of the present invention goes for fabric, braided fabric and nonwoven fabric and so on cloth and silk.And fiber of the present invention also can have been implemented the fiber of false twisting processing when being used for various dress material purposes.In the false twisting manufacturing procedure, the following processing of fiber: do not heat drawn yarn or undrawn yarn, or after heating with spicule, roll, plate object or non-contact type heater etc. after the heating, implement false twisting processing with pan or ribbon.Fiber after the draw false twisting processing is directly preferred or after further heating, batches.
The single fiber diameter of fiber of the present invention is not particularly limited, consider from can comprising to high concentration spherical magnetic material and can be used in the various uses aspect, single fiber diameter is preferably 1000 μ m or below the 1000 μ m, more preferably 0.1~100 μ m, more preferably 0.5~50 μ m.In addition, when being assembled into following brush roll in the Charging system, consider that from having good chargeding performance aspect fibre diameter of the present invention is preferably 0.5~10 μ m.
In addition, the section configuration of fiber also is not particularly limited, and in order to have the uniform fibers rerum natura, is preferably circle.In addition, according to the purposes or the purpose that fiber are installed to the enterprising enforcement usefulness of brush roll with the shape of staple fibre or fabric or braided fabric or nonwoven fabric, for example make the bending direction of fiber have anisotropy, or when in electric photographic apparatus, obtaining good contact with toner, section configuration preferred flat type, polygon, Multiblade, hollow type or unsetting type etc.
Fiber of the present invention can keep additives such as delustering agent, incombustible agent, lubricant, antioxidant, ultra-violet absorber, infrared absorbent, nucleating agent, fluorescent whitening agent and end-capping reagent on a small quantity in the scope that does not influence the invention main idea.In addition, when fiber of the present invention is made composite fibre, also can keep above-mentioned additive in the arbitrary layer in magnetosphere and/or protective layer.And fiber of the present invention also can contain other magnetic materials or conductive material in the scope that does not influence main idea of the present invention and other necessary fibrous physical properties.Herein, as other conductive materials, can enumerate than resistance value be 10000 Ω cm or below the 10000 Ω cm, 1n Ω cm or conductive carbon black more than the 1n Ω cm or metal etc.
Fiber of the present invention is according to employed purposes or shape, can be constituted to small part or all use the fabric of above-mentioned fiber.In the fabric, for example as woven, can enumerate wide cloth, organdy, lawn, apron cloth, top-weight fabric, taffeta, shantung, plain clothes such as crepe de Chine, COARSE DRILL cloth, sound of a bird chirping gurgles, TWILL CLOTH such as gabardine, the silk weaving satin, SATIN AND SATEEN CLOTH such as doeskin, basket weave, panama, the delustring fabric, hopsack, hopsacks such as OXFORD, faille, ottoman, heavy flat fabric such as the dimity, France's twill, Wei Libang, upright twills such as brokentwlllweave, reclining twill, reverse twill, brokentwlllweave, skip twills, the curve twill, the twill of adoring, or irregular satin weave, strengthen satin weave, elongate satin weave, checked satin tissue, or honeycomb weave, small neat weave, crepe weaves and Buddhist nun Agra etc.In addition, as the two-layer fabric that 2 fabrics and synthetic 1 fabric are formed, can enumerate pique, relief fabric etc. through double-layered structure, latitude bilayers such as Bei Defude bedford cord are knitted, and double-side different color pattern fabric and bag are knitted longitude and latitude bilayer such as tissue and knitted etc.In addition,, can enumerate Velveteen head tissues such as velveteen or CORDUROY as fleece, or towel, velvet, through suede etc. through pile weave construction etc.In addition, can also enumerate LENO AND GAUZE such as lace stitch or eyelet stitch, or jacquard fabrics such as multi-arm fancies or figured texture weave etc., particularly as being used for the fiber of brush roll, preferred fleece with fabric.The fiber of the present invention that uses in order to make fabric can be raw silk, boiled-off silk and finished yarn etc., and in addition, fiber form can be long fiber (long filament), also can be staple fibre (staple fibre).
In addition, fiber of the present invention can be according to the purposes that can use or shape, and part or all uses the braided fabric of above-mentioned fiber at least in formation.As braided fabric, can enumerate plain stitchs such as heavy sizing plain cloth or single fabric, rib stitch such as ribbed knitting or round ribbed knitting, purl stitchs such as concavo-convex tissue, in addition, can also enumerate weft-knitted fabrics such as deer point decorative pattern, crepe weaves, concertina rivel tissue, little pattern, petinet ocular tissue, back side napping braiding, sheet full cardigan tissue, full cardigan tissue, ripple flimsy material, Milan promise rib stitch, compound pique.In addition, as braided fabric, can enumerate tricot such as the thin and Milanese of tricot, Russell's twill etc.Particularly as brush roll with the braided fabric that uses in the braided fabric, preferred back side napping braiding or implement to make pile shape fiber to give prominence to and handle the braided fabric that obtains in the napping of textile surface.The fiber of the present invention that uses in order to make braided fabric can be raw silk, boiled-off silk and finished yarn etc., and in addition, fiber form can be long fiber (long filament), also can be staple fibre (staple fibre).
Fiber of the present invention can be according to the purposes that can use or shape, and part or all uses the nonwoven fabric of above-mentioned fiber at least in formation.As nonwoven fabric, can enumerate the nonwoven fabric that joints such as utilizing chemical adhesion method, heat viscosity method, needle point method, water spray punching (water acupuncture manipulation) method, throw a spear Method for bonding and felt method or adhering method form.The fiber of the present invention that uses in order to make nonwoven fabric can be raw silk, boiled-off silk and finished yarn etc., and in addition, fiber form can be long fiber (long filament), also can be staple fibre (staple fibre).
In the present invention, fabric or braided fabric also can adopt conventional method to implement processing such as concise, dyeing and heat setting.In addition, nonwoven fabric also can be implemented physical property processed such as glazing pressurization, embossing pressurization, compression process, soft processing and heat setting.Nonwoven fabric also can be implemented chemical processed such as bonding processing, lamination process, lining processing, antifouling processing, waterproof processing, anti-charged processing, fire prevention processing, moth resistant finish, health processing and bubble resin finishing, in addition, can also implement microwave applications, ultrasonic application, far infrared application, UV application and low temperature plasma application etc. and use processing.
In addition, in the present invention, fabric, braided fabric or nonwoven fabric also can be used fiber of the present invention and other synthetic fiber, semisynthetic fibre and the natural fabric etc. that are different from fiber of the present invention with.For example, also can and use at least a kind of fiber that is selected from cellulosic fibre, wool, thin,tough silk, drawing of fiber and the acetate fibre in fiber of the present invention.As cellulosic fibre, can enumerate natural fabrics such as cotton, fiber crops, not contain cuprammonium wool, wool and the viscose silk etc. of spherical magnetic material of the present invention.The electric conductivity that requires for the style that obtains cellulose fibre, hygroscopicity, water imbibition, antistatic behaviour etc. and fiber of the present invention or according to the magnetic field responsiveness of purposes needs, with the containing ratio of above-mentioned cellulose fiber blended fiber of the present invention preferably in 0.1~50% scope.In addition, use middle wool or the thin,tough silk that uses with and can directly use current material.For the electric conductivity of style, harsh feeling and the fiber of the present invention of the style that obtains wool, warm degree, bulking intensity, thin,tough silk or according to the magnetic field responsiveness of purposes needs, the containing ratio of the fiber of using with above-mentioned wool or thin,tough silk of the present invention is preferably in 0.1~50% scope.In addition, as the drawing of fiber of using with, can enumerate the polyurethane fiber, polybutylene terephthalate (PBT) fiber or the polytetramethylene glycol copolymerization polybutylene terephthalate (PBT) fiber that form with dry spinning or melt spinning is polyesters elastic yarn of representative etc.In the blended fabric that uses drawing of fiber, the containing ratio of fiber of the present invention is preferably about 0.1~50%.In addition, the acetate fibre that uses in using with can be diacetate fibre, also can be triacetate.For the electric conductivity of the style, distinctiveness, gloss and the fiber of the present invention that obtain acetate fibre or according to the magnetic field responsiveness of purposes needs, the containing ratio of the fiber of using with above-mentioned acetate fibre of the present invention is preferably 0.1~50% scope.
In above-mentioned various fabrics, braided fabric and nonwoven fabric, as the method for using with of the fiber of the present invention that uses, for example can enumerate fiber of the present invention as braided fabrics such as fabric such as the MIXED FABRIC of warp thread or weft yarn or reversible cloth or tricot or Russell's twill are thin etc.Fiber of the present invention also can be handed over sth. made by twisting, doubling with other fibers or interweave.
At least partly or entirely use the cloth and silks such as fabric, braided fabric or nonwoven fabric of fiber of the present invention also to comprise the above-mentioned cloth and silk of using with, also can dye.For example, can adopt following process: knitting, when weaving the back or adopting nonwoven fabric, form fiber web, adopt above-mentioned joint or adhering method to form after, adopt conventional method to carry out concise, preboarding, dyeing and finalization.In addition, when fiber of the present invention is formed by polyester polymer, also can before concise back and dyeing, adopt conventional method to carry out the acrylic acid decrement treatment as required.Concisely preferably in 40~98 ℃ temperature range, carry out.When particularly using fiber of the present invention and drawing of fiber with obtain cloth and silk, it is concise that preferred limit is carried out the cloth and silk slack side, can improve elasticity.Heat setting before and after the dyeing can omit a side or two sides omit, and for morphological stability and the dyeability that improves cloth and silk, all carries out heat setting before and after the preferred dyeing.The temperature of heat setting preferably in 120~190 ℃ scope, 140~180 ℃ scope more preferably.In addition, thermo setting time is preferably 10 seconds~5 minutes scope, more preferably 20 seconds~3 minutes scope.
Fiber of the present invention has good magnetic field responsiveness or electric conductivity, so fiber itself also is very useful, can directly use fiber.In addition, fiber of the present invention is as a form of fiber, and as mentioned above, preferably the staple fibre as 0.05~150mm length uses.The following formation of staple fibre: long filament is formed the fibre bundle that 1 independent strand or a plurality of strand bunchy obtain, its cut-out is formed staple fibre.Particularly for example bonding and flocking forms the flocking thing to the staple fibre of 0.1~10mm length in substrate with it by diversified methods such as electric flocking processing or blowing processing.Process the roughly erectility that is become 10 degree angles~vertical (i.e. 90 degree) more than 50% or 50% by bonding one-tenth with substrate of the staple fibre of flocking through electric flocking.Herein, in the scope that does not influence the invention main idea, the staple fibre that uses when forming this flocking thing also can be used the staple fibre that is made of other fibers that are not fiber of the present invention with and carry out flocking except the staple fibre that is made of fiber of the present invention.In addition, in the flocking thing, in substrate, during bonding and flocking staple fibre, for example preferably use acrylic compounds, carbamates or ester class bonding agent.The thickness of bond layer is preferably 1~500 μ m, can be for individual layer or mix multiple bonding agent as required or be divided into multilayer and use.
In addition, the substrate of flocking staple fibre can suitably be selected according to the device of assembling flocking thing or the bonding agent that uses or the intensity in magnetic field.As substrate, can enumerate film, sheet material, paper, plate and the cloth and silk etc. that constitute by synthetic resin, natural resin, synthetic fiber, natural fabric, timber, mineral or metal.Or will also use as the metal processome of the member of various uses itself, synthetic or natural resin processome or formed body as substrate.Particularly in order to improve the compatibility with above-mentioned bonding agent, the preferred sheet material that constitutes by synthesizing of forming through hydrophilicity-imparting treatment or natural resin or metal that uses.When the positive and negative of substrate is formed by above-mentioned film, sheet material, paper, plate and cloth and silk etc., can carry out flocking on the two sides of its surface and reverse side according to purposes or purpose.
Because the flocking thing for example has electric conductivity, therefore be preferably used as electrostatic brush.
Use fibroplastic fabric of the present invention, braided fabric or nonwoven fabric to be bonded in to small part and form the cloth and silk complex in the substrate.At this moment, if adopt fabric, then preferred fleece thing or the treated fabric that makes fabric face have pile or loose thread.In addition, if adopt braided fabric, then preferably there is the braided fabric of pile shape fiber napping or makes pile or loose thread be present in the braided fabric of textile surface through the napping processing.Use the cloth and silk complex of above-mentioned fabrics, braided fabric to be preferred for brushing purposes.
When being bonded in fabric, braided fabric or nonwoven fabric in the substrate, for example can use acrylic compounds, carbamates and ester class bonding agent.The thickness of bond layer is preferably 1~500 μ m.Bonding agent can be individual layer, or mixes multiple bonding agent as required, maybe can be divided into multilayer and use.In addition, bonding substrate can suitably be selected according to the device that is assembled with this cloth and silk complex, employed bonding agent or magnetic field intensity.As substrate, preferred film, sheet material, paper, plate and the cloth and silk etc. that constitute by synthetic resin, natural resin, synthetic fiber, natural fabric, timber, mineral or metal that adopt.Or will be as the metal processome of the member of various uses itself, synthetic or natural resin processome or formed body as substrate.Particularly in order to improve the compatibility with above-mentioned bonding agent, the sheet material that substrate preferably is made of synthetic or natural resin that forms through hydrophilicity-imparting treatment or metal.When substrate forms positive and negative as film, sheet material, paper, plate and cloth and silk etc., can be according to purposes or purpose, bonding above-mentioned fabrics, braided fabric or nonwoven fabric form the cloth and silk complex on the two sides of its front and reverse side.
Using method or purposes as the cloth and silk complex can be preferably used as electrostatic brush.
Can at least partly or entirely use fiber of the present invention to form dress material.When forming dress material, because excellent conductivity, the static that produces in the time of therefore can suppressing winter or drying can be made more comfortable, satisfied dress material.In addition, excellent conductivity is difficult for the absorption dust, the dustproof dress materials such as Work Clothes when therefore being preferably used as the manufacturing of operation dress or semiconductor.At this moment, preferably every several of fiber of the present invention is used as warp thread and/or weft yarn together.In addition, as its secondary effect, owing to contain spherical magnetic material, so the thermal conductivity of fiber is improved.Therefore, can be when wearing the clothes the contact coldness raw material of transient absorption heat or winter enter the warm temperature sense raw material that health basks at once when indoor etc. from cold outdoor.
Can with use the fabric of fiber of the present invention and/or braided fabric and/or nonwoven fabric be bonded at least a portion of bar-shaped object or all on, form brush roll.At this moment, if adopt fabric, then preferably use fleece or the treated fabric that has napping or loose thread at fabric face.In addition, if adopt braided fabric, then preferably use the braided fabric that there is the napping of pile shape fiber or handle and make pile or loose thread be present in the braided fabric of textile surface through napping.The bar-shaped object of bonding above-mentioned fabrics, braided fabric is specially adapted to brush purposes.
When being bonded in the fabric that uses and/or braided fabric and/or nonwoven fabric on the bar-shaped object herein, to cut off the material webs that obtains by the necessary length of the function of bar-shaped object (width of promptly reeling) carries out bonding around a week, or helically is reeled and to be cut into the number that width is the club body length/one~tens of/one's slot-shaped material on bar-shaped object, carries out bonding.As the bonding agent that uses herein, can suitably select according to purposes or the purpose used, for example can adopt various bonding agents such as acrylic compounds, ester class or carbamates.In addition, also can add electric conductivity controlling agents such as conductive carbon black or metal as required in the bonding agent, or the magnetic controlling agent of the oxide of metal such as iron, nickel, cobalt, molybdenum or above-mentioned metal or said mixture etc. etc.The thickness of bond layer is preferably 1~500 μ m.Bonding agent can be individual layer, or mixes multiple bonding agent as required, or also can be divided into the multilayer use.And in fabric and/or braided fabric and/or the nonwoven fabric stage before bonding, can fit on bonding plane has 10
2~10
10The conductive processing agent layer or the raw materials such as conductive sheet or conductive film of the ratio resistance of Ω cm.
Above-mentioned staple fibre of the present invention can be bonded at least a portion of bar-shaped object or all on, form staple fibre by the brush roll of flocking on bar-shaped object.The staple fibre of Shi Yonging is when bonding and flocking is on bar-shaped object herein, can utilize gas that staple fibre is blown, perhaps also can carry out electric flocking processing, owing to can obtain roughly upright pile effectively in bar-shaped object surfaces, flocking is carried out in the electric flocking processing of therefore preferred employing.Staple fibre is bonded in bar-shaped object surfaces by the roughly erectility with 10 degree~vertical (i.e. 90 degree) more than 50% or 50% at this moment.Herein, in the scope that does not influence the invention main idea, except the staple fibre that constitutes by fiber of the present invention, also can use the staple fibre that constitutes by other fibers that are not fiber of the present invention with and carry out flocking.In addition, as bonding agent, for example can select to use various bonding agents such as acrylic compounds, carbamates or ester class according to purposes or purpose.The thickness of bond layer is preferably 1~500 μ m.Bonding agent can be individual layer, or mixes multiple bonding agent as required, perhaps also can be divided into multilayer and use.In addition, ratio resistance value staple fibre of the present invention is bonding and the brush roll itself that flocking forms at least a portion of bar-shaped object is preferably 10
2~10
11Ω cm.
As the main material of the core of above-mentioned bar-shaped object,, can enumerate metal, synthetic resin, natural resin, timber and mineral etc. as long as adopt suitable material according to use or purpose.Above-mentioned material may be used alone, and can also use a variety of combinations.When being used as the member that is installed in the electric photographic apparatus, the bar-shaped object that preferred core mainly is made of metal.And, when bar-shaped object is metal, preferably at least a portion of metal or must the whole surface of part on the intermediate layer that is covered, bonding thereon above-mentioned fabrics and/or braided fabric and/or nonwoven fabric, or bonding and flocking staple fibre.The raw material that uses as its intermediate layer mainly act as gives bar-shaped object with resiliency, or in the time only can't being realized by the resilient stiff of brush shape fiber, provides resilient stiff complementaryly.By adopting above-mentioned formation, the toner that can further improve clearing apparatus is removed the toner of performance or developing apparatus and is given performance.Carbamates raw material, elastomer raw material, rubber raw materials or ethylene-vinyl alcohol-based raw material etc. are for example preferably used in this intermediate layer.The thickness in intermediate layer is preferably 0.05~10mm.The intermediate layer can further be contained above-mentioned electric conductivity controlling agent or magnetic controlling agent as required.
Use the above-mentioned brush roll of above-mentioned fabrics of the present invention and/or braided fabric and/or nonwoven fabric to have magnetic field responsiveness or the electric conductivity that derives from fiber itself of the present invention to small part, be fit to be installed in the clearing apparatus and use.The ratio resistance value that is installed to the brush roll itself in this clearing apparatus herein is preferably 10
2~10
7Ω cm is than resistance value more preferably 10
3~10
7Ω cm.In the clearing apparatus, the limit rotates this brush roll, and then the limit applies electricity or applies magnetic field if desired, and the limit is caught also and removed unwanted material, makes than resistance value in above-mentioned scope, can make to remove performance and become better.This clearing apparatus of electric photographic apparatus is removed toner as unwanted material from photoreceptor.When electric or magnetic is removed toner, even under the situations such as the environment change in electric photographic apparatus, particularly humidity change, the electric conductivity of brush roll or low-down coercive force also are stable.This is because brush roll uses the fiber that contains spherical magnetic material.That is, brush roll has stable performance of removing toner from photoreceptor usually, is very good clearing apparatus.In addition, as the using method of brush roll in clearing apparatus, except brush roll is directly contacted photoreceptor cleans, the also brush roll that cleans with the member of the cleaning photoreceptor of opposing (as mentioned above for brush roll or as the doctor-like member of prior art).That is,, or be used as the brush roll that the unwanted toner that will reclaim is transplanted on other positions with the member of doing clearing apparatus itself is cleaned.At this moment, the result can access more high performance clearing apparatus.In addition, can use the brush roll of 1 basic invention in the clearing apparatus of the present invention, perhaps also can use many brush rolls more than 2 or 2.
With above-mentioned fabrics of the present invention and/or braided fabric and/or nonwoven fabric be used at least a portion, with its be bonded in the brush roll that forms on the bar-shaped object or with above-mentioned staple fibre be used at least a portion, brush roll it is bonding and that flocking forms on bar-shaped object has the electric conductivity that derives from fiber itself of the present invention, be fit to be assembled in the Charging system that can be used in electric photographic apparatus and use.The ratio resistance value that is assembled into the brush roll in the Charging system is preferably 10
5~10
10Ω cm, more preferably 10
6~10
9Ω cm.The Charging system that uses above-mentioned brush roll to form is used to control the electric conductivity (than resistance value) of brush roll itself.
At this moment, this brush roll can make the photoreceptor uniform charged.And, above-mentioned environment change takes place in electric photographic apparatus, for example change lentamente or because of seasonal variations causes humidity in the running of electric photographic apparatus, above-mentioned humidity is changed, and the ratio resistance value of using in the brush roll of having added the fiber of spherical magnetic material of the present invention does not change or changes very little.Therefore, be not prone to the charged spot of photoreceptor, the result can form very good Charging system by using this brush roll.
And, existing when cleaning insufficient and residual toner at the photosensitive surface of this electric photographic apparatus, this brush roll also can the double as cleaning roller.Therefore, do not take place or take place to develop hardly or the pollution during printing.And, during with the electric photographic apparatus miniaturization, above-mentioned clearing apparatus and Charging system needn't be set separately, used as the clearing apparatus Charging system of holding concurrently, can realize the purpose of save spaceization.In addition, can use 1, many above-mentioned brush rolls more than 2 or 2 in the Charging system of the present invention.
With above-mentioned fabrics of the present invention and/or braided fabric and/or nonwoven fabric be used at least a portion, be bonded in the brush roll that forms on the bar-shaped object or with above-mentioned staple fibre be used at least a portion, brush roll bonding and that flocking forms on bar-shaped object has magnetic field responsiveness or the electric conductivity that derives from fiber itself of the present invention, be fit to be assembled in the developing apparatus and use.The image developmentization that developing apparatus will be described by laser by the photosensitive surface of above-mentioned Charging system uniform charged in electric photographic apparatus.As mentioned above, even exist humidity to change in the electric photographic apparatus, also do not occur or occur hardly brush roll itself than resistance value spot or magnetic field responsiveness spot, therefore the toner that is used for development can be offered equably photoreceptor develops, development thing that obtains or printed article are pollution-free or do not have or almost do not print spot, and be very attractive in appearance.Particularly toner be magnetic color tuner or contain metallic carrier contain the carrier toner time, developing apparatus of the present invention is very effective.
With above-mentioned fabrics of the present invention and/or braided fabric and/or nonwoven fabric be used at least a portion, be bonded in the brush roll that forms on the bar-shaped object or with above-mentioned staple fibre be used at least a portion, brush roll bonding and that flocking forms on bar-shaped object has the electric conductivity that derives from fiber itself of the present invention, be fit to be assembled in the discharge system that can in electric photographic apparatus, use use.Discharge system can show the very good electrical property that disappears by the electric conductivity (than resistance value) that reduces brush roll.Therefore, the ratio resistance value of brush roll is preferably 10
2~10
7Ω cm.When particularly brush roll of the present invention being used for electric photographic apparatus, the countless fibers on brush roll surface show stable and the electric effect that disappears uniformly.And, can improve the cleaning effect that is provided in the above-mentioned clearing apparatus behind the discharge system usually.In addition, when dwindling electric photographic apparatus, brush roll of the present invention can be assembled into wherein as the discharge system clearing apparatus of holding concurrently.
As the electric photographic apparatus that uses above-mentioned clearing apparatus of the present invention and/or Charging system and/or developing apparatus and/or discharge system to form, particularly can enumerate laser beam monochrome printers, laser beam color printer, one-color copier, color copy machine, monochrome or colour facsimile apparatus, Mobyneb compounding machine and word processor etc.Based on charged photoreceptor with laser is drawn sub-image, the mechanism of using toner to develop is developed or printed device, as mentioned above, owing to use fiber of the present invention, therefore, also can have the charged development of the stable cleaning electrical property that disappears even the environmental change in the electric photographic apparatus, particularly humidity change.Therefore, printing that obtains or development thing from needless to say, when using multiple toner colored in a large number, also can access goods attractive in appearance especially when monochromatic.In addition, the optimizations such as content of fibre length by making above-mentioned brush roll or the spherical magnetic material that contains can be given the charged development of the more stable cleaning electrical property that disappears.Therefore, the actuating speed of electric photographic apparatus be can further improve, that is, printing or developing powder (number) in the time per unit improved.In addition, use fibroplastic electric photographic apparatus of the present invention, as mentioned above, can realize more miniaturization, save spaceization and economize electrification.
Below, by embodiment, illustrate in greater detail the present invention, but the present invention is not limited to following embodiment.Physics value among the embodiment is measured by following method.
Embodiment
A. the mensuration of melt viscosity
Use the Capirograph 1B of (Co., Ltd.) Japan smart machine society system, in nitrogen atmosphere, diameter of cylinder is that 9.55mm, nozzle length are that 10mm, nozzle inside diameter are under the condition of 1mm, with 10sec
-1Shear rate measure melt viscosity.With the mean value of 5 measured values measured value as melt viscosity.For minute, in order to prevent the sample deterioration, be determined at 30 minutes with interior end 5 times.
B. the mensuration of vitrification point (Tg) and fusing point (Tm)
Utilize the differential scanning calorimetric analysis device (DSC-2) of PerkinElmer society system, use sample 10mg, with 16 ℃/minute determination of heating rate Tm and Tg.Tm and Tg are defined as follows described.At first observe the endothermic peak temperature (Tm that observes when once measuring with 16 ℃/minute programming rate
1) after, at about (Tm
1+ 20) ℃ temperature kept 5 minutes.Quenching (quenching time and room temperature retention time amount to 5 minutes), is measured with 16 ℃/minute intensification condition to room temperature again then.At this moment, the endothermic peak temperature that observes with the skew as stepped baseline is Tg, and the endothermic peak temperature that observes with the fusion temperature as crystallization is Tm.
C. the affirmation of the average grain diameter of spherical magnetic material and shape
Use the scanning electron microscope E SEM-2700 of (strain) Nikon society system,, sample is carried out platinum-palladium evaporation (evaporation mould: 25~50 dusts) after the processing, confirm average grain diameter and shape with any multiplying power of 200~100000 times with the accelerating potential of 5kV.For average grain diameter and shape, digital filming is observed photo, to calculate the average area value of particle as the WinROOF (version 2 .3) of three paddy business society systems of computer software, be judged as slightly circularly again by this average area value, calculate the average grain diameter of spherical magnetic material.In addition, for 50 in the photo spherical magnetic material particles, maximum gauge (R) and minimum diameter (r) that 1 particle is judged in range estimation carry out instrumentation, by its ratio (R/r) calculating circularity, circularity be below 1.5 or 1.5 be judged as spherical.
D. the mensuration of the initial stage tensile elasticity rate of fiber, permanent elongation rate and fracture strength
Use the tension force stretching testing machine (TENSIRON UCT-100) of Orientec society system.For undrawn yarn, with the initial stage specimen length is that 50mm, draw speed are the condition that 400mm/ divides, and for drawn yarn, is that 200mm, draw speed are the condition that 200mm/ divides with the initial stage specimen length, measure intensity and permanent elongation rate respectively, with the mean value measured for 5 times as separately measured value.
E.98 the calculating of 15 minutes shrinkage factor (boiling water shrinkage) in ℃ boiling water
To tie up the bundle that forms by the wheel of the long drawn yarn of 5 1m and fix, measure the length L 1 (the about 500mm of length this moment) of bundle with 1 clip.Then, it is in 98 ℃ the boiling water that this bundle slowly is impregnated into temperature, leave standstill 15 minutes after, take out, air-dry more than 1 hour or 1 hour.After air-dry, measure the length L 2 of bundle again.Shrinkage factor (%) is calculated by following formula.
Shrinkage factor (%)=(L1-L2) ÷ L1 * 100
F. overall merit
Estimate at magnetic field responsiveness, heat resistance, spherical magnetic material miscibility and such 4 of carrying out property of operation.
At first, for magnetic field responsiveness, the staple fibre 5g that fiber of the present invention is cut into the formation of 5mm length puts into vinyl bag.Co., Ltd. two or six is made made neodium magnet (model NE011 (size: external diameter φ 30mm, height 15mm), material N40, surface magnetic flux density 490 milli teslas) near above-mentioned staple fibre 1 minute, make its magnetization after, remove neodium magnet.Make this staple fibre near the metal part of electromagnet of energising not, confirm staple fibre whether be magnetized (becoming magnet).The staple fibre that is not magnetized is double-deck circle ◎ (good), and the staple fibre that is magnetized is △ (poor).
For heat resistance, during the boiling water shrinkage less than 5% of above-mentioned E. item for double-deck circle ◎ (good), more than 5% or 5%, less than 10% be that zero (well), 10% or 10% is △ (poor) when above.
For spherical magnetic material miscibility, the undrawn yarn that is obtained by spinning is freezed in liquid nitrogen, after directly bending makes its fracture (fiber breaks and broken string occurs), observe the plane of disruption, observe the state of aggregation of spherical magnetic material with the scanning electron microscope of above-mentioned C. item.For state of aggregation, spherical magnetic material particle contacts and promptly is judged as aggegation more than 5 or 5.Observe with each sightingpiston at a distance of 1m or above any 5 sections of 1m, in each section average observation to 10 places or be △ (poor) during the above aggegation in 10 places, have less than 10 places aggegation or do not exist the aggegation markers to be designated as double-deck round ◎ (good).
For carrying out property of operation, with the naked eye judge to fiber of the present invention cut off add man-hour cutter or operation in the wearing and tearing of guide plate.The 1kg fiber being cut off when adding man-hour and observing wearing and tearing in operation is carried out is △ (poor), when the 10kg fiber that surpasses 1kg is cut off processing and operation and can be observed wearing and tearing in carrying out is zero (well), is two bicircular ◎ (good) when also not observing guide plate in cutter or the operation when fiber surpasses 10kg and wearing and tearing.
For above-mentioned 4 assessment items, as long as there have 1 evaluation that obtains △ to be to be defective, the evaluation that does not obtain △ entirely is then for qualified.Among particularly qualified, all be " excellent " of double-deck circle ◎, have zero evaluation then to be " very ".
G. the assay method of the ratio resistance value of fiber and brush roll
The atmosphere of measuring is 23 ℃ of temperature, humidity 55% (below be sometimes referred to as usual conditions).The sample that needs are measured keeps 1 hour at least in said determination atmosphere after, measure and compare resistance value.At first, adopt under the situation of fiber, the length of fiber is 100mm or 100mm when above, and making fibre bundle is the bundle of 1000dtex, cuts into the length of 50mm, measures in the end face installing electrodes.In addition, during the curtailment 100mm of fiber, on two end faces of length 10cm (A), width 2cm, degree of depth 1cm, A, have in the insulator container of electrode, with 5kg/cm
2The pressure fiberfill fibers, after the sealing, measure, be converted into the ratio resistance value of every fibre single thread, obtain and compare resistance value.
Under the situation of brush roll, pressure is given as security in the loading that the metallic plate with brush roll ground connection is applied 500g, under this state, applies the voltage of 1kV between end of bar-shaped object and metallic plate.Measure the electric current I (μ A) that flows through this moment, obtain 1/I, as the ratio resistance value of brush roll.In addition, atmospheric condition during ratio resistance value when measuring humidity and changing except above-mentioned usual conditions, respectively temperature be 28 ℃, humidity be 85% (hot and humid degree condition), and temperature be that 10 ℃, humidity are to measure under such 3 temperature and humidity conditions of 15% (low temperature and low humidity degree condition) to obtain.
H. the mensuration of the electric conductivity of spherical magnetic material
Press JIS C 2525, under 23 ℃ temperature, measure.Particularly, use spherical magnetic material fusion, the thickness that obtains of annealing are 10mm, length 3 test films as 500mm as 0.5mm, width.Obtain the ratio resistance value (specific insulation) of 3 test films respectively, with the mean value of 3 measured values obtaining ratio resistance value as above-mentioned spherical magnetic material.
I. the mensuration of the coercive force of spherical magnetic material and saturation flux density
Press JIS C 2504, with above-mentioned H. similarly with spherical magnetic material fusion, annealing, making external diameter is that 45mm, internal diameter are that 33mm, thickness are the ring of the circular cross section of 1mm, makes 3 altogether, obtains saturation flux density and coercive force respectively.With the mean value of 3 measured values obtaining saturation flux density and coercive force as above-mentioned spherical magnetic material.
J. the purity testing of spherical magnetic material
As spherical magnetic material, use pure iron, pure nickel, following the carrying out of purity testing during material that single metal such as pure cobalt or pure molybdenum constitutes: with employed spherical magnetic material, concentration with 0.1 weight % is dissolved in hydrochloric acid and the nitric acid acid that respectively 1 equivalent mixes, to the Al beyond the element of employed spherical magnetic material, Si, Cr, Mn, Fe, Co, Ni, Cu, Zn, Mo, Pb induces coupled plasma (ICP) ICP Atomic Emission Spectrophotometer, obtain the concentration % in the spherical magnetic material, from 100%, deduct value that The above results obtains purity as spherical magnetic material.Use under the situation of multiple spherical magnetic material (mixture), or under the situation of employing as the spherical magnetic material of alloy, whole elements are carried out the ICP ICP Atomic Emission Spectrophotometer, calculate the ratio that respectively constitutes element.
K. the mensuration of the fibre length of staple fibre
To length is the loading that 20mm or the staple fibre more than the 20mm apply 0.1g/dtex, uses slide measure to measure.In addition,, use the SHADOW GRAPH Model 6 of NIPPONKOGAKU K.K system, measure the length of 50 staple fibres with 20 multiplying powers for the staple fibre of curtailment 20mm.With its mean value is fibre length.
Reference example 1 (having added the polyester of spherical magnetic material by mixing manufacturing)
Use 166 weight portion terephthalic acid (TPA)s and 75 weight portion ethylene glycol, utilize common esterification to obtain oligomer, in above-mentioned oligomer, add phosphoric acid 85% aqueous solution 0.03 weight portion respectively as the anti-coloring agent, as antimony trioxide 0.06 weight portion of polycondensation catalyst and as cobalt acetate tetrahydrate 0.06 weight portion of toner, carry out polycondensation reaction, obtain I V and be 0.70, melt viscosity is that 2050 pools (are measured 290 ℃ of temperature, 10sec
-1) the ball (pellet) of polyethylene terephthalate (hereinafter referred to as PET).
With the PET ball after carrying out vacuumize in 10 hours under 150 ℃ the temperature, use two-axis extruder (axial length L/ diameter of axle D=45), in the nitrogen atmosphere, iron (the pure element goods of iron purity 99.1% of interpolation/mixing (Co., Ltd.) high-purity chemical institute system in the PET of fusion, average grain diameter is the spherical powder (circularity is below 1.1 or 1.1 in the mensuration of above-mentioned C. item record) of 2.5 μ m, model is FEE 06PB), make in the mixture of the polyethylene terephthalate that obtains after mixing the finishing and iron, ferrous components is 10 weight %, 40 weight % or 60 weight %.Then, the gutstring (gut) of ejection with after the running water cooling, is cut with cutter, obtain containing 10 weight % iron respectively, melt viscosity is that 1890 pools (are measured 290 ℃ of temperature, 10sec
-1Down with) polyethylene terephthalate and the mixture of iron (below be designated as PET-Fe1) ball, containing 40 weight % iron, melt viscosity and be the polyethylene terephthalate of 1720 pools and the mixture of iron (below be designated as PET-Fe2) ball and containing 60 weight % iron, melt viscosity is the polyethylene terephthalate of 1580 pools and the mixture of iron (below be designated as PET-Fe3) ball.All there is no aggegation in the ball, mixing property is good.
Reference example 2 (having added the polyester of spherical magnetic material by the polymerization manufacturing)
Use 166 weight portion terephthalic acid (TPA)s and 75 weight portion ethylene glycol, utilize common esterification to obtain oligomer, in above-mentioned oligomer, as spherical magnetic material, interpolation is added the iron that uses in the reference example 1 to that to make its viscosity in the ethylene glycol be the ethylene glycol slurry of the pure iron that obtains of 10 weight %, in the polyethylene terephthalate that obtains after polymerization is finished and the mixture of iron, ferrous components is 60 weight %, then, interpolation is as phosphoric acid 85% aqueous solution 0.03 weight portion of anti-coloring agent, antimony trioxide 0.06 weight portion as polycondensation catalyst, and, carry out polycondensation reaction as cobalt acetate tetrahydrate 0.06 weight portion of toner.After finishing polycondensation reaction with the roughly the same polymerization stirring torque of the polyethylene terephthalate of reference example 1, obtaining melt viscosity is that 1520 pools (are measured 290 ℃ of temperature, 10sec
-1) polyethylene terephthalate and the mixture of iron (below be designated as PET-Fe4) ball.Do not see the iron aggegation in the ball that obtains, mixing property is good.
Embodiment 1
Use the PET-Fe3 of reference example 1, with pressing molten type melt spinning machine to carry out melt spinning.It is that 0.3mm, hole count are that 24 the circular poroid tube head and the mesh thickness of filtering layer are the filter of 20 μ that the aperture is set when spinning temperature is 290 ℃, carries out melt spinning.After adhering to non-property of water-bearing finishing agent with the adhesion amount of 1 weight % on the fiber of ejection, it is carried out tractive with draw rate that 600m/ divides, obtain the 1590dtex-24 long filament, section configuration is circular multifilament.Do not occur broken end in the spinning, spinnability is good.
During multifilament that stretching obtains, the wire feed rate of thread delivering roller be 100m/ branch, the 1st roller the wire feed rate of dividing, the 2nd roller under 90 ℃, with 100m/ at the wire feed rate of dividing, the 3rd roller under 140 ℃, with 450m/ the wire feed rate of dividing under 200 ℃ the temperature, with 500m/ is implemented above-mentioned 2 sections stretching (reaching between the 2nd~3 roller between the 1st~2 roller) and heat treatment (the 3rd roller) to fiber after, with cold roller silk is cooled to the Tg of polyester or below the Tg after, batch.In the stretching, on roller, take place to judge that draftability serves as good when monofilament is reeled with the frequency of 0.5 time/kg.In addition, the 5kg drawn yarn cut off to add observe cutter wearing and tearing man-hour, carrying out property of operation is good.The rerum natura of silk is as shown in table 1.
(table 1)
Project | (unit) | Embodiment 1 | Comparative example 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 | Embodiment 7 | Embodiment 8 | Embodiment 9 | Embodiment 10 | |
Fiber forms base polymer | (single composition) kind | - | PET | PET | PET | - | - | - | - | - | - | - | - |
(core) kind | - | - | - | - | PET | PET | Ny6 | PET | PET | PET | PET | PET-1 | |
(sheath) kind | - | - | - | - | PET | PET | PET-IS | PET | PET | PET | PET | PE | |
Spherical magnetic material | (single composition) kind | - | Pure iron | Ferrite | Pure iron | - | - | - | - | - | - | - | - |
(magnetosphere) kind | - | - | - | - | Pure iron | Pure iron | Pure iron | Pure iron | Pure iron | Pure iron | Pure iron | Pure nickel | |
(protective layer) kind | - | - | - | - | - | - | - | Pure iron | - | Pure iron | - | - | |
Content | wt%*1 | 60 | 60 | 40 | 60/0 | 60/0 | 60/0 | 60/10 | 40/0 | 40/10 | 60/0 | 60/0 | |
Shape | - | Ball | Non-ball | Ball | Ball | Ball | Ball | Ball | Ball | Ball | Ball | Ball | |
Purity | % | 99.1 | - | 99.4 | 99.1 | 99.1 | 99.1 | 99.1 | 99.1 | 99.1 | 99.1 | 99.2 | |
Average grain diameter | μm | 2.5 | 1.7 | 10.8 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 2.7 | |
Compare resistance value | μΩ·cm | 9.8 | 10 11.8 | 10.2 | 9.8 | 9.8 | 9.8 | 9.8 | 9.8 | 9.8 | 9.8 | 8.1 | |
Coercive force | A/m | 4.0 | 2100 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 40 | 4.0 | 4.0 | 0.7 | |
Saturation flux density | T (tesla) | 2.15 | 0.335 | 2.15 | 2.15 | 2.15 | 2.15 | 215 | 2.15 | 2.15 | 2.15 | 061 | |
Fiber properties | Compound type | - | Single composition | Single composition | Single composition | Bimetallic | The core sheath | The core sheath | The core sheath | The core sheath | The core sheath | The core sheath | The core sheath |
The core composition | - | - | - | - | - | Magnetosphere | Magnetosphere | Magnetosphere | Magnetosphere | Magnetosphere | Protective layer | Protective layer | |
Compound ratio | Magnetosphere/protective layer | - | - | - | 60/40 | 80/20 | 80/20 | 80/20 | 80/20 | 80/20 | 80/20 | 80/20 | |
Boiling water shrinkage | % | 2.3 | 3.1 | 2.7 | 2.6 | 2.2 | 4.5 | 1.8 | 4.2 | 3.3 | 2.0 | 4.0 | |
The permanent elongation rate | % | 11 | 5 | 21 | 14 | 18 | 25 | 10 | 18 | 16 | 12 | 15 | |
The initial stage tensile elasticity rate | cN/dtex | 18 | 13 | 12 | 20 | 25 | 15 | 20 | 25 | 23 | 18 | 13 | |
Overall merit | Magnetic field responsiveness | ◎ or △ | ◎ | △ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ |
Heat resistance | ◎ or zero or △ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | |
The soft magnetic material Combination | ◎ or △ | ◎ | △ | ○ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | |
Carrying out property of operation | ◎ or zero or △ | ○ | △ | ○ | ◎ | ◎ | ◎ | ◎ | ◎ | ◎ | ○ | ◎ | |
Comprehensive judgement | Acceptance or rejection | Qualified " very " | Defective | Qualified " very " | Qualified " excellent " | Close and iron " excellent " | Qualified " excellent " | Qualified " excellent " | Qualified " excellent " | Qualified " excellent " | Qualified " very " | Qualified " excellent " |
PET: polyethylene terephthalate, Ny6: nylon 6, PET-IS: M-phthalic acid and sulfoisophthalic acid sodium copolymerization PET
PET-I: M-phthalic acid copolymerization polyethylene terephthalate, PE: Mitsui Chemicals, Inc's system polyethylene
* the record of the content of 1 soft magnetic material: if oligomict fiber is then put down in writing the content in the fiber.If be compound silk, then put down in writing with (content of soft magnetic material in the magnetosphere)/(content of soft magnetic material in the protective layer).
Comparative example 1
In reference example 1, replace iron, similarly add soft ferrite particle (the model KNS-415 of 60 weight % family field industry (strain) system with reference example 1, be to pulverize the particle of making, in the mensuration of above-mentioned C. item record, circularity mean value is 1.8, be in addition particle surface have size for particle diameter more than 1/10th or 1/10th countless bigger concavo-convex, can not think spherical powder), carry out mixing.Because the wettability of particle and polymer is poor, or particle can't fill the most densely, so mixing property is poor, can observe countless aggegations.The mixture that use obtains carries out melt spinning by method similarly to Example 1.Frequency with 15.5 times/kg in the spinning breaks end, and the stream pressure loss in the spinning machine raises in addition, and spinnability is poor.And, use the multifilament that obtains, adopt method similarly to Example 1 to stretch.In the stretching, with the single broken end of frequency generation of 10.3 times/kg, when processing the 0.5kg fiber in the cut-out of the fiber processing in addition, can observe serious cutter and wear and tear, in addition, also can observe the guide plate wearing and tearing in the operation, carrying out property of operation is poor.The rerum natura of silk is shown in table 1.
Embodiment 2
In reference example 1, (iron purity is the pure element product more than 99% or 99% similarly to add the iron of 40 weight % (strain) high-purity chemical institute systems with reference example 1, average grain diameter is spherical powder (circularity is below 1.1 or 1.1 in the mensuration of above-mentioned C. item record), the model FEE10PB of 10.8 μ m), carry out mixing.Mixing property is good.The mixture that use obtains adopts method similarly to Example 1 to carry out melt spinning.Frequency with 1.3 times/kg in the spinning breaks end, but spinnability is good.The multifilament that adopts method similarly to Example 1 to stretch and obtain.Think that draftability is good when reeling with the frequency generation monofilament of 2.1 times/kg in the stretching.In addition, the cut-out of fiber adds wearing and tearing and the wearing and tearing of the guide plate in the operation that can observe cutter when cutting off the 4.2kg fiber man-hour, but carrying out property of operation is good.The rerum natura of silk is shown in table 1.
Embodiment 3
When carrying out the melt spinning of bimetal type,, use the PET-Fe3 of reference example 1, use the PET of reference example 1 as protective layer as magnetosphere with the extruder type composite molten spinning machine that possesses 2 single shaft extruders.With magnetosphere: the compound ratio of protective layer=6: 4 carries out the bimetal type composite spinning, and other conditions with embodiment 1 are identical, obtain the 1144dtex-24 long filament, section configuration is roughly circular bimetallic multifilament.Do not break end in the spinning, spinnability is good.
The multifilament that stretches and obtain with similarly to Example 1 method.Do not break end in the stretching, draftability is good.In addition, do not observe the guide plate wearing and tearing in cutter wearing and tearing and the manufacturing procedure, carrying out property of operation is good.The rerum natura of silk is shown in table 1.
Embodiment 4
When the composite molten spinning machine of use embodiment 3 carries out the core-sheath-type melt spinning; use the PET-Fe4 of reference example 2 as magnetosphere; use the PET of reference example 1 as protective layer; be core with the magnetosphere, be sheath with the protective layer, with magnetosphere: the compound ratio of protective layer=8: 2 carries out the core-sheath-type composite spinning; other conditions are identical with embodiment 1, obtain the 1330dtex-24 long filament, section configuration is circular core sheath multifilament.Do not break end in the spinning, spinnability is good.
The multifilament that stretches and obtain with similarly to Example 1 method.Monofilament coiling or broken end do not take place in the stretching, and draftability is good.In addition, do not observe the guide plate wearing and tearing in cutter wearing and tearing and the manufacturing procedure, carrying out property of operation is also good.The rerum natura of silk is shown in table 1.
Embodiment 5
In reference example 1, replace PET, add the nylon 6 resin " Amiran (registration mark) " (model C M1017) of mixing Dongli Ltd. system, making iron is 60 weight %, in addition, utilize the method same, obtain containing 60 weight % iron, melt viscosity is that 2530 pools (are measured 260 ℃ of temperature, 10sec with reference example 1
-1) nylon 6 and the mixture of iron (below be designated as Ny6-Fe3) ball.
Then; when utilization method is similarly to Example 4 carried out the core-sheath-type composite spinning; as magnetosphere; use above-mentioned Ny 6-Fe3; as protective layer; use copolymerization polyethylene terephthalate of obtaining of the sulfone acid sodium-salt derivative of 5 moles of % M-phthalic acids of copolymerization, 5 moles of % M-phthalic acids (below be designated as PET-IS, IV0.55) respectively in the PET of reference example 1; spinning temperature is 280 ℃; other conditions are identical with embodiment 1; carry out the core-sheath-type composite spinning, obtain the 1180dtex-24 long filament, section configuration is circular core sheath multifilament.Do not break end in the spinning, spinnability is good.
The multifilament that stretches and obtain with similarly to Example 1 method.Monofilament coiling or broken end do not take place in the stretching, and draftability is good.In addition, do not observe the guide plate wearing and tearing in cutter wearing and tearing and the manufacturing procedure, carrying out property of operation is also good.The rerum natura of silk is shown in table 1.
Embodiment 6~9
When carrying out core sheath composite spinning similarly to Example 4, magnetosphere and protective layer use the material of making in the reference example 1 respectively, carry out spinning by combination shown in the table 1.Particularly, among the embodiment 6, the magnetosphere of core uses PET-Fe3, and the protective layer of sheath uses PET-Fe1.Among the embodiment 7, the magnetosphere of core uses PET-Fe2, and the protective layer of sheath uses the PET that does not add pure iron.Among the embodiment 8, the magnetosphere of core uses PET-Fe2, and the protective layer of sheath uses PET-Fe1.Among the embodiment 9, the magnetosphere of sheath uses PET-Fe3, and the protective layer of core uses PET.In addition, spinning condition is identical with embodiment 4 with stretching condition.Only embodiment 9 observes the cutter wearing and tearing when cut-out adds man-hour and processes the 9kg fiber, but carrying out property of operation is good.The silk rerum natura of the drawn yarn that obtains etc. is shown in table 1.
Embodiment 10
In reference example 1, replace PET, the use copolymerization polyethylene terephthalate (PET-I that 5 moles of % M-phthalic acids of copolymer-1 obtain in the PET of reference example 1, IV0.70), in addition, replace iron, (nickel purity is the pure element product more than 99% or 99% to the nickel of use (strain) high-purity chemical institute system, average grain diameter is the spherical powder (circularity is below 1.1 or 1.1 in the mensuration of above-mentioned C. item record) of 2.7 μ m, model NIE02PB), in addition, utilize the method same, obtain containing 60 weight % nickel with reference example 1, melt viscosity is that 1850 pools (are measured 290 ℃ of temperature, 10sec
-1) PET-1 and the mixture of nickel (below be designated as PET-I-Ni) ball.
Then; when utilization method is similarly to Example 4 carried out the core-sheath-type composite spinning; magnetosphere uses above-mentioned PET-I-Ni; protective layer uses the high density polyethylene (HDPE) (HI-ZEX (registration mark), 7000F) of Mitsui Chemicals, Inc's system; spinning temperature is 290 ℃; other conditions are identical with embodiment 1, carry out the core-sheath-type composite spinning, obtain the 1090dtex-24 long filament, section configuration is circular core sheath multifilament.Do not break end in the spinning, spinnability is good.
The multifilament that adopts method similarly to Example 1 to stretch and obtain.In the stretching, monofilament coiling or broken end do not take place, draftability is good.In addition, do not observe the guide plate wearing and tearing in cutter wearing and tearing and the manufacturing procedure, carrying out property of operation is also good.The rerum natura of silk is shown in table 1.
Embodiment 11
With the fiber that obtains in embodiment 4 and 5 cut into 0.5,1.0,2.0 respectively, behind the staple fibre of 4.0mm length, cataloid " SnowtexOS (registration mark) " with Nissan Chemical Ind Ltd's system is handled, and adjusts the ratio resistance value of fiber.
The staple fibre that use obtains, on the polyester film " Lumilar (registration mark) QT 33 (thickness 100 μ m) " of Dongli Ltd.'s system, thickness with about 100 μ m, (100 weight % with respect to K-1500 use 2 weight %DICNALVS-20 as tackifier to be coated with the acrylic acid acid esters class bonding agent DICNAL K-1500 of big Japanese ink chemical industry Co., Ltd. system in the one side of film; Hereinafter referred to as " adhesive A ").Then, the one side of the film that has been coated with bonding agent is implemented electric flocking processing, make flocking thing (A1~A8).For flocking (degree of flocking success), judge with naked eyes, estimate by following 4 stages: the fiber lodging (△) about almost all upright (double-deck circle ◎), visible a small amount of lodging fiber (zero), half, upright fiber few (*).The results are shown in table 2.
(table 2)
Project | (unit) | Embodiment 4 | Embodiment 5 | ||||||
Fibre length | mm | 0.51 | 1.02 | 1.98 | 4.03 | 0.49 | 1.01 | 2.01 | 4.01 |
Than resistance value * 1 | Ω·cm(×10 6) | 310 | 208 | 114 | 71 | 523 | 198 | 134 | 99 |
Magnetic field responsiveness * 2 | Zero or △ | △ | ○ | ○ | ○ | △ | ○ | ○ | ○ |
The sample title of flocking thing | A1 | A2 | A3 | A4 | A5 | A6 | A7 | A8 |
* 1 than resistance value: the ratio resistance value of the staple fibre of handling through cataloid.
* 2 magnetic field responsiveness: be zero, indefinitely be △ with what sense of touch determined that rigidity increases when applying magnetic field.
In addition, make the inboard (not flocking side) of magnet, comment sense of touch to judge the whether affected by magnetic fields and rigidization (magnetic field responsiveness) of the fiber of flocking near the flocking thing made.Rigidity increases is evaluated as zero, indefinite △ of being evaluated as.
In addition, use the fiber that obtains in embodiment 4 and 5 respectively, make fleece and individual layer tricot, implement napping respectively and handle.Fabric that obtains and braided fabric and the above-mentioned adhesive A of similarly using are bonded on the above-mentioned polyester film, make cloth and silk complex B and cloth and silk complex C respectively.When similarly confirming magnetic field responsiveness, the rigidity of cloth and silk complex B, C all increases, magnetic field responsiveness good (being evaluated as zero).
Embodiment 12
Use the adhesive A of embodiment 11, the staple fibre (fibre length be respectively 0.51,1.02,1.98,4.03mm) that 4 kinds of obtaining among the embodiment 11 are derived from embodiment 4 respectively electric flocking at bar-shaped object A (only being metal bar) and bar-shaped object B (the carbamate system intermediate layer (thickness is 1.5mm) that 5% conductive carbon black has been added in lining on metal bar is at the residual 2cm in metal bar end) (in bar-shaped object B only to the enforcement of intermediate layer part).Sweep off not bonding staple fibre from bar-shaped object, (order by the fibre length of bar-shaped object A middle short fiber shortens gradually obtains brush roll A1, A2, A3, A4 to obtain brush roll; Similarly bar-shaped object B also is divided into B1, B2, B3, B4).In addition, bonding and flocking obtains brush roll C on bar-shaped object B with the fleece of embodiment 11.The ratio resistance value of brush roll B2 under usual conditions that brush roll A2 that the last fibre length of bar-shaped object A is 1.02mm and the last fibre length of bar-shaped object B are 1.02mm is respectively 10
5.1Ω cm, 10
7.6Ω cm.Then, when measuring the ratio resistance change of brush roll B2 when humidity changes, the result is 10
6.6Ω cm (hot and humid degree)-10
7.6Ω cm (usual conditions)-10
7.6Ω cm (low temperature and low humidity degree).As mentioned above, even when humidity changes, use fiber of the present invention brush roll also only be 1 figure place than resistance value spot, less, be good.In addition, when similarly measuring than resistance change to brush roll C, the result is 10
6.1Ω cm (hot and humid degree)-10
7.0Ω cm (usual conditions)-10
7.1Ω cm (low temperature and low humidity degree), B2 is identical with brush roll, and it also only is 1 figure place than resistance value spot in humidity changes, less, is good.
Embodiment 13
The brush roll A2 that obtains among the embodiment 12 is assembled in discharge system and the clearing apparatus, and in addition, B2 is assembled in the Charging system with brush roll.Make the monochromatic laser printer continuous printing for long time (printing in per 1 minute is discharged 10) that sets, together confirm printing with the humidity variation in the printer.During 1000 left and right sides of printing beginning, the humidity in the printer reduces to 22% by 62% of the initial stage, and reduces to 18% when printing 10000 left and right sides, even but when the printing number surpassed 20000, the distinctiveness of printing and toner cleaning property etc. were also good.In addition, C replaces with B2 with brush roll, when similarly studying, even distinctiveness that same printing number printed when surpassing 30000 and toner cleaning property etc. are also good.
Embodiment 14
Use the fiber that obtains among the embodiment 4 to make 2 kinds of fabrics.1 kind with the fiber that obtains among the embodiment 4 as weft yarn, and use the identical polyester fiber of fiber that obtains among fibre diameter and the embodiment 4 that only constitutes by the polyester of reference example 1 in the weft yarn, make plain cloth, use above-mentioned plain cloth, make Y shirt (dress material 1).1 kind is used warp thread and weft yarn all to adopt the fiber that obtains among the embodiment 4 to make plain cloth in addition, uses plain cloth to make Y shirt (dress material 2).Choose at random 10 male sex and monitor when wearing the clothes test, dress material 1 and dress material 2 all obtain the answer of personnel " promptly feeling cold (contact coldness is arranged) after wearing the clothes ", and the answer of " contact coldness of comparing dress material 2 with dress material 1 is stronger ".
Utilizability on the industry
The fabric that fiber of the present invention is formed as at least a portion uses above-mentioned have very good magnetic field responsiveness or the fiber of electric conductivity. Therefore, when this fabric not only uses this fiber in fabric integral body, and also can form have good magnetic field responsiveness, electric conductivity or the discharge performance fabric of (in other words being antistatic property) when in the part of fabric, using this fiber. Therefore, can be used for various material applications, such as curtain or curtain, easily the bedding such as sheet material, wall material or carpet, futon, blanket, sheet etc. of static electricity on human body's the vehicles such as automobile, railway, aviation machine occurs.
The braid that fiber of the present invention is used as at least a portion formation is the braid that similarly has magnetic field responsiveness, electric conductivity or antistatic property with above-mentioned fabrics. Therefore, this braid can be used for beddings such as various material applications, sheet material, wall material, carpet, used for vehicle sheet material or above-mentioned carpet such as vehicles such as carpet, automobile, railway aviation machine such as the wall material of building or tapestries, futon, blanket, sheet etc.
The nonwoven that fiber of the present invention is used at least a portion formation is the nonwoven that similarly has magnetic field responsiveness, electric conductivity or antistatic property with above-mentioned fabrics or braid. Therefore, this nonwoven can be used as the material same with the purposes of above-mentioned fabrics or braid, in addition, also can be widely used in the material that necessity has thickness, such as separator material or package, do not wish to occur the devices such as mat of static, the surrounding member material in room.
Fiber of the present invention is used magnetic field responsiveness and high conductive fiber as the dress material that at least a portion forms, and the static that occurs in the time of therefore can suppressing to wear the clothes can be discharged into it external. Particularly fiber of the present invention can be effective to not wish occur the work clothes of the semiconductor industry of static, or because being difficult for producing static, not adsorbing dust and be used as dust coat. In addition, fiber of the present invention uses the good spherical magnetic material of thermal conductivity, therefore can be as can be to the contact coldness clothing of release in vitro heat or can will pass to the contact warming clothing etc. of cold health from the heat of external acquisition on the contrary. For example, fiber of the present invention can be preferred for having the motion dress material (uniforms such as golf clothes, croquet, baseball, tennis, Association football, vollyball, basketball, rugby, rugby, hockey, land sports, triathlon, speed skating, ice hockey) of above-mentioned contact coldness or contact warming function or child, women, the elderly's dress material, other outdoor dress materials (footwear, bag, motion body harness, socks, anorak) etc.
Above-mentioned fabrics of the present invention and/or above-mentioned braid and/or above-mentioned nonwoven are used for the brush roll of at least a portion, bonding formation because the fiber that at least part of use has magnetic field responsiveness or electric conductivity, therefore by utilizing electric effect or magnetic action, having the function of effectively removing unwanted material or giving necessary material, is good therefore.
The fiber that the brush roll that uses above-mentioned short fiber of the present invention to form has magnetic field responsiveness or electric conductivity owing at least part of use, therefore similarly utilize electricity effect or magnetic action with above-mentioned, have and effectively give the function of removing unwanted material or giving necessary material. In addition, by the fibre length of control short fiber, can easily controlling according to the fibre flocking density of brush roll or the above-mentioned purpose of removing performance or giving performance of brush roll, is good therefore. When particularly the bar-shaped object of flocking mainly is made of metal, can control the electric conductivity (than resistance value) of brush roll itself by controlling the electric conductivity in the spherical magnetic material in the fiber of the present invention. And, when bar-shaped object was made of the intermediate layer of at least a portion of metal and coated metal, the material by the control intermediate layer or thickness etc. can be given resiliency, therefore can further improve the above-mentioned of brush roll itself and remove performance or give performance, be good.
The clearing apparatus that uses above-mentioned brush roll of the present invention to form passes through rotation brush roll itself, removes unwanted material, when cleaning, has the very good performance of removing. Such as in following electric photographic apparatus etc., can or electrically remove magnetic such as toners the time, in the situations such as environmental change, particularly humidity variation in the electric photographic apparatus, the electric conductivity of brush roll does not change yet, perhaps owing to can contain the low-down spherical magnetic material of coercive force, therefore usually having the stable performance of removing, is good. In addition, above-mentioned brush roll of the present invention can directly contact the material (for example photoreceptor in the following electric photographic apparatus) as object in this clearing apparatus, clean. And above-mentioned brush roll can come clearing apparatus itself is cleaned by removing unwanted material from other members that carry out clean-up activities. That is, also be useful as the cleaning that is used for clearing apparatus with member, the result becomes high performance clearing apparatus.
The Charging system that uses above-mentioned brush roll of the present invention to form uses by the electric conductivity (than resistance value) of control brush roll itself. Such as in following electric photographic apparatus etc., as with the brush roll of photoreceptor uniform charged the time, at first can photoreceptor is charged equably, be good therefore. In addition, in the running of the environmental change in the electric photographic apparatus, for example electric photographic apparatus or the humidity that causes of seasonal variations change, the ratio resistance value of brush roll itself may not change, or variation is very little. Therefore, owing to be difficult to show the charged spot of photoreceptor, therefore very good. And, existing on the above-mentioned photoreceptor of this electric photographic apparatus when cleaning insufficient and residual toner, this brush roll can have the function as cleaning roller concurrently, therefore develops or pollution-free during printing, or almost pollution-free, be good. And, during with the electric photographic apparatus miniaturization, above-mentioned clearing apparatus and this Charging system needn't be set separately, can dual-purpose, that is, that this brush roll is as the clearing apparatus Charging system of holding concurrently, therefore very good.
The developing apparatus that uses above-mentioned brush roll of the present invention to form similarly orders about the ratio resistance value of brush roll itself with the effect of above-mentioned Charging system and the magnetic field responsiveness of fiber uses. For example, in following electric photographic apparatus etc., when toner being attached to be depicted on the electrostatic latent image on the photoreceptor, when the environmental change such as above-mentioned humidity variation occurs, the brush roll itself that is consisted of by fiber of the present invention than resistance value spot or the magnetic field responsiveness spot does not occur or occur hardly. Therefore, toner is supplied with photoreceptor equably, carries out development, and the development thing that obtains or printed article is pollution-free or almost pollution-free, very attractive in appearance is good.
Using the discharge system of above-mentioned brush roll formation of the present invention by controlling the amount of the spherical magnetic material that contains in the fiber, reduce the electric conductivity (than resistance value) of brush roll, become the brush roll with the very good electrical property that disappears, is useful therefore. When particularly using in following electric photographic apparatus, the brush roll that is made of countless suedes (fiber) has the electric effect that disappears of stable and homogeneous, therefore can further improve the cleaning effect that is arranged on the above-mentioned clearing apparatus behind the discharge system. In addition, during with this electric photographic apparatus miniaturization, by using this brush roll, can be used as the discharge system clearing apparatus of holding concurrently and be assembled into wherein, very good.
The electric photographic apparatus that uses above-mentioned clearing apparatus of the present invention and/or Charging system and/or developing apparatus and/or discharge system to form, particularly on charged photoreceptor, describe sub-image with laser for laser beam printer, duplicator, facsimile machine, Mobyneb compounding machine or word processor etc., use toner, carry out development, even develop or the device that prints in the electric photographic apparatus environmental change occurs as mentioned above based on above-mentioned mechanism, also have the charged development of the stable cleaning electrical property that disappears, the printing or the development thing that therefore obtain are very attractive in appearance. In addition, the optimizations such as content of the fibre length by making above-mentioned brush roll or the spherical magnetic material that contains, has the charged development of the more stable cleaning electrical property that disappears, therefore can further improve the actuating speed of electric photographic apparatus, namely can improve printing or developing powder (number) in the time per unit, very preferably.
Claims (31)
1. a fiber is characterized by, and this fiber is made of the polymer with fiber forming property power, and it is the above spherical magnetic material of 0.5 tesla or 0.5 tesla that described polymer contains saturation flux density.
2. fiber as claimed in claim 1 is characterized by, and the average grain diameter of spherical magnetic material is 5 μ m or below the 5 μ m.
3. fiber as claimed in claim 1 is characterized by, and the coercive force of spherical magnetic material is 1000A/m or below the 1000A/m.
4. fiber as claimed in claim 1 is characterized by, and described fiber is the composite fibre that the protective layer that contains quantity not sufficient 20 weight % by magnetosphere that contains the spherical magnetic material of 20~90 weight % and spherical magnetic material constitutes.
5. fiber as claimed in claim 1 is characterized by, and this fiber is that magnetosphere is that core composition, protective layer are that sheath composition and this magnetosphere are the core-sheath-type composite fibre of 5~95 volume %.
6. fiber as claimed in claim 1 is characterized by, and spherical magnetic material is the metal of chosen from Fe, nickel and cobalt more than purity 98% or 98%.
7. fiber as claimed in claim 1 is characterized by, and the shrinkage factor when keeping 15 minutes in 98 ℃ of boiling water is below 10% or 10%.
8. fiber as claimed in claim 1 is characterized by, and the permanent elongation rate is 5~30%.
9. fiber as claimed in claim 1 is characterized by, and the initial stage tensile elasticity rate is 15cN/dtex or more than the 15cN/dtex.
10. fiber as claimed in claim 1, it is characterized by, the polymer with fiber forming property power is that fusing point is the polymer in polyester polymer, polyamide polymers, polyolefin polymers and the polyacrylonitrile base polymer of being selected from more than 150 ℃ or 150 ℃.
11. fiber as claimed in claim 1 is characterized by, and is 10 than resistance value
3~10
9Ω cm.
12. fiber as claimed in claim 1 is characterized by, fracture strength is 0.5cN/dtex or more than the 0.5cN/dtex.
13. a staple fibre, this staple fibre is made of the described fiber of claim 1, and it is 10 than resistance value
6~10
9Ω cm.
14. a staple fibre, this staple fibre is made of the described fiber of claim 1, and fibre length is 0.05~150mm.
15. a fabric has at least a part to use the described fiber of claim 1 and form.
16. fabric as claimed in claim 15, wherein, fabric tissue is a pile weave construction.
17. a braided fabric has at least a part to use the described fiber of claim 1 and form.
18. braided fabric as claimed in claim 17 is characterized by, and is to be selected from braided fabric that knit stitches is made of back side napping braiding and to handle braided fabric in the braided fabric that makes pile shape fiber be present in textile surface through napping.
19. a nonwoven fabric has at least a part to use the described fiber of claim 1 and form.
20. a flocking thing, the described staple fibre of bonding claim 13 carries out flocking and forms at least a portion of substrate.
21. a cloth and silk complex, the bonding cloth and silk that is selected from each described fabric of claim 15~19, braided fabric and nonwoven fabric forms at least a portion of substrate.
22. a dress material, part use the described fiber of claim 1 to form.
23. a brush roll is that at least a portion that will be selected from the cloth and silk in each described fabric of claim 15~19, braided fabric and the nonwoven fabric is bonded on the bar-shaped object and forms.
24. a brush roll, at least a portion of bar-shaped object the described staple fibre of bonding claim 13, carry out flocking and form.
25. brush roll as claimed in claim 23 is characterized by, bar-shaped object mainly is made of metal.
26. brush roll as claimed in claim 23 is characterized by, bar-shaped object mainly is made of the intermediate layer of at least a portion of metal and coated metal.
27. the clearing apparatus that uses the described brush roll of claim 23 to form.
28. the Charging system that uses the described brush roll of claim 23 to form.
29. the developing apparatus that uses the described brush roll of claim 23 to form.
30. the discharge system that uses the described brush roll of claim 23 to form.
31. an electric photographic apparatus is to use the described discharge system of described clearing apparatus of claim 27 and/or the described Charging system of claim 28 and/or the described developing apparatus of claim 29 and/or claim 30 to constitute.