CN1488485A - Product with plastic and printed sheet joint and preparing process thereof - Google Patents
Product with plastic and printed sheet joint and preparing process thereof Download PDFInfo
- Publication number
- CN1488485A CN1488485A CNA031400418A CN03140041A CN1488485A CN 1488485 A CN1488485 A CN 1488485A CN A031400418 A CNA031400418 A CN A031400418A CN 03140041 A CN03140041 A CN 03140041A CN 1488485 A CN1488485 A CN 1488485A
- Authority
- CN
- China
- Prior art keywords
- printed sheet
- sheet material
- goods
- plastic cement
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention refers to a product and the producing craft which combines with print slice material. The current plastic products are all single layer products which are crisp. The invention uses carving, silk printing, and heat transmitting print, adhering and double-layer paper-laying method. The invention uses double layer structure to print out each kind of picture, color or 3D print slice. Through cutting, heating, forming, and produces various product with high tenacity and variable surface effect. The craft is simple and the cost is low.
Description
(1) technical field
The present invention relates to a kind of goods and preparation technology thereof that plastic cement is combined with printed sheet material.
(2) background technology
At present people usually increase the aesthetic feeling and the added value of plasthetics with methods such as engraving, silk (rolling) seal, hot transfer printing, stickup gummed papers, but effect is not good enough, and product is frangible, easily split, and influence service life, and the while, there was following defective respectively in various technologies:
1. artistic carving is made: pattern that engraving is relevant on product mold or reason line, and goods use corresponding pattern after the injection mo(u)lding, but only figuratum profile and anaglyph do not have any color on the sense organ.
2. silk (rolling) is printed and is made technology: must be earlier the goods injection mo(u)lding to be come out, then with silk-screen or roll printing wire mark on product surface, this technology what a color of seal is earlier printed another color again, how many colors just will be printed how many times, because be subjected to the performance impact of operational method and machine, the conventional pattern color bits is put incorrect, influences product quality, the special colored pattern of general limitation silk-screen has gradual change, in riotous profusion part of color, a gorgeous effect of color and can't accomplish that the printing of Ke's formula is the sort of.
3. caloric transfer printing technology is made: though this technology is also earlier with the goods injection mo(u)lding, to produce figuratum plastic film then in advance contacts with goods, be placed on the heat favourable turn of having heated, the pattern of heat effect on film, pattern is because of being subjected to the heat of solution transfer printing on product surface, but this complex process, operation is many, and loss is big and production cost is high, though the plastic film printing can be the printing of Ke's formula, but the surface of limitation product is the light face, and milled sand surface, rubber face, inferior slurry face just can't be made.
4. barbola work is made: though this technology is also earlier with the goods injection mo(u)lding, the adhesive sticker paster that will print in advance then (can be gummed paper), again with manually directly being attached on the surface of product, this technology is to paste with adhesive sticker, not only come off easily, and effect is not attractive in appearance, and goods and pattern fail moltenly to make moist easily or to meet damage by water bad for one, particularly papery paster on the sense organ.
5. bilayer is put the making of paper technology: this technology most important condition is that goods must be double-deck, divide inside and outside two-layer, and skin must be transparent, technology also is the ectonexine mould-injection moulding of elder generation with goods, again the scraps of paper that print are put in the gap two-layer inside and outside goods, and then with the ectonexine fixed combination, see the scraps of paper pattern of the inside by outer field perspective, but owing to be just can see pattern through perspective, and the scraps of paper can not be close to outer wall, can not with the goods one that mixes, true to nature inadequately on the sense organ, do not have direct sense organ.
(3) summary of the invention
Being of purpose of the present invention provide a kind of quality height, it is broken to be difficult for, goods and the preparation technology thereof that plastic cement all over the body combines with printed sheet material viewed and admired and be used in to collection.
Product of the present invention can be the goods of round platforms such as water tumbler, kettle, pen container, vase or column type, it also can be the disc flat article, material is plastic cement and plastic cement printed sheet material, the plastic cement printed sheet material is that PP, PVC, PET material are main, thickness is between the 0.2-0.6mm, pattern on the plastic cement printed sheet material adopts the printing of Ke's formula, can make light face, milled sand surface, rubber face, mute plasm surface, also can make the 3D solid.
Preparation technology when making round platform or cylindrical product among the present invention is:
1. selection and cutting: choose the plastic cement printed sheet material that is printed with various patterns, color through Ke formula, carry out cutting according to the apparent size of product.
2. heat: the plastic cement printed sheet material that cuts is placed in the heating box heats, temperature is 60 °～70 ℃.
3. setting: the plastic cement printed sheet material after will heating is rolled in the round table-like cover half die cavity that is placed in mould, because the plastic cement printed sheet material has certain force of strain to be close on the mold cavity wall.
4. make finished product: set injection time according to different product, close film injection moulding injection, after the time finished, automatic die sinking took out goods and gets final product.Because use plastic material injection moulding identical with plastic cement printed sheet material attribute or that mix, plasthetics can be bonded together automatically with sheet material.Simultaneously, because the plastic cement printed sheet material is reduced by the temperature and the error of goods cooling contraction, thereby can guarantee the bonding quality of product.
In the technology when making flat article such as disc among the present invention, do not contain the setting program, remaining is identical with manufacturing round platform or cylindrical product technology.
The invention has the advantages that toughness height, good hand touch, easy to use, be beneficial to popularization, it is compared in traditional handicraft; Also possess following characteristics:
1, technological operation is simple: directly sheet is put into the mold injection molding combination, do not had technology making step complexity such as silk-screen, hot transfer printing, stickup;
2, operation uniqueness: have only unique injection moulding production process, and traditional technology is all through the injection moulding production process, again through the secondary operations operation, even more production process just can be finished surperficial figuratum goods;
3, product perfect associativity: because the plastic material that injection molding process uses is identical or mix with the plastic sheet attribute of printed patterns, sheet material becomes goods with the fused fully one of plastic cement after injection mo(u)lding, has more the difference that fused all-in-one-piece has matter than traditional stickup, hot transfer printing, two-layer process;
4, surface effect polytropy: because the pattern effect that Ke's formula prints is riotous with colour, dazzlingly beautiful, and can make 3D solid, change effect, and can make light face, milled sand surface, rubber face, mute plasm surface on the feel, this is that traditional handicraft is made and can't be accomplished;
5, view and admire valency matter height: the goods that goods that this technology is made and traditional fabrication go out have outside the equal use value, and goods appearance material sheet is the effect that Ke's formula prints, pattern can multifariously change, and color is varied, and this is the effect that other operation can't be accomplished.
6, cost of manufacture is low: since operation single, not as traditional silk-screen, hot transfer printing, barbola work sample multiple operation, defect rate is low, so cost of manufacture is relatively low.
(4) description of drawings
Fig. 1 is the overall structure schematic diagram of plastic cups goods of the present invention.
1 is plastic layer among the figure, the 2nd, and the plastic cement printed sheet material.
(5) specific embodiment
With most preferred embodiment the present invention is described in further details below:
Product of the present invention is a water tumbler, and material is plastic cement and plastic cement printed sheet material, and the plastic cement printed sheet material is the PP material, and thickness is between the 0.2-0.6mm, and the pattern on the plastic cement printed sheet material adopts the printing of Ke's formula.
Preparation technology is:
1. selection and cutting: choose the plastic cement printed sheet material that is printed with pattern, color through Ke formula, carry out cutting according to the apparent size of product.
2. heat: the plastic cement printed sheet material that cuts is placed in the heating box heats, temperature is 60 °～70 ℃.
3. setting: the plastic cement printed sheet material after will heating is rolled in the round table-like cover half die cavity that is placed in mould, because the plastic cement printed sheet material has certain force of strain to be close on the mold cavity wall.
4. make finished product: set injection time according to different product, the mold-closing injection injection, after the time finished, automatic die sinking took out goods and gets final product.
Claims (5)
1, the goods that combine with printed sheet material of a kind of plastic cement is characterized in that it is a double-decker, and its internal layer is a plastic cement, and skin is PP, PVC, PET printed sheet material.
2, the goods that combine with printed sheet material of a kind of plastic cement according to claim 1, the depth that it is characterized in that described printed sheet material is 0.2～0.5mm.
3, the goods that combine with printed sheet material of a kind of plastic cement according to claim 1 is characterized in that described goods can be plastic cups, kettle, pen container, vase and disc.
4, the preparation technology of the goods that combine with printed sheet material of a kind of plastic cement is characterized in that it being plastic sheet with the printing of Ke's formula, through the selection cutting, heat, setting, mold-closing injection make finished product.
5, the preparation technology of the goods that combine with printed sheet material of a kind of plastic cement is characterized in that described heating is 60～70 ℃.