CN1491975A - 一种一次性全降解制品的制备工艺 - Google Patents
一种一次性全降解制品的制备工艺 Download PDFInfo
- Publication number
- CN1491975A CN1491975A CNA02133255XA CN02133255A CN1491975A CN 1491975 A CN1491975 A CN 1491975A CN A02133255X A CNA02133255X A CN A02133255XA CN 02133255 A CN02133255 A CN 02133255A CN 1491975 A CN1491975 A CN 1491975A
- Authority
- CN
- China
- Prior art keywords
- degradation product
- full degradation
- water
- temperature
- lasts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及餐具生产领域,具体说是一种全降解餐具制品、工艺美术制品和包装材料的生产方法。针对市场推出的可降解餐具,存在着强度差、易变形、成本高等诸多缺陷,发明了一种新产品的生产工艺。其特征是淀粉为70~30%,食用滑石粉为60~10%,植物纤维12~6%;稻壳粉为50~40%;制备工艺,首先配料,再经过搅拌、高温定型,即可生产出成品。特点是工艺简单,产品可降解性好,成本低,不仅可作餐具容器,亦可作工艺品、包装材料,易被市场接受。在餐饮、美术工艺品行业试用,颇受欢迎。
Description
技术领域
本发明涉及人们日常餐饮容器制品、工艺美术制品和包装制品行业,具体说是采用农副产品及农业废弃物为原材料,生产餐饮容器、工艺美术制品和包装材料的生产方法。
背景技术
方便餐具以塑料等物质作原材料,造成了严重的环境污染;已在市场推出的可降解餐具,其主要原料为纸浆,或者是大米粉,该产品虽然有利于环境保护,但该产品的致命缺陷是产品强度差,易变形,成本高,工艺繁琐。
发明内容
本发明的目的是针对前述传统产品存在的缺陷,研制发明了一种新工艺,制造出了新的环保产品,以便达到降低产品成本、适于市场需求、保护环境的目的。
一次性全降解制品的制备工艺,包括餐具、工艺品、包装物的生产方法,其特征是:
A.全降解制品原料配方:
a)可降解碗、盘、杯餐具制品配方;
淀粉:70~30%;
轻质碳酸钙:15~5%;
食用级滑石粉:50~10%;
植物纤维:12~6%;
食用石膏:6~2%;
甲基纤维素:8~4%;
单甘子:3~1.5%;
食用胶:3~1.5%;
b)全降解工艺制品、包装物制品原料配方:
稻壳粉:50~40%;
植物纤维:12~6%;
重质碳酸钙:12~7%;
淀粉:30~10%;
单甘子:3.0~1.5%;
甲基纤维素:8~4%;
石膏:6~2%;
增强剂:2~1%;
c)淋涂层原料及用量:
原料采用食用级防水、防油淋涂液和环保漆;
用量:每个制品5~3g;
B.全降解制品制备工艺:
全降解制品的制备工艺:首先配料;接着按100∶35的比例加水进行搅拌,水温为100℃,历时6~7分钟;之后,进行高温定型,温度要求在180~200℃,历时35~40秒;再之后,进行冷却,12小时自然降温、收缩;接着进入涂层工序,温度控制在80~90℃,历时7~8分钟;最后,采用紫外线进行消毒杀菌。
本发明的积极效果是,工艺简单,成品率高;特别是淀粉含量适中,植物纤维量配比合理,产品强度高,韧性好,成本低,市场易接受,尤其是消除了工艺品和包装物的环境污染,市场推广应用前途广阔。
附图说明
图1,本发明的工艺流程图。
具体实施方式
实施例1
生产全降解餐具碗制品。按如下比例进行配料(以重量%计算):
1)土豆淀粉40;2)轻质碳酸钙6;3)食用滑石粉40;4)麦杆纤维6;5)食用石膏2;6)甲基纤维素4;7)单甘子1;8)食用级瓜尔豆胶1。
完成配料后,投入搅拌器内,并按100∶35的比例加入清水,水温为100℃,搅拌6~7分钟;搅拌均匀后,压制碗胚,并进行高温热定型,定型温度为180~200℃,时间为35~40秒;接着进行12小时冷却回原,使制品自然收缩;之后,进入涂层工序,温度控制在80~90℃,时间需7~8分钟,涂层物质采用防水、防油的食用淋涂液,用量按每个制品3~5g的剂量淋涂;最后,用紫外线消毒杀菌,卫生指标合格后,即可包装为成品。
实施例2
生产全降解餐具口杯。按以下原料配比(以重量%比计)进行配料。原料及配比为:
1)红薯淀粉38;2)轻质碳酸钙9;3)食用滑石粉30;4)稻草纤维9;5)食用石膏4;6)甲基纤维素6;7)单甘子2;8)食用级瓜尔豆胶2。
配料完成后,投入搅拌器内,并加入40%的水,水温达100℃搅拌,经过6~7分钟时间,搅拌均匀后即可压制成型,之后,在180~200℃温度条件下,经过45秒时间进行高温定型,随后经过10个小时的冷却回原;再转入涂层工序,对每个制品用防水、防油淋涂液进行淋涂,每个口杯按4克,进行涂层;再进行紫外线杀菌消毒后,进行包装入库。整个制品即生产完毕。
实施例3
生产全降解餐具盘。以重量百分比计,进行配料,原料配比:
木薯淀粉47.5;轻质碳酸钙5.0;食用滑石粉33.0;玉米桔杆纤维6.0;
食用石膏2.0;甲基纤维素4.0;单甘子1.0;食用瓜尔豆胶1.5。
按上述配方配料后,投入搅拌器内,再加入100∶30的清水,升温为100℃,搅拌6~7分钟;搅拌均匀后,压制盘胚,并进行高温热定型,定型温度控制在190℃,时间为40秒;接着进行12小时的自然冷却回原;之后,转入涂层工序,温度控制在85℃,时间需8分钟,涂料为食用淋涂液,用量按每个盘表面淋涂5g量控制投料速度;接着进入杀菌消毒工序,采用紫外线杀菌,符合卫生指标后,进行包装,即为生产成品。
实施例4
生产全降解苹果、香蕉、圣诞老人工艺品。首先进行原料配制,原料以重量百分比计算,具体配方如下:
稻壳粉45;稻草植物纤维10;重质碳酸钙12;木薯淀粉20;
单甘子1;甲基纤维素5;石膏6;纸浆填充剂1。
配料完成后,将物料投入搅拌器内,并加入30%的水,进行搅拌,水温为100℃沸水状态,时间约7分钟;搅拌后,按苹果、香蕉、圣诞老人等工艺品分别压制成型,接着升温至200℃,经过时间40秒后,即可转入冷却工序,经过12小时自然冷却后回原的制品,再进入涂层工序,温度控制在90℃,时间8分钟,涂层采用环保漆作涂料,每个制品涂料用量控制在3g左右;进入包装工序前要进行消毒。
实施例5
生产全降解包装材料。配料按重量百分比计量,具体配比如下:
稻壳粉50;稻草植物纤维11;重质碳酸钙8.5;木薯淀粉20;
单甘子1.5;甲基纤维素4.0;石膏4.0;纸浆1.0。
配料完成后,转入搅拌工序,搅拌完成后,进入高温定型工序,定型后的产品经过涂层、消毒杀菌后,即可进行包装入库。各工序工艺未明之处,均与前述实施例同。
Claims (1)
1.一次性全降解制品的制备工艺,包括餐具、工艺品、包装物及其生产方法,其特征是:
A.全降解制品原料配方:
a)可降解碗、盘、杯餐具制品配方;
淀粉:70~30%;
轻质碳酸钙:15~5%;
食用级滑石粉:60~10%;
植物纤维:12~6%;
食用石膏:6~2%;
甲基纤维素:8~4%;
单甘子:3~1.5%;
食用胶:3~1.5%;
b)全降解工艺制品、包装物制品原料配方:
稻壳粉:50~40%;
植物纤维:12~6%;
重质碳酸钙:12~7%;
淀粉:30~10%;
单甘子:3.0~1.5%;
甲基纤维素:8~4%;
石膏:6~2%;
增强剂:2~1%;
c)淋涂层原料及用量:
原料采用食用级防水、防油淋涂液和环保漆;
用量:按每个制品5~3g;
B.全降解制品制备工艺:
全降解制品的制备工艺:首先配料;接着按100∶35的比例加水进行搅拌,水温为100℃沸水,历时6~7分钟;之后,进行高温定型,湿度要求在180~200℃,历时35~40秒;再之后,进行冷却回原,12小时自然降温、收缩;接着进入涂层工序,温度控制在80~90℃,历时7~8分钟;最后,采用紫外线进行消毒杀菌。