CN103522726A - Textile compounding technology - Google Patents
Textile compounding technology Download PDFInfo
- Publication number
- CN103522726A CN103522726A CN201310514741.7A CN201310514741A CN103522726A CN 103522726 A CN103522726 A CN 103522726A CN 201310514741 A CN201310514741 A CN 201310514741A CN 103522726 A CN103522726 A CN 103522726A
- Authority
- CN
- China
- Prior art keywords
- base material
- textile
- auxiliary base
- lamination
- thermoplastic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a textile compounding technology, which is characterized by taking a textile as a base material, and adopting non-woven fabric, a sponge, leather or a film as an auxiliary base material. The method comprises the steps of: 1) selecting a hot melt adhesive or thermoplastic resin and conducting heating to 130-200DEG C to melt it, controlling the viscosity at 3000-200000mpas; 2) spreading the base material and the auxiliary base material; 3) coating the base material or the auxiliary base material with the molten hot melt adhesive or thermoplastic resin through a fiber coater, and keeping the coating weight at 3-40g/m<2>; 4) subjecting the base material and the auxiliary base material to lamination fusion; and 5) cooling the laminated and fused product and conducting coiling. The composite laminated textile involved in the invention has soft, comfortable and smooth handfeel, good waterproofness and vapor permeability, high strength and good flexibility, resistance to hydraulic impact, strong low temperature adaptability, good dry cleaning performance, and can prevent oil stain, dust pollution and wind and keep warm. With the characteristics of bacterial resistance and easy cleaning, the product has wide application.
Description
Technical field
The present invention relates to a kind of textile combination process.
Background technology
Textile fabric is of a great variety, in use, conventionally requires to have the function of insulation, waterproof, saturating vapour, to adapt to different need for environments.Textile not only will allow consumer be dressed elegantly as garment material but also be comfortable, possesses water proofing property and poisture-penetrability and be the basic and conflicting condition again of two of comfortable features of clothing of creating.In natural environment, in the change procedure between steam fog, water and energy three, textile will reach the requirement of Waterproof Breathable, adopts high-density fabrics at present more, and coated fabric is realized.High-density fabric is to utilize the minim gap between superfine fibre to reach water-proof air-permeable performance, but its water-resistant pressure is very low, and water resistance is very undesirable.Coated fabric is that the coating agent that is liquid condition is coated on fabric uniformly, forms the object that continuous glued membrane reaches water-proof air-permeable.Common on market is changing applying coating agent on fabric lining, although its technique is simple, cheap, because coating process determines, cannot solve the contradiction between waterproof and saturating wetting.Thereby limited the function of fabric, make that its application is little, narrow range.
Summary of the invention
For problems of the prior art, the object of the present invention is to provide a kind of technical scheme of textile combination process.
Described a kind of textile combination process, is characterized in that take that textile is as base material, take nonwoven, sponge, leather or film as auxiliary base material, comprises the steps:
1) choose PUR or thermoplastic resin heating and make its fusing, heating-up temperature is 130-200 ℃, and viscosity is 3000-200000mpas;
2) base material and the tiling of auxiliary base material are launched;
3) PUR having melted or thermoplastic resin are coated on base material or auxiliary base material by fiber spreader, coating weight is 3-40g/m
2;
4) base material and auxiliary base material lamination are merged;
5) the compound good product of lamination is batched through supercooling.
Described a kind of textile combination process, is characterized in that in described step 3), coating weight is 10-30g/m
2.
Described a kind of textile combination process, is characterized in that the lamination gap that in described step 4), lamination merges is 0.5-25mm.
Described a kind of textile combination process, is characterized in that the product after batching in described step 5) will be cured in the environment of 25 ℃ of temperature, humidity 50%, time 6-8 days.
The above-mentioned laminated textile touch of the present invention is soft, comfortable, smooth, water proofing property and steam permeability are good, powerful high and pliability is good, resistance to dry, moisture-proof friction, water pressure resistance impacts, low temperature adaptability is strong, and dry-cleaning performance is good, oil-stain-preventing, dustproof dying, wind-proof warming, resistance bacterium property, easy cleaning, product is widely used; Its manufacturing process is simple, easy to operate.
The specific embodiment
A combination process, take textile as base material, take nonwoven, sponge, leather or film as auxiliary base material, comprises the steps:
1) choose PUR or thermoplastic resin heating and make its fusing, heating-up temperature is 130-200 ℃, and viscosity is 3000-200000mpas;
2) base material and the tiling of auxiliary base material are launched;
3) PUR having melted or thermoplastic resin are coated on base material or auxiliary base material by fiber spreader, coating weight is 3-40g/m
2;
4) base material and auxiliary base material lamination are merged;
5) the compound good product of lamination is batched through supercooling.
Above-mentioned steps 3) in, coating weight is 10-30g/m
2, the lamination gap that in step 4), lamination merges is 0.5-25mm, the product after batching in step 5) will be cured in the environment of 25 ℃ of temperature, humidity 50%, time 6-8 days.
The above-mentioned laminated textile touch of the present invention is soft, comfortable, smooth, water proofing property and steam permeability are good, powerful high and pliability is good, resistance to dry, moisture-proof friction, water pressure resistance impacts, low temperature adaptability is strong, and dry-cleaning performance is good, oil-stain-preventing, dustproof dying, wind-proof warming, resistance bacterium property, easy cleaning, product is widely used; Its manufacturing process is simple, easy to operate.
Claims (4)
1. a textile combination process, is characterized in that take that textile is as base material, take nonwoven, sponge, leather or film as auxiliary base material, comprises the steps:
1) choose PUR or thermoplastic resin heating and make its fusing, heating-up temperature is 130-200 ℃, and viscosity is 3000-200000mpas;
2) base material and the tiling of auxiliary base material are launched;
3) PUR having melted or thermoplastic resin are coated on base material or auxiliary base material by fiber spreader, coating weight is 3-40g/m
2;
4) base material and auxiliary base material lamination are merged;
5) the compound good product of lamination is batched through supercooling.
2. a kind of textile combination process according to claim 1, is characterized in that in described step 3), coating weight is 10-30g/m
2.
3. a kind of textile combination process according to claim 1, is characterized in that the lamination gap that in described step 4), lamination merges is 0.5-25mm.
4. a kind of textile combination process according to claim 1, is characterized in that the product after batching in described step 5) will be cured in the environment of 25 ℃ of temperature, humidity 50%, time 6-8 days.