CN1598087A - Nano Temalen, medical stone and magnetic multi-component synthesizing fibre and its preparation technology and textile - Google Patents
Nano Temalen, medical stone and magnetic multi-component synthesizing fibre and its preparation technology and textile Download PDFInfo
- Publication number
- CN1598087A CN1598087A CN 200410072069 CN200410072069A CN1598087A CN 1598087 A CN1598087 A CN 1598087A CN 200410072069 CN200410072069 CN 200410072069 CN 200410072069 A CN200410072069 A CN 200410072069A CN 1598087 A CN1598087 A CN 1598087A
- Authority
- CN
- China
- Prior art keywords
- medical stone
- biological magnetic
- plain
- nano
- permanent biological
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention belongs to the health yarn and spinning technological field. A kind of nanometer tex agate particle, medical stone, permanence biological magnetic multi-elements multi-function complex fiber, it is made of usual complex fiber agglomerate and the three matters said above. The mass percent of the three matters is 3-40%. The preparation technique of this fiber is: tex agate particle, medical stone, permanence biological magnetic are sieved and made into nanometer powder. Then mixed with usual complex fiber agglomerate of proportion. The carcase polymer is then the nanometer multi-elements multi-function agglomerate, fiber spinning, cooling, curing, winding, drafting. Finally obtaining nanometer tex agate particle, medical stone, and permanence biological magnetic multi-elements multi-function complex fiber.
Description
Technical field
The invention belongs to field of textiles, particularly health yarn and textile technology field thereof.
Background technology
" textiles is with healthy " this idea more and more is subjected to attention human and the world textile industry.Anion in the market closes fibre and health treatment and magnetic fibre (ZL99125506.2) and health treatment thereof, and all because of element is single, and health care is not clearly.
Summary of the invention
The problem to be solved in the present invention is, provide nanometer multielement multi-functional have a significant curative effect close fibre and health treatment thereof.
The object of the present invention is achieved like this:
A kind of nano order tourmaline, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element close fine biochemical master batch and above-mentioned three kinds of materials are formed by routine, and three kinds of shared percentage by weights that close fine biochemical master batch of complex element are: 3～40%.
Described routine is closed fine biochemical master batch and is referred to polypropylene.
The shared optimum weight percentage that closes fine biochemical master batch of described three kinds of complex elements is: 8～21%.
The plain multi-functional fibre that closes of described nano order tourmaline, medical stone, permanent biological magnetic multi-element can be spun into the series at 20 dawn～1600 dawn and closes fibre.
A kind of nano order tourmaline, medical stone, the plain multi-functional fine preparation technology that closes of permanent biological magnetic multi-element, Temalen, medical stone, permanent biological magnetic screening are extracted, make nano-powder, three kinds of nano-powders are closed the percentage co-blended that fine biochemical master batch adds according to design with conventional, then the framework polymer the multi-functional biochemical master batch of nanometer multielement; Then reel off raw silk from cocoons, cooling curing is reeled, and nano order tourmaline, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element are made in drawing-off at last.
Nano order tourmaline, medical stone, the plain multifunctional health fabric of permanent biological magnetic multi-element adopt that nano order tourmaline, medical stone, permanent biological magnetic multi-element are plain multi-functionally to be closed fine braiding and form.
The thickness of above-mentioned health care fabric is 30g/m
2～2000g/m
2
Nano order tourmaline, medical stone, the plain multi-function health-care articles for use of permanent biological magnetic multi-element adopt nano order tourmaline, medical stone, the plain multifunctional health fabric of permanent biological magnetic multi-element to be sewn into.
The similar and different separately health care of utilization multielement carries out the combination of high section: as the permanent biological magnetic element of infinitesimal, can a strong magnetic field subenvironment such as even be set for human body, be that human body cell replenishes magnetism (as acupuncture); The nano order tourmaline element provides the light source of permanent release anion and emission 8～25 μ m far infrareds for human body; The nano medical stone element provides a healthy element database for human body, replenishes calcium, selenium and other trace elements to human body at any time, can also launch 8～25 μ m far infrareds simultaneously, becomes the stack light source.
With nano order tourmaline, medical stone, the various elements of permanent biological magnetic, mix by similar and different percentage science assembly respectively, adopt high section technology, complex element is added in the biochemical master batch of synthetic fiber, be spun into the multi-functional fibre that closes of multielement, and be woven into health care fabric, make the serial health articles for use.
The highest addition of percentage that the mixing nano-element accounts for biochemical master batch weight is 40%, and minimum is 3%; Optimum addition is 8～21%.
Described mix proportion scheme can be spun into the multi-functional fibre that closes of 20 dawn～1600 dawn multielements, is made into 30g/m
2～2000g/m
2The series function health care fabric, make as thin as cicada's wingsly, unlimited many health treatments of heavy as iron and steel satisfy the human health enjoyment of living.
Described Temalen (Tourmaline) element claims ruby or tourmaline again, has voltage and pyroelectricity, and emission wavelength is 8～25 μ m under the normal temperature, and emissivity is at the far infrared more than 90% and for good and all discharge negative aeroion.Can fresh air, fat-reducing, activating cell, increasing blood flow amount and flow velocity substantially improve blood microcirculation.
Described nano medical stone element has medical record to medical stone in ancient doctor's work Shennong's Herbal, is enrolled pharmacopeia by State Scientific and Technological Commission again now, numbering (the mirror word is given birth to No. 001 by 90 state sections).In the remedies of this medical ore deposit, contain more than 28 kinds the useful element of health such as calcium, selenium ..., and have very strong sterilizing function, more peculiar is the far infrared that medical stone can be launched 8～25 μ m, emissivity is more than 82%.Replenish element and activating cells such as calcium, selenium for human body, increasing blood flow amount and flow velocity substantially improve blood microcirculation.
Described permanent biological magnetic element, it is characterized in that in each magnetic particle the N-S utmost point of oneself is all arranged, the magnetic line of force that countless magnetic particles (in health care fabric) are produced forms clover leaf weak magnetic force net, and form magnetic circuit to the S utmost point by the N utmost point, constitute biological magnetic field.
The biological little magnetic field of human body cell is changed, produce magnetic induction, thereby improve blood microcirculation, eliminate extravasated blood, dredging the channel is as acupuncture moxibustion mechanism.
Nano order tourmaline of the present invention, medical stone, permanent biological magnetic multi-element are plain multi-functionally to close fibre and fabric can be made into health-care physiotherapeutic articles for use complete, evident in efficacy among the human lives.After wearing nano order tourmaline, medical stone, the plain multifunction physiotherapy and health-care articles for use of permanent biological magnetic multi-element, can substantially improve the blood of human body microcirculation, the various diseases that causes because of microcirculation disorder is all had significant curative effect.This magnetic, multi-functional health treatment is inferior health people's the thing that must use, brings restorative Gospel for the sub-health population that accounts for world population 70%, is again to offer to healthy population to delay senility, the high section gift of promoting longevity.
Above-mentionedly close fibre and health treatment feeds back through market sale, health care stack really, evident in efficacy, can substantially improve blood microcirculation, all effective in cure to the multiple disease that causes because of microcirculation disorder.And has a function of antibiotic, antiultraviolet, moisture absorbing and deodorizing, fresh air and fat-reducing.Practice confirms that the present invention is a wound 21 century high-new scientific and technical result.
The specific embodiment
Example 1:
The percentage by weight that complex element accounts for biochemical master batch is 21% o'clock, and it is as shown in table 1 that every kind of element accounts for percentage respectively:
| The element classification | ％ | ％ | ％ | ％ | ％ | ％ | ％ |
| Nano order tourmaline | 7 | ?10 | ?10 | ?6 | ?6 | ?5 | ?5 |
| Nano medical stone | 7 | ?5 | ?6 | ?10 | ?5 | ?6 | ?10 |
| Permanent biological magnetic | 7 | ?6 | ?5 | ?5 | ?10 | ?10 | ?6 |
| The biochemical master batch of polypropylene | 79 | ?79 | ?79 | ?79 | ?79 | ?79 |
Preparation technology:
Temalen, medical stone, permanent biological magnetic screening are extracted, make nano-powder, three kinds of nano-powders are closed the percentage co-blended that fine biochemical master batch adds according to design with conventional, then the framework polymer the multi-functional biochemical master batch of nanometer multielement; Then reel off raw silk from cocoons, cooling curing is reeled, and nano order tourmaline, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element are made in drawing-off at last.
By described table 1 as seen, three constituent content is can join the three elements function that spins 7 kinds of similar and different proportionings at 21% o'clock to close fibre.Adopt above-mentioned close fibre carry out tatting or knitting processing health care fabric; Be sewn into health treatment again.
Example 2:
The percentage by weight that complex element accounts for biochemical master batch is 8% o'clock, and it is as shown in table 2 that every kind of element accounts for percentage respectively:
2-1
| The element classification | ％ | ％ | ％ |
| Nano order tourmaline | 2 | ?4 | ?2 |
| Nano medical stone | 4 | ?2 | ?2 |
| Permanent biological magnetic | 2 | ?2 | ?4 |
| The biochemical master batch of polyamide fibre | 92 | ?92 | ?92 |
2-2
| The element classification | ％ | ％ | ％ | ％ | ％ | ％ |
| Nano order tourmaline | 3.5 | ?3.5 | ?2.5 | ?2.5 | ?2 | ?2 |
| Nano medical stone | 2.5 | ?2 | ?3.5 | ?2 | ?2.5 | ?3.5 |
| Permanent biological magnetic | 2 | ?2.5 | ?2 | ?3.5 | ?3.5 | ?2.5 |
| The biochemical master batch of acrylic | 92 | ?92 | ?92 | ?92 | ?92 | ?92 |
2-3
| The element classification | ％ | ％ | ％ |
| Nano order tourmaline | 2.5 | ?3 | ?2.5 |
| Nano medical stone | 2.5 | ?2.5 | ?3 |
| Permanent biological magnetic | 3 | ?2.5 | ?2.5 |
| The biochemical master batch of terylene | 92 | ?92 | ?92 |
2-4
| The element classification | ％ | ％ | ％ | ％ | ％ | ％ |
| Nano order tourmaline | 4.5 | ?4.5 | ?2 | ?2 | ?1.5 | ?1.5 |
| Nano medical stone | 1.5 | ?2 | ?1.5 | ?4.5 | ?4.5 | ?2 |
| Permanent biological magnetic | 2 | ?1.5 | ?4.5 | ?1.5 | ?2 | ?4.5 |
| The biochemical master batch of polypropylene | 92 | ?92 | ?92 | ?92 | ?92 | ?92 |
Preparation technology:
Temalen, medical stone, permanent biological magnetic screening are extracted, make nano-powder, three kinds of nano-powders are closed the percentage co-blended that fine biochemical master batch adds according to design with conventional, then the framework polymer the multi-functional biochemical master batch of nanometer multielement; Then reel off raw silk from cocoons, cooling curing is reeled, and nano order tourmaline, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element are made in drawing-off at last.
By table 2-1 to 2-4 as seen, three constituent content is 8% o'clock, can join the function that spins 18 kinds of similar and different three elements proportionings and close fibre.
Adopt above-mentioned close fibre carry out tatting or knitting health care fabric; Be sewn into health treatment again.
Every test data of its health care fabric is:
1, negative ion concentration: the three elements addition is 8% o'clock: 1100/cm
3～1300/cm
3,
The three elements addition is 21% o'clock: 2600/cm
3～2800/cm
3
2, far infrared emissivity: the three elements addition is 8% o'clock: 82%～84%,
The three elements addition is 21% o'clock: 88%～94%.
3, magnetic flux: the three elements addition is 8% o'clock: 3～5GS,
The three elements addition is 21% o'clock: 20～30GS.
Claims (8)
1, a kind of nano order tourmaline, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element close fine biochemical master batch and above-mentioned three kinds of materials are formed by routine, it is characterized in that three kinds of shared percentage by weights that close fine biochemical master batch of complex element are: 3～40%.
2, a kind of nano order tourmaline according to claim 1, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element is characterized in that described routine is closed fine biochemical master batch and referred to polypropylene.
3, a kind of nano order tourmaline according to claim 1 and 2, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element is characterized in that three kinds of shared optimum weight percentages that close fine biochemical master batch of complex element are: 8～21%.
4, nano order tourmaline according to claim 1 and 2, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element is characterized in that the series function that can be spun into for 20 dawn～1600 dawn closes fibre.
5, a kind of nano order tourmaline, medical stone, the plain multi-functional fine preparation technology that closes of permanent biological magnetic multi-element, it is characterized by, Temalen, medical stone, permanent biological magnetic screening are extracted, make nano-powder, three kinds of nano-powders are closed the percentage co-blended that fine biochemical master batch adds according to design with conventional, then the framework polymer the multi-functional biochemical master batch of nanometer multielement; Then reel off raw silk from cocoons, cooling curing is reeled, and nano order tourmaline, medical stone, the plain multi-functional fibre that closes of permanent biological magnetic multi-element are made in drawing-off at last.
6, nano order tourmaline, medical stone, the plain multifunctional health fabric of permanent biological magnetic multi-element is characterized by, and adopt that nano order tourmaline, medical stone, permanent biological magnetic multi-element are plain multi-functionally to be closed fine braiding and form.
7, nano order tourmaline according to claim 6, medical stone, the plain multifunctional health fabric of permanent biological magnetic multi-element is characterized by, and thickness is 30g/m
2～2000g/m
2
8, nano order tourmaline, medical stone, the plain multi-function health-care articles for use of permanent biological magnetic multi-element is characterized by, and adopt nano order tourmaline, medical stone, the plain multifunctional health fabric of permanent biological magnetic multi-element to be sewn into.