CN1605646A - 一种铝镇静钢脱氧剂-铝铁合金 - Google Patents
一种铝镇静钢脱氧剂-铝铁合金 Download PDFInfo
- Publication number
- CN1605646A CN1605646A CN 200410009844 CN200410009844A CN1605646A CN 1605646 A CN1605646 A CN 1605646A CN 200410009844 CN200410009844 CN 200410009844 CN 200410009844 A CN200410009844 A CN 200410009844A CN 1605646 A CN1605646 A CN 1605646A
- Authority
- CN
- China
- Prior art keywords
- steel
- ferroaluminium
- killed steel
- aluminium
- reductor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种铝镇静钢脱氧剂-铝铁合金。属于炼钢领域,尤其是适用于制作冷扎薄板的低碳低硅镇静钢、转炉45#钢和管线钢的生产。脱氧剂-铝铁合金的化学成分重量百分比为:主要元素40%≤Al≤60%;37%≤Fe≤57%;0.1%≤Mn≤10%;0.1%≤Si≤8%;0.1%≤Ti≤10%;其余元素0.1%≤C≤1.0%;0.001%≤P≤0.1;0.001%≤S≤0.1%。本脱氧剂抗粉化性强,脱氧能力强,价格低廉,使用时烧损少,收得率高,铝利用率高,可节省铝资源,降低生产成本,提高经济效益。使用上能最大限度地减少气泡产生,细化钢组织晶粒,提高钢材冲击韧性,降低冷脆和时效倾向性。
Description
技术领域
本发明属于炼钢领域,尤其是适用于制作铝镇静钢、转炉45#钢和管线钢的生产。
背景技术
纯铝一直是炼钢工业的主要脱氧剂,在生产具有高延展性、高冲压性的镇静钢钢种,尤其是适用于制作冷扎薄板的低碳镇静钢钢种时,都采用纯铝脱氧工艺,而不能使用硅铁和锰铁做脱氧剂,因为硅和锰等元素在冶炼这类钢种时,都是被严格控制的元素;而且,这类钢种需要较多的铝元素来细化晶粒。但由于铝的比重远小于钢水的比重,对钢液进行脱氧合金化时浮在钢液面上,易氧化,烧损大,这就降低了铝的利用率,增加铝的消耗量,增加了生产成本,降低经济效益。为了解决上述问题,钢铁研究部门开发了新的脱氧剂——铝铁合金。但由于该脱氧剂置于大气下易粉化,以致无法使用,从而限制了其应用。
发明内容
本发明目的是为了解决铝铁合金置于大气下易粉化,以致无法使用的问题。
经研究发现,铝铁合金由于碳元素的存在,在晶界上富积着Al4C3,在潮湿空气中,Al4C3相发生水解,放出烃类气体产生应力导致合金裂纹、粉化。研究表明,添加易与碳形成稳定化合物的元素钛能夺去碳原子,避免形成稳定碳化铝相,有效地防止合金的粉化。因此,本发明提供一种含有微量元素钛的铝铁合金,能有效延长抗粉化期,实现了铝铁合金在镇静钢钢水脱氧的应用。
一种铝镇静钢脱氧剂--铝铁合金,其特征在于脱氧剂--铝铁合金的化学成分重量百分比为:主要元素40%≤Al≤60%;37%≤Fe≤57%;0.1%≤Mn≤10%;0.1%≤Si≤8%;0.1%≤Ti≤10%;其余元素0.1%≤C≤1.0%;0.001%≤P≤0.1;0.001%≤S≤0.1%。
一种铝镇静钢脱氧剂--铝铁合金,其特征在于脱氧剂--铝铁合金的粒度要求:10-80mm
本脱氧剂抗粉化性强,脱氧能力强,价格低廉,使用时烧损少,收得率高,铝利用率高,可节省铝资源,降低生产成本,提高经济效益。使用后能最大限度地减少气泡产生,细化钢组织晶粒,提高钢材冲击韧性,降低冷脆和时效倾向性。
具体实施方式
制备方法
1、原料:
废钢;纯铝;钛铁。
2、设备:
感应炉;圆盘铸模;圆饼模铸;破碎机。
3、制作步骤:
(1)将废钢加入感应炉,加热直到完全熔化。
(2)将钛铁加入感应炉,加热直到完全熔化,搅拌。
(3)将纯铝加入感应炉,加热直到完全熔化,搅拌。
(4)出炉。
(5)浇铸。
(6)破碎。
工艺条件采用工频和中频无铁心感应加热炉,功率范围200KW-1000KW,标准容量200-2000kg。
配料方式1
废钢:500kg
钛铁:FeTi30 34kg
铝锭:铝含量99.99%,466kg
熔炼所得的铝铁合金,其成分重量百分比分别为:主要元素Al:45.74%;Fe:43.40%;Mn:2.52%;Si:0.52%;Ti:1.0%;其余元素C:0.585%;P:0.076%;S:0.19%。
配料方式2
废钢:56kg
钛铁:FeTi30 6.8kg
铝锭:铝含量99.99%,42kg
熔炼所得的铝铁合金,其成分重量百分比分别为主要元素Al:41.4%;Fe:55.40%;Mn:0.5%;Si:0.32%;Ti:2.0%;其余元素C:0.25%;P:0.001%;S:0.001%。
配料方式3
废钢:366kg
钛铁:FeTi30 34kg
铝锭:铝含量99.99%,600kg
熔炼所得的铝铁合金,其成分重量百分比分别为:主要元素Al:59.5%;Fe:38.0%;Mn:0.2%;Si:0.2%;Ti:1%;其余元素C:0.75%;P:0.002%;S:0.003%。
配料方式4
废钢:100kg
钛铁:FeTi30 150kg
铝锭:铝含量99.99%,360kg
熔炼所得的铝铁合金,其成分重量百分比分别为:主要元素Al:43.4%;Fe:29.%:Mn:9.5%;Si:7.5%;Ti:9.5%;其余元素C:0.35%;P:0.002%;S:0.019%。
Claims (4)
1.一种铝镇静钢脱氧剂--铝铁合金,其特征在于脱氧剂--铝铁合金的化学成分重量百分比为:主要元素40%≤Al≤60%;37%≤Fe≤57%;0.1%≤Mn≤10%;0.1%≤Si≤8%;0.1%≤Ti≤10%;其余元素0.1%≤C≤1.0%;0.001%≤P≤0.1%;0.001%≤S≤0.1%。
2.如权利要求1所述铝镇静钢脱氧剂--铝铁合金,其特征在于铝镇静钢脱氧剂--铝铁合金粒度要求:10-80mm。
3.如权利要求1和权利要求2所述镇静钢脱氧剂--铝铁合金,其特征在于铝镇静钢脱氧剂--铝铁合金的生产设备:工频和中频感应炉,功率范围200KW-1000KW,标准容量200-2000kg。
4、如权利要求3所述铝镇静钢脱氧剂--铝铁合金;其特征在于铝镇静钢脱氧剂--铝铁合金铸造设备是:圆盘铸模和圆饼铸模。