CN1528699A - Efficient water reducing agent of amino-sulfonic acid and manufacturing process thereof - Google Patents
Efficient water reducing agent of amino-sulfonic acid and manufacturing process thereof Download PDFInfo
- Publication number
- CN1528699A CN1528699A CNA2003101080819A CN200310108081A CN1528699A CN 1528699 A CN1528699 A CN 1528699A CN A2003101080819 A CNA2003101080819 A CN A2003101080819A CN 200310108081 A CN200310108081 A CN 200310108081A CN 1528699 A CN1528699 A CN 1528699A
- Authority
- CN
- China
- Prior art keywords
- reducing agent
- sulfonic acid
- water
- efficiency water
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a new amido-sulfonic acid system high-efficiency dehydrating agent and manufacturing technique, its formula components (weight): amido-aryl-sulfonic acid or amido-alkyl-sulfonic acid 80-180 shares, arylphenol or alkylphenol 50-120 shares, urea 40-80 shares, sulphonating agent 20-80 shares, condensing agent 180-300 shares, catalyst 2-10 shares, water 300-500 shares, and alkali 20-150 shares. The manufacturing technique includes the following steps: 1), uniformly blending all the components in the reacting kettle, where the alkali is 0-120 shares, heightening the temperature to 50-105 deg.C, and making sulphonation, polycondensation and disproportionation reaction for 2-16 hours. 2), lowering the temperature to 30-55 deg.C, adding in alkali to adjust the pH to 8.5-10.5, and uniformly stirring. Its dehydration rate is high and its alkali content is lower and its free formaldehyde content is low.
Description
Technical field:
The invention belongs to water reducer and manufacturing process thereof, a kind of high efficiency water reducing agent and manufacturing process thereof that relates to concrete and mortar of more specifically saying so.
Background technology:
Water reducer is the admixture kind of consumption maximum in the concrete.Along with the architecture science development of technology, the high performance concrete that possesses characteristics such as high serviceability, good volume stability, high strength, high-durability becomes concrete developing direction.Thus, indispensable composition material-high efficiency water reducing agent in the high performance concrete has been proposed requirements at the higher level, it not only should have superior dispersion plasticizing effect, also want effectively to reduce and to prevent slump through the time lose, to satisfy the needs of construction technology.The high efficiency water reducing agent that uses mainly comprises modified lignin mahogany sulfonate, naphthalenesulfonate formaldehyde condensation compound, sulfonated melamine compound condenses, polycarboxylic acid etc. at present, these high efficiency water reducing agents are because of the characteristics of self performance, and its range of application all is subjected to restriction in various degree.As:
Sulfonated lignin are to use water reducer the earliest, and the history of six more than ten years has been arranged as the application of admixture.It is producing the waste liquid of paper pulp or fiber pulp, makes its abundant raw material, cheap through milk of lime neutralization, filtration, spraying drying, cost is low, but this water reducer water-reducing rate is low, slow setting, the amplitude that concrete ultimate compression strength improves is little, is restricted in concrete application.Handle by it being carried out modification, obtain modified lignin mahogany sulfonate, water-reducing rate increases, and retarding effect decreases, but effect and not obvious.
Naphthalenesulfonate formaldehyde condensation compound is one of the most representative current high efficiency water reducing agent kind, has moderate cost, water-reducing rate advantage of higher; But the ubiquity inferior suitability, slump is lost defectives such as very fast, is difficult to satisfy the construction needs of actual engineering.Though can suitably solve by methods such as compound slow setting components, also produced some new problems, influence the development and the weather resistance of early age strength of concrete.
The sulfonated melamine compound condenses, as high efficiency water reducing agent, its water-reducing property and naphthalene series high-efficiency water-reducing agent are very nearly the same, but this class water reducer be used for concrete mixture viscosity and slump through the time loss all bigger, and product cost price height, often the liquid form with low concentration exists, and storage period is shorter, synthetic technological condition requires control strict, therefore only is applicable to special engineering.
The polycarboxylic acid high efficiency water reducing agent has low-dosage, the advantage of high water reducing rate; But cost is too high, and present stage is difficult to popularize.
Chinese patent application number is 01129711.5 to disclose a kind of amido sulfoacid series high-efficiency water reducer and preparation method thereof.This water reducer has higher water-reducing rate; Mix this kind water reducer in cement paste or the concrete, can improve its intensity, and have bigger degree of mobilization.But contain Sulfite lignin in this kind water reducer component, and the xylogen in the Sulfite lignin is directly related with timber kind, the age of tree as raw material; Therefore, the xylogen composition changes greatly, and the molecular structure complexity makes the performance of Sulfite lignin produce difference, thereby influences the finished product---stablizing of amido sulfoacid series high-efficiency water reducer.And the content of free formaldehyde is higher in the finished product, and this will cause the pollution to environment, and influence builder's health to a certain extent.
Summary of the invention:
At problems of the prior art, the invention provides that a kind of volume that makes an addition to concrete or sand-cement slurry is low, water-reducing rate is high, slump through the time loss little, alkali content is lower, cost is low, the free low new and effective water reducer of formaldehyde content in the finished product.
The present invention is for reaching above purpose, be to realize by such technical scheme: a kind of novel sulfamic acid series high-efficiency water-reducing agent is provided, and its recipe ingredient (by weight) is: 80～180 parts of amino-aryl sulfonic acid or aminoalkyl group sulfonic acid, aryl phenol or 50～120 parts of alkylphenols, 40～80 parts in urea, 20～80 parts of sulphonating agents, 180～300 parts of condensing agents, 2～10 parts of catalyzer, 300～500 parts in water, 20～150 parts in alkali.
The manufacturing process of this kind high efficiency water reducing agent may further comprise the steps successively:
1), will be according to the aryl phenol of recipe ingredient or alkylphenol, urea, amino-aryl sulfonic acid or aminoalkyl group sulfonic acid, sulphonating agent, water, condensing agent, catalyzer, alkali with 0～120 part, drop in the reactor, evenly stir, be warming up to 50 ℃～105 ℃, carried out sulfonation, polycondensation, disproportionation reaction 2～16 hours;
2), the material in reactor temperature is reduced to 30 ℃～55 ℃, add alkali, regulate pH value to 8.5～10.5 of mixture, evenly stir, make liquid high efficiency water reducing agent.
Liquid product through the spraying drying operation, is made meal.
The high molecular weight water soluble polymer that the novel sulfamic acid series high-efficiency water-reducing agent that adopts above-mentioned fabrication process is a kind of non-bleed, have mononuclear aromatics type constitutional features.This water reducer is huge because of its spatial configuration of molecules, and is sterically hindered big, the polar group of being with many, polarity is strong, under electrostatic repulsion and sterically hindered acting in conjunction, cement granules is had good diminishing dispersion effect and dispersed hold facility.Especially under than the low water-cement ratio condition, it is more remarkable to strengthen the diminishing characteristics, and this lays a good foundation for the development trend of concrete high-performanceization.
After in concrete, adding water reducer of the present invention, other active blending material need not be added again, the high-strength concrete of C40～C80 can be prepared; Also can improve concrete various mechanical property and endurance quality; And the reinforcing bar non-corroding is endangered; Therefore be applicable to preparation pumping, concrete product such as strong, high-strength, high water-tight concrete and pile tube early.
In building-up process, added urea, can reduce cost on the one hand, the more important thing is the content that can effectively reduce free formaldehyde in the finished product, at utmost reduced pollution environment.
During use, high efficiency water reducing agent of the present invention can be incorporated in cement or the concrete with dry powder or liquid form, and volume is 0.25%～0.75% of cement or a weight concrete, and optimum volume is 0.4%～0.6%.(by solid substance)
Embodiment:
Embodiment 1: produce liquid high efficiency water reducing agent, its prescription and production craft step are as follows:
1), with 100 the gram phenol, 40 the gram urea, 130 the gram Sulphanilic Acid, 40 the gram Sodium Pyrosulfites, 307 the gram water, 240 the gram formaldehyde, 3 the gram ammonium persulphates, 100 the gram sodium hydroxide, insert in the reactor, the limit is evenly stirred the limit and is warming up to 70 ℃, reacts 15 hours;
2), the material in reactor temperature is reduced to 30 ℃, adding sodium hydroxide, the pH value to 8.5 of adjusting mixture, evenly stirring.
Above-mentioned liquid high efficiency water reducing agent is carried out spray drying treatment, finally make powder-like product.
Embodiment 2: produce liquid high efficiency water reducing agent, its prescription and production craft step are as follows:
1), with 120 the gram benzylphenols, 80 the gram urea, 170 the gram Sodium sulfanilates, 40 the gram sodium bisulfites, 350 the gram water, 200 the gram terephthalyl alcohols, 5 the gram ammonium persulphates, be placed in the reactor, the limit is evenly stirred the limit and is warming up to 60 ℃, reacts 15.5 hours;
2), the material in reactor temperature is reduced to 40 ℃, adding sodium hydroxide, the pH value to 9 of adjusting mixture, evenly stirring.
Above-mentioned liquid high efficiency water reducing agent is carried out spray drying treatment, finally make powder-like product.
Embodiment 3: produce liquid high efficiency water reducing agent, its prescription and production craft step are as follows:
1), with 80 the gram Resorcinol, 60 the gram urea, 90 the gram diamino benzene sulfonic acids, 30 the gram S-WATs, 310 the gram water, 220 the gram formaldehyde, 8 the gram ammonium persulphates, 50 the gram sodium hydroxide, put into reactor, the limit is evenly stirred the limit and is warming up to 80 ℃, reacts 13 hours;
2), the material in reactor temperature is reduced to 50 ℃, adding sodium hydroxide, the pH value to 10 of adjusting mixture, evenly stirring.
Above-mentioned liquid high efficiency water reducing agent is carried out spray drying treatment, finally make powder-like product.
Embodiment 4: produce liquid high efficiency water reducing agent, its prescription and production craft step are as follows:
1), with 50 gram styrenated phenols, 10 gram p-cresols, 40 gram urea, 150 gram aniline sulfonic acids, 60 gram Sodium Pyrosulfites, 400 gram water, 240 gram formaldehyde, 10 gram ammonium persulphates, 30 gram sodium hydroxide, put into reactor, the limit is evenly stirred the limit and is warming up to 90 ℃, reacts 10.5 hours;
2), the material in reactor temperature is reduced to 55 ℃, adding sodium hydroxide, the pH value to 10.5 of adjusting mixture, evenly stirring.
Above-mentioned liquid high efficiency water reducing agent is carried out spray drying treatment, finally make powder-like product.
Embodiment 5: produce liquid high efficiency water reducing agent, its prescription and production craft step are as follows:
1), with 80 gram phenol, 60 gram urea, 100 gram Sulphanilic Acid, 60 Sodium sulfanilates, 60 gram sodium bisulfites, 10 gram S-WATs, 450 gram water, 280 gram formaldehyde, 9 gram ammonium persulphates, 70 gram sodium hydroxide, put into reactor, the limit is evenly stirred the limit and is warming up to 100 ℃, reacts 2 hours;
2), the material in reactor temperature is reduced to 45 ℃, adding sodium hydroxide, the pH value to 8.5 of adjusting mixture, evenly stirring.
Above-mentioned liquid high efficiency water reducing agent is carried out spray drying treatment, finally make powder-like product.
Some testing datas of using high efficiency water reducing agent of the present invention below are provided, its effect are described:
Table 1 admixture water reducer of the present invention and clean slurry degree of mobilization (mm) contrast under different volumes of other water reducer
| Title | Volume 0.5% | Volume 1% | Volume 1.2% | Volume 1.5% | Volume 1.8% | Volume 2% |
| The present invention | ????100 | ????180 | ????220 | ????250 | ????260 | ????265 |
| Naphthalene series high-efficiency water-reducing agent | ????75 | ????130 | ????165 | ????200 | ????220 | ????230 |
| The trimeric cyanamide series high-efficiency water-reducing agent | ????65 | ????120 | ????165 | ????190 | ????200 | ????210 |
The present invention of table 2 admixture and other water reducer water-reducing rate, slump, concrete performance contrast
| Title | Volume (%) | Water-reducing rate (%) | Slump (mm) | Incompressible strength ratio (Mpa/%) | ||
| 3 days | 7 days | 28 days | ||||
| The present invention | ????1.5 | ????20.0 | ????70 | ??28.8/200 | ??39.4/187 | ??52.2/167 |
| Naphthalene series high-efficiency water-reducing agent | ????1.5 | ????15.4 | ????90 | ??25.9/180 | ??30.9/147 | ??40.5/130 |
| The trimeric cyanamide series high-efficiency water-reducing agent | ????1.5 | ????14.5 | ????65 | ??22.6/157 | ??31.8/151 | ??44.6/143 |
Table 3 water reducer of the present invention and other water reducer are to cement setting time influence contrast
| Title | Volume (%) | Initial set (time-minute) | Final set (time-minute) |
| The present invention | ????1.5 | ????6-40 | ????8-30 |
| Naphthalene series high-efficiency water-reducing agent | ????1.5 | ????2-55 | ????5-44 |
| The trimeric cyanamide series high-efficiency water-reducing agent | ????1.5 | ????2-15 | ????4-40 |
The present invention of table 4 admixture and the contrast of naphthalene series high-efficiency water-reducing agent concrete performance
| Cement type | Water reducer | Water consumption (Kg/m 3) | Water cement ratio | Water-reducing rate (%) | Slump (mm) | Ultimate compression strength/compressive strength rate (Mpa) | |||
| Title | Volume (%) | ||||||||
| ??3d | ??7d | ??28d | |||||||
| Tiger Mountain 42.5 | The present invention | ??1.5 | ????155 | ????0.47 | ????22.5 | ????70 | ??28.8 ??/200 | ??39.4 ??/187 | ??52.2 ??/167 |
| Naphthalene system | ??1.5 | ????160 | ????0.48 | ????17.9 | ????90 | ??25.9 ??/180 | ??30.9 ??/147 | ??40.5 ??/130 | |
| It crane 42.5 | The present invention | ??1.5 | ????163 | ????0.49 | ????22.4 | ????75 | ??28.3 ??/179 | ??35.0 ?/155 | ??44.3 ??/138 |
| Naphthalene system | ??1.5 | ????175 | ????0.53 | ????16.6 | ????80 | ??22.9 ??/145 | ??31.8 ??/141 | ??42.5 ??/132 | |
| Fringe river 42.5 | The present invention | ??1.5 | ????162 | ????0.49 | ????20.9 | ????70 | ??38.6 ??/215 | ??42.4 ??/194 | ??62.7 ??/192 |
| Naphthalene system | ??1.5 | ????172 | ????0.52 | ????16.1 | ????90 | ??28.5 ??/159 | ??33.7 ??/155 | ??49.2 ??/151 | |
| Hangzhoupro mud 42.5 | The present invention | ??1.5 | ????173 | ????0.52 | ????24.1 | ????70 | ??28.2 ??/231 | ??30.6 ??/185 | ??45.6 ??/184 |
| Naphthalene system | ??1.5 | ????183 | ????0.55 | ????19.7 | ????80 | ??23.1 ??/189 | ??30.8 ??/186 | ??39.7 ??/160 | |
| Money tide 42.5 | The present invention | ??1.5 | ????156 | ????0.47 | ????20.0 | ????80 | ??36.8 ??/161 | ??47.4 ??/150 | ??57.6 ??/134 |
| Naphthalene system | ??1.5 | ????165 | ????0.50 | ????15.4 | ????80 | ??30.9 ??/136 | ??42.9 ??/136 | ??52.6 ??/122 | |
Annotate: the employed water reducer of above form all is that content is 40% liquid water reducer
The above only is several embodiments of the present invention; should be pointed out that for the person of ordinary skill of the art, can also make many modification and improvement; for example also can use other catalyzer, all modification or improvement all should be considered as protection scope of the present invention.
Claims (6)
1, a kind of novel sulfamic acid series high-efficiency water-reducing agent is characterized in that the recipe ingredient (by weight) of this water reducer is: 80～180 parts of amino-aryl sulfonic acid or aminoalkyl group sulfonic acid, aryl phenol or 50～120 parts of alkylphenols, 40～80 parts in urea, 20～80 parts of sulphonating agents, 180～300 parts of condensing agents, 2～10 parts of catalyzer, 300～500 parts in water, 20～150 parts in alkali.
2, a kind of novel sulfamic acid series high-efficiency water-reducing agent according to claim 1 is characterized in that: described amino-aryl sulfonic acid or aminoalkyl group sulfonic acid are that diamino benzene sulfonic acid, aniline sulfonic acid, methylamino Phenylsulfonic acid, Sulphanilic Acid and/or Sodium sulfanilate are at least a.
3, a kind of novel sulfamic acid series high-efficiency water-reducing agent according to claim 1, it is characterized in that: described aryl phenol or alkylphenol are that Resorcinol, benzylphenol, phenol, styrenated phenol, p-cresol and/or Ortho Cresol are at least a.
4, a kind of novel sulfamic acid series high-efficiency water-reducing agent according to claim 1, it is characterized in that: described sulphonating agent is that Sodium Pyrosulfite, sodium bisulfite and/or S-WAT are at least a; Described condensing agent is terephthalyl alcohol and/or formaldehyde; Described catalyzer is an ammonium persulphate; Described alkali is sodium hydroxide.
5, a kind of manufacturing process of novel sulfamic acid series high-efficiency water-reducing agent is characterized in that may further comprise the steps successively:
1), will be according to the aryl phenol of recipe ingredient or alkylphenol, urea, amino-aryl sulfonic acid or aminoalkyl group sulfonic acid, sulphonating agent, water, condensing agent, catalyzer, alkali with 0～120 part, drop in the reactor, evenly stir, be warming up to 50 ℃～105 ℃, carried out sulfonation, polycondensation, disproportionation reaction 2～16 hours;
2), the material in reactor temperature is reduced to 30 ℃～55 ℃, add alkali, regulate pH value to 8.5～10.5 of mixture, evenly stir, make liquid high efficiency water reducing agent.
6, the manufacturing process of a kind of novel sulfamic acid series high-efficiency water-reducing agent according to claim 5 is characterized in that: described liquid high efficiency water reducing agent through the spraying drying operation, is made powder-like product.