CN1460746A - Composite textile and manufacturing process - Google Patents
Composite textile and manufacturing process Download PDFInfo
- Publication number
- CN1460746A CN1460746A CN 02135264 CN02135264A CN1460746A CN 1460746 A CN1460746 A CN 1460746A CN 02135264 CN02135264 CN 02135264 CN 02135264 A CN02135264 A CN 02135264A CN 1460746 A CN1460746 A CN 1460746A
- Authority
- CN
- China
- Prior art keywords
- film
- hot melt
- melt adhesive
- base material
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a composite textile and a manufacturing process, wherein the textile is used as a base material, a PU film is used as an auxiliary base material, and a hot melt adhesive layer is pressed into the base material and the auxiliary base material; selecting and heating a moisture-curing hot melt adhesive, coating the hot melt adhesive on a PU film, laminating and fusing the textile substrate and the PU film, and flatly and naturally winding the product after composite lamination for curing to achieve the required bonding strength. The composite textile has soft, comfortable and flat hand feeling, good waterproofness and vapor permeability, high strength and good flexibility, is dry-resistant, wet-abrasion-resistant, water pressure impact-resistant, high in low-temperature adaptability, good in dry-cleaning performance, oil-stain-resistant, dust-proof, windproof, warm-keeping, bacteria-resistant, easy to clean and wide in product application. The manufacturing process is simple and easy to operate.
Description
Technical field
The present invention relates to a kind of textiles and manufacturing technique, specifically a kind of composite fabric and manufacturing technique.
Background technology
Textile fabric is of a great variety, in use, requires to have the function of insulation, waterproof, saturating vapour usually, to adapt to different environment needs.Textiles not only will allow the consumer be dressed elegantly as garment material but also be comfortable, and possessing water proofing property and poisture-penetrability is two basic and conflicting again conditions creating the clothes comfortableness.In natural environment, in the change procedure between steam fog, water and the energy three, textiles will reach the requirement of Waterproof Breathable, at present high-density fabrics that adopt more, and coated fabric is realized.High-density fabric is to utilize the minim gap between the superfine fibre to reach the water-proof air-permeable performance, but its water-resistant pressure is very low, and water resistance is very undesirable.Coated fabric is that the coating agent that will be liquid condition is coated on the fabric uniformly, forms continuous glued membrane and reaches the purpose of water-proof air-permeable.What see on the market is applying coating agent on chemical fibre dimension lining more, cheap though its technology is simple, owing to coating process determines, can't solve the contradiction between waterproof and saturating the wetting.Thereby limited the function of lining, make little, the narrow range of its Application Areas.
Summary of the invention
Technical problem to be solved by this invention is to overcome above-mentioned the deficiencies in the prior art, provides a kind of powerful height and pliability is good, and sense organ is good, applied range, the composite fabric and the manufacturing technique thereof of waterproof, saturating vapour.
The technical scheme that the present invention solves the problems of the technologies described above employing is: a kind of composite fabric, it is characterized in that with the textiles being base material, and be auxiliary base material with the PU film, with hot melt adhesive the two adhesive lamination is made.
The manufacturing technique of the above-mentioned composite fabric of the present invention comprises the steps:
(A) with the smooth expansion of textile substrate;
(B) smooth expansion PU film, and preheating;
(C) choose and heat the moisturecuring hot melt adhesive, temperature is 70 ℃-150 ℃, and viscosity is 2000-20000mpas;
(D) hot melt adhesive is coated on the PU film coating weight 5-25g/m
2, coating clearance is 0.5-25mm.
(E) textile substrate and PU film lamination are merged, the lamination gap is 0.5-25mm.
(F) product after laminated is carried out smooth natural coiling, curling pressure is 0-3bar.
(G) 25 ℃ of temperature, be cured in humidity 50% environment, the time is 6-8 days, meets the requirements of adhesive strength.
The above-mentioned laminated textile touch softness of the present invention, comfortable, smooth, water proofing property and steam permeability are good, and powerful height and pliability is good is anti-ly done, the moisture-proof friction, water pressure resistance impacts, low temperature adaptability is strong, and the dry-cleaning performance is good, anti-greasy dirt, dustproof dying, wind-proof warming, resistance bacterium property, easy cleaning, product is widely used.Its manufacturing technique is simple, and is easy to operate.
The specific embodiment
The invention will be further described below in conjunction with embodiment:
Embodiment 1: a kind of composite fabric, it is a base material with common woollen textile fabric, is auxiliary base material with the PU film, with hot melt adhesive the two adhesive lamination is made.The PU film is a hydrophilic, and its thickness is 10-50 μ m.The manufacturing technique of the said goods is: at first, choosing the HL9595 moisturecuring is hot melt adhesive, is heated to 150 ℃ solidifying the HL9595 hot melt adhesive, and viscosity reaches 20000mpas; The woollen textile fabric of smooth expansion; The hydrophilic PU film of smooth expansion, and preheating, preheat temperature is 95-100 ℃; Hot melt adhesive is coated on the hydrophilic PU film coating weight 25g/m
2, coating clearance 25mm; Woollen textile fabric and hydrophilic PU film lamination are merged, and lamination gap 25mm reels then, and the smooth pressure 3bar that curls naturally is placed on 25 ℃ of temperature, solidifies 7 days in the environment of humidity 50%.
Embodiment 2: a kind of composite fabric, it is a base material with the cotton textile fabric, is auxiliary base material with the PU film, with hot melt adhesive the two adhesive lamination is made.The PU film is a hydrophilic, and its thickness is 10-50 μ m.The manufacturing technique of the said goods is: at first, choosing curing HL9640 is hot melt adhesive, is heated to 100 ℃ solidifying the HL9640 hot melt adhesive, and viscosity reaches 10000mpas; Smooth expansion cotton textile fabric; The hydrophilic PU film of smooth expansion, and preheating, preheat temperature is 95-100 ℃; Hot melt adhesive is coated on the hydrophilic PU film coating weight 15g/m
2, coating clearance 10mm; Cotton textile fabric and hydrophilic PU film lamination are merged, and lamination gap 12mm reels then, and the smooth pressure 1.5bar that curls naturally is placed on 25 ℃ of temperature, solidifies 7 days in the environment of humidity 50%.
This lining of the present invention can be widely used in the medicine and hygiene fields.Hydrophilic PU film is a non-porous film, under hydrophilic gene action, can reach good steam permeability, waterproof, windproof and resistance bacterium property.Laminated textiles has the propagation function of waterproof and breathable performance simulation biological cell, the hydrophilic factor utilizes the molecular diffusion principle at high humility one side draught attached water molecule, by hydrophilic group on the macromolecular chain because of being delivered to the one side desorb of low humidity, form the exclusion process of absorption-transmission-desorb, thereby reach the purpose of vapour, hydrophilic PU film has extraordinary water proofing property, windproof property and resistance bacterium property.Its specific targets reach:
Saturating vapour amount: 〉=8000g/m
224h
Brute force: 〉=333.62N pulling force/continuous washing/broadwise
Washing shrinkage: TD≤2%, MD≤3%
Plain grinding: 〉=300 times
Water pressure resistance: 1000cm-2000cm static pressure water column
Anti-contamination, WATER REPELLENCY: Pyatyi.
Embodiment 3: a kind of composite fabric, it is a base material with chemical fibre terylene textile fabric, is auxiliary base material with the PU film, with hot melt adhesive the two adhesive lamination is made.The PU film is a pore type, and its thickness is 10-50 μ m.The manufacturing technique of the said goods is: at first, choosing curing HL9639 is hot melt adhesive, is heated to 70 ℃ solidifying the HL9639 hot melt adhesive, and viscosity reaches 2000mpas; Smooth expansion chemical fibre polyester fabric lining; Smooth expansion pore type PU film, and preheating, preheat temperature is 95-100 ℃; Hot melt adhesive is coated on the micropore PU film coating weight 5g/m
2, coating clearance-0.5mm; Chemical fibre terylene and micropore PU film lamination are merged one, lamination gap-0.5mm, smooth then coiling naturally, the pressure 0bar that curls is placed on 25 ℃ of temperature, solidifies 7 days in the environment of humidity 50%.Because the micropore diameter 0.01-0.03nm of micropore PU film, the average diameter of little water droplet is 10000nm, and the average diameter of stream molecule has only 0.000004nm, and water droplet can't see through so have only water vapour to see through, therefore can reach waterproof, windproof, permeability is good.
Textile substrate of the present invention is to realize that functional carrier is again the main body of product, the PU film had both embodied the major function of product, it is again the additional materials of main body, hot melt adhesive be coated on can reach behind the bonding textiles base material lamination on the PU film water-proof air-permeable, windproof, warming, the resistance bacterium property, water-fast wash high temperature resistant, anti-low temperature, because the moisturecuring hot melt adhesive is environment-friendly products, base material also is environment-friendly products, and therefore, the joint product of producing belongs to green product.Its technology is rationally, simply, and is easy to operate, easy processed finished products, and applied range, not with solvent reaction, soft fine and smooth, good hand touch.
Claims (2)
1. a composite fabric is characterized in that with the textiles being base material, is auxiliary base material with the PU film, with hot melt adhesive the two adhesive lamination is made.
2. composite fabric manufacturing technique as claimed in claim 1 is characterized in that: comprise the steps
(A) with the smooth expansion of textile substrate;
(B) smooth expansion PU film, and preheating;
(C) choose and heat the moisturecuring hot melt adhesive, temperature is 70 ℃-150 ℃, and viscosity is 2000-20000mpas;
(D) hot melt adhesive is coated on the PU film coating weight 5-25g/m
2, coating clearance is 0.5-25mm.
(E) textile substrate and PU film lamination are merged, the lamination gap is 0.5-25mm.
(F) product after laminated is carried out smooth natural coiling, curling pressure is 0-3bar.
(G) 25 ℃ of temperature, be cured in humidity 50% environment, the time is 6-8 days, meets the requirements of adhesive strength.