CN1585037A - Radiation-proof shading material and preparing method thereof - Google Patents
Radiation-proof shading material and preparing method thereof Download PDFInfo
- Publication number
- CN1585037A CN1585037A CN 200410025043 CN200410025043A CN1585037A CN 1585037 A CN1585037 A CN 1585037A CN 200410025043 CN200410025043 CN 200410025043 CN 200410025043 A CN200410025043 A CN 200410025043A CN 1585037 A CN1585037 A CN 1585037A
- Authority
- CN
- China
- Prior art keywords
- tib
- radioresistance
- tio
- radiation
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The component percentage of the anti-radiation, shielding material is Pb 2-10%, Ba 1-5%, TiO2 5-15%, TiB2 1-10%, the rest is aluminum (Al) Under the smelting temperature, the Al is melt down. Then add the anti-radiation material of Pb, Ba, TiO2 and TiB2, the distribution of the material can be controlled by utilizing the magnetic field and controlling the cooling speed. Thus the grading structure is formed. The material is applied to protect the electrnic component of the spacecraft from outer-sphere radiation damage.
Description
Technical field
The present invention relates to a kind of compound substance and preparation method thereof, particularly a kind of anti-radiation shield material and preparation method thereof.Be used for the Composite Preparation field.
Background technology
Be full of the electromagnetic radiation of various high energy charged particles and each wave band in the working environment of electron devices such as spacecrafts such as guided missile, satellite, aircraft and warship, as high energy proton, electronics, neutron, ion and radiowave, microwave, x ray, gamma-rays etc., they can bring serious radiation damage and electromagnetic interference (EMI) to electron device, are the major incentive of spacecraft fault and inefficacy.Make semiconductor devices SiO as high energy charged particles by effects of ionizing radiation
2Electronics-hole in the insulation course causes the threshold voltage shift of MOS transistor, bipolar transistor gain to descend to increasing; Generation makes microelectronic component logic state single event upset that changes and the single event latchup that makes cmos component generation controlled silicon effect; High energy particle passes through when having the high index of refraction optical material also can produce the Qie Lunkefu radiation effect, makes background the bright spot that should not have etc. occur.
By literature search, N.C.Das, people such as D.Khastgir are in the article of Composites partA:appliedscience and manufacturing magazine 2000 the 31st curly hair table " Electromagneticinference shielding effectiveness of carbon black and carbon fibra EVAand NR based composites " compound substance ", the electromagnetic interference shield effect of carbon black, carbon fiber ethylene vinyl acetate and natural rubber based composites) ".The preparation technology and the shield effectiveness of three kinds of shielding material carbon blacks, carbon fiber ethylene vinyl acetate and natural rubber based composites that this article is introduced.Its complex technical process, seriously polluted, though the compound substance for preparing has certain shield effectiveness to the X ray of 100-2000MHz and 8-12GHz, but mechanical property is not high, and because these materials under actinism, have instability, takes place crosslinked, the generation catabiosis, also be unfavorable for environmental protection, thereby be difficult to be applied to the environment for use of spacecraft and the protection of electronic instrument.And the space flight instrument requires used material to have very high mechanical property, high temperature resistant and cryogenic property and ageing resistance because its special environment for use, thus above-mentioned material to be used on the space flight instrument be inappropriate.
Summary of the invention
The present invention is directed to the deficiencies in the prior art and defective, a kind of anti-radiation shield material and preparation method thereof is provided, make its material of preparing can improve space shielding property and electromagnetic shielding action, particularly shield outer space high-energy ray.
The present invention is achieved by the following technical solutions, and anti-radiation shield material of the present invention is a matrix with aluminium, with Pb, Ba, TiO
2, TiB
2As the radioresistance hardening constituent, the percentage by weight of its component: Pb 2~10%, Ba 1~5%, TiO
25~15%, TiB
21~10%, surplus is an aluminium.
Anti-radiation shield preparation methods of the present invention is: at first under smelting temperature aluminium is melted, add Pb, Ba, TiO then respectively
2, TiB
2The radioresistance hardening constituent by controlling cooling velocity and utilizing electromagnetic field that the distribution mode of radioresistance hardening constituent in the melt is controlled, distributes it in solidified structure, form the gradient-structure of material, thereby obtains the compound substance of radioresistance gradient self-generating.
The matrix that the present invention adopts is the fine aluminium base, and concrete technological parameter is: smelting temperature is 750 ℃~1100 ℃; The addition scope of the radioresistance hardening constituent that adopts: Pb 2~10%, and Ba 1~5%, TiO
25~15%, TiB
21~10%; The cooling velocity scope that adopts: 5~30 degree/seconds; The electromagnetic field frequency scope that adopts is: 0~20kHz.
The present invention has substantive distinguishing features and obvious improvement; the spontaneous composite gradient material of its radioresistance can effectively reduce spacecraft is subjected to the high energy charged particles bombardment at the outer space radiation injury; can also effectively protect electronic devices and components are subjected in the spacecraft outside and interference each other; but also can be generalized to other field, for example: carrier rocket, spaceship, guided missile, aircraft and warship etc.Aspect civilian, can be used to prevent that vitals such as computer chip, integrated circuit are subjected to having very wide application prospect and application value in army such as the electromagnetism of generations such as ELECTROMAGNETIC BOMB, sunspot and the destruction of radiation.
Embodiment
The effect that technology of the present invention obtains material is: (1) material mechanical performance: the density of compound substance near or be a bit larger tham aluminium; (2) shield effectiveness: its radioresistance index is as shown in the table:
Ray type x ray gamma-rays α, β ray neutron ray
Shielding rate (%) 20% 10% reaches standard 10%
Below in conjunction with specific embodiment the present invention is done further understanding:
Embodiment 1:
The percentage by weight of anti-radiation shield material component: Pb 10%, Ba 1%, TiO
210%, TiB
21%, surplus is a fine aluminium.
Fine aluminium is being melted for 750 ℃, adding Pb 10%, Ba 1%, TiO
210%, TiB
21% radioresistance hardening constituent, melt are incubated to 750 ℃, at 5 degree/seconds of cooling velocity, electromagnetic frequency are to be shaped under the condition of 7kHz.This kind gradient composites has good anti-high-energy ray effect, and gamma ray shielding is reached 8.0%, and the x alpha ray shield reaches 9.2%, and α and β ray can reach standard, and the shielding of neutron ray reaches 7%, and density is 5.7%.
Embodiment 2:
The percentage by weight of anti-radiation shield material component: Pb 6%, Ba 3%, TiO
25%, TiB
28%, surplus is a fine aluminium.
Fine aluminium is being melted for 850 ℃, is adding alloying element, join the LY12 alloy melt, add Pb 6%, Ba 3%, TiO
25%, TiB
28% radioresistance hardening constituent, melt are incubated to 850 ℃, at 10 degree/seconds of cooling velocity, electromagnetic frequency are to be shaped under the condition of 10kHz.This kind gradient composites has good anti-high-energy ray effect, and gamma ray shielding is reached 9.4%, and the x alpha ray shield reaches 12.6%, and α and β ray can reach standard, and the shielding of neutron ray reaches 8.8%, and density is 4.3%.
Embodiment 3:
The percentage by weight of anti-radiation shield material component: Pb 2%, Ba 5%, TiO
215%, TiB
210%, surplus is a fine aluminium.
Fine aluminium is being melted for 1000 ℃, adding Pb 2%, Ba 5%, TiO
215%, TiB
210% radioresistance hardening constituent, melt are incubated to 1100 ℃, at 30 degree/seconds of cooling velocity, electromagnetic frequency are: be shaped under the condition of 16kHz.This kind gradient composites has good anti-high-energy ray effect, and gamma ray shielding is reached 9.8%, and the x alpha ray shield reaches 16.7%, and α and β ray can reach standard, and the shielding of neutron ray reaches 9.1%, and density is 4.8%.
Claims (4)
1, a kind of anti-radiation shield material is characterized in that, is matrix with aluminium, with Pb, Ba, TiO
2, TiB
2As the radioresistance hardening constituent, the percentage by weight of its component: Pb 2~10%, Ba 1~5%, TiO
25~15%, TiB
21~10%, surplus is an aluminium.
2, a kind of anti-radiation shield preparation methods is characterized in that, described anti-radiation shield material is to be matrix with aluminium, with Pb, Ba, TiO
2, TiB
2As the radioresistance hardening constituent, the percentage by weight of its component: Pb 2~10%, Ba 1~5%, TiO
25~15%, TiB
21~10%, surplus is an aluminium, at first under smelting temperature aluminium is melted, and adds Pb, Ba, TiO then respectively
2, TiB
2The radioresistance hardening constituent by controlling cooling velocity and utilizing electromagnetic field that the distribution mode of radioresistance hardening constituent in the melt is controlled, distributes it in solidified structure, form the gradient-structure of material, thereby obtains the compound substance of radioresistance gradient self-generating.
3, anti-radiation shield preparation methods according to claim 2 is characterized in that, smelting temperature is 750 ℃~1100 ℃.
4, anti-radiation shield preparation methods according to claim 2 is characterized in that, the cooling velocity scope: 5~30 degree/seconds, the electromagnetic field frequency scope is: 0~20kHz.