CN1475538A - Low temperature baked fluorocarbon paint and its preparation method - Google Patents
Low temperature baked fluorocarbon paint and its preparation method Download PDFInfo
- Publication number
- CN1475538A CN1475538A CNA031459323A CN03145932A CN1475538A CN 1475538 A CN1475538 A CN 1475538A CN A031459323 A CNA031459323 A CN A031459323A CN 03145932 A CN03145932 A CN 03145932A CN 1475538 A CN1475538 A CN 1475538A
- Authority
- CN
- China
- Prior art keywords
- resin
- fluoro
- agent
- fluorine
- consumption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A F-C paint suitable for low-temp baking is prepared from fluorine resin, cross-linking agent, pigment, assistant and mixed solvent. Its advantages are low temp baking, high stability, low cost and easy repair.
Description
Technical field
The present invention relates to coating industry, specifically, relate to a kind of fluorine carbon lacquer of low-temperature bake, and preparation method thereof.
Background technology
Fluorine carbon Baking Paint is applied to the decoration and the protection of external wall, aluminum screen wall link plate, coiled material and steel in the U.S., Japan, the history in existing more than 20 year.At present both at home and abroad architectural aluminum section is used fluorocarbon coating market, is mainly internationally famous coating manufacturer and occupies, as PPG, LILLY coating, Japanese Northwest coating, ippon coating etc.About fluorine carbon Baking Paint aspect, Italian Ao Simeng (AUSIMONT) company applied in 1999 once that patent, its patent No. were EP.960918A2 (1999.12.1).This series products is a main film forming substance with polyvinylidene difluoride (PVDF) (PVDF), needs fusion plastification film forming under hot conditions, and storing temperature is 232～250 ℃, and storing time is 10～20 minutes; The storing temperature height, energy consumption is big, and the high gloss of paint film is about 50, does not possess high-decoration, and because higher (120～230 yuan/kg), be difficult to be accepted by users, market is limited in this fluorine carbon Baking Paint market price.
Calendar year 2001, but a kind of fluorine carbon lacquer of low-temperature bake has been invented by Zhenbang Fluorine-coating Co., Ltd., Dalian, and applied for patent, its patent No. is CN1325928A (2001.12.12).Though this fluorine carbon Baking Paint has overcome the above-mentioned defective of inclined to one side fluorine coating (PVDF), owing to be the acid catalysis system, still there is the problem of the package stability difference of coating, therefore, be badly in need of solving the problems such as package stability of fluorine carbon lacquer coating, become the task of top priority.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art part, and a kind of fluorine carbon lacquer for preparing the trifluoro system low-temperature bake easy, that performance is good is provided, and preparation method thereof.
The object of the invention can realize by following measure:
The fluorine carbon lacquer of low-temperature bake contains fluoro-resin, linking agent, pigment, auxiliary agent and mixed solvent, the weight ratio fluoro-resin between each component: linking agent: pigment: auxiliary agent: mixed solvent=1: 0.1～0.25: 0～0.37: 0.02～0.04: 0.1～0.3; Fluoro-resin is by trifluorochloroethylene, vinyl fatty ester, hydroxyl vinyl ether and the aliphatics olefin(e) acid is quarternary copolymerized forms, its hydroxyl value 40～60mg KOH/g, and carboxylic value 3～8mg KOH/g, solid content 40～70%, and fluorine content is 15～45%; Linking agent adopts blocked isocyanate, as TDI, IPDI, HDI; Auxiliary agent is two kinds to four kinds mixtures among four kinds, and auxiliary agent is as follows:
(1) wetting dispersing agent, composition are modified polyurethane, and as EFKA-4047, BYK-161, BYK-163, consumption is 0～0.08 times of fluoro-resin;
(2) flow agent, composition are organically-modified siloxanes or fluorine-carbon modified polyacrylic acid, and as EFKA-3033, EF KA-3777, consumption are 0.01～0.02 times of fluoro-resin;
(3) defoamer, composition is a polysiloxane solution, as BYK-066, consumption is 0～0.008 times of fluoro-resin;
(4) anti-flooding agent, composition is the modification nonionic silicones, as DP-903, consumption is 0～0.008 times of fluoro-resin;
Solvent is dimethylbenzene, N-BUTYL ACETATE, S100 and dibasic ester, the mixture by 1: 0.2～0.4: 0.2～0.4: 0.05～0.1;
The linking agent blocked isocyanate good with the fluoro-resin miscible characteristic is the HDI tripolymer;
The preparation method by the formulation weight ratio, adds part fluoro-resin and wetting dispersing agent, and stirring all, the back adds pigment, give dispersion, grind, reach the regulation fineness, add the residual fluorine resin by formula ratio, linking agent and various auxiliary agent are adjusted viscosity, filter, through metering packing after the assay was approved;
Baking condition is: storing temperature: 130～160 ℃, and storing time: 20～30 minutes.
Trifluoro system low-temperature bake fluorine carbon lacquer can also contain or not contain a spot of UV light absorber, 5060 of preferred Ciba company (CIBA), and consumption is 0.01～0.02 times of fluoro-resin.
Raw material is described below:
1, three fluoro-resin: be product by our company's development and production, patent applied for, the patent No. is 95111961.3, denomination of invention is " a fluoro-containing coating compoistion and method of use ", product index: hydroxyl value 40～60mg KOH/g, carboxylic value 3～8mg KOH/g, solid content 40～70%, fluorine content are 15～45%.Three fluoro-resin of other production of units as long as performance index are qualified, can also adopt.
2, TDI: tolylene diisocyanate.
3, IPDI: isophorone diisocyanate.
4, HDI: hexamethylene diisocyanate.
5, BYK-161, BYK-163: be Bi Ke chemical company product.
6, EFKA-4047, EFKA-3033: be EFKA company product.
7, DP-903: be the modest company of moral product.
8, S100: the solvent code name is aromatic hydrocarbon, commercially available or imported product.
9, dibasic ester: be the mixture of dibasic ester,, be commercially available or imported product by the mixture of Succinic acid dimethylester, Methyl glutarate, dimethyl adipate.
The present invention has following advantage compared to existing technology:
1. trifluoro system low-temperature bake fluorine carbon of the present invention lacquer since the blocked isocyanate that adopts at 130 ℃ of deblocking, so paint film can be 130～160 ℃ of film forming, storing time is 20～30 minutes; Storing temperature is low, and power consumption is few;
2. be fit to airless spraying, the electrostatic spraying operation both can adopt one to be coated with a baking mode application, also can adopt the wet wet mode application of bumping, and can satisfy streamline operration, and technology is simple, and province's energy saves time;
3. repeat to cover with paint, lacquer, colour wash, etc. and repair easily;
4. coating surface can be low, and pollution resistance is good, easy cleaning;
5. paint film mechanical property excellence;
6. paint film ageing-resistant performance excellence;
7. can prepare high gloss (more than 80) and inferior light fluorine carbon Baking Paint;
8. excellent storage stability, period of storage is more than 1 year, improves 2～3 times than acid catalysis system.
Embodiment
Enumerate seven embodiment and four comparing embodiments below, the present invention is further specified, but be not limited only to these embodiment.
Embodiment 1
In the beaker of 1000ml, add fluoro-resin (53%) 300g, BYK-1630.80g, solvent 20g stirs, add titanium dioxide (rutile-type) 210g, give and disperse to grind with sand mill afterwards, add fluoro-resin (53%) 297g when reaching granularity 20 μ m, blocked isocyanate 95g, EFKA-30334.2g, EFKA-3777 7g and solvent 61.6g after mixing, adjust viscosity, solids content, detection performance, filtration, packing.
Embodiment 2～7
Operation steps and reaction conditions are with embodiment 1, and concrete consumption of raw material such as table 1 make trifluoro system low-temperature bake fluorine carbon lacquer performance, as table 2.
Table 1. embodiment 1～7 proportioning raw materials wt/wt
| Material name | Example 1 | Example 2 | Example 3 | Example 4 | Example 5 | Example 6 | Example 7 |
| Fluoro-resin (53%), g | ??597 | ??597 | ??597 | ????597 | ??597 | ??597 | ??597 |
| Blocked isocyanate, g | ??95 | ??95 | ??90 | ????100 | ??105 | ??110 | ??100 |
| Rutile type Titanium Dioxide, g | ??210 | ??- | ??110 | ????120 | ??- | ??- | ??150 |
| Medium chrome yellow medium yellow, g | ??- | ??- | ??- | ????60 | ??200 | ??120 | ??- |
| Phthalocyanine blue, g | ??- | ??- | ??15.37 | ????- | ??- | ??35.22 | ??29.1 |
| Organic red, g | ??- | ??- | ??- | ????10 | ??- | ??- | ??- |
| Wetting dispersing agent, g | ??0.80 | ??- | ??0.40 | ????0.50 | ??0.50 | ??0.50 | ??0.50 |
| Flow agent, g | ??11.2 | ??8 | ??8.5 | ????10 | ??8 | ??8 | ??10 |
| Defoamer, g | ??- | ??3 | ??4 | ????3 | ??3 | ??3 | ??3 |
| Anti-flooding agent, g | ??- | ??- | ??4 | ????3.5 | ??- | ??4 | ??4 |
| Solvent, g | ??81.6 | ??120 | ??135 | ????140 | ??130 | ??135 | ??135 |
Table 2. film performance test data
Comparative example 1～4
| Test event | Example 1 | Example 2 | Example 3 | Example 4 | Example 5 | Example 6 | Example 7 |
| Gloss (60 °) | ??85 | ????82 | ????81 | 83 | 80 | ??82 | 81 |
| Pencil hardness | ??2H | ????2H | ????2H | 2H | 2H | ??2H | 2H |
| Sticking power (drawing circle method/level) | ??1 | ????1 | ????1 | 1 | 1 | ??1 | 1 |
| Snappiness/mm flawless, nothing comes off | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified |
| Shock resistance 50 kgcm | By | By | By | By | By | By | By |
| Acid resistance 10%H 2SO 4, 48 hours no changes | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified |
| Alkali resistance 10%NaOH, 48 hours no changes | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified |
| Resistance to salt water 3%NACL, 48 hours no changes | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified |
| Storage stability test (50 ℃), not gel in 740 hours | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified | Qualified |
| Ageing resistance, 4000 hours no changes | No efflorescence does not have be full of cracks, does not have and bubbles, and nothing comes off, and allows variable color and loss of gloss | ||||||
Operation steps and reaction conditions are with embodiment 1, and raw material is specifically used
Amount makes fluorine carbon Baking Paint performance relatively, as table 4 as table 3.
Table 3. comparative example 1～4 proportioning raw materials wt/wt
| Material name | Comparative example 1 | Comparative example 2 | Comparative example 3 | Comparative example 4 |
| Fluoro-resin (53%), g | ????300 | ????300 | ????300 | ????300 |
| Methyl-etherified aminoresin, g | ????- | ????102 | ????96 | ????100 |
| Methyl butyl mixes etherified amino resins, g | ????250 | ????136 | ????146 | ????156 |
| Acrylic resin, g | ????150 | ????162 | ????140 | ????152 |
| Rutile type Titanium Dioxide, g | ????- | ????100 | ????120 | ????- |
| Medium chrome yellow medium yellow, g | ????- | ????- | ????68 | ????200 |
| Phthalocyanine blue, g | ????- | ????25.37 | ????- | ????- |
| Organic red, g | ????- | ????- | ????12 | ????- |
| Wetting dispersing agent, g | ????- | ????20 | ????23 | ????21 |
| Acid catalyst, g | ????12 | ????10.5 | ????11.5 | ????14.5 |
| Flow agent, g | ????5 | ????6 | ????6 | ????5 |
| Anti-flooding agent, g | ????- | ????2.1 | ????2.3 | ????- |
| Mixed solvent, g | ????60 | ????79 | ????80 | ????90 |
Table 4. film performance test result relatively
| Test event | Embodiment 1 | Comparative example 1 | Comparative example 2 | Comparative example 3 | Comparative example 4 |
| Gloss (60 °) | ??85 | 81 | 82 | ????81 | ????80 |
| Pencil hardness | ??2H | 3H | 3H | ????2H | ????2H |
| Sticking power (drawing circle method/level) | ??1 | 1 | 1 | ????1 | ????1 |
| Snappiness/mm flawless, nothing comes off | Qualified | Qualified | Defective | Qualified | Qualified |
| Shock resistance 50kgcm | By | Do not pass through | Do not pass through | By | By |
| Acid resistance 10%H 2SO 4, 48 hours no changes | Qualified | Qualified | Qualified | Qualified | Qualified |
| Alkali resistance 10%NaOH, 48 hours no changes | Qualified | Qualified | Qualified | Qualified | Qualified |
| Resistance to salt water 3%NACL, 48 hours no changes | Qualified | Defective | Defective | Defective | Defective |
| Storage stability test (50 ℃), not gel | 720 hours | 240 hours | 240 hours | 360 hours | 240 hours |
As can be seen from Table 4, product gloss of the present invention is better than comparative example 1～4, in other eight performance index, product of the present invention is compared with comparative example, outside sticking power, acid resistance are identical with the alkali resistance performance, other performances of product of the present invention all are better than comparative example as boring a hardness, snappiness, shock-resistance, resistance to salt water, package stability.
In sum, the present invention is applicable to the requirement of differing materials, can be widely used in covering with paint and protections such as aluminium section bar, steel, antitheft door, factory's streamline.
Claims (5)
1, the fluorine carbon of low-temperature bake lacquer, it is characterized in that it contains fluoro-resin, linking agent, pigment, auxiliary agent and mixed solvent, the weight ratio fluoro-resin between each component: linking agent: pigment: auxiliary agent: mixed solvent=1: 0.1～0.25: 0～0.37: 0.02～0.04: 0.1～0.3.
2, fluorine carbon lacquer according to claim 1, it is characterized in that fluoro-resin is by trifluorochloroethylene, vinyl fatty ester, hydroxyl vinyl ether and the aliphatics olefin(e) acid is quarternary copolymerized forms, its hydroxyl value 40～60mg KOH/g, carboxylic value 3～8mgKOH/g, solid content 40～70%, and fluorine content is 15～45%; Linking agent adopts blocked isocyanate, as TDI, IPDI, HDI tripolymer; Auxiliary agent is two kinds to four kinds mixtures among four kinds, and auxiliary agent is as follows:
(1) wetting dispersing agent, composition are modified polyurethane, as EFKA-4047,
BYK-161, BYK-163, consumption are 0～0.08 times of fluoro-resin;
(2) flow agent, composition are organically-modified siloxanes or fluorine-carbon modified poly-third
Olefin(e) acid, as EFKA-3033, EFKA-3777, consumption are fluoro-resin
0.01～0.02 times;
(3) defoamer, composition is a polysiloxane solution, as BYK-066,
Consumption is 0～0.008 times of fluoro-resin;
(4) anti-flooding agent, composition is the modification nonionic silicones, as DP-
903, consumption is 0～0.008 times of fluoro-resin;
Solvent is dimethylbenzene, N-BUTYL ACETATE, S100 and dibasic ester, the mixture by 1: 0.2～0.4: 0.2～0.4: 0.05～0.1.
3, fluorine carbon according to claim 1 and 2 lacquer, it is characterized in that with the good linking agent blocked isocyanate of fluoro-resin miscible characteristic be the HDI tripolymer.
4, the method for preparation fluorine carbon lacquer as claimed in claim 1, it is characterized in that by the formulation weight ratio, add part fluoro-resin and wetting dispersing agent, stirring all, the back adds pigment, give dispersion, grind, reach the regulation fineness, add the residual fluorine resin by formula ratio, linking agent and various auxiliary agent, adjust viscosity, filter, through metering packing after the assay was approved.
5, the preparation method of fluorine carbon lacquer according to claim 4 is characterized in that baking condition is: storing temperature: 130～160, and storing time: 20～30 minutes.