CN1546314A - Metallic composite panel - Google Patents
Metallic composite panel Download PDFInfo
- Publication number
- CN1546314A CN1546314A CNA2003101124164A CN200310112416A CN1546314A CN 1546314 A CN1546314 A CN 1546314A CN A2003101124164 A CNA2003101124164 A CN A2003101124164A CN 200310112416 A CN200310112416 A CN 200310112416A CN 1546314 A CN1546314 A CN 1546314A
- Authority
- CN
- China
- Prior art keywords
- board
- intermediate plate
- panel
- polyphenylene oxide
- metallic composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention is a kind of metal composite board, which is layered product which uses thin metal board as base board and panel board, the character lies in: there embeds polyphenyl ether middle board which is penetrated into the base board and the panel board between the two boards. The conception is novel, the structure is reasonable, the metal board and polyphenyl ether middle board make the surface molecular of the metal board and polyphenyl ether penetrated reciprocally through catalyst isocyanate and promotor ferrous powder, then the invention carries on recombination, there generate structural change, the catalyst is penetrated into the middle board of the metal board and polyphenyl ether, there hasn't independent bond between the metal board and polyphenyl ether, the external force must be large enough to separate the metal compound board. The boiling water, flexural strength, shearing strength, 180oC racking strength, temperature difference resistance, thermal expansion coefficient, thermal distortion temperature and son on mechanical performance standard of the metal composite board is excellent compared with normal aluminum plastic composite board.
Description
Technical field the present invention relates in fact to form the laminar product that pastes mutually as main or unique composition of thin layer and itself and thin layer that another layer is made of a kind of synthetic resin by metal, relates in particular to a kind of metallic composite panel.
The existing general plastic-aluminum metallic composite panel intermediate layer commonly used of background technology is polyethylene or polyvinyl chloride.Polyethylene has different models, and performance is different, but generally speaking, aspects such as its mechanical strength, hear resistance, serviceability temperature scope, resistance to water, dimensional stability, fire resistance and moulding processability are all far away from polyphenylene oxide.And polyvinyl chloride can produce strong fatal poison gas when burning, abroad is not used always, is also abandoned gradually at home.In addition, the binding material of existing general plastic-aluminum metallic composite panel is a macromolecule adhesive, makes as the aluminium metal sheet of substrate and panel and plastics sandwich layer as intermediate plate through the roll-in hot composition process to be bonded together.Adopt such combination process, when environment temperature sharply changes or under the external force effect, the disengaging of can coming unglued at the tack coat place.
Summary of the invention is the defective that remedies prior art, and the present invention proposes a kind of metallic composite panel.The technical scheme that adopts is as follows:
This metallic composite panel is by comprising the laminar product of thin metal blank as substrate and panel, it is characterized in that:
There are its both sides to permeate polyphenylene oxide intermediate plate in substrate and panel respectively embedding between substrate and the panel.
The further feature of this metallic composite panel is:
The polyphenylene oxide intermediate plate is that polyphenylene oxide and high impact polystyrene carry out the Noryl intermediate plate that the blending and modifying processing makes.
The polyphenylene oxide intermediate plate is that polyphenylene oxide and acrylonitrile-butadiene-styrene (ABS) ABS carry out the Noryl intermediate plate that the blending and modifying processing makes.
The polyphenylene oxide intermediate plate is that polyphenylene oxide and high density polyethylene carry out the Noryl intermediate plate that the blending and modifying processing makes.
The polyphenylene oxide intermediate plate is that polyphenylene oxide and polyphenylene thioether PPS are carried out the Noryl intermediate plate that the blending and modifying processing makes.
The polyphenylene oxide intermediate plate is that polyphenylene oxide and polyamide PA carry out the Noryl intermediate plate that the blending and modifying processing makes.
Substrate is that thickness is 0.20～1.00 millimeter metal sheet, and panel also is that thickness is 0.20～1.00 millimeter metal sheet.
Substrate generally is the aluminium metallic plate.
Panel generally is according to application and instructions for use, aluminium, zinc, titanium alloy, stainless steel, brass or bronze metallic plate.
Intermediate plate is that thickness is 1.00～6.40 millimeters Noryl intermediate plate.
The relative density of polyphenylene oxide PPO is minimum in engineering plastics, has balanced mechanical property, good hot strength, bending strength and impact strength, excellent creep resistant, stress relaxation, fatigue performance, anti-boiling water, the boiling resistance energy, and the dielectric properties that occupy the first place of plastics, and, hear resistance, good flame resistance, heat distortion temperature is 90～150 ℃, vitrification point is about 211 ℃, and fusing point is about 268 ℃, and being heated to just has the tendency of decomposition about 330 ℃, can use at-190～150 ℃ long-term, its resistance to water, water absorption rate is little to about 0.07%, not hydrolysis, use in wet environment, dimensional stability is good.The mobile performance of polyphenylene oxide own is very poor, is difficult to processing, and still, the flowability of Noryl MPPO has clear improvement, the cracking that can eliminate stress, and moulding processability is good, and molding shrinkage is little of 0.5～0.7%, and forming temperature is 260～285 ℃.Noryl is compared with other high molecular synthetic material, has excellent flame-retardant, and its burning diffusance is zero, in flame, do not produce toxic gas, add a small amount of fire retardant, fire resistance can reach the VL94V-0 level, also has the chemical property of anti-diluted acid, diluted alkaline and salting liquid.Fields such as conveying machinery, building materials, aviation and war industry such as electric, household electrical appliance, office automation machinery, automobile can be widely used in,, food and pharmaceutical industry can also be applied to because its light weight is nontoxic.
The present invention's beneficial effect against existing technologies is, novel, rational in infrastructure, metallic plate and polyphenylene oxide intermediate plate interpenetrate metallic plate and polyphenylene oxide intermediate plate top layer molecule by catalyst isocyanates, co-catalyst iron powder, recombinate, the recurring structure variation, catalyst permeates fully in metallic plate and polyphenylene oxide intermediate plate, there is not independently adhesive layer between metallic plate and the polyphenylene oxide intermediate plate, must apply enough big external force, could destroy the polyphenylene oxide intermediate plate, metallic composite panel is separated.Metallic composite panel all obviously is being better than general plastic-aluminum combined sheet material aspect physical and mechanical property index such as boiling water resistance, bending strength, shear strength, 180 ° of peel strengths, temperature difference resistance, thermal coefficient of expansion, heat distortion temperature and the template, and outstanding advantage is more being arranged aspect the environment in fire prevention with protecting.The present invention can be widely used in building, machinery and municipal works industry.
Appended drawings is a section structure schematic diagram of the present invention.
The specific embodiment
(1) this metallic composite panel is by comprising the laminar product of thin aluminum metal sheet material as substrate 1 and panel 2, has its both sides to permeate polyphenylene oxide intermediate plate 3 in substrate 1 and panel 2 respectively embedding between substrate 1 and the panel 2.
Polyphenylene oxide intermediate plate 3 is that polyphenylene oxide and HTPS carry out the Noryl intermediate plate that the blending and modifying processing makes.
Substrate 1 and panel 2 are that thickness is 0.80 millimeter thin aluminium metal sheet.
Intermediate plate 3 is that thickness is 2.40 millimeters Noryl intermediate plate.
(2) this metallic composite panel is by comprising the laminar product of thin aluminum metal sheet material as substrate 1 and panel 2, has its both sides to permeate polyphenylene oxide intermediate plate 3 in substrate 1 and panel 2 respectively embedding between substrate 1 and the panel 2.
Polyphenylene oxide intermediate plate 3 is that polyphenylene oxide and acrylonitrile-butadiene-styrene (ABS) carry out the Noryl intermediate plate that the blending and modifying processing makes.
Substrate 1 is that thickness is that 1.00 millimeters thin aluminium metal sheet and panel 2 is that thickness is 1.00 millimeters brass metallic plate.
Intermediate plate 3 is that thickness is 2.00 millimeters Noryl intermediate plate.
(3) this metallic composite panel is by comprising the laminar product of thin aluminum metal sheet material as substrate 1 and panel 2, has its both sides to permeate polyphenylene oxide intermediate plate 3 in substrate 1 and panel 2 respectively embedding between substrate 1 and the panel 2.
Polyphenylene oxide intermediate plate 3 is that polyphenylene oxide and high density polyethylene (HDPE) carry out the Noryl intermediate plate that the blending and modifying processing makes.
Substrate 1 is that thickness is 0.60 millimeter thin aluminium metal sheet, and panel 2 is that thickness is 0.60 millimeter stainless steel metal plate.
Intermediate plate 3 is that thickness is 2.80 millimeters Noryl intermediate plate.
(4) this metallic composite panel is by comprising the laminar product of thin aluminum metal sheet material as substrate 1 and panel 2, has its both sides to permeate polyphenylene oxide intermediate plate 3 in substrate 1 and panel 2 respectively embedding between substrate 1 and the panel 2.
Polyphenylene oxide intermediate plate 3 is that polyphenylene oxide and polyphenylene sulfide carry out the Noryl intermediate plate that the blending and modifying processing makes.
Substrate 1 is that thickness is 0.50 millimeter thin aluminium metal sheet, and panel 2 is that thickness is 0.50 millimeter titanium alloy sheet.
Intermediate plate 3 is that thickness is 3.50 millimeters Noryl intermediate plate.
(5) this metallic composite panel is by comprising the laminar product of thin aluminum metal sheet material as substrate 1 and panel 2, has its both sides to permeate polyphenylene oxide intermediate plate 3 in substrate 1 and panel 2 respectively embedding between substrate 1 and the panel 2.
Polyphenylene oxide intermediate plate 3 is that polyphenylene oxide and polyamide carry out the Noryl intermediate plate that the blending and modifying processing makes.
Substrate 1 is that thickness is 0.40 millimeter thin aluminium metal sheet, and panel 2 is that thickness is 0.40 millimeter bronze metallic plate.
Intermediate plate 3 is that thickness is 6.20 millimeters Noryl intermediate plate.
Claims (10)
1, a kind of metallic composite panel is by comprising the laminar product of thin metal blank as substrate and panel, and it is characterized in that has its both sides to permeate polyphenylene oxide intermediate plate in substrate and panel respectively embedding between substrate and the panel.
2, metallic composite panel as claimed in claim 1 is characterized in that the polyphenylene oxide intermediate plate is that polyphenylene oxide and HTPS carry out the Noryl intermediate plate that the blending and modifying processing makes.
3, metallic composite panel as claimed in claim 1 is characterized in that the polyphenylene oxide intermediate plate is that polyphenylene oxide and acrylonitrile-butadiene-styrene (ABS) carry out the Noryl intermediate plate that the blending and modifying processing makes.
4, metallic composite panel as claimed in claim 1 is characterized in that the polyphenylene oxide intermediate plate is that polyphenylene oxide and high density polyethylene (HDPE) carry out the Noryl intermediate plate that the blending and modifying processing makes.
5, metallic composite panel as claimed in claim 1 is characterized in that the polyphenylene oxide intermediate plate is that polyphenylene oxide and polyphenylene sulfide carry out the Noryl intermediate plate that the blending and modifying processing makes.
6, metallic composite panel as claimed in claim 1 is characterized in that the polyphenylene oxide intermediate plate is that polyphenylene oxide and polyamide carry out the Noryl intermediate plate that the blending and modifying processing makes.
7,, it is characterized in that intermediate plate is that thickness is 1.00～6.40 millimeters Noryl intermediate plate as claim 1 or 2 or 3 or 4 or 5 or 6 described metallic composite panels.
8, metallic composite panel as claimed in claim 1 is characterized in that substrate is that thickness is 0.20～1.00 millimeter metal sheet, and panel also is that thickness is 0.20～1.00 millimeter metal sheet.
9,, it is characterized in that substrate is an aluminium metal sheet as claim 1 or 8 described metallic composite panels.
10,, it is characterized in that panel is aluminium or zinc or titanium alloy or stainless steel or brass or bronze metallic plate as claim 1 or 8 described metallic composite panels.