CN1760401A - 新型金基纤维复合材料 - Google Patents
新型金基纤维复合材料 Download PDFInfo
- Publication number
- CN1760401A CN1760401A CN 200510011090 CN200510011090A CN1760401A CN 1760401 A CN1760401 A CN 1760401A CN 200510011090 CN200510011090 CN 200510011090 CN 200510011090 A CN200510011090 A CN 200510011090A CN 1760401 A CN1760401 A CN 1760401A
- Authority
- CN
- China
- Prior art keywords
- new type
- gold
- based fibers
- composite material
- type composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种滑动触点用新型金基纤维复合材料,质量百分比(%)成分为:Pd 1~3,Gd0.2~0.6,Ni 18.5~21余量Au。采用叠层挤压法制备新型金基纤维复合材料,即Au合金带与Ni带叠层制成复合锭,通过挤压方式制备新型金基纤维复合材料。该新型金基纤维复合材料相对于AuNi系合金具有以下优点:(1)通过Ni纤维增强相的加入,既可以有效地提高材料的机械性能,又能保持Au合金基体良好导电性;(2)可以通过控制复合界面扩散层及组织结构,进一步调整材料的电阻率和硬度,使材料具有优良的综合性能;(3)Ni含量高,可节约贵金属。
Description
技术领域
本发明涉及滑动触点用新型金基纤维复合材料,特别是涉及Au合金/Ni纤维复合材料。
背景技术
在航空和宇航仪表中,常用的滑动触点材料有AuNi系合金,如Au-5Ni、Au-9Ni和Au-10Ni,同时在Au-9Ni合金研制的基础上,为了提高Au-9Ni合金的耐磨性、硬度和强度,降低电阻温度系数,添加了微量元素如:Gd、Y、Zr和Rh,但AuNi系合金的电学性能和力学性能不能同时满足某些仪器用滑动触点材料的技术要求。
发明内容
本发明能提供一种滑动触点用新型金基纤维复合材料,能够解决AuNi系合金的电学性能和力学性能不能同时满足某些仪器用滑动触点材料的技术要求的问题。
实现本发明的新型金基纤维复合材料,质量百分比(%)成分为:Pd 1~3,Gd 0.2~0.6,Ni18.5~21余量Au。
本发明使用的原材料纯度:Pd≥99.95%,Gd≥99.95%,Au≥99.99%,Ni≥99.95%。
本发明允许的杂质含量(质量比):Fe≤0.002%,Pd≤0.002%,Sb≤0.002%,Bi≤0.002%。
采用叠层挤压法制备新型金基纤维复合材料,即Au合金带与Ni带叠层制成复合锭,通过挤压方式制备新型金基纤维复合材料。
本发明的新型金基纤维复合材料相对于AuNi系合金具有以下优点:(1)通过Ni纤维增强相的加入,既可以有效地提高材料的机械性能,又能保持Au合金基体良好导电性;(2)可以通过控制复合界面扩散层及组织结构,进一步调整材料的电阻率和硬度,使材料具有优良的综合性能;(3)Ni含量高,可节约贵金属。
表1为本发明的新型金基纤维复合材料性能。
表1新型金基纤维复合材料性能
实施例编号 | 复合前带材厚度mm | 复合后Ni含量% | 抗拉强度(加工态)Mpa | 硬度(加工态)Hv | 电阻率μΩ.cm | 可加工性 | |
Au Pd Gd1.6-0.4 | Ni | ||||||
1 | 0.21 | 0.12 | 20.1 | 1150 | 268 | 17.34 | 优良 |
2 | 0.25 | 0.12 | 18.7 | 975 | 250 | 10.74 | 优良 |
具体实施方式
采用下列工艺制备新型金基纤维复合材料。
按质量百分比(%):Pd 1~3,Gd 0.2~0.6,余量Au配制原料,真空或氩气保护熔炼→铸锭700℃/3h均应化处理→冷轧→550~600℃/0.5h中间热处理→精轧成厚度0.21~0.25mmAu合金带材→将Au合金带材与厚度0.12mmNi带叠层制成复合锭→800℃/3h保温挤压→冷拉→600℃/1h固溶处理→精拉得到新型金基纤维复合材料。
Claims (5)
1.一种新型金基纤维复合材料,其特征是含有质量百分比为1%~3%的Pd,0.2%~0.6%的Gd,18.5%~21%的Ni,其余为Au。
2.根据权利要求1所述的新型金基纤维复合材料,其特征是本发明使用的原材料纯度:Pd≥99.95%,Gd≥99.95%,Au≥99.99%,Ni≥99.95%。
3.一种如权利要求1所述的新型金合金材料用于滑动触点。
4.根据权利要求3所述的用于滑动触点新型金合金材料,其特征在于所述的原材料纯度为:Pd≥99.95%,Gd≥99.95%,Au≥99.99%,Ni≥99.95%。
5.根据权利要求1至4任一项所述的新型金基纤维复合材料,其特征是采用叠层挤压法制备新型金基纤维复合材料,即Au合金带与Ni带叠层制成复合锭,通过挤压方式制备新型金基纤维复合材料。